KR20190090957A - 2-coat-type aqueous heat-shielding and water-resistant paint for rooftop or roof, method for forming a heat-shielding and water-resistant coating with two layers structure using the same, and a heat-shielding and water-resistant coating with two layers structure thereby - Google Patents

2-coat-type aqueous heat-shielding and water-resistant paint for rooftop or roof, method for forming a heat-shielding and water-resistant coating with two layers structure using the same, and a heat-shielding and water-resistant coating with two layers structure thereby Download PDF

Info

Publication number
KR20190090957A
KR20190090957A KR1020180009792A KR20180009792A KR20190090957A KR 20190090957 A KR20190090957 A KR 20190090957A KR 1020180009792 A KR1020180009792 A KR 1020180009792A KR 20180009792 A KR20180009792 A KR 20180009792A KR 20190090957 A KR20190090957 A KR 20190090957A
Authority
KR
South Korea
Prior art keywords
heat
water
weight
paint
shielding
Prior art date
Application number
KR1020180009792A
Other languages
Korean (ko)
Inventor
강기준
Original Assignee
삼화페인트공업주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 삼화페인트공업주식회사 filed Critical 삼화페인트공업주식회사
Priority to KR1020180009792A priority Critical patent/KR20190090957A/en
Publication of KR20190090957A publication Critical patent/KR20190090957A/en

Abstract

The present invention relates to a two-coat type aqueous heat-shielding waterproof paint of a rooftop or a roof consisting of an aqueous heat-shielding paint and an aqueous insulating paint, wherein the aqueous heat-shielding paint dissolves or disperses heat shielding pigments, white pigments, acrylic binder resins, a diluent and other additives in water, and the aqueous insulating paint dissolves or disperses hollow pigments, the white pigments, extender pigments, elastic binder resins, the diluent and other additives in the water, to a heat-shielding waterproof coating method of two-layer structure using the same, and to a heat shielding waterproof paint film of a two-layer structure thereby. The two-coat type aqueous heat-shielding waterproof paint of a rooftop or a roof is eco-friendly and has excellent workability, and the heat shielding waterproof paint film having the two-layer structure manufactured therefrom can exhibit excellent heat shielding and heat insulating properties without deteriorating physical properties and durability even in the environment directly exposed to daylight and climate change.

Description

옥상 또는 지붕용 2-코트형 수성 차열성 방수 도료, 이를 사용한 2층 구조의 차열성 방수 도장 방법, 및 그에 따른 2층 구조의 차열성 방수 도막 {2-COAT-TYPE AQUEOUS HEAT-SHIELDING AND WATER-RESISTANT PAINT FOR ROOFTOP OR ROOF, METHOD FOR FORMING A HEAT-SHIELDING AND WATER-RESISTANT COATING WITH TWO LAYERS STRUCTURE USING THE SAME, AND A HEAT-SHIELDING AND WATER-RESISTANT COATING WITH TWO LAYERS STRUCTURE THEREBY}2-coat type water-based heat-resistant waterproof coating for roof or roof, heat-resistant waterproof coating method of two-layer structure using the same, and heat-resistant waterproof coating of two-layer structure according thereto {2-COAT-TYPE AQUEOUS HEAT-SHIELDING AND WATER- RESISTANT PAINT FOR ROOFTOP OR ROOF, METHOD FOR FORMING A HEAT-SHIELDING AND WATER-RESISTANT COATING WITH TWO LAYERS STRUCTURE USING THE SAME, AND A HEAT-SHIELDING AND WATER-RESISTANT COATING WITH TWO LAYERS STRUCTURE THEREBY}

본 발명은 옥상 또는 지붕에서 일광 등에 의한 복사열의 차열 및 단열을 위해 사용할 수 있는 2-코트형 수성 차열성 방수 도료, 이를 사용한 2층 구조의 차열성 방수 도장 방법, 및 그에 따른 2층 구조의 차열성 방수 도막에 관한 것으로, 더욱 상세하게는, 차열안료, 백색안료, 아크릴계 바인더 수지, 희석제 및 기타 첨가제를 물에 용해 또는 분산시킨 상도용 수성 차열성 페인트 및 중공안료, 백색안료, 체질안료, 탄성 바인더 수지, 희석제 및 기타 첨가제를 물에 용해 또는 분산시킨 하도용 수성 단열성 페인트로 이루어진 2-코트형 수성 차열성 방수 도료, 당해 방수 도료를 사용하는 2층 구조의 차열성 방수 도장 방법, 그에 따른 차열층 및 단열층의 2층 구조를 갖는 차열성 방수 도막에 관한 것이다. The present invention is a two-coat type water-based heat-resistant waterproof paint that can be used for the heat shielding and thermal insulation of the radiant heat by daylight or the like on the roof or roof, a heat shielding waterproof coating method of a two-layer structure using the same, and the difference between the two-layer structure The present invention relates to a heat-resistant waterproof coating, and more particularly, to a water-based heat-shielding paint and hollow pigment, white pigment, sieving pigment, and elasticity obtained by dissolving or dispersing a heat shield pigment, a white pigment, an acrylic binder resin, a diluent, and other additives in water. 2-coat type water-based heat-resistant waterproof paint consisting of an aqueous insulating paint for undercoat in which binder resin, diluent, and other additives are dissolved or dispersed in water, a heat-shielding waterproof coating method having a two-layer structure using the waterproofing paint, and the difference thereof. A heat-resistant waterproof coating film having a two-layer structure of a heat layer and a heat insulation layer.

여름철에 건물의 내부온도를 실제로 상승시키는 것은 외부 기온보다도 지붕표면의 온도이다. 일반적으로 건물의 지붕 및 외벽 등에 사용되는, 소위 "단열재"라고 하는 것은 열전도율이 낮아, 외부의 열이 내부로 전달되는 것을 억제하는 것으로서 어느 정도 두께가 있는 소재를 말하며, 대표적으로 유리섬유, 폴리스티렌폼 및 폴리우레탄폼 등이 있다.It is the roof surface temperature rather than the outside temperature that actually raises the building's internal temperature during the summer months. In general, the so-called "insulation material", used for roofs and exterior walls of buildings, refers to a material having a certain thickness as a material having low thermal conductivity and suppressing the transfer of external heat to the interior, typically glass fiber or polystyrene foam. And polyurethane foams.

반면에, 차열도료는 100∼200 ㎛의 도막두께로 태양광 중의 적외선을 효과적으로 반사시키고, 지붕표면의 온도를 낮춤으로써, 건물내부로 유입되는 열을 감소시켜 실내온도 상승을 억제하는 역할을 한다.On the other hand, the heat shielding paint effectively reflects infrared rays in sunlight with a coating thickness of 100 to 200 μm, and lowers the temperature of the roof surface, thereby reducing the heat flowing into the building and thus suppressing the increase in the indoor temperature.

상기 차열도료로 금속 표면을 도장했을 때, 특히 차열효과가 높은데, 그 이유는 금속의 장파 방사율이 낮기 때문이다. 여기서, 장파 방사율이란 지붕재 등의 고체와 공기와의 사이에서 이루어지는 열전달의 정도를 나타내는 값으로, 차열도료의 장파 방사율은 매우 높아, 뜨거워진 지붕재로부터 대기중으로 다량의 열을 방사하기 때문에, 지붕재의 온도가 내려가 실내로 진입하는 열을 감소시킨다.When the metal surface is coated with the heat shield coating, the heat shielding effect is particularly high because the long wave emissivity of the metal is low. Here, the long wave emissivity is a value indicating the degree of heat transfer between solids such as roofing materials and air, and the long wave emissivity of the heat shielding coating is very high, and since a large amount of heat is radiated from the heated roofing material into the atmosphere, the temperature of the roofing material To reduce the heat entering the room.

차열도료의 차열성과 가장 밀접한 관계가 있는 것은 일사 반사율로서, 차열도료의 일사 반사율은 매우 높기 때문에, 실제로 차열도료로 도장된 건축물의 경우 실내로 진입하는 열이 큰 폭으로 감소되어 실내온도가 낮게 유지된다. 특히, 차열도료를 단열재가 시공되지 않은 지붕에 도장하면 대폭적인 에너지 절감 효과를 기대할 수 있다.Solar heat reflectance is most closely related to heat shielding of heat shielding paints. Since the heat reflectivity of heat shielding paints is very high, in fact, in the case of buildings painted with heat shielding paints, the heat entering the room is greatly reduced and the room temperature is low. maintain. In particular, when the thermal insulation paint is applied to the roof without insulation, a significant energy saving effect can be expected.

상기와 같은 이유로, 단열도료와 차별화하여 차열도료라고 부르며, 또한 이것은 낮은 열전도율을 이용하는 소위 단열도료와 혼동하지 않기 위한 것이다.For the same reason as above, it is called thermal insulation paint differently from heat insulation paint, and this is also not to be confused with so-called heat insulation paint using low thermal conductivity.

한편, 태양 복사열을 냉각시키는 특성을 가지는 표면 코팅 조성물이 공개된 바 있으며 (국제공개공보 WO 제02/098996호), 상기 표면 코팅 조성물은 태양광 반사 도료를 함유하고 있어 태양광 흡수율이 낮고, 특히 적외선 영역에 대응하는 파장에서 우수한 방열 특성을 나타낸다. 특히, 상기 표면 코팅 조성물 내에 쉘(shell) 형태의 마이크로스피어(microsphere) 형태를 이용하여 태양광 반사 도료를 함유하나, 태양광 중 적외선 영역에 대해서만 높은 반사율을 보여, 전반적인 열 차단효과는 떨어진다는 단점이 있다.On the other hand, a surface coating composition having a property of cooling solar radiation has been disclosed (WO 02/098996), and the surface coating composition contains a solar reflecting paint, and thus has a low solar absorption rate. It exhibits excellent heat dissipation characteristics at a wavelength corresponding to the infrared region. In particular, the surface coating composition contains a solar reflecting paint using a shell-type microsphere, but shows a high reflectance only in the infrared region of the sunlight, thereby reducing the overall heat shielding effect. There is this.

또한, 복사 에너지에 노출되는 표면의 온도를 감소시키는 코팅 조성물에 대한 보고가 있다 (미국 공개특허공보 제2005/0288394호). 여기서, 상기 코팅 조성물은 방열성, 절연성, 반사특성 및 흡열성을 나타낸다고 기재되어 있으며, 주로 태양 에너지에서 열에너지로의 변환을 억제하는 기능을 가지는 코팅 조성물에 대하여 개시되어 있다.There is also a report on coating compositions that reduce the temperature of surfaces exposed to radiant energy (US Patent Publication No. 2005/0288394). Here, the coating composition is described as exhibiting heat dissipation, insulation, reflective properties, and endothermic properties, and is mainly disclosed as a coating composition having a function of suppressing the conversion of solar energy into thermal energy.

현재까지 내오염성, 가요성, 내산성 및 광택성 등이 우수한 도막을 형성하는 상도 조성물(일본 공개특허공보 제96-102287호 및 제96-102287호), 태양열 반사 효과와 단열성이 뛰어나고 외부 오염에 대한 방지성이 우수한 장점을 가지는 비오염성 태양열 차단 단열 도료 조성물(국내 공개특허공보 제1020010088084호) 및 스프레이용 빛 반사도료 조성물(국내 공개특허공보 제1020020071976호)과 같이 열을 차단하는 기능의 도료 조성물에 관한 다방면의 시도가 있으나, 상기 도료 조성물들은 단순히 열의 전달을 억제할 뿐, 전달되는 열 자체를 막지는 못한다.Topcoat compositions (Japanese Patent Laid-Open Nos. 96-102287 and 96-102287) which form coating films with excellent stain resistance, flexibility, acid resistance, and glossiness to date, have excellent solar reflecting effect and thermal insulation, and In a non-polluting heat shield thermal coating composition (Domestic Patent Publication No. 1020010088084) and spray light reflecting coating composition (Domestic Patent Publication No. 1020020071976) having an excellent anti-preventive property to a coating composition having a function of blocking heat While various attempts have been made, the paint compositions merely inhibit the transfer of heat and do not prevent the heat itself from being transferred.

하기 특허문헌 1은 차열능을 가지는 방수재용 상도 조성물 및 이를 이용한 도장 방법에 관한 것으로, 보다 자세하게는, 아크릴 수지 35 ∼ 45 중량부, 분산제 0.1 ∼ 1 중량부, 차열안료 35 ∼ 45 중량부, 침강방지제 0.1 ∼ 1 중량부, 촉매 0.1 ∼ 1 중량부 및 폴리에스테르 수지 5 ∼ 15 중량부를 함유하는 주제부; 및 폴리이소시아네이트 40 ∼ 50 중량부, 수분흡수제 0.1 ∼ 1 중량부 및 희석제 50 ∼ 60 중량부를 함유하는 경화제부를 함유하는 2액형의 차열능을 가지는 방수재용 상도 조성물 및 이를 이용한 도장방법을 개시하고 있다. 상기 문헌에 따른 상도 조성물은 폴리우레탄 수지를 주성분으로 한 방수재에 상도로서 적용함으로써, 중도를 자외선으로부터 보호하여 내구성, 굴곡성 및 내충격성 등의 물성을 나타낼 뿐만 아니라, 태양광선 중 적외선을 효과적으로 반사시켜 옥상표면의 온도를 낮추어 건축물 내부로 유입되는 열을 줄여줌에 따라 실내온도 상승을 억제시키는 차열성능을 나타내며, 이에 따른, 건축물 실내 냉방 에너지를 절감시킬 수 있다. 그러나, 상기 문헌에 따른 상도 조성물은 유기 용매를 사용하는 유성 페인트 조성물이어서, 작업 및 환경적인 측면에서 불리한 점을 가지고 있다. The following Patent Document 1 relates to a coating composition for a waterproofing material having heat shielding ability and a coating method using the same. A main part containing 0.1 to 1 part by weight of the inhibitor, 0.1 to 1 part by weight of the catalyst, and 5 to 15 parts by weight of the polyester resin; And a top coating composition for waterproofing materials having a two-part thermal insulation capability containing 40 to 50 parts by weight of polyisocyanate, 0.1 to 1 part by weight of water absorbent, and 50 to 60 parts by weight of diluent, and a coating method using the same. The top coat composition according to the above document is applied as a top coat to a waterproofing material mainly composed of a polyurethane resin, thereby protecting the midway from ultraviolet rays to exhibit physical properties such as durability, bendability and impact resistance, as well as effectively reflecting infrared rays in sunlight to form a rooftop. As the temperature of the surface is lowered to reduce the heat flowing into the interior of the building, the thermal insulation performance is suppressed to suppress the increase in the indoor temperature. However, the top coat composition according to the above document is an oil paint composition using an organic solvent, and thus has disadvantages in terms of work and environment.

하기 특허문헌 2는 아크릴 에멀젼 수지에 차열안료 및 중공안료를 함께 포함시킨 수용성 차열 도료 조성물을 아스팔트 또는 콘크리트와 같은 무기성 바닥표면에 적용하는 것이 개시되어 있다. 상기 문헌에서는, 특수 모노머로 구성된 수용성 아크릴 에멀젼 수지를 사용하고 다양한 색상의 칼라 코팅제를 함유함으로써, 주변 미관을 아름답게 하고 휘발성 유기화합물(VOC)을 최소화하고 냄새가 적으며 건조가 빠르고 은폐력, 내수성, 내오염성, 내마모성, 내구성, 내수성, 내알칼리성, 내후성이 우수하며 미끄럼 방지 기능 및 태양광선 중 적외선을 효과적으로 반사시켜 노면의 온도 상승을 억제하여 도심의 열섬현상을 억제할 수 있는 차열성능을 발휘할 수 있어 자전거 전용 도로용으로 적합하다고 개시하고 있다.Patent Document 2 discloses the application of a water-soluble heat-shielding coating composition comprising a heat-shielding pigment and a hollow pigment together in an acrylic emulsion resin to an inorganic floor surface such as asphalt or concrete. In this document, the use of water-soluble acrylic emulsion resin composed of special monomers and containing color coatings of various colors, beautifully surrounding the beauty of the appearance, minimizing volatile organic compounds (VOC), low odor, fast drying, hiding power, water resistance, water resistance Excellent pollution, abrasion resistance, durability, water resistance, alkali resistance, weather resistance, anti-skid function, and effectively reflects infrared rays from sunlight to suppress the rise of the road surface temperature, showing the heat shielding ability to suppress the heat island phenomenon in the city It is disclosed to be suitable for use on a private road.

하기 특허문헌 3은 (i) 측정된 유리전이온도(측정된 tg)가 -100 내지 0인 하나 이상의 탄성 코폴리머와 하나 이상의 메조포러스(mesoporous) 필러, 바람직하게 유기그룹 또는 잔기가 실질적으로 없는 메노포로스 필러를 포함하는 우수한 적외선(ir) 반사율을 갖는 탄성 지붕 코팅제로서 사용하기 위한 수성 또는 용매 함유 조성물을 개시하고 있으나, 차열성이나 차열안료의 사용에 대해서는 어떠한 언급이 없다. Patent Document 3 discloses (i) a meno substantially free of at least one elastic copolymer having a measured glass transition temperature (measured tg) of -100 to 0 and at least one mesoporous filler, preferably an organic group or moiety. Aqueous or solvent containing compositions are disclosed for use as elastic roof coatings having good infrared reflectivity, including poros fillers, but no mention is made of the use of heat shielding or heat shielding pigments.

따라서, 당업계에서는 상기의 문제점을 해결하기 위하여, 기존의 도료 조성물로서의 물성과 함께 우수한 차열효과를 나타내는 수성 도료 조성물의 개발이 절실하게 요구되고 있다. Therefore, in the art, in order to solve the above problems, there is an urgent need for the development of an aqueous coating composition exhibiting excellent heat shielding effect together with the physical properties of the existing coating composition.

등록특허공보 제10-0662602호 (등록일 2006.12.21.)Patent Registration No. 10-0662602 (Registration date 2006.12.21.) 공개특허공보 제10-2011-0072514호 (공개일 2011.06.29.)Publication No. 10-2011-0072514 (Published Date 2011.06.29.) 공개특허공보 제10-2016-0007365호 (공개일 2016.01.20.)Publication No. 10-2016-0007365 (published Jan. 20, 2016)

본 발명자들은, 옥상 또는 지붕에 설치되어, 직사 일광 및 가혹한 외기에 직접 노출되는 환경에서도, 차열성 및 단열성 등의 열적 특성이 뛰어나고, 친환경적인 수성 차열성 방수 도막을 설치할 수 있는 도료 및 도장 방법에 대해 예의 연구해왔다. The inventors of the present invention provide a coating and coating method that can be installed on a rooftop or a roof, which is excellent in thermal properties such as heat shielding and heat insulating properties and can be installed in an environment-friendly water-based heat-shielding waterproof coating film even in an environment where it is directly exposed to direct sunlight and harsh outdoor air. I have been studying politely.

본 발명자들은, 일광 및 기후 변화에 직접 노출되는 옥상 또는 지붕에, 중공안료 0.1∼2중량%, 백색안료 1∼5중량%, 체질안료 20∼40중량%, 탄성 바인더 수지 40∼60중량%, 희석제 1∼5중량%, 첨가제 5∼15중량% 및 잔여량의 물을 포함하는 중도용 수성 페인트를 사용한 단열성 방수층 및 차열안료 0.1∼2중량%, 백색안료 20∼40중량%, 아크릴계 바인더 수지 40∼60중량%, 희석제 1∼5중량%, 첨가제 5∼15중량% 및 잔여량의 물을 포함하는 상도용 수성 페인트을 사용한 차열층으로 된 2층 구조로 차열성 방수성 도막을, 전술한 옥상 또는 지붕에 적절히 하도 처리한 후에 설치함으로써, 전술한 문제점을 해결할 수 있음을 발견하고 본 발명을 완성하였다. The inventors of the present invention, on the roof or roof directly exposed to sunlight and climate change, 0.1-2% by weight hollow pigment, 1-5% by weight white pigment, 20-40% by weight extender pigment, 40-60% by weight elastic binder resin, Insulating waterproof layer using intermediate aqueous paint containing 1 to 5% by weight of diluent, 5 to 15% by weight of additive and residual amount of water, 0.1 to 2% by weight of thermal pigment, 20 to 40% by weight of white pigment, 40 to 40% of acrylic binder resin A two-layer structure consisting of a heat shield layer using a water-based paint for coating containing 60% by weight, 1 to 5% by weight of a diluent, 5 to 15% by weight of an additive, and a residual amount of water, is suitably applied to the roof or roof as described above. The present invention was found to be able to solve the above-mentioned problems by installing after the subprocessing, and completed the present invention.

본 발명에 따른 옥상 또는 지붕용 2-코트형 수성 차열성 방수 도료는 친환경적이고 작업성이 우수하며, 이로부터 제조된 2층 구조를 갖는 차열성 방수 도막은, 일광 및 기후 변화에 직접 노출되는 환경에서도, 물성 및 내구성의 저하없이 우수한 차열성 및 단열성을 나타낼 수 있다. The 2-coat type water-based heat-resistant waterproof coating for roof or roof according to the present invention is environmentally friendly and excellent in workability, and the heat-resistant waterproof coating having a two-layer structure manufactured therefrom is directly exposed to sunlight and climate change. Also, excellent heat shielding and heat insulating properties can be exhibited without deterioration in physical properties and durability.

도 1은 본 발명에 따른 실시예 1, 참고예 1 및 비교예 1의 상도용 수성 페인트 및 중도용 수성 페인트를 도장한 다음, 광 조사 하에 시간에 따른 내부 온도의 변화를 보여주는 그래프이다.
도 2는 본 발명에 따른 실시예 1, 참고예 1 및 비교예 1의 상도용 수성 페인트 및 중도용 수성 페인트를 도장한 다음, 광 조사 하에 시간에 따른 외부 온도의 변화를 보여주는 그래프이다. 1 is a graph showing the change of the internal temperature with time under light irradiation after coating the water-based water-based paint and the water-based water paint of Example 1, Reference Example 1 and Comparative Example 1 according to the present invention.
FIG. 2 is a graph showing changes in external temperature with time under light irradiation after coating the water-based aqueous paints and the water-based paints of Example 1, Reference Example 1 and Comparative Example 1 according to the present invention.

본 발명의 첫 번째 목적은, 상도용 수성 차열 페인트 및 하도용 수성 단열 페인트로 이루어진, 옥상 또는 지붕용 2-코트형 수성 차열성 방수 도료를 제공하는 것으로, It is a first object of the present invention to provide a two-coat type water-based heat-resistant waterproof paint for a roof or roof, which is composed of a water-based water-borne insulating paint for a top coat and a water-based adiabatic paint for a bottom.

전술한 상도용 수성 차열 페인트는 차열안료 0.1∼2중량%, 백색안료 10∼30중량%, 아크릴계 바인더 수지 40∼60중량%, 희석제 1∼5중량%, 첨가제 5∼15중량% 및 잔여량의 물을 포함하고, 및The above-mentioned water-based heat shielding paint for top coat is 0.1 to 2% by weight of thermal pigment, 10 to 30% by weight of white pigment, 40 to 60% by weight of acrylic binder resin, 1 to 5% by weight of diluent, 5 to 15% by weight of additive and residual amount of water. Including, and

전술한 하도용 수성 단열 페인트는, 중공안료 0.1∼2중량%, 백색안료 1∼5중량%, 체질안료 20∼40중량%, 탄성 바인더 수지 40∼60중량%, 희석제 1∼5중량%, 첨가제 5∼15중량% 및 잔여량의 물을 포함할 수 있다. The above-mentioned water-based insulating paint for undercoat is 0.1 to 2% by weight hollow pigment, 1 to 5% by weight white pigment, 20 to 40% by weight extender pigment, 40 to 60% by weight elastic binder resin, 1 to 5% by weight diluent, additive 5-15% by weight and residual amount of water.

본 발명의 하나의 구현예에 따르면, 전술한 수성 차열 페인트의 아크릴계 바인더 수지는, 유리전이온도가 0℃ 이상, 바람직하게는 10℃ 이상, 더욱 바람직하게는 20℃ 이상인 아크릴 에멀젼 수지로부터 선택될 수 있다. 또다르게는, 전술한 수성 차열 페인트의 아크릴 에멀젼 수지는, 코어의 유리전이온도가 30℃ 이상, 바람직하게는 40℃ 이상, 더욱 바람직하게는 50℃ 이상인 내부 가교형 코어-쉘 구조를 가질 수 있다. According to one embodiment of the present invention, the acrylic binder resin of the above-described water-based thermal barrier paint may be selected from acrylic emulsion resins having a glass transition temperature of 0 ° C or higher, preferably 10 ° C or higher, more preferably 20 ° C or higher. have. Alternatively, the above-mentioned acrylic emulsion resin of the water-based thermal barrier paint may have an internally crosslinked core-shell structure in which the glass transition temperature of the core is at least 30 ° C, preferably at least 40 ° C, more preferably at least 50 ° C. .

본 발명의 다른 하나의 구현예에 따르면, 전술한 차열안료는 알루미늄 금속 분말로부터 선택되고, 전술한 중공안료는 다공성 실리카, 다공성 티타니아, 중공 실리카 및 중공 티타니아로 구성된 군에서 선택될 수 있다. According to another embodiment of the present invention, the above-mentioned heat shield pigment is selected from aluminum metal powder, the above-described hollow pigment may be selected from the group consisting of porous silica, porous titania, hollow silica and hollow titania.

본 발명의 하나의 변법에 따르면, 전술한 수성 단열 페인트는, 실란계 또는 에폭시계 가교결합제를 더욱 포함할 수 있다. According to one variant of the present invention, the above-mentioned aqueous heat insulating paint may further include a silane-based or epoxy-based crosslinking agent.

본 발명의 하나의 바람직한 구현예에 따르면, 전술한 수성 단열 페인트는, According to one preferred embodiment of the invention, the above-mentioned water-based insulating paint,

(1a) 물에 탄성 바인더 수지(예. 아크릴 에멀젼 수지) 및 첨가제(예. 증점제, 유화제, 소포제)를 첨가하여 30분 동안 교반하고, (1a) add elastic binder resin (e.g. acrylic emulsion resin) and additives (e.g. thickener, emulsifier, antifoaming agent) to water and stir for 30 minutes;

(1b) 수득된 배합물에, 중공안료, 백색안료 및 체질안료를 첨가하여 1,000∼1,500rpm으로 1시간 동안 교반하고, (1b) To the blend obtained, hollow pigments, white pigments and extender pigments were added and stirred at 1,000 to 1500 rpm for 1 hour,

(1c) 수득된 배합물에, 추가의 탄성 바인더 수지(예. 아크릴 에멀젼 수지), 첨가제(예. 희석제, 소포제, 증점제) 및 잔여량의 물을 첨가하여 1,000∼1,500rpm으로 1시간 동안 교반함으로써 제조된 것일 수 있다. (1c) To the blend obtained, additional elastic binder resins (e.g. acrylic emulsion resins), additives (e.g. diluents, antifoams, thickeners) and residual amounts of water were added and stirred for 1 hour at 1,000 to 1500 rpm. It may be.

본 발명의 하나의 바람직한 구현예에 따르면, 전술한 수성 차열 페인트는, According to one preferred embodiment of the present invention, the above-mentioned water-based thermal barrier paint,

(2a) 물에 첨가제(예. 증점제, 분산제, 유화제, 소포제 등)를 첨가하여 1,000∼1,500rpm으로 30분 동안 교반하고, (2a) add an additive (e.g. thickener, dispersant, emulsifier, antifoaming agent, etc.) to water and stir at 1,000 to 1500 rpm for 30 minutes;

(2b) 수득된 배합물에, 차열안료 및 백색안료를 첨가하여, 안료의 평균입자직경이 20㎛ 이하가 되도록 1,000∼1,500rpm으로 1시간 30분 동안 교반하고, (2b) To the obtained blend, a heat shield pigment and a white pigment were added, and the mixture was stirred at 1,000 to 1500 rpm for 1 hour and 30 minutes so that the average particle diameter of the pigment was 20 µm or less.

(2c) 수득된 배합물에, 바인더 수지(예. 아크릴 에멀젼 수지) 및 첨가제(예. 침강방지제, 희석제, 소포제, 증점제)를 첨가하여 1,000∼1,500rpm으로 1시간 30분 동안 교반함으로써 제조된 것일 수 있다. (2c) It may be prepared by adding a binder resin (e.g. acrylic emulsion resin) and additives (e.g. antisettling agent, diluent, antifoaming agent, thickener) to the obtained compound and stirring at 1,000 to 1500 rpm for 1 hour and 30 minutes. have.

본 발명의 두 번째 목적은, 전술한 수성 차열 페인트 및 수성 단열 페인트를 사용하여, 옥상 또는 지붕에 2층 구조의 차열성 방수 도막을 형성하는, 차열성 방수 도장 방법을 제공하는 것으로, 하기 단계를 포함한다: A second object of the present invention is to provide a heat-resistant waterproof coating method for forming a heat-resistant waterproof coating film having a two-layer structure on a roof or a roof using the above-described water-based heat insulating paint and water-based insulating paint. Contains:

(1) 옥상 또는 지붕의 기재층을 준비하고, 경우에 따라서는 전술한 옥상 또는 지붕의 기재층을 임의로 하도 처리 또는 방수성 코팅 처리하고, (1) A base material layer of a rooftop or a roof is prepared, and optionally a base material layer of the above-mentioned rooftop or roof is optionally undercoated or waterproof coated,

(2) 상기 옥상 또는 지붕의 기재층, 예를 들면, 중공안료 0.1∼2중량%, 백색안료 1∼5중량%, 체질안료 20∼40중량%, 탄성 바인더 수지 40∼60중량%, 희석제 1∼5중량%, 첨가제 5∼15중량% 및 잔여량의 물을 포함하는 상도용 수성 단열 페인트를 도포 및 건조하고, 이에 의해 단열 방수성 중도를 형성하고, 이어서(2) The base layer on the roof or roof, for example, 0.1-2% by weight of hollow pigment, 1-5% by weight of white pigment, 20-40% by weight of extender pigment, 40-60% by weight of elastic binder resin, diluent 1 Applying and drying a waterborne aqueous insulating paint comprising ~ 5% by weight, 5-15% by weight of additives and residual amount of water, thereby forming a heat insulating waterproofing medium, and then

(3) 상기 단열층에, 예를 들면, 차열안료 0.1∼2중량%, 백색안료 10∼30중량%, 바인더 수지 40∼60중량%, 희석제 1∼5중량%, 첨가제 5∼15중량% 및 잔여량의 물을 포함하는 상도용 수성 차열 페인트를 도포 및 건조하고, 이에 의해 차열성 상도를 형성하고, (3) In the heat insulating layer, for example, 0.1 to 2% by weight of heat shield pigment, 10 to 30% by weight of white pigment, 40 to 60% by weight of binder resin, 1 to 5% by weight of diluent, 5 to 15% by weight of additive and residual amount Applying and drying the water-based water-based barrier paint containing a water of, thereby forming a heat-shielding top coat,

(4) 경우에 따라, 투명성 자외선 보호층을 더욱 도포함. (4) In some cases, a transparent ultraviolet protective layer is further included.

본 발명의 세 번째 목적은, 전술한 수성 차열 페인트 및 수성 단열 페인트를 사용하여 형성된 2층 구조의 차열성 방수 도막, 또는 전술한 옥상 또는 지붕에 2층 구조의 차열성 방수 도막을 형성하는 방법 또는 차열성 방수 도장 방법에 의해 형성된 2층 구조의 차열성 방수 도막을 제공하는 것이다. A third object of the present invention is to provide a two-layered heat-resistant waterproof coating film formed by using the above-described water-based thermal barrier paint and an aqueous heat-insulating paint, or a method of forming a two-layer thermal barrier waterproof coating film on a roof or a roof. It is to provide a heat shielding waterproof coating film having a two-layer structure formed by the heat shielding waterproof coating method.

이하에, 본 발명을 더욱 상세히 설명한다. In the following, the present invention is described in more detail.

본 명세서에 있어서, 차열 또는 차열성은 태양광의 가시광선 및 적외선을 반사하거나 차단함으로써 온도 상승을 방지하는 것을 의미하며, 단열 또는 단열성은 열의 전도를 억제하거나 저해함으로써 온도 저하 또는 상승을 방지하는 것을 의미한다. In the present specification, heat shielding or heat shielding means preventing temperature rise by reflecting or blocking visible light and infrared rays of sunlight, and heat insulation or heat insulation means preventing temperature drop or rise by inhibiting or inhibiting conduction of heat. do.

A. 수성 차열 페인트 및 차열층A. Water-based Thermal Paints and Thermal Shields

본 발명에 있어서, 수성 차열 페인트는 차열안료, 백색안료, 아크릴계 바인더 수지, 희석제 및 기타 첨가제를 물에 용해 또는 분산된 형태로 포함할 수 있다. 예를 들면, 전술한 수성 차열 페인트는 차열안료 0.1∼2중량%, 백색안료 20∼40중량%, 아크릴계 바인더 수지 40∼60중량%, 희석제 1∼5중량%, 첨가제 5∼15중량% 및 잔여량의 물을 포함할 수 있다. In the present invention, the water-based heat shielding paint may include a heat shielding pigment, a white pigment, an acrylic binder resin, a diluent, and other additives in a dissolved or dispersed form in water. For example, the above-mentioned water-based heat shielding paint is 0.1 to 2% by weight of the thermal pigment, 20 to 40% by weight of the white pigment, 40 to 60% by weight of the acrylic binder resin, 1 to 5% by weight of the diluent, 5 to 15% by weight of the additive and residual amount. May contain water.

전술한 수성 차열 페인트는 하기 단계를 포함하는 방법으로 제조될 수 있다:The aforementioned waterborne paint can be prepared by a method comprising the following steps:

(1a) 물에 첨가제(증점제, 분산제, 유화제, 소포제 등)를 첨가하여 1,000∼1,500rpm으로 30분 동안 교반하고, (1a) Add an additive (a thickener, a dispersant, an emulsifier, an antifoaming agent, etc.) to water, stir at 1,000 to 1500 rpm for 30 minutes,

(1b) 수득된 배합물에, 차열안료 및 백색안료를 첨가하여, 안료의 평균입자직경이 20㎛ 이하가 되도록 1,000∼1,500rpm으로 1시간 30분 동안 교반하고, (1b) To the obtained compound, a heat shield pigment and a white pigment were added, and the mixture was stirred at 1,000 to 1500 rpm for 1 hour and 30 minutes so that the average particle diameter of the pigment was 20 µm or less.

(1c) 수득된 배합물에, 바인더로서 아크릴 에멀젼 수지 및 첨가제(침강방지제, 희석제, 소포제, 증점제 등)를 첨가하여 1,000∼1,500rpm으로 1시간 30분 동안 교반함.(1c) To the blend obtained, an acrylic emulsion resin and additives (precipitating agent, diluent, antifoaming agent, thickener, etc.) were added as a binder and stirred at 1,000 to 1500 rpm for 1 hour and 30 minutes.

(A-1) 아크릴계 바인더 수지(A-1) acrylic binder resin

본 발명에 따른 수성 차열 페인트에 있어서, 전술한 아크릴계 바인더 수지는, 유리전이온도가 10℃ 이상, 바람직하게는 20℃ 이상, 더욱 바람직하게는 30℃ 이상인 아크릴 에멀젼 수지로부터 선택될 수 있으며, 바람직하게는, 코어의 유리전이온도가 30℃ 이상, 바람직하게는 40℃ 이상, 더욱 바람직하게는 50℃ 이상인 내부 가교형 코어-쉘 구조를 갖는 아크릴 에멀젼 수지로부터 선택될 수 있다. In the water-based thermal barrier paint according to the present invention, the above-described acrylic binder resin may be selected from acrylic emulsion resin having a glass transition temperature of 10 ° C or higher, preferably 20 ° C or higher, more preferably 30 ° C or higher. May be selected from acrylic emulsion resins having an internally crosslinked core-shell structure in which the glass transition temperature of the core is at least 30 ° C, preferably at least 40 ° C, more preferably at least 50 ° C.

본 발명에서 사용할 수 있는 아크릴 에멀젼 수지로는, 비제한적인 예로서, 메틸 메타아크릴레이트, 메타아크릴릭 산, 부틸 메타아크릴레이트, 하이드록시프로필 메타크릴레이트, 에틸렌 글리콜 디메타아크릴레이트, 부칠렌글리콜 트리 메타아크릴레이트, 폴리에틸렌 글리콜 트리 메타아크릴레이트, 펜타아크릴디올 트리메타아크릴레이트, 알킬 메타아크릴레이트, 사이클로알킬 메타아크릴레이트, 에틸 메타아크릴레이트, 이소부틸 메타아크릴레이트, t-부틸 메타아크릴레이트, 트리에틸프로판트리 메타아크레이트, 트리메틸올프로판트리 메타아크레이트, 2-히드록시에틸메타크릴에이트, 2-히드록시프로필메타아크릴레이트, 4-히드록시부틸아크릴레이트, 2-히드록시에틸아크릴레이트, 2-히드록시프로필아크릴레이트, 4-히드록시부틸 메타크릴레이트 등과 같은 아크릴 모노머의 공중합체 군 중에서 하나 이상 선택될 수 있다. Examples of the acrylic emulsion resin that can be used in the present invention include, but are not limited to, methyl methacrylate, methacrylic acid, butyl methacrylate, hydroxypropyl methacrylate, ethylene glycol dimethacrylate, butylene glycol tri Methacrylate, polyethylene glycol tri methacrylate, pentaacryldiol trimethacrylate, alkyl methacrylate, cycloalkyl methacrylate, ethyl methacrylate, isobutyl methacrylate, t-butyl methacrylate, triethyl Propane tree methacrylate, trimethylolpropane tree methacrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl methacrylate, 4-hydroxybutyl acrylate, 2-hydroxyethyl acrylate, 2- Hydroxypropyl acrylate, 4-hydroxybutyl methacrylate And it may be selected one or more of the group of copolymers of acrylic monomers.

전술한 아크릴 에멀젼 수지의 유리전이온도(Tg)가 지나치게 낮으면, 도막의 경도 및 부착성, 오염성, 점착성, 내마모성, 건조시간이 떨어지고, 유리전이온도(Tg)가 지나치게 높으면, 도막의 경도, 크랙, 유연성(신축성) 등이 떨어지기 때문에, 유리전이 온도(Tg)가 10∼50℃이고 내후성, 내오염성, 내수성이 우수한 수지를 사용하는 것이 바람직한데, 상기 범위 내의 아크릴 에멀젼 수지를 사용함으로써 도막의 경도 및 내구성, 부착성, 유연성(신축성)이 적절해진다.If the glass transition temperature (Tg) of the acrylic emulsion resin described above is too low, the hardness and adhesion of the coating film, contamination, adhesion, abrasion resistance, drying time is lowered, and if the glass transition temperature (Tg) is too high, the hardness, cracks of the coating film Since the flexibility (elasticity) and the like are inferior, it is preferable to use a resin having a glass transition temperature (Tg) of 10 to 50 ° C. and excellent in weather resistance, stain resistance and water resistance. Hardness and durability, adhesion, flexibility (stretchability) are appropriate.

(A-2) 차열안료 및 백색안료(A-2) Thermal Pigment and White Pigment

본 발명에 따른 수성 차열 페인트에 있어서, 차열안료는 태양열의 적외선 반사 특성을 가지고 있는 안료를 의미할 수 있으며, 일반적으로 알루미늄과 같은 금속 분말의 뛰어난 광산란력을 응용하고, 태양광선 중에서도 특히 열에너지에 변환되기 쉬운 적외선을 반사하는 기능을 가지고 있는 차열안료인 것을 특징으로 한다.In the water-based heat shielding paint according to the present invention, the heat shield pigment may mean a pigment having infrared reflecting properties of solar heat, and generally applies an excellent light scattering force of a metal powder such as aluminum, and converts it into thermal energy, especially in sunlight. It is characterized in that it is a heat shield pigment having a function of reflecting infrared rays that tend to be.

또다르게는, 본 발명에서 사용할 수 있는 차열안료로는, 비제한적인 예로서, 태양열의 적외선 반사 특성을 가지고 있는 안료인 무기계 차열안료(크롬계, 비크롬계), 유기계 차열안료(아조메틴-아조계, 페릴렌계),　감색 혼합 안료 단색계 등을 언급할 수 있다. In addition, as the heat shielding pigment which can be used in the present invention, non-limiting examples include inorganic heat shielding pigments (chromium-based, non-chromium-based), organic heat shielding pigments (azomethine-) which are pigments having infrared heat reflection characteristics of solar heat. Azo, perylene-based), navy blue mixed pigment monochromatic, and the like can be mentioned.

본 발명에 있어서, 백색안료는 산화티탄 등의 금속산화물의 미세 입자로부터 선택되며, 뛰어난 광산란력을 가지고 있으면서, 태양광선 중에서도 특히 열에너지에 변환되기 쉬운 적외선을 반사하는 기능을 가지고 있고, 근적외선 영역의 파장 광선을 반사, 투과하는 열량을 감소시킬 수 있어, 코팅의 백색도를 향상시키는 역할 뿐만 아니라, 차열안료와 함께 차열능을 향상시키는 역할을 한다. In the present invention, the white pigment is selected from fine particles of metal oxides such as titanium oxide, has excellent light scattering power, and has a function of reflecting infrared rays, especially in sunlight, which are easily converted to thermal energy, and having a wavelength in the near infrared region. The amount of heat that reflects and transmits the light can be reduced, so as to improve the whiteness of the coating as well as the heat shielding ability.

본 발명에 있어서, 전술한 차열안료 및 백색안료는, 일반 반사율 및 장파반사율이 높은 차열안료 및 백색안료를 실험적으로 사용하여, 적정 사용량을 얻음으로써 우수한 물성을 얻을 수 있다.In the present invention, the above-mentioned heat shield pigments and white pigments can be obtained experimentally by using heat shield pigments and white pigments having high general reflectance and long wave reflectance, and by obtaining an appropriate amount of use, excellent physical properties can be obtained.

본 발명의 하나의 바람직한 변법에 따르면, 상기 차열안료는 열반사율이 우수한 안료로서 중공 글라스 버블 및 착색을 겸한 차열안료로 나뉘는데, 상기 중공 글라스 버블은 근적외선의 파장영역인 300 ∼ 2,500 nm 파장을 90% 이상 반사하고, 건조 후 도막 상단에 세라믹 거품을 생성하여 열에너지를 장파 전자파로 방사함으로써 열에너지를 차단시키며, 차열안료는 지르코늄 및 알루미늄의 화합물로 전처리된 유색안료로서 일사반사율 및 장파반사율이 높아 차열효과를 극대화할 수 있다. 하지만, 중공 글라스 버블은 안료내부에 공기층이 형성되어 있어 상도재에 적용시 굴곡성 및 광택이 저하되는 단점이 있다. According to one preferred variant of the present invention, the heat shield pigment is a pigment having excellent heat reflectivity and is divided into a heat shield pigment that also serves as a hollow glass bubble and coloring, the hollow glass bubble is a wavelength region of the near infrared 300 ~ 2,500 nm 90% It reflects abnormally and forms ceramic foam on top of the coating film after drying to block the heat energy by radiating the heat energy with long wave electromagnetic waves.The heat shield pigment is a colored pigment pretreated with a compound of zirconium and aluminum, and has high solar reflectance and long wave reflectance. It can be maximized. However, the hollow glass bubble has a disadvantage in that the air layer is formed in the pigment, and thus the flexibility and gloss of the hollow glass bubble are reduced when applied to the top coat.

본 발명에 있어, 고광택의 우수한 차열효과를 나타내는 유색 차열안료(Tipaque CR-97-(주)이시하라 또는 Daipytroxide Brown 9290-(주)대일정화공업)를 사용할 수도 있다. In the present invention, a colored heat shield pigment (Tipaque CR-97-Ishihara Co., Ltd. or Daipytroxide Brown 9290-Daeil Chemical Co., Ltd.) exhibiting excellent heat shielding effect with high gloss can also be used.

본 발명에 있어, 차열안료 및 백색안료의 사용량 및 사용비율은 특별히 한정되지 않으나, 전술한 수성 차열 페인트를 기준으로, 차열안료 0.1∼2중량% 및 백색안료 10∼30중량%의 양으로 사용할 수 있다. In the present invention, the amount and ratio of use of the heat shield pigment and the white pigment are not particularly limited, but the amount of the heat shield pigment and the white pigment may be used in an amount of 0.1 to 2% by weight and 10 to 30% by weight of the white pigment. have.

(A-3) 첨가제(A-3) additive

본 발명에 따른 수성 차열 페인트에 있어서, 희석제, 소포제, 유화제, 표면조절용 첨가제, 분산제, 무기안료(유색안료), 부착 증진제, 증점제, 동결방지제, 자외선 안정제, 방부제, 도막형성제, 방충제, 항균제, 산도 조절제 등을 적절히 함유할 수 있다. In the water-based thermal barrier paint according to the present invention, a diluent, an antifoaming agent, an emulsifier, an additive for controlling the surface, a dispersant, an inorganic pigment (colored pigment), an adhesion promoter, a thickener, a cryoprotectant, an ultraviolet stabilizer, a preservative, a film forming agent, an insect repellent, an antibacterial agent, An acidity regulator etc. can be contained suitably.

상기 각 첨가제는 전체 도료 조성물 총중량을 기준으로, 희석제 1∼5 중량%, 소포제 0.1∼0.5 중량%, 유화제 0.1∼0.5 중량%, 표면 조절용 첨가제 0.1∼0.5 중량%, 분산제 0.5∼1 중량%, 무기안료(유색안료) 5∼10 중량%, 부착 증진제 0.1∼0.5 중량%, 증점제 0.1∼0.5 중량%, 동결방지제 1.∼1.5중량%, 자외선 안정제 0.1∼0.5 중량%, 방부제 0.1∼0.5 중량%, 도막형성제 1∼2 중량%, 방충제 0.1∼0.5 중량%, 항균제 0.1∼0.5중량%, 산도 조절제 0.1∼0.5%중량의 범위 내로 함유되는 것이 바람직하나, 필요에 따라 가감할 수 있다.Each of the additives, based on the total weight of the total coating composition, 1 to 5% by weight of the diluent, 0.1 to 0.5% by weight of the antifoaming agent, 0.1 to 0.5% by weight of the emulsifier, 0.1 to 0.5% by weight of the surface control additive, 0.5 to 1% by weight of the dispersant, inorganic Pigments (colored pigments) 5-10% by weight, adhesion promoter 0.1-0.5% by weight, thickener 0.1-0.5% by weight, cryoprotectant 1.-1.5% by weight, UV stabilizer 0.1-0.5% by weight, preservative 0.1-0.5% by weight, It is preferably contained in the range of 1 to 2% by weight of the film-forming agent, 0.1 to 0.5% by weight of the insect repellent, 0.1 to 0.5% by weight of the antibacterial agent, and 0.1 to 0.5% by weight of the acidity regulator, but may be added or subtracted as necessary.

희석제는, 일반적으로 수성 도료에서는 물을 의미하나, 본 발명에서는 바인더와 결합하거나 결합하지 않고 수성 도료의 농도 및/또는 점도를 조절하기 위해 첨가되는 성분을 의미한다. 이러한 희석제로는, 글리콜에테르, 에스테르 알콜, 테르펜, 또는 텍사놀(Texanol : 2,2,4-트리메틸-1,3-펜탄디올 모노이소부티레이트), 또는 이들의 혼합물이 사용될 수 있다. Diluent generally refers to water in an aqueous paint, but in the present invention means a component added to adjust the concentration and / or viscosity of the aqueous paint, with or without binding to a binder. As such diluent, glycol ether, ester alcohol, terpene, or texanol (2,2,4-trimethyl-1,3-pentanediol monoisobutyrate), or a mixture thereof can be used.

예를들면, 글리콜에테르로는 부틸 Carbitolㄾ(디에틸렌 글리콜 모노부틸 에테르); 디부틸 Carbitolㄾ(디에틸렌 글리콜 디부틸 에테르), 부틸 Carbitolㄾ 아세테이트(디에틸렌 글리콜 모노부틸 에테르 아세테이트)이 사용될 수 있고, 테르펜은 알파- 또는 베타-테르피네올이 단독 또는 혼합되어 사용될 수 있다. For example, glycol ethers include butyl Carbitol® (diethylene glycol monobutyl ether); Dibutyl Carbitol '(diethylene glycol dibutyl ether), butyl Carbitol' acetate (diethylene glycol monobutyl ether acetate) may be used, and terpenes may be used alone or in combination with alpha- or beta-terpineol.

희석제는 사용되는 다른 성분의 종류와 양, 그리고 작업조건에 따라 사용량을 조절할 수 있으나, 대체적으로 바인더 100중량부에 대해서 10 내지 200중량부로 포함되는 것이 바람직하다. 희석제가 200중량부를 초과하여 포함되면 점도와 틱소성(thixotropic)이 떨어지고 부착력이 저하되는 문제가 있고, 희석제가 10중량부 미만으로 포함되면 점도와 틱소성(thixotropic)이 높아져서 도포성이나 작업성이 저하되는 문제점이 있다. The diluent may be used according to the type and amount of the other components used, and the working conditions, but is generally included in 10 to 200 parts by weight based on 100 parts by weight of the binder. If the diluent is contained in an amount exceeding 200 parts by weight, the viscosity and thixotropic properties are lowered and the adhesion is lowered. If the diluent is included in an amount less than 10 parts by weight, the viscosity and thixotropic properties are increased, resulting in applicability or workability. There is a problem of deterioration.

소포제는 도료 도장 후 도막 형성시에 발생하는 기포의 형성을 억제하거나 발생한 기포를 제거하는 첨가제로서, 도료의 제조시나 작업시 도료 내에 있는 기포를 제거함으로써 도막 건조시 도막의 외관을 양호하게 하는데, 소포제를 사용하지 않으면 도막에 기포가 발생하고 반대로 과량을 사용하면 분화구 현상이 나타나는 등 도막의 외관이 불량해진다. 본 발명에 있어서, 수성 실리콘계 소포제를 바람직하게 사용할 수 있다. Antifoaming agent is an additive that suppresses the formation of air bubbles or removes air bubbles generated during paint film formation after paint coating, and improves the appearance of coating film during coating film drying by removing air bubbles in paint during manufacturing or operation of paint. If it is not used, bubbles are generated in the coating film. On the contrary, when an excessive amount is used, the appearance of the coating film is poor, such as a crater phenomenon. In the present invention, an aqueous silicone antifoaming agent can be preferably used.

유화제는 하나의 계에 유상과 수상이 있을 경우 그것을 서로 혼합하지 않으면 2상간의 계면이 생기는데, 계면활성제를 첨가하면 활성제의 극성기는 물에 녹고 비극성기는 유상에 용해하게 배합하여 수상과 유상간의 가교작용을 하므로, 이를 위해 유화제가 사용되며, 유화제를 사용하지 않을 경우 도료의 층 분리 및 도막 형성시 문제가 생길 수 있다. Emulsifier if the oil and water in a single system is kind that do not mix the two-phase interface between each other, the addition of surfactant polar groups of the surfactant is cross-linked between the water phase and oil phase and a non-polar soluble in water group is dissolved formulated in oil acting Therefore, an emulsifier is used for this purpose, and when the emulsifier is not used, problems may occur in layer separation and coating film formation of the paint.

표면조절용 첨가제로서, 수성 실리콘계 표면조절용 첨가제는 작업시 도막의 면을 평활하게 해주어 도막 건조시 도막의 외관을 양호하게 하며, 도막이 형성되는 동안 불충분한 습윤, 불량한 습윤성, 크래터링 형성, 안료의 색분리 등과 같은 문제를 개선시키는 역할을 한다. As a surface control additive , an aqueous silicone surface control additive smoothes the surface of the coating during operation to improve the appearance of the coating upon drying the coating, insufficient wetting, poor wettability, formation of cratering, and color separation of the pigment during the formation of the coating. To improve problems such as

분산제는 유색도료의 제조공정에서 액상 수지에 고체 안료를 균일하게 분산시켜 연화성능의 향상 및 안료의 재응집을 방지시키는 첨가제이다. 이러한 분산제는, 분산제는 도료 내에서 안료 및 체질안료의 분산을 향상 시켜줌으로서 도막의 시각적 효과 및 은폐력이 좌우되며 도료의 제조시나 저장 및 도장시에도 중요한 역할을 하는데, 분산제는 수성 도료용 습윤 분산제로 유기 무기 안료용 분산제를 사용하는 것이 바람직하다. Dispersant is an additive that uniformly disperses the solid pigment in the liquid resin in the manufacturing process of the color paint to improve the softening performance and prevent re-agglomeration of the pigment. This dispersant improves the dispersion of pigments and extender pigments in the paint, which influences the visual effect and hiding power of the coating and plays an important role in the manufacture of the paint, storage and painting. The dispersant is a wet dispersant for water-based paints. Preference is given to using dispersants for organic inorganic pigments.

무기안료(유색 안료)는 사용하여 도료의 색상을 구현할 수 있거나, 도료의 착색과 은폐력의 부여 등에 효과를 달성할 수 있다. 유색 안료로서, 당업계에 통상적으로 사용되는 무기안료 중에서 하나 이상 선택될 수 있다. 또한 이러한 무기안료(유색 안료)는 특히 내구력이 좋을 것을 요구하는데. 도료 등에서 내구력 특히, 내광성, 내산성 등이 나쁘면 도료의 색은 수십일 내에 변색이 오기도한다. 최근에는 대기 오염으로 공기는 산성 물질로 오염되고 빗물에 섞여 산성물이 되어 도막을 적시면 내산성이 약한 안료는 변색이 일어난다. 이러한 점을 고려하여 내구성이 좋은 안료를 선택하여 좋은 물성을 얻을 수 있다. Inorganic pigments (colored pigments) can be used to implement the color of the paint, or can achieve effects such as coloring and imparting hiding power of the paint. As the colored pigment, at least one of inorganic pigments commonly used in the art may be selected. In addition, these inorganic pigments (colored pigments) require particularly good durability. If the paint has a poor durability, particularly light resistance and acid resistance, the color of the paint may be discolored within a few days. Recently, due to air pollution, the air is contaminated with acidic substances, mixed with rainwater to become acidic and wet the coating film, discoloration of the weak acid resistance pigment. In consideration of this, it is possible to obtain a good physical property by selecting a pigment with good durability.

레벨링제는 도막 형성시의 대류현상 또는 표면장력의 차이 등에 의해 발생하는 도막 표면의 결함을 방지하는 첨가제이다. The leveling agent is an additive that prevents defects on the surface of the coating film caused by convection or difference in surface tension during coating film formation.

침강방지제는 도료 중의 안료가 침강하여 용기바닥에서 케이크(cake)상을 형성하는 것을 방지하는 첨가제이다. The sedimentation inhibitor is an additive which prevents the pigment in the paint from sedimenting to form a cake on the bottom of the container.

부착 증진제는 도막 건조시 소지와 도막간의 부착력을 증대시키는 역할을 하며 인산-아크릴계 및 숙시네이트 에스터계 , 아크릴레이티이드 폴리에스테르 올리고머, 감마-메타아크릴로옥사프로필트리메톡시실란, 트리스-오메가-메톡시에톡시 실란등이 사용되나 아크릴레이티이드 폴리에스테르 올리고머를 사용하는 것이 바람직하다. Adhesion promoters serve to increase the adhesion between the base and the coating when the coating is dried. Phosphoric acid-acrylic and succinate esters, acrylated polyester oligomers, gamma-methacryloxapropyltrimethoxysilane, tris-omega- Although methoxyethoxy silane etc. are used, it is preferable to use an acrylate polyester oligomer.

증점제는 점도조절, 증점 및 칙소성 부여 및 입자의 침강방지 및 재분산성 개선 및 흐름성 개선과 입자의 저장안정성 개선에 사용되어 도료의 물성 및 저장성 등에 효과가 있다. Thickeners are used to control viscosity, thicken and thixotropic, prevent sedimentation and re-dispersibility of particles, improve flowability, and improve the storage stability of particles.

동결 방지제는 수성 도료에서 사용하는 첨가제로서 수성 도료는 물을 대량 함유 하므로 저온에서 오랬동안 방치하면 동결현상이 발생하여 아크릴 에멀젼이 파괴 되는데 동결되어도 온도가 점차 올라가면서 복원하는 것이 바람직하므로 동결 방지를 목적으로 사용하며, 도료의 냉동안정성을 위한 첨가제로서 에틸렌 글리콜 프로필렌 글리콜 등의 글리콜류 중에서 하나 이상 선택될 수 있는데, 동결 방지제를 첨가하지 않을 경우 도료가 동결되어 도료의 제 기능을 잃게 된다. The cryoprotectant is an additive used in water-based paints. Since water-based paints contain a large amount of water, if left for a long time at low temperatures, freezing may occur and the acrylic emulsion will be destroyed. As an additive for freezing stability of the paint, one or more glycols such as ethylene glycol, propylene glycol, and the like may be selected. If the antifreeze agent is not added, the paint is frozen and loses its proper function.

자외선 안정제는 도막의 건조시나 건조후 자외선 및 공기와의 접촉에 의한 도막의 색이 바래는 현상을 막아주는 데 자외선 안정제는 장기적으로 색이 바래는 현상과 노랗게 변화는 것을 조절하는데 가장 우수하여 자외선 및 공기에 의한 도막의 내후성 측면에서 좋은 물성을 얻을 수 있다. 또한 자외선 안정제는 작용기능별로 자외선 흡수제, 자외선 차단제 등으로 나누어지며 벤조트리아조계, 벤조페논계, 트리아진계, 오가노니켈계 및 자외선 차단제,자외선 흡수제 중에서 하나 이상 선택하는 것을 특징으로 한다. UV stabilizer prevents the color fading of the coating due to contact with UV and air after drying or drying. The UV stabilizer is the best for controlling color fading and yellowing in the long term. Good physical properties can be obtained in terms of weather resistance of the coating film by air. In addition, the UV stabilizer is divided into UV absorbers, sunscreens, etc., by function, characterized in that at least one selected from benzotriazoles, benzophenones, triazines, organonickel and sunscreens, ultraviolet absorbers.

도막형성제는 도료의 도막 형성, 도료 물성, 오염성, 점착성등에 중요한 물질이며 수성 도막 형성 조제 중에서 하나 이상 선택될 수 있으며, 아크릴 에멀전의 유리전이온도와 MFFT(최저도막형성온도)에 따라서 도료의 물성이 달라지므로 실험적인 적정 사용양을 사용하는 것이 바람직하다. The film forming agent is an important material for coating film formation, paint properties, contaminants, and adhesion of the paint, and may be selected from one or more of aqueous coating film forming aids, and according to the glass transition temperature and the MFFT (lowest film forming temperature) of the acrylic emulsion. Since this is different, it is preferable to use an experimental use amount appropriately.

방부제는 미생물(세균, 박테리아)의 작용에 의해 도료의 용기 속에서 부패되거나 도막의 붕괴를 막아주는 역할을 하며 부패하는 것을 막고 장기적인 보존을 목적으로 방부하기 위해서 첨가하는 첨가제로서 사용하지 않을 경우 도료의 부패 및 냄새 등으로 인해 도료의 제 기능을 잃게 된다. Preservatives act to prevent decay in coating containers or collapse of coatings due to the action of microorganisms (bacteria, bacteria). They are additives added to prevent decay and preservation for long-term preservation. Due to decay and smell, the paint loses its proper function.

방충제 및 항균제는 내 곰팡이성, 내 박테리아성 및 방충성을 목적으로 하는 첨가제로서 도료의 보관 및 도막 형성후 장기적인 물성에 영향을 미친다. Insect repellents and antibacterial agents are additives aimed at mold resistance, bacterial resistance and insect repellency , which affect the long-term physical properties of the paint after storage and film formation.

산도 조절제는 도료 내에서 음이온이나 양이온 활성제는 각각 어느 일정한 pH 범위 내에서 안정하며 그범위 외에서는 불안정 하다. 에멀젼 도료에 있어서도 안정한 pH 범위가 있다. 도료의 점도는 pH의 영향을 받고 비히클이나 보호 콜로이드의 가수분해나 박테리아 번식을 막는 효과가 있다. 주로 휘발성의 염산이나 암모니아를 사용하며, 완충제로서 중탄소염류, 인산염류 등이 있다. 또한 수용성 수지 도료에 있어서도 카르본산기 혹은 슬폰산기 등으로 중화해서 수용화하는데 그 중화제로서는 암모니아, 유기아민류(3급 아민,알코올 아민류) 등이 있는데 산도 조절제를 사용함으로써 도료의 안정적인 고유의 물성을 얻을 수 있다. Acidity regulators are stable in paints and anionic or cationic activators within a certain pH range, respectively. There is also a stable pH range in emulsion paints. The viscosity of the paint is affected by pH and has the effect of preventing hydrolysis of the vehicle or protective colloid or bacterial propagation. Mainly volatile hydrochloric acid or ammonia is used, and there are medium carbon salts and phosphates as buffers. In addition, the water-soluble resin paint is neutralized with a carboxylic acid group or a sulfonic acid group and solubilized. The neutralizing agents include ammonia and organic amines (tertiary amines and alcohol amines). By using an acidity regulator, stable inherent properties of the paint can be obtained. Can be.

B. 수성 단열 페인트 및 단열층B. Water-based Insulation Paint and Insulation Layer

본 발명에 있어서, 수성 단열 페인트는, 중공안료, 백색안료, 체질안료, 탄성 바인더 수지, 희석제 및 기타 첨가제를 물에 용해 또는 분산시킨 형태로 포함할 수 있다. 예를 들면, 전술한 수성 단열 페인트는, 중공안료 0.1∼2중량%, 백색안료 1∼5중량%, 체질안료 20∼40중량%, 탄성 바인더 수지 40∼60중량%, 희석제 1∼5중량%, 첨가제 5∼15중량% 및 잔여량의 물을 포함할 수 있다. In the present invention, the water-based insulating paint may include hollow pigments, white pigments, extender pigments, elastic binder resins, diluents and other additives in the form of dissolved or dispersed in water. For example, the above-mentioned aqueous heat-insulating paint is 0.1-2 weight% of hollow pigment, 1-5 weight% of white pigment, 20-40 weight% of extender pigment, 40-60 weight% of elastic binder resin, and 1-5 weight% of diluent. 5-15% by weight of additives and residual amount of water.

전술한 수성 단열 페인트는 하기 단계를 포함하는 방법으로 제조될 수 있다:The aforementioned waterborne insulating paint can be prepared by a method comprising the following steps:

(2a) 물에 탄성 바인더 수지(예. 아크릴 에멀젼 수지) 및 첨가제(예. 증점제, 유화제, 소포제)를 첨가하여 30분 동안 교반하고, (2a) add elastic binder resin (e.g. acrylic emulsion resin) and additives (e.g. thickener, emulsifier, antifoaming agent) to water and stir for 30 minutes;

(2b) 수득된 배합물에, 중공안료, 백색안료 및 체질안료를 첨가하여 1,000∼1,500rpm으로 1시간 동안 교반하고, (2b) To the blend obtained, hollow pigments, white pigments and extender pigments were added and stirred at 1,000 to 1500 rpm for 1 hour,

(2c) 수득된 배합물에, 추가의 탄성 바인더 수지(예. 아크릴 에멀젼 수지), 첨가제(예. 희석제, 소포제, 증점제) 및 잔여량의 물을 첨가하여 1,000∼1,500rpm으로 1시간 동안 교반함으로써 제조된 것일 수 있다. (2c) To the blend obtained, additional elastic binder resins (e.g. acrylic emulsion resins), additives (e.g. diluents, antifoams, thickeners) and residual amounts of water were added to stir at 1,000 to 1500 rpm for 1 hour. It may be.

(B-1) 탄성 바인더 수지(B-1) Elastic Binder Resin

또한, 전술한 수성 단열 페인트의 탄성 바인더 수지는 아크릴 에멀젼 수지로부터 선택될 수 있고, 이의 비제한적인 예로서, 메틸 메타아크릴레이트, 메타아크릴릭 산, 부틸 메타아크릴레이트, 하이드록시프로필 메타크릴레이트, 에틸렌 글리콜 디메타아크릴레이트, 부칠렌글리콜 트리 메타아크릴레이트, 폴리에틸렌 글리콜 트리 메타아크릴레이트, 펜타아크릴디올 트리메타아크릴레이트, 알킬 메타아크릴레이트, 사이클로알킬 메타아크릴레이트, 에틸 메타아크릴레이트, 이소부틸 메타아크릴레이트, t-부틸 메타아크릴레이트, 트리에틸프로판트리 메타아크레이트, 트리메틸올프로판트리 메타아크레이트, 2-히드록시에틸메타크릴에이트, 2-히드록시프로필메타아크릴레이트, 4-히드록시부틸아크릴레이트, 2-히드록시에틸아크릴레이트, 2-히드록시프로필아크릴레이트, 4-히드록시부틸 메타크릴레이트 등과 같은 아크릴 모노머의 공중합체 군 중에서 하나 이상 선택될 수 있다.In addition, the above-mentioned elastic binder resin of the aqueous insulating paint may be selected from acrylic emulsion resins, and by way of non-limiting example, methyl methacrylate, methacrylic acid, butyl methacrylate, hydroxypropyl methacrylate, ethylene Glycol Dimethacrylate, Butylene Glycol Trimethacrylate, Polyethylene Glycol Trimethacrylate, Pentaacryldiol Trimethacrylate, Alkyl Methacrylate, Cycloalkyl Methacrylate, Ethyl Methacrylate, Isobutyl Methacrylate , t-butyl methacrylate, triethyl propane tri methacrylate, trimethylolpropane tri methacrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl methacrylate, 4-hydroxybutyl acrylate, 2-hydroxyethyl acrylate, 2-hydroxyprop Among acrylate, 4-hydroxybutyl group meth copolymers of acrylic monomers such as methacrylate may be selected or more than one.

본 발명에 있어서, 전술한 수성 아크릴 에멀젼 수지는 방수성 및 탄성 특성을 가지고 있는 것이 바람직할 수 있으며, 이를 위해, 가교성 결합기를 갖는 단량체, 올리고머 및/또는 중합체를 더욱 포함할 수 있다. In the present invention, the above-mentioned aqueous acrylic emulsion resin may preferably have waterproof and elastic properties, and for this purpose, may further include monomers, oligomers and / or polymers having a crosslinkable linking group.

(B-2) 중공안료, 백색안료 및 체질안료(B-2) Hollow pigments, white pigments and extender pigments

본 발명에 있어서, 중공안료는 공동형 충진제로서 입자가 독립기포를 가지고 있는 세라믹 구형 분말로서 비중이 가볍고 우수한 강도를 가지는 중공안료인 것을 특징으로 한다. 중공안료로서, 다공성 구조를 갖는 실리카, 티타니아 또는 지르코니아 등의 무기 산화물을 사용할 수 있으며, 바람직하게는, 실리카, 티타니아 또는 지르코니아 등의 무기 산화물로 된 껍질과 공기로 가득찬 내부구조로 되어 있고 입자가 독립기포를 가지고 있는 세라믹 구형 분말로서 미크론(㎛) 크기로부터 밀리미터(mm) 크기까지 넓은 범위의 종류가 있으나 입자 내부의 많은 공극들을 가지고 있으며 열전도율이 낮고 열에너지를 차단시키며 비중이 가볍고 우수한 강도를 가지는 중공안료를 사용할 수 있다. In the present invention, the hollow pigment is a hollow spherical pigment having a light weight and excellent strength as a ceramic spherical powder having particles having independent bubbles as a cavity filler. As the hollow pigment, an inorganic oxide such as silica, titania or zirconia having a porous structure can be used. Preferably, the hollow pigment has an inner structure filled with shells and air filled with inorganic oxides such as silica, titania or zirconia, and the particles Ceramic spherical powder with independent bubbles, which ranges from micron (μm) to millimeter (mm) in size, but has many pores inside the particle, has low thermal conductivity, blocks heat energy, has a specific gravity, and has excellent strength. Pigments may be used.

중공안료를 많이 사용하게 되면 점도조정 및 광택 저하의 문제점이 있고 적게 쓰게 되면 고유의 물성을 얻지 못하는 단점도 있다. 실험적으로 적정 사용량을 얻음으로써 우수한 물성을 얻을 수 있다.If the hollow pigments are used a lot, there are problems of viscosity adjustment and gloss deterioration. Excellent physical properties can be obtained by experimentally obtaining the proper amount of use.

본 발명에 있어, 백색안료는 전술한 (A-2) 차열안료 및 백색안료에서 사용된 것과 동일한 것들을 사용할 수 있다. In the present invention, white pigments may be the same as those used in the above-mentioned (A-2) heat shield pigments and white pigments.

본 발명에 있어서, 체질안료로는, 충전물의 혼합물 및 탄산칼슘, 활석, 규사, 마이카, 카오린 등과 같은 체질 안료 중에서 하나 이상 선택될 수 있으며, 탄산칼슘, 활석, 규사, 마이카, 카오린 등과 같은 체질 안료는 도료의 유동성, 점도 등 물성의 조절 및 도막의 강도, 내구성, 광택 조절 등에 효과가 있어 바람직하게 사용될 수 있다.In the present invention, the extender pigment may be selected from at least one of a mixture of the filler and a sieving pigment such as calcium carbonate, talc, silica, mica, kaolin and the like, and a sieving pigment such as calcium carbonate, talc, silica, mica, kaolin and the like. Is effective in controlling physical properties such as fluidity and viscosity of the paint and controlling strength, durability, glossiness of the coating film, and the like.

본 발명의 하나의 변법에 따르면, 경우에 따라서는, 전술한 바와 같은 무기안료(유색 안료)를 추가로 사용할 수 있다. According to one variant of the present invention, in some cases, the above-described inorganic pigments (colored pigments) can be further used.

(B-3) 첨가제(B-3) additive

본 발명에 따른 수성 단열 페인트에 있어서도, 첨가제로서, 소포제, 유화제, 표면조절용 첨가제, 분산제, 무기안료(유색안료), 체질안료, 부착 증진제, 증점제, 동결방지제, 자외선 안정제, 방부제, 도막형성제, 방충제, 항균제, PH 조절제 등을 적절히 함유할 수 있다. 이들의 종류, 용도, 함량은, (A-3) 첨가제에서 설명한 바와 같다. Also in the water-based insulating paint according to the present invention, as an additive, antifoaming agents, emulsifiers, surface control additives, dispersants, inorganic pigments (colored pigments), sieving pigments, adhesion promoters, thickeners, cryoprotectants, ultraviolet stabilizers, preservatives, coating film forming agent, Insect repellent, an antibacterial agent, PH regulator, etc. can be contained suitably. These kinds, uses, and contents are as described in the additive (A-3).

C. 2층 구조의 차열성 방수 도막 및 이의 형성 방법C. Heat shielding waterproof coating film of two-layer structure and its formation method

본 발명에 있어서, 차열층 및 단열층으로 된 2층 구조의 차열성 방수 도막은, 전술한 수성 차열 페인트 및 수성 단열 페인트를, 지붕이나 옥상용 기재층 또는 하도층에 도포함으로써 형성될 수 있다. In the present invention, the heat-shielding waterproof coating film having a heat shielding layer and a heat insulating layer can be formed by applying the above-mentioned water-based heat shielding paint and water-based heat insulating paint to a roof, a roof base material layer, or an undercoat layer.

구체적으로는, 본 발명에 따른 차열층 및 단열층으로 된 2층 구조의 차열성 방수 도막은, 하기 단계를 포함하는 방법에 의해, 예를 들면 옥상 또는 지붕용 기재층 또는 하도층에, 설치될 수 있다: Specifically, the heat-shielding waterproof coating film of the heat shielding layer and the heat insulating layer according to the present invention may be installed, for example, on a rooftop or roof base layer or undercoat by a method comprising the following steps. have:

(1) 금속, 플라스틱, 목재, 도료 코팅, 시멘트, 아스팔트 등으로 구성된 군에서 선택되는 옥상 또는 지붕용 기재층 또는 하도층을 준비하고, (1) prepare a roof or roof base layer or sub-layer selected from the group consisting of metal, plastic, wood, paint coating, cement, asphalt, etc.,

(2) 상기 기재층 또는 하도층의 전부 또는 일부에, 전술한 바와 같은 수성 단열 페인트를, 예를 들면, 중공안료 0.1∼2중량%, 백색안료 1∼5중량%, 체질안료 20∼40중량%, 아크릴 에멀젼 수지 40∼60중량%, 희석제 1∼5중량%, 첨가제 5∼15중량% 및 잔여량의 물을 포함하는 수성 단열 페인트를 도포하여 단열층을 형성시키고, (2) To the whole or a part of the base material layer or the undercoat layer, the above-mentioned aqueous heat-insulating paint is, for example, 0.1-2% by weight of hollow pigment, 1-5% by weight of white pigment, and 20-40 weight of extender pigment. %, An aqueous insulating paint comprising 40 to 60% by weight of an acrylic emulsion resin, 1 to 5% by weight of a diluent, 5 to 15% by weight of an additive, and a residual amount of water is applied to form a heat insulating layer,

(3) 상기 단열층의 전부 또는 일부에, 전술한 바와 같은 수성 차열 페인트를, 예를 들면, 차열안료 0.1∼2중량%, 백색안료 10∼30중량%, 아크릴 에멀젼 수지 40∼60중량%, 희석제 1∼5중량%, 첨가제 5∼15중량% 및 잔여량의 물을 포함하는 수성 차열 페인트를 도포하여 차열층을 형성시키고, (3) To all or part of the heat insulating layer, the above-mentioned water-based heat shielding paint is, for example, 0.1 to 2% by weight of a heat shield pigment, 10 to 30% by weight of a white pigment, 40 to 60% by weight of an acrylic emulsion resin, and a diluent. An aqueous thermal barrier paint comprising 1 to 5% by weight, additives 5 to 15% by weight and a residual amount of water is applied to form a thermal barrier layer,

(4) 경우에 따라, 상기 차열층 위에 투명성 자외선 보호층을 더욱 형성시킴.(4) In some cases, a transparent ultraviolet protective layer is further formed on the heat shielding layer.

전술한 투명성 자외선 보호층은 자외선 보호제를 포함하는 투명성 아크릴계 수지로 형성될 수 있고, 자외선 보호제로는 유기 자외선 보호제 또는 티타니아와 같은 무기 자외선 보호제를 포함할 수 있다. The above-mentioned transparent UV protective layer may be formed of a transparent acrylic resin including a UV protection agent, and the UV protection agent may include an organic UV protection agent or an inorganic UV protection agent such as titania.

본 발명에 있어서, 상기 옥상 또는 지붕의 하도 처리는 당업계에 통상적으로 알려진 방법으로 수행될 수 있으며, 예를 들면, 하도용 도료를 도포하거나, 중합체로 된 방수재 또는 방수 코팅을 설치함으로써 수행될 수 있다. In the present invention, the roofing treatment of the roof or roof may be carried out by a method commonly known in the art, for example, by applying a paint for the coating, or installing a waterproof material or waterproof coating made of a polymer. have.

본 발명의 하나의 이점에 따르면, 옥상 및 지붕에 차열층 및 단열층을 이층 구조로 하여 형성시킨 2층 구조의 차열성 방수 도막에 있어서, 상부의 차열층은 차열안료를 포함하고 유리전이온도가 10℃ 이상인 아크릴 에멀젼 바인더 수지를 사용하고, 이를 다른 아크릴 에멀젼 바인더 수지를 사용하는 단열층과 함께 이층 구조로 형성시킴으로써. 첫째, 차열안료 및 단열성 중공안료의 효능을 극대화할 수 있어 차열 및 단열 효과를 효과적으로 발휘할 수 있으며, 둘째, 도포 직후 및 장시간 일광 노출 후에도 차열 코팅과 옥상 및 지붕의 기재층 사이의 우수한 접착력을 유지할 수 있으며, 셋째, 광택성 및 외관이 우수하고, 넷째, 물을 기재로 하므로 환경에 유리하고 작업성이 우수하다. According to one advantage of the present invention, in the heat-resistant waterproof coating film of the two-layer structure formed by forming the heat shield layer and the heat insulating layer in the roof and roof as a two-layer structure, the heat shield layer of the upper layer includes a heat shield pigment and the glass transition temperature is 10 By using an acrylic emulsion binder resin of not lower than < RTI ID = 0.0 > C, < / RTI > First, it is possible to maximize the effectiveness of the heat shield pigments and heat insulating hollow pigments to effectively exhibit the heat shielding and heat insulation effect, and second, to maintain excellent adhesion between the heat shield coating and the base layer of the roof and roof even after long-term exposure to sunlight. Third, it is excellent in gloss and appearance. Fourth, since it is based on water, it is advantageous to the environment and excellent in workability.

본 발명의 특히 바람직한 이점에 따르면, 상이한 바인더를 사용하는 차열층 및 단열층의 이층 구조로 인해, 지붕 또는 옥상에서 장시간의 일광 노출 및 과혹한 기후 변화에 노출되더라도, 우수한 접착내구성 및 내기후성을 가질 수 있다. According to a particularly preferred advantage of the present invention, due to the two-layer structure of the thermal barrier layer and the thermal insulation layer using different binders, even if exposed to long-term sun exposure and excessive climate change on the roof or rooftop, it can have excellent adhesion durability and weather resistance. have.

이하, 본 발명의 바람직한 실시예를 기재한다. 다만, 하기의 실시예는 본 발명의 바람직한 실시예일뿐, 본 발명이 하기 실시예에 한정되는 것은 아니다.Hereinafter, preferred embodiments of the present invention will be described. However, the following examples are only preferred examples of the present invention, and the present invention is not limited to the following examples.

실시예 1Example 1

(1) 상도용 수성 차열 페인트의 제조(1) Preparation of waterborne waterborne paint for top coat

물 14.2 중량부를 교반기를 이용하여 1,000∼1,500rpm으로 교반 하면서 증점제 0.2 중량부, 분산제 0.4 중량부, 유화제 0.5 중량부, 소포제 0.4 중량부를 투입하여 30분 분산교반 하였다.14.2 parts by weight of water was stirred at 1,000 to 1,500 rpm using a stirrer, and 0.2 parts by weight of thickener, 0.4 parts by weight of dispersant, 0.5 parts by weight of emulsifier, and 0.4 parts by weight of antifoaming agent were dispersed and stirred for 30 minutes.

상기 배합물에 차열안료(JR-1000) 0.1 중량부, 백색안료(Tiona 595) 27 중량부를 투입하여 1,000∼1,500rpm으로 1시간 교반하여 안료입자경이 20㎛이하가 되도록 분산교반하였다.0.1 parts by weight of heat shield pigment (JR-1000) and 27 parts by weight of white pigment (Tiona 595) were added to the formulation, followed by stirring at 1,000 to 1500 rpm for 1 hour to disperse and stir the pigment particle diameter to 20 µm or less.

상기 배합물에 아크릴 에멀젼 수지(삼화페인트공업) 50.5 중량부, 침강방지제 0.1 중량부, 희석제(ATBC) 1.5 중량부, 소포제 0.3 중량부, 증점제 0.4 중량부를 교반기를 이용해 1,000∼1,500rpm으로 10분 정도 분산교반하였다.50.5 parts by weight of acrylic emulsion resin (Samhwa Paint Industry), 0.1 part by weight of antisettling agent, 1.5 parts by weight of diluent (ATBC), 0.3 parts by weight of antifoaming agent, 0.4 parts by weight of thickener using a stirrer and dispersed about 10 minutes at 1,000-1,500 rpm. Stirred.

(2) 중도용 수성 단열 페인트의 제조(2) Preparation of Intermediate Aqueous Insulating Paint

물 4.8 중량부에 아크릴 에멀젼 수지(ACRONAL PS 791ap) 17 중량부를 투입하고 교반하면서 증점제 0.3 중량부, 유화제 0.3 중량부, 소포제 0.2 중량부를 투입하여 30분 분산교반 하였다.17 parts by weight of an acrylic emulsion resin (ACRONAL PS 791ap) was added to 4.8 parts by weight of water, 0.3 parts by weight of a thickener, 0.3 parts by weight of an emulsifier, and 0.2 parts by weight of an antifoaming agent were added, followed by dispersion stirring for 30 minutes.

상기 배합물에 중공안료 (PG-1001) 0.1 중량부, 백색안료(Ti-Pure Rutile Titanium Dioxide R706) 2.8 중량부, 체질안료(Omyacarb 1-HB) 32.2 중량부를 투입하여 1,000∼1,500rpm으로 1시간 교반하였다.0.1 parts by weight of hollow pigment (PG-1001), 2.8 parts by weight of white pigment (Ti-Pure Rutile Titanium Dioxide R706), and 32.2 parts by weight of extender pigment (Omyacarb 1-HB) were stirred at 1,000 to 1500 rpm for 1 hour. It was.

상기 배합물에 아크릴 에멀젼 수지(ACRONAL PS 791ap) 5 중량부, 희석제(텍사놀) 2.5 중량부, 물 1.9 중량부, 소포제 0.8 중량부, 증점제 0.3 중량부를 투입하여 1,000∼1,500rpm으로 1시간 교반하였다.5 parts by weight of an acrylic emulsion resin (ACRONAL PS 791ap), 2.5 parts by weight of a diluent (texanol), 1.9 parts by weight of water, 0.8 parts by weight of an antifoaming agent, and 0.3 parts by weight of a thickener were added and stirred at 1,000 to 1500 rpm for 1 hour.

(3) 2-코트형 차열 코팅의 설치(3) Installation of 2-coat type thermal barrier coating

결과된 상도용 수성 차열 페인트 및 중도용 수성 단열 페인트를, 하도 처리된 지붕에 상도 및 중도로서 각각 적용하여 2-코트형 차열 코팅을 설치하고, 차열능, 접착력 및 일광 하의 접착내구성을 시험하였다. The resulting topcoat waterborne paint and midway waterborne insulating paint were applied to the undercoated roof as top coat and midway, respectively, to install a two-coat type heat shield, and the heat shielding ability, adhesion and adhesion durability under daylight were tested.

시험예 1 및 2에 기재된 방법을 사용하여, 전술한 2-코트형 차열 코팅은 차열능, 접착력 및 일광 하의 접착내구성이 우수함을 확인하였다(하기 표 1 참조). Using the methods described in Test Examples 1 and 2, it was confirmed that the above-described two-coat type thermal barrier coating was excellent in heat shielding ability, adhesive force and adhesion durability under sunlight (see Table 1 below).

참고예 1Reference Example 1

차열안료를 사용하는 상도용 수성 차열 페인트 및 중공안료를 사용하지 않는 중도용 수성 페인트를 각각 제조하였다. Aqueous waterborne paints for top coats using thermal barrier pigments and intermediate waterborne paints without hollow pigments were prepared, respectively.

결과된 상도용 수성 차열 페인트 및 중도용 수성 페인트를, 하도 처리된 지붕 기재층에 상도 및 중도로서 각각 적용하여 2-코트형 차열 코팅을 설치하고, 차열능, 접착력 및 일광 하의 접착내구성을 시험하였다. The resulting topcoat waterborne paint and midway waterborne paint were applied to the undercoated roof substrate layer as topcoat and midway, respectively, to install a two-coat type thermal barrier coating and to test the thermal insulation ability, adhesion and adhesion durability under sunlight. .

시험예 1 및 2에 기재된 방법을 사용하여, 차열성, 접착력 및 일광 하의 접착내구성이 우수함을 확인하였지만, 단열성이 실시예 1에 비해 떨어지는 것을 확인하였다(하기 표 1 참조). 장기간 일광 조사 후에, 단열층의 일부 물성이 불량해지거나 더많이 저하될 우려가 있다. Using the methods described in Test Examples 1 and 2, it was confirmed that the heat shielding property, the adhesive strength and the adhesion durability under sunlight was excellent, but it was confirmed that the thermal insulation is inferior to Example 1 (see Table 1 below). After long-term sunlight irradiation, there is a fear that some physical properties of the heat insulation layer may be deteriorated or further reduced.

비교예 1(대조)Comparative Example 1 (Control)

차열안료 및 중공안료를 사용하지 않고 상도용 수성 페인트 및 하도용 수성 페인트(방수재)를 각각 제조하고, 하도 처리된 지붕 기재층에 상도 및 중도로서 각각 적용하여 2-코트형 도료 코팅을 설치하고, 시험예 1 및 2에 기재된 방법을 사용하여, 차열능, 접착력 및 일광 하의 접착내구성을 시험하였다. Without using heat shielding and hollow pigments, water-based paints for water and water-based paints (water repellents) are respectively prepared, and 2-coat type paint coatings are installed by applying them as top coats and middle coats to the undercoated roof substrate layers, respectively. Using the methods described in Test Examples 1 and 2, the thermal shielding ability, adhesion, and adhesion durability under sunlight were tested.

접착력 및 일광 하의 접착내구성은 실시예 1 및 참고예 1의 결과와 유사하였지만, 차열성은 나타내지 않았다(하기 표 1 참조). The adhesion and adhesion durability under daylight were similar to those of Example 1 and Reference Example 1, but showed no heat shielding (see Table 1 below).

시험예 1: 도료의 물성 측정Test Example 1 Measurement of Physical Properties of Paint

상기 실시예 1 및 비교예 1 및 2에서 제조된 차열성 페인트 및 단열성 페인트를 각각 건조 도막 두께 100 ㎛로 도장하여 실온에서 7일 동안 자연건조시킨 다음, 하기의 방법으로 물성을 측정하였다. The heat insulating paint and the heat insulating paint prepared in Example 1 and Comparative Examples 1 and 2 were respectively coated with a dry coating thickness of 100 μm, and naturally dried at room temperature for 7 days, and then physical properties were measured by the following method.

1-1. 광택(60° 광택도) 측정방법1-1. Glossiness (60 ° glossiness) measuring method

KS M 5000의 시험방법 3312에 따라 60ㅀ광택도 측정기(Tri-Microgloss 20-60-85)로 도막의 광택도를 측정하여 수치로 나타낸다. According to Test Method 3312 of KS M 5000, the glossiness of the coating film was measured and measured with a 60 ㅀ glossiness meter (Tri-Microgloss 20-60-85).

1-2. 내수성 측정방법1-2. How to measure water resistance

유리판(15mm×15mm×5mm)에 필름 어플리케이터(Film Applicator)로 건조 도막약 50 ㎛가 되도록 도장하고 실온에서 7일 동안 자연건조시켜 수득된 도막(샘플 1)을, 증류수에 168시간 동안 침적시킨 후, 도막의 이상 유무를 육안검사한다.After coating the glass plate (15mm × 15mm × 5mm) with a film applicator to a dry coating film of about 50 μm and immersing the coating film (sample 1) obtained by naturally drying for 7 days at room temperature for 168 hours. Visually inspect the coating for abnormalities.

1-3. 내알카리성 측정방법1-3. Alkali resistance measuring method

상기와 동일하게 제조된 도막(샘플 1)을 수산화나트륨 5% 수용액에 168시간 동안 침적시킨 후, 도막의 이상 유무를 육안검사한다.The coating film prepared as described above (sample 1) was immersed in a 5% aqueous sodium hydroxide solution for 168 hours, and then visually inspected for abnormalities of the coating film.

1-4. 내용제성 측정방법1-4. Solvent resistance measuring method

상기와 동일하게 제조된 도막(샘플 1)을 크실렌에 168시간 동안 침적시킨 후, 도막의 이상 유무를 육안검사한다.The coating film (sample 1) prepared in the same manner as above was deposited on xylene for 168 hours, and then visually inspected for abnormalities of the coating film.

1-5. 내충격성 측정방법1-5. Impact resistance measuring method

주석판(15mm×10mm×0.1mm)에 필름 어플리케이터로 건조 도막 두께가 약 50 ㎛가 되도록 도장한 다음, 실온에서 7일 동안 자연건조시켜 수득된 도막(샘플 2)을, 듀퐁 타입(DUPONT Type)의 충격시험기로 500g의 하중을 가진 추로 30cm의 높이에서 낙하시켜 육안검사시 도막이 박리되지 않으면 양호, 도막이 박리되면 불량으로 한다. 이때 충격면은 1/2 인치인 구면을 사용한다.The coating film (Sample 2) obtained by coating a tin plate (15 mm x 10 mm x 0.1 mm) with a film applicator to have a dry coating thickness of about 50 μm, and then naturally drying at room temperature for 7 days was prepared as a DuPont Type. If the coating film is not peeled off during visual inspection by dropping it at a height of 30cm with a weight of 500g with an impact tester, it is considered to be defective if the coating film is peeled off. At this time, use the spherical surface 1/2 inch.

1-6. 굴곡성 측정방법1-6. Flexibility Measurement Method

상기와 동일하게 제조된 도막(샘플 2)으로 제조된 시험편의 중간점을 만드렐 시험기(Mandrel Tester) 1/8 인치에 올려놓고 1초동안 완전히 꺽는다. 이때 시험편의 꺽인 부분에서 육안검사시 도막의 갈라짐과 박리가 발생하지 않으면 양호, 도막의 갈라짐과 박리가 발생하면 불량으로 한다.Place the midpoint of the test piece prepared with the coating film (Sample 2) prepared in the same manner as above in 1/8 inch of the Mandrel Tester and fold completely for 1 second. At this time, if the splitting or peeling of the coating film does not occur during visual inspection at the bent part of the test piece, it is good.

1-7. 부착성 측정방법1-7. Adhesiveness Measurement Method

ASTM D3359의 Test Method B의 테스트 방법에 따라 건조된 도막을 2 ㎝간격으로 6개씩 서로 교차되게 칼로 긁어 25개의 칸을 만들어 3M 투명 테이프로 그 부위에 접착을 시킨 후 그 떨어진 정도에 따라 6단계로 평가한다.According to the test method of Test Method B of ASTM D3359, the dried coating film was scraped by 6 pieces at intervals of 2 ㎝ by crossing each other to make 25 cells. Evaluate.

5B: 도막 박리가 전혀 없음5B: no peeling of coating

4B: 도막 박리 5% 미만4B: less than 5% of coating peeling

3B: 도막 박리 5 ∼ 15%3B: 5-15% of coating peeling

2B: 도막 박리 15 ∼ 35%2B: coating film peeling 15 to 35%

1B: 도막 박리 35 ∼ 65%1B: 35 to 65% of film peeling

0B: 도막 박리 65% 이상0B: coating film peeling 65% or more

1-8. 촉진내후성 측정방법1-8. Accelerated weather resistance measurement method

KS M 5000의 시험방법 3231에 따라 시험편을 촉진내후성기(ATLAS Ci5/DMC Weather-ometer)에 250시간 노출시킨 후 도막외관의 이상 유무를 육안검사한다.According to Test Method 3231 of KS M 5000, the specimen is exposed to the ATLAS Ci5 / DMC Weather-ometer for 250 hours and visually inspected for abnormalities of the coating film.

결과는 하기 표 1에 기재한다. The results are shown in Table 1 below.

실시예 1Example 1 참고예 1Reference Example 1 비교예 1Comparative Example 1 광택Polish 8585 8585 8787 내수성Water resistance 이상없음clear 이상없음clear 이상없음clear 내알칼리성Alkali resistance 이상없음clear 이상없음clear 이상없음clear 내용제성Solvent resistance 이상없음clear 이상없음clear 이상없음clear 내충격성Impact resistance 양호Good 양호Good 양호Good 굴곡성 Flexibility 양호Good 양호Good 양호Good 부착성Adhesion 5B5B 5B5B 5B5B 촉진내후성Weathering resistance 이상없음clear 이상없음clear 이상없음clear

시험예Test Example 2: 2층 도료의  2: two-layer paint 차열성Heat shield 및 단열성 측정 And insulation measurement

상기 실시예 1, 참고예 1 및 비교예 1의 상도용 수성 페인트 및 중도용 수성 페인트를 각각 건조 도막 두께 100 ㎛로 도장한 다음, 실온에서 7일 동안 자연건조시켜 하기의 방법으로 차열성 및/또는 단열성을 측정하고, 그 결과를 표 2에 기재하고, 도 1 (내부온도) 및 도 2(외부온도)에 그래프로 도시하였다. Coating the water-based water-based paints and the water-based water-based paints of Example 1, Reference Example 1 and Comparative Example 1 with a thickness of 100 μm of a dry coating film, respectively, and then naturally dried at room temperature for 7 days to provide thermal insulation and / Or heat insulation was measured, and the result is shown in Table 2, and is shown graphically in FIG. 1 (internal temperature) and FIG. 2 (external temperature).

구체적으로, 하도처리된 철판(300mm×300mm×0.5mm)에 붓 또는 스프레이를 이용하여, 건조두께가 약 100 ㎛이 되도록 도장한 다음, 실온에서 7일 동안 자연 건조시켜 시험편을 제조하고, 이를 스치로폼의 재질로 지붕부분이 개방되게 제작된 모형집(250mm×250mm×150mm)의 지붕부분에 거치하고, 외부공기가 유입되지 않도록 밀봉하였다. 시험편의 상부 30 cm 높이에서 적외선 램프(PHILIPS IP 250R-230V, 230W)로 30분간 조사하고, 시간 경과에 따라 지붕의 표면 온도(즉, 시험편의 표면 온도)와 지붕 아래의 실내 온도 (즉, 내부 온도)를 디지털 온도센서(OMEGA, Model HH21)로 측정하고, 초기, 30분 및 60분 조사 후의 온도차로서 상대적 차열성능을 측정한다. 전술한 차열 및 단열 성능 측정 설비는 밀폐된 장소에 설치한다.Specifically, using a brush or spray on the undercoat iron plate (300mm × 300mm × 0.5mm), the coating is coated to a dry thickness of about 100 ㎛, and then naturally dried at room temperature for 7 days to prepare a test piece, Styrofoam It was mounted on the roof of the model house (250mm × 250mm × 150mm), which was made so that the roof part was made of open material, and sealed to prevent the inflow of external air. Irradiate for 30 minutes with an infrared lamp (PHILIPS IP 250R-230V, 230 W) at the top 30 cm height of the specimen, and over time the surface temperature of the roof (i.e. surface temperature of the specimen) and room temperature under the roof (i.e. internal Temperature) is measured with a digital temperature sensor (OMEGA, Model HH21) and the relative thermal insulation performance is measured as the temperature difference after the initial, 30 and 60 minute irradiation. The above-described heat shielding and thermal insulation performance measuring equipment is installed in a closed place.

위치location 도막Coating 초기Early 5분5 minutes 10분10 minutes 20분20 minutes 30분30 minutes 40분40 minutes 50분50 minutes 60분60 minutes 온도차
(30분)Temperature difference
(30 minutes) 온도차
(60분)Temperature difference
(60 minutes) 내부 온도
(℃)Internal temperature
(℃) 비교예 1Comparative Example 1 22.122.1 32.532.5 38.738.7 45.145.1 49.949.9 53.753.7 58.758.7 27.827.8 37.637.6 참고예 1Reference Example 1 22.722.7 28.928.9 32.432.4 35.935.9 38.538.5 40.740.7 42.642.6 43.943.9 15.815.8 21.221.2 실시예 1Example 1 22.522.5 28.628.6 32.132.1 35.435.4 3838 40.340.3 42.342.3 43.543.5 15.515.5 21.021.0 외부 온도
(℃)Outside temperature
(℃) 비교예 1Comparative Example 1 23.523.5 50.650.6 55.355.3 59.359.3 6363 65.565.5 67.667.6 69.169.1 39.539.5 45.645.6 참고예 1Reference Example 1 23.223.2 36.536.5 39.339.3 41.341.3 43.443.4 45.245.2 47.247.2 47.847.8 20.220.2 24.624.6 실시예 1Example 1 2323 36.736.7 39.539.5 41.641.6 43.343.3 45.145.1 47.247.2 47.547.5 20.320.3 24.524.5

상기 표 1로부터, 일반 상도용 수성 페인트 및 중도용 수성 페인트를 사용한 2-코트형 도료 (비교예 1)에 비해, 본 발명에 따른 상도용 수성 차열 페인트를 사용하여 형성된 2-코트형 도료(실시예 1 및 참고예 1)는 우수한 차열성을 나타냄을 알 수 있다. From the above Table 1, compared with the 2-coat type paint (comparative example 1) using the normal top water paint and the intermediate water paint (comparative example 1), the 2-coat type paint formed using the top coat aqueous heat-shielding paint which concerns on this invention (implementation It can be seen that Example 1 and Reference Example 1) exhibit excellent heat shielding properties.

또한, 본 발명에 따른 중도용 수성 단열 페인트를 적용한 경우(실시예 1), 이를 적용하지 않은 경우(참고예 1)에 비해 내부온도가 최대 0.5℃까지 차이가 나는 것을 알 수 있으며, 이에 의해 우수한 열차단 효과, 즉 단열성이 나타남을 보여준다. In addition, when the intermediate water-based insulating paint according to the present invention is applied (Example 1), it can be seen that the internal temperature is up to 0.5 ℃ difference compared to when not applied (Reference Example 1), thereby excellent It is shown that the thermal barrier effect, that is, thermal insulation is shown.

본 발명은 페인트 산업에서 산업적으로 유용하게 사용될 수 있다. The present invention can be industrially useful in the paint industry.

Claims (10)

차열안료 0.1∼2중량%, 백색안료 20∼40중량%, 아크릴계 바인더 수지 40∼60중량%, 희석제 1∼5중량%, 첨가제 5∼15중량% 및 잔여량의 물을 포함하는 수성 차열 페인트, 및 중공안료 0.1∼2중량%, 백색안료 1∼5중량%, 체질안료 20∼40중량%, 탄성 바인더 수지 40∼60중량%, 희석제 1∼5중량%, 첨가제 5∼15중량% 및 잔여량의 물을 포함하는 수성 단열성 페인트로 이루어진, 옥상 또는 지붕용 2-코트형 수성 차열성 방수 도료. An aqueous heat shield paint comprising 0.1 to 2% by weight of a thermal pigment, 20 to 40% by weight of a white pigment, 40 to 60% by weight of an acrylic binder resin, 1 to 5% by weight of a diluent, 5 to 15% by weight of an additive, and a residual amount of water; and Hollow pigment 0.1-2%, white pigment 1-5%, extender pigment 20-40%, elastic binder resin 40-60%, diluent 1-5%, additive 5-15%, and residual water Made of an aqueous insulating paint comprising a, roof- or roof 2-coat type water-based heat-resistant waterproof paint. 제 1 항에 있어서,
상기 수성 차열 페인트의 아크릴계 바인더 수지는, 유리전이온도가 10℃ 이상 아크릴 에멀젼 수지로부터 선택되는 것을 특징으로 하는, 옥상 또는 지붕용 2-코트형 수성 차열성 방수 도료. The method of claim 1,
The acrylic binder resin of the water-based thermal barrier paint is a glass-coated temperature is selected from an acrylic emulsion resin of 10 ℃ or more, roof- or roof 2-coat type water-based heat-shielding waterproof coating. 제 2 항에 있어서,
상기 수성 차열 페인트의 아크릴계 에멀젼 수지는, 코어의 유리전이온도가 30℃ 이상인 내부 가교형 코어-쉘 구조를 가지는 것을 특징으로 하는, 옥상 또는 지붕용 2-코트형 수성 차열성 방수 도료. The method of claim 2,
The acrylic emulsion resin of the water-based heat shield paint has an internal crosslinked core-shell structure having a glass transition temperature of 30 ° C. or higher, and a roof or roof 2-coat water-based heat-shielding waterproof coating. 제 1 항에 있어서,
상기 차열안료는 알루미늄 금속 분말로부터 선택되고, 상기 중공안료는 다공성 실리카, 다공성 티타니아, 중공 실리카 및 중공 티타니아로 구성된 군에서 선택되는 것을 특징으로 하는, 옥상 또는 지붕용 2-코트형 수성 차열성 방수 도료. The method of claim 1,
The heat shield pigment is selected from aluminum metal powder, the hollow pigment is selected from the group consisting of porous silica, porous titania, hollow silica and hollow titania, roof or roof 2-coat type water-based heat-resistant waterproof paint . 제 1 항에 있어서,
상기 수성 단열 페인트는,
(1a) 물에 아크릴 에멀젼 수지 및 첨가제(증점제, 유화제, 소포제)를 첨가하여 30분 동안 교반하고,
(1b) 수득된 배합물에, 중공안료, 백색안료 및 체질안료를 첨가하여 1,000∼1,500rpm으로 1시간 동안 교반하고,
(1c) 수득된 배합물에, 추가의 아크릴 에멀젼 수지, 첨가제(희석제, 소포제, 증점제) 및 잔여량의 물을 첨가하여 1,000∼1,500rpm으로 1시간 동안 교반함으로써 제조된 것임을 특징으로 하는, 옥상 또는 지붕용 2-코트형 수성 차열성 방수 도료. The method of claim 1,
The water-based insulating paint,
(1a) add acrylic emulsion resin and additives (thickener, emulsifier, antifoaming agent) to water and stir for 30 minutes,
(1b) To the blend obtained, hollow pigments, white pigments and extender pigments were added and stirred at 1,000 to 1500 rpm for 1 hour,
(1c) roofing or roofing, characterized in that it is prepared by adding an additional acrylic emulsion resin, an additive (diluent, antifoaming agent, thickener) and a residual amount of water and stirring at 1,000 to 1500 rpm for 1 hour. 2-coat type water-based water-resistant waterproof paint. 제 1 항에 있어서,
상기 수성 차열 페인트는,
(2a) 물에 첨가제(증점제, 분산제, 유화제, 소포제 등)를 첨가하여 1,000∼1,500rpm으로 30분 동안 교반하고,
(2b) 수득된 배합물에, 차열안료 및 백색안료를 첨가하여, 안료의 평균입자직경이 20㎛ 이하가 되도록 1,000∼1,500rpm으로 1시간 30분 동안 교반하고,
(2c) 수득된 배합물에, 바인더로서 아크릴 에멀젼 수지 및 첨가제(침강방지제, 희석제, 소포제, 증점제)를 첨가하여 1,000∼1,500rpm으로 1시간 30분 동안 교반함으로써 제조된 것임을 특징으로 하는, 옥상 또는 지붕용 2-코트형 수성 차열성 방수 도료. The method of claim 1,
The water-based thermal paint,
(2a) Add an additive (a thickener, a dispersant, an emulsifier, an antifoaming agent, etc.) to water, stir at 1,000 to 1500 rpm for 30 minutes,
(2b) To the obtained blend, a heat shield pigment and a white pigment were added, and the mixture was stirred at 1,000 to 1500 rpm for 1 hour and 30 minutes so that the average particle diameter of the pigment was 20 µm or less.
(2c) A rooftop or roof, characterized in that it is prepared by adding acrylic emulsion resin and additives (precipitating agent, diluent, antifoaming agent, thickener) as a binder and stirring at 1,000 to 1500 rpm for 1 hour and 30 minutes. 2-coat type water-based, heat-resistant waterproof paint. 옥상 또는 지붕에 차열층 및 단열층으로 된 2층 구조의 차열성 방수 도장 방법으로서:
(1) 옥상 또는 지붕용 기재층 또는 하도층을 준비하는 단계,
(2) 상기 기재층 위에, 중공안료 0.1∼2중량%, 백색안료 1∼5중량%, 체질안료 20∼40중량%, 탄성 바인더 수지 40∼60중량%, 희석제 1∼5중량%, 첨가제 5∼15중량% 및 잔여량의 물을 포함하는 수성 단열 페인트를 도포 및 건조하여, 단열층을 형성시키는 단계,
(3) 상기 단열층 위에, 차열안료 0.1∼2중량%, 백색안료 20∼40중량%, 아크릴계 바인더 수지 40∼60중량%, 희석제 1∼5중량%, 첨가제 5∼15중량% 및 잔여량의 물을 포함하는 수성 차열 페인트를 도포 및 건조하여, 차열층을 형성시키는 단계
를 포함하는, 2층 구조의 차열성 방수 도장 방법. As a heat shielding waterproof coating method of a two-layer structure having a thermal insulation layer and a thermal insulation layer on a roof or a roof:
(1) preparing a roofing or roofing substrate layer or an undercoating layer,
(2) On the base layer, 0.1-2% by weight hollow pigment, 1-5% by weight white pigment, 20-40% by weight extender pigment, 40-60% by weight elastic binder resin, 1-5% by weight diluent, additive 5 Applying and drying an aqueous insulating paint comprising ˜15% by weight and a residual amount of water to form an insulating layer,
(3) On the heat insulating layer, 0.1 to 2% by weight of heat shield pigment, 20 to 40% by weight of white pigment, 40 to 60% by weight of acrylic binder resin, 1 to 5% by weight of diluent, 5 to 15% by weight of additive and residual amount of water Applying and drying a water-based thermal barrier paint to form a thermal barrier layer
Including, heat-resistant waterproof coating method of a two-layer structure. 제 7 항에 있어서,
상기 옥상 또는 지붕용 기재층은, 하도 처리되거나 방수성 코팅 처리된 것임을 특징으로 하는, 2층 구조의 차열성 방수 도장 방법.The method of claim 7, wherein
The roof or roof base layer is heat-resistant or waterproof coating, characterized in that the heat-resistant waterproof coating method of a two-layer structure. 제 7 항에 있어서,
(4) 상기 차열층 위에, 투명성 자외선 보호층을 더욱 도포하는 단계를 포함하는 것을 특징으로 하는, 2층 구조의 차열성 방수 도장 방법. The method of claim 7, wherein
(4) The heat-shielding waterproof coating method of the two-layer structure, characterized by further comprising applying a transparent ultraviolet protective layer on the heat shielding layer. 제 7 항 내지 제 9 항 중의 어느 한 항에 따른 구조의 차열성 방수 도장 방법에 따라 형성된, 차열층 및 단열층으로 된 2층 구조의 차열성 방수 도막.
A heat-resistant waterproof coating film having a two-layer structure consisting of a heat shielding layer and a heat insulating layer, formed according to the heat shielding waterproof coating method of the structure according to any one of claims 7 to 9.
KR1020180009792A 2018-01-26 2018-01-26 2-coat-type aqueous heat-shielding and water-resistant paint for rooftop or roof, method for forming a heat-shielding and water-resistant coating with two layers structure using the same, and a heat-shielding and water-resistant coating with two layers structure thereby KR20190090957A (en)