CN1446869A - Colored heat insulation anti soak coating material - Google Patents
Colored heat insulation anti soak coating material Download PDFInfo
- Publication number
- CN1446869A CN1446869A CN 03114175 CN03114175A CN1446869A CN 1446869 A CN1446869 A CN 1446869A CN 03114175 CN03114175 CN 03114175 CN 03114175 A CN03114175 A CN 03114175A CN 1446869 A CN1446869 A CN 1446869A
- Authority
- CN
- China
- Prior art keywords
- coating
- heat insulation
- powder
- water
- calcium carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
An insulating color paint resisting water immersion is prepared from white jade powder, nano calcium carbonate, light calcium carbonate, water, talc powder, mica-Ag-Pt powder, water pigment, silicic propylene emulsion, F-C emulsion and assistant through sequentially mixing and reaction. Its advantages are exellent heat insulating and dissipating performance, high resistance to ultravidet ray and dirt, and high weatherability.
Description
Technical field
The present invention relates to the field of heat-insulating waterproof coating, in particular for the coating of top of building or platform.
Background technology
Heat-insulating waterproof coating in the past, as Chinese patent ZL99117156.X disclosed " a kind of heat insulation, waterproof paint ", its existing problems have:
1. effect of heat insulation is poor;
2. monochromatic heat insulation-adularescent;
3. water resistance is poor;
4. easily lose the waterproof and heat-insulating performance;
5. distributing harmful thing exceeds standard.
Because traditional used inferior coarse grain ash calcium powder of heat-insulating waterproof coating makes its heat-proof quality humble; Coating self color is restricted, only by white part reflected sunlight heat, can not modulate multiple color thermal insulating coating; Because the benzene of benzene emulsion contains the Chemical Composition of harmful to human, not environmental protection of coating; The water-repellancy of polyvinyl alcohol adhesive, weathering resistance extreme difference, antifouling property is extreme difference also, because thermal insulating coating is mainly used in exterior wall, flooring, expose to the weather and drench with rain, so using, heat-insulating waterproof coating in the past then lost effect of heat insulation in two to three months, even be subjected to rain drop erosion and come off, be a loss greatly to the user, be difficult to apply.
Summary of the invention
First purpose of the present invention is: a kind of coloury heat insulation anti-efficient coating that soaks is provided;
Second purpose of the present invention is: provide that a kind of antifouling property is good, the heat insulation anti-efficient coating that soaks of good weatherability, long service life;
The 3rd purpose of the present invention is: provide a kind of cost low, the simple heat insulation anti-efficient coating that soaks of constructing.
The object of the present invention is achieved like this: the heat insulation anti-dip-coating material of a kind of colour, and its composition is:
Beautiful white stone powder 20%-30%
The nano-calcium carbonate 6%-10% of particle diameter 15nm-30nm
Water 15%-25%
Light calcium carbonate 6%-10%
Talcum powder 3%-6%
Mica silver-platinum powder 0.05%-0.1%
Water-based paint 0.05%-0.08%
Organosilicon crylic acid latex 10%-20%
Fluorine carbon emulsion 5%-10%
Auxiliary agent 1%-3%
Wherein auxiliary agent contains defoamer 0.1%-0.3%, wetting agent 0.5%-1%, dispersion agent 0.1-0.5%, softening agent 0.5%-1%, sanitas 0.5%-1%.The coat-thickness that this coating forms is 0.5mm-1mm.
The present invention adopts beautiful white stone powder, nano-calcium carbonate, light calcium carbonate, talcum powder, mica silver-platinum powder, water-based paint, organosilicon crylic acid latex fluorine carbon emulsion, the reaction of auxiliary agent batch mixing, the coating that draws is evenly brushed, brushing parches the rete that is coated with of formation, has superior heat insulation, heat dispersion.The nano-calcium carbonate wherein and the association reaction of organosilicon crylic acid latex, Nano particles of calcium carbonate is coated the formed coating layer in back by the silicon molecule, has stronger anti-solar ultraviolet optical property, acid resistance, antifouling property; Nano-calcium carbonate combines with mica silver-platinum powder, goes up different colours even transfer, and its effect of heat insulation can not be affected substantially yet.Test shows that coating of the present invention is used for the iron sheet tiling, and its iron sheet surface is up to 27 ℃, and the indoor temperature difference has only 8 ℃.Almost by isolated, the continuous bubble of coating soaks and did not come off in 4000 hours cement works flooring solar thermal energy.Artificial ageing resistance reaches 500 hours.
The heat insulation anti-dip-coating material of colour of the present invention can be made into various abundant colors, and the insulating water-proof performance is same excellent with white.Wherein light calcium carbonate plays anti-heavy effect, and talcum powder can increase levelling property, and defoamer is eliminated the coating bubble, and wetting agent, sanitas never degenerate coating for a long time, and dispersion agent is even with colo(u)rant dispersion, does not have granules of pigments, and softening agent strengthens the coatingsurface tenacity.
The household buildings is used the heat insulation anti-dip-coating material of colour of the present invention, and summer is nice and cool, the rainy day ne-leakage, and it is relieved, happy to live; Factory building is used the heat insulation anti-dip-coating material of colour of the present invention, and indoor air temperature reduces greatly, and the working environment of workers improves greatly, and working efficiency improves greatly.The heat insulation anti-dip-coating material cost of colour of the present invention is low, effective, construction is simple, long service life.
Embodiment
Embodiment one:heat insulation anti-each component of dip-coating material of pink is as follows:(unit K G; Gross weight 1000KG) beautiful albarium 250 nano-calcium carbonates 80 precipitated calcium carbonates 100 talcum powder 50 Japanese SB-100 mica silver-platinum powder 1 pink aqueous pigment 0.8 Silicone acrylic emulsion 150 fluorine carbon emulsions 100 water 250 auxiliary agents 18.2 extra large river chemical industry 309 type defoamers 3 wherein
River, sea chemical industry P200 type wetting agent 5.4,
River, sea chemical industry 503 type dispersion agents 5,
Dibutylester softening agent 4,
River, sea chemical industry 315 type sanitass 0.8, the coat-thickness that this coating forms is 0.6mm.
Embodiment two:blue heat insulation anti-each component of dip-coating material is as follows:(unit K G; Gross weight 1000KG) beautiful albarium 200 nano-calcium carbonates 100 precipitated calcium carbonates 100 talcum powder 60 Japanese SB-100 mica silver-platinum powder 1 blue water-based pigment 1 Silicone acrylic emulsion 180 fluorine carbon emulsions 120 water 220 auxiliary agents 18 defoamer 3 wherein; Wetting agent 5; Dispersant 5
Softening agent 4, sanitas 1, composition and enforcement
Example one identical, the content difference.
The coat-thickness that this coating forms is 1mm.
The production method of coating:
(1) distilled water, organosilicon crylic acid latex, fluorine carbon emulsion being put into reactor stirred 10 minutes;
(2) beautifulr white stone powder, nano-calcium carbonate, light calcium carbonate, talcum powder are put into reactor and stirred 30 minutes, stop carrying out in 20 minutes reactive polymeric;
(3) mica silver-platinum powder, water-based paint, auxiliary agent are put into reactor and stirred 40 minutes, stopped restir 20 minutes 20 minutes;
(4) above-mentioned materials being put into shredder grinds;
(5) will put into strainer through the material that grinds filters;
(6) with product packing, packing.
Above-mentioned process sequence is (1), (2), (3), (4), (5), (6).
Certainly, only enumerated two kinds of embodiments here, other composition that roughly the same, is equal to, technology, content etc. all should belong to the protection domain of this patent, repeat no more here.
Claims (3)
1. heat insulation anti-dip-coating material of colour is characterized in that:
Beautiful white stone powder 20%-30%
The nano-calcium carbonate 6%-10% of particle diameter 15nm-30nm
Water 15%-25%
Light calcium carbonate 6%-10%
Talcum powder 3%-6%
Mica silver-platinum powder 0.05%-0.1%
Water-based paint 0.05%-0.08%
Organosilicon crylic acid latex 10%-20%
Fluorine carbon emulsion 5%-10%
Auxiliary agent 1%-3%
Wherein auxiliary agent contains defoamer 0.1%-0.3%, wetting agent 0.5%-1%, dispersion agent 0.1-0.5%, softening agent 0.5%-1%, sanitas 0.5%-1%.
2. the described coating of claim 1, the coat-thickness that this coating forms is 0.5mm-1mm.
3. the described coating of claim 1, mica silver-platinum powder is Japanese import SB-100 product.