CN115368018A - Glass container sesame glaze and glazing method thereof - Google Patents
Glass container sesame glaze and glazing method thereof Download PDFInfo
- Publication number
- CN115368018A CN115368018A CN202211007563.4A CN202211007563A CN115368018A CN 115368018 A CN115368018 A CN 115368018A CN 202211007563 A CN202211007563 A CN 202211007563A CN 115368018 A CN115368018 A CN 115368018A
- Authority
- CN
- China
- Prior art keywords
- glaze
- glass container
- parts
- sesame
- workpiece
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a glass container sesame glaze, which comprises a glaze pigment for the bottom surface of a glass container and a glaze pigment for sprinkling points on the glass container; the glaze pigment for the bottom surface of the glass container comprises the following raw materials in parts by weight: 1500-2100 parts of bright red glaze, 200-300 parts of bright purple glaze, 10-30 parts of bright black glaze and 320-510 parts of matte powder glaze; the glaze pigment for sprinkling points on the glass container comprises the following raw materials in parts by weight: 60-150 parts of matte black glaze. The invention also discloses a glazing method of the glass container sesame glaze. The sesame glaze of the glass container prepared by the low-temperature glaze has high qualification rate, the color and the glossiness of the glass container are excellent, and the effect of ceramic glaze can be achieved.
Description
Technical Field
The invention relates to the technical field of glass container glaze, in particular to glass container sesame glaze and a glazing method thereof.
Background
The glass container is made of more than ten raw materials of cullet, soda ash, sodium nitrate, shellfish carbonate, quartz sand and the like through the processes of high-temperature melting and shaping at 1600 ℃ and the like. Glass bottle containers can be classified into bottles for wines, daily packaging glass bottles, can bottles, medical bottles and bottles for chemical reagents according to different purposes; can be divided into colorless transparent bottles, white bottles, brown bottles, green bottles and blue bottles according to different colors; can be divided into a neck bottle, a non-neck bottle, a long-neck bottle, a short-neck bottle, a thick-neck bottle and a thin-neck bottle according to the shape of the bottle neck.
At present, in order to improve the appearance grade of a glass bottle, one or more layers of pearlescent paint are often sprayed on the surface of the glass bottle, so that the glass bottle has visual effects of metallic feeling, high brightness, frosted feeling and the like.
The 'sesame glaze' belongs to one of the sauce glazes, is a high-temperature colored glaze with iron oxide as a coloring agent, the fired porcelain has a smooth and bright glaze surface, and the surface of the porcelain has uniform small sesame dots and twinkles with metallic luster. The ceramic glaze is a glaze applied on a ceramic ware, and generally quartz, feldspar and clay are used as raw materials, ground, mixed with water, coated on the surface of a blank, roasted at a certain temperature to be molten, and when the temperature is reduced, a vitreous thin layer on the surface of the ceramic is formed. It can increase the mechanical strength, thermal stability, dielectric strength and prevent the erosion of liquid and gas. The glaze can also improve the beautiful appearance of the porcelain, is convenient to wash and wipe, is not stained by dust, and the like.
In the prior art, most of glass containers adopt high-temperature glaze materials in the glazing process, few enterprises adopt low-temperature glaze materials to glaze, the glass containers prepared by glazing with the low-temperature glaze materials have extremely low qualification rate, and the color, the glossiness and the physicochemical property of the prepared glass containers can not achieve the effect of ceramic glaze, so that the low-temperature glaze materials and the glazing method are urgently needed, and the glaze surface can meet the requirement of the ceramic glaze while the qualification rate of the prepared glass containers is ensured.
Disclosure of Invention
The invention aims to provide a glass container sesame glaze and a glazing method thereof, which are used for solving the technical problem that the color and the glossiness of the glaze of the prepared glass container cannot achieve the effect of ceramic glaze when the glass container is glazed by using low-temperature glaze in the prior art.
In order to achieve the above object, one embodiment of the present invention provides a glass container sesame glaze, comprising a glass container bottom glaze pigment and a glass container dispensing glaze pigment;
the glaze pigment for the bottom surface of the glass container comprises the following raw materials in parts by weight: 1500-2100 parts of bright red glaze material, 200-300 parts of bright purple glaze material, 10-30 parts of bright black glaze material and 320-510 parts of matte powder glaze material;
the glaze pigment for sprinkling points on the glass container comprises the following raw materials in parts by weight: 60-150 parts of matte black glaze.
In one preferable scheme of the invention, the glaze pigment for the bottom surface of the glass container comprises the following raw materials in parts by weight: 1600-2060 parts of bright red glaze, 220-270 parts of bright purple glaze, 13-25 parts of bright black glaze and 360-450 parts of matte glaze;
the glaze pigment for sprinkling points on the glass container comprises the following raw materials in parts by weight: 76-135 parts of matte black glaze.
Based on the glass container sesame glaze disclosed by the invention, the invention also discloses a glazing method of the glass container sesame glaze, which comprises the following steps:
step (1): heating the workpiece;
step (2): dedusting a workpiece;
and (3): spraying base coat: spraying the ground glaze on the glass container obtained in the step (2) by using glaze pigment on the bottom surface of the glass container, standing after the spraying is finished, and entering the step (4) after the surface of the glass container is dried;
and (4): spraying sesame glaze: rotating the workpiece obtained in the step (3) at a constant speed, and uniformly spraying glaze pigment on a sprinkling point of a glass container onto the glass container through an air spray gun;
and (5): leveling sesame glaze: leveling the workpiece obtained in the step (4), and drying after leveling;
and (6): and (6) cooling.
In one preferable scheme of the invention, in the step (1), the heating temperature of the workpiece is 50-70 ℃, and the heating time of the workpiece is 3-7 min.
In the step (3), an auxiliary agent is added when the ground coat spraying is carried out on the workpiece, and the auxiliary agent is a mixture of ethanol, n-butyl alcohol and cellulose.
In one preferable scheme of the invention, the mass ratio of ethanol, n-butanol and cellulose in the mixture of ethanol, n-butanol and cellulose is 11-45.
In one preferable embodiment of the present invention, in the step (3), the standing time is 2min to 4min.
In one preferable embodiment of the present invention, in the step (4), the rotation speed of the workpiece is 1r/s to 3r/s, and the pressure of the air lance is 0.1Pa to 0.2Pa.
In the step (4), a multi-gun spraying process is adopted for spraying the sesame glaze on the workpiece.
According to one preferable scheme of the invention, in the step (5), natural leveling is adopted for leveling, the leveling time is 4-6 min, the drying temperature is 150-200 ℃, and the drying time is 13-17 min; in the step (6), the cooling is natural cooling.
In conclusion, the beneficial effects of the invention are as follows:
1. the sesame glaze of the glass container prepared by the low-temperature glaze has high qualification rate, the color and the glossiness of the glass container are excellent, and the effect of ceramic glaze can be achieved.
2. In the glazing method of the glass container sesame glaze, the sesame glaze is sprayed by an air spray gun, and the pressure of the air spray gun is limited to be 0.1Pa-0.2Pa. The pressure of the air spray gun is limited so that the glass container dispensing point glaze pigment exhibits an atomizing effect during the spraying process.
3. In the glazing method of the glass container sesame glaze, an auxiliary agent is also added in the process of spraying the ground coat, and the auxiliary agent is a mixture of ethanol, n-butyl alcohol and cellulose. The effect of adding the ethanol is to ensure that the sprayed ground coat is more uniform and has better dispersibility; the purpose of adding the cellulose is to make the ground glaze have granular feel, improve the surface viscosity of the low-temperature glaze and simultaneously have the defoaming effect.
Detailed Description
Example 1
A glass container sesame glaze comprises a glaze pigment for the bottom surface of a glass container and a glaze pigment for sprinkling points on the glass container;
the glaze pigment for the bottom surface of the glass container comprises the following raw materials in parts by weight: 1800 parts of bright red, 240 parts of bright purple, 15 parts of bright black and 400 parts of matte powder;
the glaze pigment for sprinkling points on the glass container comprises the following raw materials in parts by weight: 102 parts of matte black;
the model of bright red is LLY-TFL2C305, the model of bright purple is TFLC109S, the model of bright black is LW-TFLC901, the model of matte powder is 40001, and the model of matte black is LW-TFLU905.
A glazing method of glass container sesame glaze comprises the following steps:
step (1): heating a workpiece: and (3) putting the workpiece into a workpiece heating device for heating treatment to increase the adhesive force of subsequent glaze, wherein the workpiece is heated at the temperature of 50-70 ℃ for 3-7 min.
Step (2): workpiece dust removal: putting the workpiece into a dust removal device for dust removal treatment so as to ensure the quality of the finally prepared glass container;
and (3): spraying base coat: spraying the ground coat on the glass container obtained in the step (2) by using a glaze pigment on the bottom surface of the glass container, adding an auxiliary agent in the process of spraying the ground coat, wherein the auxiliary agent is a mixture of ethanol, n-butanol and cellulose, the mass ratio of the ethanol, the n-butanol and the cellulose is 50; the addition of the auxiliary agent aims at improving the spraying effect of the ground coat, wherein the ethanol is used for enabling the sprayed ground coat to be more uniform and better in dispersity, and the cellulose is used for enabling the ground coat to have granular feel, improving the surface viscosity of the low-temperature glaze and simultaneously having a defoaming effect.
And (4): spraying sesame glaze: rotating the workpiece obtained in the step (3) at a constant speed, wherein the rotation speed is 1r/s-3r/s, spraying glaze pigment on a glass container through an air spray gun, and uniformly spraying the glass container with the glaze pigment, wherein the pressure of the air spray gun is 0.1Pa-0.2Pa, and meanwhile, spraying sesame glaze on the workpiece can be carried out by adopting a multi-gun spraying process;
and (5): leveling sesame glaze: and (4) naturally leveling the workpiece obtained in the step (4) for 4-6 min, and drying the workpiece in an oven at the drying temperature of 150-200 ℃ for 13-17 min after leveling.
Example 2
A glass container sesame glaze comprises a glaze pigment for the bottom surface of a glass container and a glaze pigment for sprinkling points on the glass container;
the glaze pigment for the bottom surface of the glass container comprises the following raw materials in parts by weight: 2100 parts of bright red, 200 parts of bright purple, 30 parts of bright black and 320 parts of matte powder;
the glaze pigment for sprinkling points on the glass container comprises the following raw materials in parts by weight: 60 parts of matte black;
the model of bright red is LLY-TFL2C305, the model of bright purple is TFLC109S, the model of bright black is LW-TFLC901, the model of matte powder is 40001, and the model of matte black is LW-TFLU905.
A glazing method of glass container sesame glaze comprises the following steps:
step (1): heating a workpiece: and (3) putting the workpiece into a heating device for heating treatment to increase the adhesive force of subsequent glaze, wherein the heating temperature of the workpiece is 50-70 ℃, and the heating time of the workpiece is 3-7 min.
Step (2): workpiece dust removal: performing dust removal treatment on the workpiece to ensure the quality of the finally prepared glass container;
and (3): spraying base coat: carrying out ground coat spraying on the glass container obtained in the step (2) by using a glaze pigment on the bottom surface of the glass container, adding an auxiliary agent in the process of the ground coat spraying, wherein the auxiliary agent is a mixture of ethanol, n-butyl alcohol and cellulose, the mass ratio of the ethanol to the n-butyl alcohol to the cellulose is 11; the auxiliary agent is added to improve the spraying effect of the ground coat, wherein the ethanol has the functions of enabling the sprayed ground coat to be more uniform and better in dispersity, and the cellulose has the functions of enabling the ground coat to have granular feel, improving the surface viscosity of the low-temperature glaze and simultaneously having the defoaming effect.
And (4): spraying sesame glaze: rotating the workpiece obtained in the step (3) at a constant speed, wherein the rotation speed is 1r/s-3r/s, spraying glaze pigment on a glass container through an air spray gun, and uniformly spraying the glass container with the glaze pigment, wherein the pressure of the air spray gun is 0.1Pa-0.2Pa, and meanwhile, spraying sesame glaze on the workpiece can be carried out by adopting a multi-gun spraying process;
and (5): leveling sesame glaze: and (4) naturally leveling the workpiece obtained in the step (4) for 4-6 min, and drying the workpiece in an oven at the drying temperature of 150-200 ℃ for 13-17 min after leveling.
Example 3
A glass container sesame glaze comprises a glaze pigment for the bottom surface of a glass container and a glaze pigment for sprinkling points on the glass container;
the glaze pigment for the bottom surface of the glass container comprises the following raw materials in parts by weight: 1500 parts of bright red, 300 parts of bright purple, 10 parts of bright black and 510 parts of matte powder;
the glaze pigment for sprinkling points on the glass container comprises the following raw materials in parts by weight: 150 parts of matte black;
the model of bright red is LLY-TFL2C305, the model of bright purple is TFLC109S, the model of bright black is LW-TFLC901, the model of matte powder is 40001, and the model of matte black is LW-TFLU905.
A glazing method of glass container sesame glaze comprises the following steps:
step (1): heating a workpiece: and (3) putting the workpiece into a heating device for heating treatment to increase the adhesive force of subsequent glaze, wherein the heating temperature of the workpiece is 50-70 ℃, and the heating time of the workpiece is 3-7 min.
Step (2): workpiece dust removal: performing dust removal treatment on the workpiece to ensure the quality of the finally prepared glass container;
and (3): spraying base coat: spraying the ground coat on the glass container obtained in the step (2) by using a glaze pigment on the bottom surface of the glass container, adding an auxiliary agent in the process of spraying the ground coat, wherein the auxiliary agent is a mixture of ethanol, n-butyl alcohol and cellulose, the mass ratio of the ethanol, the n-butyl alcohol and the cellulose is 45; the addition of the auxiliary agent aims at improving the spraying effect of the ground coat, wherein the ethanol is used for enabling the sprayed ground coat to be more uniform and better in dispersity, and the cellulose is used for enabling the ground coat to have granular feel, improving the surface viscosity of the low-temperature glaze and simultaneously having a defoaming effect.
And (4): spraying sesame glaze: rotating the workpiece obtained in the step (3) at a constant speed, wherein the rotation speed is 1r/s-3r/s, spraying glaze pigment on a glass container through an air spray gun, and uniformly spraying the glaze pigment on the glass container, wherein the pressure of the air spray gun is 0.1Pa-0.2Pa, and meanwhile, spraying sesame glaze on the workpiece can be carried out by adopting a multi-gun spraying process;
and (5): leveling sesame glaze: and (5) naturally leveling the workpiece obtained in the step (4) for 4-6 min, and drying the workpiece in an oven after leveling, wherein the drying temperature is 150-200 ℃, and the drying time is 13-17 min.
Example 4
A glass container sesame glaze comprises a glaze pigment for the bottom surface of a glass container and a glaze pigment for sprinkling points on the glass container;
the glaze pigment for the bottom surface of the glass container comprises the following raw materials in parts by weight: 1600 parts of bright red, 270 parts of bright purple, 25 parts of bright black and 450 parts of matte powder;
the glaze pigment for sprinkling points on the glass container comprises the following raw materials in parts by weight: 135 parts of matte black;
the model of bright red is LLY-TFL2C305, the model of bright purple is TFLC109S, the model of bright black is LW-TFLC901, the model of matte powder is 40001, and the model of matte black is LW-TFLU905.
A glazing method of glass container sesame glaze comprises the following steps:
step (1): heating a workpiece: and (3) putting the workpiece into a heating device for heating treatment to increase the adhesive force of subsequent glaze, wherein the heating temperature of the workpiece is 50-70 ℃, and the heating time of the workpiece is 3-7 min.
Step (2): workpiece dust removal: performing dust removal treatment on the workpiece to ensure the quality of the finally prepared glass container;
and (3): spraying base coat: spraying the ground coat on the glass container obtained in the step (2) by using a glaze pigment on the bottom surface of the glass container, adding an auxiliary agent in the process of spraying the ground coat, wherein the auxiliary agent is a mixture of ethanol, n-butyl alcohol and cellulose, the mass ratio of the ethanol, the n-butyl alcohol and the cellulose is 20; the auxiliary agent is added to improve the spraying effect of the ground coat, wherein the ethanol has the functions of enabling the sprayed ground coat to be more uniform and better in dispersity, and the cellulose has the functions of enabling the ground coat to have granular feel, improving the surface viscosity of the low-temperature glaze and simultaneously having the defoaming effect.
And (4): spraying sesame glaze: rotating the workpiece obtained in the step (3) at a constant speed, wherein the rotation speed is 1r/s-3r/s, spraying glaze pigment on a glass container through an air spray gun, and uniformly spraying the glass container with the glaze pigment, wherein the pressure of the air spray gun is 0.1Pa-0.2Pa, and meanwhile, spraying sesame glaze on the workpiece can be carried out by adopting a multi-gun spraying process;
and (5): leveling sesame glaze: and (5) naturally leveling the workpiece obtained in the step (4) for 4-6 min, and drying the workpiece in an oven after leveling, wherein the drying temperature is 150-200 ℃, and the drying time is 13-17 min.
Example 5
A glass container sesame glaze comprises a glaze pigment for the bottom surface of a glass container and a glaze pigment for sprinkling points on the glass container;
the glaze pigment for the bottom surface of the glass container comprises the following raw materials in parts by weight: bright red 2060 parts, bright purple 220 parts, bright black 13 parts and matte 360 parts;
the glaze pigment for sprinkling points on the glass container comprises the following raw materials in parts by weight: 76 portions of matte black;
the model of bright red is LLY-TFL2C305, the model of bright purple is TFLC109S, the model of bright black is LW-TFLC901, the model of matte powder is 40001, and the model of matte black is LW-TFLU905.
A glazing method of glass container sesame glaze comprises the following steps:
step (1): heating a workpiece: and (3) putting the workpiece into a heating device for heating treatment to increase the adhesive force of subsequent glaze, wherein the heating temperature of the workpiece is 50-70 ℃, and the heating time of the workpiece is 3-7 min.
Step (2): workpiece dust removal: performing dust removal treatment on the workpiece to ensure the quality of the finally prepared glass container;
and (3): spraying base coat: spraying the ground coat on the glass container obtained in the step (2) by using a glaze pigment on the bottom surface of the glass container, adding an auxiliary agent in the process of spraying the ground coat, wherein the auxiliary agent is a mixture of ethanol, n-butyl alcohol and cellulose, the mass ratio of the ethanol, the n-butyl alcohol and the cellulose is 48; the auxiliary agent is added to improve the spraying effect of the ground coat, wherein the ethanol has the functions of enabling the sprayed ground coat to be more uniform and better in dispersity, and the cellulose has the functions of enabling the ground coat to have granular feel, improving the surface viscosity of the low-temperature glaze and simultaneously having the defoaming effect.
And (4): spraying sesame glaze: rotating the workpiece obtained in the step (3) at a constant speed, wherein the rotation speed is 1r/s-3r/s, spraying glaze pigment on a glass container through an air spray gun, and uniformly spraying the glaze pigment on the glass container, wherein the pressure of the air spray gun is 0.1Pa-0.2Pa, and meanwhile, spraying sesame glaze on the workpiece can be carried out by adopting a multi-gun spraying process;
and (5): leveling sesame glaze: and (5) naturally leveling the workpiece obtained in the step (4) for 4-6 min, and drying the workpiece in an oven after leveling, wherein the drying temperature is 150-200 ℃, and the drying time is 13-17 min.
In conclusion, the glass container with the sesame glaze prepared by the invention has high qualification rate, and the glaze surface of the glass container has excellent color, uniformity and glossiness, and can achieve the effect of ceramic glaze. The sesame glaze material for the glass container and the glazing method meet the qualification rate of the glass container, and the glaze surface of the glass container can achieve the effect of ceramic glaze.
Claims (10)
1. The glass container sesame glaze is characterized in that: comprises glaze pigment for the bottom surface of a glass container and glaze pigment for sprinkling points on the glass container;
the glaze pigment for the bottom surface of the glass container comprises the following raw materials in parts by weight: 1500-2100 parts of bright red glaze, 200-300 parts of bright purple glaze, 10-30 parts of bright black glaze and 320-510 parts of matte powder glaze;
the glaze pigment for sprinkling points on the glass container comprises the following raw materials in parts by weight: 60-150 parts of matte black glaze.
2. The glass container sesame glaze of claim 1 wherein: the glaze pigment for the bottom surface of the glass container comprises the following raw materials in parts by weight: 1600-2060 parts of bright red glaze, 220-270 parts of bright purple glaze, 13-25 parts of bright black glaze and 360-450 parts of matte glaze;
the glaze pigment for sprinkling points on the glass container comprises the following raw materials in parts by weight: 76-135 parts of matte black glaze.
3. A glazing method of glass container sesame glaze is characterized by comprising the following steps:
step (1): heating a workpiece;
step (2): dedusting a workpiece;
and (3): spraying base coat: spraying the bottom glaze on the glass container obtained in the step (2) by using glaze pigment on the bottom surface of the glass container, standing after the spraying is finished, and entering the step (4) until the surface of the glass container is dried;
and (4): spraying sesame glaze: rotating the workpiece obtained in the step (3) at a constant speed, and uniformly spraying glaze pigment on a sprinkling point of a glass container onto the glass container through an air spray gun;
and (5): leveling sesame glaze: leveling the workpiece obtained in the step (4), and drying after leveling;
and (6): and (6) cooling.
4. A glazing method of glass container sesame glaze according to claim 1, characterized in that: in the step (1), the workpiece is heated at 50-70 ℃ for 3-7 min.
5. A glazing method of glass container sesame glaze according to claim 1, characterized in that: in the step (3), an auxiliary agent is added when the workpiece is subjected to ground coat spraying, wherein the auxiliary agent is a mixture of ethanol, n-butanol and cellulose.
6. A glazing method of glass container sesame glaze according to claim 5, wherein: the mass ratio of the ethanol to the n-butanol to the cellulose in the mixture of the ethanol to the n-butanol to the cellulose is 11-45.
7. A glazing method of glass container sesame glaze according to claim 3, wherein: in the step (3), the standing time is 2-4 min.
8. A glazing method of glass container sesame glaze according to claim 3, characterized in that: in the step (4), the rotation speed of the workpiece is 1r/s-3r/s, and the pressure of the air spray gun is 0.1Pa-0.2Pa.
9. A glazing method of glass container sesame glaze according to claim 3, wherein: in the step (4), the sesame glaze is sprayed on the workpiece by adopting a multi-gun spraying process.
10. A glazing method of glass container sesame glaze according to claim 3, wherein: in the step (5), natural leveling is adopted for leveling, the leveling time is 4-6 min, the drying temperature is 150-200 ℃, and the drying time is 13-17 min; in the step (6), the cooling is natural cooling.