- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Links
Landscapes
- Paints Or Removers (AREA)
Abstract
本发明涉及一种水基高分子防水涂料,是对乙烯—醋酸乙烯共聚液为基料的防水涂料的改进,利用廉价的乙烯工业下料—乙烯焦油作为改性剂,配以增塑、分散助剂、填料及色料,还加入适量水以调整体系粘度。通过改性后,防水涂料的柔软性、抗撕裂性、耐水性和粘结性均得到改善,价格较低,寿命长,很受用户欢迎。
Description
本发明涉及一种水基高分子防水涂料,属于含醋酸乙烯共聚物的涂料组合物技术领域。
建筑行业所用的防水涂料中一类以沥青及乳化沥青为主要成份,其特点是成本低,但性能较差,施工工艺性也不理想;另一类以各种高分子材料为主要成份,如氯丁橡胶、丙烯酸酯、聚氨脂及聚苯乙烯涂料,虽然性能有所提高,但不同程度存在成本高、毒性大或水溶性差等缺陷。在申请号为94113969的一项名为彩色防水弹性涂料的发明中提出以乙烯-酸酸乙烯共聚液为基料生产防水涂料的技术方案,代表了国内建筑防水涂料行业的一个新趋势,但这种涂料的耐水性、粘结性和抗撕裂性有待改善,成本仍偏高。
本发明的目的在于公开一种水基高分子防水涂料,通过对乙烯-醋酸乙烯的改性,提高涂膜的耐水性、粘结性和抗撕裂性,并降低产品成本。
本发明的任务是这样实现的:对以乙烯-醋酸乙烯共聚液为基料,包括助剂、填料、色料和消泡剂的涂料组合物中,加入乙烯焦油改性,乙烯-醋酸乙烯与乙烯焦油的重量比为1∶0.4~0.6。
乙烯-醋酸乙烯为基料的涂料具有良好的柔性、湿粘性和耐水耐侯性,使用廉价的焦油改性,可提高涂膜的柔软性和抗撕裂性,改善其耐水性和粘结性,并使产品成本下降,它的性能价格比在国内目前所有的水基高分子防水涂料中是最高的。这种涂料对柔性防水卷材、刚性水泥砂浆面均有良好的粘结性和防水性,可单独应用形成单纯性防水层,也可与玻璃布或无纺布配合使用形成“一布四胶”的加强防水层,使用寿命长,生产工艺较简单,可获得较好的经济效益及社会效益。
下面结合实施例,对本发明作具体说明。
乙烯-醋酸乙烯共聚液和乙烯焦油是涂料中的两种基本成份,用量比为1∶0.4-0.6;助剂中包括常用乳化剂OP-10和增塑剂邻苯二甲酯类,填料为重钙、轻钙和滑石粉为主,还含有微量色料和硅油类消泡剂;其中助剂用量占总量0.5-2%,填料用量占总量20-35%。
乙烯的引入使乙酰基不连续,高分子主链变得柔软,增大分子间活动性,从而改善其粘结性,此外非极性的乙烯基的引入对提高共聚物的耐水性也是十分有利的。
焦油和沥青常被用于防水涂料,直接的,经改性,或作为改性剂。由于乙烯-醛酸乙烯共聚物的特殊性能,在引入焦油沥青类进行改性试验中,我们发现目前被用于防水涂料的沥青、焦油类,如各种牌号石油沥青、原油及煤焦油等均不合适,不是结块,就是起不到正面改性作用。分析其原因,可能是这些焦油或沥青成份复杂,性能不一,不适用于乙烯-醛酸乙烯这种特定高分子共聚物。最后我们选择重油裂化提取乙烯后所得的下级料-俗称乙烯焦油,获得成功。这种焦油,平均分子链较短,主要含烷烯烃类、芳香烃量少。试验表明乙烯焦油的引入可使共聚物颗粒软化,增加流动性和粘结性。而被软化了的共聚物又能加速凝聚,改善施工性能和涂膜的耐水性。相对地说,乙烯焦油的成份较稳定,使改性的工艺控制容易实现。乙烯焦油的用量为共聚物的2/5-3/5,视改性过程中时间、颜色及粘度的变化以及产品性能测定值调整。
改性过程中助剂及填料的加入会使体系的粘度不断增大,造成搅拌困难,同时也影响产品的施工性能和应有的固体含量,加入少量水即可使体系的粘度下降,并不影响产品的其他基本性能。这是乙烯-醛酸乙烯水基涂料的一个特性。水的加入量一般为2-4%,最好为去离子水,体系实际含水最高不超过7%。用量的变化主要受填料和气候的影响。填料粒度细,表面积大,容易使体系变稠,需要增加用水量;而气候潮湿时,细的填料又容易吸附水汽,又需要降低加入的水量。体系含水量过多,填料会沉淀。
本产品的另一特点是加工工艺较简单:15℃以上室温操作,将乙烯-醋酸乙烯共聚液与乙烯焦油加入反应釜中搅拌,先加入二分之一的填料,搅拌过程中不断点加助剂,视起泡程度,加入硅油消泡,加水调整粘度。然后过一次胶体磨。再加入其余填料继续搅拌,滴加消泡剂和水,直至体系成金黄色。第二次过胶体磨。总搅拌改性时间30-45分。
本涂料主要性能指标如表1,粘结性能如表2,经济效益比较如表3。如表3。表1 水基高分子防水涂料的基本性能
表2 涂料与卷材、沥青油毡的粘结性能
表3 经济效益比较
项目 | 粘度 | 干燥时间(小时) | 低温柔性 | 耐热性 | 延伸率 |
(涂-4杯)秒 | 表干 实干 | -40℃ φ30mm棒绕 | 100土2℃ | % | |
85 | 2 <24 | 无断裂,垂直悬挂 | 无流淌 | 180 |
粘结剥离性 | ||
剥离强度N/cm2 | 破坏形式 | |
氯化聚乙烯卷材-防水涂料 | 20.50 | 涂膜内聚破坏 |
沥青油毡-防水涂料 | 5.07 | 油毡破坏 |
材料名称 | 厚度mm | 材料单价元/m2 | 防水层造价元/m2 | 施工方法 |
SBS改性沥青油毡 | 3-4 | 10-14 | 13-15 | 两毡三油热施工 |
氯丁胶再生胶沥青防水涂料 | 2 | 10-12 | 15-18 | 二布六油冷施工 |
聚氨酯涂膜防水涂料 | 1-1.3 | 24-30 | 30-35 | 涂刷3-6遍冷施工 |
本产品 | 1.2-1.5 | 8-10 | 12-14 | 一布3-5遍冷施工 |
Claims (3)
1、一种水基高分子防水涂料,以乙烯-醋酸乙烯共聚液为基料,包含助剂、填料、色料和消泡剂,其特征是在该组合物中还加入乙烯焦油改性,乙烯-醋酸乙烯与乙烯焦油的重量比为1∶0.4~0.6。
2、按权利要求1所述的水基高分子防水涂料,其特征是所述的助剂中含有OP-10类乳化剂,邻苯二甲酯类增塑剂,助剂量占体系总量0.5-2%填料用量占总量20-35%。
3、按权利要求1或2所述的水基高分子防水涂料,其特征是所述涂料组合物中还含有水,体系含水量不超过7%。
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN96112893A CN1059222C (zh) | 1996-09-20 | 1996-09-20 | 水基高分子防水涂料 |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN96112893A CN1059222C (zh) | 1996-09-20 | 1996-09-20 | 水基高分子防水涂料 |
Publications (2)
Publication Number | Publication Date |
---|---|
CN1180090A true CN1180090A (zh) | 1998-04-29 |
CN1059222C CN1059222C (zh) | 2000-12-06 |
Family
ID=5121650
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
CN96112893A Expired - Fee Related CN1059222C (zh) | 1996-09-20 | 1996-09-20 | 水基高分子防水涂料 |
Country Status (1)
Country | Link |
---|---|
CN (1) | CN1059222C (zh) |
Family Cites Families (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN1031851A (zh) * | 1987-08-22 | 1989-03-22 | 天津市军粮城防水涂料厂 | 高分子三防冷涂料及其制造法 |
CN1045457C (zh) * | 1994-11-11 | 1999-10-06 | 高林萍 | 彩色防水涂料 |
CN1167869A (zh) * | 1997-03-21 | 1997-12-17 | 孙宝恒 | 徒步上行牵引装置 |
-
1996
- 1996-09-20 CN CN96112893A patent/CN1059222C/zh not_active Expired - Fee Related
Also Published As
Publication number | Publication date |
---|---|
CN1059222C (zh) | 2000-12-06 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CN101665675B (zh) | 一种水性聚氨酯粘合剂及超细纤维合成革的制备方法 | |
CN102020859B (zh) | 具有蠕变特性的改性沥青组合物及其制备方法 | |
DK3081599T3 (en) | PLANT-BASED BINDING MATERIALS, COMPOSITIONS THEREOF AND PROCEDURE TO REDUCE THE QUANTITY OF OIL-BASED BITUM | |
US5721302A (en) | Water dispersible adhesive | |
US4430465A (en) | Asphalt composition | |
CN101925652A (zh) | 耐冲洗热固化性环氧树脂粘合剂 | |
CN101821332A (zh) | 由一些嵌段共聚物制备的最终使用用途 | |
CN102190895B (zh) | 一种强配伍性乳化沥青及其制备方法 | |
CN102471663A (zh) | 含有环己烷多羧酸衍生物的粘合剂和密封剂 | |
KR101508888B1 (ko) | 자착식 아스팔트 방수시트 | |
CN1223644C (zh) | 聚酯增粘剂及粘合剂组合物 | |
CN101921545A (zh) | 建筑用沥青防水涂料及其制备方法 | |
CN101824294A (zh) | 四元共聚水性聚氨酯汽车内饰胶的制备方法 | |
KR101757190B1 (ko) | 고점착 자착형 고무화 아스팔트 방수재의 제조방법 | |
CN104910812A (zh) | 一种防水涂料 | |
DK3081600T3 (en) | PLANT ORIGIN OF THE PLANT ORIGIN, COMPOSITIONS INCLUDING THE SAME, AND PROCEDURE TO REDUCE THE QUANTITY OF THE OIL BITUM | |
CN108084881B (zh) | 一种潮湿地面用非固化橡胶沥青防水涂料及其制备方法 | |
CN102211895A (zh) | 使混凝土结构外部防水的胶化沥青膜/毡片复合防水材料 | |
CN112175570B (zh) | 一种聚氨酯胶及其制备方法 | |
US5713996A (en) | Asphalt coating composition and method for coating a surface using the same | |
CN116042043A (zh) | 用于高分子自粘胶膜防水卷材的水性非沥青基防水涂料及其制备方法和用途 | |
CN1059222C (zh) | 水基高分子防水涂料 | |
CN111440584A (zh) | 一种用于粘结自粘沥青防水卷材的单组分湿固化聚氨酯防水胶黏剂 | |
CN102433071A (zh) | 含有改性有机硅系聚合物的冷施工无溶剂沥青涂膜防水材料及其制造方法 | |
CN101984197B (zh) | 氧化锌阻根改性沥青自粘防水卷材及其制备方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
C06 | Publication | ||
PB01 | Publication | ||
C10 | Entry into substantive examination | ||
SE01 | Entry into force of request for substantive examination | ||
C14 | Grant of patent or utility model | ||
GR01 | Patent grant | ||
C19 | Lapse of patent right due to non-payment of the annual fee | ||
CF01 | Termination of patent right due to non-payment of annual fee |