CN1259451C - 常温磷化液 - Google Patents

常温磷化液 Download PDF

Info

Publication number
CN1259451C
CN1259451C CN 02135551 CN02135551A CN1259451C CN 1259451 C CN1259451 C CN 1259451C CN 02135551 CN02135551 CN 02135551 CN 02135551 A CN02135551 A CN 02135551A CN 1259451 C CN1259451 C CN 1259451C
Authority
CN
China
Prior art keywords
nitrate
present
liquid
sodium
normal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 02135551
Other languages
English (en)
Other versions
CN1401820A (zh
Inventor
于安军
王子健
施茜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China National Heavy Duty Truck Group Taian Wuyue Special Vehicle Co Ltd
China National Heavy Duty Truck Group Co Ltd
Original Assignee
China National Heavy Duty Truck Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by China National Heavy Duty Truck Group Co Ltd filed Critical China National Heavy Duty Truck Group Co Ltd
Priority to CN 02135551 priority Critical patent/CN1259451C/zh
Publication of CN1401820A publication Critical patent/CN1401820A/zh
Application granted granted Critical
Publication of CN1259451C publication Critical patent/CN1259451C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明属于表面化学的技术领域，特别涉及一种对钢铁表面进行磷化处理的常温磷化液。适用于汽车等大型设备在比较恶劣的环境下使用。本发明的常温磷化液，是由以下物质按重量百分比组成，磷酸2.0-4.0%，氧化锌0.4-0.6%，硝酸锌0.5-1.5%，硝酸镍3.0-5.0%，硝酸锰2.0-4.0%，硼氟酸钠0.2-1.0%，氯酸钠2.0-3.0%，柠檬酸0.5-2.0%，软化水，余量。本发明的常温磷化液具有磷化液稳定性好、成膜时间长、成膜强度大、耐蚀性强的优点。

Description

常温磷化液
(一)技术领域
本发明属于表面化学的技术领域，特别涉及一种对钢铁表面进行磷化处理的常温磷化液。
(二)背景技术
对钢铁表面进行磷化处理，传统使用的磷化液使用温度高、耗能大、时间长、成本高。特别对于象汽车底盘及零部件等大型工件，如果进行中、高温磷化，对一些中小企业来说，比较困难。如中国专利CN1076225、CN1077757就公开了2种进行分步处理的黑色化液及其工艺，分步处理虽可获得黑色磷化膜，但成膜比较疏松，且工艺过程长，成本高。如中国专利CN1231705公开磷化液及共其工艺，其使用温度为15-75度，成本比较高，成膜时间长，成膜疏松，耐蚀性差，不适合象汽车底盘这样工作在环境比较恶劣的工件。
(三)发明内容
本发明的目的在于提供一种磷化液稳定性好、成膜时间长、成膜强度大、耐蚀性强的常温磷化液。
本发明的目的是这样实现的：
本发明的常温磷化液，是由以下物质按重量百分比组成，
磷酸            2.0-4.0％
氧化锌          0.4-0.6％
硝酸锌          0.5-1.5％
硝酸镍          3.0-5.0％
硝酸锰            2.0-4.0％
硼氟酸钠          0.2-1.0％
氯酸钠            2.0-3.0％
柠檬酸            0.5-2.0％
软化水            余量
本发明的常温磷化液，由于加入了复合加速剂和复合钝化剂——硝酸镍、硝酸锰、硼氟酸钠和氯酸钠，使磷化膜与工件的结合速度快，结合更牢固。使磷化液磷化速度加快，并且使成膜和强度大。
本发明的常温磷化液的生产方法，首先将氧化锌用少量水混合湿润，加入磷酸，溶解完全后，再加入其它的原料，搅拌均匀即可。
本发明的常温磷化液，其使用方法也比较简单，被处理工件先要经预处理、脱脂、表调等工艺，使工件表面无油、无锈及脏物，采用浸渍或喷淋方法施工，在常温下处理3-5分钟，无需加热，节省能源，操作方便。被处理的工件成膜致密、均匀、连续，成膜时间短，成膜强度大，能够满足汽车等工件的要求。
因此，本发明的常温磷化液具有磷化液稳定性好、成膜时间长、成膜强度大、耐蚀性强的优点。
(四)具体实施方式
实施例1：
本发明的常温磷化液，是由以下物质按重量百分比组成：
磷酸            4.0％
氧化锌          0.55％
硝酸锌          1.5％
硝酸镍          3.0％
硝酸锰          3.5％
硼氟酸钠        0.8％
氯酸钠          2.5％
柠檬酸          2.0％
软化水          余量
实施例2：本发明的常温磷化液，是由以下物质按重量百分比组成：
磷酸            3.0％
氧化锌          0.5％
硝酸锌          1.0％
硝酸镍          3.5％
硝酸锰          3.0％
硼氟酸钠        0.5％
氯酸钠          2.5％
柠檬酸          1.0％
软化水          余量

Claims (3)

1.一种常温磷化液，其特征在于：是由以下物质按重量百分比组成，
磷酸      2.0-4.0％
氧化锌    0.4-0.6％
硝酸锌    0.5-1.5％
硝酸镍    3.0-5.0％
硝酸锰    2.0-4.0％
硼氟酸钠  0.2-1.0％
氯酸钠    2.0-3.0％
柠檬酸    0.5-2.0％
软化水    余量。
2.根据权利要求1所述的常温磷化液，其特征在于：是由以下物质按重量百分比组成：
磷酸      4.0％
氧化锌    0.55％
硝酸锌    1.5％
硝酸镍    3.0％
硝酸锰    3.5％
硼氟酸钠  0.8％
氯酸钠    2.5％
柠檬酸    2.0％
软化水    余量。
3.根据权利要求1所述的常温磷化液，其特征在于：是由以下物质按重量百分比组成：
磷酸      3.0％
氧化锌    0.5％
硝酸锌    1.0％
硝酸镍    3.5％
硝酸锰    3.0％
硼氟酸钠  0.5％
氯酸钠    2.5％
柠檬酸    1.0％
软化水    余量
CN 02135551 2002-09-18 2002-09-18 常温磷化液 Expired - Fee Related CN1259451C (zh)