CN114349580A - 一种硝酸磷肥副产品制成的土壤调理剂及其造粒方法 - Google Patents
一种硝酸磷肥副产品制成的土壤调理剂及其造粒方法 Download PDFInfo
- Publication number
- CN114349580A CN114349580A CN202210169985.5A CN202210169985A CN114349580A CN 114349580 A CN114349580 A CN 114349580A CN 202210169985 A CN202210169985 A CN 202210169985A CN 114349580 A CN114349580 A CN 114349580A
- Authority
- CN
- China
- Prior art keywords
- parts
- nitrophosphate fertilizer
- byproduct
- soil conditioner
- stirring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种硝酸磷肥副产品制成的土壤调理剂及其造粒方法。本发明的方法包括：所述土壤调理剂通过将硝酸磷肥副产品、粘结物、营养添加剂、水混合搅拌，造粒干燥制成；其中硝酸磷肥副产品、粘结物、营养添加剂和水按如下质量份数混合：硝酸磷肥副产品70~85份、粘结物10~25份、营养添加剂0~6份、水0~10份；所述粘结物为黏土、生石灰、生石膏、熟石膏、硝酸铵钙副产品的一种或几种，其中硝酸铵钙副产品中氧化钙含量为25~35%；所述营养添加剂为氧化镁、碳酸镁、硼砂、尿素、硫酸铜、钼酸铵、硫酸锌、硫酸亚铁、腐殖酸中的一种或一种以上。本发明能够解决由硝酸磷肥副产品碳酸钙制成优质土壤调理剂的难题，提高颗粒强度，提升造粒效率，工艺简单。
Description
技术领域
本发明涉及复合肥生产技术领域，具体涉及一种硝酸磷肥副产品制成的土壤调理剂及其造粒方法。
背景技术
硝酸磷肥副产品由硝酸分解磷矿，再经离子交换取得，因其碳酸钙含量达到72%以上，常被称为“碳酸钙滤饼”或“CC滤饼”。硝酸磷肥工业常配套建设水泥厂，将上述副产品用于生产水泥。现环保投入大，水泥生产成本高。因此，将硝酸磷肥副产品简单处理或造粒后，制成土壤调理剂产品，用在农业领域，可改良酸性土壤。
而现有的技术方案中，需要按比例添加硫酸铵、尿素，在管式反应器中造粒，再经烘干，产品存在结块、强度不够、工艺指标不稳定、生产成本较高等问题。
如发明专利申请公告号为CN 113546592 A的一种硝酸铵钙的生产方法及装置，以冷冻法生产硝酸磷肥过程中产生的硝酸钙液和青石为原料，经中和反应后，通入石灰乳调节PH至6-6.8，经压滤、蒸发浓缩后，得到成品浆料，造粒即得硝酸铵钙，生产过程中产生的副产品中含有硝酸无法分解的酸不溶物，主要是硅，还有一部分的氧化钙和氢氧化钙，其中氧化钙含量在30%左右，这部分副产品得不到充分的利用，造成浪费。
为了解决以上技术问题，本发明提出了一种硝酸磷肥副产品制成的土壤调理剂及其造粒方法。
发明内容
本发明的目的是克服现有技术的不足，提出一种硝酸磷肥副产品制成的土壤调理剂及其造粒方法，能够解决由硝酸磷肥副产品制成优质土壤调理剂的难题，同时充分利用硝酸铵钙副产品，提高颗粒强度，提升造粒效率，工艺简单。
为实现以上目的，本发明提出以下技术方案：
一种硝酸磷肥副产品制成的土壤调理剂，其特征在于：所述土壤调理剂通过将硝酸磷肥副产品、粘结物、营养添加剂、水混合搅拌，造粒干燥制成；
其中硝酸磷肥副产品、粘结物、营养添加剂和水按如下质量份数混合：硝酸磷肥副产品70~85份、粘结物10~2份、营养添加剂0~6份、水0~10份；
所述硝酸磷肥副产品由硝酸分解磷矿经离子交换所得，其中碳酸钙含量为72%以上；
所述粘结物为黏土、生石灰、生石膏、熟石膏、硝酸铵钙副产品的一种或几种，其中硝酸铵钙副产品是以冷冻法生产硝酸磷肥过程中产生的硝酸钙液和青石为原料，经中和反应后所得的副产品，硝酸铵钙副产品中氧化钙含量为25~35%；
所述营养添加剂为氧化镁、碳酸镁、硼砂、尿素、硫酸铜、钼酸铵、硫酸锌、硫酸亚铁、腐殖酸中的一种或一种以上。
优选地，所述土壤调理剂中硝酸磷肥副产品、粘结物、营养添加剂和水的质量份数为：硝酸磷肥副产品80~82份、粘结物15~20份、营养添加剂3~3.5份、水5~7份。
一种制作所述土壤调理剂的造粒方法，其特征在于：
a)将硝酸磷肥副产品与粘结物以及营养添加剂混合，高速搅拌；
b)高速搅拌0.5~2min后，加水，继续搅拌1.5~3.5min；降速，造粒，干燥；
c)将干燥后的颗粒物筛分，保留粒径2-4mm之间的颗粒。
优选地，所述造粒方法，其特征在于：
a)将硝酸磷肥副产品与粘结物以及营养添加剂混合，高速搅拌，采用强力搅拌机，并保持犁刀转子1900~2100r/min，滚筒转速50~55r/min；
b)高速搅拌1~1.5min后，加水，继续搅拌2~3min；降速，犁刀转子转速降至250~450r/min，滚筒转速调为22~27r/min；造粒，在滚筒干燥设备中干燥，干燥温度为100~110℃，干燥时间为1.5~2.5h；
c)将干燥后的颗粒物筛分，保留粒径2~4mm之间的颗粒。
优选地，所述造粒方法，其特征在于：
a)将硝酸磷肥副产品与粘结物以及营养添加剂混合，高速搅拌，采用强力搅拌机，并保持犁刀转子2000r/min，滚筒转速52r/min；
b)高速搅拌1~1.5min后，加水，继续搅拌2~3min；降速，犁刀转子转速降至300~400r/min，滚筒105℃，干燥时间为2h；
c)将干燥后的颗粒物筛分，保留粒径2~4mm之间的颗粒。
具体地，利用硝酸磷肥副产品碳酸钙制成的土壤调理剂，其主要成分为：硝酸磷肥副产品、粘结物、营养添加剂和水，质量份数为硝酸磷肥副产品70~85份、粘结物10~25份、营养添加剂0~6份、水0~1份；
所述硝酸磷肥副产品由硝酸分解磷矿，再经离子交换取得，其中碳酸钙含量为72%以上；
所述粘结物为黏土、生石灰、生石膏、熟石膏、硝酸铵钙副产品的一种或几种；
其中硝酸铵钙副产品是在以冷冻法生产硝酸磷肥过程中产生的硝酸钙液和青石为原料，经中和反应后，造粒制得硝酸铵钙的过程中产生的，硝酸铵钙副产品含有氧化钙和氢氧化钙，其中氧化钙含量在30%左右；
所述营养添加剂为氧化镁、碳酸镁、硼砂、尿素、硫酸铜、钼酸铵、硫酸锌、硫酸亚铁、腐殖酸中的一种或一种以上。
利用硝酸磷肥副产品制作土壤调理剂的操作步骤如下：
（1）将硝酸磷肥副产品与粘结物以及营养添加剂按照各质量分数混合，放入强力搅拌机，开启高速搅拌，保持犁刀转子的转速为1900~2100r/min，滚筒50~55r/min；
（2）高速搅拌0.5~2min后，从搅拌机加料口加入适量的水，控制流速和流量，均匀加入搅拌物料当中，继续高速搅拌1.5~3.5min；
（3）降低犁刀转子转速至250~450r/min，同时将滚筒转速调为低速挡22~27r/min，进入造粒阶段；
（4）适时从搅拌机观察窗观察造粒情况，必要时可通过加料口取样查看，当观察到所需颗粒已经大部分形成，及时关闭搅拌机；
（5）将步骤（4）制得的颗粒物转移至滚筒干燥设备，干燥温度为100~110℃，干燥时间为1.5~2.5h；
（6）将步骤（5）烘干后的颗粒物通过振荡筛，保留粒径2~4mm之间的颗粒。
硝酸铵钙副产品是指以冷冻法生产硝酸磷肥过程中产生的硝酸钙液和青石为原料，经中和反应后通入石灰乳调节PH至6-6.8，经压滤、蒸发浓缩后，得到成品浆料，造粒制得硝酸铵钙的生产过程中产生的副产品，副产品中含有硝酸无法分解的酸不溶物，主要是硅，还有一部分的氧化钙和氢氧化钙，其中氧化钙含量在30%左右，可以用来调理酸化土壤；因此硝酸铵钙副产品可以作为土壤调理剂的添加剂，优化土壤调理剂的改善土质功能。
硝酸磷肥副产品制得的土壤调理剂，其所含有的碳酸钙进入酸性土壤后，在氢离子的作用下，释放出钙离子、碳酸氢根、氢氧根等，第一阶段，碳酸氢根和氢氧根中和土壤中的活性酸即氢离子；第二阶段，钙离子置换土壤颗粒或胶体吸附的氢离子和铝离子，使潜在酸转变为活性酸，随后被中和。通过上述过程，减少土壤中氢离子和水溶性铝的含量，提高土壤pH值，减轻“铝毒”对作物的伤害。
本发明有益效果在于：
采用上述方案，本发明能够解决由硝酸磷肥副产品碳酸钙制成优质土壤调理剂的难题，同时充分利用硝酸铵钙副产品，提高颗粒强度，提升造粒效率，工艺简单。
具体实施方式
实施例1：
称取硝酸磷肥副产品2000g、黏土250g，加入强力搅拌机，开启高速搅拌，取165mL水从加料口加入搅拌机，3min后，调整搅拌机参数，进入造粒阶段；
实时观察造粒情况，7min后停机，从搅拌机取出颗粒物，转移至滚筒烘干，温度105℃，时间2h，筛分出2.00~4.00mm的颗粒。
实施例2：
称取硝酸磷肥副产品2000g、黏土200g、硝酸铵钙副产品230g，加入强力搅拌机，开启高速搅拌，3min后，调整搅拌机参数，进入造粒阶段；
实时观察造粒情况，9min后停机，从搅拌机取出颗粒物，转移至滚筒烘干，温度105℃，时间2h，筛分出2.00~4.00mm的颗粒。
实施例3：
称取硝酸磷肥副产品2000g、黏土200g、熟石膏200g，加入强力搅拌机，开启高速搅拌，取50mL水从加料口加入搅拌机，3min后，调整搅拌机参数，进入造粒阶段；
实时观察造粒情况，11min后停机，从搅拌机取出颗粒物，转移至滚筒烘干，温度105℃，时间2h，筛分出2.00~4.00mm的颗粒。
实施例4：
称取硝酸磷肥副产品2000g、黏土200g、硝酸铵钙副产品200g、石膏100g，加入强力搅拌机，开启高速搅拌，3min后，调整搅拌机参数，进入造粒阶段；
实时观察造粒情况，14min后停机，从搅拌机取出颗粒物，转移至滚筒烘干，温度105℃，时间2h，筛分出2.00~4.00mm的颗粒。
实施例5：
称取硝酸磷肥副产品2000g、黏土200g、硝酸铵钙副产品180g、熟石膏100g、生石灰100g，加入强力搅拌机，开启高速搅拌，3min后，调整搅拌机参数，进入造粒阶段；
实时观察造粒情况，10min后停机，从搅拌机取出颗粒物，转移至滚筒烘干（105℃）2h，筛分出2.00~4.00mm的颗粒。
实施例6：
称取硝酸磷肥副产品2000g、黏土250g、腐殖酸80g、熟石膏100g，加入强力搅拌机，开启高速搅拌，取220mL水从加料口加入搅拌机，3min后，调整搅拌机参数，进入造粒阶段；
实时观察造粒情况，10min后停机，从搅拌机取出颗粒物，转移至滚筒烘干（105℃）2h，筛分出2.00~4.00mm的颗粒。
实施例1~6所得样品的各项指数如下表所示，由下表可知，各实施例符合国家标准。
| 检验项目 | 标准规定 | 实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | 实施例6 |
| 外观 | 灰白色粉状，无机械杂质 | 灰白色粉状，无机械杂质 | 灰白色粉状，无机械杂质 | 灰白色粉状，无机械杂质 | 灰白色粉状，无机械杂质 | 灰白色粉状，无机械杂质 | 灰白色粉状，无机械杂质 |
| 氧化钙的质量分数 | ≥40.0% | 41.24% | 42.44% | 42.36% | 41.17% | 41.75% | 42.87% |
| pH值（10%水溶液） | 8~10 | 8.2 | 8.54 | 8.1 | 8.5 | 9.1 | 9.0 |
| 水分（游离水）的质量分数 | ≤15.0% | 1.80% | 0.5% | 1.5% | 2.0% | 1.1% | 1.7% |
以上仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明的保护范围之内。
Claims (8)
1.一种硝酸磷肥副产品制成的土壤调理剂，其特征在于：所述土壤调理剂通过将硝酸磷肥副产品、粘结物、营养添加剂、水混合搅拌，造粒干燥制成；
其中硝酸磷肥副产品、粘结物、营养添加剂和水按如下质量份数混合：
硝酸磷肥副产品70~85份、粘结物10~25份、营养添加剂0~6份、水0~10份；所述硝酸磷肥副产品中碳酸钙含量为72%以上；
所述粘结物为黏土、生石灰、生石膏、熟石膏、硝酸铵钙副产品的一种或几种，其中硝酸铵钙副产品中氧化钙含量为25~35%；
所述营养添加剂为氧化镁、碳酸镁、硼砂、尿素、硫酸铜、钼酸铵、硫酸锌、硫酸亚铁、腐殖酸中的一种或一种以上。
2.根据权利要求1所述的土壤调理剂，其特征在于：
所述土壤调理剂中硝酸磷肥副产品、粘结物、营养添加剂和水的质量份数为：硝酸磷肥副产品80~82份、粘结物15~20份、营养添加剂3~3.5份、水5~7份。
3.一种制作如权利要求1~2任一项所述土壤调理剂的造粒方法，其特征在于：包括以下步骤：
a）将硝酸磷肥副产品与粘结物以及营养添加剂混合，高速搅拌；
b）高速搅拌0.5~2min后，加水，继续搅拌1.5~3.5min；降速，造粒，干燥；
c）将干燥后的颗粒物筛分，保留粒径2~4mm之间的颗粒。
4.根据权利要求3所述的造粒方法，其特征在于：
步骤a中高速搅拌采用强力搅拌机，并保持犁刀转子转速1900~2100r/min，滚筒转速50~55r/min。
5.根据权利要求3所述的造粒方法，其特征在于：
步骤b中降速即降低犁刀转子转速至250~450r/min，滚筒转速调为22~27r/min；干燥温度为100~110℃，干燥时间为1.5~2.5h。
6.根据权利要求3所述的造粒方法，其特征在于：步骤b中高速搅拌1~1.5min后加水，继续搅拌2~3min。
7.根据权利要求4所述的造粒方法，其特征在于：
步骤a中高速搅拌保持犁刀转子2000r/min，滚筒52r/min。
8.根据权利要求5所述的造粒方法，其特征在于：
步骤b中降速即降低犁刀转子转速至300~400r/min，滚筒调为25r/min；干燥温度为105℃，干燥时间为2h。