CN114031967A - 家具漆用多效合一添加剂及制备方法和应用 - Google Patents
家具漆用多效合一添加剂及制备方法和应用 Download PDFInfo
- Publication number
- CN114031967A CN114031967A CN202111185377.5A CN202111185377A CN114031967A CN 114031967 A CN114031967 A CN 114031967A CN 202111185377 A CN202111185377 A CN 202111185377A CN 114031967 A CN114031967 A CN 114031967A
- Authority
- CN
- China
- Prior art keywords
- antibacterial
- parts
- zinc oxide
- additive
- aldehyde
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种家具漆用多效合一添加剂及制备方法和应用，家具漆用多效合一添加剂由抗菌防霉剂、复合氧化锌抗菌除醛材料、除醛剂和溶剂按照一定比例制备而成。抗菌防霉剂优选有机复合型抗菌防霉剂，复合氧化锌抗菌除醛材料为氧化石墨烯负载纳米氧化锌复合物，纳米氧化锌复合物是由水热法制备的片层花瓣状氧化锌和四针状氧化锌晶须按照一定比例复合而成。家具漆用多效合一添加剂制备时将各原料混合均匀即得，应用时在木器漆里面的添加量为2‑6wt％。该添加剂具有良好抗菌防霉除甲醛性能，持久性也较好，综合性能好。
Description
技术领域
本发明涉及一种家具漆添加剂，特别是一种具有抗菌、防霉、 除甲醛作用的家具漆用添加剂。
背景技术
当今涂料市场，尤其是在家具涂料上，环保健康的产品已经成 为消费者的主要需求，消费者对家具的要求从简单的美观、实用逐 渐向健康、安全方面延伸。
制作家具会用到大量的木材，尤其是胶合板、纤维板等人造 板，这些人造板制作的木门、木质家具、木质玩具、木质装饰等人 造板制品表面容易吸附滋生细菌、霉菌，严重影响人造板制品的美 观及人体的健康。同时人造板制品中含有有机污染物甲醛、苯、氨等，为了降低有机污染物对人体的伤害，目前，常常在这些木门、 木质家具、木质玩具、木质装饰的表面涂覆木器漆以密封或减缓有 机污染物的挥发。但是，现有的木器漆不能长时间密封有机污染 物，有机污染物仍会挥发至空气中而被人体吸收，危害人体健康。
当前木器漆(包括家具和室内装饰装修涂料)的主要品种有硝基 漆(NC)、聚氨酯漆(PU)、紫外光固化漆(UV)和水性漆等。
目前，木器漆所使用的抗菌剂主要为有机抗菌剂、光催化抗菌 剂。有机抗菌剂主要是通过破坏微生物的细胞膜结构，使微生物死 亡，从而达到抗菌效果，其缺点为持久性较差。光催化抗菌剂需要 在紫外光照射条件下，才能具有抗菌性，因此不适合在室内应用。
目前，木器漆所使用的除甲醛主要有光催化氧化法、化学固定 法，光催化氧化法主要就是使用光触媒来将甲醛氧化分解，这种方 法同样需要在紫外光照射条件下进行。化学固定法一般采用胺类化 合物来固定甲醛，此法甲醛去除的持久性较差。
目前，功能性家具在生产过程中抗菌和除醛功能一般分两步进 行添加，这样不仅增加了成本问题，同时对能源和环境是一种较高 的消耗和污染。在国家倡导企业节能减排的大环境下，提供一种能 够集抗菌防霉除醛一体的家具漆添加剂，使得多步工序变为一步是 十分有必要的。
发明内容
本发明的目的在于提供一种可以达到抗菌防霉除醛功效的家具 漆添加剂，制备方法和应用。
一种家具漆用多效合一添加剂，其包括如下质量份的各组分： 抗菌防霉剂10-25份，复合氧化锌抗菌除醛材料5-8份，除醛剂22-40 份，溶剂30-60份。
一种优选的技术方案要求家具漆用多效合一添加剂包括如下质 量份的各组分：抗菌防霉剂15-25份，复合氧化锌抗菌除醛材料5-8 份，除醛剂25-35份，溶剂30-60份。
另一种优选的技术方案要求家具漆用多效合一添加剂包括如下 质量份的各组分：抗菌防霉剂20-25份，复合氧化锌抗菌除醛材料 5-8份，除醛剂27-35份，溶剂30-60份。
另外，也可以采用以下的配方组合制备家具漆用多效合一添加 剂：
抗菌防霉剂20-25份，复合氧化锌抗菌除醛材料6份，除醛剂 27-28份，溶剂30-60份；
或者抗菌防霉剂20-25份，复合氧化锌抗菌除醛材料6份，除醛 剂29-31份，溶剂30-60份；
或者抗菌防霉剂20-25份，复合氧化锌抗菌除醛材料6份，除醛 剂32-35份，溶剂30-60份；
或者抗菌防霉剂20-23份，复合氧化锌抗菌除醛材料5-8份，除 醛剂28-32份，溶剂30-60份。
多效合一是指添加剂同时具有抗菌、防霉和除甲醛的功效。
抗菌防霉剂选择苯醚甲环唑、腈菌唑、嘧霉胺、抑霉唑、戊唑 醇、3-碘代-2-丙炔醇-丁基甲氨酸酯、尼泊金乙酯、尼泊金丙酯、尼 泊金丁酯、对氯间二甲苯酚、脱氢乙酸、脱氢乙酸钠等中的一种或 几种。可以采用其中的任意一种作为抗菌防霉剂，也可以采用其中的任意两种或者更多种类进行复配得到复合型抗菌防霉剂。优选 的，抗菌防霉剂主要为有机复合型抗菌防霉剂。例如有机复合型抗 菌防霉剂是苯醚甲环唑、腈菌唑、抑霉唑、戊唑醇中的任意一种与 嘧霉胺、脱氢乙酸、脱氢乙酸钠中的任意一种，以及3-碘代-2-丙炔 醇-丁基甲氨酸酯、尼泊金乙酯、尼泊金丙酯、尼泊金丁酯、对氯间 二甲苯酚中的任意一种的复合物。有机复合型抗菌防霉剂也可以是 苯醚甲环唑、腈菌唑、抑霉唑、戊唑醇中的任意两种，与嘧霉胺、 脱氢乙酸、脱氢乙酸钠中的任意一种和/或3-碘代-2-丙炔醇-丁基甲氨 酸酯、尼泊金乙酯、尼泊金丙酯、尼泊金丁酯、对氯间二甲苯酚中 的任意一种形成的复合物。
一种具体的优选技术方案是，将苯醚甲环唑、腈菌唑、抑霉 唑、戊唑醇中的任意一种(抗菌防霉剂A)与嘧霉胺、脱氢乙酸、 脱氢乙酸钠中的任意一种(抗菌防霉剂B)，以及3-碘代-2-丙炔醇- 丁基甲氨酸酯、尼泊金乙酯、尼泊金丙酯、尼泊金丁酯、对氯间二 甲苯酚中的任意一种(抗菌防霉剂C)按照质量比(0.9-3.5):(0.9- 3.5):1；如可以采用A：B：C＝(3-3.5)：(3-3.5)：1或者(1- 1.5)：(1-1.5)：1或者(0.9-1)：(0.9-1)：1的比例复配，与其他组分充分混合后，按照2％-6％的比例添加到漆中，漆的抗菌性、 防霉性、除醛性以及各方面的持久性表现更好。
复合氧化锌抗菌除醛材料为氧化石墨烯负载纳米氧化锌复合 物，制备方法是将市售氧化石墨烯分散液与纳米氧化锌复合物按质 量比20:(1-2)进行超声分散，加入螯合剂分散均匀，得到复合氧化 锌抗菌除醛材料。氧化石墨烯分散液与螯合剂的质量比为(20-35):1。
氧化石墨烯分散液的浓度为10mg/ml。氧化石墨烯分散液是将氧 化石墨烯分散在有机溶剂中形成的，有机溶剂可以是NMP、乙醇等 对氧化石墨烯具有良好分散效果的溶剂，同时这些溶剂的使用对多 效合一添加剂中其他成分的效果不产生明显的不良影响。
纳米氧化锌复合物是由水热法制备的片层花瓣状氧化锌和四针 状氧化锌晶须复合而成。片层花瓣状氧化锌和四针状氧化锌晶须的 质量比为3-4:1，在保证长效性的同时降低其成本。纳米氧化锌复合 物与甲醛清除剂配合不但能够提高甲醛清除能力，还能够使祛甲醛 添加剂具有长效祛甲醛的能力；纳米氧化锌复合物与抗菌防霉剂配 合不但能够提高抗菌防霉能力，还能够使抗菌防霉效果更持久。为 了配合抗菌防霉剂，特便是有机复合型抗菌防霉剂，使漆获得抗菌 防霉祛甲醛的长效性，将片层花瓣状氧化锌和四针状氧化锌晶须的 质量比设计为3-4:1。
螯合剂可以为柠檬酸钠、三聚磷酸钠、马来酸等中的一种或几 种。在制备复合氧化锌抗菌除醛材料的不同方案中，可以仅采用柠 檬酸钠为螯合剂，或者仅采用三聚磷酸钠为螯合剂，或者仅采用马 来酸为螯合剂，或者采用柠檬酸钠、三聚磷酸钠、马来酸三者之二复合为螯合剂，或者同时使用柠檬酸钠、三聚磷酸钠、马来酸三种 成分复配成螯合剂。通过螯合剂使纳米氧化锌复合物稳定地负载到 氧化石墨烯上。
除醛剂为2-咪唑烷酮、尿素、铵盐等中的一种或几种。如在多 效合一添加剂的不同方案中分别仅使用2-咪唑烷酮为除醛剂，仅使 用尿素为除醛剂，仅使用铵盐为除醛剂，或者在多效合一添加剂的 不同方案中使用2-咪唑烷酮与尿素合用为除醛剂，或者使用2-咪唑 烷酮和铵盐合用为除醛剂，或者使用尿素和铵盐合用为除醛剂，以 及还可以使用2-咪唑烷酮、尿素、铵盐三种成分复配成除醛剂。除 醛剂能够与甲醛反应，生成稳定的化合物。
多效合一添加剂中使用的溶剂为水、乙醇、丙二醇等中的一种 或几种。在多效合一添加剂的不同方案中，可以仅以水为溶剂，或 者仅以乙醇为溶剂，或者仅以丙二醇为溶剂，或者以一定体积分数 的乙醇水溶液为溶剂，或者以丙二醇、水为混合溶剂，或者以乙醇、丙二醇为混合溶剂。
家具漆用多效合一添加剂在木器漆里面的添加量为2-6wt％。这 里的添加量，是指质量，即每100g木器漆里面含有多效合一添加剂 2g至6g。在该添加范围内添加所述添加剂后，家具漆的抗细菌性能 可达到99％以上，抗霉菌性能可达到1级以上，抗细菌持久性能可保 持在95％以上、抗霉菌持久性能可保持在1级以上，甲醛净化效率可 达85％，甲醛净化效果持久性可保持在81％以上。并且在2-6％的添 加范围内，使用量越低，经济效益越高，使用量越高，抗菌性能、 除甲醛性能及效果持久性越好。使用低于2％的添加剂，将导致性能 中的一项或者多项明显下滑而不能体现家具漆的优势，使用高于6％ 的添加剂对各项性能并没有显著的提升，但由于成本显著升高，影 响家具漆的经济效益。
所述的木器漆包括水性漆、PU漆(即聚氨酯涂料)、UV漆 (即光固化涂料)、NC漆(硝基漆)。本发明在进行实施例和对比 例的效果验证时，使用的水性漆、PU漆、UV漆、NC漆分别是立邦 净味120水性木器漆、紫荆花PU木器漆、百川UV辊涂面漆、长颈鹿 硝基清面漆。在水性漆、PU漆、UV漆、NC漆中添加家具漆用多效 合一添加剂时(假如使用配方完全相同的添加剂)，在达到相同的 抗菌防霉除甲醛综合效果的情形下，在2-6％添加范围内，水性漆添 加量最小，NC漆添加量最大，PU、UV添加量居中。
所述的家具漆用多效合一添加剂的制备方法是将抗菌防霉剂10- 25质量份、复合氧化锌抗菌除醛材料5-8质量份、除醛剂22-40质量 份、溶剂30-60质量份混合均匀即得。
所述的家具漆用多效合一添加剂的应用方法是将家具漆用多效 合一添加剂添加到木器漆中，添加量为2-6wt％。
上述家具漆用多效合一添加剂采用抗菌防霉剂、除醛剂、复合 氧化锌抗菌除醛材料按照特定的比例进行复配。在抗菌防霉方面， 通过有机抗菌防霉剂快速破坏细菌细胞结构，辅以复合氧化锌材料 使之达到长效抗菌防霉的作用；在除醛方面，通过有机除醛剂快速 与甲醛发生反应，生成稳定的化合物，辅以复合氧化锌材料使之达 到长效除醛的作用。其使用方便，添加量较低。此添加剂可一定程 度上对家具周围的甲醛等污染物进行分解，从而改善家具周围的空 气质量。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结 合实施例，对本发明进行进一步详细说明。应当理解，此处所描述 的具体实施例仅仅用以解释本发明，并不用于限定本发明。
一、复合氧化锌抗菌除醛材料的制备
(一)复合氧化锌抗菌除醛材料A
将水热法制备的片层花瓣状氧化锌和四针状氧化锌晶须按照质 量比为3:1在乙醇和水的混合溶液中超声分散均匀，得到纳米氧化锌 复合物。其中混合溶液中乙醇和水的比例为1:1。
将市售氧化石墨烯分散液(浓度为10mg/ml)与所述的纳米氧化 锌复合物按质量比20:1进行超声分散，加入螯合剂柠檬酸钠分散均 匀，氧化石墨烯分散液与螯合剂的质量比为20:1，得到复合氧化锌 抗菌除醛材料A，这是本发明各实施例使用的复合氧化锌抗菌除醛 材料。
(二)复合氧化锌抗菌除醛材料B
将水热法制备的片层花瓣状氧化锌和四针状氧化锌晶须按照质 量比为10:1在乙醇和水的混合溶液中超声分散均匀，得到纳米氧化 锌复合物。其中混合溶液中乙醇和水的比例为1:1。
将市售氧化石墨烯分散液(浓度为10mg/ml)与纳米氧化锌复合 物按质量比20:1进行超声分散，加入螯合剂柠檬酸钠分散均匀，氧 化石墨烯分散液与螯合剂的质量比为20:1得到复合氧化锌抗菌除醛 材料B，由于片层花瓣状氧化锌和四针状氧化锌晶须的质量比不满 足本发明技术方案的要求，复合氧化锌抗菌除醛材料B仅用于对比 实施例。
二、添加剂以及漆的制备
实施例1-10使用复合氧化锌抗菌除醛材料A，对比例1不使用复 合氧化锌抗菌除醛材料，对比例2-3、6-7都使用复合氧化锌抗菌除 醛材料A，对比例4使用复合氧化锌抗菌除醛材料B，对比例5使用纳 米氧化锌复合物代替复合氧化锌抗菌除醛材料A。
实施例1
对氯间二甲苯酚3份，脱氢乙酸钠10份，戊唑醇10份，复合氧化 锌抗菌除醛材料A6份，2-咪唑烷酮32份，水39份。将各原料组分溶 于溶剂、搅拌均匀，即得多效合一添加剂成品。在水性漆中添加2％ 的多效合一添加剂，混合均匀后即得抗菌防霉除醛水性漆。
实施例2
腈菌唑3份，抑霉唑7份，脱氢乙酸7份，3-碘代-2-丙炔醇-丁基 甲氨酸酯7份，复合氧化锌抗菌除醛材料A 6份，2-咪唑烷酮31份， 乙醇30份，丙二醇9份。将各原料组分溶于溶剂、搅拌均匀，即得成 品。在PU漆中添加4％的多效合一添加剂，混合均匀后即得抗菌防霉除醛PU漆。
实施例3
苯醚甲环唑7份，嘧霉胺7份，尼泊金丁酯7.5份，复合氧化锌抗 菌除醛材料A 6份，硝酸铵28份，乙醇31份。将各原料组分溶于溶 剂、搅拌均匀，即得成品。在UV漆中添加3％的多效合一添加剂， 混合均匀后即得抗菌防霉除醛UV漆。
实施例4
苯醚甲环唑8份，抑霉唑8份，对氯间二甲苯酚7份，复合氧化锌 抗菌除醛材料A 6份，尿素32份，丙二醇39份。将各原料组分溶于溶 剂，搅拌均匀，即得成品。在NC漆中添加6％的多效合一添加剂， 混合均匀后即得抗菌防霉除醛NC漆。
实施例5
嘧霉胺11份，尼泊金丁酯11.5份，复合氧化锌抗菌除醛材料A 6 份，硝酸铵28份，乙醇31份。将各原料组分溶于溶剂、搅拌均匀， 即得成品。在UV漆中添加3％的多效合一添加剂，混合均匀后即得 抗菌防霉除醛UV漆。
实施例6
苯醚甲环唑3份，嘧霉胺9份，尼泊金丁酯9.5份，复合氧化锌抗 菌除醛材料A 6份，硝酸铵28份，乙醇31份。将各原料组分溶于溶 剂、搅拌均匀，即得成品。在UV漆中添加3％的多效合一添加剂， 混合均匀后即得抗菌防霉除醛UV漆。
实施例7
苯醚甲环唑11份，尼泊金丁酯11.5份，复合氧化锌抗菌除醛材 料A 6份，硝酸铵28份，乙醇31份。将各原料组分溶于溶剂、搅拌均 匀，即得成品。在UV漆中添加3％的多效合一添加剂，混合均匀后 即得抗菌防霉除醛UV漆。
实施例8
脱氢乙酸钠23份，复合氧化锌抗菌除醛材料A 6份，2-咪唑烷酮 32份，水39份。将各原料组分溶于溶剂、搅拌均匀，即得成品。在 水性漆中添加2％的多效合一添加剂，混合均匀后即得抗菌防霉除醛 水性漆。
实施例9
对氯间二甲苯酚1份，脱氢乙酸钠4.5份，戊唑醇4.5份，复合氧 化锌抗菌除醛材料A 6份，2-咪唑烷酮32份，水39份。将各原料组分 溶于溶剂、搅拌均匀，即得成品。在水性漆中添加2％的多效合一添 加剂，混合均匀后即得抗菌防霉除醛水性漆。
实施例10
对氯间二甲苯酚3份，脱氢乙酸钠10份，戊唑醇10份，复合氧化 锌抗菌除醛材料A6份，2-咪唑烷酮22份，水39份。将各原料组分溶 于溶剂、搅拌均匀，即得成品。在水性漆中添加2％的多效合一添加 剂，混合均匀后即得抗菌防霉除醛水性漆。
对比例1
未使用复合氧化锌抗菌除醛材料。苯醚甲环唑7份，嘧霉胺7 份，尼泊金丁酯7.5份，硝酸铵28份，乙醇31份。将各原料组分溶于 溶剂、搅拌均匀，即得成品。将成品与UV漆按比例(3％)混合均 匀后，即得对比例产品1。
对比例2
未使用抗菌防霉剂。复合氧化锌抗菌除醛材料A 6份，硝酸铵28 份，乙醇31份。将各原料组分溶于溶剂、搅拌均匀，即得成品。将 成品与UV漆按比例(3％)混合均匀后，即得对比例产品2。
对比例3
未使用除醛剂。苯醚甲环唑7份，嘧霉胺7份，尼泊金丁酯7.5 份，复合氧化锌抗菌除醛材料A 6份，乙醇31份。将各原料组分溶于 溶剂、搅拌均匀，即得成品。将成品与UV漆按比例(3％)混合均 匀后，即得对比例产品3。
对比例4
苯醚甲环唑7份，嘧霉胺7份，尼泊金丁酯7.5份，复合氧化锌抗 菌除醛材料B 6份，硝酸铵28份，乙醇31份。将各原料组分溶于溶 剂、搅拌均匀，即得成品。将成品与UV漆按比例(3％)混合均匀 后，即得对比例产品4。
对比例5
苯醚甲环唑7份，嘧霉胺7份，尼泊金丁酯7.5份，复合氧化锌抗 菌除醛材料A中使用的纳米氧化锌复合物6份(代替复合氧化锌抗 菌除醛材料A)，硝酸铵28份，乙醇31份。将各原料组分溶于溶 剂、搅拌均匀，即得成品。将成品与UV漆按比例(3％)混合均匀 后，即得对比例产品5。
对比例6
对氯间二甲苯酚3份，脱氢乙酸钠10份，戊唑醇10份，复合氧化 锌抗菌除醛材料A6份，2-咪唑烷酮32份，水39份。将各原料组分溶 于溶剂、搅拌均匀，即得成品。将成品按1％与水性漆混合，即得对 比例产品6。
对比例7
对氯间二甲苯酚3份，脱氢乙酸钠10份，戊唑醇10份，复合氧化 锌抗菌除醛材料A6份，2-咪唑烷酮32份，水39份。将各原料组分溶 于溶剂、搅拌均匀，将各原料组分溶于溶剂、搅拌均匀，即得成 品。将成品按7％与水性漆混合，即得对比例产品7。
对比例8
未添加抗菌防霉除醛多效合一添加剂的UV漆。
各实施例与对比例样品抗细(霉)菌性能、抗细(霉)菌耐久 性能、甲醛净化性能、甲醛净化效果持久性检测标准分别是：抗菌 性能检测标准为HG/T 3950-2007《抗菌涂料》、甲醛净化性能检 测标准为JC/T 1074-2008《室内空气净化功能涂覆材料净化性 能》。
其中抗细菌、霉菌耐久性能检测按HG/T 3950-2007《抗菌涂 料》6.6抗菌耐久性能测试要求进行：将样品放置于指定波长、瓦数 的紫外灯下，照射100h后，按抗细菌、霉菌性能测试。
甲醛净化性能持久性检测按JC/T 1074-2008《室内空气净化功 能涂覆材料净化性能》6.6净化效果持久性测试要求进行：将经过饱 和实验的样品再次进行甲醛净化效率测试。
检测结果见表1至表3所示。
表1实施例和对比例的样品的抗细菌性能
表2实施例和对比例的样品的抗霉菌性能
表3实施例和对比例的样品的甲醛净化性能
整个检测过程中均未提供额外光照条件。由以上检测结果可见， 实施例1至实施例4具有较好的抗菌、防霉、祛甲醛性能，同时具有 较好的持久性。实施例5-8因使用的抗菌防霉剂配比与实施例1-4不 同，因此在抗菌防霉效果及持久性方面略有差异，但也能达到较好的 抗菌、防霉、祛甲醛的性能。实施例9-10分别使用了较少的抗菌防 霉剂和除醛剂，因此抗菌防霉性能或者除醛性能与实施例1-8略有降 低，根据抗菌防霉祛甲醛的级别要求，也可以选择性使用。
对比例1因未使用复合氧化锌抗菌除醛材料而导致抗菌、防霉、 祛甲醛性能降低，特别是持久性明显变差。对比例2由于未使用抗菌 防霉剂，所以抗菌、防霉性能变差，但由于使用了复合氧化锌抗菌除 醛材料，其持久性比对比例1明显更高。对比例3由于未使用复合除 醛剂，所以祛甲醛效率和祛甲醛持久性变差，但由于使用了复合氧化 锌抗菌除醛材料，其祛甲醛持久性比对比例1明显更高，对其抗菌、 防霉性能影响较小或者无影响。对比例4使用复合氧化锌抗菌除醛材 料B，因水热法制备的片层花瓣状氧化锌和四针状氧化锌晶须按照质 量比为10:1配制，与复合氧化锌抗菌除醛材料A的比例3-4:1形成 明显的差异，从效果来看，除醛性能、抗菌性能和持久性能有一定程 度的降低；对比例5使用纳米氧化锌复合粉代替了复合氧化锌抗菌除 醛材料A，其性能也有一定程度的降低。对比例6和对比例7使用不 同的添加量，性能有差异，当添加量降低时，抗菌防霉祛甲醛的综合 性能下降，当添加量上升时，抗菌防霉祛甲醛的综合性能有一定的提 升，但最优添加范围为2-6％，低于2％则使综合性能明显下降，高于 6％虽使综合性能小幅度变得优化，但是成本明显上升，并不经济，说 明不同添加量会对效果有影响，2-6％的添加量不但满足综合性能需求，也满足商品的经济性要求。对比例8为空白组，其不具备抗菌、 防霉、除甲醛性能。
尽管这里参照本发明的解释性实施例对本发明进行了描述，但是， 应该理解，本领域技术人员可以设计出很多其他的修改和实施方式， 这些修改和实施方式将落在本申请公开的原则范围和精神之内。更具 体地说，在本申请公开的范围内，可以对主题组合布局的组成部件和 /或布局进行多种变型和改进。除了对组成部件和/或布局进行的变型 和改进外，对于本领域技术人员来说，其他的用途也将是明显的。
Claims (10)
1.家具漆用多效合一添加剂，其特征在于，包括如下按质量份计量的各组分：抗菌防霉剂10-25份，复合氧化锌抗菌除醛材料5-8份，除醛剂22-40份，溶剂30-60份。
2.根据权利要求1所述的家具漆用多效合一添加剂，其特征在于，包括如下按质量份计量的各组分：抗菌防霉剂20-25份，复合氧化锌抗菌除醛材料5-8份，除醛剂27-35份，溶剂30-60份。
3.根据权利要求1所述的家具漆用多效合一添加剂，其特征在于，所述抗菌防霉剂选自苯醚甲环唑、腈菌唑、嘧霉胺、抑霉唑、戊唑醇、3-碘代-2-丙炔醇-丁基甲氨酸酯、尼泊金乙酯、尼泊金丙酯、尼泊金丁酯、对氯间二甲苯酚、脱氢乙酸、脱氢乙酸钠中的一种或几种；所述复合氧化锌抗菌除醛材料为氧化石墨烯负载纳米氧化锌复合物。
4.根据权利要求1所述的家具漆用多效合一添加剂，其特征在于，所述除醛剂为2-咪唑烷酮、尿素、铵盐中的一种或几种。
5.根据权利要求3所述的家具漆用多效合一添加剂，其特征在于，所述抗菌防霉剂是由抗菌防霉剂A、抗菌防霉剂B、抗菌防霉剂C按照质量比(0.9-3.5):(0.9-3.5):1复配而得的有机复合型抗菌防霉剂，所述抗菌防霉剂A选自苯醚甲环唑、腈菌唑、抑霉唑、戊唑醇中的任意一种，所述抗菌防霉剂B选自嘧霉胺、脱氢乙酸、脱氢乙酸钠中的任意一种，所述抗菌防霉剂C选自3-碘代-2-丙炔醇-丁基甲氨酸酯、尼泊金乙酯、尼泊金丙酯、尼泊金丁酯、对氯间二甲苯酚中的任意一种。
6.根据权利要求5所述的家具漆用多效合一添加剂，其特征在于，所述抗菌防霉剂A、抗菌防霉剂B、抗菌防霉剂C按照质量比(3-3.5)：(3-3.5)：1复配，或者按照质量比(1-1.5)：(1-1.5)：1复配，或者按照质量比(0.9-1)：(0.9-1)：1复配。
7.根据权利要求3所述的家具漆用多效合一添加剂，其特征在于，所述氧化石墨烯负载纳米氧化锌复合物的制备方法是：将市售氧化石墨烯分散液与纳米氧化锌复合物按质量比20:(1-2)进行超声分散，加入螯合剂分散均匀而得；所述氧化石墨烯分散液的浓度为10mg/ml，所述氧化石墨烯分散液与螯合剂的质量比为(20-35):1，所述螯合剂选自柠檬酸钠、三聚磷酸钠、马来酸中的一种或几种。
8.根据权利要求7所述的家具漆用多效合一添加剂，其特征在于，所述纳米氧化锌复合物是由水热法制备的片层花瓣状氧化锌和四针状氧化锌晶须复合而成，片层花瓣状氧化锌和四针状氧化锌晶须的质量比为3-4:1。
9.权利要求1-8任意一项所述的家具漆用多效合一添加剂的制备方法，其特征在于，将抗菌防霉剂10-25质量份、复合氧化锌抗菌除醛材料5-8质量份、除醛剂22-40质量份、溶剂30-60质量份混合均匀即得。
10.权利要求1-8任意一项所述的家具漆用多效合一添加剂的应用方法，其特征在于将家具漆用多效合一添加剂添加到木器漆中，添加量为2-6wt％。