CN115895370A - 耐火防水超耐候单组分微水泥涂料 - Google Patents
耐火防水超耐候单组分微水泥涂料 Download PDFInfo
- Publication number
- CN115895370A CN115895370A CN202211314318.8A CN202211314318A CN115895370A CN 115895370 A CN115895370 A CN 115895370A CN 202211314318 A CN202211314318 A CN 202211314318A CN 115895370 A CN115895370 A CN 115895370A
- Authority
- CN
- China
- Prior art keywords
- resistant
- parts
- portions
- cement
- fire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种耐火防水超耐候单组分微水泥涂料，其包括以下重量份的组分：抗结剂0.7～1份、木质纤维1～2份、润湿剂4～5份、分散剂8～10份、丙二醇50～60份、纤维素纤维1～2份、消泡剂2～3份、纯丙乳液400～500份、成膜助剂30～40份、增稠剂1～2份、防腐剂1～2份、水泥140～160份、偏高岭土10～20份、抗碱剂2～3份、石英粉200～240份。该涂料形成的涂膜强韧富有弹性、耐刮擦、抗雨痕、耐沾污、超强耐候，耐冻融、耐紫外线、抗碱、快干，防水性能优异。
Description
技术领域
本发明涉及涂料领域，尤其涉及一种集阻燃、防水、超耐候于一体的适用于室内外装修墙及地面的涂料。
背景技术
传统水泥主要成分为石灰石、粘土，是一种粉状水硬性无机胶凝材料，加水搅拌后成浆体，能把砂、石等材料牢固地胶结在一起，是建筑业中不可或缺的重要材料。微水泥与传统水泥的主要区别是，其中加入了树脂材料。微水泥是英文中MICROCEMENT直译而成，是指含有硅酸盐水泥与乳液的混合而成的一种建筑装饰材料。现阶段，70％以上的内外墙饰面涂料以有机合成丙烯酸乳液为胶粘材料，其耐污、耐候性能差，且不具备防水性能。而90％以上的防水涂料又不具备良好的饰面效果，而同时兼具耐候性、抗沾污、耐水和防水功能的涂料市场上却鲜有销售。
目前，现有技术中的同时兼具耐候性、抗沾污、耐水及装饰作用的涂料绝大部分是双组分的，但双组分防水浆料，其液体组分在寒冷季节运输和储存及其不便，容易被冻坏，影响产品质量稳定性，而且在施工前还需要再进行配置，造成极大的不便。
如中国专利申请CN201811273632.X公开了一种集隔热、防水、超耐候于一体的复合型双组分涂料，该双组分装置涂料由以下重量份的组分组成：杀菌剂：0.2～3；阴离子表面活性剂：2～12；润湿剂：0.2～7；消泡剂：0.1～6；纤维素：0.3～9；钛白浆：20～150；纯丙乳液：700～920；成膜组剂：40～92；AMP 95：0.5～3；优创：40～80；增稠剂：0.2～4，进口水泥：500；偏高岭土：30；石英粉：470；木纤：2。但是，该复合型双组分涂料在施工过程前需要添加乳液、水进行搅拌后才可使用，对施工人员的专业性要求高。
又如专利申请CN 202111302421.6公开了一种外墙彩绘用涂料及其制备方法，包括以下成分：水、纯丙烯酸乳液、助剂、填料、钝化剂、水泥、水性色浆、紫外光吸收剂及光稳定剂。但是，该外墙彩绘用涂料也是双组分涂料，在施工过程中先将钝化剂加入水泥，搅拌形成膏状物质，再加入母料中，使水泥不能直接产生水化反应，因此施工前配料过程复杂，对施工人员的专业性要求高。
因此，提供一种配料过程简单并可集阻燃、防水、超耐候于一体的耐火防水超耐候单组分微水泥涂料成为业内急需解决的问题。
发明内容
本发明的目的是提供一种耐火防水超耐候单组分微水泥涂料，其集防水与装饰于一体，同时兼具超耐候、抗碱、快干、强韧性、耐刮擦、耐沾污及阻燃于一体。
为了实现上述目的，本发明提供了一种耐火防水超耐候单组分微水泥涂料，其包括以下重量份的组分：抗结剂0.7～1份、木质纤维1～2份、润湿剂4～5份、分散剂8～10份、丙二醇50～60份、纤维素纤维1～2份、消泡剂2～3份、纯丙乳液400～500份、成膜助剂30～40份、增稠剂1～2份、防腐剂1～2份、水泥140～160份、偏高岭土10～20份、抗碱剂2～3份、石英粉200～240份。
在本发明的耐火防水超耐候单组分微水泥涂料中，高含固乳液与丙二醇起到钝化作用，把水泥包裹，终止了水泥的水化反应，然后抗结剂捕捉体系内游离的钙、镁等离子，从而也起到终止水泥水化反应的作用，保证了单组分微晶水泥中水泥性质稳定，对水泥的硬化无不利影响。
可选择地，抗结剂为微晶纤维素或硅铝酸钠。
可选择地，润湿剂为辛基酚聚氧乙烯醚。优选地，润湿剂的型号为润湿剂X-405。
可选择地，分散剂为聚羧酸钠盐型的阴离子表面活性剂。
优选地，阴离子表面活性剂为分散剂5040。
优选地，纤维素纤维为人造纤维，主要包括粘胶纤维、醋酸纤维、铜氨纤维等，是利用棉短绒、木材、竹子、甘蔗渣、芦苇等天然物质，通过一定的工艺处理方法对其纤维素分子重塑而得。
优选地，消泡剂为消泡剂NXZ。
优选地，成膜助剂为十二碳醇酯。
可选择地，增稠剂选自甲基纤维素、羟乙基甲基纤维素、乙基纤维素、羟乙基纤维素、羟丙基甲基纤维素中的至少一种。
可选择地，防腐剂选自苯甲酸、苯甲酸盐、山梨酸、山梨酸盐、对羟基苯甲酸酯类中的至少一种。
可选择地，水泥选自硫铝酸盐水泥或硅酸盐水泥中的至少一种，比如硅酸盐水泥42.5或硅酸盐水泥52.5。
优选地，抗碱剂为火山灰和介孔二氧化硅按质量比1～2:1混合而成。
可选择地，石英粉的粒度为200～300目。
本发明的有益效果是：(1)、涂膜强韧富有弹性，可直接覆盖0.2毫米的裂缝；(2)、涂膜强度高，耐刮擦，抗雨痕、耐沾污，可免罩面；(3)、超强耐候，耐冻融、耐紫外线；(4)、具有抗碱性，如无平整度要求，可免腻子层、免抗碱底漆；(5)、防水性能优异，具有快干性，可淋雨、防水抗渗。
具体实施方式
下面详细描述本发明的实施例，下面描述的实施例是示例性的，旨在用于解释本发明，而不能理解为对本发明的限制。
作为一种非限制性实施方式，耐火防水超耐候单组分微水泥涂料包括以下重量份的组分：抗结剂0.7～1份、木质纤维1～2份、润湿剂4～5份、分散剂8～10份、丙二醇50～60份、纤维素纤维1～2份、消泡剂2～3份、纯丙乳液400～500份、成膜助剂30～40份、增稠剂1～2份、防腐剂1～2份、水泥140～160份、偏高岭土10～20份、抗碱剂2～3份、石英粉200～240份。
下面，将通过具体实施例说明本发明的耐火防水超耐候单组分微水泥涂料组成及性能。
表1实施例1～3的耐火防水超耐候单组分微水泥涂料
表2实施例4～6的耐火防水超耐候单组分微水泥涂料
表3实施例1～6的物理力学性能
由3的测试结果可以看出，实施例1～6的涂膜强韧富有弹性，在室外15～25度的条件下，2分钟即可凝固，约2小时表干，并且可以淋雨并具有隔热的效果。
在实施例1～6中，纯丙乳液和丙二醇起到钝化作用，把水泥包裹，终止了水泥的水化反应，然后微晶纤维或硅铝酸钠捕捉体系内游离的钙、镁等离子，从而也起到终止水泥水化反应的作用。由此，使得单组分微晶水泥的性能稳定，不会影响水泥的硬化，此外，纯丙乳液还可以作为粘接剂，使得涂料具有抗污及耐候的性能。
此外，实施例1～6的耐火防水超耐候单组分微水泥涂料中的分散剂5040的分散性优异，添加少量即可调整低粘度涂料，使得涂料的安定性比较好，涂料的粘度不发生变化。由于能够很好地分散颜料，故涂料无浮色，色斑，不需与其他润湿剂并用，可得到耐水性良好的涂膜。使用分散剂5040可以得到起泡少，破泡快的涂料，干燥时间不长，涂料容易涂布。
润湿剂X-405在酸性或碱性中，化学性能稳定。十二碳醇酯能促进高分子化合物塑性流动和弹性变形，改善聚结性能，能在较广泛施工温度范围内成膜。偏高岭土可以增强涂层后期的强度。石英粉作为骨料，可增加涂料强度。木质纤维可有效防止喷涂过程中产生飞溅的现象。
在本说明书的描述中，参考术语“一个实施例”、“一些实施例”、“示例”、“具体示例”、或“一些示例”等的描述意指结合该实施例或示例描述的具体特征、结构或者特点包含于本发明的至少一个实施例或示例中。在本说明书中，对上述术语的示意性表述不必须针对的是相同的实施例或示例。此外，在不相互矛盾的情况下，本领域的技术人员可以将本说明书中描述的不同实施例或示例以及不同实施例或示例的特征进行结合和组合。
尽管上面已经示出和描述了本发明的实施例，可以理解的是，上述实施例是示例性的，不能理解为对本发明的限制，本领域的普通技术人员在本发明的范围内可以对上述实施例进行变化、修改、替换和变型。
Claims (10)
1.一种耐火防水超耐候单组分微水泥涂料，其特征在于，包括以下重量份的组分：抗结剂0.7～1份、木质纤维1～2份、润湿剂4～5份、分散剂8～10份、丙二醇50～60份、纤维素纤维1～2份、消泡剂2～3份、纯丙乳液400～500份、成膜助剂30～40份、增稠剂1～2份、防腐剂1～2份、水泥140～160份、偏高岭土10～20份、抗碱剂2～3份、石英粉200～240份。
2.如权利要求1所述的耐火防水超耐候单组分微水泥涂料，其特征在于，所述抗结剂为微晶纤维素或硅铝酸钠。
3.如权利要求2所述的耐火防水超耐候单组分微水泥涂料，其特征在于，所述润湿剂为辛基酚聚氧乙烯醚。
4.如权利要求3所述的耐火防水超耐候单组分微水泥涂料，其特征在于，所述分散剂为聚羧酸钠盐型的阴离子表面活性剂。
5.如权利要求1所述的耐火防水超耐候单组分微水泥涂料，其特征在于，所述消泡剂为消泡剂NXZ。
6.如权利要求1所述的耐火防水超耐候单组分微水泥涂料，其特征在于，所述成膜助剂为十二碳醇酯。
7.如权利要求1所述的耐火防水超耐候单组分微水泥涂料，其特征在于，所述增稠剂选自甲基纤维素、羟乙基甲基纤维素、乙基纤维素、羟乙基纤维素、羟丙基甲基纤维素中的至少一种。
8.如权利要求1所述的耐火防水超耐候单组分微水泥涂料，其特征在于，所述防腐剂选自苯甲酸、苯甲酸盐、山梨酸、山梨酸盐、对羟基苯甲酸酯类中的至少一种。
9.如权利要求1所述的耐火防水超耐候单组分微水泥涂料，其特征在于，所述水泥选自硅酸盐水泥或硫铝酸盐水泥中的至少一种。
10.如权利要求1所述的耐火防水超耐候单组分微水泥涂料，其特征在于，所述石英粉的粒度为200～300目。