CN117945715A - 一种瓷砖胶及其制备方法 - Google Patents
一种瓷砖胶及其制备方法 Download PDFInfo
- Publication number
- CN117945715A CN117945715A CN202410100511.4A CN202410100511A CN117945715A CN 117945715 A CN117945715 A CN 117945715A CN 202410100511 A CN202410100511 A CN 202410100511A CN 117945715 A CN117945715 A CN 117945715A
- Authority
- CN
- China
- Prior art keywords
- parts
- vinyl acetate
- tile glue
- glue according
- wetting agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种瓷砖胶，包括如下的原料：硅酸盐水泥，烧结砂，灰钙粉，叔醋丙三元聚合乳液，液态柔性树脂，二氧化硅，硅酸镁锂，碱溶胀增稠剂，阴离子润湿剂，阳离子表面活性剂及水。该瓷砖胶具有优异的粘合性能，能有效提高柔性瓷砖贴片的铺贴的牢固程度。
Description
技术领域
本发明属于建筑材料技术领域，特别涉及一种瓷砖胶及其制备方法。
背景技术
瓷砖胶类产品是应用较为广泛，且市场使用量非常大的一类特种砂浆产品。目前的瓷砖胶产品最常见的使用场合还是集中于硬质的瓷砖、瓷片、玻化砖、岩板、石材、文化石等产品当中。而目前由于市场在近几年新推出了一类柔性瓷砖贴片类产品，被成为“软瓷”或“柔瓷”的仿砖类产品，在相同体积下该类产品自身重量仅为传统瓷砖重量的五分之一，因此广受市场的关注和好评。相比传统的硬质瓷砖，柔性瓷砖贴片背面比较光滑，因此采用现有的水泥基瓷砖胶来贴合柔性瓷砖贴片，容易出现贴合不牢的问题，因此，亟需对现有的瓷砖胶进行改进以满足柔性瓷砖贴片的铺贴要求。
发明内容
本发明旨在至少解决现有技术中存在的技术问题之一。为此，本发明提出一种瓷砖胶及其制备方法，该瓷砖胶具有优异的粘合性能，能有效提高柔性瓷砖贴片的铺贴的牢固程度。
本发明的上述技术目的是通过以下技术方案得以实现的：
一种瓷砖胶，包括如下的原料：硅酸盐水泥，烧结砂，灰钙粉，叔醋丙三元聚合乳液，液态柔性树脂，二氧化硅，硅酸镁锂，碱溶胀增稠剂，阴离子润湿剂，阳离子表面活性剂及水。
优选地，所述瓷砖胶包括如下重量份数的原料：硅酸盐水泥20-25份，烧结砂65-75份，灰钙粉5-10份，叔醋丙三元聚合乳液4-6份，液态柔性树脂1-2份，二氧化硅0.05-0.1份，硅酸镁锂0.2-0.3份，碱溶胀增稠剂0.4-0.6份，阴离子润湿剂0.01-0.03份，阳离子表面活性剂0.01-0.02份，水20-50份。
优选地，所述硅酸盐水泥为P.II 42.5及P.O42.5中的一种。
优选地，所述烧结砂的粒度为50-100目，所述烧结砂的密度≤3.0g/cm3，该特定的烧结砂具有轻质中空的特点，使用在本发明的瓷砖胶中能进一步保证瓷砖胶的粘合性能。
优选地，所述灰钙粉的粒度为300-500目。
优选地，所述叔醋丙三元聚合乳液为型号为SZS-111的叔醋丙乳液。
优选地，：所述液态柔性树脂为环氧树脂LS-835、环氧树脂LS-832及环氧树脂LS-828中的至少一种。
优选地，所述二氧化硅为气相二氧化硅，所述二氧化硅的粒径小于1mm。
优选地，所述硅酸镁锂的粒度为600-1000目。
优选地，所述碱溶胀增稠剂为聚羧酸。
优选地，所述阴离子润湿剂为亚甲基二萘磺酸钠及十二烷基磺酸钠中的至少一种。
优选地，所述阳离子表面活性剂为聚乙烯亚胺。
一种如上所述瓷砖胶的制备方法，包括以下步骤：
(1)将硅酸盐水泥，烧结砂，灰钙粉，二氧化硅，硅酸镁锂混合成固态物料；
(2)将叔醋丙三元聚合乳液，液态柔性树脂、碱溶胀增稠剂，阴离子润湿剂，阳离子表面活性剂及水混合成液态物料；
(3)将步骤(1)制得的固态物料与步骤(2)制得的液态物料混合即得。
本发明的有益效果是：
(1)本发明的瓷砖胶中的灰钙粉为气硬性材料，可以避免瓷砖胶早期硬化刚性较高而造成的表层柔韧性降低，而搭配硅酸盐水泥材料，可以保证后期的强度增长，从而可以提高产品柔韧性；
(2)本发明的瓷砖胶中特定的叔醋丙三元聚合乳液可以有效提升瓷砖胶的耐候性，搭配特定的液态柔性树脂和阳离子表面活性剂，可以有效提高后期界面强度与粘结性，而特定阴离子润湿剂的加入可以最大程度避免早期的润湿性不足而导致的铺贴牢固度问题。
具体实施方式
下面结合具体实施例对本发明做进一步的说明。
实施例1：
一种瓷砖胶，包括如下重量份数的原料：硅酸盐水泥20份，烧结砂65份，灰钙粉5份，叔醋丙三元聚合乳液4份，液态柔性树脂1份，气相二氧化硅0.05份，硅酸镁锂0.2份，碱溶胀增稠剂0.4份，阴离子润湿剂0.01份，阳离子表面活性剂0.01份，水20份，其中硅酸盐水泥为P.II 42.5，烧结砂的粒度为80目，烧结砂的密度为2.13g/cm3，灰钙粉的粒度为300目，叔醋丙三元聚合乳液为武汉超时代电商有限公司销售的型号为SZS-111的叔醋丙乳液，液态柔性树脂为环氧树脂LS-835，气相二氧化硅的粒径小于100nm，硅酸镁锂的粒度为600目，碱溶胀增稠剂为阿克苏诺贝尔特种化学(上海)有限公司销售的牌号为T-615的聚羧酸，阴离子润湿剂为亚甲基二萘磺酸钠，阳离子表面活性剂为聚乙烯亚胺。
上述瓷砖胶的制备方法，包括以下步骤：
(1)将硅酸盐水泥，烧结砂，灰钙粉，气相二氧化硅，硅酸镁锂混合后1300rpm搅拌10分钟，制得固态物料；
(2)将叔醋丙三元聚合乳液，液态柔性树脂、碱溶胀增稠剂，阴离子润湿剂，阳离子表面活性剂及水混合后1800rpm搅拌15分钟，制得液态物料；
(3)在2000rpm的搅拌状态下将步骤(1)制得的固态物料缓慢加入步骤(2)制得的液态物料中混合均匀即得。
实施例2：
一种瓷砖胶，包括如下重量份数的原料：硅酸盐水泥25份，烧结砂75份，灰钙粉10份，叔醋丙三元聚合乳液6份，液态柔性树脂2份，气相二氧化硅0.1份，硅酸镁锂0.3份，碱溶胀增稠剂0.6份，阴离子润湿剂0.03份，阳离子表面活性剂0.02份，水50份，其中硅酸盐水泥为PO42.5，烧结砂的粒度为80目，烧结砂的密度为2.13g/cm3，灰钙粉的粒度为500目，叔醋丙三元聚合乳液为武汉超时代电商有限公司销售的型号为SZS-111的叔醋丙乳液，液态柔性树脂为环氧树脂LS-832，气相二氧化硅的粒径小于100nm，硅酸镁锂的粒度为1000目，碱溶胀增稠剂为阿克苏诺贝尔特种化学(上海)有限公司销售的牌号为T-615的聚羧酸，阴离子润湿剂为十二烷基磺酸钠，阳离子表面活性剂为聚乙烯亚胺。
上述瓷砖胶的制备方法，包括以下步骤：
(1)将硅酸盐水泥，烧结砂，灰钙粉，气相二氧化硅，硅酸镁锂混合后1300rpm搅拌10分钟，制得固态物料；
(2)将叔醋丙三元聚合乳液，液态柔性树脂、碱溶胀增稠剂，阴离子润湿剂，阳离子表面活性剂及水混合后1800rpm搅拌15分钟，制得液态物料；
(3)在2000rpm的搅拌状态下将步骤(1)制得的固态物料缓慢加入步骤(2)制得的液态物料中混合均匀即得。
实施例3：
一种瓷砖胶，包括如下重量份数的原料：硅酸盐水泥23份，烧结砂70份，灰钙粉8份，叔醋丙三元聚合乳液5份，液态柔性树脂1.5份，气相二氧化硅0.08份，硅酸镁锂0.25份，碱溶胀增稠剂0.5份，阴离子润湿剂0.02份，阳离子表面活性剂0.01份，水30份，其中硅酸盐水泥为P.II 42.5，烧结砂的粒度为80目，烧结砂的密度为2.13g/cm3，灰钙粉的粒度为300目，叔醋丙三元聚合乳液为武汉超时代电商有限公司销售的型号为SZS-111的叔醋丙乳液，液态柔性树脂为环氧树脂LS-835，气相二氧化硅的粒径小于100nm，硅酸镁锂的粒度为600目，碱溶胀增稠剂为阿克苏诺贝尔特种化学(上海)有限公司销售的牌号为T-615的聚羧酸，阴离子润湿剂为亚甲基二萘磺酸钠，阳离子表面活性剂为聚乙烯亚胺。
上述瓷砖胶的制备方法，包括以下步骤：
(1)将硅酸盐水泥，烧结砂，灰钙粉，气相二氧化硅，硅酸镁锂混合后1300rpm搅拌10分钟，制得固态物料；
(2)将叔醋丙三元聚合乳液，液态柔性树脂、碱溶胀增稠剂，阴离子润湿剂，阳离子表面活性剂及水混合后1800rpm搅拌15分钟，制得液态物料；
(3)在2000rpm的搅拌状态下将步骤(1)制得的固态物料缓慢加入步骤(2)制得的液态物料中混合均匀即得。
实施例4：
一种瓷砖胶，包括如下重量份数的原料：硅酸盐水泥22份，烧结砂66份，灰钙粉9份，叔醋丙三元聚合乳液5份，液态柔性树脂1.3份，气相二氧化硅0.05份，硅酸镁锂0.2份，碱溶胀增稠剂0.45份，阴离子润湿剂0.015份，阳离子表面活性剂0.015份，水35份，其中硅酸盐水泥为P.II 42.5，烧结砂的粒度为80目，烧结砂的密度为2.13g/cm3，灰钙粉的粒度为300目，叔醋丙三元聚合乳液为武汉超时代电商有限公司销售的型号为SZS-111的叔醋丙乳液，液态柔性树脂为环氧树脂LS-835，气相二氧化硅的粒径小于100nm，硅酸镁锂的粒度为600目，碱溶胀增稠剂为阿克苏诺贝尔特种化学(上海)有限公司销售的牌号为T-615的聚羧酸，阴离子润湿剂为亚甲基二萘磺酸钠，阳离子表面活性剂为聚乙烯亚胺。
上述瓷砖胶的制备方法，包括以下步骤：
(1)将硅酸盐水泥，烧结砂，灰钙粉，气相二氧化硅，硅酸镁锂混合后1300rpm搅拌10分钟，制得固态物料；
(2)将叔醋丙三元聚合乳液，液态柔性树脂、碱溶胀增稠剂，阴离子润湿剂，阳离子表面活性剂及水混合后1800rpm搅拌15分钟，制得液态物料；
(3)在2000rpm的搅拌状态下将步骤(1)制得的固态物料缓慢加入步骤(2)制得的液态物料中混合均匀即得。
实施例5：
一种瓷砖胶，包括如下重量份数的原料：硅酸盐水泥24份，烧结砂73份，灰钙粉6份，叔醋丙三元聚合乳液5份，液态柔性树脂1.8份，气相二氧化硅0.08份，硅酸镁锂0.28份，碱溶胀增稠剂0.56份，阴离子润湿剂0.02份，阳离子表面活性剂0.018份，水40份，其中硅酸盐水泥为P.II 42.5，烧结砂的粒度为80目，烧结砂的密度为2.13g/cm3，灰钙粉的粒度为300目，叔醋丙三元聚合乳液为武汉超时代电商有限公司销售的型号为SZS-111的叔醋丙乳液，液态柔性树脂为环氧树脂LS-835，气相二氧化硅的粒径小于100nm，硅酸镁锂的粒度为600目，碱溶胀增稠剂为阿克苏诺贝尔特种化学(上海)有限公司销售的牌号为T-615的聚羧酸，阴离子润湿剂为亚甲基二萘磺酸钠，阳离子表面活性剂为聚乙烯亚胺。
上述瓷砖胶的制备方法，包括以下步骤：
(1)将硅酸盐水泥，烧结砂，灰钙粉，气相二氧化硅，硅酸镁锂混合后1300rpm搅拌10分钟，制得固态物料；
(2)将叔醋丙三元聚合乳液，液态柔性树脂、碱溶胀增稠剂，阴离子润湿剂，阳离子表面活性剂及水混合后1800rpm搅拌15分钟，制得液态物料；
(3)在2000rpm的搅拌状态下将步骤(1)制得的固态物料缓慢加入步骤(2)制得的液态物料中混合均匀即得。
对比例1：
一种瓷砖胶，与实施例3的不同之处仅在于不含灰钙粉。
对比例2：
一种瓷砖胶，与实施例3的不同之处仅在于不含叔醋丙三元聚合乳液。
对比例3：
一种瓷砖胶，与实施例3的不同之处仅在于不含液态柔性树脂。
对比例4：
一种瓷砖胶，与实施例3的不同之处仅在于不含阳离子表面活性剂。
对比例5：
一种瓷砖胶，与实施例3的不同之处仅在于不含阴离子润湿剂。
试验例：
参照JC/T547-2017标准对实施例1-5及对比例1-5的瓷砖胶进行性能测试，测试结果见如下表1：
表1：性能测试结果
由表1可知，本发明的瓷砖胶的拉伸粘结原强度能达到2.73MPa以上，泡水后的拉伸粘结强度能达到2.21MPa以上，热老化后的拉伸粘结强度能达到2.03MPa以上，冻融3次循环后的拉伸粘结强度能达到1.95MPa以上，紫外光照射20min后的拉伸粘结强度能达到2.05MPa以上，具有优异的粘合性能和耐候性能，能有效提高柔性瓷砖贴片的铺贴的牢固程度。
同时，对比实施例3与对比例1-5可知，当其他条件不变，当瓷砖胶中缺少灰钙粉、叔醋丙三元聚合乳液、液态柔性树脂、阳离子表面活性剂及阴离子润湿剂中的一种时，瓷砖的粘合性能和耐候性能均会下降。
上述实施例为本发明较佳的实施方式，但本发明的实施方式并不受上述实施例的限制，其他的任何未背离本发明的精神实质与原理下所作的改变、修饰、替代、组合、简化，均应为等效的置换方式，都包含在本发明的保护范围之内。
Claims (10)
1.一种瓷砖胶，其特征在于：包括如下的原料：
硅酸盐水泥，烧结砂，灰钙粉，叔醋丙三元聚合乳液，液态柔性树脂，二氧化硅，硅酸镁锂，碱溶胀增稠剂，阴离子润湿剂，阳离子表面活性剂及水。
2.根据权利要求1所述的一种瓷砖胶，其特征在于：包括如下重量份数的原料：硅酸盐水泥20-25份，烧结砂65-75份，灰钙粉5-10份，叔醋丙三元聚合乳液4-6份，液态柔性树脂1-2份，二氧化硅0.05-0.1份，硅酸镁锂0.2-0.3份，碱溶胀增稠剂0.4-0.6份，阴离子润湿剂0.01-0.03份，阳离子表面活性剂0.01-0.02份，水20-50份。
3.根据权利要求1所述的一种瓷砖胶，其特征在于：所述叔醋丙三元聚合乳液为型号为SZS-111的叔醋丙乳液。
4.根据权利要求1所述的一种瓷砖胶，其特征在于：所述液态柔性树脂为环氧树脂LS-835、环氧树脂LS-832及环氧树脂LS-828中的至少一种。
5.根据权利要求1所述的一种瓷砖胶，其特征在于：所述二氧化硅为气相二氧化硅，所述二氧化硅的粒径小于100nm。
6.根据权利要求1所述的一种瓷砖胶，其特征在于：所述硅酸镁锂的粒度为600-1000目。
7.根据权利要求1所述的一种瓷砖胶，其特征在于：所述碱溶胀增稠剂为聚羧酸。
8.根据权利要求1所述的一种瓷砖胶，其特征在于：所述阴离子润湿剂为亚甲基二萘磺酸钠及十二烷基磺酸钠中的至少一种。
9.根据权利要求1所述的一种瓷砖胶，其特征在于：所述阳离子表面活性剂为聚乙烯亚胺。
10.一种如权利要求1至9任一项所述瓷砖胶的制备方法，其特征在于：包括以下步骤：
(1)将硅酸盐水泥，烧结砂，灰钙粉，二氧化硅，硅酸镁锂混合成固态物料；
(2)将叔醋丙三元聚合乳液，液态柔性树脂、碱溶胀增稠剂，阴离子润湿剂，阳离子表面活性剂及水混合成液态物料；
(3)将步骤(1)制得的固态物料与步骤(2)制得的液态物料混合即得。