CN113292290A - 一种以铅锌尾矿为主料的瓷砖胶及其制备和使用方法 - Google Patents
一种以铅锌尾矿为主料的瓷砖胶及其制备和使用方法 Download PDFInfo
- Publication number
- CN113292290A CN113292290A CN202110579967.XA CN202110579967A CN113292290A CN 113292290 A CN113292290 A CN 113292290A CN 202110579967 A CN202110579967 A CN 202110579967A CN 113292290 A CN113292290 A CN 113292290A
- Authority
- CN
- China
- Prior art keywords
- lead
- zinc
- zinc tailings
- main material
- tile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于瓷砖粘合材料技术领域，具体公开了一种以铅锌尾矿为主料的瓷砖胶及其制备和使用方法，该瓷砖胶由以下重量百分比的原料组成：水泥30‑35％，铅锌尾矿55‑60％，重钙粉1‑6％，可再分散乳胶粉2‑4％，PP纤维0.8‑1％，纤维素醚0.2‑0.25％，淀粉醚0.02‑0.03％。本发明以铅锌尾矿、普通硅酸盐水泥、外加剂等制备的一种瓷砖胶，该瓷砖胶具有成本低、施工性能好、粘接强度高、优良的稳定性等优势，且该瓷砖胶在浸水、高温以及冷冻的条件下，仍保留很好的强度，证明本发明所述瓷砖胶对施工环境的温度和湿度适应力强；经推广发展，可解决了在开采铅锌矿时造成的对土地资源的占用和环境污染等问题，促进铅锌尾矿的高效率利用，具有良好经济效益和社会效益。
Description
技术领域
本发明涉及瓷砖粘合材料技术领域，特别是一种以铅锌尾矿为主料的瓷砖胶及其制备和使用方法。
背景技术
瓷砖胶泥又称瓷砖胶、瓷砖粘合剂或粘结剂、粘胶泥等多种叫法，是现代装潢的新型材料，替代了传统水泥黄沙，胶粘结力是水泥砂浆的数倍，能有效粘贴大型的瓷砖石材，避免掉砖的风险。主要用于粘贴瓷砖、面砖、地砖等装饰材料,广泛适用于内外墙面、地面、浴室、厨房等建筑的饰面装饰场所。其主要特点是粘接强度高、耐水、耐冻融、耐老化性能好及施工方便，是一种非常理想的粘结材料。
随着黄砂、河砂等短缺，价格的上涨，造成瓷砖胶成本的增加。
铅锌尾矿是铅锌矿选矿行业中对铅锌元素进行选取后，经排放堆积于尾矿库形成的固体矿物废料。1t铅锌原矿经提炼后将产生0.95t以上的尾矿，各矿点经多年的生产已排出数以千万吨的尾矿，不但占用大量的土地，其中含有的大量重金属在地表生物地球化学作用下通过释放和迁移导致了土壤及河流严重的重金属污染。在排除其放射性危害的前提下，从环保角度出发，综合利用矿产资源，寻求新的二次资源开发利用途径，无疑对企业的经济效益和环境保护均是一件有益的事情。
如果能将铅锌尾矿用于瓷砖胶的制作，既能实现固体废弃物的资源化利用，拓宽固体废弃物的使用途径，降低成本，又可节约天然资源，节能减排，具有良好的经济效益和环境效益。
因此，亟待开发一种以铅锌尾矿为主料的瓷砖胶。
发明内容
本发明的目的是要缓解在开采铅锌矿时造成的对土地资源的占用和环境污染等问题，提供一种以铅锌尾矿为主料的瓷砖胶及其制备和使用方法。
为达到上述目的，本发明是按照以下技术方案实施的：
本发明的第一个目的是要提供一种以铅锌尾矿为主料的瓷砖胶，该瓷砖胶由以下重量百分比的原料组成：
作为本发明的优选方案，所述铅锌尾矿为铅锌矿选矿行业中对铅锌元素进行选取后，经排放堆积于尾矿库形成的固体矿物废料，经筛选，细度为70-150目。
作为本发明的优选方案，所述纤维素醚为羟丙基甲基纤维素，羟丙基甲基纤维素的粘度为6-10万mpa.s。
作为本发明的优选方案，所述淀粉醚为羟烷基淀粉、羧甲基淀粉、阳离子淀粉中的一种或多种。
作为本发明的优选方案，所述重钙粉的细度为200目。
作为本发明的优选方案，所述水泥为PO52.5级普通硅酸盐水泥。
本发明的第二个目的是要提供一种以铅锌尾矿为主料的瓷砖胶的制备方法，按重量比例称量水泥、铅锌尾矿、重钙粉、可再分散性乳胶粉、PP纤维、纤维素醚和淀粉醚，投入混料机，通过机械混合均匀后，得到包含铅锌尾矿的瓷砖胶。
本发明的第三个目的是要提供一种以铅锌尾矿为主料的瓷砖胶的使用方法，在瓷砖胶中加水，水与瓷砖胶重量比为0.24，搅拌至膏状即形成瓷砖胶结剂。
与现有技术相比，本发明以铅锌尾矿、普通硅酸盐水泥、外加剂等制备的一种瓷砖胶，该瓷砖胶具有成本低、施工性能好、粘接强度高、优良的稳定性等优势，且该瓷砖胶在浸水、高温以及冷冻的条件下，仍保留很好的强度，证明本发明所述瓷砖胶对施工环境的温度和湿度适应力强；经推广发展，可解决了在开采铅锌矿时造成的对土地资源的占用和环境污染等问题，促进铅锌尾矿的高效率利用，具有良好经济效益和社会效益。
具体实施方式
为使本发明的目的、技术方案及优点更加清楚明白，以下结合实施例，对本发明进行进一步的详细说明。此处所描述的具体实施例仅用于解释本发明，并不用于限定发明。
实施例1
一种由铅锌尾矿制备的瓷砖胶，由以下重量份数的原料组成：PO52.5级普通硅酸盐水泥30kg，铅锌尾矿60kg，重钙粉(细度为200目)6kg，德国瓦克化学公司产5010N胶粉4kg，PP纤维(聚丙烯纤维)0.8kg，粘度为6-10万mpa.s的羟丙基甲基纤维素(可直接在市面上购买，本实施例不再列举具体型号)0.25kg，羟烷基淀粉(可直接在市面上购买，本实施例不再列举具体型号)0.03kg。
实施例2
一种以铅锌尾矿为主料的瓷砖胶，由以下原料组成：PO52.5级普通硅酸盐水泥35kg，铅锌尾矿60kg，重钙粉(细度为200目)1kg，德国瓦克化学公司产5010N胶粉4kg，PP纤维(聚丙烯纤维)0.8kg，粘度为6-10万mpa.s的羟丙基甲基纤维素(可直接在市面上购买，本实施例不再列举具体型号)0.25kg，羧甲基淀粉(可直接在市面上购买，本实施例不再列举具体型号)0.03kg。
实施例3
一种以铅锌尾矿为主料的瓷砖胶，由以下原料组成：PO52.5级普通硅酸盐水泥35kg，铅锌尾矿55kg，重钙粉(细度为200目)6kg，德国瓦克化学公司产5010N胶粉4kg，PP纤维(聚丙烯纤维)0.8kg，粘度为6-10万mpa.s的羟丙基甲基纤维素(可直接在市面上购买，本实施例不再列举具体型号)0.2kg，阳离子淀粉(可直接在市面上购买，本实施例不再列举具体型号)0.02kg。
实施例4
一种以铅锌尾矿为主料的瓷砖胶，由以下原料组成：PO52.5级普通硅酸盐水泥35kg，铅锌尾矿60kg，重钙粉(细度为200目)3kg，德国瓦克化学公司产5010N胶粉2kg，PP纤维(聚丙烯纤维)0.8kg，粘度为6-10万mpa.s的羟丙基甲基纤维素(可直接在市面上购买，本实施例不再列举具体型号)0.25kg，羟烷基淀粉(可直接在市面上购买，本实施例不再列举具体型号)0.01kg，阳离子淀粉(可直接在市面上购买，本实施例不再列举具体型号)0.03kg。
实施例5
一种以铅锌尾矿为主料的瓷砖胶，由以下原料组成：PO52.5级普通硅酸盐水泥35kg，铅锌尾矿55kg，重钙粉(细度为200目)6kg，德国瓦克化学公司产5010N胶粉4kg，PP纤维(聚丙烯纤维)1kg，粘度为6-10万mpa.s的羟丙基甲基纤维素(可直接在市面上购买，本实施例不再列举具体型号)0.2kg，羧甲基淀粉(可直接在市面上购买，本实施例不再列举具体型号)0.01kg，阳离子淀粉(可直接在市面上购买，本实施例不再列举具体型号)0.01kg。
分别取上述实施例1-实施例5的瓷砖胶混合均匀，加水搅拌至膏状，水灰比为0.24，按照标准JC/T 547-2017《陶瓷砖胶结剂》规定的测试方法进行测试，其测试结果见表1，表1为实施例1-实施例5性能测试的结果。
表1
由表1实验数据可以看出，本发明实施例1-5制备得到的瓷砖胶均具有非常优异的粘接强度，拉伸粘接强度为1.01-1.49MPa，经浸水、热老化、冻融循环厚数据仍比较优异，说明本发明所述的瓷砖胶在浸水、高温以及冷冻的条件下，仍保留很好的强度，证明本发明所述瓷砖胶对施工环境的温度和湿度适应力强，这是本领域所期望的。
本发明的技术方案不限于上述具体实施例的限制，凡是根据本发明的技术方案做出的技术变形，均落入本发明的保护范围之内。
Claims (8)
1.一种以铅锌尾矿为主料的瓷砖胶，其特征在于：该瓷砖胶由以下重量百分比的原料组成：
2.根据权利要求1所述的以铅锌尾矿为主料的瓷砖胶，其特征在于：所述铅锌尾矿为铅锌矿选矿行业中对铅锌元素进行选取后，经排放堆积于尾矿库形成的固体矿物废料，经筛选，细度为70-150目。
3.根据权利要求1所述的以铅锌尾矿为主料的瓷砖胶，其特征在于：所述纤维素醚为羟丙基甲基纤维素，羟丙基甲基纤维素的粘度为6-10万mpa.s。
4.根据权利要求1所述的以铅锌尾矿为主料的瓷砖胶，其特征在于：所述淀粉醚为羟烷基淀粉、羧甲基淀粉、阳离子淀粉中的一种或多种。
5.根据权利要求1所述的以铅锌尾矿为主料的瓷砖胶，其特征在于：所述重钙粉的细度为200目。
6.根据权利要求1所述的以铅锌尾矿为主料的瓷砖胶，其特征在于：所述水泥为PO52.5级普通硅酸盐水泥。
7.一种如权利要求1-6任一所述的以铅锌尾矿为主料的瓷砖胶的制备方法，其特征在于：按重量比例称量水泥、铅锌尾矿、重钙粉、可再分散性乳胶粉、PP纤维、纤维素醚和淀粉醚，投入混料机，通过机械混合均匀后，得到包含铅锌尾矿的瓷砖胶。
8.一种如权利要求1所述的以铅锌尾矿为主料的瓷砖胶的使用方法，其特征在于：在瓷砖胶中加水，水与瓷砖胶重量比为0.24，搅拌至膏状即形成瓷砖胶结剂。