CN113582193A - 一种改性β沸石、催化裂化催化剂及其制备方法和应用 - Google Patents
一种改性β沸石、催化裂化催化剂及其制备方法和应用 Download PDFInfo
- Publication number
- CN113582193A CN113582193A CN202010367845.XA CN202010367845A CN113582193A CN 113582193 A CN113582193 A CN 113582193A CN 202010367845 A CN202010367845 A CN 202010367845A CN 113582193 A CN113582193 A CN 113582193A
- Authority
- CN
- China
- Prior art keywords
- beta zeolite
- zeolite
- modified beta
- modified
- catalytic cracking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本公开涉及一种改性β沸石、催化裂化催化剂及其制备方法和应用,以改性β沸石的干基重量为基准,改性β沸石含有以氧化物计的0.5‑15重量%的IVB族金属元素,所述改性β沸石中等强度酸中心数量占总酸量的30‑60%,强酸中心数量占总酸量的5‑25%,B酸与L酸的比值为0.8以上,改性β沸石体相的IVB族金属元素的重量含量与表面的IVB族金属元素的重量含量的比值为0.1‑0.8。含有本发明的改性β沸石的催化裂化催化剂具有良好的碳四烯烃的选择性和产率。
Description
技术领域
本发明涉及一种改性β沸石、催化裂化催化剂及其制备方法和应用。
背景技术
随着环保意识的增强,车用汽油质量标准不断升级换代。车用汽油新标准暨GB17930-2016明确规定从2019年起将在全国范围分阶段实施国Ⅵ标准汽油,与国Ⅴ标准相比,国Ⅵ标准下汽油的苯、芳烃、烯烃含量都将降低,目前我国汽油调和组分方案已难以满足要求。由于烷基化汽油辛烷值高,烯烃、芳烃、苯含量为零,在国Ⅵ标准下,相对传统的催化汽油和重整汽油,是很好的汽油调和组分,在汽油调和组分中的比例将会大幅提高。烷基化装置的主要原料是异丁烷和碳四烯烃。全球近70%的碳四烯烃来自催化裂化装置,并且由催化裂化装置生产碳四烯烃馏分技术具有投资少、成本低的优势,不少公司试图从催化裂化过程获取更大量的碳四烯烃产率。
为了增产低碳烯烃,通常在催化剂中加入择形分子筛。美国Engelhard公司于1993年首次在美国专利USP5243121中公开了增产异丁烯和异戊烯的裂化催化剂,通过水热处理来降低裂化催化剂中Y沸石的晶胞尺寸,可以提高催化剂在烃裂化时对产品中烯烃的选择性,催化剂中还可以加入相当量的ZSM-5沸石作为助剂,不但可以降低生焦量,而且可以提高活性。US3758403公开了以ZSM-5和大孔沸石(主要是Y型沸石)为活性组元的催化剂,在提高汽油辛烷值的同时也增加了C3、C4烯烃的产率,其中大孔沸石对原料进行裂化生成汽油、柴油,ZSM-5择形分子筛进一步将其裂化成低碳烯烃。
β沸石由Mobil公司的Wadlinger等于1967年首次合成,到1988年Higgins等揭示了其特有的三维结构特征,它是唯一一种具有交叉十二元环通道体系的高硅沸石,平行于(001)晶面的一维孔道的12元环孔径为0.75~0.57nm,另一个与(100)晶面平行的二维孔道的12元环孔径为0.65~0.56nm。由于其结构的特殊性,兼具酸催化特性和结构选择性,近年来已迅速发展为一种新型的催化材料。β沸石在使用中的主要问题是:一方面在脱除模板剂的过程中容易使其结构受到损害,另一方面是在反应过程中容易脱铝使活性稳定性变差。因此,关于β沸石的改性有许多研究报道。
CN103771437A公开了一种含磷的改性β分子筛,以P2O5计磷含量占3-10重%,该分子筛的27Al MAS NMR中,化学位移为40±3ppm共振信号峰面积与化学位移为54ppm±3ppm共振信号峰面积之比大于等于1。该分子筛中磷与骨架铝配位充分,骨架铝得到充分保护,具有优异的水热稳定性和更好的产品选择性。
CN1179994A公开了一种β沸石的改性方法,将Naβ沸石用铵离子交换至沸石上的Na2O含量小于0.1重%;然后将上述铵交换的β沸石用酸处理抽去部分骨架铝,使其硅铝比大于50;将上述脱铝后的β沸石与磷酸或磷酸盐混合均匀后烘干,使所得沸石上P2O5的量为2~5重%;最后将所得产物在水蒸汽气氛下于450~650℃水热焙烧0.5~4小时。通过该方法改性后的β沸石在用于烃类的裂化反应时可以得到较高的烯烃,尤其是异构烯烃的产率以及较低的焦炭产率。
CN105621432A公开了一种改性β分子筛及其制备方法,对铵交换后的β分子筛进行预处理、干燥,进行积炭反应,高温焙烧处理,然后经脱铝处理、干燥、烧炭处理,得到改性β分子筛;改性β分子筛体相硅铝比为30~80,其中表面层硅铝比50~130,表面层硅铝比高于体相硅铝比30~70;比表面积400~800m2/g,孔容0.2~0.60ml/g;红外酸含量0.1~0.6mmol/g;相对结晶度100%~150%。本发明分子筛表面层的硅铝比要高于体相硅铝比,加氢裂化反应过程中有广阔的应用前景。
CN107899607A提供了一种改性β分子筛及其制备方法和应用。该催化剂是方法包括以β分子筛为基体,以金属元素为改性剂,利用金属元素可溶盐的溶液,采用离子交换法制备得到改性β分子筛;金属元素选自Cu、Al、Zn、Fe和Sn中的一种或多种的混合;金属元素在制得的改性β分子筛中的质量含量为0.5-4%。
将β沸石应用于催化裂化催化剂生产低碳烯烃的报道也很多。美国专利US4837396公开了一种含有β沸石和Y沸石的催化剂,将含有金属离子型化合物作为稳定剂提高催化剂的水热稳定和机械强度。该稳定剂可以直接与β沸石作用,也可以在制备过程中引入。
CN1055105C公开了一种多产异丁烯和异戊烯的裂化催化剂,含有磷和稀土的五元环高硅沸石6~30重%,USY沸石5~20重%,β沸石1~5重%,粘土30~60重%和无机氧化物15~30重%,该催化剂在催化裂化的工艺条件下具有多产异丁烯和异戊烯的特点,同时可联产高辛烷值汽油。
CN107971003A公开了一种含有磷和负载金属的Beta分子筛的催化裂化助剂及其制备方法,助剂含有以干基计的10-75重量%的含有含磷和负载金属的Beta分子筛、以干基计的0-60重量%的粘土、以干基计的15-60重量%的无机氧化物粘结剂、以P2O5计的0-25重量%的磷添加剂和以氧化物计的0-15重量%的Ⅷ族金属添加剂,其中,分子筛的Al分布参数D满足:0.4≤D≤0.8;分子筛的微孔比表面积为420-520m2/g,分子筛的介孔体积占总孔体积的比例为30-70%;分子筛的强酸酸量占总酸量的比例为65-80%,B酸酸量与L酸酸量之比为25-90。将该助剂应用于催化裂化能够提高异丁烯和丙烯的产率,提高汽油辛烷值,但是液化气中总丁烯浓度提高不显著。
CN104998681A公开了一种提高低碳烯烃浓度的催化裂化助剂及其制备方法,该助剂包括硼改性的含磷和金属的β分子筛、无机氧化物粘结剂、VIII族金属添加剂、磷添加剂以及任选的粘土。该催化裂化助剂应用于石油烃的催化裂化,能增加催化裂化液化气中异丁烯的浓度,减少焦炭的产量。
CN107971000A公开了一种含有含磷Beta分子筛的催化裂化助剂及其制备方法,该助剂含有以干基计的10-75重量%的含磷Beta分子筛,以干基计的0-60重量%的粘土、以干基计的15-60重量%的无机氧化物粘结剂、以P2O5计的0-25重量%的磷添加剂和以氧化物计的0-15重量%的Ⅷ族金属添加剂。该助剂应用于催化裂化能够提高异丁烯和丙烯的产率,提高汽油辛烷值。
将上述技术制备的各种催化剂/助剂用于催化裂化过程中,可以在一定程度上实现增产低碳烯烃的目的,但还存在以下问题:一是在增加丙烯和丁烯的同时,液化气产率也增加,导致液化气中丙烯或者丁烯的浓度变化不大;另一方面,在增加丁烯的同时,丙烯产率也增加,导致丁烯的选择性变差。
从催化裂化过程碳四烯烃的生成和转化机理分析,催化裂化过程碳四烯烃的生成主要来自两个方面,一是原料中烃类大分子经单分子裂化反应或双分子裂化反应生成的活性中间体进行裂化的产物,二是裂化反应中形成的低碳数烯烃进行二次反应的产物。催化裂化过程中生成的碳四烯烃可进一步发生裂化反应、异构反应、二聚反应和氢转移反应。
发明内容
本发明的目的是提供一种改性β沸石、催化裂化催化剂及其制备方法和应用,本发明的催化裂化催化剂具有良好的碳四烯烃选择性和产率。
为了实现上述目的,本发明第一方面提供一种改性β沸石,以所述改性β沸石的干基重量为基准,所述改性β沸石含有以氧化物计的0.5-15重量%的IVB族金属元素,所述改性β沸石中等强度酸中心数量占总酸量的30-60%,强酸中心数量占总酸量的5-25%,B酸与L酸的比值为0.8以上,所述改性β沸石体相的IVB族金属元素的重量含量与表面的IVB族金属元素的重量含量的比值为0.1-0.8。
可选地,所述B酸与所述L酸的比值为1.0-1.5。
可选地,所述中等强度酸中心数量占所述总酸量的35-55%。
可选地,所述强酸中心数量占所述总酸量的5-20%。
可选地,以所述改性β沸石的干基重量为基准,所述改性β沸石含有以氧化物计的1-12重量%的IVB族金属元素。
可选地,所述IVB族金属元素为Zr和/或Ti,优选为Zr;所述Zr元素的重量以ZrO2计,所述Ti元素的重量以TiO2计。
可选地,所述改性β沸石体相的IVB族金属元素的重量含量与表面的IVB族金属元素的重量含量的比值为0.1-0.6。
本发明第二方面提供一种催化裂化催化剂,以所述催化裂化催化剂的干基重量为基准,所述催化裂化催化剂含有20-50重量%的Y型沸石、2-40重量%的改性β沸石、10-70重量%的粘土和5-60重量%的耐热无机氧化物,所述改性β沸石为本发明第一方面提供的改性β沸石。
可选地,所述Y型沸石选自含磷和/或稀土的Y型沸石、超稳Y沸石,以及,含磷和/或稀土的超稳Y沸石中的一种或几种;
所述粘土选自高岭土、累托土、硅藻土、蒙脱土、膨润土和海泡石中的一种或者几种;
所述耐热无机氧化物选自氧化铝、氧化硅和无定型硅铝中的一种或几种。
可选地,所述催化裂化催化剂含有30-45重量%的所述Y型沸石、5-30重量%的所述改性β沸石、10-50重量%的所述粘土和5-40重量%的所述耐热无机氧化物。
本发明第三方面提供一种制备本发明第一方面提供的改性β沸石的方法,该方法包括:
(1)将含IVB族金属的化合物、碳源和第一溶剂混合,调节混合物pH值为4-9,得到第一浆料;所述碳源包括天然高分子有机化合物和/或半合成高分子有机化合物;
(2)将所述第一浆料和β沸石在20-100℃下搅拌混合10-180min,取出固体在350-650℃下进行第一焙烧0.5-5小时。
步骤(2)中,调节所述第一浆料的pH值为5-8。
可选地,所述含IVB族金属的化合物和所述β沸石用量的重量比为(0.005-0.15):1,所述β沸石和所述碳源用量的重量比为1:(0.001-0.15),所述含IVB族金属的化合物以IVB族金属的氧化物计,所述β沸石以干基重量计。
可选地,所述β沸石选自氢型β沸石、钠型β沸石、含磷的β沸石、含稀土金属的β沸石,以及,含有磷和稀土金属的β沸石中的一种或几种;
所述碳源选自淀粉、木质素、粘胶纤维、甲基纤维素、羟丙基甲基纤维素、羟乙基纤维素和羧甲基纤维素中的一种或几种;
所述含IVB族金属的化合物选自四氯化锆、醋酸锆、异丙醇锆、四氯化钛、硫酸氧钛、氟钛酸铵、硫酸锆、硝酸锆、氧氯化锆、硫酸钛、钛酸四丁酯、三氯化钛和硫酸亚钛中的一种或几种;
所述第一溶剂选自去离子水、乙醇、丙酮和正己烷中的一种或几种。
本发明第四方面提供一种制备本发明第二方面提供的催化裂化催化剂的方法,该方法包括:将所述Y型沸石、本发明第一方面提供的改性β沸石、所述粘土、所述耐热无机氧化物和第二溶剂混合,将得到的第二浆料进行造粒,并进行干燥和/或第二焙烧。
可选地,所述干燥的温度为80-200℃,时间为0.5-24小时;所述第二焙烧的温度为350-700℃,时间为0.5-5小时。
本发明第五方面提供一种本发明第一方面提供的所述改性β沸石或本发明第二方面提供的催化裂化催化剂在重质油催化裂化中的应用。
通过上述技术方案,本发明的改性β沸石具有优异的酸分布和IVB族金属分布,含有该改性β沸石的催化裂化催化剂具有良好催化性能,将其用于重质油的催化裂化过程时,重油的裂化性能优异,可以在汽油和液化气产率不减少的情况下,提高液化气中碳四烯烃的浓度,增加碳四烯烃的产率和选择性。
本发明的方法简单,可以改善IVB族金属氧化物在β沸石上的分布状态和分布量,调整β沸石的孔道分布,能够制备得到具有良好物化性质的改性β沸石。
本公开的其他特征和优点将在随后的具体实施方式部分予以详细说明。
具体实施方式
以下对本公开的具体实施方式进行详细说明。应当理解的是,此处所描述的具体实施方式仅用于说明和解释本公开,并不用于限制本公开。
本发明第一方面提供一种改性β沸石,以改性β沸石的干基重量为基准,改性β沸石含有以氧化物计的0.5-15重量%,例如2-13.5重量%的IVB族金属元素,改性β沸石中等强度酸中心数量占总酸量的30-60%例如30-50%,强酸中心数量占总酸量的5-25%例如10-25%,B酸与L酸的比值为0.8以上例如0.9-1.5,改性β沸石体相的IVB族金属元素的重量含量与表面的IVB族金属元素的重量含量的比值为0.1-0.8例如为0.15-0.45。
与传统β沸石相比,本发明的改性β沸石其具有优异的酸性分布和B酸与L酸比值,并且中等强度酸中心的数量增多,优化了催化裂化反应过程中碳正离子的异构化反应与裂化反应的比值,有利于催化裂化过程生成的C6~C10烯烃先进行异构化反应再进行β位断裂反应,提高了碳四烯烃的选择性;同时改性β沸石具有优异的重油裂化能力。
根据本发明,IVB族金属元素可以为Zr和/或Ti,优选为Zr;Zr元素的重量以ZrO2计,Ti元素的重量以TiO2计。根据本发明,β沸石表面的IVB族金属元素可以以IVB族金属氧化物的形式存在。在一种优选的具体实施方式中,IVB族金属氧化物为ZrO2和/或TiO2,更优选为ZrO2。
在一种优选的具体实施方式中,以改性β沸石的干基重量为基准,改性β沸石含有1-12重量%的IVB族金属元素例如2-12重量%,中等强度酸中心数量占总酸量的35-55例如35-50%或35-45%,强酸中心数量占总酸量的5-20%例如10-20%,B酸与L酸的比值为0.8以上例如1.0-1.5或1.1-1.5,改性β沸石体相的IVB族金属元素的重量含量与表面的IVB族金属元素的重量含量的比值为0.1-0.6例如为0.15-0.45。
本发明第二方面提供一种催化裂化催化剂,以催化裂化催化剂的干基重量为基准,催化裂化催化剂含有20-50重量%的Y型沸石、2-40重量%的改性β沸石、10-70重量%的粘土和5-60重量%的耐热无机氧化物,改性β沸石为本发明第一方面提供的改性β沸石。
本发明的发明人发现,将Y沸石和改性β沸石相配合可以促进重油大分子的裂化过程,降低油浆和柴油产率、提高汽油产率,为多产碳四烯烃提供更多的潜在组分,进一步增加碳四烯烃的选择性。将本发明的催化裂化催化剂用于重质油的催化裂化过程时,可以在汽油和液化气产率不减少的情况下,提高液化气中碳四烯烃的浓度,增加碳四烯烃的产率和选择性。
在一种优选的具体实施方式中,催化裂化催化剂含有30-45重量%的Y型沸石、5-30重量%的改性β沸石、10-50重量%的粘土和5-40重量%的耐热无机氧化物。
根据本发明,耐热无机氧化物可以选自用作催化裂化催化剂基质和/或粘结剂组分的耐热无机氧化物,如氧化铝、氧化硅和无定型硅铝中的一种或几种,这些耐热无机氧化物本身及其制备方法为本领域人员所公知。
根据本发明,Y型沸石、粘土为本领的技术人员所熟知的,例如,Y型沸石可以选自含磷和/或稀土的Y型沸石、超稳Y沸石,以及,含磷和/或稀土的超稳Y沸石中的一种或几种;粘土可以选自高岭土、累托土、硅藻土、蒙脱土、膨润土和海泡石中的一种或者几种。
本发明第三方面提供一种制备本发明第一方面提供的改性β沸石的方法,该方法包括:
(1)将含IVB族金属的化合物、碳源和第一溶剂混合,调节混合物pH值为4-9,得到第一浆料;碳源包括天然高分子有机化合物和/或半合成高分子有机化合物;
(2)将第一浆料和β沸石在20-100℃下搅拌混合10-180min,取出固体在350-650℃下进行第一焙烧0.5-5小时。
其中,对第一焙烧的氛围不做具体限制,例如可以为空气气氛和/或惰性气氛,惰性气氛中的惰性气体选自氮气、氦气和氩气中的一种或几种。对步骤(1)中进行混合的温度和时间也不做具体限制,例如可以在40-90℃下混合30-120分钟。对取出固体的方式也不做具体限制,例如可以采用过滤或者烘干的方法,优选采用过滤的方法。
根据本发明,含IVB族金属的化合物和β沸石用量的重量比可以为(0.005-0.15):1,β沸石和碳源用量的重量比可以为1:(0.001-0.15),含IVB族金属的化合物以IVB族金属的氧化物计,β沸石以干基重量计;优选地,含IVB族金属的化合物和β沸石用量的重量比为(0.01-0.12):1,β沸石和碳源用量的重量比为1:(0.005-0.10);更优选地,含IVB族金属的化合物为含Zr的化合物和/或含Ti的化合物。
根据本发明,碳源可以为有机高分子化合物,例如为天然高分子化合物和/或半合成高分子化合物;在一种具体实施方式中,碳源可以选自淀粉、木质素、粘胶纤维、甲基纤维素、羟丙基甲基纤维素、羟乙基纤维素和羧甲基纤维素中的一种或几种。以上述高分子有机化合物和/或半合成高分子有机化合物制备得到的改性β沸石表面的IVB族金属元素的重量含量高于体相的IVB族金属元素的重量含量,改性β沸石具有较优的催化性能,将其用重质油的催化裂化过程时,可以在汽油和液化气产率不减少的情况下,提高液化气中碳四烯烃的浓度,增加碳四烯烃的产率和选择性。
根据本发明,含IVB族金属的化合物中的IVB族金属可以为钛和/或锆,在一种具体实施方式中,含IVB族金属的化合物可以选自四氯化锆、硫酸锆、硝酸锆、氧氯化锆、醋酸锆、异丙醇锆、四氯化钛、硫酸氧钛、氟钛酸铵、硫酸钛、钛酸四丁酯、三氯化钛和硫酸亚钛中的一种或几种。对第一溶剂的种类不做具体限制,只要是能够将含IVB族金属的化合物溶解,并使β沸石分散即可,例如可以选自去离子水、乙醇、丙酮和正己烷中的一种或几种。
根据本发明,β沸石为本领域的技术人员所熟知,例如可以选自氢型β沸石、钠型β沸石、含磷的β沸石、含稀土金属的β沸石,以及,含磷和稀土金属的β沸石中的一种或几种,优选为氢型β沸石和含磷的β沸石。
根据本发明,步骤(1)中,可以调节所述第一浆料的pH值为5-8,优选地,调节第一浆料的pH值为6-8。对调节pH值的方式不做具体限制,例如可以通过加入碱性溶液来调节第一浆料的pH值,碱性溶液可以为氨水、水玻璃水溶液、偏铝酸钠水溶液和氢氧化钠水溶液中的一种或几种,优选为氨水。碱性溶液的浓度可以在较大的范围内变化,在一种具体实施方式中,碱性溶液以OH-计的浓度可以为2-20重量%,优选为3-15重量%。在另一种具体实施方式中,碱性溶液为稀氨水,稀氨水以NH3计的浓度为2-20重量%,优选为3-15重量%。通过调节混合物的pH值,可以使得IVB族金属离子形成氢氧化物沉淀,有利于含IVB族金属的沉淀物在β沸石表面的均匀分散。
本发明第三方面提供一种制备本发明第二方面提供的催化裂化催化剂的方法,该方法包括:将Y型沸石、本发明第一方面提供的改性β沸石、所述粘土、耐热无机氧化物和第二溶剂混合,将得到的第二浆料进行造粒,并进行干燥和/或第二焙烧。
根据本发明,耐热无机氧化物包括耐热无机氧化物本身和/或耐热无机氧化物前身物。耐热无机氧化物本身可以选自用作裂化催化剂基质和粘结剂组分的耐热无机氧化物中的一种或几种,如氧化铝、氧化硅和无定型硅铝中的一种或几种;耐热无机氧化物前身物是指在本发明催化剂制备过程中能形成耐热无机氧化物的物质,如氧化铝的前身物可选自铝溶胶、拟薄水铝石、薄水铝石、三水合氧化铝和无定形氢氧化铝中的一种或几种;如氧化硅的前身物可选自硅溶胶、硅凝胶和水玻璃中的一种或几种。这些耐热无机氧化物本身或/和耐热无机氧化物前身物及其制备方法为本领域人员所公知。
一种优选的具体实施方式,将粘土、耐热无机氧化物与第一溶剂打浆,将得到的浆料与改性β沸石和Y型沸石混合搅拌,经过喷雾造粒、焙烧,任选地洗涤和干燥,得到本发明的催化裂化催化剂。优选地,在打浆时加入酸,或者,在打浆后加入酸,调节浆料的pH值为1-5,优选为2-4,并于30-90℃老化0.5-5小时。酸可以为溶于水的无机酸或者有机酸,优选为盐酸、硝酸和磷酸中的一种或几种。其中,喷雾干燥的方法和条件为本领域的技术人员所熟知的,在此不再赘述。
根据本发明,第二浆料的固含量可以在较大的范围内变化,例如第二浆料的固含量为15-50重量%,优选为20-45重量%。
根据本发明,干燥的温度可以为80-200℃,时间可以为0.5-24小时,优选地,温度为80-120℃,时间为0.5-12小时;第二焙烧的温度可以为350-700℃,时间可以为0.5-5小时,优选地,温度为400-650℃,时间为1-4小时,可以在任意气氛中进行焙烧,例如空气气氛。
本发明第四方面提供本发明第一方面提供的改性β沸石或本发明第二方面提供的催化裂化催化剂在重质油催化裂化中的应用。
下面通过实施例来进一步说明本公开,但是本公开并不因此而受到任何限制。
高岭土由苏州高岭土公司生产,固含量为76重量%;铝溶胶中的氧化铝含量为21.5重量%;拟薄水铝石由山东铝厂生产,固含量为62.0重量%;酸化拟薄水铝石固含量为12.0重量%,盐酸酸化,酸化时酸(HCl)与氧化铝的摩尔比为0.15;所用的超稳Y沸石USY的固含量94.7%,晶胞常数为以重量百分比含量计,Na2O含量为1.3%,RE2O3含量为2.5%;稀土超稳Y沸石REUSY的固含量84.8%,晶胞常数为以重量百分比含量计,Na2O含量为1.6%,RE2O3含量为12.0%;含磷Y沸石PREHY的固含量92.4%,晶胞常数为以重量百分比含量计,Na2O含量为1.5%,P2O5含量为7.5%,RE2O3含量为8.5%。氢型β沸石的固含量75%,SiO2/Al2O3(摩尔比)=25,Na2O含量为0.15%。磷改性β沸石的固含量82.5%,SiO2/Al2O3(摩尔比)=25,Na2O含量为0.15%,P2O5含量为7.0%。
上述Y型沸石、β沸石均由中国石化催化剂有限公司生产,其余试剂由国药集团化学试剂有限公司生产,规格均为分析纯。所述含量中,未特别注明的,为重量百分含量。
稀氨水以NH3计的浓度为12重量%。
改性β沸石性质的测试方法:
(1)酸量和酸强度的测定:采用热重-程序升温脱附(TG-TPD)技术,以NH3作为碱性吸附气体,将沸石样品在室温下吸附饱和,然后由热重-差热天平(PCT-2型)检测程序升温解吸过程中NH3的失重量,以NH3的解吸量作为样品的酸量,沸石的弱酸中心、中等强度酸中心和强酸中心的温区分别为120-270℃、270-390℃及390-560℃,对应的温度范围内脱附的NH3摩尔量对应为沸石的酸量。
(2)B酸与L酸:采用美国尼高力公司Nicolet 560型红外光谱仪表征催化剂表面酸性,波数为1400-1700cm-1。催化剂中的B酸是以在1540cm-1的特征峰进行表征,催化剂中的L酸是以1450cm-1的特征峰进行表征,由相应的峰面积积分计算,B酸与L酸的比值是指B酸的特征峰的峰面积与L酸的特征峰的峰面积的比值。
(3)改性β沸石表面的IVB族金属元素的重量含量和体相的IVB族金属元素的重量含量:沸石表面的IVB族金属元素的重量含量是指使用X射线光电子能谱法(XPS)在沸石表面2-5nm范围内分析测得的IVB族金属元素的重量含量。
改性β沸石体相的IVB族金属元素的重量含量是通过化学法分析(ICP(Jarrell-Ash,ICAP 9000)元素分析方法进行测定)测得的沸石中IVB族金属元素的重量含量。
在本申请中,改性β沸石含有的IVB族金属元素即指改性β沸石体相含有的IVB族金属元素。将所测得的改性β沸石体相的IVB族金属元素的重量含量进行换算即可得到改性β沸石含有的以氧化物计的IVB族金属元素的重量含量,换算方法为本领域的技术人员所熟知的,在此不再赘述。实施例和对比例制备的改性β沸石性质见表1。
催化剂组成分析:采用X射线荧光光谱(XRF)法。
催化剂组成分析结果见表2-4。
实施例1-8为制备改性β沸石的实施例,对比例1-4为制备改性β沸石的对比例:
实施例1
(1)将2250g的去离子水、39.23g的氧氯化锆(ZrOCl2·8H2O)和7.5g的羟丙基甲基纤维素混合,用稀氨水调节混合物的pH值为7.0,搅拌40分钟,得到第一浆料;
(2)将第一浆料和150g的氢型β沸石混合,在40℃下搅拌90分钟;过滤,将所得滤饼在空气气氛中于550℃下焙烧2小时,得到本发明的改性β沸石,记为B1。
其中,氧氯化锆、β沸石和羟丙基甲基纤维素用量的重量比为0.1:1:0.05,氧氯化锆以氧化锆计,β沸石以干基重量计。
实施例2
(1)将1500g的去离子水、28.34g的异丙醇锆和3g的甲基纤维素混合,用稀氨水调节混合物的pH值为5.0,搅拌60分钟,得到第一浆料;
(2)将第一浆料和150g氢型β沸石混合,在60℃搅拌120分钟,过滤,将所得滤饼在空气气氛中于500℃下焙烧3小时,得到本发明的改性β沸石,记为B2。
其中,异丙醇锆、β沸石和甲基纤维素用量的重量比为0.06:1:0.02,异丙醇锆以氧化锆计,β沸石以干基重量计。
实施例3
(1)将750g的去离子水、10.45g的硝酸锆(Zr(NO3)4·5H2O)和0.8g的木质素混合,用稀氨水调节混合物的pH值为5,搅拌30分钟,得到第一浆料;
(2)将第一浆料和150g的氢型β沸石混合,在80℃搅拌180分钟,过滤,将所得的滤饼在空气气氛中于550℃下焙烧1小时,得到本发明的改性β沸石,记为B3。
其中,硝酸锆、β沸石和木质素用量的重量比为0.02:1:0.005,硝酸锆以氧化锆计,β沸石以干基重量计。
实施例4
(1)将3000g的去离子水、47.08g的氧氯化锆(ZrOCl2·8H2O)和15g的粘胶纤维混合,用稀氨水调节混合物的pH值为7.5,搅拌60分钟,得到第一浆料;
(2)将第一浆料和150g的氢型β沸石混合,85℃搅拌45分钟,过滤,将所得滤饼在空气气氛中于450℃下焙烧3小时,得到本发明的改性β沸石,记为B4。
其中,氧氯化锆、β沸石和粘胶纤维用量的重量比为0.12:1:0.1,氧氯化锆以氧化锆计,β沸石以干基重量计。
实施例5
(1)将1500g的去离子水、18.9g的异丙醇锆和6g的羟乙基纤维素混合,用稀氨水调节混合物的pH值为5.5,搅拌30分钟,得到第一浆料;
(2)将第一浆料和150g的磷改性β沸石混合,在80℃搅拌60分钟,过滤,将所得滤饼在空气气氛中于550℃下焙烧2小时,得到本发明提供的改性β沸石,记为B5。
其中,异丙醇锆、β沸石和羟乙基纤维素用量的重量比为0.04:1:0.04,异丙醇锆以氧化锆计,β沸石以干基重量计。
实施例6
采用与实施例1相同的方法制备改性β沸石B6,不同之处仅在于,步骤(1)中,将2250g的去离子水、39.23的氧氯化锆(ZrOCl2·8H2O)和0.12g的羟丙基甲基纤维素混合,用稀氨水调节混合物的pH值为7.0,搅拌40分钟,得到第一浆料。
其中,氧氯化锆、β沸石和羟丙基甲基纤维素用量的重量比为0.10:1:0.0008,氧氯化锆以氧化锆计,β沸石以干基重量计。
实施例7
采用与实施例1相同的方法制备改性β沸石B7,不同之处仅在于,步骤(1)中,(1)将2250g的去离子水、62.78g的氧氯化锆(ZrOCl2·8H2O)和7.5g的羟丙基甲基纤维素混合,用稀氨水调节混合物的pH值为7.0,搅拌40分钟,得到第一浆料。
其中,氧氯化锆、β沸石和羟丙基甲基纤维素用量的重量比为0.16:1:0.05,氧氯化锆以氧化锆计。
实施例8
采用与实施例1相同的方法制备改性β沸石B8,不同之处仅在于,步骤(1)中,将2250g的去离子水、35.61g的四氯化钛和7.5g的羟丙基甲基纤维素混合,用稀氨水调节混合物的pH值为7.0,搅拌40分钟,得到第一浆料。
其中,四氯化钛、β沸石和羟丙基甲基纤维素用量的重量比为0.1:1:0.05,四氯化钛以氧化钛计,β沸石以干基重量计。
对比例1
采用与实施例1相同的方法制备改性β沸石,不同之处仅在于,不调节第一浆料的pH值。
(1)将取2250g去离子水、39.2g氧氯化锆ZrOCl2·8H2O和7.5g羟丙基甲基纤维素混合,搅拌40分钟,得到第一浆料,所得浆液pH值为1.4;
(2)将第一浆料和200g氢型β沸石混合,在40℃搅拌90分钟;过滤,将所得滤饼在空气气氛中于550℃下焙烧2小时,得得到对比的β沸石,记DB1。
对比例2
采用与实施例2相同的方法制备改性β沸石,不同之处仅在于,不加入碳源。
(1)将1500g去离子水和28.3g异丙醇锆混合均匀,用稀氨水调节混合物的pH值为5.0,搅拌60分钟,得到第一浆料;
(2)将第一浆料和200g氢型β沸石混合,升温至60℃搅拌120分钟;过滤,将所得滤饼在空气气氛中于500℃下焙烧3小时,得到对比的β沸石,记DB2。
对比例3
采用常规水溶液浸渍法制备改性β沸石。
室温下,取200g的Hβ沸石,用1500g的去离子水打浆后,加入45g的(NH4)2SO4,混合均匀,然后升温到90℃交换1小时,过滤并用去离子水洗涤,将滤饼在600℃焙烧2小时,得到氢型β沸石。
将47.1g氧氯化锆(ZrOCl2·8H2O)溶于200g去离子水中制成浸渍液,所得浸渍液与处理后的Hβ沸石混合均匀,室温下静置1h,然后在500℃下焙烧4小时,得到改性β沸石,记为DB3。
对比例4
采用有机溶剂溶液浸渍法制备改性的β沸石,记为DB4。
室温下,取200g的Hβ沸石,用1500g的去离子水打浆后,加入45g的(NH4)2SO4,混合均匀,然后升温到90℃交换1小时,过滤并用去离子水洗涤,将滤饼在600℃焙烧2小时,得到氢型β沸石。
将47.1g氧氯化锆(ZrOCl2·8H2O)溶于200g乙醇中制成浸渍液,所得浸渍液与处理后的β沸石混合均匀,室温下静置1h,然后在500℃下焙烧4小时,得到改性β沸石,记为DB4。
实施例9-22为含有的本发明的改性β沸石的催化裂化催化剂的实施例,对比例5-8和对比例9-10为含有对比的改性β沸石的催化裂化催化剂的对比例:
实施例9
将447g高岭土、372g铝溶胶与513g脱阳离子水加入到打浆罐中打浆,然后加入1666g酸化拟薄水铝石,搅拌60分钟后,再加入271g的REUSY沸石和150g(干基)改性β沸石B1与578g去离子水打浆形成的浆液,均质分散(搅拌)30分钟,然后将得到的浆液喷雾干燥成型,于500℃焙烧2小时,得到本发明提供的催化裂化催化剂C1。
实施例10-16
采用与实施例9相同的方法制备催化裂化催化剂C2-C8,不同之处仅在于,制备催化裂化催化剂的改性β沸石分别为实施例2-8制备的改性β沸石B2-B8。
对比例5-8
采用与实施例9相同的方法制备催化裂化催化剂DC1-DC4,不同之处仅在于,制备催化裂化催化剂的改性β沸石分别为对比例1-4制备的改性β沸石DB1-DB4。
实施例17
将421g高岭土、372g铝溶胶与487g脱阳离子水加入到打浆罐中打浆,然后加入1666g酸化拟薄水铝石,搅拌60分钟后,再加入105g的USY沸石、236g的REUSY和100g(干基)上述改性β沸石B1与847g去离子水打浆形成的浆液,均质分散(搅拌)30分钟,然后将得到的浆液喷雾干燥成型,于500℃焙烧2小时,得到本发明提供的催化裂化催化剂C9。
实施例18
将421g高岭土、372g铝溶胶与537g脱阳离子水加入到打浆罐中打浆,然后加入1666g酸化拟薄水铝石,搅拌60分钟后,再加入294g的REUSY沸石和150g(干基)上述改性β沸石B2与560g去离子水打浆形成的浆液,均质分散(搅拌)30分钟,然后将得到的浆液喷雾干燥成型,于500℃焙烧2小时,得到本发明提供的催化裂化催化剂C10。
实施例19
将421g高岭土、372g铝溶胶与540g脱阳离子水加入到打浆罐中打浆,然后加入1666g酸化拟薄水铝石,搅拌60分钟后,再加入105g的USY沸石、294g的REUSY沸石和50g(干基)上述改性β沸石B3与844g去离子水打浆形成的浆液,均质分散(搅拌)30分钟,然后将得到的浆液喷雾干燥成型,于500℃焙烧2小时,得到本发明提供的催化裂化催化剂C11。
实施例20
将421g高岭土、372g铝溶胶与487g脱阳离子水加入到打浆罐中打浆,然后加入1666g酸化拟薄水铝石,搅拌60分钟后,再加入162g的PREUSY沸石和250g(干基)上述改性β沸石B4与640g去离子水打浆形成的浆液,均质分散(搅拌)30分钟,然后将得到的浆液喷雾干燥成型,于500℃焙烧2小时,得到本发明提供的催化裂化催化剂C12。
实施例21
将421g高岭土、372g铝溶胶与487g脱阳离子水加入到打浆罐中打浆,然后加入1666g酸化拟薄水铝石,搅拌60分钟后,再加入105g的USY沸石、259g的REUSY沸石和80g(干基)上述改性β沸石B5与867g去离子水打浆形成的浆液,均质分散(搅拌)30分钟,然后将得到的浆液喷雾干燥成型,于500℃焙烧2小时,得到本发明提供的催化裂化催化剂C13。
实施例22
将421g高岭土、372g铝溶胶与487g脱阳离子水加入到打浆罐中打浆,然后加入1666g酸化拟薄水铝石,搅拌60分钟后,再加入190g的USY沸石、235g的REUSY和20g(干基)上述改性β沸石B1与847g去离子水打浆形成的浆液,均质分散(搅拌)30分钟,然后将得到的浆液喷雾干燥成型,于500℃焙烧2小时,得到本发明提供的催化裂化催化剂C14。
对比例9
本对比例制备不含β沸石的催化裂化催化剂。
按照实施例17的方法制备催化剂,将421g的高岭土、372g的铝溶胶与487g的脱阳离子水加入到打浆罐中打浆,然后加入1666g的酸化拟薄水铝石,搅拌60分钟后,再加入211g的USY沸石、236g的REUSY与841g去离子水打浆形成的浆液,均质分散(搅拌)30分钟,然后将得到的浆液喷雾干燥成型,于500℃焙烧2小时,得到对比催化裂化催化剂DC5。
对比例10
按照CN104998681A中实施例4的方法,制备磷和铁改性β沸石DB5。
然后按照实施例21的方法制备催化剂,将421g高岭土、372g铝溶胶与487g脱阳离子水加入到打浆罐中打浆,然后加入1666g酸化拟薄水铝石,搅拌60分钟后,再加入105g的USY沸石、259g的REUSY沸石和80g(干基)上述磷和铁改性β沸石与867g去离子水打浆形成的浆液,均质分散(搅拌)30分钟,然后将得到的浆液喷雾干燥成型,于500℃焙烧2小时,得到对比催化裂化催化剂DC6。
催化裂化催化剂评价
将催化裂化催化剂C1-C8和DC1-DC4预先在固定床老化装置上进行800℃、100%水蒸汽老化12小时,然后在小型固定流化床装置上进行评价,反应原料油性质见表8,反应温度500℃,剂油重量比为5.92。
将催化裂化催化剂C9-C14和DC5-DC6预先在固定床老化装置上进行800℃、100%水蒸汽老化8小时,然后在小型固定流化床装置上进行评价,反应原料油性质见表8,反应温度500℃,剂油重量比为4.0。
其中,转化率=汽油收率+液化气收率+干气收率+焦炭收率;
碳四烯烃收率=1-丁烯收率+2-丁烯收率+异丁烯收率;
碳四烯烃浓度=碳四烯烃收率/液化气收率;
碳四烯烃选择性=碳四烯烃收率/碳四馏分收率。
评价结果见表5-表7,表中强酸量/总酸量是指强酸中心数量占总酸量的数值,中强酸量/总酸量是指中等强度酸中心数量占总酸量的数值。
表1改性β沸石性质
由表1的结果可知,与对比例1相比,当含锆化合物加入量一样的情况下,采用实施例1制备的改性β沸石的氧化锆含量高,表明采用稀氨水调节浆液的pH更有利于含锆化合物的充分利用,有利于使含锆化合物沉淀在β沸石表面,而对比例1中含锆化合物在过滤中流失。因此实施例1中沸石体相IVB族金属元素的重量含量/沸石表面IVB族金属元素的重量含量的比值较低,B酸/L酸比值较高,中等强度酸中心数量较多。与对比例3相比,采用实施例5制备的改性β沸石具有更高的B酸/L酸和中等强度酸中心数量。
表2催化裂化催化剂组成
表3催化裂化催化剂组成
表4催化裂化催化剂组成
表5评价结果
表6评价结果
表7评价结果
表8原料油性质
表5和表7的结果表明,与对比例5制备的催化剂DC1相比,本发明实施例9制备的催化剂C1,其汽油和液化气总收率明显提高1.11个百分点,重油收率降低0.16个百分点,柴油收率降低0.97个百分点,碳四烯烃收率提高0.65个百分点,液化气中碳四烯烃浓度提高2.91个百分点,碳四烯烃选择性增加5.01个百分点,液化气中丙烯浓度变化不大。表明本发明采用稀氨水调节浆料的pH值使含锆化合物沉积在β沸石的表面,所制备的改性β沸石具有更高的活性和重油裂化能力,具有优异的碳四烯烃产率和选择性。
与对比例2制备的催化剂DC2相比,以本发明实施例10制备的催化剂C2,其汽油和液化气总收率明显提高1.41个百分点,重油收率降低0.59个百分点,柴油收率降低1.31个百分点,碳四烯烃收率提高0.87个百分点,液化气中碳四烯烃浓度提高4.61个百分点,碳四烯烃选择性增加7.15个百分点,液化气中丙烯浓度变化不大。表明本发明采用碳源制备的改性β沸石具有更高的活性和重油裂化能力,具有优异的碳四烯烃产率和选择性。
与对比例3制备的催化剂DC3相比,以本发明实施例13制备的催化剂C5,其汽油和液化气总收率明显提高2.13个百分点,重油收率降低0.10个百分点,柴油收率降低2.58个百分点,碳四烯烃收率提高0.76个百分点,液化气中碳四烯烃浓度提高4.8个百分点,碳四烯烃选择性增加5.81个百分点,液化气中丙烯浓度变化不大。表明本发明制备的含磷的改性β沸石具有更高的活性和重油裂化能力,具有优异的碳四烯烃产率和选择性。
与对比例5-8相比,在催化剂中改性β沸石含量相当的情况下,以本发明实施例9-16制备的催化裂化催化剂C1-C9具有较高的重油裂化能力,较低的柴油收率,较高的碳四烯烃产率,在液化气产率基本变化不大的情况下,液化气中碳四烯烃浓度增加。
以上详细描述了本公开的优选实施方式,但是,本公开并不限于上述实施方式中的具体细节,在本公开的技术构思范围内,可以对本公开的技术方案进行多种简单变型,这些简单变型均属于本公开的保护范围。
另外需要说明的是,在上述具体实施方式中所描述的各个具体技术特征,在不矛盾的情况下,可以通过任何合适的方式进行组合,为了避免不必要的重复,本公开对各种可能的组合方式不再另行说明。
此外,本公开的各种不同的实施方式之间也可以进行任意组合,只要其不违背本公开的思想,其同样应当视为本公开所公开的内容。
Claims (17)
1.一种改性β沸石,以所述改性β沸石的干基重量为基准,所述改性β沸石含有以氧化物计的0.5-15重量%的IVB族金属元素,所述改性β沸石中等强度酸中心数量占总酸量的30-60%,强酸中心数量占总酸量的5-25%,B酸与L酸的比值为0.8以上,所述改性β沸石体相的IVB族金属元素的重量含量与表面的IVB族金属元素的重量含量的比值为0.1-0.8。
2.根据权利要求1所述的改性β沸石,其中,所述B酸与所述L酸的比值为1.0-1.5。
3.根据权利要求1所述的改性β沸石,其中,所述中等强度酸中心数量占所述总酸量的35-55%。
4.根据权利要求1所述的改性β沸石,其中,所述强酸中心数量占所述总酸量的5-20%。
5.根据权利要求1所述的改性β沸石,其中,以所述改性β沸石的干基重量为基准,所述改性β沸石含有以氧化物计的1-12重量%的IVB族金属元素。
6.根据权利要求1所述的改性β沸石,其中,所述IVB族金属元素为Zr和/或Ti,优选为Zr;所述Zr元素的重量以ZrO2计,所述Ti元素的重量以TiO2计。
7.根据权利要求1所述的改性β沸石,其中,所述改性β沸石体相的IVB族金属元素的重量含量与表面的IVB族金属元素的重量含量的比值为0.1-0.6。
8.一种催化裂化催化剂,以所述催化裂化催化剂的干基重量为基准,所述催化裂化催化剂含有20-50重量%的Y型沸石、2-40重量%的改性β沸石、10-70重量%的粘土和5-60重量%的耐热无机氧化物,所述改性β沸石为权利要求1-3中任意一项所述的改性β沸石。
9.根据权利要求8所述的催化裂化催化剂,其中,所述Y型沸石选自含磷和/或稀土的Y型沸石、超稳Y沸石,以及,含磷和/或稀土的超稳Y沸石中的一种或几种;
所述粘土选自高岭土、累托土、硅藻土、蒙脱土、膨润土和海泡石中的一种或者几种;
所述耐热无机氧化物选自氧化铝、氧化硅和无定型硅铝中的一种或几种。
10.根据权利要求8所述的催化裂化催化剂,其中,所述催化裂化催化剂含有30-45重量%的所述Y型沸石、5-30重量%的所述改性β沸石、10-50重量%的所述粘土和5-40重量%的所述耐热无机氧化物。
11.一种制备权利要求1-7中任意一项所述的改性β沸石的方法,该方法包括:
(1)将含IVB族金属的化合物、碳源和第一溶剂混合,调节混合物pH值为4-9,得到第一浆料;所述碳源包括天然高分子有机化合物和/或半合成高分子有机化合物;
(2)将所述第一浆料和β沸石在20-100℃下搅拌混合10-180min,取出固体在350-650℃下进行第一焙烧0.5-5小时。
12.根据权利要求11所述的方法,其中,步骤(2)中,调节所述第一浆料的pH值为5-8。
13.根据权利要求11所述的方法,其中,所述含IVB族金属的化合物和所述β沸石用量的重量比为(0.005-0.15):1,所述β沸石和所述碳源用量的重量比为1:(0.001-0.15),所述含IVB族金属的化合物以IVB族金属的氧化物计,所述β沸石以干基重量计。
14.根据权利要求11所述的方法,其中,所述β沸石选自氢型β沸石、钠型β沸石、含磷的β沸石、含稀土金属的β沸石,以及,含有磷和稀土金属的β沸石中的一种或几种;
所述碳源选自淀粉、木质素、粘胶纤维、甲基纤维素、羟丙基甲基纤维素、羟乙基纤维素和羧甲基纤维素中的一种或几种;
所述含IVB族金属的化合物选自四氯化锆、醋酸锆、异丙醇锆、四氯化钛、硫酸氧钛、氟钛酸铵、硫酸锆、硝酸锆、氧氯化锆、硫酸钛、钛酸四丁酯、三氯化钛和硫酸亚钛中的一种或几种;
所述第一溶剂选自去离子水、乙醇、丙酮和正己烷中的一种或几种。
15.一种制备权利要求8-10中任意一项所述的催化裂化催化剂的方法,该方法包括:将所述Y型沸石、所述改性β沸石、所述粘土、所述耐热无机氧化物和第二溶剂混合,将得到的第二浆料进行造粒,并进行干燥和/或第二焙烧,所述改性β沸石为权利要求1-7中任意一项所述的改性β沸石。
16.根据权利要求15所述的方法,其中,所述干燥的温度为80-200℃,时间为0.5-24小时;所述第二焙烧的温度为350-700℃,时间为0.5-5小时。
17.权利要求1-7中任意一项所述的改性β沸石或权利要求8-10中任意一项所述的催化裂化催化剂在重质油催化裂化中的应用。