CN116043229A - 一种环保型对镀锌层友好的制管液及其制备方法 - Google Patents
一种环保型对镀锌层友好的制管液及其制备方法 Download PDFInfo
- Publication number
- CN116043229A CN116043229A CN202211726985.7A CN202211726985A CN116043229A CN 116043229 A CN116043229 A CN 116043229A CN 202211726985 A CN202211726985 A CN 202211726985A CN 116043229 A CN116043229 A CN 116043229A
- Authority
- CN
- China
- Prior art keywords
- friendly
- organic
- pipe making
- environment
- making liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种环保型对镀锌层友好的制管液,其包括以下重量百分比的组分：醇胺10％‑20％；聚醚10％‑20％；有机脂肪二元羧酸10％～15％；有机杂环三元羧酸20％～25％；有机酰基氨基酸10％～15％；水余量。本发明相较于现有技术可以解决现有技术中镀锌制管液防锈性能不理想、不环保的问题。
Description
技术领域
本发明涉及镀锌制管液领域，尤其涉及一种环保型对镀锌层友好的制管液及其制备方法。
背景技术
镀锌是将金属产品浸入熔融的锌浴中进行涂覆。镀锌适合钢产品，因为熔融的锌与钢反应，在金属上形成保护性密封。镀锌的成本比许多其他精加工方法低，并且使用寿命长。镀锌的一个主要好处是，如果金属被损坏，其余区域仍受到保护，因此较小的损坏无需修补。
镀锌是一个过程，保护层只需要浸一浸就可以保护产品。其他涂料则需要上漆或喷涂，花费更多的时间。镀锌的干燥过程也更快，只需较短的时间，而其它涂层则需要更长的时间。
制管液在钢板加工过程中起润滑，冷却，清洗，防锈的作用。钢铁在现代生活中作用重大，是生产生活的重要原料，是国民经济的重要支柱。目前中国钢铁产能雄厚，钢板在加工，放置，运输，堆放过程中，由于和空气中的水分和氧气以及加工介质中的电解质接触，极易发生腐蚀生锈，影响产品品质，造成经济损失。所以，防锈技术的研究意义深远。
镀锌制管液一般由防锈剂、pH调整剂、金属缓蚀剂、抗菌添加剂、润滑添加剂、抗硬水添加剂，沉降剂以及水等组成。目前防锈添加剂有铬酸盐，硅酸盐，亚硝酸盐，硼酸盐和酯等。铬酸盐防锈好，但易失效，而且对人和环境有害，早已禁用。硅酸盐防锈效果有限，时间久了易结垢。亚硝酸盐防锈好，但易结晶和析出，形成白点，而且其是致癌物质，对人体有害已逐步退出工业生产。
发明内容
本发明的目的在于：为了解决现有技术中镀锌制管液防锈性能不理想、不环保的问题，而提出的一种环保型对镀锌层友好的制管液及其制备方法。
为此，一方面，本发明提供了一种环保型对镀锌层友好的制管液,其包括以下重量百分比的组分：
作为上述技术方案的进一步描述：
包括以下重量百分比的组分：醇胺12％-18％；聚醚13％-19％；有机脂肪二元羧酸14％～19％；有机杂环三元羧酸21％～24％；有机酰基氨基酸11％～14％；水余量。
作为上述技术方案的进一步描述：
包括以下重量百分比的组分：醇胺15％；聚醚16％；有机脂肪二元羧酸16％；有机杂环三元羧酸23％；有机酰基氨基酸13％；水余量。
作为上述技术方案的进一步描述：
所述有机脂肪二元羧酸为有机脂肪二元羧酸C10-C12。
作为上述技术方案的进一步描述：
所述有机脂肪二元羧酸C10-C12的牌号为DDDA。
作为上述技术方案的进一步描述：
所述有机杂环三元羧酸的牌号为L190。
作为上述技术方案的进一步描述：
所述有机酰基胺基酸的牌号为NEUF 585。
作为上述技术方案的进一步描述：
所述醇胺为三乙醇胺。
作为上述技术方案的进一步描述：
所述聚醚为巴斯夫聚醚1740。
另一方面，本发明还提供了一种环保型对镀锌层友好的制管液的制备方法，其包括以下步骤：
1)根据上述的组分及其配比，准备各物料；
2)将所述物料搅拌均匀即成。
综上所述，由于采用了上述技术方案，本发明的有益效果是：
本发明提供的一款环保型对镀锌层友好的制管液，主要针对使用液的防锈性进行研究，本发明中的各种添加剂的复配之后的效果，不论是防锈，还是抗硬水性能，泡沫效果都远比一种添加剂的效果好；此外，复配之后的添加剂包的添加量也比单一的添加剂用量少，相对而言，成本降低；另外，几种添加剂可生物降解，环保；选择有机酸与醇胺反应得到的有机羧酸醇铵盐和烷基醇酰胺作为主防锈剂，二者分子中的氮原子和氧原子都有孤对电子，可与铁等有空轨道的金属表面作用生成络合物膜，阻止氧、水等分子与金属表面接触，起到防锈。
因此，本发明相较于现有技术具有以下优点：
1)环保，低毒，且具有优良的生物降解性能；
2)泡沫低，使用液不会产生大量泡沫；
3)防锈性能优异，提供长效的防锈防腐；
4)清净性卓越，没有形成粘性残渣的倾向；
5)理想的抗硬水性能，水质适应性强。
具体实施方式
下面将更详细地描述本公开的示例性实施例。虽然显示了本公开的示例性实施例，然而应当理解，可以以各种形式实现本公开而不应被这里阐述的实施例所限制。相反，提供这些实施例是为了能够更透彻地理解本公开，并且能够将本公开的范围完整的传达给本领域的技术人员。
所涉及的化学添加剂基本信息(以下各种添加剂均可以通过商业途径购买到)：
DDDA化学成分：十二碳二酸；活性物含量：约99.7％；作为有机防锈剂被广泛应用，以取代无机防锈剂。能够在低浓度，无毒，可生物降解等条件下达到极好的防锈效果；
L190化学成分：有机杂环三元羧酸；活性物含量：约65％；出色的防锈效果，优异的水溶性，抗硬水好，泡沫小，不易形成胶状物，环保无害；
NEUF 585化学成分：有机酰基胺基酸；活性物含量：≥96.5％；
醇胺化学成分：三乙醇胺；活性物含量：约99.7％；作为有机防锈剂被广泛应用，能够在低浓度，无毒，可生物降解等条件下达到极好的防锈效果；
聚醚化学成分：1740；具有优异的水溶性，气味非常低，起泡低消泡快，低温流动性好，出色的润滑性能，易生物降解。
通过实验得出三种添加剂复配之后效果最佳，复配比例如下：
醇胺15％；聚醚16％；有机脂肪二元羧酸16％；有机杂环三元羧酸23％；有机酰基氨基酸13％；水余量；
还可以为以下范围内的其他配比：
按比例取制备材料:
取包括以下重量百分比的制备材料：将有机脂肪二元羧酸16％、有机杂环三元羧酸23％和有机酰基氨基酸13％混合搅拌均匀，然后加入醇胺15％、聚醚16％和水搅拌均匀。
实施例一：
取一款普通的钢板水基加工液A，普通型制管液B与上述配方样品(以下称“环保制管液”)进行防锈性能、抗硬水性能、消泡性能以及环保性对比，实验数据如下表：
对比结果：结果表明，环保制管液各项性能与两组样品对比都很优异，尤其是防锈性能和抗硬水性能。
本发明提供的一款环保型对镀锌层友好的制管液，主要针对使用液的防锈性进行研究，本发明中的各种添加剂的复配之后的效果，不论是防锈，还是抗硬水性能，泡沫效果都远比一种添加剂的效果好；此外，复配之后的添加剂包的添加量也比单一的添加剂用量少，相对而言，成本降低；另外，几种添加剂可生物降解，环保；选择有机酸与醇胺反应得到的有机羧酸醇铵盐和烷基醇酰胺作为主防锈剂，二者分子中的氮原子和氧原子都有孤对电子，可与铁等有空轨道的金属表面作用生成络合物膜，阻止氧、水等分子与金属表面接触，起到防锈。
因此，本发明相较于现有技术具有以下优点：
1)环保，低毒，且具有优良的生物降解性能；
2)泡沫低，使用液不会产生大量泡沫；
3)防锈性能优异，提供长效的防锈防腐；
4)清净性卓越，没有形成粘性残渣的倾向；
5)理想的抗硬水性能，水质适应性强。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (10)
1.一种环保型对镀锌层友好的制管液,其特征在于，包括以下重量百分比的组分：
2.根据权利要求1所述的一种环保型对镀锌层友好的制管液，其特征在于，包括以下重量百分比的组分：醇胺12％-18％；聚醚13％-19％；有机脂肪二元羧酸14％～19％；有机杂环三元羧酸21％～24％；有机酰基氨基酸11％～14％；水余量。
3.根据权利要求1所述的一种环保型对镀锌层友好的制管液，其特征在于，包括以下重量百分比的组分：醇胺15％；聚醚16％；有机脂肪二元羧酸16％；有机杂环三元羧酸23％；有机酰基氨基酸13％；水余量。
4.根据权利要求1-3任一所述的一种环保型对镀锌层友好的制管液，其特征在于，所述有机脂肪二元羧酸为有机脂肪二元羧酸C10-C12。
5.根据权利要求4任一所述的一种环保型对镀锌层友好的制管液，其特征在于，所述有机脂肪二元羧酸C10-C12的牌号为DDDA。
6.根据权利要求1-3任一所述的一种环保型对镀锌层友好的制管液，其特征在于，所述有机杂环三元羧酸的牌号为L190。
7.根据权利要求1-3任一所述的一种环保型对镀锌层友好的制管液，其特征在于，所述有机酰基胺基酸的牌号为NEUF 585。
8.根据权利要求1-3任一所述的一种环保型对镀锌层友好的制管液，其特征在于，所述醇胺为三乙醇胺。
9.根据权利要求1-3任一所述的一种环保型对镀锌层友好的制管液，其特征在于，所述聚醚为巴斯夫聚醚1740。
10.一种环保型对镀锌层友好的制管液的制备方法，其特征在于，包括以下步骤：
1)根据权利要求1-9任一所述的组分及其配比，准备各物料；
2)将所述物料搅拌均匀即成。