CN1311280A - Water-proof adhesive and method for mounting mosaic glazed tile onto ceiling - Google Patents
Water-proof adhesive and method for mounting mosaic glazed tile onto ceiling Download PDFInfo
- Publication number
- CN1311280A CN1311280A CN 00110160 CN00110160A CN1311280A CN 1311280 A CN1311280 A CN 1311280A CN 00110160 CN00110160 CN 00110160 CN 00110160 A CN00110160 A CN 00110160A CN 1311280 A CN1311280 A CN 1311280A
- Authority
- CN
- China
- Prior art keywords
- water
- proof
- cement
- proof adhesive
- ceiling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
This invention nrelates to water-proof adhesive and method for mounting mosaic glazed tile onto ceiling. The ratio of components are: organo-silicic liquid: water: water glass =1:8:1. And cement water-proof materials is composed of (wt. ratio): cement: sands: water-proof adhesive=1.5:1.5:1. The construction procedure are: first mixing organo silicic liquid and water evenly and then adding water glass and mixing then evenly for prepn. of water-proof adhesive; and then mixing cement and sands evenly, the adding water-proof adhesive to produce paste and so cement water proof material is produced. The procedure for mounting glazed tile is: distributing adhesive, mounting glazed tile. The advantage is solving problems of water leakage from ceiling.
Description
The present invention relates to a kind of water-proof adhesive and with it in the method that ceiling is inlayed ceramic tile, be mainly used in the indoor ceiling of buildings and inlay ceramic tile and waterproof, satisfy the finishing of building and repair kind construction requirement.
The ground of kitchen, toilet and wall were inlayed very generally in the past, and inlayed ceramic tile above the ceiling, and be then unprecedented.Especially ceiling the problem that moisture seepage leaks often occurs and happens occasionally, and handles and be difficult to eradicate, and has become the long-standing problem in the daily life, treats that suddenly research manages to solve.
The objective of the invention is at the problem of above-mentioned existence and a kind of water-proof adhesive is provided and inlays the method for ceramic tile at ceiling with it.The objective of the invention is by add water-proof adhesive in cement and fine sand mixture, the formation waterproofing membrane is realized.
Water-proof adhesive of the present invention mainly is made of by weight following component:
Organosilicon water: water: water glass=1: 8: 1
Cement water-proof of the present invention is got the raw materials ready and mainly is made up of by weight following component:
Cement: fine sand: water-proof adhesive=1.5: 1.5: 1
Its constructional method is:
1, the envrionment temperature of working-yard should be more than 5 degrees centigrade.
2, the preparation water-proof adhesive is got organosilicon water, water mixing and stirring earlier, adds the water glass mixing and stirring again, promptly is mixed with water-proof adhesive;
3, the preparation cement water-proof is got the raw materials ready, and gets cement, fine sand mixing and stirring according to the above ratio, adds water-proof adhesive again and is mixed into pasty state, promptly is mixed with cement water-proof and gets the raw materials ready; This is got the raw materials ready to have and quickens to strengthen the solidified effect.When construction, must after mixing, construct immediately by the consumption requirement by stages, each consumption was finished with interior at 40 minutes in limited time;
4, smooth bright and clean to the ceiling surface requirements, brush one deck water-proof adhesive earlier on its surface, play agglutinating effect in advance;
5, ceramic tile is soaked in water 15 minutes, pull out treat that surface water is done after, spread the thick cement water-proof of 5mm gets the raw materials ready at its back side, be placed on ceiling and want to press with hand on the position of paving, knock smooth gently with wooden stick or rubber mallet then, discharge gas, treated for 10 seconds, can make ceramic tile inhale multiple coincideing and solidify the location that the seasoning of slipping out of the hand is firm with the ceiling surface;
6, when the paving ceramic tile, to will leaving the dilatation joint of 1-2mm between the ceramic tile, heave in case produce internal stress and to come off.
Advantage of the present invention is to utilize the water-proof adhesive of preparation, be implemented in the indoor ceiling of buildings and inlay ceramic tile, have waterproof, decorate, repair kind, health, characteristics such as attractive in appearance, and can thoroughly solve the problem that the ceiling moisture seepage leaks, adopt water-proof adhesive of the present invention, make the ceiling surface form one deck waterproofing membrane, reach the waterproof purpose, its rate of surging is 99%, and it is firm to inlay ceramic tile through evidence at indoor ceiling, weather resistance is strong, does not come off.Constructional method is simple, and the present invention not only is confined to indoor ceiling and inlays ceramic tile, can also widen its range of application, makes it be applied to industry, civilian, indoor and outdoor wall inlaid with porcelain brick.
Describe the present invention in detail below in conjunction with embodiment:
Embodiment 1: water-proof adhesive of the present invention mainly is made of by weight following component:
Organosilicon water: water: water glass=1: 8: 1
Cement water-proof of the present invention is got the raw materials ready and mainly is made up of by weight following component:
Cement: fine sand: water-proof adhesive=1.5: 1.5: 1
Its construction concrete grammar is:
1, the envrionment temperature of working-yard is 15 degrees centigrade.
2, preparation water-proof adhesive: according to the above ratio, get silicon water 1kg, water 8kg mixing and stirring earlier, add water glass 1kg mixing and stirring again, promptly be mixed with water-proof adhesive;
3, the preparation cement water-proof is got the raw materials ready, and gets cement 15kg, fine sand 15kg mixing and stirring according to the above ratio, adds water-proof adhesive 10kg again and is mixed into pasty state, promptly is mixed with cement water-proof and gets the raw materials ready;
4, smooth bright and clean to the ceiling surface requirements, brush one deck water-proof adhesive earlier on its surface, play agglutinating effect in advance, the preparation of water-proof adhesive is with above-mentioned 2;
5, ceramic tile is soaked in water 15 minutes, pull out treat that surface water is done after, spread the thick cement water-proof of 5mm gets the raw materials ready at its back side, be placed on ceiling and want to press with hand on the position of paving, knock smooth gently with wooden stick then, discharge gas, treated for 10 seconds, can make ceramic tile and ceiling surface inhale multiple coincideing and solidify the location that the seasoning of slipping out of the hand is firm;
6, when the paving ceramic tile, leave the dilatation joint of 1.5mm between the ceramic tile.
Claims (2)
1, a kind of water-proof adhesive, it is characterized in that it mainly by following component by weight forming:
Organosilicon water: water: water glass=1: 8: 1;
Its compound method is to get silicon water, water mixing and stirring earlier, adds the water glass mixing and stirring again, promptly is mixed with water-proof adhesive; Envrionment temperature should be more than 5 degrees centigrade.
2, a kind of water-proof adhesive according to claim 1 in the method that ceiling is inlayed ceramic tile, is characterized in that cement water-proof gets the raw materials ready mainly by following component by weight forming with it:
Cement: fine sand: water-proof adhesive=1.5: 1.5: 1;
Its compound method is:
1. get cement, fine sand mixing and stirring according to the above ratio, add water-proof adhesive again and be mixed into pasty state, promptly be mixed with cement water-proof and get the raw materials ready;
2. smooth bright and clean to the ceiling surface requirements, brush one deck water-proof adhesive earlier on its surface, play agglutinating effect in advance;
3. ceramic tile is soaked in water 15 minutes, pull out treat that surface water is done after, spread the thick cement water-proof of 5mm gets the raw materials ready at its back side, be placed on ceiling and want to press with hand on the position of paving, knock smooth gently with wooden stick or rubber mallet then, discharge gas, treated for 10 seconds, can make ceramic tile inhale multiple coincideing and solidify the location that the seasoning of slipping out of the hand is firm with the ceiling surface;
4. when the paving ceramic tile,, heave in case produce internal stress and to come off leaving the dilatation joint of 1-2mm between the ceramic tile;
5. its envrionment temperature should be more than 5 degrees centigrade.