CN115259787A - 一种无机抗渗阻燃门窗缝填充砂浆及生产工艺 - Google Patents
一种无机抗渗阻燃门窗缝填充砂浆及生产工艺 Download PDFInfo
- Publication number
- CN115259787A CN115259787A CN202210824772.1A CN202210824772A CN115259787A CN 115259787 A CN115259787 A CN 115259787A CN 202210824772 A CN202210824772 A CN 202210824772A CN 115259787 A CN115259787 A CN 115259787A
- Authority
- CN
- China
- Prior art keywords
- inorganic
- flame
- parts
- window
- impervious
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及建筑材料技术领域，具体的涉及一种无机抗渗阻燃门窗缝填充砂浆及生产工艺，由硅酸盐水泥200～400份、石英砂300～500份、硅灰粉100～200份、膨胀珍珠岩0.2～1份、粘结剂5～10份、无机抗渗剂0.1～0.4份、保水剂0.1～0.3份以及淀粉酶0.05～0.2份组成，本发明的无机抗渗阻燃门窗缝填充砂浆使用硅酸盐水泥体系，加入膨胀特性的珍珠岩，很好的控制砂浆的收缩与膨胀，不会收缩、不易开裂，防渗漏性能好，加入VAE可再分散胶粉和淀粉醚，增加修补砂浆的粘结力，提高修补砂浆的粘结性能，起防水作用，引入无机抗渗剂，增加填缝材料的热阻，避免门窗框处出现冷热桥，起到防火阻燃和抗渗的特效。
Description
技术领域
本发明涉及建筑材料技术领域，具体的涉及一种无机抗渗阻燃门窗缝填充砂浆及生产工艺。
背景技术
长时间以来住宅建筑门窗渗漏水问题一直是较为普遍的现象，这也是住宅用户反映最为强烈的问题之一。房屋墙面出现这种因渗漏导致大面积墙面剥落，最终导致房屋潮湿而使房间霉味很浓，不仅损坏了室内的装饰，也直接影响到住户的身心健康。不仅如此，为修补建筑渗漏房室，人们为此花费的人务和物力及财力是相当巨大的，扰乱着人们的工作、生活，影响着整幢建筑物的使用寿命。填缝密封材料选用及质量的好坏是影响门窗工程质量的最主要原因之一。在门窗安装中最常用的填缝材料为水泥砂浆、聚氨酯泡沫等，由于普通水泥砂浆粘结力差，变形能力差，容易收缩开裂，很容易出现渗漏现象。聚氨酯发泡密封胶粘接性好，填缝施工速度也较快、弹性好，具有优良复原性，可适合于动态接缝，但聚氨酯密封胶也有一些缺点，如施工质量不易控制、发泡剂填充不密实易造成漏水，材料本身耐水性能较差，特别是耐碱水、耐热性能差，单组分胶贮存稳定性受包装及外界影响较大，通常固化较慢，高温热环境下可能产生气泡和裂纹，许多场合需要底涂，成本较高也影响了此种材料的应用。因此，研制新型施工方便、耐久性好且价格便宜的门窗填缝密封材料是亟待解决的问题。
申请号为201910912317.5的中国专利复合型门窗填缝砂浆及其使用方法，其中粉料包括以下重量份数的组份：水泥50-65份，矿物掺合料15-25份，密实剂10-16份，抗收缩剂0.2-0.4份，聚苯乙烯颗粒3-5份，纤维素醚0.1-0.3份，触变剂0.3-0.5份，憎水剂0.2-0.4份，减水剂0.05-0.3份；其中液料包括以下重量份数的组份：聚合物乳液20-35份，消泡剂0.1-0.5份，分散剂0.05-0.6份，抑菌剂0.03-0.2份，水60-70份；粉料与液料的质量比为1:0.35-0.45。该种复合型门窗填缝砂浆具有许多优点，但也有一些不足之处，由于该复合型门窗填缝砂浆为了增加抗渗性能以及加固能力和抗变形能力，采用了过量的有机物原料，导致填充后的门窗缝存在填充材料发泡、填充效果时间短以及漏水情况，严重时还可能产生有毒物质以及引发火灾的可能，针对以上不足，本发明充分利用无机抗渗剂的优点，抗渗、防火、阻燃等特点，生产一种无机抗渗阻燃门窗缝填充砂浆，并且材料本身无毒环保，是一种环境友好型材料。
发明内容
本发明的目的是为了克服现有技术所存在的技术缺陷，提供一种无机抗渗阻燃门窗缝填充砂浆及生产工艺。
为了实现上述目的，本发明提供一种无机抗渗阻燃门窗缝填充砂浆，包括如下重量份的组分：硅酸盐水泥200～400份、石英砂300～500份、硅灰粉100～200份、膨胀珍珠岩0.2～1份、粘结剂5～10份、无机抗渗剂0.1～0.4份、保水剂0.1～0.3份以及淀粉酶0.05～0.2份。
优选地，无机抗渗阻燃门窗缝填充砂浆包括如下重量份的组分：硅酸盐水泥300份、石英砂400份、硅灰粉150份、膨胀珍珠岩0.5份、粘结剂8份、无机抗渗剂0.2份、保水剂0.2份以及淀粉酶0.1份。
优选地，硅酸盐水泥为PO42.5或PO52.5型号。
优选地，石英砂级配为20～60目。
优选地，膨胀珍珠岩粒径为1～3mm。
优选地，粘结剂为VAE可再分散胶粉。
优选地，保水剂为甲基羧甲基纤维素。
本发明还提供一种无机抗渗阻燃门窗缝填充砂浆的生产工艺，按配方称取各种原材料，在搅拌仓中依次加入硅酸盐水泥、石英砂、硅灰粉、膨胀珍珠岩、粘结剂、无机抗渗剂、保水剂以及淀粉酶，充分搅拌均匀，得到无机抗渗阻燃门窗缝填充砂浆产品，然后转到成品仓进行包装。
优选地，搅拌的时间为10min。
通过本发明提供的这种方法生产的无机抗渗阻燃门窗缝填充砂浆，有益效果是：
1、该材料施工性能好，操作简便，可操作时间长，该材料加水搅拌即可使用，可采用填缝枪注射填充缝隙，施工快速高效。
2、使用硅酸盐水泥体系，再加入膨胀特性的珍珠岩，从而很好的控制砂浆的收缩与膨胀，从而不会收缩、不易开裂，防渗漏性能好。
3、该材料中加入VAE可再分散胶粉和淀粉醚，可增加修补砂浆的粘结力，提高修补砂浆的粘结性能，起防水作用，同时加入无机抗渗剂，增加填缝材料的热阻，可避免在门窗框处出现冷热桥，起到防火阻燃和抗渗的特效。
4、该填充砂浆材料以无机材料为主要成分，耐久性好、不存在老化问题，而且无毒，可以很好的保护生产施工人员的健康。
具体实施方式
在本文中所披露的范围的端点和任何值都不限于该精确的范围或值，这些范围或值应当理解为包含接近这些范围或值的值。对于数值范围来说，各个范围的端点值之间、各个范围的端点值和单独的点值之间，以及单独的点值之间可以彼此组合而得到一个或多个新的数值范围，这些数值范围应被视为在本文中具体公开。
本发明提供一种无机抗渗阻燃门窗缝填充砂浆，包括如下重量份的组分：硅酸盐水泥200～400份、石英砂300～500份、硅灰粉100～200份、膨胀珍珠岩0.2～1份、粘结剂5～10份、无机抗渗剂0.1～0.4份、保水剂0.1～0.3份以及淀粉酶0.05～0.2份。
进一步的，无机抗渗阻燃门窗缝填充砂浆包括如下重量份的组分：硅酸盐水泥300份、石英砂400份、硅灰粉150份、膨胀珍珠岩0.5份、粘结剂8份、无机抗渗剂0.2份、保水剂0.2份以及淀粉酶0.1份。
进一步的，硅酸盐水泥为PO42.5或PO52.5型号。
进一步的，石英砂级配为20～60目。
进一步的，膨胀珍珠岩粒径为1～3mm。
进一步的，粘结剂为VAE可再分散胶粉。
进一步的，保水剂为甲基羧甲基纤维素。
本发明还提供一种无机抗渗阻燃门窗缝填充砂浆的生产工艺，按配方称取各种原材料，在搅拌仓中依次加入硅酸盐水泥、石英砂、硅灰粉、膨胀珍珠岩、粘结剂、无机抗渗剂、保水剂以及淀粉酶，充分搅拌均匀，得到无机抗渗阻燃门窗缝填充砂浆产品，然后转到成品仓进行包装。
进一步的，搅拌的时间为10min。
以下将通过实施例对本发明进行详细描述。
实施例1
本实施例用于说明本发明所述的无机抗渗阻燃门窗缝填充砂浆。
按配方称取各种原材料，在搅拌仓中依次加入硅酸盐水泥、石英砂、硅灰粉、膨胀珍珠岩、VAE可再分散胶粉、无机抗渗剂、甲基羧甲基纤维素以及淀粉酶，充分搅拌10min，得到无机抗渗阻燃门窗缝填充砂浆产品，然后转到成品仓进行包装。
其中无机抗渗阻燃门窗缝填充砂浆配方为：PO42.5硅酸盐水泥300份、20～60石英砂400份、硅灰粉150份、1～3mm膨胀珍珠岩0.5份、VAE可再分散胶粉8份、无机抗渗剂0.2份、甲基羧甲基纤维素0.2份以及淀粉酶0.1份。
实施例2
本实施例用于说明本发明所述的无机抗渗阻燃门窗缝填充砂浆。
按配方称取各种原材料，在搅拌仓中依次加入硅酸盐水泥、石英砂、硅灰粉、膨胀珍珠岩、VAE可再分散胶粉、无机抗渗剂、甲基羧甲基纤维素以及淀粉酶，充分搅拌10min，得到无机抗渗阻燃门窗缝填充砂浆产品，然后转到成品仓进行包装。
其中无机抗渗阻燃门窗缝填充砂浆配方为：PO52.5硅酸盐水泥300份、20～60石英砂400份、硅灰粉150份、1～3mm膨胀珍珠岩0.5份、VAE可再分散胶粉8份、无机抗渗剂0.2份、甲基羧甲基纤维素0.2份以及淀粉酶0.1份。
实施例3
本实施例用于说明本发明所述的无机抗渗阻燃门窗缝填充砂浆。
按配方称取各种原材料，在搅拌仓中依次加入硅酸盐水泥、石英砂、硅灰粉、膨胀珍珠岩、VAE可再分散胶粉、无机抗渗剂、甲基羧甲基纤维素以及淀粉酶，充分搅拌10min，得到无机抗渗阻燃门窗缝填充砂浆产品，然后转到成品仓进行包装。
其中无机抗渗阻燃门窗缝填充砂浆配方为：PO42.5硅酸盐水泥200份、20～60石英砂份500份、硅灰粉100份、1～3mm膨胀珍珠岩1份、VAE可再分散胶粉10份、无机抗渗剂0.4份、甲基羧甲基纤维素0.3份以及淀粉酶0.2份。
实施例4
本实施例用于说明本发明所述的无机抗渗阻燃门窗缝填充砂浆。
按配方称取各种原材料，在搅拌仓中依次加入硅酸盐水泥、石英砂、硅灰粉、膨胀珍珠岩、VAE可再分散胶粉、无机抗渗剂、甲基羧甲基纤维素以及淀粉酶，充分搅拌10min，得到无机抗渗阻燃门窗缝填充砂浆产品，然后转到成品仓进行包装。
其中无机抗渗阻燃门窗缝填充砂浆配方为：PO42.5硅酸盐水泥400份、20～60石英砂份300份、硅灰粉200份、1～3mm膨胀珍珠岩0.2份、VAE可再分散胶粉5份、无机抗渗剂0.1份、甲基羧甲基纤维素0.1份以及淀粉酶0.05份。
对比例1
本实施例用于说明本发明所述的无机抗渗阻燃门窗缝填充砂浆。
按配方称取各种原材料，在搅拌仓中依次加入硅酸盐水泥、石英砂、硅灰粉、膨胀珍珠岩、VAE可再分散胶粉、无机抗渗剂、甲基羧甲基纤维素以及淀粉酶，充分搅拌10min，得到无机抗渗阻燃门窗缝填充砂浆产品，然后转到成品仓进行包装。
其中PO42.5硅酸盐水泥300份、20～60石英砂400份、硅灰粉150份、1～3mm膨胀珍珠岩0.5份、VAE可再分散胶粉8份、甲基羧甲基纤维素0.2份以及淀粉酶0.1份，本对比例中未添加无机抗渗剂。
对比例2
本实施例用于说明本发明所述的无机抗渗阻燃门窗缝填充砂浆。
按配方称取各种原材料，在搅拌仓中依次加入硅酸盐水泥、石英砂、硅灰粉、膨胀珍珠岩、VAE可再分散胶粉、无机抗渗剂、甲基羧甲基纤维素以及淀粉酶，充分搅拌10min，得到无机抗渗阻燃门窗缝填充砂浆产品，然后转到成品仓进行包装。
其中PO42.5硅酸盐水泥450份、20～60石英砂300份、硅灰粉250份、1～3mm膨胀珍珠岩2份、VAE可再分散胶粉15份、无机抗渗剂0.5份、甲基羧甲基纤维素0.5份以及淀粉酶0.4份，本对比例中各原料不在本发明范围内。
对比例3
本实施例用于说明本发明所述的无机抗渗阻燃门窗缝填充砂浆。
按配方称取各种原材料，在搅拌仓中依次加入硅酸盐水泥、石英砂、硅灰粉、膨胀珍珠岩、VAE可再分散胶粉、无机抗渗剂、甲基羧甲基纤维素以及淀粉酶，充分搅拌10min，得到无机抗渗阻燃门窗缝填充砂浆产品，然后转到成品仓进行包装。
其中PO42.5硅酸盐水泥150份、20～60石英砂550份、硅灰粉50份、1～3mm膨胀珍珠岩0.1份、VAE可再分散胶粉3份、无机抗渗剂0.05份、甲基羧甲基纤维素0.05份以及淀粉酶0.03份，本对比例中各原料不在本发明范围内。
将实施例1-4和对比例1-3的无机抗渗阻燃门窗缝填充砂浆按照标准JGJ/T70-2009《建筑砂浆基本性能试验方法标准》规定的测试方法进行测试，其测试结果见下表1。
表1实施例1-4和对比例1-3的无机抗渗阻燃门窗缝填充砂浆检测结果
由表1可以看出，实施例1-4的无机抗渗阻燃门窗缝填充砂浆具有优异的拉伸粘结能力，抗渗的能力更高，且具有良好的加固能力和抗变形能力；收缩率小，不容易收缩开裂。
以上详细描述了本发明的优选实施方式，但是，本发明并不限于此。在本发明的技术构思范围内，可以对本发明的技术方案进行多种简单变型，包括各个技术特征以任何其它的合适方式进行组合，这些简单变型和组合同样应当视为本发明所公开的内容，均属于本发明的保护范围。
Claims (9)
1.一种无机抗渗阻燃门窗缝填充砂浆，其特征在于：包括如下重量份的组分：硅酸盐水泥200～400份、石英砂300～500份、硅灰粉100～200份、膨胀珍珠岩0.2～1份、粘结剂5～10份、无机抗渗剂0.1～0.4份、保水剂0.1～0.3份以及淀粉酶0.05～0.2份。
2.根据权利要求1所述的一种无机抗渗阻燃门窗缝填充砂浆，其特征在于，包括如下重量份的组分：硅酸盐水泥300份、石英砂400份、硅灰粉150份、膨胀珍珠岩0.5份、粘结剂8份、无机抗渗剂0.2份、保水剂0.2份以及淀粉酶0.1份。
3.根据权利要求1所述的一种无机抗渗阻燃门窗缝填充砂浆，其特征在于，所述硅酸盐水泥为PO42.5或PO52.5型号。
4.根据权利要求1所述的一种无机抗渗阻燃门窗缝填充砂浆，其特征在于，所述石英砂级配为20～60目。
5.根据权利要求1所述的一种无机抗渗阻燃门窗缝填充砂浆，其特征在于，所述膨胀珍珠岩粒径为1～3mm。
6.根据权利要求1所述的一种无机抗渗阻燃门窗缝填充砂浆，其特征在于，所述粘结剂为VAE可再分散胶粉。
7.根据权利要求1所述的一种无机抗渗阻燃门窗缝填充砂浆，其特征在于，所述保水剂为甲基羧甲基纤维素。
8.根据权利要求1～7任一项所述的一种无机抗渗阻燃门窗缝填充砂浆的生产工艺，其特征在于，按配方称取各种原材料，在搅拌仓中依次加入硅酸盐水泥、石英砂、硅灰粉、膨胀珍珠岩、粘结剂、无机抗渗剂、保水剂以及淀粉酶，充分搅拌均匀，得到无机抗渗阻燃门窗缝填充砂浆产品，然后转到成品仓进行包装。
9.根据权利要求8所述的一种无机抗渗阻燃门窗缝填充砂浆的生产工艺，所述搅拌的时间为10min。