CN1233641A - 稀土激活的碱土金属硼铝酸盐长余辉荧光体 - Google Patents

稀土激活的碱土金属硼铝酸盐长余辉荧光体 Download PDF

Info

Publication number
CN1233641A
CN1233641A CN 98108144 CN98108144A CN1233641A CN 1233641 A CN1233641 A CN 1233641A CN 98108144 CN98108144 CN 98108144 CN 98108144 A CN98108144 A CN 98108144A CN 1233641 A CN1233641 A CN 1233641A
Authority
CN
China
Prior art keywords
long
gram
rare earth
alkaline earth
earth metal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 98108144
Other languages
English (en)
Other versions
CN1101844C (zh
Inventor
赵成久
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGCHUN PHYS INST CHINESE
Original Assignee
CHANGCHUN PHYS INST CHINESE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGCHUN PHYS INST CHINESE filed Critical CHANGCHUN PHYS INST CHINESE
Priority to CN98108144A priority Critical patent/CN1101844C/zh
Publication of CN1233641A publication Critical patent/CN1233641A/zh
Application granted granted Critical
Publication of CN1101844C publication Critical patent/CN1101844C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种稀土激活的碱土金属硼铝酸盐水余辉荧光体,属于发光材料技术领域。以MAl2O4·nB2O3:Eu·Dy表示的这类长余辉荧光体,还可以添加Sb、Ga等元素,也可以加入作为电荷补偿剂的氯化物。本发明的荧光体在紫外300—450nm或可见光经10分钟照射下,在暗室内可见发射520nm左右的绿色余辉光,持续20小时左右。

Description

稀土激活的碱土金属硼铝酸盐长余辉荧光体
本发明属于发光材料技术领域。
以往光致贮能发光材料，采用ZnS:Cu，其余辉仅为30分钟至2小时左右。近年中国专利报道了一系列以碱土铝酸盐为基质的长余辉发光材料，例如日本根本特殊化学株式会社公开的94103944.7和95118116.5《夜光性荧光体》，报道了以M1-xAl2O4-x表示的化合物，M是选自Ca、Sr、Ba中至少一种，可向M中添加Mg、Eu做为活化剂，也可添加共活化剂。
肖志国等(94106023.2)也公开了以碱土金属铝酸盐为主要发光基质，稀土离子Eu、Ce、Tb、Dy和非稀土离子Sb、Sn共激活的多离子激活发光材料，该材料对短波可见光具有很强吸收能力，并可持续12小时以上余辉发光，颜色呈蓝、绿、黄色。顾茗桥(94100482.1)则公开了一种由m(Sr1-xEux)O·nAl2O3·aBaCl2·bCaO表示的含铕夜光材料。迄今尚未有以碱土硼铝酸盐为基质的长余辉光致发光材料的报道。
本发明的目的是以碱土硼铝酸盐为发光基质，由稀土和非稀土离子激活、开发出一系列长余辉发光材料。
本发明长余辉荧光体是由MAl2O4·nB2O3:Eu·Dy表示的化合物晶状荧光体，M是选自Ca、Sr、Ba、Mg或Li中的至少一种以上的金属元素，并添加了Sb、Ga多种元素构成的化合物；在该荧光体中，可加入相当于M表示的金属元素的0.0025摩尔％至25摩尔％的激活剂Eu。还可以加入相当于M表示的金属元素的0.0025摩尔％至25摩尔％的La、Ce、Nd、Pr、Gd、Tb、Dy、Ho、Er、Dm、Ln、Mn、Bi、Sn、Iu、Be当中至少一种作为共激活剂，还可以向荧光体中在向M中加入了Sb、Ga的同时再添加Ca、Sr、Ba、Mg、Li、Na中至少一种以上的氯化物作为电荷补偿剂。
本发明上述荧光体的制造方法如下：
1、称取试剂级物料，用球磨机充分混匀；
2、装入Al2O3坩埚中，在N2、H2或C气氛中1200-1300℃灼烧1-3小时；
3、取出冷却后粉碎过100目筛即得。
本发明经烧结后粉碎100目过筛后得到的粉末荧光体，在紫外300-450nm或可见光经10分钟照射后，在暗室内可见发射520nm左右的绿色余辉光，余辉可持续达20小时左右，指肉眼能够辨其发光。
实施例1：按下列计量称取试剂物料
SrCO3(AR)       147.63克  Al2O3(指定纯)  153克
H3BO3(AR)      20克      Sb2O3(3N)      4克
Eu2O3(AR)      1.85克    Dy2O3(3N)      2.3克
SrCl2·6H2O(AR) 2克
球磨充分混匀，装入Al2O3坩埚中，在氮、氢或碳气氛中1200-1300℃灼烧1-3小时，取出冷却后，粉碎过100目筛即得荧光体。
实施例2：
SrCO3(AR)        147.62克   Al2O3(指定纯)   202克
H3BO3(AR)       19克       Sb2O3(3N)       4克
Eu2O3(4N)       1.85克     Dy2O3(3N)       2.3克
MgCl2·bH2O(AR) 2克
烧制条件同实施例1
实施例3：
SrCO3(AR)    147.62克   Al2O3(指定纯)   255克
H3BO3(AR)   18克       Sb2O3(3N)       4克
Dy2O3(3N)   2.3克      Eu2O3(4N)       1.85克
                          KCl(AR)           2克
烧制条件同实施例1
实施例4：
SrCO3(AR)     147.62克   Al2O3(指定纯)   306克
H3BO3(AR)    17克       Sb2O3(3N)       4克
Eu2O3(4N)    1.85克     Dy2O3(3N)       2.3克
NaCl(AR)        2克
烧制条件同实施例1实施例5：SrCO3(AR)         147.62克  Al2O3(指定纯)  306克H3BO3(AR)        16克      Sb2O3(3N)      4克Eu2O3(4N)        1.85克    Dy2O3(3N)      2.3克LiCl·H2O(AR)     2克烧制条件同实施例1实施例6：SrCO3(AR)         147.62克   Al2O3(指定纯)  510克H3BO3(AR)        15克       Sb2O3(3N)      4克Eu2O3(4N)        1.85克     Dy2O3(3N)      2.3克BaCl2·2H2O(AR)2克烧制条件同实施例1

Claims (4)

1、一种长余辉荧光体，其特征在于它是由MAl2O4·nB2O3:Eu·Dy表示的化合物晶状荧光体，M是选自Ca、Sr、Ba、Mg或Li中的至少一种以上的金属元素，n代表的B2O3含量为0.5＜n＜0.005摩尔。
2、根据权利要求1的荧光体，其特征是可向M中再添加Sb、Ga等多种元素构成的化合物。
3、根据权利要求1的荧光体，其特征是在该荧光体中，可加入相当于M表示的金属元素的0.0025摩尔％至25摩尔％的激活剂Eu，还可以加入上述量La、Ce、Nd、Pr、Gd、Tb、Dy、Ho、Er、Dm、Lu、Mn、Bi、Sn、In或Be当中至少一种作为共激活剂。
4、根据权利要求1或2的荧光体，其特征是在向M中加入了Sb、Ga的同时，再添加Ca、Sr、Ba、Mg、Li、Na中至少一种以上的氯化物。
CN98108144A 1998-04-27 1998-04-27 稀土激活的碱土金属硼铝酸盐长余辉荧光体 Expired - Fee Related CN1101844C (zh)