CN1262284A - 制备高分子吸水树脂的方法 - Google Patents
制备高分子吸水树脂的方法 Download PDFInfo
- Publication number
- CN1262284A CN1262284A CN 99112072 CN99112072A CN1262284A CN 1262284 A CN1262284 A CN 1262284A CN 99112072 CN99112072 CN 99112072 CN 99112072 A CN99112072 A CN 99112072A CN 1262284 A CN1262284 A CN 1262284A
- Authority
- CN
- China
- Prior art keywords
- preparing
- drying
- molecular resin
- hydroscopic high
- organic alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种制备高分子吸水树脂的方法,由丙烯酸及其盐经过水溶液聚合反应,制得含水树脂胶体,含水树脂干燥前用有机醇进行处理。该方法解决了现有方法中存在的干燥难、粉碎难等缺点,并且有效地提高了产品的吸水性能,具有较高的推广价值。
Description
本发明涉及高分子吸水树脂，特别涉及以水溶液聚合法制备交联聚丙烯酸盐型高分子吸水性树脂的制备方法。
高分子吸水性树脂是新型功能高分子材料，具有广泛的用途。从品种来说，主要有接枝淀粉类(淀粉与丙烯酸盐接技共聚合体交联物)和交联聚丙烯酸盐两大类。其中，后者抗离子性相对较强，稳定性高，不易霉变，是发展前景十分广阔的产品。
虽然交联聚丙烯酸盐型高吸水性树脂在八十年代就已问世，但是其制造方法却仍然存在着较大的难点问题未得到解决，即由丙烯酸及其盐经过水溶液聚合反应制得的含水树脂胶体很难干燥和粉碎。目前常用的处理方法，如1997年美国DoW化学公司的D.E.Henton等研究人员发表的研究成果中提到，把含水树脂胶体先切成薄片，然后在100℃以上的温度连续干燥约20小时，而且产物质地坚韧，难以粉碎，吸水性能不高，吸去离子水为400～600ml/g，吸生理盐水为35～60ml/g。
由于交联聚丙烯酸盐型高吸水性树脂制备方法存在着上述难点问题，所以至今很难形成规模化生产，严重阻碍着这种新型材料的推广应用。
本发明的目的是提出了一种交联聚丙烯酸盐型高吸水性树脂的新型制备方法，不仅解决了含水树脂胶体难干燥，难粉碎的问题，而且还使该产品的吸水性能大幅度提高，便于规模化生产，利于该产品的推广应用。
本发明是通过如下的技术方案实现的：
一种制备高分子吸水树脂的方法，由丙烯酸及其盐经过水溶液聚合反应，制得含水树脂胶体，经干燥，粉碎后制得，其主要技术特点是含水树脂干燥前用有机醇进行处理。
本发明所述有机醇最好是用甲醇；甲醇的含水量最好在25％以下；处理方法是用有机醇进行萃取。萃取时间为15～25小时，萃取时可以在常温下进行。其它工艺同现有技术。
本发明具有如下的优点：
(1)经过处理的树脂易干燥，干燥后的产物硬度大大降低，而且已无韧性，易于粉碎加工；(2)产品吸水性能有显著提高，吸去离子水为1200ml/g以上；吸生理盐水为85ml/g以上；(3)便于规模化生产，有利于该产品的推广应用。
下面结合实施例对本发明作进一步说明：
实施例1：
在50L的搪玻璃反应釜中投入1.5％的聚乙烯醇水溶液10.50Kg，丙烯酸6.5Kg搅拌，通冷却水，控制温度在20-30℃，滴加30％液碱9Kg，继续搅拌5分钟后，加入0.61％N，N’-亚甲基双丙烯酰胺水溶液0.50Kg，升温至50℃，滴加0.88％过硫酸钾水溶液0.70Kg，然后升温至55℃，继续搅拌90分钟，将反应液装入直径40mm的聚乙烯薄膜筒中，将筒口扎紧后放入60-65℃恒温水浴槽中，6小时后将已聚合好的棒状胶体取出，剥下聚乙烯薄膜，得到含水胶体状树脂26.9Kg。
将上述胶体(约含水65％)切成厚度约5mm片状，放入盛有20.25Kg工业甲醇的容器中浸泡，每小时搅拌一次，10小时后更换10Kg新甲醇继续萃取10小时，取出，在110℃干燥5小时，取出冷却，用锤式粉碎机粉碎至80～160目。
实施例2：
以与实施例1同样的方法制得的胶体29.5Kg(含水65％)切成厚度约5mm片状，放入盛有35Kg已含水10％的甲醇容器中浸泡，每小时搅拌一次，10小时后更换15Kg新甲醇继续萃取10小时，取出切片，烘干、冷却，粉碎至成品。
Claims (6)
1、一种制备高分子吸水树脂的方法，由丙烯酸及其盐经过水溶液聚合反应，制得含水树脂胶体，经干燥，粉碎后制得，其特征在于含水树脂干燥前用有机醇进行处理。
2.根据权利要求1所述的方法，其特征在于处理用的有机醇是甲醇。
3.根据权利要求1或者2所述的方法，其特征在于甲醇的含水量在25％以下。
4.根据权利要求1所述的方法，其特征在于含水树脂干燥前用有机醇进行萃取。
5.根据权利要求4所述的方法，其特征在于萃取时间为15～25小时。
6.根据权利要求4，5所述的方法，其特征在于萃取时在常温下进行。