CN103614019A - Fluorocarbon coating for external wall and construction process of fluorocarbon coating - Google Patents
Fluorocarbon coating for external wall and construction process of fluorocarbon coating Download PDFInfo
- Publication number
- CN103614019A CN103614019A CN201310614043.4A CN201310614043A CN103614019A CN 103614019 A CN103614019 A CN 103614019A CN 201310614043 A CN201310614043 A CN 201310614043A CN 103614019 A CN103614019 A CN 103614019A
- Authority
- CN
- China
- Prior art keywords
- mixture
- mass parts
- agent
- exterior wall
- fluorocarbon coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a building coating, and particularly relates to a fluorocarbon coating for an external wall. The fluorocarbon coating for the external wall comprises a mixture A and a mixture B, wherein the mass ratio of the mixture A to the mixture B is 10:1; the mixture A comprises the following substances in percentage by mass: 50%-60% of fluorocarbon resin, 18%-22% of fillers, 2%-3% of pigments, 0.5%-0.8% of auxiliary agents and the balance of solvents; the mixture B comprises the following substances in percentage by mass: 60%-70% of anti-yellowing polyisocyanate and 30%-40% of butyl ester. The fluorocarbon coating disclosed by the invention solves the problem of lower weather resistance of the fluorocarbon coating.
Description
Technical field
The present invention relates to a kind of building coating, specifically relate to a kind of fluorocarbon coating for exterior wall; The invention still further relates to a kind of manufacture and construction technology of fluorocarbon coating.
Background technology
In recent years, develop rapidly along with the building decorating industry of China's economy, environmental stress also gets up more serious, and people are increasingly strict and optimization to various coating specifications functional, decorative and protective building coating, and particularly the anti-dirty performance for exterior coating has had higher requirement.
Fluorocarbon coating is a kind of take the coating that fluorocarbon resin is base-material, and it has high-insulation, and paint film molecular structure is fine and close, demonstrates good not adhesivity, low surface tension, low friction and scolds water, scolds oil, scolds the performances such as dirt.Chemically showing as good thermostability and unreactiveness, be more 20 years its outdoor work-ing life, considerably beyond general coating.
Existing fluorocarbon coating ubiquity weathering resistance a little less than.
Summary of the invention
The object of the invention is, a kind of fluorocarbon coating for exterior wall is provided; This fluorocarbon coating be take fluorocarbon resin as base-material; adding functional control auxiliary agent, weather-proof level color stuffing etc. is prepared from; have excellent weathering resistance, pollution resistance, erosion resistance and chemical-resistant, can be building provides long-effective protection and the foofaraw effect of 20 years.
The present invention is achieved through the following technical solutions above-mentioned purpose:
For a fluorocarbon coating for exterior wall, it contains mixture A, mixture B, and the mass ratio of mixture A and mixture B is 10:1;
Described mixture A is comprised of the material of following mass percent: 50～60% fluorocarbon resins, and 18～22% fillers, 2～3% pigment, 0.5～0.8% auxiliary agent, all the other are solvent;
Described mixture B is comprised of the material of following mass percent: 60～70% polymeric polyisocyanates of resistance to xanthochromia, 30～40% butyl esters.
Further, described filler is a kind of in water-ground limestone, light Kaolin, barium sulfate, mica powder, talcum powder or its mixture.
Further, described pigment is Rutile type Titanium Dioxide.
Further, described auxiliary agent contains organobentonite, wetting agent, defoamer, dispersion agent, flow agent, anti-settling agent.Preferably, described auxiliary agent also contains siccative, promotor, feel wax powder, sand streak wax powder, mute powder, aluminium powder and aligns agent, adhesion promoter, anti-flood and anti-float agent.
Further, described solvent is the mixture that in ketones solvent, butyl ester kind solvent, one or both and benzene kind solvent form; Wherein to account for the mass percent of mixture A be 4.0～5.0% to benzene kind solvent.
The present invention also provides a kind of preparation method of the fluorocarbon coating for exterior wall.
The preparation method of the described fluorocarbon coating for exterior wall, comprises the following steps:
1) mixture A preparation: by 4.0～5.0 mass parts benzene kind solvents, 0.5～0.8 mass parts auxiliary agent mix and blend 5～10 minutes, rotating speed was 500～600r/min; Then add 50～60 mass parts fluorocarbon resins, stir 20～30 minutes, rotating speed is 700～800r/min; And then add 18～22 mass parts fillers, 2～3 mass parts pigment, stir 30～40 minutes, rotating speed is 800～1000r/min; Then add gradually a kind of or its mixture in 9.2～25.5 mass parts ketones solvents, butyl ester kind solvent, stir until the fineness of mixture reaches 25 microns, viscosity is 70～110 pascal seconds, obtains 100 mass parts mixture A;
2) mixture B preparation: 60～70 mass parts polymeric polyisocyanates of resistance to xanthochromia, 30～40 mass parts butyl esters are mixed, obtain 100 mass parts mixture B;
3) by mixture A and mixture B in mass ratio 10:1 mix.
Further, described filler is a kind of in water-ground limestone, light Kaolin, barium sulfate, mica powder, talcum powder or its mixture.
Further, described pigment is Rutile type Titanium Dioxide.
Further, described auxiliary agent contains organobentonite, wetting agent, defoamer, dispersion agent, flow agent, anti-settling agent.Preferably, described auxiliary agent also contains siccative, promotor, feel wax powder, sand streak wax powder, mute powder, aluminium powder and aligns agent, adhesion promoter, anti-flood and anti-float agent.
The present invention also provides a kind of exterior wall coating decoration method.
A kind of described exterior wall coating decoration method, comprises the following steps:
1) base treatment
Clean metope substrate, metope criticize fill whole; Criticize and scrape putty of the thick end of the first layer exterior wall; Lay cracking resistance glass fiber net; Criticize and scrape putty of the thick end of second layer exterior wall; Criticize and scrape the special-purpose fine flour putty of fluorine carbon; Criticize and scrape fluorine carbon special-purpose polishing putty; Grinding process, water seasoning, until alkalescence, water ratio and intensity are qualified; Detect construction environment condition, do not make application position temporary protection;
2) coating decoration
The fluorocarbon coating for exterior wall that application is above-mentioned; Application fluorine carbon finishing paint; Construction quality checks, repairs.
Relative prior art, the present invention has excellent weathering resistance, pollution resistance, erosion resistance and chemical-resistant for the fluorocarbon coating of exterior wall, and can be building provides long-effective protection and the foofaraw effect of 20 years.
Embodiment
Embodiment mono-
Mixture A preparation: by 4.65 mass parts dimethylbenzene, 0.5 mass parts auxiliary agent mix and blend 5 minutes, rotating speed was 600r/min; Then add 50 mass parts fluorocarbon resins, disturb 20 minutes, rotating speed is 800r/min; And then add 22 mass parts water-ground limestones, 3 mass parts Rutile type Titanium Dioxides, disturb 30 minutes, rotating speed is 1000r/min; Then add gradually 19.85 mass parts hexones, stir until the fineness of mixture reaches 25 microns, viscosity is 70～110 pascal seconds, obtains 100 mass parts mixture A;
Mixture B preparation: the 60 mass parts polymeric polyisocyanates of resistance to xanthochromia, 40 mass parts butyl esters are mixed, obtain 100 mass parts mixture B;
By mixture A and mixture B in mass ratio 10:1 mix the fluorocarbon coating that can obtain for exterior wall.
Described auxiliary agent is comprised of following material: BT-838S organobentonite, Hensic H-423 wetting agent, Hensic H-231 defoamer, Hensic H-4200 dispersion agent, Hensic H-126 flow agent, 6900-20X anti-settling agent.
Embodiment bis-
Mixture A preparation: by 4 mass parts hexanaphthenes, 0.8 mass parts auxiliary agent mix and blend 5 minutes, rotating speed was 500r/min; Then add 60 mass parts fluorocarbon resins, disturb 30 minutes, rotating speed is 800r/min; And then add 18 mass parts fillers, 2 mass parts Rutile type Titanium Dioxides, disturb 30 minutes, rotating speed is 1000r/min; Then add gradually 15.2 mass parts hexones, stir until the fineness of mixture reaches 25 microns, viscosity is 70～110 pascal seconds, obtains 100 mass parts mixture A;
Mixture B preparation: the 70 mass parts polymeric polyisocyanates of resistance to xanthochromia, 30 mass parts butyl esters are mixed, obtain 100 mass parts mixture B;
By mixture A and mixture B in mass ratio 10:1 can obtain the fluorocarbon coating for exterior wall.
Described auxiliary agent is comprised of following material: BT-838S organobentonite, BT-838B organobentonite, Hensic H-423 wetting agent, Hensic H-231 defoamer, Hensic H-4200 dispersion agent, Hensic H-210 defoamer, Hensic H-6500 wetting agent, Hensic H-126 flow agent, Hensic H-143 flow agent, BYK104s dispersion agent, BYK066 defoamer, BYK306 flow agent, 6900-20X anti-settling agent.
Described filler is comprised of water-ground limestone, light Kaolin, barium sulfate.
Embodiment tri-
Mixture A preparation: by 4.5 mass parts dimethylbenzene, 0.6 mass parts auxiliary agent mix and blend 8 minutes, rotating speed was 550r/min; Then add 55 mass parts fluorocarbon resins, disturb 25 minutes, rotating speed is 760r/min; And then add 19 mass parts fillers, 2 mass parts Rutile type Titanium Dioxides, disturb 35 minutes, rotating speed is 900r/min; Then add gradually 18.9 mass parts pimelinketone, stir until the fineness of mixture reaches 25 microns, viscosity is 70～110 pascal seconds, obtains 100 mass parts mixture A;
Mixture B preparation: the 65 mass parts polymeric polyisocyanates of resistance to xanthochromia, 35 mass parts butyl esters are mixed, obtain 100 mass parts mixture B;
By mixture A and mixture B in mass ratio 10:1 can obtain the fluorocarbon coating for exterior wall.
Described auxiliary agent is comprised of following material: BT-838S organobentonite, BT-838B organobentonite, Hensic H-423 wetting agent, Hensic H-231 defoamer, Hensic H-4200 dispersion agent, Hensic H-210 defoamer, Hensic H-6500 wetting agent, Hensic H-126 flow agent, Hensic H-143 flow agent, BYK104s dispersion agent, BYK066 defoamer, BYK306 flow agent, 6900-20X anti-settling agent, Hensic MH5220 anti-settling agent, 7410 siccative.
Described filler is comprised of mica powder, talcum powder.
Embodiment tetra-
Mixture A preparation: by 5.0 mass parts hexanaphthenes, 0.7 mass parts auxiliary agent mix and blend 5 minutes, rotating speed was 600r/min; Then add 57 mass parts fluorocarbon resins, stir 30 minutes, rotating speed is 800r/min; And then add 20 mass parts fillers, 2.5 mass parts Rutile type Titanium Dioxides, stir 30 minutes, rotating speed is 1000r/min; Then add gradually 14.8 mass parts pimelinketone, stir until the fineness of mixture reaches 25 microns, viscosity is 70～110 pascal seconds, obtains 100 mass parts mixture A;
Mixture B preparation: the 66 mass parts polymeric polyisocyanates of resistance to xanthochromia, 34 mass parts butyl esters are mixed, obtain 100 mass parts mixture B;
By mixture A and mixture B in mass ratio 10:1 can obtain the fluorocarbon coating for exterior wall.
Described auxiliary agent is comprised of following material: BT-838S organobentonite, BT-838B organobentonite, Hensic H-423 wetting agent, Hensic H-231 defoamer, Hensic H-4200 dispersion agent, Hensic H-210 defoamer, Hensic H-6500 wetting agent, Hensic H-126 flow agent, Hensic H-143 flow agent, BYK104s dispersion agent, BYK066 defoamer, BYK306 flow agent, 6900-20X anti-settling agent, Hensic MH5220 anti-settling agent, 7410 siccative, HI-54K promotor, tetrafluoroethylene.
Described filler is comprised of water-ground limestone, light Kaolin, barium sulfate, mica powder, talcum powder.
Embodiment five
Mixture A preparation: by 4.0 mass parts dimethylbenzene, 0.5 mass parts auxiliary agent mix and blend 8 minutes, rotating speed was 600r/min; Then add 50 mass parts fluorocarbon resins, disturb 23 minutes, rotating speed is 800r/min; And then add 18 mass parts fillers, 2 mass parts Rutile type Titanium Dioxides, disturb 33 minutes, rotating speed is 850r/min; Then add gradually 25.5 mass parts butylacetates, stir until the fineness of mixture reaches 25 microns, viscosity is 70～110 pascal seconds, obtains 100 mass parts mixture A;
Mixture B preparation: the 62 mass parts polymeric polyisocyanates of resistance to xanthochromia, 38 mass parts butyl esters are mixed, obtain 100 mass parts mixture B;
By mixture A and mixture B in mass ratio 10:1 can obtain the fluorocarbon coating for exterior wall.
Described auxiliary agent is comprised of following material: BT-838S organobentonite, BT-838B organobentonite, Hensic H-423 wetting agent, Hensic H-231 defoamer, Hensic H-4200 dispersion agent, Hensic H-210 defoamer, Hensic H-6500 wetting agent, Hensic H-126 flow agent, Hensic H-143 flow agent, BYK104s dispersion agent, BYK066 defoamer, BYK306 flow agent, 6900-20X anti-settling agent, Hensic MH5220 anti-settling agent, 7410 siccative, HI-54K promotor, tetrafluoroethylene, 25 μ sand streak wax powder, 202 matting agents (mute powder), Hensic H-212 defoamer, SP-640 aluminium powder aligns agent.
Described filler is comprised of light Kaolin, barium sulfate, mica powder, talcum powder.
Embodiment six
Mixture A preparation: by 5.0 mass parts hexanaphthenes, 0.8 mass parts auxiliary agent mix and blend 7 minutes, rotating speed was 600r/min; Then add 60 mass parts fluorocarbon resins, stir 30 minutes, rotating speed is 800r/min; And then add 22 mass parts fillers, 3 mass parts Rutile type Titanium Dioxides, stir 40 minutes, rotating speed is 1000r/min; Then add gradually 9.2 mass parts butylacetates, stir until the fineness of mixture reaches 25 microns, viscosity is 70～110 pascal seconds, obtains 100 mass parts mixture A;
Mixture B preparation: the 70 mass parts polymeric polyisocyanates of resistance to xanthochromia, 30 mass parts butyl esters are mixed, obtain 100 mass parts mixture B;
By mixture A and mixture B in mass ratio 10:1 can obtain the fluorocarbon coating for exterior wall.
Described auxiliary agent is comprised of following material: BT-838S organobentonite, BT-838B organobentonite, Hensic H-423 wetting agent, Hensic H-231 defoamer, Hensic H-4200 dispersion agent, Hensic H-210 defoamer, Hensic H-6500 wetting agent, Hensic H-126 flow agent, Hensic H-143 flow agent, BYK104s dispersion agent, BYK066 defoamer, BYK306 flow agent, 6900-20X anti-settling agent, Hensic MH5220 anti-settling agent, 7410 siccative, HI-54K promotor, tetrafluoroethylene, 25 μ sand streak wax powder, 202 matting agents (mute powder), Hensic H-212 defoamer, SP-640 aluminium powder aligns agent, ADP adhesion promoter, Hensic H-403s anti-flood and anti-float agent.
Described filler is comprised of light Kaolin, barium sulfate, mica powder, talcum powder.
Embodiment seven
Mixture A preparation: by 4.6 mass parts hexanaphthenes, 0.7 mass parts auxiliary agent mix and blend 5 minutes, rotating speed was 600r/min; Then add 51 mass parts fluorocarbon resins, stir 27 minutes, rotating speed is 800r/min; And then add 19 mass parts fillers, 2 mass parts Rutile type Titanium Dioxides, stir 37 minutes, rotating speed is 1000r/min; Then the mixture being comprised of butylacetate, pimelinketone that adds gradually 22.7 mass parts, stirs until the fineness of mixture reaches 25 microns, and viscosity is 70～110 pascal seconds, obtains 100 mass parts mixture A;
Mixture B preparation: the 69 mass parts polymeric polyisocyanates of resistance to xanthochromia, 31 mass parts butyl esters are mixed, obtain 100 mass parts mixture B;
By mixture A and mixture B in mass ratio 10:1 can obtain the fluorocarbon coating for exterior wall.
Described auxiliary agent is comprised of following material: BT-838B organobentonite, Hensic H-423 wetting agent, Hensic H-231 defoamer, Hensic H-4200 dispersion agent, Hensic H-126 flow agent, 6900-20X anti-settling agent, 7410 siccative, HI-54K promotor, tetrafluoroethylene, 50 μ sand streak wax powder, 202 matting agents (mute powder), SP-640 aluminium powder aligns agent, ADP adhesion promoter, Hensic H-403s anti-flood and anti-float agent.
Described filler is comprised of light Kaolin, barium sulfate, mica powder, talcum powder.
The product performance of the fluorocarbon coating for exterior wall of embodiment mono-to seven all reach following index (adopting HG/T3792-2005 standard):
Embodiment eight
An exterior wall coating decoration method, comprises the following steps:
1) base treatment
Clean metope substrate, metope criticize fill whole; Criticize and scrape putty of the thick end of the first layer exterior wall; Lay cracking resistance glass fiber net; Criticize and scrape putty of the thick end of second layer exterior wall; Criticize and scrape the special-purpose fine flour putty of fluorine carbon; Criticize and scrape fluorine carbon special-purpose polishing putty; Grinding process, water seasoning, until alkalescence, water ratio and intensity are qualified; Detect construction environment condition, do not make application position temporary protection;
2) coating decoration
Application embodiment mono-to seven is a kind of fluorocarbon coating for exterior wall wherein; Application fluorine carbon finishing paint; Construction quality checks, repairs.
The above embodiment has only expressed part embodiment of the present invention, and it describes comparatively concrete and detailed, but can not therefore be interpreted as the restriction to the scope of the claims of the present invention.It should be pointed out that for the person of ordinary skill of the art, without departing from the inventive concept of the premise, can also make some distortion and improvement, these all belong to protection scope of the present invention.Therefore, the protection domain of patent of the present invention should be as the criterion with claims.
Claims (10)
1. for a fluorocarbon coating for exterior wall, it is characterized in that: it contains mixture A, mixture B, the mass ratio of mixture A and mixture B is 10:1;
Described mixture A is comprised of the material of following mass percent: 50～60% fluorocarbon resins, and 18～22% fillers, 2～3% pigment, 0.5～0.8% auxiliary agent, all the other are solvent;
Described mixture B is comprised of the material of following mass percent: 60～70% polymeric polyisocyanates of resistance to xanthochromia, 30～40% butyl esters.
2. the fluorocarbon coating for exterior wall according to claim 1, is characterized in that: described filler is a kind of in water-ground limestone, light Kaolin, barium sulfate, mica powder, talcum powder or its mixture.
3. the fluorocarbon coating for exterior wall according to claim 1, is characterized in that: described pigment is Rutile type Titanium Dioxide.
4. the fluorocarbon coating for exterior wall according to claim 1, is characterized in that: described auxiliary agent contains organobentonite, wetting agent, defoamer, dispersion agent, flow agent, anti-settling agent.
5. the fluorocarbon coating for exterior wall according to claim 4, is characterized in that: described auxiliary agent also contains siccative, promotor, feel wax powder, sand streak wax powder, mute powder, aluminium powder and aligns agent, adhesion promoter, anti-flood and anti-float agent.
6. the fluorocarbon coating for exterior wall according to claim 1, is characterized in that: described solvent is the mixture that in ketones solvent, butyl ester kind solvent, one or both and benzene kind solvent form; Wherein to account for the mass percent of mixture A be 4.0～5.0% to benzene kind solvent.
7. for a preparation method for the fluorocarbon coating of exterior wall, it is characterized in that, comprise the following steps:
1) mixture A preparation: by 4.0～5.0 mass parts benzene kind solvents, 0.5～0.8 mass parts auxiliary agent mix and blend 5～10 minutes, rotating speed was 500～600r/min; Then add 50～60 mass parts fluorocarbon resins, stir 20～30 minutes, rotating speed is 700～800r/min; And then add 18～22 mass parts fillers, 2～3 mass parts pigment, stir 30～40 minutes, rotating speed is 800～1000r/min; Then add gradually a kind of or its mixture in 9.2～25.5 mass parts ketones solvents, butyl ester kind solvent, stir until the fineness of mixture reaches 25 microns, viscosity is 70～110 pascal seconds, obtains 100 mass parts mixture A;
2) mixture B preparation: 60～70 mass parts polymeric polyisocyanates of resistance to xanthochromia, 30～40 mass parts butyl esters are mixed, obtain 100 mass parts mixture B;
3) by mixture A and mixture B in mass ratio 10:1 mix.
8. the preparation method of the fluorocarbon coating for exterior wall according to claim 7, is characterized in that: described filler is a kind of in water-ground limestone, light Kaolin, barium sulfate, mica powder, talcum powder or its mixture.
9. the preparation method of the fluorocarbon coating for exterior wall according to claim 7, is characterized in that: described pigment is Rutile type Titanium Dioxide; Described auxiliary agent contains organobentonite, wetting agent, defoamer, dispersion agent, flow agent, anti-settling agent.
10. an exterior wall coating decoration method, is characterized in that, comprises the following steps:
1) base treatment
Clean metope substrate, metope criticize fill whole; Criticize and scrape putty of the thick end of the first layer exterior wall; Lay cracking resistance glass fiber net; Criticize and scrape putty of the thick end of second layer exterior wall; Criticize and scrape the special-purpose fine flour putty of fluorine carbon; Criticize and scrape fluorine carbon special-purpose polishing putty; Grinding process, water seasoning, until alkalescence, water ratio and intensity are qualified; Detect construction environment condition, do not make application position temporary protection;
2) coating decoration
The fluorocarbon coating for exterior wall described in application claim 1 to 6 any one; Application fluorine carbon finishing paint; Construction quality checks, repairs.