CN102690091A - 一种中空微珠砌筑专用保温砂浆与专用抹面砂浆 - Google Patents
一种中空微珠砌筑专用保温砂浆与专用抹面砂浆 Download PDFInfo
- Publication number
- CN102690091A CN102690091A CN201210161274XA CN201210161274A CN102690091A CN 102690091 A CN102690091 A CN 102690091A CN 201210161274X A CN201210161274X A CN 201210161274XA CN 201210161274 A CN201210161274 A CN 201210161274A CN 102690091 A CN102690091 A CN 102690091A
- Authority
- CN
- China
- Prior art keywords
- special
- mortar
- thermal insulation
- stones
- hollow beads
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种中空微珠砌筑专用保温砂浆与专用抹面砂浆涉及一种建筑节能技术,尤其是一种墙体自保温***配套专用的中空微珠砌筑专用保温砂浆与专用抹面砂浆。中空微珠砌筑专用保温砂浆包括下列重量组份的原料:特种水泥20-30%、粉煤灰2-6%、石英砂20-35%、母料5-8%、中空微珠35-45%、重质碳酸钙3-6%;中空微珠砌筑专用抹面砂浆包括下列重量组份的原料:普硅水泥28-40%、粉煤灰3-6%、聚合物7-10%、石英砂40-55%、中空微珠10-16%、重质碳酸钙1-3%。本发明提供了一种导热系数低、保温隔热效果好、抗压强度高、粘接强度高、收缩性小、环保、防火的墙体自保温***配套专用的保温砂浆与抹面砂浆,综合经济效益显著。可广泛推广运用于墙体自保温***建筑物。
Description
技术领域
本发明涉及一种建筑节能技术,尤其是一种墙体自保温***配套专用的中空微珠砌筑专用保温砂浆与专用抹面砂浆。
背景技术
墙体自保温***是指按照一定的建筑构造,采用节能型墙体材料及配套专用的砂浆,使墙体热工性能等物理性能指标符合相应标准的建筑墙体保温隔热***。
墙体自保温***按基层墙体材料不同可分为蒸压加气混凝土砌块墙体自保温***,节能型烧结页岩空心砌块墙体自保温***,陶粒混凝土小型空心砌块墙体自保温***等,都采用的是轻质保温砌块。
普通砌筑砂浆一般为水泥砂浆或混合砂浆,其表观密度一般在1600——1800kg/ ,导热系数为0.8——1.0W/(m·k);而轻质保温砌块的表观密度一般在450——950 kg/,导热系数为0.15——0.35W/(m·k)。用普通砌筑砂浆砌筑轻质保温砌块墙体时由于二者的导热系数相差较大,致使整个砌体存在“冷桥”现象,由砌筑灰缝引起的能量损失很大,甚至会出现墙面结露等现象,导致建筑物使用寿命缩短和使用功能降低。使用一般的保温砂浆砌筑轻质保温砌块墙体时,砌体强度会受到影响,而且砂浆与轻质砌块的粘接不理想。因此,研究具有良好的和易性、粘接强度以及在干缩变形、导热性能上与轻质砌块相近的专用保温砌筑砂浆,具有重要的意义。
本申请人——湖北天泉新型建筑材料有限公司研究开发的、专利号为200910127347.1《一种玻化微珠保温隔热材料及其制备方法》已获得发明专利权,作为实心墙体的保温隔热层其保温隔热效果良好、又外罩防渗抗裂抹面砂浆,保证保温隔热层的质量效果,导热系数低、保温隔热性能好、强度高、具有独特的性能优势,在建筑行业得到广泛使用。
本申请人针对墙体自保温***砌筑砂浆的性能要求研发、生产的中空微珠砌筑专用保温砂浆与专用抹面砂浆的导热系数为0.25W/(m· k)、抗压强度≥5Mpa/、粘接强度≥0.20Mpa/、收缩性能≤1mm/m,是墙体自保温***理想的砌筑专用保温砂浆与专用抹面砂浆。
经检索,国内尚未有与本发明相同的专利申请。
发明内容
针对上述存在的不足之处,本发明提供一种导热系数低、保温隔热性能好、防渗抗裂性能好、和易性好、粘接强度高、在干缩变形、导热性能上与轻质砌块相近的一种中空微珠砌筑专用保温砂浆与专用抹面砂浆。
本发明解决其技术问题的技术方案是:一种中空微珠砌筑专用保温砂浆与专用抹面砂浆包括中空微珠砌筑专用保温砂浆、中空微珠砌筑专用抹面砂浆,所述的中空微珠砌筑专用保温砂浆包括下列重量组份的原料:特种水泥20-30%、粉煤灰2-6%、石英砂20-35%、母料5-8%、中空微珠35-45%、重质碳酸钙3-6%,六组份原料按比例配料搅拌而成,其中所述的母料包括下列重量组份的原料——可再分散乳胶粉1.5-2.5%、甲基羟丙纤维素醚0.6-1.1%、有机硅憎水剂0.3-0.7%、引气剂0.15-0.45%、糖蜜缓凝剂0.10-0.30%、硫铝酸钙基的膨胀剂0.5-1.2%、木质纤维0.5-1.2%、减水剂0.1-0.5%;所述的中空微珠砌筑专用抹面砂浆包括下列重量组份的原料:普硅水泥28-40%、粉煤灰3-6%、聚合物7-10%、石英砂40-55%、中空微珠10-16%、重质碳酸钙1-3%,六组份原料按比例配料搅拌而成,其中所述的聚合物为下列重量组份的原料——甲基羟丙纤维素醚0.5-1.5%、可再分散乳胶粉1-3%、羟丙基冷水可溶淀粉醚0.01-1.0%、聚丙乙烯纤维0.2-1.5%、木质纤维0.2-1.2%、触变润滑剂0.1-0.8%、灰钙1-3%、增稠胶粉0.5-1%、渗透结晶型防水剂1.0-2.2%;所述的中空微珠是由硅酸盐矿物质经过高温工艺生产而成的,粒径为50-100μm的不规则中空球状体,也叫玻化微珠,容重80-100㎏/,堆积密度0.1-0.3 g/,导热系数0.03-0.045 W/(m·k);所述的特种水泥为硫铝酸盐水泥;所述的粉煤灰采用Ⅱ级粉煤灰;所述的重质碳酸钙为100目重质碳酸钙;所述的石英砂为40-60目的石英砂;所述的可再分散乳胶粉采用台湾大连化工生产的VINAVIL -1410可再分散乳胶粉;所述的甲基羟丙纤维素醚可采用HPMC甲基羟丙纤维素醚;所述的有机硅憎水剂采用VINAVIL.HPB有机硅憎水剂;所述的木质纤维长度为5-8mm;所述的羟丙基冷水可溶淀粉醚选用300-800mpa.s淀粉醚;所述的聚丙乙烯纤维长度为5-8 mm。
本发明的有益效果是:
1.本发明保温隔热效果好,导热系数低,能消除墙体灰缝带来的冷热桥。使用作保温隔热材料的中空微珠也叫玻化微珠是由硅酸盐矿物质经过高温工艺生产而成的,粒径为50-100μm的不规则中空球状体,强度高、防火,导热系数低,保温隔热效果好。按国家建材行业标准GC890_2001《蒸压加气混凝土用砌筑砂浆与抹面砂浆》的导热系数小于1.1 W/(m·k),本发明的中空微珠砌筑专用保温砂浆与专用抹面砂浆实测导热系数为0.25 W/(m·k),大大减少了砌筑灰缝引起的能量损失,还由于容重低减轻了墙体结构重量、减少基础荷载,同时在收缩性能、导热性能上与轻质砌块相近,很好地消除了墙体灰缝带来的冷热桥现象。
2.本发明强度高、粘接性能好,具有与建筑同寿命。本发明的中空微珠砌筑专用保温砂浆在粘接材料中采用特种水泥,其特点是早期强度高,在降低压折比、弹性模量、和提高粘接强度方面则采用聚合物可再分散乳胶粉来实现、保水剂使材料中的水分逐渐释放,防止高温环境下的水化热反应太快、控制早期开裂,同时加入了无机纤维和有机高弹模量的纤维,防止整体开裂。实测抗压强度≥5Mpa/、粘接强度≥0.20Mpa/、收缩性能≤1mm/m,纠正了其它传统保温砂浆中诸多缺陷和不足,如克服了膨胀珍珠岩吸水性大、易粉化、干固后收缩率大、易造成产品后期强度低,保温性能降低等现象。
3.本发明具有环保优势——无毒、无污染、无辐射、不怕火。现有建筑保温材料和粘接剂中多数含有甲醛等有害物质,属有机保温材料,已成为我国保温住宅中的公害,成为危害人体健康的污染源。本发明的中空微珠砌筑专用保温砂浆和中空微珠砌筑专用抹面砂浆属无机保温材料,无毒、无污染、无辐射、不怕火,且生产过程不用更多能源、不用高温蒸压,无废气、无污水排放,是理想的、环保的、砌筑专用保温材料。
4.本发明在墙体自保温***的保温隔热墙体表面再抹涂中空微珠砌筑专用抹面砂浆——防渗抗裂柔性砂浆罩面,防止开裂导致潮气或雨水的侵蚀,造成保温隔热传导系数的增大而降低保温隔热效果,同时该砂浆是用柔性控制变形,改变压力传导方向、控制裂缝产生,而混合物中的抗裂剂是高耐拉聚丙乙烯纤维和木质纤维,在1平方米的砂浆中分布有几亿根均匀无序状分布的纤维,犹如几亿根“微钢筋”***砂浆中,极大地提高了抗开裂、抗冲击、防渗效果。
5.用本发明中空微珠砌筑专用保温砂浆与中空微珠砌筑专用抹面砂浆替代普通砂浆进行砌筑与抹面,不需要其他辅助材料、施工工序少、施工方便、施工速度块,据测算可提高综合劳动效率20%以上,降低工程造价10%左右,综合经济效益显著。
可广泛推广运用于墙体自保温***建筑物。
具体实施方式
本发明是一种中空微珠砌筑专用保温砂浆与专用抹面砂浆,包括中空微珠砌筑专用保温砂浆、中空微珠砌筑专用抹面砂浆,具体实施运用在墙体自保温***中,作为基层墙体为轻质保温砌块的砌筑专用保温砂浆和专用抹面砂浆。
实施例一
1.中空微珠砌筑专用保温砂浆:
中空微珠砌筑专用保温砂浆包括下列重量组份的原料:特种水泥21%、粉煤灰5%、石英砂26%、母料6%、中空微珠38%、重质碳酸钙4%,六组份原料按比例配料搅拌而成,其中所述的母料包括下列重量组份的原料——可再分散乳胶粉2.1%、甲基羟丙纤维素醚0.85%、有机硅憎水剂0..55%、引气剂0.35%、糖蜜缓凝剂0.22%、硫铝酸钙基的膨胀剂0.8%、木质纤维0.8%、减水剂0.33%。
2.中空微珠砌筑专用抹面砂浆:
中空微珠砌筑专用抹面砂浆包括下列重量组份的原料:普硅水泥30%、粉煤灰4%、聚合物8%、石英砂44%、中空微珠12%、重质碳酸钙2%,六组份原料按比例配料搅拌而成,其中所述的聚合物为下列重量组份的原料——甲基羟丙纤维素醚0.8%、可再分散乳胶粉2.25%、羟丙基冷水可溶淀粉醚0.05%、聚丙乙烯纤维0.2%、木质纤维0.6%、触变润滑剂0.1%、灰钙2%、增稠胶粉0.6%、渗透结晶型防水剂1.4%。
中空微珠砌筑专用保温砂浆和中空微珠砌筑专用抹面砂浆是采用预混合干拌技术,在工厂将上述各原料严格按重量组份、按生产工艺要求的时间均匀混合后包装成袋。本发明产品为单组份包装,运至施工现场,只需加规定的水量,搅拌至塑性良好的膏状浆料后即可施工使用。
①中空微珠砌筑专用保温砂浆浆料的制作:
在施工现场按照包装袋上的说明,进行操作:料浆水、灰重量比为0.4:1。先将规定的水量放入搅拌容器中,再将中空微珠砌筑专用保温砂浆放入加水后的搅拌容器中,搅拌3-5min,使其浆料成为塑性良好的膏状体,即可使用。料浆必须即配即用,配制好的料浆需在2h或3h内用完、并不得二次加水使用。
②中空微珠砌筑专用抹面砂浆浆料的制作:
在施工现场按照包装袋上的说明,进行操作:料浆水、灰重量比为0.4:1。先将规定的水量放入搅拌容器中,再将中空微珠砌筑专用抹面砂浆放入加水后的搅拌容器中,搅拌3-5min,使其浆料成为塑性良好的膏状体,即可使用。料浆必须即配即用,配制好的料浆需在2h或3h内用完、并不得二次加水使用。
实施例二
1.中空微珠砌筑专用保温砂浆:
中空微珠砌筑专用保温砂浆包括下列重量组份的原料:特种水泥23%、粉煤灰4%、石英砂28%、母料5%、中空微珠35%、重质碳酸钙5%,六组份原料按比例配料搅拌而成,其中所述的母料包括下列重量组份的原料——可再分散乳胶粉2 %、甲基羟丙纤维素醚0.7%、有机硅憎水剂0.4%、引气剂0.2%、糖蜜缓凝剂0.1%、硫铝酸钙基的膨胀剂0.7%、木质纤维0.7%、减水剂0.2%。
2.中空微珠砌筑专用抹面砂浆:
中空微珠砌筑专用抹面砂浆包括下列重量组份的原料:普硅水泥32%、粉煤灰3%、聚合物7%、石英砂42%、中空微珠13%、重质碳酸钙3%,六组份原料按比例配料搅拌而成,其中所述的聚合物为下列重量组份的原料——甲基羟丙纤维素醚0.7%、可再分散乳胶粉2.1%、羟丙基冷水可溶淀粉醚0.05%、聚丙乙烯纤维0.1%、木质纤维0.5%、触变润滑剂0.05%、灰钙1.7%、增稠胶粉0.5%、渗透结晶型防水剂1.3%。
实施例二的中空微珠砌筑专用保温砂浆和中空微珠砌筑专用抹面砂浆的制作方法与料浆配制方法与实施例一相同。
Claims (7)
1.一种中空微珠砌筑专用保温砂浆与专用抹面砂浆,其特征在于:该一种中空微珠砌筑专用保温砂浆与专用抹面砂浆包括中空微珠砌筑专用保温砂浆、中空微珠砌筑专用抹面砂浆,所述的中空微珠砌筑专用保温砂浆包括下列重量组份的原料:特种水泥20-30%、粉煤灰2-6%、石英砂20-35%、母料5-8%、中空微珠35-45%、重质碳酸钙3-6%,六组份原料按比例配料搅拌而成,其中所述的母料包括下列重量组份的原料——可再分散乳胶粉1.5-2.5%、甲基羟丙纤维素醚0.6-1.1%、有机硅憎水剂0.3-0.7%、引气剂0.15-0.45%、糖蜜缓凝剂0.10-0.30%、硫铝酸钙基的膨胀剂0.5-1.2%、木质纤维0.5-1.2%、减水剂0.1-0.5%;所述的中空微珠砌筑专用抹面砂浆包括下列重量组份的原料:普硅水泥28-40%、粉煤灰3-6%、聚合物7-10%、石英砂40-55%、中空微珠10-16%、重质碳酸钙1-3%,六组份原料按比例配料搅拌而成,其中所述的聚合物为下列重量组份的原料——甲基羟丙纤维素醚0.5-1.5%、可再分散乳胶粉1-3%、羟丙基冷水可溶淀粉醚0.01-1.0%、聚丙乙烯纤维0.2-1.5%、木质纤维0.2-1.2、触变润滑剂0.1-0.8%、灰钙1-3%、增稠胶粉0.5-1%、渗透结晶型防水剂1.0-2.2%。
3.根据权利要求1所述的一种中空微珠砌筑专用保温砂浆与专用抹面砂浆,其特征在于:所述的特种水泥为硫铝酸盐水泥。
4.根据权利要求1所述的一种中空微珠砌筑专用保温砂浆与专用抹面砂浆,其特征在于:所述的粉煤灰采用Ⅱ级粉煤灰。
5.根据权利要求1所述的一种中空微珠砌筑专用保温砂浆与专用抹面砂浆,其特征在于:所述的重质碳酸钙为100目重质碳酸钙。
6.根据权利要求1所述的一种中空微珠砌筑专用保温砂浆与专用抹面砂浆,其特征在于:所述的石英砂为40-60目石英砂。
7.根据权利要求1所述的一种中空微珠砌筑专用保温砂浆与专用抹面砂浆,其特征在于:所述的可再分散乳胶粉采用台湾大连化工生产的VINAVIL -1410可再分散乳胶粉;所述的甲基羟丙纤维素醚可采用HPMC甲基羟丙纤维素醚;所述的有机硅憎水剂采用VINAVIL.HPB有机硅憎水剂;所述的木质纤维长度为5-8mm;所述的羟丙基冷水可溶淀粉醚选用300-800mpa.s淀粉醚;所述的聚丙乙烯纤维长度为5-8 mm。