CN114425400A - 一种耐磨损催化裂化催化剂及其制备方法与应用 - Google Patents
一种耐磨损催化裂化催化剂及其制备方法与应用 Download PDFInfo
- Publication number
- CN114425400A CN114425400A CN202011020394.9A CN202011020394A CN114425400A CN 114425400 A CN114425400 A CN 114425400A CN 202011020394 A CN202011020394 A CN 202011020394A CN 114425400 A CN114425400 A CN 114425400A
- Authority
- CN
- China
- Prior art keywords
- catalytic cracking
- cracking catalyst
- molecular sieve
- heat capacity
- specific heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种耐磨损催化裂化催化剂及其制备方法和应用,所述催化裂化催化剂含有1‑60重量%的裂化活性组元、1‑50重量%的高比热容基质材料、1‑70重量%的粘土和1‑70重量%的粘结剂;所述基质材料含有5‑94.5重量%的氧化铝、5‑94.5重量%氧化锰以及0.5‑10重量%的磷氧化物,所述裂化活性组元包括第一分子筛和任选的第二分子筛。其制备方法包括:将裂化活性组元、高比热容基质材料、粘土和粘结剂形成浆液喷雾干燥的步骤。所述催化裂化催化剂抗磨损性能好,在重油催化裂化的过程中具有较好的重油转化能力,选择性好。
Description
技术领域
本发明属于催化裂化技术领域,涉及一种催化裂化催化剂及其制备方法 与应用。
背景技术
随着石油资源的日益短缺,原油价格不断攀升,各大炼厂通过深度加工 重质油和使用劣质油来降低成本,以使效益最大化,目前催化裂化是重油加 工的重要手段。
然而,劣质原油的重金属(如钒、镍)含量一般较高,尤其近年来,由 于原料油的重质化、劣质化程度加重以及机会原油的加工,催化裂化催化剂 金属中毒的现象日益普遍。众多研究结果表明,铁、镍等金属一旦在表面沉 积就难以迁移,而且会与硅、铝、钒、钠等元素相互作用形成低熔点共熔物, 使催化剂表面烧结,进而在表面形成一层2-3μm厚的致密层,堵塞反应物进 入催化剂以及产物扩散的孔道,恶化产品分布。严重的金属污染会导致催化 剂流化性能变差,活性中心的可接近性降低,催化剂选择性变差,干气、焦 炭产率增加等突出问题,有的装置甚至面临停工的风险。
为了减少油品中的金属对催化裂化的影响,现有技术中采用添加金属捕 集组分以消除或弱化其影响,然而,由于大部分金属捕集组分同时也会对催 化剂的活性造成影响,因而大多以单独助剂的形式引入到催化剂***,当直 接引入催化剂中时,添加受到严格限制,往往不能发挥出期望的作用。
CN101939095A公开一种分子筛催化剂及其制备方法以在高温高湿的 恶劣环境中通过催化裂解石脑油而制备轻质烯烃。具体来说,所述催化剂 是通过对混合浆料进行喷雾干燥并煅烧而制备的,其中在所述混合浆料中, 将0.01-5.0重量%的MnO2和1-15重量%的P2O5同时嵌入到由沸石、粘土 和无机复合物构成的催化剂中。其将锰和磷以溶解的形式混合在催化剂浆 料中,对催化剂的改进效果非常有限,且该催化剂主要用于石脑油转化,没有涉及重油转化。
发明内容
本发明要解决的技术问题是提供一种耐磨损的重油催化裂化催化剂,该 催化剂具有较好的耐磨性,并具有良好的催化裂化性能。本发明要解决的另 外的技术问题是提供所述催化裂化催化剂的制备方法以及所述催化裂化催 化剂在重油催化裂化中的应用。
本发明提供一种催化裂化催化剂,以所述催化裂化催化剂的总重量为基 准,所述催化裂化催化剂含有1-60重量%的裂化活性组元、1-50重量%的高 比热容基质材料、1-70重量%的粘土和1-70重量%的粘结剂;所述高比热容 基质材料含有5-94.5重量%的氧化铝,以MnO2计5-94.5重量%氧化锰,以 及以P2O5计0.5-10重量%的磷氧化物,所述高比热容基质材料在温度为 1000k的比热容为1.3-2.0J/(g·K),所述裂化活性组元包括第一分子筛和任 选的第二分子筛,所述第一分子筛为Y型分子筛。
根据上述技术方案所述的催化裂化催化剂,其中,所述高比热容基质材 料的比表面积为300-500m2·g-1或330-400m2·g-1。
根据上述任一技术方案所述的催化裂化催化剂,其中,所述高比热容基 质材料的孔体积为0.5-1.5cm3/g。
根据上述任一技术方案所述的催化裂化催化剂,其中,所述高比热容基 质材料的平均孔直径为3-20nm或9-13nm。
根据上述任一技术方案所述的催化裂化催化剂,其中,所述高比热容基 质材料的XRD图谱,在2θ角为18±0.5°和2θ角为37±0.5°处峰的强度比为1: (3-10)。
本发明还提供了所述催化裂化催化剂的制备方法,该方法包括将所述裂 化活性组元、高比热容基质材料、粘土和粘结剂混合打浆,然后再进行喷雾 干燥,洗涤、过滤和干燥。
根据上述技术方案所述的催化裂化催化剂制备方法,其中,所述高比热 容基质材料可采用包括下述步骤的制备方法制得:
(5)使铝源与碱混合成胶,得到含铝胶体,所得含铝胶体的pH值为 7-11;
(6)使pH值为3-7的锰盐溶液与尿素混合,得到锰源溶液;
(7)使含铝胶体、锰源溶液和任选的氮化硼形成混合物,陈化;
(8)使陈化固体沉淀物与磷源接触,任选洗涤和/或干燥和/或焙烧。
根据上述任一技术方案所述的催化裂化催化剂制备方法,其中,所述使 铝源与碱混合成胶包括:将铝源溶液、碱的溶液混合,形成温度为室温至85℃、 pH值为7-11的胶体。
根据本发明,所述室温为15-40℃。
根据上述任一技术方案所述的催化裂化催化剂制备方法,其中,所述铝 源溶液中氧化铝的浓度优选为150-350gAl2O3/L。
根据上述任一技术方案所述的催化裂化催化剂制备方法,其中,碱的溶 液中碱的浓度优选为0.1-1mol/L。
根据上述任一技术方案所述的催化裂化催化剂制备方法,其中,所说的 铝源可选自硝酸铝、硫酸铝、磷酸铝和氯化铝等中的一种或多种;所述的碱 可以为溶于水的碳酸盐、溶于水的碳酸氢盐、溶于水的氢氧化物中的一种或 多种。
根据上述任一技术方案所述的催化裂化催化剂制备方法,其中,所述碱 的溶液优选为含有CO3 2-、HCO3 -或OH-中的一种或多种的碱性水溶液,所述 碱的溶液中CO3 2-的浓度为0-0.6mol/L,OH-的浓度为0-0.5mol/L,HCO3 -的 浓度为0-1mol/L。
根据上述任一技术方案所述的催化裂化催化剂制备方法,其中,步骤(2) 中,尿素与锰离子摩尔比优选为1-5例如为2-4。所述锰盐溶液中锰盐的浓 度以MnO2计可以为50-500g·L-1。
根据上述任一技术方案所述的催化裂化催化剂制备方法,其中,一种实 施方式,步骤(2)在所述锰盐溶液中加入尿素,然后在室温搅拌30-60分 钟,得到锰源溶液。
根据上述任一技术方案所述的催化裂化催化剂制备方法,其中,步骤(3) 中,所述陈化温度可以为室温至120℃,优选为60-100℃。优选的,在搅拌 下陈化。
根据上述任一技术方案所述的催化裂化催化剂制备方法,其中,所述陈 化的陈化时间优选为4-72小时,陈化时间优选为12-36h。
根据上述任一技术方案所述的催化裂化催化剂制备方法,其中,所述的 使陈化固体沉淀物与磷源接触,一种实施方式,其过程包括:将陈化固体沉 淀物与水按陈化固体沉淀物干基:水=1:(2-5)的重量比混合打浆,再将磷 源与所述浆液于室温至90℃下混合,然后搅拌或静置0.2-5小时。
根据上述任一技术方案所述的催化裂化催化剂制备方法,其中,所述的 锰盐可以选自硝酸锰、硫酸锰、磷酸锰或氯化锰等中的一种或多种,所述的 氮化硼可选自六方氮化硼(h-BN)、立方氮化硼(c-BN)、菱方氮化硼(r-BN) 和纤锌矿氮化硼(w-BN)中的至少一种,所述的磷源可选自磷酸铵、磷酸氢二 铵、磷酸二氢铵或磷酸中的一种或多种。
根据上述任一技术方案所述的催化裂化催化剂制备方法,其中,步骤(4) 中所述焙烧,一种实施方式,焙烧温度为500℃-900℃,焙烧时间为4-8小 时。
本发明还提供所述催化裂化催化剂在重油催化裂化中的应用。
本发明提供的催化裂化催化剂通过将裂化活性组元与特定的高比热容 材料、粘土和粘结剂配合使用,能够提高催化裂化催化剂的比热容,有利于 反应器中重油大分子的雾化和裂化,并具有较好的耐磨损性能。本发明提供 的催化裂化催化剂用于重油催化裂化,具有较好的重油转化能力、较高轻质 油收率;意外的是还具有较高的抗多种金属污染能力,在金属钒、Ni和铁污 染的情况下,可以具有较高的重油转化率,具有较高的轻质油收率,具有较 高的总液收,干气和焦炭选择性好。
本发明的其他特征和优点将在随后的具体实施方式部分予以详细说明。
具体实施方式
以下对本发明的具体实施方式进行详细说明。应当理解的是,此处所描 述的具体实施方式仅用于说明和解释本发明,并不用于限制本发明。
本发明提供了一种催化裂化催化剂,其中,以所述催化裂化催化剂的总 重量为基准,以干基计,所述催化裂化催化剂含有1-60重量%的裂化活性组 元、1-50重量%例如5-45重量%的高比热容基质材料、1-70重量%的粘土和 1-70重量%的粘结剂。所述高比热容基质材料含有5-94.5重量%的氧化铝, 以MnO2计5-94.5重量%氧化锰,以及以P2O5计0.5-10重量%的磷氧化物, 所述高比热容基质材料在温度为1000k时的比热容为1.3-2.0J/(g·K)。所述 的高比热容基质材料和裂化活性组元处于同一种颗粒中。
干基为物质800℃焙烧1小时后得到的不挥发固体产物。
根据本发明提供的催化裂化催化剂,优选地,以所述催化裂化催化剂的 总重量为基准,所述催化裂化催化剂含有10-50重量%的裂化活性组元、5-45 重量%或5-40重量%或10-45重量%的高比热容基质材料、10-60重量%的粘 土和10-60重量%的粘结剂,将上述各组分的含量控制在该优选的范围内能 够使得到的催化裂化催化剂具有更好的综合性能。
根据本发明提供的催化裂化催化剂,所述的高比热容基质材料,含有以 Al2O3计5-94.5重量%的氧化铝和以MnO2计5-94.5重量%锰氧化物、以干基 计0-40重量%的氮化硼和以P2O5计0.5-10重量%的磷氧化物,例如所述的 高比热容基质材料包括15-70重量%或20-65重量%或30-61重量%的锰氧化 物和29-84或35-80重量%或39-70重量%的氧化铝、5-35重量%的氮化硼和 1-8重量%的磷氧化物。
根据本发明提供的催化裂化催化剂,所述的高比热容基质材料,其比热 容为1.3-2.0J/(g·K)。所述高比热容基质材料(简称基质材料)中可以含或 不含氮化硼。
根据本发明提供的催化裂化催化剂,第一种具体实施方式,所述的高比 热容基质材料,含有以Al2O3计5-94.5重量%的氧化铝、以MnO2计5-94.5 重量%锰氧化物和以P2O5计0.5-10重量%的磷氧化物,不含氮化硼。例如所 述的高比热容基质材料包括15-70重量%或20-65重量%或25-60重量%的锰 氧化物、29-84重量%或35-80重量%或39-74重量%的氧化铝和0.8-8重量% 的磷氧化物。
根据本发明提供的催化裂化催化剂,第一种具体实施方式中,所述高比 热容基质材料的比表面积为250-400m2·g-1例如280-350m2·g-1。所述高比热 容基质材料的孔体积为0.5-1.0cm3/g例如0.55-0.8cm3/g。所述高比热容基质 材料的平均孔直径为3-12nm例如6-10nm。
根据本发明提供的催化裂化催化剂,第二种具体实施方式,所述的高比 热容基质材料含有氮化硼,其比热容为1.3-2.0J/(g·K),例如为1.4-1.96J/ (g·K)或1.51-1.96J/(g·K)。所述高比热容基质材料以重量比计的无水化 学表达式可表示为(5-94)Al2O3·(5-94)MnO2·(0.5-40)BN·(0.5-10)P2O5, 例如可以为(20-80)Al2O3·(15-75)MnO2·(5-30)BN·(1-8)P2O5。优选 情况下,以所述高比热容基质材料的重量为基准,所述高比热容基质材料含 有5-94重量%的氧化铝,5-94重量%的氧化锰、0.5-10重量%的磷氧化物和 以干基计大于0且不超过40重量%例如0.5-35重量%的氮化硼。例如所述高 比热容基质材料含有15-80重量%氧化铝、15-70重量%氧化锰、0.8-9重量% 磷氧化物和5-30重量%的氮化硼;进一步,所述高比热容基质材料含有19-74 重量%的氧化铝、0.8-8重量%的磷氧化物、15-60重量%的氧化锰和8-26重 量%的氮化硼。所述的基质材料含有氮化硼,可以大大提高催化剂的耐磨损 性能。
根据本发明提供的催化裂化催化剂,第二种具体实施方式,所述高比热 容基质材料的比表面积为300-500m2·g-1例如320-450m2·g-1或330-400m2·g-1, 所述高比热容基质材料的孔体积为0.5-1.5cm3·g-1例如0.8-1.3cm3·g-1或 0.9-1.25cm3·g-1,所述高比热容基质材料的平均孔直径为3-20nm例如为 5-18nm或7-15nm或9-13nm或11-13nm。
根据本发明提供的催化裂化催化剂,所述的高比热容基质材料的制备方 法,一种具体实施方式,包括下述步骤:
(1)铝源溶液与碱溶液在室温至85℃下混合成胶,控制成胶形成的 胶体的pH值为7-11;
(2)配置pH值为3-7的锰盐溶液,将锰盐溶液与尿素混合,搅拌; 尿素与锰离子摩尔比为1-5;该锰盐溶液与尿素混合的温度没有特殊要求, 例如在室温下进行所述混合,搅拌的时间例如30-60分钟;
(3)步骤(1)得到的产物、步骤(2)得到的产物和任选的氮化硼 混合,在室温至120℃下陈化4-72小时;和
(4)步骤(3)得到的陈化产物过滤,任选进行第一洗涤,得到陈 化固体沉淀物,陈化固体沉淀物与含磷源接触,任选进行第二洗涤,然后干 燥、焙烧得到高比热容基质材料。
所述的高比热容基质材料制备方法的具体实施方式中,步骤(1)中所 述碱溶液的可选范围较宽,优选的,步骤(1)中所述碱溶液为含有CO3 2-、 HCO3 2-和OH-的至少一种的碱性水溶液,更优选地,所述的碱性水溶液为包 括碳酸氢铵、碳酸铵、氢氧化钠、氢氧化钾中的一种或多种的水溶液,或者 为碳酸铵、氢氧化钠、氢氧化钾中的一种或多种的组合与氨水的混合溶液。 于一种实施方式,所述的碱溶液中,CO3 2-的浓度为0-0.6mol/L,例如为 0.3-0.5mol/L;OH-的浓度为0-0.5mol/L,例如为0.2-0.35mol/L,HCO3 2-的浓 度为0-1.0mol/L例如为0.4-1.0mol/L。优选的,所述碱溶液中碱的总浓度为 0.1-1mol/L。步骤(1)成胶得到的胶体pH值优选为7.5-11例如8.5-11或9-10。 在选用氨水时,假设氨水全部电离,根据计算得到的氢氧根计算氨水需要的 加入量。
所述的高比热容基质材料制备方法的具体实施方式,所述铝源的种类的 可选范围较宽,能够溶于水的水溶性铝源均可用于本发明,例如所述铝盐选 自硝酸铝、硫酸铝、磷酸铝和氯化铝中的一种或多种优选硝酸铝、硫酸铝和 氯化铝等中的一种或多种。
所述的高比热容基质材料制备方法的具体实施方式,步骤(2)中使特 定pH值的锰盐溶液与尿素混合形成混合物,所述锰盐溶液的pH值为3-7 优选为5-7。使尿素与锰盐溶液混合的条件的可选范围较宽,针对本发明, 一种实施方式,步骤(2)中所述混合的方法包括:在锰盐溶液中加入尿素, 于室温搅拌40-60分钟,尿素和锰离子摩尔比优选为2-4之间。步骤(2)中 所述锰盐溶液可选自水溶性锰盐的水溶液和/或锰氧化物、锰氢氧化物与酸接触后形成的盐溶液。所述锰盐的种类的可选范围较宽,能够溶于水的水溶性 锰盐均可用于本发明,所述锰盐例如硝酸锰、硫酸锰、磷酸锰或氯化锰等中 的一种或多种,优选为硝酸锰、硫酸锰或氯化锰等中的一种或多种。锰盐溶 液也可由锰氧化物和/或锰氢氧化物与酸接触而制得,所述锰氧化物例如一氧 化锰、四氧化三锰、三氧化二锰、二氧化锰中的一种或多种,所述酸例如盐 酸、硫酸、磷酸、硝酸中的一种或多种,优选为盐酸、硫酸、硝酸中的一种 或多种。
所述的高比热容基质材料制备方法的具体实施方式,步骤(3)中所述 步骤(1)得到的产物以Al2O3计、步骤(2)得到的产物以MnO2计和氮化 硼以干基计的重量用量比例为(5-95)Al2O3:(5-95)MnO2:(0-40)BN例 如为(20-80)Al2O3:(15-75)MnO2:(5-30)BN或(20-70)Al2O3:(15-60) MnO2:(8-25)BN。
所述的高比热容基质材料制备方法的具体实施方式,步骤(3)中所述 陈化条件的可选范围较宽,优选的,步骤(3)中所述陈化条件包括:陈化 温度为60-100℃,陈化时间12-36h,搅拌下陈化。对于搅拌的方式没有特殊 要求,例如,搅拌速度可以为50-300转/min。
所述的高比热容基质材料制备方法的具体实施方式,所述氮化硼选自六 方氮化硼(h-BN)、立方氮化硼(c-BN)、菱方氮化硼(r-BN)和纤锌矿氮化 硼(w-BN)中的一种或多种。
所述的高比热容基质材料制备方法的具体实施方式,步骤(4)中,步 骤(3)得到的陈化产物过滤,任选进行第一洗涤,得到陈化固体沉淀物, 然后使陈化固体沉淀物与磷源接触,任选进行第二洗涤。其中所说的磷源以 P2O5计、其投料量与高比热容基质材料的干基的重量比为(0.005~0.1):1。 优选的,步骤(3)中所述步骤(1)得到的产物、步骤(2)得到的产物、 氮化硼和磷源的用量使制备得到的基质材料中含有5-94重量%例如15-80重 量%或19-74重量%或20-80重量%的氧化铝,以MnO2计5-94重量%例如 15-75重量%或15-70重量%或14-66重量%的氧化锰、以干基计大于0且不 超过40重量%例如0.5-35重量%或5-30重量%或8-26重量%的氮化硼和以 P2O5计0.5-10重量%的磷氧化物。所述第一洗涤或第二洗涤可以用水洗涤, 优选的,所述洗涤使洗涤后的洗涤液为中性(中性是指pH值为6.5-7.5)例 如用去离子水冲洗至洗涤后的去离子水为中性。优选的,所述的第一洗涤和第二洗涤至少进行一次,优选的,至少进行第一洗涤。
所述的高比热容基质材料制备方法的具体实施方式,步骤(4)中,将 陈化固体沉淀物与磷源接触处理,优选的过程包括将所得固体沉淀物按沉淀 物(干基):H2O=1:(2~5)的重量比与水混合打浆,再将磷源加入上述浆 液中,在室温至90℃下接触处理(例如搅拌)0.2~5小时,优选0.5~3小 时,任选过滤、任选进行第二洗涤;可选的方法也可以是将所得陈化固体沉 淀物直接与磷源按比例混合,研磨均匀。其中以P2O5计的磷源与以干基计的陈化固体沉淀物的重量比可以是0.005~0.1:0.9~0.995。
所述的高比热容基质材料制备方法的具体实施方式,所述磷源包括含磷 化合物,所述含磷化合物可以是磷酸铵、磷酸氢二铵、磷酸二氢铵或磷酸中 的一种或多种。
所述的高比热容基质材料制备方法的具体实施方式,步骤(4)中所述 干燥条件和焙烧条件的可选范围较宽。所述干燥、焙烧的方法均可参照现有 技术进行,本发明对此无特殊要求。例如,步骤(4)中所述干燥条件包括: 在100-150℃下干燥6-24h;步骤(4)中所述焙烧条件包括:在550-800℃例 如550-750℃下焙烧4-8h。
根据本发明提供的催化裂化催化剂,所述裂化活性组元含有第一分子筛, 所述第一分子筛为Y型分子筛。其中,所述Y型分子筛的种类可以为本领 域的常规选择,例如,可以为含稀土的Y型分子筛(如REHY分子筛)、含 磷和稀土的Y型分子筛(如DOSY分子筛)、超稳Y分子筛(如DASY分 子筛)、含磷和/或稀土的超稳Y分子筛等中的一种或多种。例如,所述的Y型分子筛为REY分子筛、REHY分子筛、DASY分子筛、RE-DASY分子筛、 USY分子筛、RE-USY分子筛、PSRY分子筛、HSY分子筛、SOY分子筛 中的一种或多种此外,任选地,所述裂化活性组元还可含有第二分子筛,所 述第二分子筛为除Y分子筛以外的其它八面沸石、Beta沸石、MFI结构分 子筛(如ZRP-1分子筛)和丝光沸石中的一种或多种。其中,以所述裂化活 性组元的总重量为基准,所述Y型分子筛的含量可以为75重量%以上,优 选为90重量%以上,更优选为95重量%以上;所述第二分子筛的含量可以 为25重量%以下,优选为10重量%以下,更优选为5重量%以下。
根据本发明提供的催化裂化催化剂,所述粘土可以为现有的各种能够用 于催化裂化催化剂中的粘土,例如,可以选自高岭土、多水高岭土、蒙脱土、 硅藻土、埃洛石、皂石、累托土、海泡石、凹凸棒石、水滑石和膨润土中的 一种或几种。
根据本发明提供的催化裂化催化剂,所述粘结剂可以为现有的各种能够 用于催化裂化催化剂中的粘结剂,例如,可以选自硅溶胶、铝溶胶和拟薄水 铝石中的一种或几种。
本发明提供的催化裂化催化剂中,还可以含有外加稀土。所述外加稀土 可以是在制备所述催化裂化催化剂的过程中通过额外加入氯化稀土而形成 的。在所述催化裂化催化剂中,所述外加稀土通常以稀土氧化物(RE2O3) 的形式存在。以所述催化裂化催化剂的干基重量为基准,以稀土氧化物计的 所述外加稀土的含量可以为0-3重量%,优选为0.5-2重量%。其中,所述外 加稀土中的稀土元素是指催化裂化催化剂领域中涉及的各种常规的稀土元 素,例如可以为镧、铈、镨、钕、钷、钐、铕中的一种或多种。
本发明提供的催化裂化催化剂的制备方法包括将所述裂化活性组元、高 比热容基质材料、粘土和粘结剂混合打浆,然后再依次进行喷雾干燥、洗涤、 过滤和干燥。此外,当所述催化裂化催化剂还含有外加稀土时,本发明提供 的催化裂化催化剂的制备方法还包括将所述氯化稀土与所述裂化活性组元、 中孔活性硅磷铝材料、粘土和粘结剂一起混合打浆,然后再依次进行喷雾干 燥、洗涤、过滤和干燥。
根据本发明提供的催化裂化催化剂的制备方法,将所述裂化活性组元、 高比热容基质材料、粘土和粘结剂以及任选的氯化稀土混合打浆,以及后续 的喷雾干燥、洗涤、过滤和干燥,这些工序的实施方法均可采用常规的方法 实施,它们的具体实施方法例如在CN1916166A、CN1362472A、CN1132898C、 CN1727442A、CN1098130A和CN1727445A中都有详尽的描述,这里一并 引入本发明中以作参考。此外,一般地,在所述喷雾干燥之后、洗涤之前,所述催化裂化催化剂的制备方法通常还包括将喷雾干燥产物进行焙烧的步 骤。所述焙烧的条件通常包括焙烧温度可以为500-700℃,焙烧时间可以为 1-4小时。
此外,本发明还提供了所述催化裂化催化剂在重油催化裂化中的应用。
本发明提供的所述催化裂化催化剂在重油催化裂化中的应用方法,包括 将所述催化裂化催化剂与重油接触反应的步骤,所述的重油例如减压渣油、 减压瓦斯油、常压渣油、常压瓦斯油、脱沥青油中的一种或多种。所述接触 反应的反应条件,包括:反应温度为480-530℃例如490-520℃,剂油比(重 量比)为3-10例如4-8,反应时间为0.5-15秒优选1-5秒。
以下将通过实施例对本发明进行详细描述。
以下制备例、对比制备例、实施例和对比例中使用的原料如下:
盐酸由北京化工厂生产,化学纯,浓度为36重量%;
钠水玻璃为市售,SiO2浓度为26.0重量%,模数为3.2;
高岭土为苏州高岭土公司产品,固含量为74.0重量%;
拟薄水铝石为山东铝厂工业产品,固含量为62.0重量%;
铝溶胶为中国石化催化剂齐鲁分公司产品,Al2O3含量为21.5重量%;
DASY分子筛(固含量为92.0重量%,RE2O3含量为1.8重量%,Na2O 含量为1.0重量%,结晶度60%)、ZRP-1分子筛(固含量为97.8重量%, Na2O含量为1.1重量%,结晶度70%)、REHY分子筛(固含量为88.0重量%, RE2O3含量为5.0重量%,Na2O含量为0.9重量%,结晶度65%)、Beta分子 筛(固含量为95.2重量%,Na2O含量为1.2重量%,结晶度60%),DOSY 分子筛(固含量为93.5重量%,RE2O3含量为8.0重量%,Na2O为0.8重量%, 结晶度80%)、HSY分子筛(固含量91.5重量%,RE2O3含量为10.5重量%, Na2O为0.9重量%,结晶度85%)、HRY分子筛(固含量91重量%,RE2O3含量为6.5重量%,Na2O含量为1.1重量%,结晶度70%)均由中国石化催 化剂齐鲁分公司生产;
氯化稀土购自包钢稀土高科技股份有限公司,其中的稀土元素为La和 Ce。
下面通过实施例对本发明予以进一步说明,但并不因此而限制本发明。
本发明中,剂油比指的是催化剂与原料油的质量比。
本发明中,如未特别说明,ppm为以重量计的ppm。
所用BN,为六方氮化硼。
在各实施例和对比例中,样品中Al2O3、MnO2、B、N、Fe的含量用X 射线荧光法测定(参见《石油化工分析方法(RIPP实验方法)》,杨翠定等 编,科学出版社,1990年出版)。样品物相采用X射线衍射法测定。样品比 表面积、孔体积、平均孔径由低温氮吸附-脱附法测定、BJH法计算得到孔 径分布。
制备例1
本实例说明本发明提供的高比热容基质材料的制备过程。
将浓度350gAl2O3/L的Al2(SO4)3溶液与CO3 2-浓度为0.10mol/L的碳酸 铵溶液在20℃下混合成胶,所得胶体pH值=7.5,得到浆液A。向浓度 145gMnO2/L的MnCl2溶液中加入盐酸(浓度36重量%),控制pH值=3.5, 然后向溶液中加入尿素,尿素与锰离子摩尔比为2,室温下搅拌30分钟,得 到溶液B。将溶液B加入到浆液A中,80℃下搅拌陈化24h,待体系温度降至室温,过滤,用去离子水冲洗,至冲洗后的水为中性,得到陈化固体沉淀 物,然后按陈化固体沉淀物(干基):H2O=1:2的重量比将所得陈化固体 沉淀物与水混合打浆,并按P2O5:高比热容基质材料干基=0.01:1的重量 比加入磷酸,再于50℃下搅拌2小时,然后于120℃下干燥12h得基质材料 前驱体,然后于550℃下焙烧6h,随炉冷却至室温得到本发明提供的高比热 容基质材料,记为AM-1。AM-1的配方、制备参数、比热容、比表面积、 孔容及平均孔径列于表1中。
AM-1的X射线衍射谱图中2θ角为18±0.5°、37±0.5°、48±0.5°、59±0.5°、 66±0.5°处具有衍射峰,其中2θ角为18±0.5°和2θ角为37±0.5°处特征峰的强 度比为1:4.1;其元素分析重量化学组成为28.9%MnO2、70.2%Al2O3、 0.9%P2O5;比热容1.33J/(g·K),比表面积308m2/g,孔容0.59cm3/g,平均 孔径7.7nm。
制备例2-4
实施例2-4用于说明本发明提供的高比热容基质材料的制备。
按照实施例1的方法制备高比热容基质材料AM-2至AM-4,不同的是 原料配比、制备条件参数,其中将溶液B和氮化硼加入到浆液A中,然后 进行所述陈化。原料配比、制备条件参数、产品的元素组成、比热容、比表 面积、孔容及平均孔径列于表1中。
制备例5
在25℃室温下,将浓度350gAl2O3/L的Al(NO3)3溶液与CO3 2-浓度为 0.1mol/L碳酸铵、OH-浓度为0.15mol/L的氨水的溶液混合,搅拌1小时,控 制pH为10.5,得到浆液A。将Mn3O4与盐酸、水混合,得到浓度87.5gMnO2/L 的氯化锰溶液,控制pH为6,然后向溶液中加入尿素,尿素与锰离子摩尔 浓度比为3,室温下搅拌40分钟,得到溶液B。将溶液B、145.6gBN(固含 量80重量%)加入浆液A中,60℃、搅拌下陈化24h,待体系温度降至室 温,用去离子水冲洗,至冲洗后的水为中性,过滤,将所得陈化固体沉淀物 按陈化固体沉淀物(干基):H2O=1:4的重量比与水混合打浆,并按P2O5: 高比热容材料干基=0.05:1的重量比加入磷酸铵,再于50℃下反应2小时, 然后于120℃下干燥12h得基质材料前驱体,然后于650℃下焙烧4h,随炉 冷却至室温得到本发明提供的基质材料,记为AM-5。AM-5的配方、制备 参数、比热容、比表面积、孔容及平均孔径列于表1中。
AM-5的元素分析化学组成以重量百分比计为15.6%MnO2、59.4%Al2O3、 19.5%BN、5.5%P2O5;比热容1.45J/(g·K),比表面积380m2/g,孔容1.12cm3/g, 平均孔径11.8nm。
制备例6
制备例6用于说明本发明提供的高比热容介孔基质材料的制备过程。
按照制备例5的方法制备基质材料AM-6,不同的是配方、制备参数、 元素组成、比表面积、比表面积、孔容及平均孔径列于表1中。碱溶液中 CO3 2-浓度为0.15mol/L和OH-浓度为0.25mol/L。
AM-2至AM-6的XRD谱图于AM-1的类似,中2θ角为18±0.5°、37±0.5°、 48±0.5°、59±0.5°、66±0.5°处具有衍射峰。
对比制备例1
使用去离子水分别配制浓度为350gAl2O3/L的Al(NO3)3溶液和浓度为 145gMnO2/L的硝酸锰溶液,混合均匀,得到溶液A。配制碳酸氢铵溶液, 控制pH=10.0,记为溶液B。连续搅拌下将溶液A和溶液B混合,得到母液 C,混合过程中通过控制溶液B的加入量控制母液C的PH为8-9。混合完 毕后180℃下陈化20h,待体系温度降至室温,用去离子水冲洗至中性,得 到陈化固体沉淀物,然后按陈化固体沉淀物(干基):H2O=1:3的重量比 将所得陈化固体沉淀物与水混合打浆,并按P2O5:所得到的基质材料干基= 0.01:1的重量比加入磷酸,再于50℃下搅拌2小时,然后于120℃下干燥 12h得锰铝基质前驱体,然后于1000℃下焙烧4h,随炉冷却至室温得到基质 材料,记为DAM-1。
DAM-1的X射线衍射谱图,其中2θ角为18±0.5°和2θ角为37±0.5° 处具有特征峰,二者的强度比为1:1.5;DAM-1的元素分析化学组成为30.2 重量%MnO2、68.9重量%Al2O3、0.9%P2O5;比热容0.58J/(g·K),比表面积 284m2/g,孔容0.41cm3/g,平均孔径5.8nm。
对比制备例2
将浓度350gAl2O3/L的Al2(SO4)3溶液与碳酸铵混合成胶,控制PH=10.0, 得到浆液A。将浓度209.7gMnO2/L的MnSO4溶液加入浆液A,室温下搅拌 30分钟,得到浆液B。将溶液B、95.4g氮化硼(固含量80重量%)加入浆 液A中,80℃下陈化24h,待体系温度降至室温,分别用去离子水冲洗至中 性,得到陈化固体沉淀物,然后按陈化固体沉淀物(干基):H2O=1:4的 重量比将所得陈化固体沉淀物与水混合打浆,并按P2O5:所得到的基质材料 干基=0.03:1的重量比加入磷酸,再于50℃下搅拌2小时,于120℃下干 燥12h得锰铝基质前驱体,然后于900℃下焙烧6h,随炉冷却至室温得到基 质材料,记为DAM-2。
DAM-2的元素分析化学组成为33.3重量%MnO2、54.7重量%Al2O3、 9.1重量%BN和2.9重量%P2O5;比热容0.89J/(g·K),比表面积249m2/g, 孔容0.35cm3/g,平均孔径5.6nm。
表1
表1的I1/I2中,I1为XRD谱图中2θ角为18±0.5°峰的强度,I2为2θ角为37±0.5°峰的强度。
实施例1
该实施例用于说明本发明提供的催化裂化催化剂及其制备方法。
将以干基计的25重量份的拟薄水铝石与去离子水混合打浆(浆液固含 量为15重量%),并向得到的浆液中加入盐酸胶溶,酸铝比(重量)为0.20: 1,然后将温度升至65℃酸化1小时,接着分别加入以干基计的30重量份高 岭土的浆液(固含量为25重量%)、以干基计的6重量份的铝溶胶以及以干 基计的12重量份的由制备例1制备的高比热容基质材料AM-1的浆液(固 含量为18重量%),搅拌20分钟,之后再向其中加入以干基计的27重量份的所述HRY分子筛浆液(固含量为35重量%),继续搅拌后喷雾干燥制成 微球催化剂。然后将该微球催化剂在500℃下焙烧1小时,再在60℃下用 (NH4)2SO4液洗涤(其中,(NH4)2SO4:微球催化剂:H2O=0.05:1:10)至 Na2O含量小于0.25重量%,接着用去离子水淋洗并过滤,之后再于110℃下 烘干,得到催化裂化催化剂C1,其中,以所述催化裂化催化剂C1的总重量为基准,所述催化裂化催化剂C1中含有12重量%的高比热容基质材料、27 重量%的HRY分子筛、30重量%的高岭土、31重量%的Al2O3粘结剂。
对比例1
该对比例用于说明参比的催化裂化催化剂及其制备方法。
按照实施例1的方法制备催化裂化催化剂,不同的是,将由制备例1制 备的高比热容基质材料AM-1用相同重量份的由对比制备例1制备的基质材 料DAM-1代替,得到参比催化裂化催化剂CB1,其中,以所述参比催化裂 化催化剂CB1的总重量为基准,所述参比催化裂化催化剂CB1中含有12重 量%的对比基质材料、27重量%的HRY分子筛、30重量%的高岭土、31重 量%的Al2O3粘结剂。
对比例2
该对比例用于说明参比的催化裂化催化剂及其制备方法。
按照实施例1的方法制备催化裂化催化剂,不同的是,将由制备例1制 备的高比热容基质材料AM-1用相同重量份的由对比制备例1制备的基质材 料DAM-2代替,得到参比催化裂化催化剂CB2,其中,以所述参比催化裂 化催化剂CB2的总重量为基准,所述参比催化裂化催化剂CB2中含有12重 量%的对比基质材料、27重量%的HRY分子筛、30重量%的高岭土、31重 量%的Al2O3粘结剂。
对比例3
该对比例用于说明参比的催化裂化催化剂及其制备方法。
按照实施例1的方法制备催化裂化催化剂,不同的是,不加入高比热容 基质材料AM-1,而将高比热容基质材料AM-1用相同干基重量的高岭土替 代,得到参比催化裂化催化剂CB3,其中,以所述参比催化裂化催化剂CB3 的总重量为基准,所述参比催化裂化催化剂CB3中含有27重量%的HRY分 子筛、42重量%的高岭土、31重量%的Al2O3粘结剂。
实施例2
该实施例用于说明本发明提供的催化裂化催化剂及其制备方法。
将以干基计的27重量份高岭土与去离子水混合打浆(浆液固含量为40 重量%),再加入以干基计的20重量份的拟薄水铝石,并向得到的浆液中加 入盐酸胶溶,酸铝比(重量)为0.20:1,然后将温度升至65℃酸化1小时, 接着分别加入以干基计的8重量份的铝溶胶、以干基计的20重量份的由制 备例2制备的高比热容基质材料AM-2的浆液(固含量为20重量%),搅拌 20分钟,之后再向其中加入以干基计的20重量份的所述HSY分子筛、以干 基计的5重量份的所述ZRP-1分子筛的混合浆液(固含量为35重量%),继 续搅拌30min,喷雾干燥制成微球催化剂。然后将该微球催化剂在500℃下 焙烧1小时,再在60℃下用(NH4)2SO4溶液洗涤(其中,(NH4)2SO4:微球催 化剂:H2O=0.05:1:10)至Na2O含量小于0.25重量%,接着用去离子水 淋洗并过滤,之后再于110℃下烘干,得到催化裂化催化剂C2,其中,以所 述催化裂化催化剂C2的总重量为基准,所述催化裂化催化剂C2中含有20 重量%的高比热容基质材料、20重量%的HSY分子筛、5重量%的ZRP-1分 子筛、27重量%的高岭土、28重量%的Al2O3粘结剂。
实施例3
该实施例用于说明本发明提供的催化裂化催化剂及其制备方法。
将以干基计的28重量份高岭土与去离子水混合打浆,再加入以干基计 的15重量份的拟薄水铝石,并向得到的浆液中加入盐酸进行胶溶,酸铝比 (重量)为0.20:1,然后将温度升至65℃酸化1小时,接着分别加入以干 基计的10重量份的由制备例3制备的高比热容基质材料AM-3的浆液(固 含量为25重量%)和以干基计5重量份的铝溶胶,搅拌20分钟,之后再向 其中加入以干基计的15重量份的所述DASY分子筛与以干基计的5重量份 的所述Beta分子筛的混合浆液(固含量为35重量%)以及以稀土氧化物计 的2重量份的氯化稀土溶液,继续搅拌后喷雾干燥制成微球催化剂。然后将 该微球催化剂在500℃下焙烧1小时,再在60℃下用(NH4)2SO4溶液洗涤(其 中,(NH4)2SO4:微球催化剂:H2O=0.05:1:10)至Na2O含量小于0.25重 量%,接着用去离子水淋洗并过滤,之后再于110℃下烘干,得到催化裂化催化剂C3,其中,以所述催化裂化催化剂C3的总重量为基准,所述催化裂 化催化剂C3中含有10重量%的高比热容基质材料、15重量%的DASY分 子筛、5重量%的Beta分子筛、28重量%的高岭土、20重量%的Al2O3粘结 剂、2重量%的氧化稀土。
实施例4
该实施例用于说明本发明提供的催化裂化催化剂及其制备方法。
将以干基计的39重量份的高岭土与以干基计的18重量份的铝溶胶以及 以干基计的15重量份的由制备例4制备的高比热容基质材料AM-4的浆液 (固含量为20重量%)混合打浆,搅拌120分钟,之后再向其中加入以干 基计的28重量份的所述DOSY分子筛浆液(固含量为35重量%),继续搅 拌后喷雾干燥制成微球催化剂。然后将该微球催化剂在500℃下焙烧1小时, 再在60℃下用(NH4)2SO4溶液洗涤(其中,(NH4)2SO4:微球催化剂:H2O=0.05: 1:10)至Na2O含量小于0.25重量%,接着用去离子水淋洗并过滤,之后再 于110℃下烘干,得到催化裂化催化剂C4,其中,以所述催化裂化催化剂 C4的总重量为基准,所述催化裂化催化剂C4中含有15重量%的高比热容 基质材料、28重量%的DOSY分子筛、39重量%的高岭土、18重量%的Al2O3粘结剂。
实施例5
该实施例用于说明本发明提供的催化裂化催化剂及其制备方法。
(1)制备硅溶胶:
将1.7L盐酸用8.0kg脱阳离子水进行稀释,将7.7kg钠水玻璃用8.0kg 脱阳离子水进行稀释,搅拌下将稀释过的钠水玻璃缓慢加入上述盐酸稀溶液 中,得到SiO2浓度为7.8重量%、pH值为2.8的硅溶胶。
(2)制备催化裂化催化剂:
在以干基计的15重量份的上述硅溶胶中加入以干基计的20重量份的高 岭土,搅拌1h后加入以干基计的40重量份的由制备例5制备的高比热容基 质材料AM-5的浆液(固含量为18重量%)混合打浆,之后再向其中加入以 干基计的25重量份的所述DASY分子筛浆液(固含量为30重量%),继续 搅拌后喷雾干燥制成微球催化剂。然后将该微球催化剂在60℃下用 (NH4)2SO4溶液洗涤(其中,(NH4)2SO4:微球催化剂:H2O=0.05:1:10) 至Na2O含量小于0.25重量%,接着用去离子水淋洗并过滤,之后再于110℃ 下烘干,得到催化裂化催化剂C5,其中,以所述催化裂化催化剂C5的总重 量为基准,所述催化裂化催化剂C5中含有40重量%的高比热容基质材料、 25重量%的DASY分子筛、20重量%的高岭土、15重量%的SiO2粘结剂。
实施例6
该实施例用于说明本发明提供的催化裂化催化剂及其制备方法。
将以干基计的10重量份的高岭土与以干基计的17重量份的铝溶胶以及 以干基计的45重量份的由制备例6制备的高比热容基质材料AM-6的浆液 (固含量为20重量%)混合打浆,搅拌120分钟,之后再向其中加入以干 基计的28重量份的所述HSY分子筛浆液(固含量为35重量%),继续搅拌 后喷雾干燥制成微球催化剂。然后将该微球催化剂在500℃下焙烧1小时, 再在60℃下用(NH4)2SO4溶液洗涤(其中,(NH4)2SO4:微球催化剂:H2O=0.05: 1:10)至Na2O含量小于0.25重量%,接着用去离子水淋洗并过滤,之后再 于110℃下烘干,得到催化裂化催化剂C6,其中,以所述催化裂化催化剂 C6的总重量为基准,所述催化裂化催化剂C6中含有45重量%的高比热容 基质材料、28重量%的HSY分子筛、10重量%的高岭土、17重量%的Al2O3粘结剂。
实施例7-12
实施例10-18用于说明本发明提供的催化裂化催化剂性能的测试。
将上述制备的催化裂化催化剂C1-C9分别采用Mitchell方法浸渍污染铁4000ppm、镍4000ppm、钒4000ppm,即以环烷酸钒为钒源、环烷酸镍为镍 源、环烷酸铁为铁源,甲苯为溶剂,制备含金属溶液,催化剂在含金属溶液 中浸渍,然后烘干,再在约600℃下焙烧除去有机质。在800℃、100%水蒸 气条件下老化处理6小时,在小型固定流化床上进行裂化性能评价,每个样 品的评价过程进行了五次反应-再生循环,即同一个催化剂不卸出的情况下 连续进行五次原料油反应和再生过程,取最后一次反应的结果作为催化剂裂 化性能评价结果。重油微反的评价条件为:剂油比5(重量比),样品装量 9g,反应温度520℃,WHSV为8h-1,进油时间70秒,再生温度720℃,原 料油为减压瓦斯油。原料油性质如表2所示。评价结果列于表3中。
对比例4-6
将上述制备的催化裂化参比剂CB1-CB3按照实施例7-12相同的方法进 行性能测试,评价结果列于表3中。
表2
表3
w%指重量%
本发明中,转化率=汽油收率+液化气收率+干气收率+焦炭收率,
总液收(又称总液体产品收率)=汽油收率+柴油收率+液化气收率,
焦炭选择性=焦炭收率/转化率、干气选择性=干气收率/转化率。
由表3的结果可见,与沸石含量相同但不含高比热容基质材料的催化剂 相比,本发明提供的催化剂磨损指数更低,本发明提供的催化剂具有优异的 抗金属污染能力,在金属污染的情况下,重油转化能力极大提高,产品分布 明显改善,尤其能够明显改善干气、焦炭的选择性。与各组分含量相同但采 用的基质材料不同于本发明的基质材料的催化剂相比,本发明提供的催化剂 磨损指数下降,干气选择性明显降低、焦炭产率降低,总液收明显提高,轻 质油收率(汽油和液化气收率)明显提高。可见,本发明提供的催化裂化催 化剂具有优异的抗金属污染性能。
Claims (24)
1.一种耐磨损催化裂化催化剂,以所述催化裂化催化剂的总重量为基准,所述催化裂化催化剂含有1-60重量%的包括第一分子筛和任选的第二分子筛的裂化活性组元、1-50重量%的高比热容基质材料、1-70重量%的粘土和1-70重量%的粘结剂;所述第一分子筛为Y型分子筛;所述高比热容基质材料含有5-94.5重量%的氧化铝,以MnO2计5-94.5重量%氧化锰,以及以P2O5计0.5-10重量%的磷氧化物,所述高比热容基质材料在温度为1000k时的比热容为1.3-2.0J/(g·K)。
2.按照权利要求1所述的催化裂化催化剂,其中,以所述催化裂化催化剂的总重量为基准,所述催化裂化催化剂含有5-45重量%的高比热容基质材料、10-50重量%的裂化活性组元、10-60重量%的粘土和10-60重量%的粘结剂。
3.按照权利要求1所述的催化裂化催化剂,其中,所述高比热容基质材料含有以干基计0-40重量%或4-26重量%的氮化硼。
4.按照权利要求1所述的催化裂化催化剂,其中,所述高比热容基质材料的比表面积为300-500m2·g-1或330-400m2·g-1。
5.按照权利要求1所述的催化裂化催化剂,其中,所述高比热容基质材料的孔体积为0.5-1.5cm3/g;所述高比热容基质材料的平均孔直径为3-20nm或9-13nm。
6.按照权利要求1所述的催化裂化催化剂,其中,所述高比热容基质材料的XRD图谱,在2θ角为18±0.5°和2θ角为37±0.5°处峰的强度比为1:(3-10)。
7.按照权利要求1-6中任意一项所述的催化裂化催化剂,其中,所述的Y型分子筛为REY分子筛、REHY分子筛、DASY分子筛、USY分子筛、RE-DASY分子筛、RE-USY分子筛、PSRY分子筛、HSY分子筛、SOY分子筛中的一种或多种。
8.按照权利要求19所述的催化裂化催化剂,其中,所述第二分子筛为Y沸石以外的其它八面沸石、Beta沸石、MFI结构分子筛和丝光沸石中的一种或多种。
9.按照权利要求20所述的催化裂化催化剂,其中,以所述裂化活性组元的总重量为基准,所述Y型分子筛的含量为75重量%以上,所述第二分子筛含量为25重量%以下。
10.权利要求1-9任意一项所述的催化裂化催化剂的制备方法,该方法包括将所述裂化活性组元、高比热容基质材料、粘土和粘结剂混合打浆,喷雾干燥,洗涤,过滤和干燥。
11.按照权利要求10所述的催化裂化催化剂制备方法,其中,所述高比热容基质材料的制备方法,包括下述步骤:
(1)使铝源与碱混合成胶,得到含铝胶体,所得含铝胶体的pH值为7-11;
(2)使pH值为3-7的锰盐溶液与尿素混合,得到锰源溶液;
(3)使含铝胶体、锰源溶液和任选的氮化硼形成混合物,陈化;
(4)使陈化固体沉淀物与磷源接触,任选洗涤和/或干燥和/或焙烧。
12.按照权利要求11所述的催化裂化催化剂制备方法,其中,所述使铝源与碱混合成胶包括:将铝源溶液、碱的溶液混合,形成温度为室温至85℃、pH值为7-11的胶体。
13.按照权利要求11所述的催化裂化催化剂制备方法,其中,所述铝源溶液中氧化铝的浓度为150-350gAl2O3/L,碱的溶液中碱的浓度为0.1-1mol/L。
14.按照权利要求11所述的催化裂化催化剂制备方法,其中,所说的铝源选自硝酸铝、硫酸铝、磷酸铝和氯化铝等中的一种或多种;所述的碱为溶于水的碳酸盐、溶于水的碳酸氢盐、溶于水的氢氧化物中的一种或多种。
15.按照权利要求11所述的催化裂化催化剂制备方法,其中,所述碱的溶液选自含有CO3 2-、HCO3 -或OH-中的一种或多种的碱性水溶液,所述碱的溶液中CO3 2-的浓度为0-0.6mol/L,OH-的浓度为0-0.5mol/L,HCO3 -的浓度为0-1mol/L。
16.按照权利要求11所述的催化裂化催化剂制备方法,其中,步骤(2)中,尿素与锰离子摩尔比为1-5例如为2-4,所述锰盐溶液中锰盐的浓度以MnO2计可以为50-500g·L-1。
17.按照权利要求11所述的催化裂化催化剂制备方法,其中,步骤(2)在所述锰盐溶液中加入尿素,然后在室温搅拌30-60分钟,得到锰源溶液。
18.按照权利要求11所述的催化裂化催化剂制备方法,其中,步骤(3)中,陈化温度为室温至120℃,陈化时间为4-72小时。
19.按照权利要求11所述的催化裂化催化剂制备方法,其中,所述陈化温度为60-100℃,陈化时间为12-36h,搅拌陈化。
20.按照权利要求11所述的催化裂化催化剂制备方法,其中,所述的使陈化固体沉淀物与磷源接触,其过程包括:将陈化固体沉淀物与水按陈化固体沉淀物干基:水=1:(2-5)的重量比混合打浆,再将磷源与所述浆液于室温至90℃下混合,然后搅拌或静置0.2-5小时。
21.按照权利要求11所述的催化裂化催化剂制备方法,其中,所述的锰盐选自硝酸锰、硫酸锰、磷酸锰或氯化锰等中的一种或多种,所述的氮化硼选自六方氮化硼(h-BN)、立方氮化硼(c-BN)、菱方氮化硼(r-BN)和纤锌矿氮化硼(w-BN)中的至少一种,所述的磷源选自磷酸铵、磷酸氢二铵、磷酸二氢铵或磷酸中的一种或多种。
22.按照权利要求11所述的催化裂化催化剂制备方法,其中,步骤(4)中所述焙烧,焙烧温度为500℃-900℃,焙烧时间为4-8小时。
23.权利要求10-22任一项所述方法制备的催化裂化催化剂。
24.权利要求1-9中任意一项或权利要求23所述的催化裂化催化剂在重油催化裂化中的应用。