CN116726462A - Wood golf club head and method for manufacturing wood golf club head - Google Patents
Wood golf club head and method for manufacturing wood golf club head Download PDFInfo
- Publication number
- CN116726462A CN116726462A CN202310193211.0A CN202310193211A CN116726462A CN 116726462 A CN116726462 A CN 116726462A CN 202310193211 A CN202310193211 A CN 202310193211A CN 116726462 A CN116726462 A CN 116726462A
- Authority
- CN
- China
- Prior art keywords
- layer
- club head
- golf club
- wood golf
- laminated structure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention aims to provide a wood golf club head which can realize light weight and high rigidity for a desired part of an outer shell. A wood golf club head (1) according to one embodiment of the present invention is provided with a hollow club head body (10) having an outer shell (20) including a face portion (2), a crown portion (3), and a sole portion (4), wherein a laminated structure (30) having a first layer (11) and a second layer (12) arranged at a distance in the thickness direction and a center layer (13) arranged between the first layer (11) and the second layer (12) is provided on at least a part of the outer shell (20), and the apparent density of the center layer (13) is smaller than the apparent density of the first layer (11) and the second layer (12).
Description
Technical Field
The present invention relates to a wood golf club head and a method of manufacturing the wood golf club head.
Background
For wood golf having a hollow head body, weight reduction is desired.
From such a point of view, the use of fiber reinforced resin (FRP) or the like in the outer shell of the head body has been studied (see patent document 1).
Prior art literature
Patent literature
Patent document 1: japanese patent laid-open publication No. 2005-58034
Patent document 2: japanese patent laid-open No. 63-264085
Disclosure of Invention
Technical problem to be solved by the invention
Patent document 1 describes using a plate-like member in which prepregs in which carbon fibers are dispersed in an epoxy resin are laminated in a plurality of layers in a crown portion. However, according to this structure, in order to obtain the required rigidity, the number of sheets of prepreg needs to be increased, and thus there is a technical problem in terms of promoting weight reduction.
Patent document 2 describes a hollow club head in which wall portions extending from a sole surface to an upper surface or from an upper surface to a sole surface are provided in the interior of the club head, thereby forming hollow chambers of a honeycomb structure. Patent document 2 describes that the entire head can be reinforced by providing hollow chambers having a honeycomb structure. However, with the structure described in patent document 2, a desired rigidity cannot be given to a desired portion of the outer shell of the head body with an appropriate weight.
The present invention has been made in view of such a situation, and an object of the present invention is to provide a wood golf club head capable of realizing weight reduction and high rigidity for a desired portion of an outer housing.
Technical scheme for solving technical problems
A wood golf club head according to an aspect of the present invention includes a hollow club head body having an outer shell including a face portion, a crown portion, and a sole portion, wherein a laminated structure having a first layer and a second layer arranged at intervals in a thickness direction and a center layer arranged between the first layer and the second layer is provided on at least a part of the outer shell, and an apparent density of the center layer is smaller than an apparent density of the first layer and the second layer.
The first layer and the second layer may be fiber-reinforced resin layers, respectively.
The core layer may be porous.
The core layer may have a plurality of through holes penetrating in the thickness direction.
The middle core layer may comprise a foamed resin or a honeycomb core.
The ratio of the average thickness of the core layer to the average thickness of the laminated structure is preferably 0.4 to 0.9.
The apparent density of the core layer is preferably 10kg/m 3 200kg/m above 3 The following is given.
The laminated structure may be disposed at the crown.
In another aspect of the present invention, a method for manufacturing a wood golf club head includes a hollow head body having an outer shell including a face portion, a crown portion, and a sole portion, wherein a laminated structure is provided on at least a part of the outer shell, and wherein a center layer having an apparent density smaller than that of the first layer and the second layer is disposed between the first layer and the second layer, which are disposed at intervals in a thickness direction, via an adhesive, and a clamping pressure is applied to the first layer and the second layer, and the first layer and the second layer are bonded to the center layer via the adhesive.
In the present invention, "apparent density" means "apparent density" according to JISK7222:2005, the values measured. "average thickness" refers to the average of the thickness at any 10 points. The term "average thickness" refers to an average value of thickness at any 10 points at a portion having no irregularities or the like in the case where irregularities or the like exist in a portion of a measurement object.
ADVANTAGEOUS EFFECTS OF INVENTION
In the wood golf club head according to one aspect of the present invention, a laminated structure formed by sandwiching the center layer between the first layer and the second layer is provided in at least a part of the outer shell, and therefore, the desired part of the outer shell can be reduced in weight and increased in rigidity by the laminated structure. That is, the apparent density of the center layer of the wood golf club head is smaller than the apparent densities of the first layer and the second layer, and thus, even if the thickness of the center layer is relatively increased, weight reduction of the entire laminated structure can be achieved. Further, the rigidity of the laminated structure can be improved by sandwiching the core layer between the first layer and the second layer. As a result, the wood golf club head can be reduced in weight and increased in rigidity for a desired portion of the outer shell, as compared with, for example, a conventional structure having a uniform layer structure.
Drawings
Fig. 1 is a schematic front view of a wood golf club head according to one embodiment of the present invention.
Fig. 2 is a schematic top view of the wood golf club head of fig. 1.
Fig. 3 is a schematic cross-sectional view of a crown of the wood golf club head of fig. 1 taken in a thickness direction.
Fig. 4 is a cross-sectional view taken along line IV-IV of fig. 3.
Fig. 5 is a flowchart showing a method of manufacturing a wood golf club head according to an embodiment of the present invention.
Description of the reference numerals
1 a wood golf club head;
2 a face portion;
3 crowns;
3a cover body;
4, the bottom of the rod;
a 10-head body;
11 a first layer;
12 a second layer;
13a middle core layer;
13a through holes;
13b column construction;
20 an outer housing;
30 a laminated structure;
an average thickness of the T-stack structure;
average thickness of core layer in T1.
Detailed Description
Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings. Note that, for the numerical values described in the present specification, only one of the upper limit value and the lower limit value described may be used or the upper limit value and the lower limit value may be arbitrarily combined. In the present specification, numerical ranges that can be combined are described as preferable ranges.
< Wood club head >
The wood golf club head 1 of fig. 1 and 2 includes a hollow head body 10. The head body 10 has an outer shell 20 including a face portion 2, a crown portion 3, and a sole portion 4. The wood golf club head 1 can be used, for example, as a driver, an iron, a fairway wood, or the like. Among them, the wood-type golf club head 1 is preferably used as a driver.
As shown in fig. 3, a laminated structure 30 including a first layer 11 and a second layer 12 arranged with a gap therebetween in the thickness direction and a core layer 13 arranged between the first layer 11 and the second layer 12 is provided in at least a part of the outer case 20. The apparent density of the middle core layer 13 is less than the apparent density of the first layer 11 and the second layer 12. In the wood-type golf club head 1, the specific configuration of the portion other than the laminated structure 30 is not particularly limited. For example, the material of the outer case 20 other than the laminated structure 30 is not particularly limited, and for example, a metal or an alloy containing titanium, stainless steel, martensitic steel, aluminum, magnesium, or the like as a main component can be used. The term "main component" means a component having the largest content in terms of mass, and for example, means a component having a content of 50 mass% or more.
(laminated Structure)
The laminated structure 30 will be described in detail with reference to fig. 3. The laminated structure 30 is a three-layer structure in which the first layer 11, the middle core layer 13, and the second layer 12 are laminated in this order from the outer surface side toward the inner surface side of the outer case 20. In the present embodiment, the first layer 11 constitutes an outer surface of the outer case 20, and the second layer 12 constitutes an inner surface of the outer case 20.
The laminated structure 30 constitutes a part of the outer case 20. The laminated structure 30 can be disposed at any position of the outer case 20, and can be disposed on the face portion 2, the sole portion 4, and the like, for example. Among them, the laminated structure 30 is preferably arranged in the crown 3. In the rules of golf, the crown 3 is required to be strong, and in view of the requirement for lowering the center of gravity of the head body 10, the weight thereof is required to be light. In this regard, in the wood golf club head 1, by disposing the laminated structure 30 on the crown 3, rigidity against pressing pressure of the crown 3 can be improved, the rigidity can be ensured, and the weight of the crown 3 can be reduced.
As shown in fig. 2, the wood golf club head 1 is provided with a cover 3a at a crown 3. The cover 3a has a laminated structure 30 of fig. 3. The ratio of the cap 3a to the crown 3 (that is, the ratio of the laminated structure 30 to the crown 3) is not particularly limited, and may be, for example, 50% by volume or more, and preferably 70% by volume or more.
[ first layer ]
The first layer 11 may be a fiber-reinforced resin layer, or a metal layer containing a metal or alloy such as titanium, stainless steel, martensitic steel, aluminum, or magnesium as a main component. Among them, the fiber-reinforced resin layer is preferable as the first layer 11 from the viewpoint of easily realizing the weight reduction and the high rigidity of the laminated structure 30. In the case where the first layer 11 is a fiber-reinforced resin layer (first fiber-reinforced resin layer), the first layer 11 has a first resin matrix and first fibers dispersed in the first resin matrix. The first layer 11 is, for example, a laminate of a plurality of prepregs in which the first fibers are dispersed in the first resin matrix.
Examples of the first fibers include inorganic fibers such as carbon fibers and glass fibers, and organic fibers such as aramid fibers and poly-p-phenylene benzobisoxazole fibers (PBO fibers). Examples of the main component of the first resin matrix include thermosetting resins such as epoxy resins and unsaturated polyesters, and thermoplastic resins such as polyolefin and polyamide. In the case where the first fibers are carbon fibers, the first layer 11 is formed as a carbon fiber reinforced resin layer (CFRP layer). In the case where the first fibers are glass fibers, the first layer 11 is formed as a glass fiber reinforced resin layer (GFRP layer).
Preferably, the first layer 11 is a carbon fiber reinforced resin layer (CFRP layer). With this structure, the laminated structure 30 can be easily reduced in weight and increased in rigidity.
The apparent density of the first layer 11 may be, for example, 800kg/m 3 4500kg/m of the above 3 The following is given.
[ second layer ]
The second layer 12 may be, for example, a fiber-reinforced resin layer or a metal layer containing a metal or alloy such as titanium, stainless steel, martensitic steel, aluminum, magnesium, or the like as a main component. Among them, the fiber-reinforced resin layer is preferable as the second layer 12 from the viewpoint of easily realizing weight reduction and high rigidity of the laminated structure 30. In the case where the second layer 12 is a fiber-reinforced resin layer (second fiber-reinforced resin layer), the second layer 12 has a second resin matrix and second fibers dispersed in the second resin matrix. The second layer 12 is, for example, a laminate of a plurality of prepregs in which the second fibers are dispersed in the second resin matrix.
As the second fibers, carbon fibers, glass fibers, aramid fibers, poly-p-phenylene benzobisoxazole fibers (PBO fibers), and the like can be used as the first fibers. As the main component of the second resin matrix, a thermosetting resin such as an epoxy resin or an unsaturated polyester, or a thermoplastic resin such as a polyolefin or a polyamide can be used as in the case of the first resin matrix.
The second fibers may be the same as or different from the first fibers. The main component of the second resin matrix may be the same as or different from the main component of the first resin matrix. However, the second layer 12 is preferably a carbon fiber reinforced resin layer (CFRP layer), and more preferably both the first layer 11 and the second layer 12 are carbon fiber reinforced resin layers (CFRP layers). With this structure, the laminated structure 30 can be easily reduced in weight and increased in rigidity.
The apparent density of the second layer 12 may be, for example, 800kg/m 3 4500kg/m of the above 3 The following is given.
The average thickness of the first layer 11 may be different from the average thickness of the second layer 12. In this case, from the viewpoint of strength against external force, it is preferable that the average thickness of the first layer 11 is larger than the average thickness of the second layer 12. From the viewpoint of stabilizing the shape of the laminated structure 30, the average thickness of the first layer 11 and the average thickness of the second layer 12 are preferably similar. The ratio of the average thickness of the second layer 12 to the average thickness of the first layer 11 is, for example, preferably 0.8 or more and 1.2 or less, more preferably 0.9 or more and 1.1 or less, and still more preferably 1.0.
[ middle core layer ]
The middle core layer 13 is bonded to the first layer 11 and the second layer 12 by an adhesive. That is, the center layer 13 is directly laminated with the first layer 11 and the second layer 12.
Examples of the material of the core layer 13 include wood, synthetic resin, metal, and fiber. The core layer 13 may be made of a single material, or may be made of two or more materials by impregnating fibers into a fiber synthetic resin, for example.
The center layer 13 is disposed between the first layer 11 and the second layer 12 in order to reduce the weight and increase the rigidity of the laminated structure 30. Therefore, the rigidity of the laminated structure 30 can be improved for the center layer 13 because of its light weight and being sandwiched by the first layer 11 and the second layer 12.
The core layer 13 is preferably porous. By configuring the center layer 13 in this manner, the laminated structure 30 can be made lightweight. Further, by reducing the weight of the center layer 13, the thickness of the center layer 13 can be easily increased. As a result, the rigidity of the laminated structure 30 can be further improved.
In the case where the core layer 13 is porous, as shown in fig. 4, the core layer 13 preferably has a plurality of through holes 13a penetrating in the thickness direction. With this configuration, the bending rigidity of the center layer 13 can be easily improved. Further, the apparent density of the core layer 13 is easily reduced by penetrating the through holes 13a in the thickness direction. As a result, the laminated structure 30 can be reduced in weight and increased in rigidity.
When the center layer 13 is porous, the center layer 13 preferably has a pillar structure 13b divided by the through holes 13a. The pillar structures 13b extend over both ends of the central core layer 13 in the thickness direction, and serve as supports (stays) for maintaining the distance between the first layer 11 and the second layer 12. The column structure 13b can be provided by forming a plurality of through holes 13a in one solid body. The center layer 13 can easily improve bending rigidity by having the pillar structures 13b. Further, according to this structure, the apparent density of the center layer 13 is easily reduced. As a result, the laminated structure 30 can be reduced in weight and increased in rigidity.
When the core layer 13 is porous, the core layer 13 preferably includes a foamed resin or a honeycomb core (the structure of the core layer 13 including the honeycomb core is illustrated in fig. 4). According to this structure, the laminated structure 30 can be easily reduced in weight and increased in rigidity.
When the core layer 13 includes a foaming resin, the main component of the foaming resin is not particularly limited, and examples thereof include polymethacrylimide, rigid urethane resin, phenol resin, urea resin, polyoxysilane resin, and epoxy resin. Among them, a polymethacrylimide which is excellent in heat resistance, facilitates formation of the laminated structure 30, and facilitates weight reduction and high rigidity is preferable.
When the middle core layer 13 includes a honeycomb core, examples of the honeycomb core include an aluminum honeycomb, an aramid honeycomb, and a paper honeycomb. In the case where the middle core layer 13 includes a honeycomb core, the honeycomb core is configured as the pillar structure 13b described above. With this configuration, the laminated structure 30 can be easily and reliably reduced in weight and increased in rigidity. In addition, since the middle core layer 13 includes a honeycomb core, as will be described later, even when the first layer 11 and the second layer 12 are bent, the middle core layer 13 is easily arranged to follow the bent shape.
The lower limit of the average thickness T1 (see fig. 3) of the center layer 13 is preferably 0.4mm, more preferably 0.5mm. On the other hand, the upper limit of the average thickness T1 of the center layer 13 is preferably 3.0mm, more preferably 2.5mm, and further preferably 2.0mm. If the average thickness T1 does not satisfy the lower limit, there is a possibility that the rigidity of the laminated structure 30 cannot be sufficiently improved. In contrast, if the average thickness T1 exceeds the upper limit, there is a problem in that it is difficult to sufficiently achieve the weight reduction of the laminated structure 30.
The lower limit of the ratio (T1/T) of the average thickness T1 of the center layer 13 to the average thickness T of the laminated structure 30 is preferably 0.4, more preferably 0.5, and even more preferably 0.6. On the other hand, the upper limit of the ratio (T1/T) is preferably 0.9, more preferably 0.8. If the ratio (T1/T) does not satisfy the lower limit, the thickness of the core layer 13 may be insufficient, the rigidity of the laminated structure 30 may not be sufficiently obtained, or the total thickness of the first layer 11 and the second layer 12 may be excessively large, and it may be difficult to achieve weight reduction of the laminated structure 30. In contrast, if the ratio (T1/T) exceeds the upper limit, the thickness of the center layer 13 becomes excessively large, and there is a possibility that it is difficult to achieve weight reduction of the laminated structure 30 or that it is difficult to sufficiently reinforce the center layer 13 from both sides by the first layer 11 and the second layer 12.
As the lower limit of the apparent density of the core layer 13, it is preferably 10kg/m 3 More preferably 20kg/m 3 . On the other hand, the upper limit of the apparent density of the core layer 13 is preferably 200kg/m 3 More preferably 150kg/m 3 Further preferably 100kg/m 3 . If the apparent density does not satisfy the lower limit, there is a possibility that the laminated structure 30 is insufficiently stiff. In contrast, if the apparent density exceeds the upper limit, there is a possibility that it is difficult to sufficiently achieve the weight reduction of the laminated structure 30.
In the case where the first layer 11 and the second layer 12 are both carbon fiber reinforced resin layers (CFRP layers), the lower limit of the ratio of the apparent density of the intermediate layer 13 to the apparent density of the first layer 11 and the second layer 12 is preferably 0.01, more preferably 0.02. On the other hand, the upper limit of the ratio is preferably 0.10, more preferably 0.05, and further preferably 0.04. By setting the ratio within the above range, the weight reduction and the high rigidity of the laminated structure 30 are easily promoted.
Method for manufacturing wooden golf club head
An example of a method of manufacturing the wood golf club head 1 will be described with reference to fig. 5. The method for manufacturing a wood-type golf club head (hereinafter simply referred to as "the manufacturing method") is used as a method for manufacturing a wood-type golf club head 1 having a hollow head body 10, which has an outer shell 20 including a face portion 2, a crown portion 3, and a sole portion 4, and a laminated structure 30 provided on at least a part of the outer shell 20. In the manufacturing method, a core layer 13 having an apparent density smaller than that of the first layer 11 and the second layer 12 is arranged between the first layer 11 and the second layer 12 arranged at intervals in the thickness direction via an adhesive (S1), a sandwiching pressure is applied to the first layer 11 and the second layer 12 (S2), and the first layer 11 and the second layer 12 are bonded to the core layer 13 via the adhesive (S3).
(S1)
In S1, the first layer 11 and the second layer 12 are molded, for example, using molds, respectively. In S1, the surface of the first layer 11 and the second layer 12 (the surface on the side where the layers are laminated with the core layer 13) is subjected to a surface treatment. Specific means of the surface treatment include, for example, a sand blast method, a peeling method (a method of adhering a release layer and peeling after curing), and the like. The surface treatment is performed, for example, to roughen the facing surface to improve wettability of the adhesive. In the case where there is no obstacle in applying the adhesive to the facing surfaces of the first layer 11 and the second layer 12, the surface treatment may be omitted.
Next, in S1, the adhesive is applied to the facing surfaces of the first layer 11 and the second layer 12, respectively. As the adhesive, for example, an adhesive containing a thermosetting resin such as an epoxy resin, an acrylic resin, or polyurethane can be used.
Next, in S1, the core layer 13 is disposed between the facing surfaces of the first layer 11 and the second layer 12 to which the adhesive is applied, respectively. At this time, by using a type including a honeycomb core as the center layer 13, even when the facing surfaces of the first layer 11 and the second layer 12 are curved, the center layer 13 is easily curved to follow the curved shape of the first layer 11 and the second layer 12.
(S2)
In S2, a clamping pressure is applied to the first layer 11 and the second layer 12 in a state of the core layer 13 in the adhesive arrangement between the facing surfaces of the first layer 11 and the second layer 12. The clamping of S2 can be performed using a mold corresponding to the shape of the outer case 20, for example.
(S3)
S3 may be performed simultaneously with S2 or after S2. In the case where the adhesive contains a thermosetting resin, the intermediate layer 13 is bonded to the first layer 11 and the second layer 12 by heating the adhesive in S3. The stacked structure 30 is formed by bonding in S3.
< advantage >
In the wood-type golf club head 1, since the laminated structure 30 formed by sandwiching the center layer 13 between the first layer 11 and the second layer 12 is provided in at least a part of the outer shell 20, the laminated structure 30 can achieve weight reduction and high rigidity of a desired part of the outer shell 20. That is, since the apparent density of the center layer 13 of the wood golf club head 1 is smaller than the apparent densities of the first layer 11 and the second layer 12, the weight of the entire laminated structure 30 can be reduced even if the thickness of the center layer 13 is relatively large. Further, the rigidity of the laminated structure 30 can be improved by sandwiching the intermediate layer 13 between the first layer 11 and the second layer 12. As a result, the wood-type golf club head 1 can be reduced in weight and increased in rigidity in a desired portion of the outer shell 20, as compared with, for example, a conventional structure having a homogeneous layer structure (e.g., a structure in which a plurality of prepregs are laminated in a plurality of layers).
The method for manufacturing a wood golf club head can manufacture a wood golf club head 1 having an outer shell 20 capable of realizing weight reduction and high rigidity of a desired portion.
Other embodiments
The embodiment is not limited to the configuration of the present invention. Therefore, the above-described embodiments can omit, replace, or add constituent elements of each part of the above-described embodiments based on the description of the present specification and the common technical knowledge, and should be interpreted as falling within the scope of the present invention.
The structure of the whole outer case is not limited to the structure described in the above embodiment. For example, the outer shell may have no cover at the crown. In addition, even when the cap is provided in the crown portion, the laminated structure may be disposed at a portion other than the cap.
From the viewpoint of weight reduction, the center layer is preferably porous. However, the wood golf club head may be configured such that the core layer does not have voids by using a material having a small specific gravity as the material of the core layer. In the case where the core layer is porous, the shape of the hollow holes provided in the core layer is not limited to the shape described in the above embodiment.
Industrial applicability
As described above, the wood-type golf club head according to the aspect of the present invention is suitable for a case where weight reduction and rigidity increase are achieved for a desired portion of the outer case.
Claims (9)
1. A wood golf club head is characterized by comprising a hollow club head body having an outer shell comprising a face portion, a crown portion and a sole portion,
a laminated structure having a first layer and a second layer arranged with a gap therebetween in the thickness direction and a core layer arranged between the first layer and the second layer is provided on at least a part of the outer case,
the apparent density of the central layer is less than the apparent density of the first and second layers.
2. A wood golf club head according to claim 1, wherein,
the first layer and the second layer are fiber reinforced resin layers, respectively.
3. A wood golf club head according to claim 1 or 2, wherein,
the middle core layer is porous.
4. A wood golf club head according to claim 3, wherein,
the core layer has a plurality of through holes penetrating in the thickness direction.
5. A wood golf club head according to claim 3 or 4, wherein,
the middle core layer comprises a foaming resin or a honeycomb core.
6. A wood golf club head according to any one of claims 1 to 5,
the ratio of the average thickness of the core layer to the average thickness of the laminated structure is 0.4 to 0.9.
7. A wood golf club head according to any one of claims 1 to 6,
the apparent density of the middle core layer is 10kg/m 3 200kg/m above 3 The following is given.
8. The wood golf club head according to any one of claims 1 to 7, wherein,
the laminated structure is disposed at the crown.
9. A method for manufacturing a wood-type golf club head comprising a hollow club head body having an outer shell comprising a face portion, a crown portion and a sole portion, wherein at least a part of the outer shell has a laminated structure,
and a core layer having an apparent density smaller than that of the first layer and the second layer is disposed between the first layer and the second layer disposed at intervals in the thickness direction, and the first layer and the second layer are bonded to the core layer by the adhesive agent by applying a clamping pressure to the first layer and the second layer.