CN114425402B - 重、渣油加氢脱硫催化剂及其制备方法 - Google Patents
重、渣油加氢脱硫催化剂及其制备方法 Download PDFInfo
- Publication number
- CN114425402B CN114425402B CN202011182280.4A CN202011182280A CN114425402B CN 114425402 B CN114425402 B CN 114425402B CN 202011182280 A CN202011182280 A CN 202011182280A CN 114425402 B CN114425402 B CN 114425402B
- Authority
- CN
- China
- Prior art keywords
- catalyst
- macroporous
- pore volume
- alumina
- catalyst body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
反应温度,℃ | 385 |
反应压力,MPa | 15.0 |
体积空速,h-1 | 0.4 |
氢油比,V/V | 800 |
运转时间,h | 催化剂A脱硫率,% | 催化剂F脱硫率,% | 催化剂D1脱硫率,% | 催化剂D2脱硫率,% |
100 | 100 | 98.8 | 95.3 | 97.2 |
500 | 99.7 | 97.6 | 92.6 | 96.1 |
1000 | 99.4 | 96.6 | 90.4 | 94.8 |
1500 | 99.0 | 95.8 | 88.5 | 93.5 |
2000 | 98.6 | 95.0 | 86.9 | 92.1 |
Claims (16)