CN1304502C - Curing nanometer building paint from fluoride carbon resin at normal temperature and production thereof - Google Patents
Curing nanometer building paint from fluoride carbon resin at normal temperature and production thereof Download PDFInfo
- Publication number
- CN1304502C CN1304502C CNB2004100499745A CN200410049974A CN1304502C CN 1304502 C CN1304502 C CN 1304502C CN B2004100499745 A CNB2004100499745 A CN B2004100499745A CN 200410049974 A CN200410049974 A CN 200410049974A CN 1304502 C CN1304502 C CN 1304502C
- Authority
- CN
- China
- Prior art keywords
- coating
- paint
- agent
- nano
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
Project | Index | The method of inspection | ||||
Embodiment 1 | Embodiment 2 | Embodiment 3 | ||||
The shock-resistant kg.cm of gloss sticking power (method of drawing a circle) level hardness (fork method) | 90 1 0.65 50 | 90 1 0.65 50 | 90 1 0.65 50 | GB/T9754 GB/T9286 GB/T6739 GB/T1732 | ||
The heatproof difference changes and abrasion resistance | Can normally use 12000 paint films not have breakage in-40 ℃~140 ℃ scopes | GB/T1765 | ||||
Chemical proofing | 10% sulfuric acid, 10% hydrochloric acid, 10% sodium hydroxide, 10% ammoniacal liquor toluene | The unchanged paint film of the unchanged paint film of the unchanged paint film of the unchanged paint film of paint film is unchanged | The unchanged paint film of the unchanged paint film of the unchanged paint film of the unchanged paint film of paint film is unchanged | The unchanged paint film of the unchanged paint film of the unchanged paint film of the unchanged paint film of paint film is unchanged | GB/T1765 | |
Salt spray resistance experiment 2000 hours | Paint film is non-foaming, do not come off | GB/T1765 | ||||
The artificial accelerated aging experiment | 2000 hours | Paint film loss of gloss rate 11%, 2 grades of variable colors | GB/T1765 | |||
5000 hours | Paint film loss of gloss rate 25%, paint film does not have efflorescence, and variable color is that 2 grades (value of chromatism 3.2) do not have be full of cracks and other catabiosis | GB/T1865 |
Claims (10)