CN1413930A - 一种电子元件封接玻璃 - Google Patents
一种电子元件封接玻璃 Download PDFInfo
- Publication number
- CN1413930A CN1413930A CN 02130776 CN02130776A CN1413930A CN 1413930 A CN1413930 A CN 1413930A CN 02130776 CN02130776 CN 02130776 CN 02130776 A CN02130776 A CN 02130776A CN 1413930 A CN1413930 A CN 1413930A
- Authority
- CN
- China
- Prior art keywords
- electronic component
- seal glass
- component seal
- rod
- molten state
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明是一种电子元件封接玻璃,其特点在于组成成分包括SiO2、B2O、ZnO、Sb2O3、Al2O3、Na2O、K2O、Bi2O3、Li2O3、CaO,通过熔化、浇铸、退火等步骤制得所需的产品。本发明的产品不含铅及其它有害物质,有利于环保,有利于人体健康,而且完全符合使用要求。
Description
技术领域
本发明涉及特殊性能玻璃,具体地说,是一种不含铅的电子元件封接玻璃。
背景技术
现有的电子元件封接玻璃含有大量的金属铅,如现有的电子封接玻璃牌号DB-435的铅含量为34%、DH-704铅含量为77%。我们知道,重金属铅对人体是有害的,是不符合环保要求的。
发明内容
本发明的目的是克服已有技术的缺点,提供一种不含铅的电子元件封接玻璃。
本发明的封接玻璃的组成及其重量百分含量:SiO245-62%、Bi2O30.5-8%、BaO3-15%、ZnO2-8%、Sb2O30.5-4%、Al2O30-3%、Na2O6-15%、K2O2-6%Bi2O30-5%、Li2O30-5%、CaO2-8%。
本发明的封接玻璃的具体制备方法:
(1)硅钼棒电炉加热至1350-1450℃后,将混匀的物料加入其中,然后升温至1450-1500℃,搅拌1.5小时,物料呈熔融状态;
(2)将步骤(1)得到的熔融状态的物料浇铸在已预热至400-430℃的模具中,浇铸成棒,然后取出棒,入退火炉中,在400-500℃下保温1-5小时即制得所需的电子元件封接玻璃。
本发明优点效果:
本发明的特点是产品中不含重金属铅及其它有害物质,有利于环保,有利于人体健康,是一种符合绿色环保要求的产品;本发明的产品也完全符合使用要求。
具本实施方式
实例1-4
实例1-4组成配方及操作条件分别见表1和表2,产品性能见表3。
表1
成份 | 实例1 | 实例2 | 实例3 | 实例4 |
SiO2,% | 48 | 52 | 59 | 57 |
B2O3,% | 0.5 | 3 | 4 | 8 |
BaO,% | 7 | 14 | 5 | 6 |
ZnO,% | 0.5 | 2 | 6 | 8 |
Sb2O3,% | 0.5 | 3.5 | 0.5 | 0.5 |
Al2O3,% | 1 | 2 | 0 | 0 |
Na2O,% | 8 | 10 | 7.5 | 12.5 |
K2O,% | 6 | 5 | 4 | 6 |
Bi2O3,% | 26 | 0 | 7 | 0 |
Li2O3,% | 0 | 2.5 | 3 | 0 |
CaO,% | 2.5 | 6 | 4 | 2 |
表2
项目 | 实例1 | 实例2 | 实例3 | 实例4 |
加料温度,℃ | 1450 | 1350 | 1400 | 1400 |
熔化温度,℃ | 1480 | 1450 | 1480 | 1450 |
退火温度,℃ | 460 | 420 | 450 | 420 |
保温时间,小时 | 2 | 5 | 3 | 4 |
表3
膨胀系数 | 98×10-7/℃ |
转变点(Tg) | 475±5℃ |
变形点(Tf) | 540±5℃ |
软化点(TS) | 618±5℃ |
2/3球点 | 784±5℃ |
1/2球点 | 845±5℃ |
流动点 | 947±5℃ |
Claims (1)
1.一种电子元件封接玻璃,其特征在于组成成份及重量百分含量为:SiO245-62%、B2O30.5-8%、BaO3-15%、ZnO2-8%、Sb2O30.5-4%、Al2O30-3%、Na2O6-15%、K2O2-6%、Bi2O30-30%、Li2O30-5%、CaO2-8%,具体制备方法如下:
(1)硅钼棒电炉加热至1350-1450℃后,将混匀的物料加入其中,然后升温至1450-1500℃,搅拌1.5小时,物料呈熔融状态;
(2)将步骤(1)得到的熔融状态的物料浇铸在已预热至400-430℃的模具中,浇铸成棒,然后取出棒,入退火炉中,在400-500℃下保温1-5小时即制得所需的电子元件封接玻璃。