CN113493673A - 一种阻燃硅酮密封胶及其制备方法 - Google Patents
一种阻燃硅酮密封胶及其制备方法 Download PDFInfo
- Publication number
- CN113493673A CN113493673A CN202010196538.XA CN202010196538A CN113493673A CN 113493673 A CN113493673 A CN 113493673A CN 202010196538 A CN202010196538 A CN 202010196538A CN 113493673 A CN113493673 A CN 113493673A
- Authority
- CN
- China
- Prior art keywords
- parts
- silicone
- silicone oil
- flame
- catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种阻燃硅酮密封胶，包括以下重量份的原料：三甲氧基封端聚二甲基硅氧烷、增塑剂、填料、交联剂、偶联剂、阻燃剂、催化剂、有机羟基硅酮、有机甲基硅酮、碳酸钙、橡胶、十二烷基硫酸钠、单氟磷酸钠、双氧水、乙二醇、酚醛树脂、水玻璃、香料、端乙烯基硅油、高乙烯基硅油、催化剂、二甲基硅油、乙炔环己醇、硅氮烷、绢云母粉、丙烯酸树脂和硅烷偶联剂；一种阻燃硅酮密封胶的制备方法，包括以下步骤：S1、搅拌混合；S2、加入溶剂；S3、加入香料：将S2中形成的胶体物逐渐加入等量重量份的香料，进行搅拌混合，形成所述的一种阻燃硅酮密封胶。
Description
技术领域
本发明涉及密封胶领域，尤其是涉及一种阻燃硅酮密封胶及其制备方法。
背景技术
硅酮密封胶具有优异的耐温、耐候、抗老化、不龟裂、抗震和防潮等特点，在建筑、电子电器、汽车、航天航空领域有广泛应用。硅酮密封材料广泛使用的建筑密封材料，然而一般低伸长率的防火阻燃密封胶不能满足混凝土接缝的高度位移能力的要求，其与混凝土本身的粘结性能不好，容易拉裂，从而使密封作用丧失，且重新维护成本过高。随着人们消防安全意识的增强，对密封胶的防火级别要求越来越高。虽然普通硅酮密封胶具有一定阻燃性能，但其阻燃性能仍不能达到行业要。
发明内容
本发明为克服上述情况不足，旨在提供一种能解决上述问题的技术方案。
一种阻燃硅酮密封胶，包括以下重量份的原料：三甲氧基封端聚二甲基硅氧烷40-55份、增塑剂15-25份、填料30-50份、交联剂0.1-3份、偶联剂1-10份、阻燃剂4-8份、催化剂0.1-3份、有机羟基硅酮10-20份、有机甲基硅酮10-30份、碳酸钙80-90份、橡胶4-6份、十二烷基硫酸钠1-2份、单氟磷酸钠0.5-2份、双氧水0.5-2份、乙二醇0.5-2份、酚醛树脂1-4份、水玻璃0.5-2份、香料0.5-2份、端乙烯基硅油0.5-2份、高乙烯基硅油0.5-2份、催化剂0.5-2份、二甲基硅油10-15份、乙炔环己醇10-15份、硅氮烷10-20份、绢云母粉10-30份、丙烯酸树脂10-20份和硅烷偶联剂10-20份。
一种阻燃硅酮密封胶的制备方法，用于制备所述的一种阻燃硅酮密封胶，包括以下步骤：
S1、搅拌混合：将等量重量份的三甲氧基封端聚二甲基硅氧烷、有机羟基硅酮、有机甲基硅酮、碳酸钙、橡胶、十二烷基硫酸钠、单氟磷酸钠、酚醛树脂、水玻璃、乙炔环己醇、硅氮烷、绢云母粉和丙烯酸树脂和硅烷偶联剂分别倒置于化学搅拌机中，进行搅拌混合，形成混合物；
S2、加入溶剂：将S1中形成的混合物逐渐加入等量重量份的增塑剂、填料、交联剂、偶联剂、阻燃剂、催化剂、双氧水、乙二醇、橄榄油、端乙烯基硅油、高乙烯基硅油、催化剂和二甲基硅油，进行搅拌混合，形成胶体物；
S3、加入香料：将S2中形成的胶体物逐渐加入等量重量份的香料，进行搅拌混合，形成所述的一种阻燃硅酮密封胶。
作为本发明进一步的方案：所述S1中化学搅拌机的搅拌速度控制在40r/min—50r/min。
作为本发明进一步的方案：所述S2中化学搅拌机的搅拌速度控制在65r/min—75r/min。
作为本发明进一步的方案：所述S3中化学搅拌机的搅拌速度控制在25r/min—35r/min。
与现有技术相比，本发明的有益效果是：能够及时将燃烧时产生的烟雾吸收，起到隔绝火焰、烟雾与防火的作用；此外，该阻燃剂的添加量超过普通阻燃剂的添加量，同时不影响防火阻燃密封胶与混凝土、石材等建筑材料具有优良的粘结性。
本发明的附加方面和优点将在下面的描述中部分给出，部分将从下面的描述中变得明显，或通过本发明的实践了解到。
具体实施方式
下面将结合本发明的实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例一
一种阻燃硅酮密封胶，包括以下重量份的原料：三甲氧基封端聚二甲基硅氧烷40-55份、增塑剂15-25份、填料30-50份、交联剂0.1-3份、偶联剂1-10份、阻燃剂4-8份、催化剂0.1-3份、有机羟基硅酮10-20份、有机甲基硅酮10-30份、碳酸钙80-90份、橡胶4-6份、十二烷基硫酸钠1-2份、单氟磷酸钠0.5-2份、双氧水0.5-2份、乙二醇0.5-2份、酚醛树脂1-4份、水玻璃0.5-2份、香料0.5-2份、端乙烯基硅油0.5-2份、高乙烯基硅油0.5-2份、催化剂0.5-2份、二甲基硅油10-15份、乙炔环己醇10-15份、硅氮烷10-20份、绢云母粉10-30份、丙烯酸树脂10-20份和硅烷偶联剂10-20份。
一种阻燃硅酮密封胶的制备方法，用于制备所述的一种阻燃硅酮密封胶，包括以下步骤：
S1、搅拌混合：将等量重量份的三甲氧基封端聚二甲基硅氧烷、有机羟基硅酮、有机甲基硅酮、碳酸钙、橡胶、十二烷基硫酸钠、单氟磷酸钠、酚醛树脂、水玻璃、乙炔环己醇、硅氮烷、绢云母粉和丙烯酸树脂和硅烷偶联剂分别倒置于化学搅拌机中，进行搅拌混合，形成混合物；
S2、加入溶剂：将S1中形成的混合物逐渐加入等量重量份的增塑剂、填料、交联剂、偶联剂、阻燃剂、催化剂、双氧水、乙二醇、橄榄油、端乙烯基硅油、高乙烯基硅油、催化剂和二甲基硅油，进行搅拌混合，形成胶体物；
S3、加入香料：将S2中形成的胶体物逐渐加入等量重量份的香料，进行搅拌混合，形成所述的一种阻燃硅酮密封胶。
实施例二
一种阻燃硅酮密封胶，包括以下重量份的原料：三甲氧基封端聚二甲基硅氧烷40份、增塑剂15份、填料30份、交联剂0.1份、偶联剂1份、阻燃剂4份、催化剂0.1份、有机羟基硅酮10份、有机甲基硅酮10份、碳酸钙80份、橡胶4份、十二烷基硫酸钠1份、单氟磷酸钠0.5份、双氧水0.5份、乙二醇0.5份、酚醛树脂1份、水玻璃0.5份、香料0.5份、端乙烯基硅油0.5份、高乙烯基硅油0.5份、催化剂0.5份、二甲基硅油10份、乙炔环己醇10份、硅氮烷10份、绢云母粉10份、丙烯酸树脂10份和硅烷偶联剂10份。
一种阻燃硅酮密封胶的制备方法，用于制备所述的一种阻燃硅酮密封胶，包括以下步骤：
S1、搅拌混合：将等量重量份的三甲氧基封端聚二甲基硅氧烷、有机羟基硅酮、有机甲基硅酮、碳酸钙、橡胶、十二烷基硫酸钠、单氟磷酸钠、酚醛树脂、水玻璃、乙炔环己醇、硅氮烷、绢云母粉和丙烯酸树脂和硅烷偶联剂分别倒置于化学搅拌机中，进行搅拌混合，形成混合物；
S2、加入溶剂：将S1中形成的混合物逐渐加入等量重量份的增塑剂、填料、交联剂、偶联剂、阻燃剂、催化剂、双氧水、乙二醇、橄榄油、端乙烯基硅油、高乙烯基硅油、催化剂和二甲基硅油，进行搅拌混合，形成胶体物；
S3、加入香料：将S2中形成的胶体物逐渐加入等量重量份的香料，进行搅拌混合，形成所述的一种阻燃硅酮密封胶。
实施例三
一种阻燃硅酮密封胶，包括以下重量份的原料：三甲氧基封端聚二甲基硅氧烷50份、增塑剂20份、填料45份、交联剂1.5份、偶联剂8份、阻燃剂6份、催化剂1.5份、有机羟基硅酮15份、有机甲基硅酮20份、碳酸钙85份、橡胶5份、十二烷基硫酸钠1.5份、单氟磷酸钠1份、双氧水1份、乙二醇1份、酚醛树脂1.5份、水玻璃1份、香料1份、端乙烯基硅油1份、高乙烯基硅油1份、催化剂1份、二甲基硅油13份、乙炔环己醇13份、硅氮烷15份、绢云母粉20份、丙烯酸树脂15份和硅烷偶联剂15份。
一种阻燃硅酮密封胶的制备方法，用于制备所述的一种阻燃硅酮密封胶，包括以下步骤：
S1、搅拌混合：将等量重量份的三甲氧基封端聚二甲基硅氧烷、有机羟基硅酮、有机甲基硅酮、碳酸钙、橡胶、十二烷基硫酸钠、单氟磷酸钠、酚醛树脂、水玻璃、乙炔环己醇、硅氮烷、绢云母粉和丙烯酸树脂和硅烷偶联剂分别倒置于化学搅拌机中，进行搅拌混合，形成混合物；
S2、加入溶剂：将S1中形成的混合物逐渐加入等量重量份的增塑剂、填料、交联剂、偶联剂、阻燃剂、催化剂、双氧水、乙二醇、橄榄油、端乙烯基硅油、高乙烯基硅油、催化剂和二甲基硅油，进行搅拌混合，形成胶体物；
S3、加入香料：将S2中形成的胶体物逐渐加入等量重量份的香料，进行搅拌混合，形成所述的一种阻燃硅酮密封胶。
实施例四
一种阻燃硅酮密封胶，包括以下重量份的原料：三甲氧基封端聚二甲基硅氧烷55份、增塑剂25份、填料50份、交联剂3份、偶联剂10份、阻燃剂8份、催化剂3份、有机羟基硅酮20份、有机甲基硅酮30份、碳酸钙90份、橡胶6份、十二烷基硫酸钠2份、单氟磷酸钠2份、双氧水2份、乙二醇2份、橄榄油3份、酚醛树脂4份、水玻璃2份、香料2份、端乙烯基硅油2份、高乙烯基硅油2份、催化剂2份、二甲基硅油15份、乙炔环己醇15份、硅氮烷20份、绢云母粉30份、丙烯酸树脂20份和硅烷偶联剂20份。
一种阻燃硅酮密封胶的制备方法，用于制备所述的一种阻燃硅酮密封胶，包括以下步骤：
S1、搅拌混合：将等量重量份的三甲氧基封端聚二甲基硅氧烷、有机羟基硅酮、有机甲基硅酮、碳酸钙、橡胶、十二烷基硫酸钠、单氟磷酸钠、酚醛树脂、水玻璃、乙炔环己醇、硅氮烷、绢云母粉和丙烯酸树脂和硅烷偶联剂分别倒置于化学搅拌机中，进行搅拌混合，形成混合物；
S2、加入溶剂：将S1中形成的混合物逐渐加入等量重量份的增塑剂、填料、交联剂、偶联剂、阻燃剂、催化剂、双氧水、乙二醇、橄榄油、端乙烯基硅油、高乙烯基硅油、催化剂和二甲基硅油，进行搅拌混合，形成胶体物；
S3、加入香料：将S2中形成的胶体物逐渐加入等量重量份的香料，进行搅拌混合，形成所述的一种阻燃硅酮密封胶。
所述三甲氧基封端聚二甲基硅氧烷由初级形态二甲基环体硅氧烷为主要原料，经过水解合成，以硅氧(Si-O)键为主链，硅原子上直接连接有机基的有机－无机化合物；初级形态二甲基环体硅氧烷分子结构呈现环状，主要包括六甲基环三硅氧烷(D3)、八甲基环四硅氧烷(D4)、十甲基环五硅氧烷(D5)、十二甲基环六硅氧烷(D6)、以及六甲基环三硅氧烷(D3)及或八甲基环四硅氧烷(D4)及或十甲基环五硅氧烷(D5)及或十二甲基环六硅氧烷(D6)含量达到50％以上的无色透明或乳白色液体，可燃，无异味，不溶于水，溶于苯等有机溶剂。
所述橡胶是指具有可逆形变的高弹性聚合物材料，在室温下富有弹性，在很小的外力作用下能产生较大形变，除去外力后能恢复原状；所述橡胶为天然橡胶或合成橡胶其中一种，且本发明所述的橡胶采用天然橡胶；所述天然橡胶是由胶乳制造的，胶乳中所含的非橡胶成分有一部分就留在固体的天然橡胶中。一般天然橡胶中含橡胶烃92％-95％，而非橡胶烃占5％-8％。
所述酚醛树脂也叫电木，又称电木粉。原为无色或黄褐色透明物，市场销售往往加着色剂而呈红、黄、黑、绿、棕、蓝等颜色，有颗粒、粉末状；耐弱酸和弱碱，遇强酸发生分解，遇强碱发生腐蚀。不溶于水，溶于丙酮、酒精等有机溶剂中。苯酚醛或其衍生物缩聚而得。
所述高乙烯基硅油主要有端乙烯基聚二甲基硅氧烷(Vi-PDMS)和端乙烯基聚甲基乙烯基硅氧烷(Vi-PMVS)，可根据需要提供不同粘度和乙烯基含量的产品；高乙烯基硅油可分为：端乙烯基硅油和高乙烯基硅油，是加成型液体硅橡胶、有机硅凝胶等的主要原料；混炼胶的改性剂/塑料添加剂/补强材料等。
所述二甲基硅油又名甲基硅油、聚二甲基硅氧烷液体；无色透明粘稠液体、无味、无臭、无毒；分子式为CH3[Si(cH3)2]nSi(CH3)3、平均分子量5000～100000；根据分子量不同，运动粘度从1.0×10-6～100000×10-6平方米/秒不等；长期使用温度范围-50～180℃，在隔绝空气条件下或在惰性气体中可在200℃下长期使用；粘度系数0.31～0.61；表面张力1.59～2.15×10-4N/cm；介电常数(23℃，100Hz)2.18～2.17；体积电阻率(23℃)1.0×1014～1.0×1016Ωcm3；介质损耗角正切值(23℃，100Hz)0.00002～0.00004；击穿电压强度13.7～17.7kV/mm。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
Claims (8)
1.一种阻燃硅酮密封胶，其特征在于，包括以下重量份的原料：三甲氧基封端聚二甲基硅氧烷40-55份、增塑剂15-25份、填料30-50份、交联剂0.1-3份、偶联剂1-10份、阻燃剂4-8份、催化剂0.1-3份、有机羟基硅酮10-20份、有机甲基硅酮10-30份、碳酸钙80-90份、橡胶4-6份、十二烷基硫酸钠1-2份、单氟磷酸钠0.5-2份、双氧水0.5-2份、乙二醇0.5-2份、酚醛树脂1-4份、水玻璃0.5-2份、香料0.5-2份、端乙烯基硅油0.5-2份、高乙烯基硅油0.5-2份、催化剂0.5-2份、二甲基硅油10-15份、乙炔环己醇10-15份、硅氮烷10-20份、绢云母粉10-30份、丙烯酸树脂10-20份和硅烷偶联剂10-20份。
2.根据权利要求1所述的一种阻燃硅酮密封胶，其特征在于，包括以下重量份的原料：三甲氧基封端聚二甲基硅氧烷40份、增塑剂15份、填料30份、交联剂0.1份、偶联剂1份、阻燃剂4份、催化剂0.1份、有机羟基硅酮10份、有机甲基硅酮10份、碳酸钙80份、橡胶4份、十二烷基硫酸钠1份、单氟磷酸钠0.5份、双氧水0.5份、乙二醇0.5份、酚醛树脂1份、水玻璃0.5份、香料0.5份、端乙烯基硅油0.5份、高乙烯基硅油0.5份、催化剂0.5份、二甲基硅油10份、乙炔环己醇10份、硅氮烷10份、绢云母粉10份、丙烯酸树脂10份和硅烷偶联剂10份。
3.根据权利要求1所述的一种阻燃硅酮密封胶，其特征在于，包括以下重量份的原料：三甲氧基封端聚二甲基硅氧烷50份、增塑剂20份、填料45份、交联剂1.5份、偶联剂8份、阻燃剂6份、催化剂1.5份、有机羟基硅酮15份、有机甲基硅酮20份、碳酸钙85份、橡胶5份、十二烷基硫酸钠1.5份、单氟磷酸钠1份、双氧水1份、乙二醇1份、酚醛树脂1.5份、水玻璃1份、香料1份、端乙烯基硅油1份、高乙烯基硅油1份、催化剂1份、二甲基硅油13份、乙炔环己醇13份、硅氮烷15份、绢云母粉20份、丙烯酸树脂15份和硅烷偶联剂15份。
4.根据权利要求1所述的一种阻燃硅酮密封胶，其特征在于，包括以下重量份的原料：三甲氧基封端聚二甲基硅氧烷55份、增塑剂25份、填料50份、交联剂3份、偶联剂10份、阻燃剂8份、催化剂3份、有机羟基硅酮20份、有机甲基硅酮30份、碳酸钙90份、橡胶6份、十二烷基硫酸钠2份、单氟磷酸钠2份、双氧水2份、乙二醇2份、橄榄油3份、酚醛树脂4份、水玻璃2份、香料2份、端乙烯基硅油2份、高乙烯基硅油2份、催化剂2份、二甲基硅油15份、乙炔环己醇15份、硅氮烷20份、绢云母粉30份、丙烯酸树脂20份和硅烷偶联剂20份。
5.一种阻燃硅酮密封胶的制备方法，用于制备权利要求1-4所述的一种阻燃硅酮密封胶，其特征在于，包括以下步骤：
S1、搅拌混合：将等量重量份的三甲氧基封端聚二甲基硅氧烷、有机羟基硅酮、有机甲基硅酮、碳酸钙、橡胶、十二烷基硫酸钠、单氟磷酸钠、酚醛树脂、水玻璃、乙炔环己醇、硅氮烷、绢云母粉和丙烯酸树脂和硅烷偶联剂分别倒置于化学搅拌机中，进行搅拌混合，形成混合物；
S2、加入溶剂：将S1中形成的混合物逐渐加入等量重量份的增塑剂、填料、交联剂、偶联剂、阻燃剂、催化剂、双氧水、乙二醇、橄榄油、端乙烯基硅油、高乙烯基硅油、催化剂和二甲基硅油，进行搅拌混合，形成胶体物；
S3、加入香料：将S2中形成的胶体物逐渐加入等量重量份的香料，进行搅拌混合，形成所述的一种阻燃硅酮密封胶。
6.根据权利要求5所述的一种阻燃硅酮密封胶的制备方法，其特征在于，所述S1中化学搅拌机的搅拌速度控制在40r/min—50r/min。
7.根据权利要求5所述的一种阻燃硅酮密封胶的制备方法，其特征在于，所述S2中化学搅拌机的搅拌速度控制在65r/min—75r/min。
8.根据权利要求5所述的一种阻燃硅酮密封胶的制备方法，其特征在于，所述S3中化学搅拌机的搅拌速度控制在25r/min—35r/min。