CN116043554A - 一种涤纶及涤纶混纺织物去污精练剂及用途 - Google Patents
一种涤纶及涤纶混纺织物去污精练剂及用途 Download PDFInfo
- Publication number
- CN116043554A CN116043554A CN202211722727.1A CN202211722727A CN116043554A CN 116043554 A CN116043554 A CN 116043554A CN 202211722727 A CN202211722727 A CN 202211722727A CN 116043554 A CN116043554 A CN 116043554A
- Authority
- CN
- China
- Prior art keywords
- terylene
- polyester
- acid
- detergent
- blended
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种涤纶及涤纶混纺织物去污精练剂及其用途。该去污精练剂按质量份数计其组成为腰果酚烷氧基化合物10～40份，螯合分散剂1～10份，余量为水。本发明可以应用于不加碱剂的前处理加工工艺，也可以应用于高温精练染色同浴加工工艺，能有效去除涤纶及涤纶混纺织物因织造时造成的油剂残留和因工厂管理不当、存放不当而造成布面污渍，避免面料浪费，节约成本。
Description
技术领域
本发明属于纺织印染前处理技术领域，一种涤纶及涤纶混纺织物去污精练剂及用途。
背景技术
近年来，织机的针织油沾污、坯布的室外堆置，使涤纶及涤纶混纺织物在加工前出现了更多的沾污。污物的成分也越来越复杂，包括织机的针织油、设备老化的润滑油、场地上的灰尘、脚印以及其他生产污迹。这些污物如果无法完全去除，会造成面料的浪费和影响面料的整洁度。目前对于涤纶及涤纶混纺织物大片污渍去除问题，还没有具备广泛的市场认可度的产品，同时此类产品通用性也不强，前处理加工过程中必须加碱剂才能获得最佳的应用效果，在高温精练染色同浴加工时也没有良好的应用效果。
因此，迫切需要开发出一种去污能力优异、适用范围较广的涤纶及涤纶混纺织物去污精练剂，可以应对不同条件下的前处理，同时保证后续染色、后整体加工需求的前处理效果。
发明内容
本发明主要是解决现有技术中存在的不足，提供一种从而使因织造残留油剂、工厂管理不当、存放不当而造成布面污渍污染的布样可以正常加工的一种涤纶及涤纶混纺织物去污精练剂及用途。
本发明的上述技术问题主要是通过下述技术方案得以解决的：
一种涤纶及涤纶混纺织物去污精练剂，包括以下质量份数：
腰果酚烷氧基化合物：10～40份；螯合分散剂：1～10份；余量为水。
作为优选，所述腰果酚烷氧基化合物的通式为：
其中，R1为碳原子数2～3的亚烷基，n为1～30的整数；
R2的通式为C15H31、C15H29、C15H27、C15H25。
作为优选，所述所述螯合分散剂为柠檬酸、柠檬酸钠、葡萄糖酸、葡萄糖酸钠、乙二胺四乙酸(EDTA)、二乙基三胺五乙酸(DTPA)、氮川三乙酸(NTA)、HEDP、DTPMPA、聚丙烯酸、聚马来酸、聚马来酸丙烯酸、改性聚丙烯酸中的一种或两种以上的混合。
作为优选，为了减少泡沫对加工处理的影响以及保证精练剂的存储安定性，精练剂还包括下述组分：消泡剂0～0.5份，防腐剂0～0.5份。
作为优选，所述的消泡剂为聚醚类消泡剂或有机硅类消泡剂，所述防腐剂为异噻唑啉酮类。
一种涤纶及涤纶混纺织物去污精练剂的用途，包括：
用于涤纶及涤纶混纺织物去污前处理；
用于涤纶及涤纶混纺织物去污增白前处理；
用于涤纶及涤纶混纺织物染色去污一浴处理。
作为优选，用于涤纶及涤纶混纺织物去污前处理，按以下步骤进行：
(1)、在25～60℃下将涤纶或涤纶混纺织物、按比例配制好的前处理液加入高温高压染色机中；其中，所述前处理液是由30％双氧水0～5g/L，烧碱0～1.5g/L，精练剂1～3g/L共同配制完成；
(2)设置参数，以2～3℃/min升温至90～100℃，保温运行20～40min；
(3)然后洗净酸中和10～15min，冷水洗净，烘干，即制得去污处理后的涤纶或涤纶混纺织物。
作为优选，用于涤纶及涤纶混纺织物去污增白前处理，按以下步骤进行：
(1)在25～60℃下将涤纶或涤纶混纺织物、按比例配制好的前处理液加入高温高压染色机中；其中，所述前处理液是由30％双氧水0～5g/L，烧碱0～1.5g/L，精练剂1～3g/L，荧光增白剂0～0.5g/L共同配制完成；
(2)设置参数，以2-3℃/min升温至120～135℃，保温运行20～40min；
(3)然后洗净酸中和15～30min，冷水洗净，烘干，即制得去污处理后的涤纶或涤纶混纺织物。
作为优选，用于涤纶及涤纶混纺织物染色去污一浴处理，按以下步骤进行：
(1)在25～60℃下将涤纶或涤纶混纺织物、按比例配制好的处理液加入高温高压染色机中；其中，所述处理液是由醋酸0.5～1g/L，精练剂1～3g/L,匀染剂0.5～1.5g/L，分散染料0.3～5g/L共同配制完成；
(2)设置参数，以2-3℃/min升温至120～135℃，保温运行20～40min；
(3)然后降温至80℃，在80℃下还原洗净15～30min，酸中和，冷水洗净，烘干，即制得去污处理后的涤纶或涤纶混纺织物。
与现有技术相比，本发明的有益效果：
(1)本发明提供了一种涤纶及涤纶混纺织物去污精练剂，本发明可以对涤纶及涤纶混纺织物因织造时造成的油剂残留和因工厂管理不当、存放不当而造成布面污物有良好的洗涤、去除效果，可以做到基本洗净的效果。该精练剂适用范围较广，在前处理加工过程中即使在不加碱剂的条件下，也有良好的去污能力，可以省除碱性精练后的中和工序，节约成本。
(2)本发明对涤纶及涤纶混纺织物上油剂有优良的乳化、去除效果，且在精练染色同浴加工时，对染料分散性影响小，精练效果好。
附图说明
图1为本发明中去污前处理前后织物布面污渍去除效果图：(a)去除前，(b)去除后。
图2为本发明中去污增白前处理前后织物布面污渍去除效果图：(c)去除前，(d)去除后。
具体实施方式
下面通过实施例，对本发明的技术方案作进一步具体的说明。
在下文的描述中，给出了大量具体的细节以便提供对本发明更为彻底的理解。然而，对于本领域技术人员而言显而易见的是，本发明可以无需一个或多个这些细节而得以实施。在其他的例子中，为了避免与本发明发生混淆，对于本领域公知的一些技术特征未进行描述。
下面结合实施例，对本发明作进一步说明，所述的实施例的示例旨在解释本发明，而不能理解为对本发明的限制。实施例中未注明具体技术和反应条件者，可按照本领域内的文献所描述的技术或条件或产品说明书进行。
实施例1-5中：一种涤纶及涤纶混纺织物去污精练剂的组分及用量(重量份)，如表1所示。
表1：去污精练剂的组分及用量：
对比例1:
本对比例与实施例1的区别在于，去污精练剂中腰果酚烷氧基化合物为10份。
对比例2:
本对比例与实施例1的区别在于，去污精练剂中腰果酚烷氧基化合物为50份。
对比例3:
本对比例与实施例1的区别在于，去污精练剂中采用常规的脂肪醇烷氧基化合物代替腰果酚烷氧基化合物。
以下通过实验对本发明提供的精练剂在不同用途上的性能效果进行测试。
一、用于涤纶及涤纶混纺织物去污前处理
工艺流程：污渍布样挑选→前处理液配制→去污前处理
污渍布样挑选：所述布样为工厂室内、室外长期堆放，存在油渍污迹、鞋底印污迹及其他生产污迹的涤纶或涤纶混纺布样。
前处理液配制：所述前处理液是由30％双氧水3g/L，烧碱1g/L，精练剂2g/L共同配制而成的。
去污前处理：在室温下将污渍布样、按比例配制好的前处理液加入高温高压染色机中；设置参数，以2℃/min升温至90℃，保温运行30min；然后降温，洗净酸中和15min，冷水洗净，烘干，即制得去污处理后的涤纶或涤纶混纺织物。
实施例1-4和对比例1-3所制得的涤纶或涤纶混纺织物的去污效果，如表2所示。
表2：去污前处理后织物去污效果
二、用于涤纶及涤纶混纺织物去污增白前处理
工艺流程：污渍布样制造→前处理液配制→去污增白前处理
污渍布样制造：使用石炭、灰尘、铁锈磨成粉末并混合矿物油、针织油、墨汁等制成污染液，于涤纶或涤纶混纺针织布样滴下以上污染液，放置两天后170℃定型1min，制成污渍布样。
前处理液配制：所述前处理液是由30％双氧水3g/L，烧碱1g/L，精练剂2g/L，荧光增白剂0.3g/L共同配制而成的。
去污增白前处理：在室温下将污渍布样、按比例配制好的前处理液加入高温高压染色机中；设置参数，以3℃/min升温至130℃，保温运行30min；然后降温，洗净酸中和15min，冷水洗净，烘干，即制得去污处理后的涤纶或涤纶混纺织物。
白度测试：采用Datacolor反射分光光度仪对织物进行白度测试。白度值越大，表明织物去污后白度越好。
实施例1-4和对比例1-3所制得的涤纶或涤纶混纺织物的去污和白度结果，如表3所示。
表3：去污增白前处理后织物去污效果和白度结果
三、用于涤纶及涤纶混纺织物染色去污一浴处理
工艺流程：污渍布样挑选→处理液配制→染色去污一浴处理
污渍布样挑选：所述布样为工厂室内、室外长期堆放，存在油渍污迹、鞋底印污迹及其他生产污迹的涤纶或涤纶混纺布样。
处理液配制：所述处理液是由醋酸1g/L，精练剂2g/L，分散染料1g/L，匀染剂1g/L共同配制而成的，其中分散染料为市售79#蓝染料，匀染剂为市售匀染剂日华化学NICCASUNSOLT匀染剂。
染色去污一浴处理：在室温下将织物、按比例配置好的处理液加入高温高压染色机中；设置参数，以3℃/min升温至130℃，保温运行30min；然后降温至80℃，在80℃下还原洗20min，酸中和，冷水洗净，烘干，即制得染色去污一浴处理后的涤纶或涤纶混纺织物。
颜色深度(K/S值)测试：采用Datacolor反射分光光度仪对染色织物进行K/S值测试。
摩擦牢度测试：按照GB/T 3920-2008方法，对染色织物进行干湿摩擦测试。
实施例1-4和对比例1-3所制得的涤纶或涤纶混纺织物的性能效果，如表4所示。
表4：染色去污一浴处理后织物性能效果
综上所述，本发明采用腰果酚烷氧基化合物作为精练剂的主体成分，对布面上残留的油剂和污渍具有良好的乳化、去除效果，并且在精练染色同浴加工时，对染色性能影响小；同时与螯合分散剂复配，增强了精练剂的螯合性能，减少钙、镁等离子对精练效果的影响。
Claims (9)
1.一种涤纶及涤纶混纺织物去污精练剂，其特征在于：包括以下质量份数：
腰果酚烷氧基化合物：10～40份；螯合分散剂：1～10份；余量为水。
2.根据权利要求1所述的一种涤纶及涤纶混纺织物去污精练剂，其特征在于：所述腰果酚烷氧基化合物的通式为：
其中，R1为碳原子数2～3的亚烷基，n为1～30的整数；
R2的通式为C15H31、C15H29、C15H27、C15H25。
3.根据权利要求1所述的一种涤纶及涤纶混纺织物去污精练剂，其特征在于：所述所述螯合分散剂为柠檬酸、柠檬酸钠、葡萄糖酸、葡萄糖酸钠、乙二胺四乙酸(EDTA)、二乙基三胺五乙酸(DTPA)、氮川三乙酸(NTA)、HEDP、DTPMPA、聚丙烯酸、聚马来酸、聚马来酸丙烯酸、改性聚丙烯酸中的一种或两种以上的混合。
4.根据权利要求1所述的一种涤纶及涤纶混纺织物去污精练剂，其特征在于：为了减少泡沫对加工处理的影响以及保证精练剂的存储安定性，精练剂还包括下述组分：消泡剂0～0.5份，防腐剂0～0.5份。
5.根据权利要求4所述的一种涤纶及涤纶混纺织物去污精练剂，其特征在于：所述的消泡剂为聚醚类消泡剂或有机硅类消泡剂，所述防腐剂为异噻唑啉酮类。
6.一种涤纶及涤纶混纺织物去污精练剂的用途，其特征在于：包括：
用于涤纶及涤纶混纺织物去污前处理；
用于涤纶及涤纶混纺织物去污增白前处理；
用于涤纶及涤纶混纺织物染色去污一浴处理。
7.根据权利要求6所述的一种涤纶及涤纶混纺织物去污精练剂的用途，其特征在于：用于涤纶及涤纶混纺织物去污前处理，按以下步骤进行：
(1)、在25～60℃下将涤纶或涤纶混纺织物、按比例配制好的前处理液加入高温高压染色机中；其中，所述前处理液是由30％双氧水0～5g/L，烧碱0～1.5g/L，精练剂1～3g/L共同配制完成；
(2)设置参数，以2～3℃/min升温至90～100℃，保温运行20～40min；
(3)然后洗净酸中和10～15min，冷水洗净，烘干，即制得去污处理后的涤纶或涤纶混纺织物。
8.根据权利要求6所述的一种涤纶及涤纶混纺织物去污精练剂的用途，其特征在于：用于涤纶及涤纶混纺织物去污增白前处理，按以下步骤进行：
(1)在25～60℃下将涤纶或涤纶混纺织物、按比例配制好的前处理液加入高温高压染色机中；其中，所述前处理液是由30％双氧水0～5g/L，烧碱0～1.5g/L，精练剂1～3g/L，荧光增白剂0～0.5g/L共同配制完成；
(2)设置参数，以2-3℃/min升温至120～135℃，保温运行20～40min；
(3)然后洗净酸中和15～30min，冷水洗净，烘干，即制得去污处理后的涤纶或涤纶混纺织物。
9.根据权利要求6所述的一种涤纶及涤纶混纺织物去污精练剂的用途，其特征在于：用于涤纶及涤纶混纺织物染色去污一浴处理，按以下步骤进行：
(1)在25～60℃下将涤纶或涤纶混纺织物、按比例配制好的处理液加入高温高压染色机中；其中，所述处理液是由醋酸0.5～1g/L，精练剂1～3g/L,匀染剂0.5～1.5g/L，分散染料0.3～5g/L共同配制完成；
(2)设置参数，以2-3℃/min升温至120～135℃，保温运行20～40min；
(3)然后降温至80℃，在80℃下还原洗净15～30min，酸中和，冷水洗净，烘干，即制得去污处理后的涤纶或涤纶混纺织物。