CN115917366A - 光学层叠体、物品、光学层叠体的制造方法 - Google Patents
光学层叠体、物品、光学层叠体的制造方法 Download PDFInfo
- Publication number
- CN115917366A CN115917366A CN202180051438.0A CN202180051438A CN115917366A CN 115917366 A CN115917366 A CN 115917366A CN 202180051438 A CN202180051438 A CN 202180051438A CN 115917366 A CN115917366 A CN 115917366A
- Authority
- CN
- China
- Prior art keywords
- layer
- optical
- antifouling
- optical laminate
- less
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
该光学层叠体(101)是依次层叠塑料薄膜(11)、密合层(13)、光学功能层(14)和防污层(15)而成的光学层叠体,防污层(15)由蒸镀防污性材料而成的蒸镀膜构成,防污层(15)的膜厚为2.5nm以上,水蒸气透过率为1.5g/(m2·1天)以下,与液温55℃、浓度0.1mol/L的氢氧化钠水溶液接触4小时后的将正反射光考虑在内(SCI)的反射色的色相变化ΔE值小于10。
Description
技术领域
本发明涉及在表面具有防污层的光学层叠体以及具备该光学层叠体的物品、光学层叠体的制造方法。
本申请基于2020年9月10日在日本申请的特愿2020-151806号主张优先权,并在此引用其内容。
背景技术
例如,在平板显示器(FPD)、触摸面板、太阳能电池等中,作为光学层叠体,为了防止表面的反射而使用各种防反射膜。
以往,作为防反射膜,提出了具备在透明基板上依次层叠有高折射率层和低折射率层的多层膜的防反射膜。在这样的防反射膜的最外表面,通常以表面的保护、防污为目的而形成有防污层(表面保护层)。
近年来,防反射膜(光学层叠体)多用于智能手机、各种操作设备的触摸面板。由此,要求提高光学层叠体的耐磨损性。
例如,专利文献1中公开了通过将防污层的构成材料中所含的氟量设为特定的范围来提高耐磨损性的透明基板层叠体。
专利文献2中记载了一种防污层的形成方法,其在形成防污层之前,对被处理基材上的至少单面进行预处理,在该预处理后的表面形成防污层。另外,专利文献2中记载了预处理为高频放电等离子体法、电子束法、离子束法、蒸镀法、溅射法、碱处理法、酸处理法、电晕处理法、大气压辉光放电等离子体法中的任一种。
专利文献3中记载了一种防污性光学物品的制造方法,其通过蒸镀在基板表面形成防反射膜后,导入氧或氩进行等离子体处理,然后,真空蒸镀含氟有机硅化合物而形成防污层。
现有技术文献
专利文献
专利文献1:国际公开第2019/078313号
专利文献2:日本特开2006-175438号公报
专利文献3:日本特开2005-301208号公报
专利文献4:日本特许第6542970号公报
发明内容
发明所要解决的课题
然而,专利文献1中记载的透明基板层叠体存在如下课题:若反复摩擦,则对耐磨损性有帮助的未反应物被擦去,无法维持高耐磨损性。要求具备即使对于反复摩擦也能够维持高耐磨损性的防污层的光学层叠体。
本发明是鉴于上述问题而完成的,其目的在于提供具备耐久性优异的防污层的光学层叠体以及具备该光学层叠体的物品、光学层叠体的制造方法。
用于解决课题的方法
为了解决上述课题,本发明提出了以下的方法。
(1)本发明的第一方式的光学层叠体是依次层叠塑料薄膜、密合层、光学功能层和防污层而成的光学层叠体,上述防污层由蒸镀防污性材料而成的蒸镀膜构成,上述防污层的膜厚为2.5nm以上,水蒸气透过率为1.5g/(m2·1天)以下,与液温55℃、浓度0.1mol/L的氢氧化钠水溶液接触4小时后的将正反射光考虑在内(SCI)的反射色的色相变化ΔE值小于10。
(2)本发明的第二方式的光学层叠体是依次层叠塑料薄膜、密合层、光学功能层和防污层而成的光学层叠体,上述防污层由蒸镀防污性材料而成的蒸镀膜构成,上述防污层的膜厚为2.5nm以上,水蒸气透过率为1.5g/(m2·1天)以下,在与液温55℃、浓度0.1mol/L的氢氧化钠水溶液接触4小时后,使用荧光X射线分析法(XRF)测定的氟的残存率为85%以上。
(3)上述方式的光学层叠体中,下述式(1)所示的表面粗糙度的变化率可以为5~35%或下述式(2)所示的要素的平均长度的变化率可以为7~70%;
表面粗糙度的变化率(%)=((Ra2/Ra1)-1)×100(%)…式(1)
式(1)中,Ra1表示未进行表面处理而形成了防污层的、光学层叠体的防污层的表面粗糙度(Ra),Ra2表示对表面进行处理后形成了防污层的、光学层叠体的防污层的表面粗糙度(Ra);
要素的平均长度的变化率(%)=((RSm2/RSm1)-1)×100(%)…式(2)
式(2)中,RSm1表示未进行表面处理而形成了防污层的、光学层叠体的防污层的要素的平均长度(RSm),RSm2表示对表面进行处理后形成了防污层的光学层叠体的、防污层的要素的平均长度(RSm);
其中,Ra2为3nm以上且10nm以下,Rsm2为55nm以上且90nm以下。
(4)上述方式的光学层叠体中,雾度可以为2%以下,使布头往复4000次的擦伤性试验前后相对于水的接触角差为12°以下。
(5)上述方式的光学层叠体中,雾度可以为2%以下,使用依据JIS L0849的使用了钢丝棉的摩擦试验机,摩擦前与使钢丝棉水平往复运动500次的摩擦后相对于水的接触角差为12°以下。
(6)上述方式的光学层叠体中,雾度可以为2%以下,摩擦前和使钢丝棉水平往复运动500次的摩擦后的将正反射光考虑在内(SCI)的反射色的变化量(ΔE值)可以为3.0以下。
(7)上述方式的光学层叠体中,在氟系溶剂中照射40KHz、240W的超声波10分钟进行清洗后的通过XRF得到的防污层中的氟原子的残存量可以为70%以上。
(8)上述方式的光学层叠体中,雾度可以超过2%,使布头往复4000次的擦伤性试验前后相对于水的接触角差为7°以下。
(9)上述方式的光学层叠体中,使用荧光X射线分析法(XRF)测定的氟的初始量可以为0.03以上。
(10)上述方式的光学层叠体中,上述光学功能层可以包含选自防反射层和选择反射层中的任意1种。
(11)上述方式的光学层叠体中,上述光学功能层可以具备低折射率层。
(12)上述方式的光学层叠体中,上述光学功能层可以由低折射率层和高折射率层交替层叠而成的层叠体构成。
(13)上述方式的光学层叠体中,上述防污层可以与上述低折射率层接触而设置。
(14)上述方式的光学层叠体中,上述密合层可以包含金属或金属的氧化物。
(15)上述方式的光学层叠体中,上述密合层和上述光学功能层可以通过溅射形成。
(16)上述方式的光学层叠体中,上述防污性材料可以包含氟系有机化合物。
(17)上述方式的光学层叠体中,可以在上述透明基材与上述密合层之间进一步具备硬涂层。
(18)本发明的第四方式的物品可以具备上述方式的光学层叠体。
(19)本发明的第五方式的光学层叠体的制造方法为上述方式的光学层叠体的制造方法,其具有:光学功能层的成膜工序,其交替地具有在小于0.5Pa的真空度下形成低折射率层的工序和在小于1.0Pa的真空度下形成高折射率层的工序;辉光放电处理工序,其利用辉光放电对上述光学功能层的表面进行表面处理;以及防污层形成工序,其在上述光学功能层的一面侧形成由蒸镀膜构成的上述防污层,上述蒸镀膜通过真空蒸镀而蒸镀有防污性材料。
(20)上述方式的光学层叠体的制造方法可以具有通过溅射形成上述光学功能层的光学功能层形成工序,在减压下连续进行上述光学功能层形成工序和上述防污层形成工序。
发明效果
根据本发明,能够提供具备耐久性优异的防污层的光学层叠体以及具备该光学层叠体的物品、光学层叠体的制造方法。
附图说明
[图1]是示出本实施方式的光学层叠体的一例的截面图。
[图2]为示出本实施方式的光学层叠体的另一例的截面图。
[图3]为示出本实施方式的光学层叠体的另一例的截面图。
图4]是用于说明可用于本实施方式的光学层叠体的制造方法的制造装置的一例的概略图。
具体实施方式
以下,适当参照附图对本实施方式进行详细说明。在以下的说明中使用的附图中,为了容易理解本发明的特征,方便起见,有时将成为特征的部分放大表示,各构成要素的尺寸比率等有时与实际不同。在以下的说明中例示的材质、尺寸等是一个例子,本发明并不限定于此,能够在起到其效果的范围内适当变更来实施。
[光学层叠体]
图1是用于说明本实施方式的光学层叠体的一例的截面图。
如图1所示,本实施方式的光学层叠体101是依次层叠透明基材11、密合层13、光学功能层14和防污层15而成的。
密合层13是显现密合的层。
光学功能层14是表现出光学功能的层。光学功能是指控制作为光的性质的反射和透射、折射的功能,例如可列举出防反射功能、选择反射功能、透镜功能等。
光学功能层14优选包含选自防反射层和选择反射层中的任意1种。作为防反射层、选择反射层,可以使用公知的层。防反射层、选择反射层均可以为单层,也可以为多层的层叠体。
图2是表示本实施方式的光学层叠体的另一例的截面图。
图2所示的光学层叠体102是依次层叠透明基材11、硬涂层12、密合层13、光学功能层14和防污层15而成的。
密合层13是显现密合的层。
光学功能层14是表现出光学功能的层。光学功能是指控制作为光的性质的反射和透射、折射的功能,例如可列举出防反射功能、选择反射功能、透镜功能等。
光学功能层14优选包含选自防反射层和选择反射层中的任意1种。作为防反射层和选择反射层,可以使用公知的防反射层和选择反射层。防反射层、选择反射层均可以为单层,也可以为多层的层叠体。
图3是表示本实施方式的光学层叠体的另一例的截面图。
图3所示的光学层叠体101设置有防反射层作为图2所示的光学层叠体102中的光学功能层14。如图2所示,光学功能层14(防反射层)由交替层叠有低折射率层14b和高折射率层14a的层叠体构成。图2所示的光学功能层14从透明基材11侧起依次层叠有硬涂层12、密合层13、高折射率层14a、低折射率层14b、高折射率层14a、低折射率层14b、防污层15。因此,防污层15与光学功能层14所具有的低折射率层14b接触。
透明基材11由能够透过可见光区域的光的透明材料形成即可。例如,作为透明基材11,优选使用塑料薄膜。作为塑料薄膜的构成材料的具体例,可列举出聚酯系树脂、乙酸酯系树脂、聚醚砜系树脂、聚碳酸酯系树脂、聚酰胺系树脂、聚酰亚胺系树脂、聚烯烃系树脂、(甲基)丙烯酸系树脂、聚氯乙烯系树脂、聚偏二氯乙烯系树脂、聚苯乙烯系树脂、聚乙烯醇系树脂、聚芳酯系树脂、聚苯硫醚系树脂。
需要说明的是,本发明中所说的“透明材料”是指在不损害本发明的效果的范围内使用波长区域的光的透射率为80%以上的材料。
另外,在本实施方式中,“(甲基)丙烯酸”是指甲基丙烯酸和丙烯酸。
只要不显著损害光学特性,透明基材11中也可以含有增强材料。增强材料例如为纤维素纳米纤维、纳米二氧化硅等。特别优选使用聚酯系树脂、乙酸酯系树脂、聚碳酸酯系树脂、聚烯烃系树脂作为增强材料。具体而言,优选使用三乙酰纤维素(TAC)基材作为增强材料。
另外,透明基材11也可以使用作为无机基材的玻璃膜。
塑料薄膜为TAC基材时,在其一面侧形成硬涂层12时,会形成构成硬涂层12的成分的一部分渗透而成的渗透层。其结果是,透明基材11与硬涂层12的密合性变得良好,并且能够抑制由彼此的层间的折射率差引起的干涉条纹的产生。
透明基材11也可以是被赋予了光学功能和/或物理功能的膜。作为具有光学功能和/或物理功能的膜的例子,可列举出偏振板、相位差补偿膜、热射线屏蔽膜、透明导电膜、增亮膜、阻隔性提高膜等。
透明基材11的厚度没有特别限定,例如优选为25μm以上。透明基材11的膜厚更优选为40μm以上。
若透明基材11的厚度为25μm以上,则可确保基材自身的刚性,即使对光学层叠体10施加应力也不易产生褶皱。另外,透明基材11的厚度为25μm以上时,即使在透明基材11上连续地形成硬涂层12,也不易产生褶皱,制造上的担心少,因此优选。透明基材11的厚度为40μm以上时,更不易产生褶皱,是优选的。
在制造时,在用辊实施的情况下,透明基材11的厚度优选为1000μm以下,更优选为600μm以下。透明基材11的厚度为1000μm以下时,容易将制造中途的光学层叠体10和制造后的光学层叠体10卷绕成辊状,能够高效地制造光学层叠体10。另外,透明基材11的厚度为1000μm以下时,能够实现光学层叠体10的薄膜化、轻量化。透明基材11的厚度为600μm以下时,能够更高效地制造光学层叠体10,并且能够进一步薄膜化、轻量化,是优选的。
透明基材11可以对表面预先实施溅射、电晕放电、紫外线照射、电子束照射、化学转化、氧化等蚀刻处理和/或底涂处理。通过预先实施这些处理,能够提高与形成于透明基材11上的硬涂层12的密合性。另外,也优选在透明基材11上形成硬涂层12之前,根据需要对透明基材11的表面进行溶剂清洗、超声波清洗等,由此预先对透明基材11的表面进行除尘、清洁化。
作为硬涂层12,可以使用公知的硬涂层。硬涂层12可以仅由粘合剂树脂构成,也可以与粘合剂树脂一起在不损害透明性的范围内包含填料。作为填料,可以使用由有机物构成的填料,也可以使用由无机物构成的填料,还可以使用由有机物和无机物构成的填料。
作为硬涂层12中使用的粘合剂树脂,优选为透明性的粘合剂树脂,例如可以使用作为通过紫外线、电子射线而固化的树脂的电离放射线固化型树脂、热塑性树脂、热固性树脂等。
作为硬涂层12的粘合剂树脂中使用的电离放射线固化型树脂,可以举出(甲基)丙烯酸乙酯、(甲基)丙烯酸乙基己酯、苯乙烯、甲基苯乙烯、N-乙烯基吡咯烷酮等。
另外,作为具有2个以上不饱和键的电离放射线固化型树脂的化合物,例如可以举出三羟甲基丙烷三(甲基)丙烯酸酯、三丙二醇二(甲基)丙烯酸酯、二乙二醇二(甲基)丙烯酸酯、二丙二醇二(甲基)丙烯酸酯、季戊四醇三(甲基)丙烯酸酯、季戊四醇四(甲基)丙烯酸酯、二季戊四醇六(甲基)丙烯酸酯、1,6-己二醇二(甲基)丙烯酸酯、新戊二醇二(甲基)丙烯酸酯、三羟甲基丙烷三(甲基)丙烯酸酯、二(三羟甲基丙烷)四(甲基)丙烯酸酯、二季戊四醇五(甲基)丙烯酸酯、三季戊四醇八(甲基)丙烯酸酯、四季戊四醇十(甲基)丙烯酸酯、异氰脲酸三(甲基)丙烯酸酯、异氰脲酸二(甲基)丙烯酸酯、聚酯三(甲基)丙烯酸酯、聚酯二(甲基)丙烯酸酯、双酚二(甲基)丙烯酸酯、二甘油四(甲基)丙烯酸酯、金刚烷基二(甲基)丙烯酸酯、异冰片基二(甲基)丙烯酸酯、二环戊烷二(甲基)丙烯酸酯、三环癸烷二(甲基)丙烯酸酯、二(三羟甲基丙烷)四(甲基)丙烯酸酯等多官能化合物等。其中,优选使用季戊四醇三丙烯酸酯(PETA)、二季戊四醇六丙烯酸酯(DPHA)及季戊四醇四丙烯酸酯(PETTA)。需要说明的是,“(甲基)丙烯酸酯”是指甲基丙烯酸酯和丙烯酸酯。另外,作为电离放射线固化型树脂,也可以使用将上述化合物用PO(环氧丙烷)、EO(环氧乙烷)、CL(己内酯)等改性而得到的树脂。
作为硬涂层12的粘合剂树脂中使用的热塑性树脂,例如可以举出苯乙烯系树脂、(甲基)丙烯酸系树脂、乙酸乙烯酯系树脂、乙烯基醚系树脂、含卤素树脂、脂环式烯烃系树脂、聚碳酸酯系树脂、聚酯系树脂、聚酰胺系树脂、纤维素衍生物、有机硅系树脂及橡胶或弹性体等。上述热塑性树脂优选为非结晶性且可溶于有机溶剂(特别是能够溶解多种聚合物、固化性化合物的共用溶剂)。特别是从透明性和耐候性的观点出发,优选苯乙烯系树脂、(甲基)丙烯酸系树脂、脂环式烯烃系树脂、聚酯系树脂、纤维素衍生物(纤维素酯类等)等。
作为硬涂层12的粘合剂树脂中使用的热固性树脂,例如可以举出酚醛树脂、尿素树脂、邻苯二甲酸二烯丙酯树脂、三聚氰胺树脂、胍胺树脂、不饱和聚酯树脂、聚氨酯树脂、环氧树脂、氨基醇酸树脂、三聚氰胺-尿素共缩合树脂、硅树脂、聚硅氧烷树脂(包括笼状、梯状等所谓的倍半硅氧烷等)等。
硬涂层12可以包含有机树脂和无机材料,也可以是有机无机混合材料。作为一例,可以举出通过溶胶凝胶法形成的物质。作为无机材料,例如可列举出二氧化硅、氧化铝、氧化锆、二氧化钛。作为有机材料,例如可列举出丙烯酸树脂。
从防眩性、与后述的光学功能层14的密合性、抗粘连性的观点出发,硬涂层12中所含的填料可以根据光学层叠体10的用途选择各种填料。具体而言,例如可以使用二氧化硅(Si的氧化物)粒子、氧化铝(三氧化二铝)粒子、有机微粒等公知的物质。
硬涂层12例如可以包含粘合剂树脂和作为填料的二氧化硅粒子和/或氧化铝粒子。通过在硬涂层12中分散有作为填料的二氧化硅粒子和/或氧化铝粒子,能够在硬涂层12的表面形成微细的凹凸。这些二氧化硅粒子和/或氧化铝粒子可以在硬涂层12的光学功能层14侧的表面露出。在该情况下,硬涂层12的粘合剂树脂与光学功能层14牢固地接合。因此,硬涂层12与光学功能层14的密合性提高,硬涂层12的硬度变高,并且光学层叠体10的耐擦伤性变得良好。
硬涂层12的填料的平均粒径例如为800nm以下,优选为780nm以下,进一步优选为100nm以下。作为该尺寸的填料,例如优选使用二氧化硅粒子、氧化铝粒子等。若填料的粒径在该范围内,则光学层叠体10整体的雾度值为2%以下。雾度为2%以下的光学层叠体10的透明度高,成为所谓的透明型的防反射膜。
硬涂层12的填料的平均粒径例如可以为0.5μm以上。作为该尺寸的填料,例如优选使用丙烯酸树脂等有机微粒。若填料的粒径在该范围内,则光学层叠体10整体的雾度值超过2%。雾度超过2%的光学层叠体10具有防眩性,成为所谓的防眩(AG)型的防反射膜。在该情况下,填料的平均粒径也优选为10μm以下,进一步优选为5μm以下,特别优选为3μm以下。
作为硬涂层12中含有的填料,为了对硬涂层12赋予强韧性,可以在不损害光学特性的范围内使用各种增强材料。作为增强材料,例如可列举出纤维素纳米纤维。
硬涂层12的厚度没有特别限定,例如优选为0.5μm以上,更优选为1μm以上。硬涂层12的厚度优选为100μm以下。硬涂层12的厚度为0.5μm以上时,可得到充分的硬度,因此难以产生制造上的划痕。另外,硬涂层12的厚度为100μm以下时,能够实现光学层叠体10的薄膜化、轻量化。另外,硬涂层12的厚度为100μm以下时,难以产生制造中途的光学层叠体10弯曲时产生的硬涂层12的微裂纹,生产率变得良好。
硬涂层12可以是单一的层,也可以是多个层层叠而成的层。另外,也可以对硬涂层12进一步赋予例如紫外线吸收性能、抗静电性能、折射率调整功能、硬度调整功能等公知的功能。
另外,赋予硬涂层12的功能可以赋予单一的硬涂层中,也可以分割为多个层而赋予。
密合层13是为了使作为有机膜的透明基材11或硬涂层12与作为无机膜的光学功能层14的密合良好而形成的层。图3所示的光学层叠体10中,在硬涂层12与光学功能层14之间具备密合层13。密合层13具有使硬涂层12与光学功能层14密合的功能。密合层13优选由氧欠缺状态的金属氧化物或金属构成。氧欠缺状态的金属氧化物是指氧数与化学计量组成相比不足的状态的金属氧化物。作为氧欠缺状态的金属氧化物,例如可列举出SiOx、AlOx、TiOx、ZrOx、CeOx、MgOx、ZnOx、TaOx、SbOx、SnOx、MnOx等。另外,作为金属,可列举出Si、Al、Ti、Zr、Ce、Mg、Zn、Ta、Sb、Sn、Mn、In等。密合层13例如可以是SiOx中的x大于0且小于2.0的层。另外,密合层可以由多种金属或金属氧化物的混合物形成。
从维持透明性和与光学功能层的密合性、得到良好的光学特性的观点出发,密合层的厚度优选为超过0nm且20nm以下,特别优选为1nm以上且10nm以下。
光学功能层14是表现出防反射功能的层叠体。图3所示的光学功能层14是从密合层13侧起依次交替层叠有高折射率层14a和低折射率层14b的合计4层的层叠体。高折射率层14a和低折射率层14b的层数没有特别限定,高折射率层14a和低折射率层14b的层数可以设为任意的层数。
在图3所示的光学层叠体10中,光学功能层14由交替层叠有低折射率层14b和高折射率层14a的层叠体构成,因此从防污层15侧入射的光被光学功能层14扩散。因此,可以得到防止从防污层15侧入射的光向一个方向反射的防反射功能。
低折射率层14b例如包含金属的氧化物。从获得的容易性和成本的观点出发,低折射率层14b可以包含Si的氧化物,优选为以SiO2(Si的氧化物)等为主成分的层。SiO2单层膜为无色透明。在本实施方式中,低折射率层14b的主成分是指在低折射率层14b中含有50质量%以上的成分。
在低折射率层14b是以Si的氧化物为主成分的层的情况下,也可以包含小于50质量%的其他元素。与Si的氧化物不同的元素的含量优选为10%以下。作为其他元素,例如可以含有以提高耐久性为目的的Na、以提高硬度为目的的Zr、Al或N、以及以提高耐碱性为目的的Zr、Al。
低折射率层14b的折射率优选为1.20~1.60,更优选为1.30~1.50。作为低折射率层14b中使用的电介质,可列举氟化镁(MgF2,折射率1.38)等。
高折射率层14a的折射率优选为2.00~2.60,更优选为2.10~2.45。作为高折射率层14a中使用的电介质,可列举出五氧化铌(Nb2O5,折射率2.33)、氧化钛(TiO2,折射率2.33~2.55)、氧化钨(WO3,折射率2.2)、氧化铈(CeO2,折射率2.2)、五氧化钽(Ta2O5,折射率2.16)、氧化锌(ZnO,折射率2.1)、氧化铟锡(ITO,折射率2.06)、氧化锆(ZrO2,折射率2.2)等。
在想要对高折射率层14a赋予导电特性的情况下,例如可以选择ITO、氧化铟锌(IZO)。
光学功能层14例如优选使用由五氧化铌(Nb2O5,折射率2.33)构成的层作为高折射率层14a,使用由SiO2构成的层作为低折射率层14b。
低折射率层14b的膜厚只要为1nm以上且200nm以下的范围即可,可根据需要防反射功能的波长区域而适当选择。
高折射率层14a的膜厚例如为1nm以上200nm以下即可,可根据需要防反射功能的波长区域适当选择。
高折射率层14a及低折射率层14b的膜厚可分别根据光学功能层14的设计而适当选择。
例如,可以从密合层13侧起依次设为5~50nm的高折射率层14a、10~80nm的低折射率层14b、20~200nm的高折射率层14a、50~200nm的低折射率层14b。
在形成光学功能层14的层中,低折射率层14b配置在防污层15侧。在光学功能层14的低折射率层14b与防污层15接触的情况下,光学功能层14的防反射性能变得良好,因此优选。
防污层15形成于光学功能层14的最外表面,防止光学功能层14的污损。另外,防污层15在应用于触摸面板等时,通过耐磨损性抑制光学功能层14的损耗。
本实施方式的防污层15由蒸镀防污性材料而成的蒸镀膜构成。在本实施方式中,防污层15通过在构成光学功能层14的低折射率层14b的一面真空蒸镀作为防污性材料的氟系有机化合物而形成。本实施方式中,防污性材料包含氟系有机化合物,因此成为耐摩擦性及耐碱性更良好的光学层叠体10。
当作为构成防污层15的氟系有机化合物,优选使用包含氟改性有机基团和反应性甲硅烷基(例如烷氧基硅烷)的化合物。作为市售品,可列举OPTOOL DSX(大金株式会社制)、KY-100系列(信越化学工业株式会社制)等。
作为构成防污层15的氟系有机化合物,使用包含氟改性有机基团和反应性甲硅烷基(例如烷氧基硅烷)的化合物作为氟系有机化合物,使用由SiO2构成的层作为与防污层15接触的光学功能层14的低折射率层14b时,在作为氟系有机化合物的骨架的硅烷醇基与SiO2之间形成硅氧烷键。因此,光学功能层14与防污层15的密合性变得良好,是优选的。
防污层15的光学厚度为1nm以上且20nm以下的范围即可,优选为2.5nm以上且10nm以下的范围。若防污层15的厚度为1nm以上,则在将光学层叠体10应用于触摸面板用途等时,能够充分确保耐磨损性。另外,防污层15的厚度为3nm以上时,光学层叠体10的耐液性等提高。另外,防污层15的厚度为20nm以下时,蒸镀所需的时间为短时间即可,能够高效地制造。
防污层15的表面粗糙度Ra根据光学层叠体的用途、构成而不同。例如为不具有防眩功能的透明的防反射层(透明型的防反射膜)时,防污层15的表面粗糙度Ra例如优选为3nm以上,进一步优选为5nm以上。上限没有特别限制,例如从耐擦伤性的观点出发,优选为10nm以下。另一方面,在为具有防眩功能的防反射层(AG型的防反射膜)的情况下,例如优选为10nm以上,更优选为30nm以上。这里所说的防污层15的表面粗糙度Ra反映光学功能层14的表面粗糙度。需要说明的是,是进行耐擦伤性试验等试验前的值。
防污层15根据光学层叠体的用途、构成而不同。例如,在光学层叠体为具有防眩功能的防反射层(AG型的防反射膜)的情况下,防污层15的要素的平均长度RSm例如优选为55nm以上,更优选为90nm以下。这里所说的防污层的要素的平均长度RSm反映光学功能层14的要素的平均长度。需要说明的是,这里所说的防污层15的要素的平均长度RSm是进行耐擦伤性试验前的值。
防污层15根据需要可以含有光稳定剂、紫外线吸收剂、着色剂、抗静电剂、润滑剂、流平剂、消泡剂、抗氧化剂、阻燃剂、红外线吸收剂、表面活性剂等添加剂。
通过蒸镀而形成的防污层15与光学功能层14通过化学键的形成、由光学功能层的粗糙度带来的锚固效果而牢固地结合,空隙少且致密。由此,本实施方式的防污层15与通过防污性材料的涂布等以往的方法形成的防污层不同,显示良好的特性。
例如,本实施方式的透明型的光学层叠体10的防污层15具有以下的特性。
(1)通过使钢丝棉水平往复运动500次而进行的擦伤性试验后相对于水的接触角差为12°以下。
(2)通过使钢丝棉水平往复运动500次而进行的擦伤性试验后相对于水的接触角为109°以上。
(3)通过使布头(无纺布擦拭器)往复4000次而进行的擦伤性试验后的相对于水的接触角为100°以上。
(4)通过使钢丝棉水平往复运动500次而进行的擦伤性试验前后的SCI(SpecularComponent Include(包括镜面反射),将正反射光考虑在内的反射色的测定方法)的下述式(3)所示的L*a*b*值的变化量(ΔE值)为3.0以下。
[数1]
式(3)中,L0*、a0*、b0*为擦伤性试验前的值,L1*、a1*、b1*为擦伤性试验后的值。
(5)通过使钢丝棉水平往复运动500次而进行的擦伤性试验前后的SCE(SpecularComponent Exclude(不包括镜面反射),不将正反射光考虑在内的反射色的测定法)的下述式(4)所示的L*a*b*值的变化量(ΔE值)为0.5以下。
[数2]
式(4)中,L0*、a0*、b0*为擦伤性试验前的值,L1*、a1*、b1*为擦伤性试验后的值。
(6)通过在浓度0.1mol/L的NaOH溶液(液温55℃)中浸渍4小时后的荧光X射线分析法(XRF)测定的氟残存率为85%以上。
(7)通过使布头(无纺布擦拭器)往复4000次而进行的擦伤性试验前后的相对于水的接触角差为12°以下。
(8)在氟系溶剂中以40KHz、240W施加10分钟超声波后,通过荧光X射线分析法(XRF)测定的氟残存率为70%以上。
(9)水蒸气透过率为1.5g/(m2·1天)以下。
另外,例如,本实施方式的AG型的光学层叠体10的防污层15具有以下的特性。
(1)通过使布头(无纺布擦拭器)往复4000次而进行的擦伤性试验前后的相对于水的接触角差为7°以下。
(2)在浓度0.1mol/L的NaOH溶液(液温55℃)中浸渍4小时后的上述式(2)所示的L*a*b*值的变化量(ΔE值)为5.0以下。
(3)在浓度0.1mol/L的NaOH溶液(液温55℃)中浸渍4小时后的通过荧光X射线分析法(XRF)测定的氟残存率为90%以上。
(4)在氟系溶剂中以40KHz、240W施加10分钟超声波后,通过荧光X射线分析法(XRF)测定的氟残存率为75%以上。
(5)水蒸气透过率为1.5g/(m2·1天)以下。
具备通过蒸镀而形成的本实施方式的防污层15的光学层叠体10与通过涂布而形成的防污层相比,空隙少且致密地形成。另外,在本实施方式的光学层叠体10中,防污层15牢固地接合于与防污层15接触的低折射率层14b。因此,本实施方式的光学层叠体10的可见光透过性优异,对于反复摩擦能够维持高的耐磨损性,并且对于耐碱性也能够维持高的耐性。
[光学层叠体的制造方法]
图3所示的本实施方式的光学层叠体10例如可以通过以下所示的方法来制造。
在本实施方式中,作为光学层叠体10的制造方法的一例,以使用卷绕成辊状的透明基材11来制造光学层叠体10的情况为例进行说明。
首先,将卷绕成辊状的透明基材11放卷。然后,通过公知的方法在透明基材11上涂布包含成为硬涂层12的材料的浆料,通过与成为硬涂层12的材料对应的公知的方法使其固化。由此,形成硬涂层12(硬涂层形成工序)。然后,通过公知的方法将表面形成有硬涂层12的透明基材11卷取成辊状。
接着,进行在硬涂层12上形成密合层13的密合层形成工序和形成光学功能层14的光学功能层形成工序。然后,进行在光学功能层14上形成防污层15的防污层形成工序。在本实施方式中,优选在光学功能层形成工序之前,进行对硬涂层12的表面进行处理的第一表面处理工序,然后进行密合层形成工序和光学功能层形成工序。另外,在本实施方式中,优选在光学功能层形成工序之后,进行对光学功能层14的表面进行处理的第二表面处理工序,然后进行防污层形成工序。
在本实施方式的光学层叠体10的制造方法中,第一表面处理工序、密合层形成工序、光学功能层形成工序、第二表面处理工序和防污层形成工序优选在将制造中途的光学层叠体维持在减压下的状态下连续进行。在将制造中途的光学层叠体维持在减压下的状态下连续地进行第一表面处理工序、密合层形成工序、光学功能层形成工序、第二表面处理工序和防污层形成工序的情况下,例如,作为溅射装置,可以使用具备专利文献4中记载的薄膜形成装置的装置等。
作为能够在本实施方式的光学层叠体的制造方法中使用的制造装置,具体而言,可列举出图4所示的制造装置20。
图4所示的制造装置20具备辊放卷装置4、预处理装置2A、溅射装置1、预处理装置2B、蒸镀装置3以及辊卷取装置5。如图4所示,这些装置4、2A、1、2B、3、5依次连结。图4所示的制造装置20是如下的辊对辊方式的制造装置:从辊将基材放卷,使其连续地通过所连结的装置(在图4中为预处理装置2A、溅射装置1、预处理装置2B、蒸镀装置3)之后进行卷取,由此在基材上连续地形成多层。
在使用辊对辊方式的制造装置制造光学层叠体10的情况下,制造中途的光学层叠体10的输送速度(线速度)可以适当设定。输送速度例如优选为0.5~20m/min,更优选为0.5~10m/min。
<辊放卷装置>
图4所示的辊放卷装置4具有内部为规定的减压气氛的腔室34、将腔室34内的气体排出而成为减压气氛的1个或多个真空泵21(在图4中为1个)以及设置于腔室34内的放卷辊23及导辊22。如图4所示,腔室34经由预处理装置2A与溅射装置1的腔室31连结。
在放卷辊23上卷绕有在表面形成有硬涂层12的透明基材11。放卷辊23以规定的输送速度将表面形成有硬涂层12的透明基材11供给到预处理装置2A。
<预处理装置2A>
图4所示的预处理装置2A具有内部为规定的减压气氛的腔室32、罐状辊26、多个(图4中为2个)导辊22和等离子体放电装置42。如图4所示,罐状辊26、导辊22和等离子体放电装置42设置在腔室32内。如图4所示,腔室32与溅射装置1的腔室31连结。
罐状辊26及导辊22以规定的搬送速度搬送从辊放卷装置4送来的形成有硬涂层12的透明基材11,并将硬涂层12的表面经处理的透明基材11送出至溅射装置1。
如图4所示,等离子体放电装置42与罐状辊26的外周面以规定的间隔分离地对置配置。等离子体放电装置42通过辉光放电使气体电离。作为气体,优选低价且非活性且不影响光学特性的气体,例如可以使用氩气、氧气、氮气、氦气等。在本实施方式中,作为气体,优选使用氩气或氧气。
<溅射装置>
图4所示的溅射装置1具有内部为规定的减压气氛的腔室31、将腔室31内的气体排出而成为减压气氛的1个或多个真空泵21(在图4中为2个)、成膜辊25、多个(在图4中为2个)导辊22、多个(在图4所示的例子中为4个)成膜部41。如图4所示,成膜辊25、导辊22、成膜部41设置于腔室31内。如图4所示,腔室31与预处理装置2B的腔室32连结。
成膜辊25及导辊22以规定的搬送速度搬送从预处理装置2A送来的形成有表面经处理的硬涂层12的透明基材11,并将在硬涂层12上形成有密合层13及光学功能层14的透明基材11供给至预处理装置2B。
在图4所示的溅射装置1中,在行进于成膜辊25上的透明基材11的硬涂层12上,通过溅射来层叠密合层13,在其上交替层叠高折射率层14a和低折射率层14b,从而形成光学功能层14。
如图4所示,成膜部41与成膜辊25的外周面以规定的间隔分离地对置配置,以包围成膜辊25的方式设置有多个。成膜部41的数量根据密合层13、形成光学功能层14的高折射率层14a和低折射率层14b的合计层叠数来决定。当由于密合层13和形成光学功能层14的高折射率层14a和低折射率层14b的合计层叠数多,因此难以确保相邻的成膜部41间的距离的情况下,也可以在腔室31内设置多个成膜辊25,在各成膜辊25的周围配置成膜部41。在设置多个成膜辊25的情况下,也可以根据需要进一步设置导辊22。也可以连结多台设置有成膜辊25和成膜部41的腔室31。另外,为了容易确保相邻的成膜部41间的距离,也可以适当变更成膜辊25的直径。
在各成膜部41分别设置有规定的靶(未图示)。通过公知的结构对靶施加电压。在本实施方式中,在靶的附近设置有以规定的流量向靶供给规定的反应性气体和载气的气体供给部(未图示)和在靶的表面形成磁场的公知的磁场产生源(未图示)。
靶的材料及反应性气体的种类及流量根据在成膜部41与成膜辊25之间通过从而形成于透明基材11上的密合层13、高折射率层14a、低折射率层14b的组成来适当决定。例如,在形成由SiO2构成的层的情况下,使用Si作为靶,使用O2作为反应性气体。另外,例如,在形成由Nb2O5构成的层的情况下,使用Nb作为靶,使用O2作为反应性气体。低折射率层14b优选在小于0.5Pa的真空度下成膜,高折射率层14a优选在小于1.0Pa的真空度下成膜。若在该真空度下对这些层进行成膜,则光学功能层14变得致密,水蒸气透过率降低,耐久性等提高。
在本实施方式中,从成膜速度的高速化的观点出发,作为溅射法,优选使用磁控溅射法。
另外,溅射法并不限定于磁控溅射法,也可以使用利用通过直流辉光放电或高频产生的等离子体的双极溅射方式、附加热阴极的三极溅射方式等。
溅射装置1具备光学监视器(未图示),其作为在将成为密合层13和光学功能层14的各层成膜后,测定光学特性的测定部。由此,能够确认所形成的密合层13和光学功能层14的品质。在溅射装置1例如具有2个以上的腔室的情况下,优选在各腔室内设置光学监视器。
作为光学监视器(未图示),例如可列举出利用能够在宽度方向上扫描的光学头测定形成于硬涂层12上的密合层13和光学功能层14的宽度方向的光学特性的光学监视器。在具备这样的光学监视器的情况下,例如,通过测定反射率的峰值波长并换算为光学厚度,能够测定密合层13和光学功能层14的宽度方向的光学厚度分布作为光学特性。通过使用光学监视器测定光学特性,能够实时地调整溅射条件,并且形成具备具有最佳光学特性的密合层13和光学功能层14的光学层叠体10。
<预处理装置2B>
图4所示的预处理装置2B具有内部为规定的减压气氛的腔室32、罐状辊26、多个(图4中为2个)导辊22和等离子体放电装置42。如图4所示,罐状辊26、导辊22和等离子体放电装置42设置在腔室32内。如图4所示,腔室32与蒸镀装置3的腔室33连结。
罐状辊26及导辊22以规定的输送速度输送从溅射装置1送来的形成有直至光学功能层14的各层的透明基材11,并将光学功能层14的表面被处理后的透明基材11向蒸镀装置3送出。
作为等离子体放电装置42,例如能够使用与预处理装置2A相同的装置。
<蒸镀装置>
图4所示的蒸镀装置3具有内部为规定的减压气氛的腔室33、将腔室33内的气体排出而成为减压气氛的1个或多个真空泵21(在图4中为1个)、多个(在图4中为4个)导辊22、蒸镀源43和加热装置53。如图4所示,导辊22和蒸镀源43设置于腔室33内。腔室33与辊卷取装置5的腔室35连结。
蒸镀源43与在相邻的2个导辊22之间大致水平地被输送的、光学功能层14的表面经处理的透明基材11相对地配置。蒸镀源43将由成为防污层15的材料构成的蒸发气体供给到光学功能层14上。蒸镀源43的朝向能够任意地设定。
加热装置53将成为防污层15的材料加热至蒸气压温度。作为加热装置53,能够使用以电阻加热方式、加热器加热方式、感应加热方式、电子束方式进行加热的装置等。在电阻加热方式中,将容纳成为防污层15的防污性材料的容器作为电阻体进行通电加热。在加热器加热方式中,利用配置于容器的外周的加热器对容器进行加热。在感应加热方式中,通过电磁感应作用从设置于外部的感应线圈对容器或防污性材料进行加热。
图4所示的蒸镀装置3具备将由蒸镀源43蒸发的蒸镀材料引导至规定的位置的引导板(未图示)、观察通过蒸镀而形成的防污层15的厚度的膜厚计(未图示)、测定腔室33内的压力的真空压力计(未图示)以及电源装置(未图示)。
引导板只要能够将蒸发的蒸镀材料引导至所希望的位置,则可以是任何形状。引导板如果不是必要的话也可以不具备。
作为真空压力计,例如可以使用离子测量仪等。
作为电源装置,例如可列举出高频电源等。
<辊卷取装置>
图4所示的辊卷取装置5具有内部为规定的减压气氛的腔室35、将腔室35内的气体排出而成为减压气氛的1个或多个真空泵21(在图4中为1个)以及设置于腔室35内的卷取辊24和导辊22。
在卷取辊24上卷绕有在表面形成有直至防污层15的各层的透明基材11(光学层叠体10)。卷取辊24及导辊22以规定的卷取速度卷取光学层叠体10。
根据需要,也可以使用载体膜。
作为图4所示的制造装置20所具备的真空泵21,例如能够使用干式泵、油旋转泵、涡轮分子泵、油扩散泵、低温泵、溅射泵、吸气泵等。真空泵21能够在各腔室31、32、33、34、35中为了形成所希望的减压状态而适当选择或组合使用。
真空泵21只要能够将溅射装置1的腔室31和蒸镀装置3的腔室33这两者维持在期望的减压状态即可,制造装置20中的真空泵21的设置位置和数量没有特别限定。另外,在图4所示的制造装置20中,辊放卷装置4、预处理装置2A、溅射装置1、预处理装置2B、蒸镀装置3以及辊卷取装置5连结。因此,真空泵21可以分别设置于腔室31、32、33、34、35,只要能够将溅射装置1的腔室31和蒸镀装置3的腔室33双方维持在所希望的减压状态,则也可以仅设置于腔室31、32、33、34、35中的一部分腔室。
接着,对使用图4所示的制造装置20,在将制造中途的光学层叠体10维持在减压下的状态下连续进行第一表面处理工序和密合层形成工序以及光学功能层形成工序、第二表面处理工序和防污层形成工序的方法进行说明。
首先,在辊放卷装置4的腔室34内,设置卷绕有在表面形成有硬涂层12的透明基材11的放卷辊23。然后,使放卷辊23及导辊22旋转,以规定的输送速度将表面形成有硬涂层12的透明基材11向预处理装置2A送出。
接着,在预处理装置2A的腔室32内,作为对形成密合层13和光学功能层14的表面的预处理,进行第一表面处理工序。在本实施方式中,对形成硬涂层12的透明基材11进行第一表面处理工序。
在第一表面处理工序中,使罐状辊26和导辊22旋转,一边以规定的输送速度输送形成有硬涂层12的透明基材11,一边对在罐状辊26上行进的硬涂层12的表面进行处理。
作为硬涂层12的表面处理方法,例如可以使用辉光放电处理、等离子体处理、离子蚀刻、碱处理等。其中,由于能够进行大面积处理,因此优选使用辉光放电处理。辉光放电处理例如能够以0.1~10kwh的处理强度进行。
通过对硬涂层12的表面进行辉光放电处理,硬涂层12的表面以纳米水平被粗糙化,并且存在于硬涂层12的表面的结合力弱的物质被除去。其结果是,硬涂层12与形成于硬涂层12上的光学功能层14的密合性变得良好。
接着,在溅射装置1的腔室31内进行密合层形成工序和光学功能层形成工序。具体而言,使成膜辊25和导辊22旋转,一边以规定的输送速度输送形成有硬涂层12的透明基材11,一边在行进于成膜辊25上的硬涂层12上形成密合层13和光学功能层14。
在本实施方式中,通过改变设置于各成膜部41的靶的材料或从气体供给部供给的反应性气体的种类及流量进行溅射,形成密合层13,在其上交替层叠高折射率层14a和低折射率层14b。即,密合层形成工序和光学功能层形成工序在溅射装置1内连续进行。由此,形成密合层13和作为防反射层的光学功能层14。
高折射率层14a和低折射率层14b分别在规定的真空度以下的条件下成膜。具体而言,在小于1.0Pa的真空度下对高折射率层14a进行成膜,在小于0.5Pa的真空度下对低折射率层14b进行成膜。
在形成SiOx膜作为密合层13的情况下,优选使用硅靶,通过基于氧气与氩气的混合气体气氛的反应性溅射来形成。
在通过溅射连续地层叠密合层13、高折射率层14a和低折射率层14b的情况下,也可以在密合层13的成膜时、高折射率层14a的成膜时和低折射率层14b的成膜时改变靶的材料来进行成膜。另外,例如,也可以使用1种材料作为靶,通过改变溅射时的氧(反应性气体)流量,交替地形成由靶材料构成的层和由靶材料的氧化物构成的层,作为密合层13、高折射率层14a和低折射率层14b。
用于形成密合层13和光学功能层14的溅射时的压力根据溅射的金属而不同,可以为2Pa以下,优选为1Pa以下,更优选为0.6Pa以下,特别优选为0.2Pa以下。如果是溅射时的压力为1Pa以下的减压下的状态,则成膜分子的平均自由程变长,在成膜分子的能量较高的状态下层叠,因此成为致密且更良好的膜质。高折射率层与低折射率层的溅射时的压力优选不同。这是因为每个成膜种类的平均自由程不同。通过按成膜种类改变压力,能够形成更致密的膜。
然后,通过成膜辊25及导辊22的旋转,将在硬涂层12上形成有密合层13及光学功能层14的透明基材11送出至预处理装置2B。
接着,在预处理装置2B的腔室32内,作为对形成防污层15的表面的预处理,进行第二表面处理工序。在本实施方式中,使通过光学功能层形成工序得到的形成有光学功能层14的透明基材11不与大气接触,在维持减压下的状态下连续地进行第二表面处理工序。
在第二表面处理工序中,一边使罐状辊26和导辊22旋转,以规定的输送速度输送形成有直至光学功能层14的各层的透明基材11,一边对在罐状辊26上行进的光学功能层14的表面进行放电处理。
作为光学功能层14的表面处理方法,例如可以使用辉光放电处理、等离子体处理、离子蚀刻、碱处理等。其中,由于能够进行大面积处理,因此优选使用辉光放电处理。
当对光学功能层14的表面进行放电处理时,光学功能层14的表面被蚀刻,光学功能层14的表面状态发生变化。光学功能层14的表面状态由表面粗糙度Ra或要素的平均长度RSm表示。例如,在光学功能层14的雾度为2.0以下的透明型的防反射膜的情况下,光学功能层14的表面状态容易由表面粗糙度Ra来定义。另外,例如,在光学功能层14的雾度超过2.0的AG型的防反射膜的情况下,光学功能层14的表面状态容易由要素的平均长度RSm定义。光学功能层的表面粗糙度、要素的平均长度可以用防污层形成后的表面粗糙度Ra、要素的平均长度RSm来评价。表面粗糙度Ra和要素的平均长度RSm根据JIS B0601(ISO4287)进行测定。
辉光放电处理时的累积输出优选为130W·min/m2以上且2000W·min/m2以下。通过辉光放电处理的累积输出,光学功能层14的表面状态发生变化。在本实施方式中,累积输出是指在放电处理时对光学功能层14照射的辉光放电输出与照射时间之积除以每单位面积而得到的值。
放电处理的条件可以适当设定。通过适当地设定放电处理的条件,光学功能层14与形成于其上的防污层15的密合性变得良好,可得到耐摩擦性及耐碱性更良好的光学层叠体10。
放电处理后的光学功能层14的表面粗糙度Ra及要素的平均长度RSm根据设置于光学功能层14之下的硬涂层12的表面粗糙度及要素的平均长度RSm而不同。
另外,放电处理后的光学功能层14的表面粗糙度Ra和要素的平均长度RSm对形成于光学功能层14上的防污层15的表面粗糙度Ra和要素的平均长度RSm产生影响。因此,在利用防污层形成后的表面粗糙度Ra、要素的平均长度RSm来评价光学功能层的表面粗糙度Ra、要素的平均长度RSm的情况下,需要使放电处理以外的条件一致来进行比较。
在第二表面处理工序中,例如,以使由下述(式1)表示的表面粗糙度的变化率为5~35%的方式对光学功能层的表面进行处理。特别是透明型的防反射膜的情况下,在该条件下对光学功能层的表面进行处理。
表面粗糙度的变化率(%)=((Ra2/Ra1)-1)×100(%)…式(1)
式(1)中,Ra1表示未进行表面处理而形成了防污层的、光学层叠体的防污层的表面粗糙度(Ra),Ra2表示对表面进行处理后形成了防污层的、光学层叠体的防污层的表面粗糙度(Ra)。
第二表面处理工序优选以(式1)表示的表面粗糙度的变化率成为5%~35%的方式进行,更优选以成为10~30%的方式进行。(式1)表示的表面粗糙度的变化率为5%以上时,通过进行第二表面处理工序而带来的光学功能层14与防污层15的密合性提高效果变得显著。另外,若由(式1)表示的表面粗糙度的变化率为35%以下,则从能够维持施以耐久性试验后的光学特性的方面考虑是优选的。
另外,在第二表面处理工序中,以下述式表示的要素的平均长度的变化率为7~65%的方式对光学功能层的表面进行处理。特别是在AG型的防反射膜的情况下,在该条件下处理光学功能层的表面。例如,放电处理时的累积输出是影响要素的平均长度的参数之一。
要素的平均长度的变化率(%)=((RSm2/RSm1)-1)×100(%)…式(2)
式(2)中,RSm1表示未进行表面处理而形成了防污层的、光学层叠体的防污层的要素的平均长度(RSm),RSm2表示对表面进行处理后形成了防污层的、光学层叠体的防污层的要素的平均长度(RSm)。
第二表面处理工序优选以式(2)所示的要素的平均长度(RSm)的变化率成为7~70%的方式进行,进一步优选以成为10~65%的方式进行。如果式(2)所示的要素的平均长度的变化率在上述范围内,则通过进行第二表面处理工序而带来的光学功能层14与防污层15的密合性提高效果变得显著。另外,若由式(2)所示的要素的平均长度的变化率为规定值以下,则从能够维持施以耐久性试验后的光学特性的方面考虑是优选的。
在本实施方式中,防污层15的表面粗糙度Ra和要素的平均长度可以使用原子力显微镜(AFM:Atomic Force Microscope)来测定。表面粗糙度Ra在防污层15的表面的面积1μm2的范围内测定,要素的平均长度RSm在防污层15的表面的面积0.5μm2的范围内测定。
然后,通过罐状辊26和导辊22的旋转,将光学功能层14的表面被处理后的透明基材11送出到蒸镀装置3。
接着,在蒸镀装置3的腔室33内进行防污层形成工序。在本实施方式中,使通过第二表面处理工序得到的光学功能层14的表面经处理的透明基材11不与大气接触,在维持减压下的状态下连续地进行防污层形成工序。
在防污层形成工序中,使导辊22旋转,一边以规定的输送速度输送光学功能层14的表面经处理的透明基材11,一边在光学功能层14的表面蒸镀蒸镀源43。
在本实施方式中,例如,通过加热装置53将成为防污层15的包含氟系有机化合物的防污性材料加热至蒸气压温度,在减压环境下从蒸镀源43供给所得到的蒸发气体,使其附着于表面经处理的光学功能层14,通过真空蒸镀形成防污层15。
进行防污层15的真空蒸镀时的压力例如优选为0.05Pa以下,更优选为0.01Pa以下,特别优选为0.001Pa以下。若进行真空蒸镀时的压力为0.05Pa以下的减压下的状态,则成膜分子的平均自由程变长,蒸镀能量变高,因此可得到致密且更良好的防污层15。
通过以上的方法,得到在通过溅射形成的密合层13和光学功能层14上通过真空蒸镀形成有防污层15的光学层叠体10。成膜后的防污层15优选使用荧光X射线分析法(XRF)测定的氟的初始量为0.03以上。
然后,通过导辊22的旋转,将形成有直至防污层15的各层的透明基材11(光学层叠体10)送出至辊卷取装置5。
然后,在辊卷取装置5的腔室35内,通过卷取辊24及导辊22的旋转,将光学层叠体10卷绕于卷取辊24。
在本实施方式中,优选在减压下连续进行光学功能层形成工序和防污层形成工序。特别是,如使用图4所示的制造装置20的本实施方式的制造方法那样,在将光学层叠体10以辊对辊方式作为卷绕体连续地制造的情况下,更优选在维持减压状态的状态下在线连续地进行光学功能层形成工序和防污层形成工序。在线是指在不使光学功能层形成工序中形成的光学功能层14与大气接触的情况下进行防污层形成工序。通过在减压下连续进行光学功能层形成工序和防污层形成工序,在形成防污层15之前,可抑制在光学功能层形成工序中形成的光学功能层14上生成自然氧化膜。另外,能够防止辊卷取时的异物等污染物附着在光学功能层14上而阻碍光学功能层14与防污层15的密合性。因此,与在光学功能层形成工序后,将形成有直至光学功能层14的各层的透明基材11从减压状态的腔室中取出,然后再次设置于腔室内并在减压下进行防污层形成工序的情况(后述的实施例4的情况)相比,可得到光学功能层14与防污层15的密合性良好、透明性优异的光学层叠体。
另外,本实施方式的光学层叠体10所具有的防污层15为蒸镀膜,因此例如与通过涂布法形成的防污膜相比,可得到高的耐磨损性。推测这是由于以下所示的理由。即,在通过涂布法形成的防污膜中,存在由涂料中所含的溶剂引起的空隙。与此相对,在蒸镀膜中不存在由溶剂引起的空隙。因此,推测蒸镀膜与通过涂布法形成的防污膜相比为高密度,可得到高的耐磨损性、耐碱性。
本实施方式的光学层叠体10的制造方法包括形成密合层13的密合层形成工序、通过交替层叠高折射率层14a和低折射率层14b而形成光学功能层14的光学功能层形成工序、对光学功能层14的表面进行处理的第二表面处理工序和在经表面处理的光学功能层14上形成防污层15的防污层形成工序。因此,光学功能层14与形成于光学功能层14上的防污层15的密合性良好,成为摩擦性和耐碱性更良好的光学层叠体。
特别是,在第二表面处理工序中,在以使式(1)所示的表面粗糙度的变化率为5~35%的方式对光学功能层的表面进行处理的情况下,光学功能层14的表面变化为适当的粗糙度,并且通过蚀刻而使表面活化,因此与形成于光学功能层14上的防污层15的反应性提高,因此优选。
另外,在本实施方式的光学层叠体10的制造方法中,能够以辊对辊方式连续地形成光学层叠体10,并且能够以高精度控制膜厚,因此优选在光学功能层形成工序中通过溅射来形成光学功能层14。
在本实施方式中,在将制造中途的光学层叠体维持在减压下的状态下连续地进行第一表面处理工序、光学功能层形成工序、第二表面处理工序和防污层形成工序的情况下,只要在不妨碍各制造工序的范围内,例如在溅射装置和蒸镀装置中,腔室内的减压条件也可以不同。
在本实施方式中,优选在密合层形成工序、光学功能层形成工序、防污层形成工序中的任意1个以上的工序中,利用测定器经时地测定成膜结果,将其结果反馈至相当于后续工序的制造工序的条件中。由此,容易使光学层叠体整体的特性最佳化,能够使光学层叠体的面内的特性均匀。另外,也能够通过测定器进行同一工序中的制造条件的反馈。在该情况下,在该工序中成膜的层具有均匀且稳定的特性。
在本实施方式中,以在光学功能层形成工序与防污层形成工序之间进行第二表面处理工序的情况为例进行了说明,但第二表面处理工序根据需要进行即可,也可以不进行。即使在不进行第二表面处理工序的情况下,也优选在减压下连续进行光学功能层形成工序和防污层形成工序。
另外,在本实施方式的制造方法中,在规定的真空度以下的条件下形成光学功能层。因此,光学功能层14变得致密,水蒸气透过率降低,耐摩擦性及耐碱性提高。进而,通过使防污层的膜厚为规定的厚度以上,能够确保充分的耐擦伤性和耐碱性。
在本实施方式中,以使用具备预处理装置2A、溅射装置1、预处理装置2B、蒸镀装置3、辊放卷装置4和辊卷取装置5的图4所示的制造装置20,以辊对辊方式连续地制造光学层叠体10的情况为例进行了说明,但制造光学层叠体10的制造装置并不限定于图4所示的制造装置20。
例如,也可以使用不包括预处理装置2A和预处理装置2B而将辊放卷装置4、溅射装置1、蒸镀装置3和辊卷取装置5依次连结而成的制造装置。
在图4所示的制造装置20中,可以在蒸镀装置3的腔室33与预处理装置2B的腔室32之间设置用于清洗形成防污层15的光学功能层14的表面的预处理室(未图示)。
在图4所示的制造装置20中,可以在蒸镀装置3的腔室33与辊卷取装置5的腔室35之间设置后处理室(未图示),该后处理室用于进行形成有直至防污层15的各层的透明基材11的冷却和/或检查。
在图4所示的制造装置20中,可以在辊放卷装置4与溅射装置1之间设置用于在透明基材11的表面形成硬涂层12的硬涂层形成装置。在该情况下,不仅光学功能层14和防污层15,硬涂层12也能够以辊对辊方式连续地制造,是优选的。
在本实施方式中,以使用溅射装置进行光学功能层形成工序、使用蒸镀装置进行防污层形成工序的情况为例进行了说明,但在不进行第二表面处理工序的情况下,也可以用相同的装置(1个腔室内)进行光学功能层形成工序和防污层形成工序。
在本实施方式的光学层叠体10中,可以根据需要在透明基材的与形成有光学功能层等的面相对的面上设置各种层。例如,也可以设置用于与其他构件的粘接的粘着剂层。另外,也可以隔着该粘着剂层设置其他光学膜。作为其他光学膜,例如可列举出偏振膜、相位差补偿膜、作为1/2波长板、1/4波长板发挥功能的膜等。
另外,也可以在透明基材的相对的面上直接形成具有防反射、选择反射、防眩、偏振光、相位差补偿、视角补偿或放大、导光、扩散、亮度提高、色相调整、导电等功能的层。
另外,光学层叠体的形状可以为平滑的形状,也可以为具有蛾眼、呈现防眩功能的纳米级的凹凸结构的形状。另外,也可以是透镜、棱镜等微米到毫米级的几何学形状。形状例如可以通过光刻和蚀刻的组合、形状转印、热压等来形成。在本实施方式中,由于通过蒸镀等进行成膜,因此即使在基材具有例如凹凸形状的情况下,也能够维持该凹凸形状。
本实施方式的物品例如为液晶显示面板、有机EL显示面板等在图像显示部的显示面设置有上述光学层叠体10的物品。由此,例如能够对智能手机、操作设备的触摸面板显示部赋予高耐磨损性和耐碱性,能够实现耐久性优异的、适于实际使用的图像显示装置。
另外,作为物品并不限定于图像显示装置,例如只要是表面设置有本实施方式的光学层叠体的窗玻璃、护目镜、太阳能电池的受光面、智能手机的画面、个人计算机的显示器、信息输入终端、平板终端、AR(增强现实)设备、VR(虚拟现实)设备、电光显示板、玻璃桌表面、游戏机、飞机、电车等运行辅助装置、导航***、仪表盘、光学传感器的表面等能够应用光学层叠体10的物品,则可以是任意物品。
以上,对本发明的实施方式进行了说明,但该实施方式是作为例子而提示的,并不意图限定发明的范围。该实施方式能够以其他各种方式实施,在不脱离发明的主旨的范围内,能够进行各种省略、置换、变更。这些实施方式或其变形包含在发明的范围或主旨中,并且包含在权利要求书所记载的发明及其等同的范围内。
例如,可以代替硬涂层12而形成防眩层,或者根据需要附加具有柔软性的软涂层等任意的功能层。它们也可以层叠。
实施例
验证了本发明的效果。
需要说明的是,以下的实施例和比较例中制作的光学层叠体是作为防反射膜发挥功能的一例,本发明的主旨并不限定于这些。
(实施例1)
首先,准备平均粒径50nm的二氧化硅粒子(填料)的含量相对于树脂组合物(粘合剂树脂)的固体成分整体为28质量%的光固化性的树脂组合物。如表1所示,树脂组合物通过将二氧化硅颗粒、丙烯酸酯、流平剂和光聚合引发剂溶解在溶剂中来制备。
[表1]
SR610:聚乙二醇二丙烯酸酯、聚乙二醇链的平均分子量600
CN968:具有聚酯骨架的6官能脂肪族氨基甲酸酯丙烯酸酯
Irgacure 184:1-羟基-环己基-苯基-酮
<硬涂层形成工序>
准备厚度80μm、长度3900m的辊状的TAC膜作为透明基材11,利用凹版涂布机在TAC膜上涂布表1所示的光固化性的树脂组合物,照射光而使其固化,形成厚度5μm的硬涂层12。
接着,以辊对辊方式,通过以下所示的方法,在形成有硬涂层12的透明基材11上依次连续地制造密合层13、光学功能层14和防污层15,制作实施例1的光学层叠体(防反射膜)。
作为制造装置,使用了图4所示的制造装置20。另外,线速度为2m/min。将第一表面处理工序、密合层形成工序、光学功能层形成工序、第二表面处理工序和防污层形成工序在将制造中途的光学层叠体维持在减压下的状态下连续地进行。
<第一表面处理工序>
接着,对于硬涂层12,使辉光放电处理的处理强度为4000W·min/m2,进行辉光放电处理。
<密合层形成工序和光学功能层形成工序>
密合层形成工序中,将SiOx层作为密合层13,在压力小于0.5Pa的条件下成膜。成膜使用Si靶,向腔室内导入氧来进行。氧量通过等离子体发光监测来控制。Si元素一边被氧化一边成膜,由此形成由SiOx构成的密合层。密合层的厚度为5nm。接着,将高折射率层和低折射率层交替地各成膜2层。高折射率层使用Nb靶,向腔室内导入氧而进行。腔室内的压力设为1.0Pa以下。Nb元素一边被氧化一边成膜,由此形成由Nb2O5构成的高折射率层。低折射率层与密合层同样地使用Si靶,向腔室内导入氧而进行。腔室内的压力设为小于0.5Pa。Si元素一边被氧化一边成膜,由此形成由SiO2构成的低折射率层。
<第二表面处理工序>
对光学功能层14的表面进行辉光放电处理。辉光放电处理的累积输出为321W·min/m2。
<防污层形成工序>
接着,在光学功能层14上,以蒸镀室内压力0.01Pa以下、蒸镀温度230℃、线速度2.0m/min,通过蒸镀形成由作为具有氟的有机化合物的具有全氟聚醚基的烷氧基硅烷化合物(KY-1901,信越化学工业株式会社制)构成的防污层15。所得防污层15的光学膜厚如表2所示。
然后,卷取成辊状,得到实施例1的光学层叠体(防反射膜)。
[表2]
(实施例2)
除了防污层15的光学膜厚为4nm以外,与实施例1同样地操作,得到实施例2的光学层叠体(防反射膜)。
(实施例3)
除了防污层15的光学膜厚为3nm、累积输出为326W·min/m2以外,与实施例1同样地操作,得到实施例3的光学层叠体(防反射膜)。
(实施例4)
与实施例1同样地进行至光学功能层形成工序后,将形成有硬涂层12、密合层13和光学功能层14的TAC膜卷取并从制造装置中取出,在大气中,在温度25℃、湿度55%的环境下静置30天。然后,将形成有硬涂层12、密合层13和光学功能层14的TAC膜设置在制造装置中放卷,与实施例1同样地进行第二表面处理工序和防污层形成工序,由此在光学功能层14上形成防污层15,卷取成辊状。通过以上的工序,制作实施例4的光学层叠体(防反射膜)。
将实施例4的光学层叠体的防污层15的光学膜厚示于表2。
(实施例5)
变更了对光学功能层14的表面的第二表面处理的条件,这一点与实施例4不同。
辉光放电处理的输出功率为0.7kW,累积输出功率为755W·min/m2。
(比较例1、2)
与实施例1同样地进行至光学功能层形成工序后,将形成有硬涂层12、密合层13和光学功能层14的TAC膜卷取并从制造装置取出,设置于辊对辊方式的涂布装置(涂布机)。然后,在大气压下,将形成有硬涂层12、密合层13和光学功能层14的TAC膜放卷,以线速度20m/min,使用凹版涂布机在光学功能层14的SiO2膜(低折射率层)上涂布防污剂。
作为防污剂,使用将具有全氟聚醚基的烷氧基硅烷化合物(KY-1901,信越化学工业株式会社制)使用氟溶剂(Fluorinert FC-3283:3M日本株式会社制)稀释至浓度0.1质量%而得到的防污剂。以干燥后的厚度成为表2所示的膜厚的方式涂布防污剂。
(比较例3)
除了不进行第一表面处理工序(硬涂层的表面的辉光放电处理)和第二表面处理工序(光学功能层的表面的辉光放电处理)以外,与实施例1同样地操作,得到比较例3的光学层叠体(防反射膜)。需要说明的是,将比较例3的防污层的表面粗糙度Ra设为成为实施例1~5、比较例4、5的防污层的表面粗糙度的变化率的计算基准的Ra1。
(比较例4)
将低折射率层成膜时的压力设为0.5Pa以上且小于1.0Pa,将高折射率层成膜时的压力设为小于1.0Pa,除此以外,以与实施例1相同的方式获得比较例4的光学层叠体(防反射膜)。
(比较例5)
将防污层的膜厚设为2.0nm,除此以外,与实施例1同样地操作,得到比较例4的光学层叠体(防反射膜)。
(实施例6~8)
实施例6~8在改变了硬涂层的构成这一点上与实施例1不同。实施例6~8中,不进行硬涂层形成工序,使用具有硬涂层的市售品(大日本印刷株式会社制)的膜。硬涂层是具有平均粒径2μm的填料的丙烯酸系树脂组合物的固化物。硬涂层的膜厚为3μm。该硬涂层层叠在厚度80μm的TAC(透明基材)上。然后,对该硬涂层依次进行第一表面处理工序、密合层形成工序、光学功能层形成工序、第二表面处理工序和防污层形成工序。
实施例6以1.0kW的输出进行第二表面处理工序,累积输出为1086W·min/m2。另外,实施例6将防污层的膜厚设为5.0nm。
实施例7在以1.5kW的输出进行第二表面处理工序这一点上与实施例6不同,累积输出为1629W·min/m2。
实施例8与实施例6的不同点在于,防污层的膜厚为4.0nm。
(实施例9~12)
实施例9~12在改变了硬涂层的构成这一点上与实施例1不同。实施例9~12中,不进行硬涂层形成工序,使用具有硬涂层的市售品(大日本印刷株式会社制)的膜。硬涂层是具有平均粒径2μm的填料的丙烯酸系树脂组合物的固化物。硬涂层的膜厚为5μm。该硬涂层层叠在厚度60μm的TAC(透明基材)上。然后,对该硬涂层依次进行第一表面处理工序、密合层形成工序、光学功能层形成工序、第二表面处理工序和防污层形成工序。
实施例9以1.0kW的输出进行第二表面处理工序,累积输出为1086W·min/m2。另外,实施例9将防污层的膜厚设为5.0nm。
实施例10在以1.5kW的输出进行第二表面处理工序这一点上与实施例9不同,累积输出为1629W·min/m2。
实施例11在以0.5kW的输出进行第二表面处理工序这一点上与实施例9不同,累积输出为543W·min/m2。
实施例12与实施例9的不同点在于,防污层的膜厚为4.0nm。
(比较例6)
除了不进行第一表面处理工序(硬涂层的表面的辉光放电处理)和第二表面处理工序(光学功能层的表面的辉光放电处理)以外,与实施例6同样地操作,得到比较例6的光学层叠体(防反射膜)。需要说明的是,比较例6的防污层的要素的平均长度RSm设为实施例6~8的防污层的要素的平均长度RSm的变化率的计算基准RSm1。
(比较例7)
与实施例7同样地进行至光学功能层形成工序后,将形成有硬涂层12、密合层13和光学功能层14的TAC膜卷取并从制造装置取出,设置于辊对辊方式的涂布装置(涂布机)。然后,在大气压下,将形成有硬涂层12、密合层13和光学功能层14的TAC膜放卷,以线速度20m/min,使用凹版涂布机在光学功能层14的SiO2膜(低折射率层)上涂布防污剂。
作为防污剂,使用将具有全氟聚醚基的烷氧基硅烷化合物(KY-1901,信越化学工业株式会社制)使用氟溶剂(Fluorinert FC-3283:3M日本株式会社制)稀释至浓度0.1质量%而得到的防污剂。以干燥后的厚度成为表3A、表3B所示的膜厚的方式涂布防污剂。
(比较例8)
除了不进行第一表面处理工序(硬涂层的表面的辉光放电处理)和第二表面处理工序(光学功能层的表面的辉光放电处理)以外,与实施例9同样地操作,得到比较例8的光学层叠体(防反射膜)。需要说明的是,比较例8的防污层的要素的平均长度RSm设为实施例9~12的防污层的要素的平均长度RSm的变化率的计算基准RSm1。
(比较例9)
与实施例9同样地进行至光学功能层形成工序后,将形成有硬涂层12、密合层13和光学功能层14的TAC膜卷取并从制造装置取出,设置于辊对辊方式的涂布装置(涂布机)。然后,在大气压下,将形成有硬涂层12、密合层13和光学功能层14的TAC膜放卷,以线速度20m/min,使用凹版涂布机在光学功能层14的SiO2膜(低折射率层)上涂布防污剂。
作为防污剂,使用将具有全氟聚醚基的烷氧基硅烷化合物(KY-1901,信越化学工业株式会社制)用氟溶剂(Fluorinert FC-3283:3M日本株式会社制)稀释至浓度0.1质量%而得到的防污剂。以干燥后的厚度成为表3A、表3B所示的膜厚的方式涂布防污剂。
(比较例10)
将低折射率成膜层时的压力设为0.5Pa以上且小于1.0Pa,将高折射率层成膜时的压力设为小于1.0Pa,除此以外,以与实施例6相同的方式获得比较例10的光学层叠体(防反射膜)。
(比较例11)
将防污层的膜厚设为2.0nm,除此以外,与实施例1同样地操作,得到比较例11的光学层叠体(防反射膜)。
[表3A]
[表3B]
(防污层的表面粗糙度Ra)
所得到的实施例1~5、比较例1~5的光学层叠体(防反射膜)的表面粗糙度Ra通过以下的方法进行测定。
从卷取光学层叠体而成的各辊的长度方向中央的位置且辊宽度方向中央的位置切出50mm×50mm的测定样品。使用原子力显微镜(AFM:Atomic Force Microscope)(商品名SPA400,NanoNaviII;日立株式会社制)观察样品的表面,测定面积1μm2的范围内的表面粗糙度Ra。测定在样品上的3处进行,将其平均值作为测定值。
另外,将下述式(1)所示的表面粗糙度的变化率示于表2。
表面粗糙度的变化率(%)=((Ra2/Ra1)-1)×100(%)…式(1)
式(1)中,Ra1表示未进行表面处理而形成了防污层的、光学层叠体的防污层的表面粗糙度(Ra),Ra2表示对表面进行处理后形成了防污层的、光学层叠体的防污层的表面粗糙度(Ra)。
(防污层的要素的平均长度RSm)
所得到的实施例6~12、比较例6~12的光学层叠体(防反射膜)中的要素的平均长度RSm通过以下的方法进行测定。
从卷取光学层叠体而成的各辊的长度方向中央的位置且辊宽度方向中央的位置切出50mm×50mm的测定样品。使用原子力显微镜(AFM:Atomic Force Microscope)(商品名SPA400,NanoNaviII;日立株式会社制)测定样品的表面,选定3处不受到硬涂层中所含的用于表现防眩功能的填料的影响的俯视下的直线,由该3处直线中的实际的凹凸计算要素的平均长度RSm。
另外,在这些实施例和比较例中,测定下述式(2)所示的要素的平均长度的变化率。
要素的平均长度的变化率(%)=((RSm2/RSm1)-1)×100(%)…式(2)
式(2)中,RSm1表示未进行表面处理而形成了防污层的、光学层叠体的防污层的要素的平均长度(RSm),RSm2表示对表面进行处理后形成了防污层的光学层叠体的、防污层的要素的平均长度(RSm)。
防污层的表面粗糙度Ra和要素的平均长度RSm受到其下的光学功能层的表面粗糙度Ra和要素的平均长度RSm的影响。特别是在通过蒸镀形成的防污层中,不存在如通过涂布法形成的防污层那样由涂料中所含的溶剂引起的空隙,高密度地形成,因此与通过涂布法形成的防污层相比,其下方的光学功能层的表面粗糙度Ra和要素的平均长度RSm的影响大。如果对光学功能层的表面进行辉光放电处理,则认为防污层的表面状态受到其影响而发生变化。关于实施例1与实施例4的表面粗糙度的差,认为是有在直至第二表面处理的期间解除了减压的影响。另外,实施例1与比较例3的表面粗糙度之差起因于有无辉光放电处理。
(水蒸气透过率)
实施例和比较例中的水蒸气透过率在以下的条件下测定。
将切成100mm×100mm的光学层叠体设置于水蒸气透过率测定装置(商品名PERMATRAN-W3/34,MOCON公司制),利用依据JIS K7129(ISO15106-2)的红外线传感器法在40℃、相对湿度90%的条件下继续测定,将24小时后的测定值作为水蒸气透过率。
另外,对实施例1~12、比较例1~12的光学层叠体(防反射膜)分别调查特性。将其结果示于以下的表中。实施例1~12、比较例1~12的特性测定中使用的试验片是从卷取光学层叠体而成的辊的长度方向大致中央附近切出的试验片。需要说明的是,比较例5、11的初始的氟量少,未进行关于耐久性的试验。
[表4]
[表5]
[表6]
[表7]
[表8]
[表9A]
[表9B]
(1)接触角(防污性)
(1-1)对纯水的接触角测定试验
使用全自动接触角计DM-700(协和界面化学株式会社制),在以下的条件下通过椭圆拟合法进行测定。将蒸馏水放入玻璃注射器中,在其前端安装不锈钢制的针,向光学层叠体(试验片)滴加纯水。
纯水的滴加量:2.0μL
测定温度:25℃
在试验片表面的任意6处测定滴加纯水经过4秒后的接触角,将其平均值作为纯水接触角。
(1-2)对油酸、正十六烷、二碘甲烷(试剂)的接触角测定试验
使用全自动接触角计DM-700(协和界面化学株式会社制),在以下的条件下通过椭圆拟合法进行测定。将上述各试剂放入玻璃注射器中,在其前端安装不锈钢制的针,在光学层叠体(试验片)上分别滴加各试剂。
各试剂的滴加量:2.0μL
测定温度:25℃
在试验片表面的任意10处测定滴加各试剂经过4秒后的接触角,将其平均值作为油酸、正十六烷、二碘甲烷各自的接触角。
(2)氟量测定试验
测定光学层叠体(试验片)的氟量(cps:每单位时间的计数)(清洗前氟量(初始状态的氟量))。
在氟量的测定中,使用X射线光电子能谱测定器(Electron Spectroscopy forChemical Analysis,化学分析电子光谱,ESCA)(PHI5000 VersaProb*eIII,ULVAC-PHI株式会社制)和荧光X射线分析法(X-ray fluorescence analysis,XRF)(EDX-8000,株式会社岛津制作所制)。通过X射线光电子能谱测定器和荧光X射线分析法求出的氟值(cps)是由初始状态下测定n=3、耐碱试验后测定n=15而得到的结果计算的平均值。
(3)耐碱性试验
测定光学层叠体(试验片)的光学特性(处理前样品)。
接着,制备浓度为0.1mol/L的氢氧化钠水溶液(试剂)。
然后,使内径38mm的圆筒状构件密合于光学层叠体(试验片),向其中滴加试剂,用玻璃板在上表面开口盖上盖子。然后,保持液温55℃静置4小时后,用蒸馏水清洗各试验片,得到处理后样品。
(3-1)光学特性测定(色相变化)
用透明胶带将上述的处理前样品和处理后样品的背面粘贴于黑色亚克力板,消除背面反射。然后,测定光学特性。
光学测定中使用积分球分光测色计(SP-64:X-rite株式会社制)。设定为D65光源、10°,计算处理前样品和处理后样品的基于SCI(Specular Component Include,将正反射光考虑在内的反射色的测定方法)的上述式(2)所示的L*a*b*(依据CIE1976)值的变化量即ΔE值。需要说明的是,作为上述式(2)中的L0*、a0*、b0*,代入处理前样品的值,作为L1*、a1*、b1*,代入与氢氧化钠水溶液接触后的处理后样品的值。
(3-2)利用碱溶液的氟残存量测定试验
与上述(2)的试验同样地操作,使用ESCA或XRF测定基于碱溶液的处理后样品的氟量(cps),计算处理后样品的氟的残存率(%)。
(4)使用钢丝棉的擦伤性试验
使用依据JIS L0849的摩擦试验机I型,使摩擦体沿着光学层叠体(试验片)的表面进行水平往复运动,得到试验片。
使用钢丝棉(BONSTAR株式会社制#0000号)作为摩擦体。试验设定为载荷1000g/cm2、行程75mm、速度7mm/s。表6、7表示摩擦体的水平往复次数。
(4-1)接触角
与上述(1-1)的试验同样地测定摩擦后的试验片的接触角,求出摩擦前与水平往复运动500次的摩擦后的试验片的接触角差。试验在摩擦后30分钟以内实施。
(4-2)光学特性测定(色相变化)
与上述(3-1)的试验同样地操作,计算摩擦前与水平往复运动500次(实施例6~12和比较例4~7为100次)的摩擦后的试验片的基于SCI的ΔL*a*b*值的变化量即ΔE值。
另外,与上述(3-1)的试验同样地操作,计算摩擦前与水平往复运动500次(实施例6~12和比较例4~7为100次)的摩擦后的试验片的基于SCE(Specular ComponentExclude,不将正反射光考虑在内的反射色的测定法)的上述式(3)所示的L*a*b*值的变化量即ΔE值。
(5)使用了布头(无纺布擦拭器)的擦伤性试验
除了使用布头(无纺布擦拭器)(Bemcot Lintfree CT-8,旭化成工业株式会社制)作为摩擦体以外,与使用钢丝棉的擦伤性试验同样地实施擦伤性试验。试验设定为载荷250g/cm2、行程25mm、速度50mm/s。表4、表5中示出摩擦体的水平往复运动次数。
(5-1)接触角
与上述(1-1)的试验同样地测定摩擦后的试验片的接触角,求出摩擦前与水平往复运动4000次的摩擦后的试验片的接触角差。试验在摩擦后30分钟以内实施。
(5-2)氟残存量测定试验
与上述(2)的试验同样地操作,使用ESCA测定进行4000次使用布头的水平往复运动后的处理后样品的氟量(cps),计算处理后样品的氟的残存率(%)。
(6)超声波清洗试验
将氟系溶剂(Fluorinert FC-3283:3M日本株式会社制)放入容器中,浸渍光学层叠体(试验片),使用超声波清洗机(USK-5R、ASONE公司制),以40KHz、240W施加10分钟超声波。然后,使用上述氟系溶剂冲洗试验片。
与上述(2)的试验同样地,使用XRF测定超声波清洗后样品的氟量(cps),计算清洗后样品的氟的残存率(%)。
(7)笔滑动试验
作为摩擦体,使用触控笔用笔尖(Bamboo Sketch/Bamboo Tip替换芯(中等类型)株式会社WACOM制),施加250g的载荷,确认进行20000次往复滑动后有无伤痕。
[通过蒸镀形成的防污层相对于通过涂布形成的防污层的优越性]
实施例1~4的光学层叠体与比较例1和2相比,使用了布头(无纺布擦拭器)的擦伤性试验中的接触角差小。实施例1的光学层叠体与比较例1和2相比,使用了布头(无纺布擦拭器)的擦伤性试验中的氟的残存率高。
实施例1~4的光学层叠体与比较例1和2相比,耐碱性试验中的色相变化小,氟的残存率高。
根据表2所示的结果,在显示防污性的接触角的测定中,对于油酸、正十六烷、二碘甲烷,与通过涂布形成的防污层(比较例2)相比,确认了通过蒸镀形成的防污层(实施例1)的优越性。
另外,确认了通过碱溶液、物理摩擦,实施例1与比较例2相比也能够进一步抑制光学特性的变化。
实施例1~4的光学层叠体在布头耐擦伤性试验中,接触角差为15°以下,变化少,能够维持初始的特性,为良好。另外,实施例1~4的光学层叠体在耐碱试验中的色相变化ΔE小,为10以下,为良好。实施例1的光学层叠体在钢丝棉耐擦伤性试验中,接触角差为15°以下,变化少,能够维持初始的特性,是良好的。
另外,在超声波清洗试验中,实施例1、4的氟的残存率均高,为70%以上,但在比较例1、2中,氟的残存率低,为62.7%、39.8%。
[辉光放电处理的效果]
在布头耐擦伤性试验中,实施例1~4的光学层叠体的接触角差均为12°以下,变化小,能够维持初始的特性,为良好,但在比较例3中,接触角差为22°,变化大。
另外,在耐碱性试验中,实施例1~4的光学层叠体的色相变化ΔE(SCI)均小,为小于10,氟的残存率也高,为85%以上,但在比较例3中,色相变化ΔE(SCI)大,为29.5,氟的残存率也低,为18.9%。
在钢丝棉耐擦伤性试验中,实施例1~3的光学层叠体的接触角差均为12°以下,变化小,色相变化ΔE(SCI)也小,为2.4以下,能够维持初始的特性,是良好的,但在比较例3中,接触角差为18°,变化大,色相变化ΔE(SCI)也大,为3.9。
在超声波清洗试验中,实施例1、4的氟的残存率均高,为70%以上,但比较例3的氟的残存率低,为60.9%。
以上的辉光放电处理的效果,即耐磨损性和耐碱性的提高,是由于光学功能层14表面被粗糙化成适当的粗糙度,存在于表面的结合力弱的物质被除去,从而光学功能层与防污层的密合性提高的结果。在耐碱性试验中,色相变化被显著抑制推测是防止了碱成分侵入光学功能层的最上表面的SiO2层的结果,推测这是因为构成防污层的分子高密度地与光学功能层化学键合。进一步进行考察,实施例1~4的防污层的表面粗糙度Ra和表面粗糙度的变化率RSm也有可能适合于构成防污层的分子的化学键的高密度化。
[光学功能层的成膜条件的效果]
比较例4与实施例1相比,水蒸气透过率高,耐碱试验后的氟的残存率低。比较例10与实施例6相比也具有同样的倾向。
即,认为若调整光学功能层的成膜时的压力,则光学功能层自身变得致密,难以透过水蒸气等。另外,认为通过使光学功能层自身变得致密,耐久性提高。
如上所述,若调整光学功能层的成膜时的压力,对光学功能层的表面进行处理,通过蒸镀且以规定的膜厚以上将防污层成膜,则各层变得致密,且与其他层的密合性提高,因此可得到显示所期望的特性的光学层叠体。
[AG型中的、通过蒸镀而形成的防污层相对于通过涂布而形成的防污层的优越性]
根据表5所示的结果,若在硬涂层的膜厚为3μm的情况下进行比较,则实施例6~8的光学层叠体与比较例7相比,耐碱性试验中的色相变化ΔE(SCI)小,为小于10,氟的残存率也高,为85%以上。在硬涂层的厚度为5μm的情况下的实施例9~12与比较例9的对比中也为同样的结果。
另外,在笔滑动试验中,与通过涂布形成的防污层相比,造成损伤的容易度不同,通过蒸镀法形成的防污层不会产生损伤。
[AG型中的辉光放电处理的效果]
对于辉光放电处理的效果,在硬涂层的厚度为5μm的情况下,与实施例9-12和比较例8相比,RSm为55nm~90nm时,耐碱性试验中的色相变化ΔE(SCI)小,为小于10,氟的残存率也高,为85%以上,是良好的。在硬涂层的厚度为3μm的情况下,实施例6~8与比较例6的对比也为同样的结果。
[防污层的膜厚的影响]
实施例6~8的光学层叠体的防污层的膜厚为2.5nm以上,与2nm的比较例11相比,耐碱性试验中的氟残存率高,为良好的结果。
符号说明
10、101、102…光学层叠体,11…透明基材,12…硬涂层,13…密合层,14…光学功能层,14a…高折射率层,14b…低折射率层,15…防污层,20…制造装置,1…溅射装置,2A、2B…预处理装置,3…蒸镀装置,4…辊放卷装置,5…辊卷取装置,20…制造装置,21…真空泵,22…导辊,23…放卷辊,24…卷取辊,25…成膜辊,26…罐状辊,31、32、33、34、35…腔室,41…成膜部,42…等离子放电装置,43…蒸镀源,53…加热装置。
Claims (20)
1.一种光学层叠体,其是依次层叠塑料薄膜、密合层、光学功能层和防污层而成的光学层叠体,
所述防污层由蒸镀防污性材料而成的蒸镀膜构成,
所述防污层的膜厚为2.5nm以上,
水蒸气透过率为1.5g/(m2·1天)以下,
与液温55℃、浓度0.1mol/L的氢氧化钠水溶液接触4小时后的将正反射光考虑在内即SCI的反射色的色相变化ΔE值小于10。
2.一种光学层叠体,其是依次层叠塑料薄膜、密合层、光学功能层和防污层而成的光学层叠体,其中,
所述防污层由蒸镀防污性材料而成的蒸镀膜构成,
所述防污层的膜厚为2.5nm以上,
水蒸气透过率为1.5g/(m2·1天)以下,
在与液温55℃、浓度0.1mol/L的氢氧化钠水溶液接触4小时后,使用荧光X射线分析法即XRF测定的氟的残存率为85%以上。
3.根据权利要求1或2所述的光学层叠体,其中,由下述式(1)所示的表面粗糙度的变化率为5~35%或由下述式(2)所示的要素的平均长度的变化率为7~70%;
表面粗糙度的变化率(%)=((Ra2/Ra1)-1)×100(%)…式(1)
式(1)中,Ra1表示未进行光学功能层的表面处理而形成了防污层的、光学层叠体的防污层的表面粗糙度即Ra,Ra2表示对光学功能层的表面进行处理后形成了防污层的、光学层叠体的防污层的表面粗糙度即Ra,
要素的平均长度的变化率(%)=((RSm2/RSm1)-1)×100(%)…式(2)
式(2)中,RSm1表示不进行光学功能层的表面处理而形成了防污层的、光学层叠体的防污层的要素的平均长度即RSm,RSm2表示对光学功能层的表面进行处理后形成了防污层的、光学层叠体的防污层的要素的平均长度即RSm,
其中,Ra2为3nm以上且10nm以下,Rsm2为55nm以上且90nm以下。
4.根据权利要求1~3中任一项所述的光学层叠体,其中,雾度为2%以下,使布头往复4000次的擦伤性试验前后的相对于水的接触角差为12°以下。
5.根据权利要求1~4中任一项所述的光学层叠体,其中,雾度为2%以下,使用依据JISL0849的使用了钢丝棉的摩擦试验机,摩擦前与使钢丝棉水平往复运动500次的摩擦后相对于水的接触角差为12°以下。
6.根据权利要求1~5中任一项所述的光学层叠体,其中,雾度为2%以下,摩擦前和使钢丝棉水平往复运动500次的摩擦后的将正反射光考虑在内即SCI的反射色的变化量即ΔE值为3.0以下。
7.根据权利要求1~6中任一项所述的光学层叠体,其中,雾度为2%以下,在氟系溶剂中照射40KHz、240W的超声波10分钟进行清洗后的通过XRF得到的防污层中的氟原子的残存量为70%以上。
8.根据权利要求1~3中任一项所述的光学层叠体,其中,雾度超过2%,使布头往复4000次的擦伤性试验前后的相对于水的接触角差为7°以下。
9.根据权利要求1~8中任一项所述的光学层叠体,其中,使用荧光X射线分析法即XRF测定的氟的初始量为0.03以上。
10.根据权利要求1~9中任一项所述的光学层叠体,其中,所述光学功能层包含选自防反射层和选择反射层中的任意1种。
11.根据权利要求1~10中任一项所述的光学层叠体,其中,所述光学功能层具备低折射率层。
12.根据权利要求1~11中任一项所述的光学层叠体,其中,所述光学功能层由低折射率层和高折射率层交替层叠而成的层叠体构成。
13.根据权利要求11或12所述的光学层叠体,其中,所述防污层与所述低折射率层接触而设置。
14.根据权利要求1~13中任一项所述的光学层叠体,其中,所述密合层包含金属或金属的氧化物。
15.根据权利要求1~14中任一项所述的光学层叠体,其中,所述密合层和所述光学功能层通过溅射而形成。
16.根据权利要求1~15中任一项所述的光学层叠体,其中,所述防污性材料包含氟系有机化合物。
17.根据权利要求1~16中任一项所述的光学层叠体,其中,在所述塑料薄膜与所述密合层之间还具备硬涂层。
18.一种物品,其具备权利要求1~17中任一项所述的光学层叠体。
19.一种光学层叠体的制造方法,其为权利要求1~18中任一项所述的光学层叠体的制造方法,具有:
光学功能层的成膜工序,其交替地具有在小于0.5Pa的真空度下将低折射率层成膜的工序和在小于1.0Pa的真空度下将高折射率层成膜的工序,
辉光放电处理工序,其利用辉光放电对所述光学功能层的表面进行表面处理,以及
防污层形成工序,其在所述光学功能层的一面侧形成由蒸镀膜构成的所述防污层,所述蒸镀膜通过真空蒸镀而蒸镀有防污性材料。
20.根据权利要求19所述的光学层叠体的制造方法,其特征在于,具有通过溅射形成所述光学功能层的光学功能层形成工序,在减压下连续进行所述光学功能层形成工序和所述防污层形成工序。