CN114369950A - 一种迷彩服专用阻燃剂及其制备方法 - Google Patents
一种迷彩服专用阻燃剂及其制备方法 Download PDFInfo
- Publication number
- CN114369950A CN114369950A CN202111673883.9A CN202111673883A CN114369950A CN 114369950 A CN114369950 A CN 114369950A CN 202111673883 A CN202111673883 A CN 202111673883A CN 114369950 A CN114369950 A CN 114369950A
- Authority
- CN
- China
- Prior art keywords
- flame retardant
- epoxy resin
- coupling agent
- parts
- initiator
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及阻燃剂领域，具体涉及到一种迷彩服专用阻燃剂及其制备方法。其阻燃剂原料组成至少包括主料60‑80份，偶联剂1‑8份，自由基聚合单体400‑1000份，引发剂2‑10份，环氧树脂10‑25份，余量为溶剂；本发明制备的阻燃剂绿色环保，不仅具有高的阻燃性而且其密度低，用于迷彩服时能够其穿着舒适度，此外，该阻燃剂在迷彩服面料上的固着率好，从而改善了迷彩服的耐水洗性。
Description
技术领域
本发明涉及阻燃剂领域IPC分类号：C08K，具体涉及到一种迷彩服专用阻燃剂及其制备方法。
背景技术
迷彩服是由绿、黄、茶、黑等颜色组成不规则保护色图案用于伪装的服装。它被广泛应用于作战场上，极大提高了部队行动的隐秘性，能够有效的减少人员伤亡。然而，由于迷彩服一般使用的面料为化纤面料，现代战场情况的复杂性极易造成迷彩服的燃烧，进而对部队人员的生命构成极大的威胁，因此，开发出一种具有阻燃功能的迷彩服至关重要。
目前，具有阻燃功能的迷彩服可以分为两种，一种是由多层面料粘结而成，这种迷彩服降低了穿着舒适度；另外一种是在迷彩服表面涂覆阻燃剂，这种迷彩服虽然提高了其穿着舒适度，然而阻燃剂容易从迷彩服表面脱落，造成这种迷彩服不耐水洗、阻燃功能不持久等问题。
专利申请号201510723516.3的专利公开了一种改进的纤维面料阻燃剂，包括三氯化铁7-11份，双巯基乙酸异辛酯二正辛基锡2-6份，聚四氟乙烯3-9份，丁基卡必醇3-8份，壳聚糖2-5份，聚氧乙烯6-10份，羟甲基三聚氰胺9-17份，甲醛3-8份，对环氧氯丙烷5-9份，无水乙醇5-8份，氢氧化铝9-15份，半补强炭黑5-10份，氢氧化镁9-11份，氧化铝6-8份。该阻燃剂用于纤维面料时并未解决固着率的问题，因而造成阻燃功能不持久问题。
专利申请号201410609424.8的专利公开了一种纤维面料阻燃剂，该阻燃剂用于纤维面料时同样未解决固着率的问题。
发明内容
为了解决上述技术问题，本发明第一个方面提供了一种迷彩服专用阻燃剂，按重量份数计，其制备原料至少包括如下组分：主料60-80份，偶联剂1-8份，自由基聚合单体400-1000份，引发剂2-10份，环氧树脂10-25份，余量为溶剂。
在一种优选的实施方式中，所述迷彩服专用阻燃剂，按重量份数计，其制备原料包括如下组分：主料70份，偶联剂4份，自由基聚合单体800份，引发剂5份，环氧树脂15份，余量为溶剂。
主料
本发明中，所述主料为在阻燃剂中主要起到阻燃的作用。
在一种优选的实施方式中，所述主料选用磷酸三丁酯、磷酸三甲苯酯、氢氧化镁、三氯溴甲烷、三氧化二锑、氢氧化铝、五氧化二锑、六溴环十二烷、氧化石墨烯和十溴联苯醚中一种或几种。
在一种更优选的实施方式中，所述主料为氢氧化镁和氧化石墨烯的混合物，其中，氢氧化镁和氧化石墨烯的质量比在(15-30)：1。
在一种最优选的实施方式中，所述氢氧化镁和氧化石墨烯的质量比为20:1。
所述氢氧化镁购买于潍坊凯博镁盐有限公司，牌号：Q-KB-2。
所述氧化石墨烯购买于郑州市裕博化工产品，牌号：ZY-SM1512。
本发明采用氢氧化镁和石墨烯混合物作为阻燃剂主料，在保证阻燃性能好的基础上进一步减轻阻燃剂涂料的密度，进而在涂覆于迷彩服时减轻其重量，改善它的穿着舒适度。申请人发现，当氢氧化镁和氧化石墨烯的质量比在(15-30)：1范围时，该阻燃剂能够平衡阻燃性能与密度之间的平衡。申请人认为，由于相对于石墨烯而言，氢氧化镁的阻燃性更高，密度更大。当氢氧化镁过多时，虽然该阻燃剂的阻燃性增加，但是该阻燃剂的密度较大，当完全覆盖迷彩服化纤面料时所需的体积越多进而增加了迷彩服的重量，降低了穿着舒适度；当氢氧化镁过少时，一方面降低了阻燃剂的阻燃性，另一方由于阻燃剂的密度过小而造成阻燃剂的蓬松，不利于阻燃剂在迷彩服化纤面料上的固着，进而缩短了阻燃剂的使用寿命。
偶联剂
本发明中，所述偶联剂，是一类具有两不同性质官能团的物质，其分子结构的最大特点是分子中含有化学性质不同的两个基团，一个是亲无机物的基团，易与无机物表面起化学反应；另一个是亲有机物的基团，能与合成树脂或其它聚合物发生化学反应或生成氢键溶于其中。因此偶联剂被称作“分子桥”，用以改善无机物与有机物之间的界面作用，从而大大提高复合材料的性能。
在一种优选的实施方式中，所述偶联剂为铝钛复合偶联剂和/或硅烷偶联剂。
所述硅烷偶联剂选用γ-氨基丙基三乙氧基硅烷、γ-环氧化丙氧基三乙氧基硅烷、α-苯氨基甲基三乙氧基硅烷、乙烯基三甲氧基硅烷和乙烯基三乙氧基硅烷中一种或几种。
在一种更优选的实施方式中，所述偶联剂为铝钛复合偶联剂和γ-环氧化丙氧基三乙氧基硅烷的复合物，其中，铝钛复合偶联剂和γ-环氧化丙氧基三乙氧基硅烷的质量比为(1～3)：1。
通过偶联剂采用铝钛复合偶联剂和γ-环氧化丙氧基三乙氧基硅烷的复合物，能够有效对阻燃剂主料的接枝改性，改善了氢氧化镁和石墨烯混合均匀程度，进而提高阻燃剂在迷彩服面料上的固着均匀性。
在一种最优选的实施方式中，所述铝钛复合偶联剂和γ-环氧化丙氧基三乙氧基硅烷(CAS号为2530-83-8)的质量比为2:1。
所述铝钛复合偶联剂购买于安徽省天长市绿色化工助剂厂，牌号：TL-TA1618。
自由基聚合单体
本发明中，所述自由基聚合单体是一种通过引发剂引发而能够发生聚合并且使链增长不断增长的一种单体。
在一种优选的实施方式中，所述自由基聚合单体选用单烯烃、共轭双烯烃和非共轭双烯烃中一种或几种。
在一种更优选的实施方式中，所述自由基聚合单体为单烯烃。
所述单烯烃选用苯乙烯、醋酸乙烯酯、丙烯酰胺和甲基丙烯酸甲酯中一种或几种。
在一种最优选的实施方式中，所述自由基聚合单体选用丙烯酰胺(CAS号为79-06-1)。
引发剂
本发明中，所述引发剂是能引发单体进行聚合反应的物质。
在一种优选的实施方式中，所述引发剂选用有机过氧化物引发剂、无机过氧化物引发剂、偶氮类引发剂和氧化还原引发剂中一种或几种。
在一种更优选的实施方式中，所述引发剂为偶氮类引发剂和氧化还原引发剂的复合物，其中，偶氮类引发剂和氧化还原引发剂的质量比为(0.8-1.5)：1；
所述偶氮类引发剂选用偶氮二异丁腈、偶氮二异庚腈、偶氮二异丁酸二甲酯和偶氮二异丁基脒中一种或几种；
所述氧化还原引发剂选用过氧化苯甲酰/N，N-二甲基苯胺、过硫酸铵/亚硫酸氢钠、过硫酸钾/亚硫酸氢钠、过硫酸钾/硝酸银、过硫酸盐/硫醇和异丙苯过氧化氢/氯化亚铁中一种或几种。
在一种最优选的实施方式中，所述引发剂为偶氮二异丁酸二甲酯和过氧化苯甲酰/N，N-二甲基苯胺的复合物，其中，偶氮二异丁酸二甲酯(CAS号为2589-57-3)和过氧化苯甲酰(CAS号为94-36-0)/N，N-二甲基苯胺(CAS号为121-69-7)的质量比为1:1。
通过采用偶氮类引发剂和氧化还原引发剂的混合物作为引发剂能够有效缩短自由基单体聚合速率进而提高其产率。
环氧树脂
本发明中，所述环氧树脂为一种高分子聚合物，是指分子中含有两个以上环氧基团的一类聚合物的总称。
在一种优选的实施方式中，所述环氧树脂为双酚A型环氧树脂和/或酚醛环氧树脂。
在一种更优选的实施方式中，所述环氧树脂选用双酚A型环氧树脂。
本申请的发明人发现，环氧树脂通过选用双酚A型环氧树脂，可以有效提高了阻燃剂在迷彩服化纤面料上的固着率。申请人认为，其可能原因是，一方面双酚A型环氧树脂结构中存在大量的羟基和醚基，羟基和醚基有高度的极性，易与迷彩服化纤面料表面羟基形成极性键，该极性键具有强的作用力，另一方面双酚A型环氧树脂上的环氧基易与阻燃剂中的游离键起反应，形成化学键，二者相结合共同提高了阻燃剂在迷彩服化纤面料上的固着率，从而改善了迷彩服的耐水洗性。此外，申请人还意外的发现，双酚A型环氧树脂的存在也有助于提高阻燃剂的阻燃效果，申请人认为，其可能原因是，由于双酚A型环氧树脂在高温燃烧时呈现出高的吸热反应并在迷彩服化纤面料表面生成一种致密的碳化层覆盖物，可以有效隔绝空气与面料之间的接触，从而减缓了面料的燃烧，提高了其阻燃性能。
所述双酚A型环氧树脂选用双酚A型环氧树脂E-03、双酚A型环氧树脂E-06、双酚A型环氧树脂E-12、双酚A型环氧树脂E-20、双酚A型环氧树脂E-35、双酚A型环氧树脂E-42、双酚A型环氧树脂E-44、双酚A型环氧树脂E-51、双酚A型环氧树脂E-55中的一种或多种。
在一种最优选的实施方式中，所述环氧树脂为双酚A型环氧树脂E-06。
所述双酚A型环氧树脂E-06购买于衡阳锦亿生物科技有限公司，牌号：E-06(607)。
溶剂
在一种优选的实施方式中，所述溶剂选用甲苯、乙醇、苯、甲醇和水中一种或几种。
在一种更优选的实施方式中，所述溶剂为乙醇(CAS号为200-578-6)。
本发明的第二个方面提供了一种彩服专用阻燃剂的制备方法，所述制备方法包括如下步骤：
S1.将主料与偶联剂分散于溶剂中，在条件为50-120℃下反应3-8小时，获得偶联剂接枝的主料溶液；
S2.将引发剂加入到S1所获得的偶联剂接枝改性的主料溶液中，在条件为30-60℃下反应1-9小时，获得引发剂接枝的主料溶液；
S3.自由基聚合单体和环氧树脂加入到S2所得的引发剂接枝的主料溶液，在条件为20-70℃下反应1-5小时，即得。
有益效果
1.采用氢氧化镁和氧化石墨烯的混合物作为阻燃剂的主体，能够在确保阻燃性能好的条件下有效的降低阻燃剂的密度，进而改善迷彩服的穿着舒适度。
2.通过偶联剂采用铝钛复合偶联剂和γ-环氧化丙氧基三乙氧基硅烷的复合物，能够有效对阻燃剂主料的接枝改性，改善了氢氧化镁和石墨烯混合均匀程度，进而提高阻燃剂在迷彩服面料上的固着均匀性。
3.采用偶氮类引发剂和氧化还原引发剂的混合物作为引发剂能够有效缩短自由基单体聚合速率进而提高其产率。
4.通过环氧树脂选用双酚A型环氧树脂，可以有效提高阻燃剂在迷彩服上的固着率，从而改善了迷彩服的耐水洗性。
5.该阻燃剂绿色环保，不含致癌致畸物质且无毒无害，挥发性低，对人体无刺激。
具体实施方式
实施例1
实施例1提供了一种迷彩服专用阻燃剂，按重量份数计，包括如下组分：主料70份，偶联剂4份，自由基聚合单体800份，引发剂5份，环氧树脂15份，溶剂500份；
所述主料为氢氧化镁和氧化石墨烯的混合物，其中，氢氧化镁和氧化石墨烯的质量比为20:1；
所述氢氧化镁购买于潍坊凯博镁盐有限公司，牌号：Q-KB-2。
所述氧化石墨烯购买于郑州市裕博化工产品，牌号：ZY-SM1512。
所述偶联剂为铝钛复合偶联剂和γ-环氧化丙氧基三乙氧基硅烷的复合物，其中，铝钛复合偶联剂和γ-环氧化丙氧基三乙氧基硅烷(CAS号为2530-83-8)的质量比为2：1；
所述铝钛复合偶联剂购买于安徽省天长市绿色化工助剂厂，牌号：TL-TA1618。
所述自由基聚合单体选用丙烯酰胺(CAS号为79-06-1)；
所述引发剂为偶氮二异丁酸二甲酯和过氧化苯甲酰/N，N-二甲基苯胺的复合物，其中，偶氮二异丁酸二甲酯(CAS号为2589-57-3)和过氧化苯甲酰(CAS号为94-36-0)/N，N-二甲基苯胺(CAS号为121-69-7)的质量比为1:1；
所述环氧树脂为双酚A型环氧树脂E-06；
所述双酚A型环氧树脂E-06购买于衡阳锦亿生物科技有限公司，牌号：E-06(607)；
所述溶剂为乙醇(CAS号为200-578-6)；
一种迷彩服专用阻燃剂的制备方法，包括以下步骤：
S1.将主料与偶联剂分散于溶剂中，在条件为80℃下反应5小时，获得偶联剂接枝的主料溶液；
S2.将引发剂加入到S1所获得的偶联剂接枝改性的主料溶液中，在条件为40℃下反应5小时，获得引发剂接枝的主料溶液；
S3.自由基聚合单体和环氧树脂加入到S2所得的引发剂接枝的主料溶液，在条件为50℃下反应1小时，即得。
实施例2
实施例2提供了一种迷彩服专用阻燃剂，按重量份数计，包括如下组分：主料60份，偶联剂1份，自由基聚合单体400份，引发剂2份，环氧树脂10份，溶剂300份；
所述主料为氢氧化镁和氧化石墨烯的混合物，其中，氢氧化镁和氧化石墨烯的质量比为20:1；
所述氢氧化镁购买于潍坊凯博镁盐有限公司，牌号：Q-KB-2。
所述氧化石墨烯购买于郑州市裕博化工产品，牌号：ZY-SM1512。
所述偶联剂为铝钛复合偶联剂和γ-环氧化丙氧基三乙氧基硅烷的复合物，其中，铝钛复合偶联剂和γ-环氧化丙氧基三乙氧基硅烷(CAS号为2530-83-8)的质量比为2：1；
所述铝钛复合偶联剂购买于安徽省天长市绿色化工助剂厂，牌号：TL-TA1618。
所述自由基聚合单体选用丙烯酰胺(CAS号为79-06-1)；
所述引发剂为偶氮二异丁酸二甲酯和过氧化苯甲酰/N，N-二甲基苯胺的复合物，其中，偶氮二异丁酸二甲酯(CAS号为2589-57-3)和过氧化苯甲酰(CAS号为94-36-0)/N，N-二甲基苯胺(CAS号为121-69-7)的质量比为1:1；
所述环氧树脂为双酚A型环氧树脂E-06；
所述双酚A型环氧树脂E-06购买于衡阳锦亿生物科技有限公司，牌号：E-06(607)；
所述溶剂为乙醇(CAS号为200-578-6)；
一种迷彩服专用阻燃剂的制备方法，包括以下步骤：
S1.将主料与偶联剂分散于溶剂中，在条件为60℃下反应3小时，获得偶联剂接枝的主料溶液；
S2.将引发剂加入到S1所获得的偶联剂接枝改性的主料溶液中，在条件为30℃下反应3小时，获得引发剂接枝的主料溶液；
S3.自由基聚合单体和环氧树脂加入到S2所得的引发剂接枝的主料溶液，在条件为50℃下反应1小时，即得。
实施例3
实施例3提供了一种迷彩服专用阻燃剂，按重量份数计，包括如下组分：主料80份，偶联剂8份，自由基聚合单体1000份，引发剂10份，环氧树脂25份，溶剂700份；
所述主料为氢氧化镁和氧化石墨烯的混合物，其中，氢氧化镁和氧化石墨烯的质量比为20:1；
所述氢氧化镁购买于潍坊凯博镁盐有限公司，牌号：Q-KB-2。
所述氧化石墨烯购买于郑州市裕博化工产品，牌号：ZY-SM1512。
所述偶联剂为铝钛复合偶联剂和γ-环氧化丙氧基三乙氧基硅烷的复合物，其中，铝钛复合偶联剂和γ-环氧化丙氧基三乙氧基硅烷(CAS号为2530-83-8)的质量比为2：1；
所述铝钛复合偶联剂购买于安徽省天长市绿色化工助剂厂，牌号：TL-TA1618。
所述自由基聚合单体选用丙烯酰胺(CAS号为79-06-1)；
所述引发剂为偶氮二异丁酸二甲酯和过氧化苯甲酰/N，N-二甲基苯胺的复合物，其中，偶氮二异丁酸二甲酯(CAS号为2589-57-3)和过氧化苯甲酰(CAS号为94-36-0)/N，N-二甲基苯胺(CAS号为121-69-7)的质量比为1:1；
所述环氧树脂为双酚A型环氧树脂E-06；
所述双酚A型环氧树脂E-06购买于衡阳锦亿生物科技有限公司，牌号：E-06(607)；
所述溶剂为乙醇(CAS号为200-578-6)；
一种迷彩服专用阻燃剂的制备方法，包括以下步骤：
S1.将主料与偶联剂分散于溶剂中，在条件为100℃下反应3小时，获得偶联剂接枝的主料溶液；
S2.将引发剂加入到S1所获得的偶联剂接枝改性的主料溶液中，在条件为30℃下反应8小时，获得引发剂接枝的主料溶液；
S3.自由基聚合单体和环氧树脂加入到S2所得的引发剂接枝的主料溶液，在条件为50℃下反应1小时，即得。
对比例1
对比例1提供了一种迷彩服专用阻燃剂，按重量份数计，包括如下组分：主料70份，偶联剂4份，自由基聚合单体800份，引发剂5份，环氧树脂15份，溶剂500份；
所述主料为氢氧化镁和氧化石墨烯的混合物，其中，氢氧化镁和氧化石墨烯的质量比为10:1；
所述氢氧化镁购买于潍坊凯博镁盐有限公司，牌号：Q-KB-2。
所述氧化石墨烯购买于郑州市裕博化工产品，牌号：ZY-SM1512。
所述偶联剂为铝钛复合偶联剂和γ-环氧化丙氧基三乙氧基硅烷的复合物，其中，铝钛复合偶联剂和γ-环氧化丙氧基三乙氧基硅烷(CAS号为2530-83-8)的质量比为2：1；
所述铝钛复合偶联剂购买于安徽省天长市绿色化工助剂厂，牌号：TL-TA1618。
所述自由基聚合单体选用丙烯酰胺(CAS号为79-06-1)；
所述引发剂为偶氮二异丁酸二甲酯和过氧化苯甲酰/N，N-二甲基苯胺的复合物，其中，偶氮二异丁酸二甲酯(CAS号为2589-57-3)和过氧化苯甲酰(CAS号为94-36-0)/N，N-二甲基苯胺(CAS号为121-69-7)的质量比为1:1；
所述环氧树脂为双酚A型环氧树脂E-06；
所述双酚A型环氧树脂E-06购买于衡阳锦亿生物科技有限公司，牌号：E-06(607)；
所述溶剂为乙醇(CAS号为200-578-6)；
一种迷彩服专用阻燃剂的制备方法，包括以下步骤：
S1.将主料与偶联剂分散于溶剂中，在条件为80℃下反应5小时，获得偶联剂接枝的主料溶液；
S2.将引发剂加入到S1所获得的偶联剂接枝改性的主料溶液中，在条件为40℃下反应5小时，获得引发剂接枝的主料溶液；
S3.自由基聚合单体和环氧树脂加入到S2所得的引发剂接枝的主料溶液，在条件为50℃下反应1小时，即得。
对比例2
对比例2提供了一种迷彩服专用阻燃剂，按重量份数计，包括如下组分：主料70份，偶联剂4份，自由基聚合单体800份，引发剂5份，环氧树脂15份，溶剂500份；
所述主料为氢氧化镁和氧化石墨烯的混合物，其中，氢氧化镁和氧化石墨烯的质量比为5:1；
所述氢氧化镁购买于潍坊凯博镁盐有限公司，牌号：Q-KB-2。
所述氧化石墨烯购买于郑州市裕博化工产品，牌号：ZY-SM1512。
所述偶联剂为铝钛复合偶联剂和γ-环氧化丙氧基三乙氧基硅烷的复合物，其中，铝钛复合偶联剂和γ-环氧化丙氧基三乙氧基硅烷(CAS号为2530-83-8)的质量比为2：1；
所述铝钛复合偶联剂购买于安徽省天长市绿色化工助剂厂，牌号：TL-TA1618。
所述自由基聚合单体选用丙烯酰胺(CAS号为79-06-1)；
所述引发剂为偶氮二异丁酸二甲酯和过氧化苯甲酰/N，N-二甲基苯胺的复合物，其中，偶氮二异丁酸二甲酯(CAS号为2589-57-3)和过氧化苯甲酰(CAS号为94-36-0)/N，N-二甲基苯胺(CAS号为121-69-7)的质量比为1:1；
所述环氧树脂为双酚A型环氧树脂E-06；
所述双酚A型环氧树脂E-06购买于衡阳锦亿生物科技有限公司，牌号：E-06(607)；
所述溶剂为乙醇(CAS号为200-578-6)；
一种迷彩服专用阻燃剂的制备方法，包括以下步骤：
S1.将主料与偶联剂分散于溶剂中，在条件为80℃下反应5小时，获得偶联剂接枝的主料溶液；
S2.将引发剂加入到S1所获得的偶联剂接枝改性的主料溶液中，在条件为40℃下反应5小时，获得引发剂接枝的主料溶液；
S3.自由基聚合单体和环氧树脂加入到S2所得的引发剂接枝的主料溶液，在条件为50℃下反应1小时，即得。
对比例3
对比例3提供了一种迷彩服专用阻燃剂，按重量份数计，包括如下组分：主料70份，偶联剂4份，自由基聚合单体800份，引发剂5份，环氧树脂15份，溶剂500份；
所述主料为氢氧化镁和氧化石墨烯的混合物，其中，氢氧化镁和氧化石墨烯的质量比为20:1；
所述氢氧化镁购买于潍坊凯博镁盐有限公司，牌号：Q-KB-2。
所述氧化石墨烯购买于郑州市裕博化工产品，牌号：ZY-SM1512。
所述偶联剂为铝钛复合偶联剂和γ-环氧化丙氧基三乙氧基硅烷的复合物，其中，铝钛复合偶联剂和γ-环氧化丙氧基三乙氧基硅烷(CAS号为2530-83-8)的质量比为2：1；
所述铝钛复合偶联剂购买于安徽省天长市绿色化工助剂厂，牌号：TL-TA1618。
所述自由基聚合单体选用丙烯酰胺(CAS号为79-06-1)；
所述引发剂为偶氮二异丁酸二甲酯和过氧化苯甲酰/N，N-二甲基苯胺的复合物，其中，偶氮二异丁酸二甲酯(CAS号为2589-57-3)和过氧化苯甲酰(CAS号为94-36-0)/N，N-二甲基苯胺(CAS号为121-69-7)的质量比为1:1；
所述环氧树脂为酚醛环氧树脂；
所述酚醛环氧树脂为酚醛环氧树脂F-44；
所述双酚酚醛环氧树脂F-44购买于上海帆啸化工科技有限公司，牌号：F-44；
所述溶剂为乙醇(CAS号为200-578-6)；
一种迷彩服专用阻燃剂的制备方法，包括以下步骤：
S1.将主料与偶联剂分散于溶剂中，在条件为80℃下反应5小时，获得偶联剂接枝的主料溶液；
S2.将引发剂加入到S1所获得的偶联剂接枝改性的主料溶液中，在条件为40℃下反应5小时，获得引发剂接枝的主料溶液；
S3.自由基聚合单体和环氧树脂加入到S2所得的引发剂接枝的主料溶液，在条件为50℃下反应1小时，即得。
性能测试方法
阻燃性能测试：参考GB/T5455-2014测试方法，将实施例1-3和对比例1-3所制备的阻燃剂涂覆于迷彩服面料进行阻燃性能测试。
表1
Claims (10)
1.一种迷彩服专用阻燃剂，其特征在于，按重量份计，至少包括如下组分：主料60-80份，偶联剂1-8份，自由基聚合单体400-1000份，引发剂2-10份，环氧树脂10-25份，余量为溶剂。
2.根据权利要求1所述的一种迷彩服专用阻燃剂，其特征在于，所述主料选用磷酸三丁酯、磷酸三甲苯酯、氢氧化镁、三氯溴甲烷、三氧化二锑、氢氧化铝、五氧化二锑、六溴环十二烷、氧化石墨烯和十溴联苯醚中一种或几种。
3.根据权利要求2所述的一种迷彩服专用阻燃剂，其特征在于，所述主料为氢氧化镁和/或氧化石墨烯。
4.根据权利要求1所述的一种迷彩服专用阻燃剂，其特征在于，所述偶联剂为铝钛复合偶联剂和/或硅烷偶联剂。
5.根据权利要求4所述的一种迷彩服专用阻燃剂，其特征在于，所述硅烷偶联剂选用γ-氨基丙基三乙氧基硅烷、γ-环氧化丙氧基三乙氧基硅烷、α-苯氨基甲基三乙氧基硅烷、乙烯基三甲氧基硅烷和乙烯基三乙氧基硅烷中一种或几种。
6.根据权利要求1所述的一种迷彩服专用阻燃剂，其特征在于，所述自由基聚合单体选用单烯烃、共轭双烯烃和非共轭双烯烃中一种或几种。
7.根据权利要求1-6所述的任一项一种迷彩服专用阻燃剂，其特征在于，所述引发剂选用有机过氧化物引发剂、无机过氧化物引发剂、偶氮类引发剂和氧化还原引发剂中一种或几种。
8.根据权利要求1所述的一种迷彩服专用阻燃剂，其特征在于，所述环氧树脂为双酚A型环氧树脂和/或酚醛环氧树脂。
9.根据权利要求8所述的一种迷彩服专用阻燃剂，其特征在于，所述环氧树脂为双酚A型环氧树脂。
10.一种根据权利要求1-9任一项所述的迷彩服专用阻燃剂的制备方法，其特征在于，包括以下步骤：
S1.将主料与偶联剂分散于溶剂中，在条件为50-120℃下反应3-8小时，获得偶联剂接枝的主料溶液；
S2.将引发剂加入到S1所获得的偶联剂接枝改性的主料溶液中，在条件为30-60℃下反应1-9小时，获得引发剂接枝的主料溶液；
S3.自由基聚合单体和环氧树脂加入到S2所得的引发剂接枝的主料溶液，在条件为20-70℃下反应1-5小时，即得。