CN1376754A - 耐高温输送带难燃胶粘剂 - Google Patents

耐高温输送带难燃胶粘剂 Download PDF

Info

Publication number
CN1376754A
CN1376754A CN 02108660 CN02108660A CN1376754A CN 1376754 A CN1376754 A CN 1376754A CN 02108660 CN02108660 CN 02108660 CN 02108660 A CN02108660 A CN 02108660A CN 1376754 A CN1376754 A CN 1376754A
Authority
CN
China
Prior art keywords
conveying belt
group
burn
tackiness agent
component
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 02108660
Other languages
English (en)
Other versions
CN1164708C (zh
Inventor
刘雪颖
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB021086605A priority Critical patent/CN1164708C/zh
Publication of CN1376754A publication Critical patent/CN1376754A/zh
Application granted granted Critical
Publication of CN1164708C publication Critical patent/CN1164708C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及一种耐高温输送带难燃胶粘剂包括胶粘剂(甲组)和固化剂(乙组)两个组份,其中:胶粘剂(甲组)是由下述重量份的原料制成的:含羧基的聚氯丁二烯80－100份、三氯乙烯450－600份、烷基酚醛树脂30－80份、氢氧化铝4－6份、氢氧化镁6－8份、1·1·1－三氯乙烷140－320份、乙醇0.5－2份、异丙醇5－20份;固化剂(乙组)是由下述重量份的原料制成的:四异氰酸脂8－10份、正丁基黄原酸锌0.2－0.6份、活性氧化镁0.6－5份。其优点是耐高温、难燃烧、粘合强度高,胶液稳定性好,不分层,易贮存。主要用于输送带等在高温环境下使用的需要粘合的物品。

Description

耐高温输送带难燃胶粘剂
本发明涉及一种耐高温输送带难燃胶粘剂，属于粘合剂类。
目前，输送带在常温常压下进行快速粘接所采用的胶粘剂均为热塑性的。这样的输送带在高温环境下使用时，胶膜会逐渐软化发粘，内聚强度急剧下降，这不仅使输送带的寿命大大缩短，而且也直接影响着使用单位的效益。此外，这种胶粘剂胶液易燃烧，易分层，贮存稳定性差，难以满足使用要求。
本发明的目的是提供一种耐高温、难燃烧，胶液稳定性好，不易分层的耐高温输送带难燃胶粘剂。
本发明的目的是由以下方式实现的：
本发明包括胶粘剂(甲组)和固化剂(乙组)两个组份，其中：胶粘剂(甲组)是由下述重量份的原料制成的：含羧基的聚氯丁二烯80-100份、三氯乙烯450-600份、烷基酚醛树脂30-80份、氢氧化铝4-6份、氢氧化镁6-8份、1·1·1-三氯乙烷140-320份、乙醇0.5-2份、异丙醇5-20份；固化剂(乙组)是由下述重量份的原料制成的：四异氰酸脂8-10份、正丁基黄原酸锌0.2-0.6份、活性氧化镁0.6-5份。
本发明的制备方法是按重量份将氢氧化铝、氢氧化镁与烷基酚醛树脂在1·1·1-三氯乙烷中，经异丙醇、乙醇的催化作用，反应制得溶液，再经沉淀、过滤得到不溶物小于1％的热固性树脂，然后，将热固性树脂与含有羧基的聚氯丁二烯、三氯乙烯混合溶解即得到不分层的胶粘剂组份。将正丁基黄原酸锌在低温10℃下加入到四异氰酸酯中反应4小时，再加入活性氧化镁搅拌12小时，并使液温逐渐回升至室温，即制得固化剂(乙组)组份。
使用时，将胶粘剂(甲组)和固化剂(乙组)两种组份按10∶1的比例混合搅拌均匀，在经打毛、去污、干燥的待粘物表面均匀涂刷两次混合胶液，待第二次胶液干燥至略有粘性时，即可粘合，并施以接触压即可。本发明的胶粘剂不仅可用于粘接输送带，也可用于其它在高温环境下使用的需要粘合的物品，如：防火板、扬声器等。
本发明的优点是耐高温、难燃烧、粘合强度高，胶液稳定性好，不分层，易贮存。
下面给出本发明的实施例：
一、配方：
  组份   序号     原料名称   用量(重量份)
胶粘剂组     1     含羧基聚氯丁二烯     100
    2     三氯乙烯     575
    3     烷基酚醛树脂     35
    4     氢氧化铝     5
    5     氢氧化镁     7
    6     1·1·1-三氯乙烷     140
    7     乙醇     2
    8     异丙醇     10
    固化剂组     1     四异氰酸脂     10
    2     正丁基黄原酸锌     0.4
    3     活性氧化镁     4
二、合成工艺：
胶粘剂(甲组)组份：
1、将原料烷基酚醛树脂、氢氧化铝、氢氧化镁、1·1·1-三氯乙烷投入反应釜中，在搅拌下升温至40至℃，再缓慢加入乙醇、异丙醇，保温搅拌20小时，然后沉淀、过滤、控制不溶物小于1％，得到热固性树脂，待用；
2、将原料含羧基聚氯丁二烯和三氯乙烯投入带搅拌的反应釜中搅拌8-10小时至完全溶解，将上述热固性树脂投入其中混合搅拌6-8小时，即得到浅棕色透明的胶粘剂组份。
固化剂(乙组)组份：
在低温10℃以下，将正丁基黄原酸锌加入到四异氰酸脂中搅拌4小时，再加入活性氧化镁，然后缓慢升温至25℃开始搅拌12小时，即得到固化剂(乙组)组份，整个过程应在氮气保护下进行。
性能测试：
1、抗拉伸剪切强度(帆布/帆布)：150℃×2h≥1.7MPa；
2、抗拉伸剪切强度(橡胶/橡胶)：150℃×2h≥1.56MPa；
3、抗拉伸剪切强度(防火板/防火板)：150℃×2h≥1.35MPa；
4、难燃性：酒精喷灯燃烧，续燃时间＜0.1秒；
5、贮存稳定性：静放三个月，无分层、凝胶现象；
6、适用期：40分钟内不发生凝胶；
7、固化起始时间：45分钟后开始发生凝胶，粘度增大。
将上述胶粘剂用于包头钢铁公司的输送带上进行接头粘接试验，该输送带在180℃的环境下使用三个月未见开胶及粘接部位损坏的现象。

Claims (1)

1、一种耐高温输送带难燃胶粘剂，其特征是该胶粘剂包括胶粘剂(甲组)和固化剂(乙组)两个组份，其中：
胶粘剂(甲组)是由下述重量份的原料制成的：含羧基的聚氯丁二烯80-100份、三氯乙烯450-600份、烷基酚醛树脂30-80份、氢氧化铝4-6份、氧氧化镁6-8份、1·1·1-三氯乙烷140-320份、乙醇0.5-2份、异丙醇5-20份；
固化剂(乙组)是由下述重量份的原料制成的：四异氰酸脂8-10份、正丁基黄原酸锌0.2-0.6份、活性氧化镁0.6-5份。
CNB021086605A 2002-04-12 2002-04-12 耐高温输送带难燃胶粘剂 Expired - Fee Related CN1164708C (zh)