CN114506127A - Barite medical protective clothing material and preparation method thereof - Google Patents
Barite medical protective clothing material and preparation method thereof Download PDFInfo
- Publication number
- CN114506127A CN114506127A CN202210159493.8A CN202210159493A CN114506127A CN 114506127 A CN114506127 A CN 114506127A CN 202210159493 A CN202210159493 A CN 202210159493A CN 114506127 A CN114506127 A CN 114506127A
- Authority
- CN
- China
- Prior art keywords
- barite
- protective clothing
- woven fabric
- medical protective
- clothing material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of medical protective clothing materials, and particularly relates to a barite medical protective clothing material and a preparation method thereof. The barite medical protective clothing material provided by the invention comprises an isolation layer and an outer protective layer, wherein the thickness of the isolation layer is 190-300 mu m, and the thickness of the outer protective layer is 150-230 mu m; the preparation method comprises the following steps: physically purifying and grinding barite; mixing the barite fine powder with polyethylene according to the weight ratio: 3.5: 6.5 or 4: 7.5, uniformly kneading, and performing hot press molding to obtain the non-woven fabric of the isolation layer; and carrying out hot rolling compounding on the isolating layer non-woven fabric and the polypropylene spun-bonded non-woven fabric to obtain the barite medical protective clothing material. The material has the advantages of good radiation protection performance and low preparation cost, has good air permeability and moisture permeability, and can be reused after washing and disinfection.
Description
The application is a divisional application with application date of 2017, 10 and 08, application number of 201710926767.0 and invention name of barite medical protective clothing material and a preparation method thereof.
Technical Field
The invention belongs to the technical field of medical protective clothing materials, and particularly relates to a barite medical protective clothing material and a preparation method thereof.
Background
In recent years, radiological intervention has been widely performed with advanced X-ray diagnosis, development and rapid popularization of angiocardiography and angioplasty. In the fine operation of cardiovascular angiography and angioplasty, the medical radiologist needs to be exposed to the X-ray field for a long time. If the body is continuously or intermittently exposed to X-rays for a long time and reaches a certain dose, cells in the tissue are inactivated by ionizing radiation, thereby causing radioactive damage, such as hematopoietic tissue damage, and even causing leukemia, skin cancer, etc. If the eye is exposed to overdose radiation for a long time, the eye can cause lens lesion and generate radiation cataract.
The research on medical X-ray protection is mostly limited to walls, building materials, baffles of medical equipment and the like, the attention on the protective equipment of medical staff is less, and due to reasons such as cost and the like, most medical units cannot use protective clothing with better protective performance, and the protective clothing is disposable under special conditions, so that the resource waste is caused, the cost is high, and the health safety of the medical staff is difficult to ensure. Early medical X-ray protective clothing generally used lead as a shielding material, and because of heavy weight and hard texture, muscles of the back and the waist of medical radiology workers are tired and even damaged, and the medical radiology workers are expensive and easy to cause lead poisoning. Under the development trend, how to protect medical staff from various rays is particularly important.
With the rapid development of the non-woven fabric, medical surgical gowns are also different day by day, the non-woven fabrics such as the anti-sticking fabric, the spunlace fabric, the SMS composite fabric and the flash evaporation fabric are produced, and the anti-sticking fabric has the advantages and the disadvantages when being applied to the medical surgical gowns, is poor in air permeability, texture, low in hydrostatic pressure and protection performance and low in price, so that the anti-sticking fabric is the main non-woven fabric for manufacturing the surgical gowns in China. Generally, in order to achieve a protective effect, the fabric of the surgical gown is subjected to lamination or laminating treatment, so that the fabric is thick and has very poor air permeability; the spunlace fabric is most like a traditional woven fabric, is soft and has good drapability, but the spunlace technology is limited, the spunlace non-woven fabrics used for the surgical gown are few, and the spunlace surgical gown is generally imported from abroad and has high price, so that few hospitals use the spunlace surgical gown in China; the SMS non-woven fabric has good protective performance, strength and abrasion resistance, but the online composite SMS has high cost and poor hand feeling; the flash cloth has good filtration performance, but is very uneven, and is only available from dupont and asahi chemical companies with monopoly technology, which is very expensive.
Disclosure of Invention
The barite medical protective clothing material provided by the invention has the advantages of X-ray protection function and low preparation cost, has good air and moisture permeability, and can be reused after being washed and/or disinfected.
In order to achieve the purpose, the invention adopts the following technical scheme to realize the purpose: the barite medical protective clothing material comprises an isolation layer and an outer protective layer, wherein the isolation layer is prepared from barite fine powder and polyethylene according to a weight ratio of 3.5: 6.5 or 4: 7.5, the thickness is 190-300 mu m; the outer protective layer is made of polypropylene spun-bonded non-woven fabric, and the thickness of the outer protective layer is 150-230 microns;
BaSO in the barite fine powder4The content is more than or equal to 98 percent; the particle size of the barite fine powder is 1000-1250 meshes; the thickness of the medical protective clothing material is 420-450 mu m.
The invention also provides a preparation method of the barite medical protective clothing material, which comprises the following steps:
(1) selecting Hunan Henan barite ore, and performing hand selection, gravity selection and magnetic separation physical purification to obtain BaSO4Barite with content more than or equal to 98%; grinding the barite to obtain barite fine powder with the particle size of 1000-1250 meshes;
(2) mixing the barite fine powder obtained in the step (1) with polyethylene according to a weight ratio of 3.5: 6.5 or 4: 7.5, uniformly kneading, and performing hot press molding to obtain the non-woven fabric of the isolation layer;
(3) and (3) carrying out hot rolling compounding on the non-woven fabric of the isolating layer in the step (2) and the polypropylene spun-bonded non-woven fabric, and controlling the hot rolling temperature to be 130-140 ℃ to obtain the barite medical protective clothing material.
Preferably, the temperature of the hot press molding in the step (2) is 105-120 ℃.
According to the barite medical protective clothing material provided by the invention, the non-woven fabric is combined with the barite in the non-metal mineral, so that the characteristics of light texture of the non-woven fabric are maintained, the advantages of X-ray protection function and low preparation cost are achieved, the material has good air permeability and moisture permeability, and the material can be repeatedly used after being washed and/or disinfected.
The preparation method provided by the invention has the advantages of simple process and low preparation cost.
Drawings
In order to more clearly illustrate the embodiments of the present invention or the technical solutions in the prior art, the drawings needed to be used in the embodiments will be briefly described below, and it is obvious that the drawings in the following description are only some embodiments of the present invention, and it is obvious for those skilled in the art to obtain other drawings without inventive exercise.
FIG. 1 is a flow chart of a preparation process of barite medical protective clothing.
Detailed Description
To further illustrate the present invention, the following detailed description of the invention is given in conjunction with the accompanying drawings, but they are not to be construed as limiting the scope of the invention.
Example 1:
the barite medical protective clothing material comprises an isolation layer and an outer protective layer, wherein the isolation layer is prepared from barite fine powder and polyethylene according to a weight ratio of 3.5: 6.5, the outer protective layer is made of polypropylene spun-bonded non-woven fabric and has the thickness of 230 mu m. The preparation method comprises the following steps:
(1) preparing raw materials: firstly, selecting Hunan barite ore, and carrying out hand selection, gravity selection and magnetic separation physical purification to obtain BaSO4Barite with content more than or equal to 98%;
and secondly, grinding the barite prepared in the step I into powder, wherein the grain size of the ground powder is 1250 meshes.
(2) Preparing an isolation layer: mixing the barite fine powder prepared in the step (1) with polyethylene according to a weight ratio of 3.5: 6.5, uniformly kneading, and carrying out hot press molding at 105 ℃ to obtain the protective clothing isolating layer non-woven fabric with the thickness of 190 microns.
(3) Preparing a medical protective clothing material: and (3) carrying out hot rolling compounding on the non-woven fabric of the isolating layer prepared in the step (2) and the polypropylene spun-bonded non-woven fabric, wherein the hot rolling temperature is controlled at 130 ℃ and is not more than 140 ℃ at most.
In the preparation method, the thickness of the polypropylene spun-bonded non-woven fabric selected in the step (3) is 230 microns, and the thickness of the prepared medical protective clothing is 420 microns.
Example 2
The barite medical protective clothing material comprises an isolation layer and an outer protective layer, wherein the isolation layer is prepared from barite fine powder and polyethylene according to a weight ratio of 4: 7.5, the thickness is 300 μm, the outer protective layer is polypropylene spun-bonded non-woven fabric, and the thickness is 150 μm. The preparation method comprises the following steps:
(1) preparing raw materials: firstly, selecting Hunan barite ore, and carrying out hand selection, gravity selection and magnetic separation physical purification to obtain BaSO4Barite with content more than or equal to 98%;
and secondly, grinding the barite prepared in the step I into powder, wherein the particle size of the ground powder is 1000 meshes.
(2) Preparing an isolation layer: mixing the barite fine powder prepared in the step (1) with polyethylene according to a weight ratio of 4: 7.5, uniformly kneading, and carrying out hot press molding at the temperature of 120 ℃ to obtain the protective clothing isolating layer non-woven fabric with the thickness of 190 mu m.
(3) Preparing a medical protective clothing material: and (3) carrying out hot rolling compounding on the non-woven fabric of the isolating layer prepared in the step (2) and the polypropylene spun-bonded non-woven fabric, wherein the hot rolling temperature is controlled at 135 ℃.
In the preparation method, the thickness of the polypropylene spun-bonded non-woven fabric selected in the step (3) is 150 microns, and the thickness of the prepared medical protective clothing is 450 microns.
The barite medical protective clothing material prepared in the examples 1 and 2 is inspected and cut into a medical protective clothing finished product after being naturally cooled.
The protective clothing prepared by the invention is compared with other medical protective clothing on the market, and the following table shows.
TABLE 1 comparison of several protective garment Properties
As can be seen from the table above, the medical radiation-proof protective clothing prepared by the invention has better performance in all aspects than the products on the market, and has great advantages in the aspects of tensile strength, air permeability, moisture permeability, ray protection and the like.
Although the above embodiments have been described in detail, they are only a part of the embodiments of the present invention, not all of the embodiments, and other embodiments can be obtained without inventive step according to the embodiments, and all of the embodiments belong to the protection scope of the present invention.
Claims (3)
1. The barite medical protective clothing material is composed of an isolation layer and an outer protective layer, and is characterized in that the isolation layer is prepared from barite fine powder and polyethylene according to a weight ratio of 3.5: 6.5 or 4: 7.5, the thickness is 190-300 mu m; the outer protective layer is made of polypropylene spun-bonded non-woven fabric, and the thickness of the outer protective layer is 150-230 microns;
BaSO in the barite fine powder4The content is more than or equal to 98 percent; the particle size of the barite fine powder is 1000-1250 meshes; the thickness of the medical protective clothing material is 420-450 mu m.
2. The preparation method of the barite medical protective clothing material as claimed in claim 1, which comprises the following steps:
(1) selecting Hunan Henan barite ore, and performing hand selection, gravity selection and magnetic separation physical purification to obtain BaSO4Barite with content more than or equal to 98%; grinding the barite to obtain barite fine powder with the particle size of 1000-1250 meshes;
(2) mixing the barite fine powder obtained in the step (1) with polyethylene according to a weight ratio of 3.5: 6.5 or 4: 7.5, uniformly kneading, and performing hot press molding to obtain the non-woven fabric of the isolation layer;
(3) and (3) carrying out hot rolling compounding on the non-woven fabric of the isolating layer in the step (2) and the polypropylene spun-bonded non-woven fabric, and controlling the hot rolling temperature to be 130-140 ℃ to obtain the barite medical protective clothing material.
3. The preparation method according to claim 2, wherein the temperature of the hot press molding in the step (2) is 105 to 120 ℃.