CN1131501A - 聚烯烃类树脂被复膜及植物的栽培方法 - Google Patents
聚烯烃类树脂被复膜及植物的栽培方法 Download PDFInfo
- Publication number
- CN1131501A CN1131501A CN95121755A CN95121755A CN1131501A CN 1131501 A CN1131501 A CN 1131501A CN 95121755 A CN95121755 A CN 95121755A CN 95121755 A CN95121755 A CN 95121755A CN 1131501 A CN1131501 A CN 1131501A
- Authority
- CN
- China
- Prior art keywords
- overlay film
- polyolefin resin
- weight
- film
- ultra
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了在园艺设施温室、地窖栽培中，即使使用无机硫剂处理土壤和/或植物也不产生劣化的聚烯烃类树脂被覆膜及植物栽培方法。该薄膜是由受阻胺类化合物、水滑石类化合物、紫外线吸收剂及聚烯烃类树脂构成的。
Description
本发明涉及在园艺设施温室、地窑(ハウス·トンネル)内，即使使用无机硫剂处理土壤和/或植物也不产生劣化的被复薄膜和其使用方法。进而本发明涉及在园艺温度、地窖内用无机硫剂至少一次处理土壤和/或植物的方法及使用该处理方法的园艺、地窖栽培方法。
以往，用于园艺温室、地窑等用的被复膜，主要是使用聚氯乙烯膜和聚烯烃类树脂膜，例如聚乙烯薄膜、乙烯-醋酸乙烯共聚物薄膜等。在日本国内，大量地使用着聚氯乙烯被复膜。
园艺设施的目的是人为的调节植物栽培环境，制作出适合植物生长的环境，可将露天地栽培植物的不可能时期的变成能栽培，以及在生产率低的时期可以提高生产量。可是环境的要素(光、温度、湿度、二氧化碳浓度、水、土壤等)和植物的生长性是密切相关的，有必要在考虑经济性的基础上，制作出合适的生产环境。
形成称为设施的人工空间时，对于必需的被复材料要求的性能是依赖于使用目的和用途，进而与所栽培植物的不同而不同。温室和地窖用的一次性被复材料和保温帘等的被复材料所要求的主要性能有：耐气候性(在光照充足的屋外可长时间使用的耐用性能)、去滴性(温室、地窖内部由于是高湿度，被复膜内面因结露的微小水滴而被复盖，使得透明度恶化，防止上述现象的性能)、保温性(夜间可保持设施内高温度性能)、透光性(透明性)。
另一方面，在地球环境问题的日益高涨理论中，一种比废弃燃烧时发生盐酸气的聚氯乙烯被复膜更易于完全燃烧，而且不产生有害气体的聚烯烃类树脂被复膜更为引人注目。进而由于聚烯烃类树脂被复膜比农业用聚氯乙烯膜的机械特性(撕裂强度、耐寒性等)及耐气候性、热稳定性等优良，所以农业用聚氯乙烯膜正在被聚烯烃系树脂被复膜取代。
可是，近年来普及的农业用聚烯烃类树脂被复膜，应用在园艺设施温室上后，出现了由于农药而引起薄膜的耐久性显著下降的问题。在特开昭63-175072号公报中，公开了当使用有机硫类、有机氯类、有机磷类等农药时，在热可塑性树脂中配合了受阻胺类化合物和水滑石类化合物的抗农药性优良的农用薄膜。
近年来，在农药的低减趋势中，作为杀菌剂使用历史上极其古老的无机硫剂，即，石灰硫黄合剂、硫黄粉剂、水合硫黄剂、硫黄驱烟剂等，符合了消费者的安全性和自然潮流，并有使用量增加的趋势。
使用这些无机硫剂时，与使用有机类农药一样，往往也会引起农业用聚烯烃类树脂被复膜的耐气候性劣化，进而，对于如特开昭63-175072号公报中所记载的，即使在热可塑树脂中配合了受阻胺类化合物和水滑石类化合物的农用薄膜，当使用无机硫剂时，也未必能充分地保持耐气候性。
特别是果树栽培，由于是多年生，在结果实时期等的栽培重要时期，若薄膜产生劣化或破裂现象，那将会成为很大的问题。
本发明的目的是对于地球环境不产生破坏的聚烯烃类树脂为基材的被复膜构成的设施园艺、地窖，提供了使用无机硫剂的低量有机农药的园艺设施、地窖栽培用聚烯烃类树脂被复薄膜。
本发明人对于农用被复膜，特别是以聚烯烃类树脂为基材的被复膜，及使用它的低量有机农药的园艺设施方法进行了深入的研究，其结果发现了在由受阻胺类化合物、水滑石类化合物、紫外线吸收剂及聚烯烃类树脂构成的聚烯烃类树脂被复膜作成的温室内，使用无机硫剂对土壤和/或植物处理时，可以在解决薄膜耐气候性劣化问题条件下，对植物进行栽培，从而完成了本发明。
即，本发明涉及由受阻胺类化合物、水滑石类化合物、紫外线吸收剂及聚烯烃类树脂构成的，并应用于使用无机硫剂对土壤和/或植物处理的园艺设施温室、地窖栽培的聚烯烃类树脂被复薄膜及其使用方法。进而本发明提供了用无机硫剂，在用该被复膜被复的园艺设施温室、地窖内处理土壤和/或植物的方法，以及植物的栽培方法。
以下，详细地说明本发明。
本发明所使用的受阻胺类化合物，优选的是分子量250以上，具有4一位取代基的2，2，6，6-四烷基哌啶衍生物，作为其4位上的取代基可举出羧酸残基、烷氧基、烷氨基等，此外在N位上也可以用烷基取代。
具体的可举出下述(1)～(22)所示的化合物。
本发明所使用的受阻胺类化合物的加入量，从耐气候性观点看，优选为相当于聚烯烃类系树脂被复膜总重量的0.02重量％以上，更优选0.1重量％以上。从得到的被复膜的外观，特别是可以抑制模糊现象观点看，受阻胺类化合物的加入量优选相当于聚烯烃类树脂被复膜总重量的5重量％以下，更优选的是2重量％以下。此外，这些受阻胺类化合物可以单独使用，或二种以上混合使用。
受阻胺类化合物中，例如使用上述的(6)～(8)所示的化合物得到的被复膜的耐气候性和外观更为优良。
本发明中所使用的水滑石类可以举出用通式(1)表示的化合物，
M2+ 1-xAlx(OH)2(An-)x/n·mH2O (1)(式中，M2+表示从镁、钙及锌中选出的2价金属离子，X及m应满足以下条件，0＜x＜0.5、0≤m≤2，An-表示n价的阴离子)。
对于n价阴离子没有特定的限制，可以举出Cl-、Br-、I-、NO3 -、ClO4 -、SO4 2-、CO3 2-、SiO3 2-、HPO4 3-、HBO4 3-、PO4 3-、Fe(CN)4 3-、Fe(CN)4 4-、CH3COO-、C6H4(OH)COO-、(COO)2 2-、对苯二甲酸离子、萘磺酸离子等的阴离子。
具体例可以举出天然水滑石(Mg0.75Al0.25(OH)2(CO3)0.125·0.5H2O)、合成水滑石(Mg0.69Al0.31(OH)2(CO3)0.15·0.54H2O商品名DHT-4A(协和化学工业制造)等。
从改良耐气候观点看，本发明中所使用的水滑石类化合物的加入量优选为相当聚烯烃类树脂被复膜总重量的0.1重量％以上，更优选1重量％以上。另外从得到的被复膜透明性和薄膜强度观点来看，优选25重量％以下，更优选10重量％以下。水滑石类化合物的平均粒径在5μm以下时被复膜的透明性好，更优选的粒径是0.05～2μm。另外，为了提高对薄膜的分散性，可以用高级脂肪酸、高级脂肪酸的碱金属盐等进行的表面处理。
本发明所使用的紫外线吸收剂，大致分为二苯甲酮类紫外线吸收剂、苯并***类紫外线吸收剂、苯甲酸盐类紫外线吸收剂、氰基丙烯酸盐类紫外线吸收剂。具体的可以举出用下式(23)～(31)表示的化合物。
本发明所使用的紫外线吸收剂的加入量，从耐气候性观点看，优选为相当聚烯烃类树脂被复膜总重量的0.01重量％以上，更优选0.05重量％以上。另外从得到被复膜的外观、特别是可以抑制模糊现象观点看，优选3重量％以下，更优选1重量％以下，另外，这些紫外线吸收剂可单独使用，或者2种以上混合使用。
作为本发明使用的聚烯烃类树脂，可以举出聚乙烯、聚丙烯等的乙烯或碳原子数3～10的α烯烃均聚物；乙烯-丙烯共聚物、乙烯-1-丁烯共聚物、乙烯-4-甲基-1-戊烯共聚物、乙烯-己烯共聚物、乙烯-辛烯共聚物等的乙烯和碳原子数3～10的α烯烃共聚物；乙烯-醋酸乙烯共聚物、乙烯-丙烯酸共聚物、乙烯-甲基丙烯酸甲酯共聚物、乙烯-醋酸乙烯-甲基丙烯酸甲酯共聚物、离子型聚合物树脂等的以乙烯为主成分的乙烯和具有极性乙烯基的单体的共聚物等。
这些树脂中，聚乙烯、特别是密度0.93g/cm3以下的低密度聚乙烯、乙烯-α-烯烃共聚物或者含有醋酸乙烯30重量％以下的乙烯-醋酸乙烯共聚物等，从可得的透明性及柔软性优良，及廉价的薄膜方面考虑是优良的。
本发明聚烯烃类树脂被复薄膜的厚度，从得薄膜强度方面考虑，优选0.02mm以上，另外从中间加工性和被复操作性等二次加工性考虑，优选0.3mm以下。更优选的薄膜厚度为0.03～0.2mm。
在本发明的被复薄膜中，在不影响本发明目的的范围内，还可以添加去滴剂、热稳定剂、耐气候剂、填充剂、防雾剂、润滑剂、着色剂等各种的添加剂。
例如，为了防止由于结露产生的微小水滴复盖被复薄膜的内面，而引起该薄膜透明性的恶化现象，可添加的去滴剂，该去滴剂在常温(23℃)有固体状的和液体状的。作为固体状的去滴剂有非离子性表面活性剂，例如山梨糖醇酐单硬酯酸酯、山梨糖醇酐十六烷酸酯、山梨糖醇酐廿二烷酸酯等的山梨糖醇酐脂肪酸酯类表面活性剂、甘油单月桂酸酯、甘油单十六烷酸酯、甘油单硬脂酸酯、二甘油二硬脂酸酯、三甘油单硬脂酸酯等的甘油脂肪酸酯类表面活性剂、聚乙二醇单十六烷酸酯、聚乙二醇单硬脂酸酯等的聚乙二醇类表面活性剂、烷基酚的烯化氧加成物、山梨糖醇酐/甘油缩合物和有机酸形成的酯等。另外，作为液体的去滴剂可以举出例如：甘油单油酸酯、二甘油单油酸酯、二甘油倍半单油酸酯、四甘油单油酸酯，六甘油单油酸酯，甘油五油酸酯，二甘油五油酸酯，四甘油五油酸酯，六甘油五油酸酯，四甘油单月桂酸酯，六甘油单月桂酸酯等的甘油类脂肪酸酯，或者山梨糖醇酐单油酸酯、山梨糖醇酐二油酸酯、山梨糖醇酐五油酸酯等的山梨糖醇酐脂肪酸酯。作为防雾剂可以举出具有全氟烷基、W-氢氟烷基的氟化物(特别是含氟表面活性剂)、具有烷基硅氧基的硅类化合物(特别是硅酮类表面活性剂)等。作为热稳定剂有2，6-二烷基苯酚衍生物和2-烷基苯酚衍生物等的受阻酚类化合物、含有二价硫原子硫醇键或具有硫醇键的含硫化合物，或者含有3价磷原子亚磷酸酯类化合物等；作为耐气候剂有含镍化合物等，作为填充剂有氧化镁、氧化钙、氧化铝、氧化硅、氧化钛、氢氧化锂、氢氧化镁、氢氧化钙、氢氧化铝、碳酸镁、碳酸钙、硫酸钾、硫酸镁、硫酸钙、硫酸锌、硫酸铝、磷酸锂、磷酸钠、磷酸钾、磷酸钙、硅酸镁、硅酸钙、硅酸铝、硅酸钛、铝酸钠、铝酸钾、铝酸钙、铝硅酸钠、铝硅酸钾、铝硅酸钙、高岭土、滑石、白土等。
本发明的聚烯烃类树脂被复膜可以是单层结构，也可以是二层以上叠层的多层结构。多层结构时，各层是由受阻胺类化合物、水滑石类化合物以及紫外线吸收剂中的至少1种和聚烯烃类树脂构成的组合物。各层树脂的、添加剂的加入比例可以不同。常常使用3种3层和2种3层的结构，在设施的外侧的层面上进行防尘处理，设施内侧的层面可进行去滴、防雾处理，在中间层中可以使用以无机填充剂等为主的保温剂。
作为去滴的处理方法，除了加入上述去滴剂的方法外，也可以至少在该膜的内面(设施内侧面)形成一个防浊性(去滴性)的被膜的方法。
这种防浊性被膜可以举出如特公昭49-32668号公报、特公昭50-11348号公报等为代表的使用胶体硅和胶体铝的无机氧化凝胶被膜、及作为其应用在特公昭63-45432号公报、特公昭63-45717号公报、特公昭64-2158号公报、特开平3-207643号公报为代表的无机氧化物凝胶和有机化合物(表面活性剂和树脂等)等的被复膜、以表面活性剂为主成分的液体被复膜、以亲水性树脂为主成分的膜(作为亲水性树脂可举出聚乙烯醇、多糖类、聚丙烯酸等，成膜方法可以采用涂敷法，也可在制膜后叠层成膜)等。另外，这些防浊性被膜可以叠成2层以上使用。
本发明的聚烯烃类树脂被复膜例如可用以下的方法制造。在聚烯烃类树脂中加入规定量的受阻胺类化合物、水滑石类化合物、紫外线吸收剂及必要时，加入去滴剂、热稳定剂、耐气候剂等各种添加剂，而后用带式混合机、超级混练机、封闭式混合机、单轴或双轴挤出机等的通常的混合、混练机进行混合、混练。接着用挤出T型膜成形法、吹塑膜成形法等的通常的成形法制造出薄膜。
用上述方法得到的聚烯烃类树脂被复膜可适用于园艺设施温室、地窖中的被复薄膜。
本发明中所称的园艺设施温室、地窖，是指通常农家等使用的，用本发明的聚烯烃类树脂被复膜而被复了的园艺温室、地窖。另外在园艺设施温室、地窖内若设置内衬幕时，也可以将该薄膜作为内衬幕使用。
用于本发明的无机硫剂，例如可以举出石灰硫黄合剂、硫黄粉剂、水合硫黄剂、硫黄驱烟剂、石灰硫黄气溶胶等。这些无机硫黄剂在农药手册1985年版(农药手册1985年版编委员会编，日本植物防疫协会发行1985年)上有如下的记载″无机硫剂中作为杀菌成分可认为是硫黄单体的微粒子。其作用机理是通过单质硫来切断病原菌的电子传递***，来达到阻止菌的ATP合成，消灭菌的目的。作为杀菌剂的应用是1851年开始于在法国使用的石灰硫黄合剂。其作用特性具有霉病、白粉病的杀菌效果，对于叶螨、介彀虫具有杀虫效果。广泛地适用于以苹果、柿子、栗子、梨、桃、葡萄、密柑等为主的果树类以及草莓、甜瓜、西瓜、黄瓜、白菜、酒花、麦类、蔷薇、菊、山黧豆属、茶、松、桑、芝麻等(其用途，使用方法等进一步有详细的记载″。其主要目的是杀菌、杀虫，用于土壤和/或植物的处理。
使用本发明的无机硫剂处理土壤和/或植物的方法，通常是在用本发明的聚烯烃类树脂被复膜复盖了的园艺设施、地窖内，至少散布1次无机硫剂，散布的时期为在开始栽培植物前后的任何一个时期。无机硫剂的散布方法及散布量可按上述农药手册叙述的方法及量即可，对此没有特殊的限制。
用本发明进行的植物园艺设施温室、地窖的栽培方法，包括了在用本发明的被复膜覆盖的园艺设施、地窖内，至少进行1次用无机硫剂对土壤和/或植物进行处理的方法，其他没有特殊的限制。作为植物可举出苹果、柿子、梨、桃、葡萄、密柑等果树类和草莓、甜瓜、西瓜、黄瓜、白菜、蔷薇、菊等。无机硫剂优选的是使用上述的石灰硫黄合剂、水合硫黄剂、硫黄驱烟剂等。无机硫黄剂含有一般的天然硫黄元素，其目的是用来减少有机农药的散布次数。特别是对于蔷微(白粉病、叶螨)、草莓(白粉病、叶螨、灰色霉病)、菊(白霉病)等的栽培中，使用电热式硫黄驱蒸具有大大减低农药用量的效果。另外，在柿子、葡萄、密柑等的果树类栽培中最好使用石灰硫黄合剂。
使用本发明的聚烯烃类树脂被复薄膜的温室、地窖进行栽培中，用无机硫剂处理土壤和/或植物后，可以有效地抑制通常引起的被复薄膜耐气候性下降的问题，而且可减少使用农药。特别是对于果树栽培，因为是多年生植物，如果在结果实的时期等的栽培重要时期发生薄膜劣化或破裂会造成很大的问题，但是使用本发明的被复薄膜可以作到长期稳定地进行栽培。进而对于草莓、甜瓜、西瓜、黄瓜、蔷薇、盆花类、蕨类等可用电热式硫黄驱烟方法作到降低使用有机农药的栽培。
根据本发明，可以提供对无机硫剂有耐性，适于环境的聚烯烃类树脂被复膜，可以作到显著地降低有机农药的植物栽培。
进而，本发明的聚烯烃类树脂被复膜，作成复合层薄膜也是有效的。
以下是本发明的实施例，但本发明不受此限制，另外，实施例中的试验方法如下。
耐气候试验：
将用JIS1号哑铃型冲压机冲出的试片浸渍在稀释7倍的石灰硫黄合剂(多硫化钙27.5％水溶液，北兴化学工业制)中24小时后，进行洗涤、干燥处理。将此试片放在顶部开口的气候仪中(斯加试验机社制)，在黑体板温度63℃的条件下曝露一定时间。对于曝露过的试片，使用自动曲线机DSS100(岛津制作所制)进行拉伸试验，测定拉伸率(％)，求出拉伸率相当于原试片的拉伸率一半时的耐气候试验时间(以下称为″耐气候性半衰期″)。此时间的值越大，越表示耐气候性优良，将1000小时作为本试验合格标准。
拉伸率(％)＝[断裂时的标线间距离(mm)
-拉伸试验前的标线间距离
(mm)]÷[拉伸试验前的标线
距离(mm)]×100
实施例1
在乙烯-醋酸乙烯共聚物(商品名埃巴特H2020，醋酸乙烯含量15重量％，住友化学工业制)中，加入受阻胺类化合物A(商品名其努品622-LD其巴盖义制)0.6重量％、水滑石类化合物(商品名DHT4A协和化学工业制)8.0重量％、紫外线吸收剂(商品名斯密索布130住友化学制)0.1重量％、抗氧化剂(商品名伊尔卡克斯1010其巴盖义制)0.1重量％、作为防浊剂的单甘油单硬脂酸酯1.4重量％、二甘油二硬脂酸酯0.6重量％、作为润滑剂的硬脂酸酰胺0.2重量％(均表示树脂组合物中的重量％)，使用密闭混合机，在130℃下混练5分钟后，用造粒机进行造粒，得到组合物颗粒。将其作为树脂组合物①。接着在乙烯-醋酸乙烯共聚物中(商品名埃巴特D2011，醋酸乙烯含量5重量％，住友化学工业制)加入受阻胺类化合物A0.6重量％、紫外线吸收剂(商品名斯密索布130，住友化学制)0.1重量％、抗氧化剂R0.1重量％、单甘油单硬脂酸酯1.4重量％、二甘油二硬脂酸酯0.6重量％、硬脂酸酰胺0.2重量％(均表示树脂组合物中的重量％)，与树脂组合物①同样地得到颗粒。将其作为树脂组合物②。以树脂组合物①作为中间层，树脂组合物②作为两个外层，使用吹塑成形机制作膜厚为100μm的薄膜(中间层60μm、两外层各20μm)，进行耐气候性试验。结果如第1表所示得到优良的薄膜。
实施例2～4
除了按第1表进行配合外，其它与实施例1相同地得到薄膜，进行耐气候试验。其结果与第1表一样显示了优良的性能。
实施例5
除了在实施例1中的树脂组合物①②中分别添加作为防雾剂的含氟表面活性剂(商品名尤尼达因DS403、大金工业制)0.1重量％以外，与实施例1一样地得到薄膜，进行耐气候试验。耐气候半衰期是1000小时以上。
比较例1～4
除了按第1表进行配合外，与实施例同样地得到薄膜，进行耐气候试验。其结果如第1表所示，性质低劣。(但是在耐气候性试验中，在未用石灰硫黄合剂液浸渍时，除去比较例3，其它的耐气候半衰期都是1000小时以上。)
实施例6
在用实施例1的薄膜被复了的温室中进行葡萄栽培试验(岛根具：第拉威、东西栋AP温室、1994年2月～8月间，栽培，二个月一次，每一反(991.7平方公尺)以1001的比例散布20倍的石灰硫黄合剂稀释液。8月份取南面薄膜作为试样，按照上述耐气候试验标准进行拉伸试验。结果，拉伸强度，拉伸度均有90％以上的保持率，完全没有劣化。
比较例5：
使用比较例1的薄膜进行与实施例5相同的试验，结果一部分温室的膜破裂。
实施例7
在用实施例1的薄膜被复了的温室中进行草莓栽培试验(岐阜县：东西栋AP温室.1993年10月～5月间栽培，用电热式硫黄驱烟剂(商品名新果那，东海物产制)薰蒸，室内每100m3，设一台薰蒸装置，每天蒸8小时，烟剂用量为2个月用50g。栽培期间内完全抑制了白粉病，叶螨，灰色霉病)5月将南面的膜作试样，按照上述耐气候试验标准进行拉伸试验。结果，拉伸强度，拉伸度均有90％以上的保持率，完全没有劣化。
比较例6
使用比较例1的薄膜，进行与实施例6相同的试验。结果，拉伸强度、拉伸度均低到约40％的保持率。
表1：
| 中间层 | 两外层 | 耐气候性半衰期(时间) | |||||||||||||
| 树脂种类 | 受阻胺类化合物 | 紫外线吸收剂 | 无机化合物 | 树脂 | 受阻胺类化合物 | 紫外线吸收剂 | 无机化合物 | ||||||||
| A(重量％) | B(重量％) | 种类 | 加入量(重量％) | 种类 | 加入量(重量％) | 种类 | A(重量％) | B(重量％) | 种类 | 加入量(重量％) | 种类 | 加入量(重量％) | |||
| 实施例1 | a | 0.60 | ---- | X | 0.10 | A | 8.0 | b | 0.60 | ---- | X | 0.10 | - | ---- | ＞1000 |
| 实施例2 | c | 0.60 | ---- | Y | 0.07 | A | 8.0 | c | 0.60 | ---- | Y | 0.07 | A | 2.0 | ＞1000 |
| 实施例3 | a | 0.35 | 0.45 | - | ---- | A | 3.0 | d | 0.35 | 0.45 | X | 0.30 | A | 3.0 | ＞1000 |
| 实施例4 | b | 0.35 | 0.45 | X | 0.20 | A | 3.0 | b | 0.35 | 0.45 | X | 0.20 | A | 3.0 | ＞1000 |
| 比较例1 | a | 0.60 | ---- | - | ---- | A | 8.0 | b | 0.60 | ---- | - | ---- | - | ---- | 700 |
| 比较例2 | a | 0.60 | ---- | X | 0.10 | A | ---- | b | 0.60 | ---- | X | 0.10 | - | ---- | 450 |
| 比较例3 | a | ---- | ---- | Y | 0.10 | A | 8.0 | b | ---- | ---- | Y | 0.10 | A | 2.0 | 300＞ |
| 比较例4 | b | 0.35 | 0.45 | X | 0.20 | B | 3.0 | b | 0.35 | 0.45 | X | 0.20 | B | 3.0 | 600 |
树脂a：埃巴特H2020(住友化学工业制，乙烯醋酸乙烯共聚物，醋酸乙烯15重量％)
树脂b：埃巴特D2011(住友化学工业制，乙烯醋酸乙烯共聚物，醋酸乙烯5重量％)
树脂c：斯密卡森F208-0(住友化学工业制，低密度聚乙烯)
树脂d：斯密卡森LFA201-0(住友化学工业制，低密度聚乙烯)(乙烯-1-丁烯共聚物)
受阻胺类化合物A：其努品622-LD(其巴盖义社制)
受阻胺类化合物B：基马索布944-LD(其巴盖义社制)
紫外线吸收剂X：斯密索布130(住友化学工业制，羟基二苯甲酮类紫外线吸收剂)
紫外线吸收剂Y：斯密索布300(住友化学工业制羟基苯并***类紫外线吸收剂)
无机化合物A：DHT4A(协合化学工业制，合成水滑石)
无机化合物B：斯诺马克SP-10(金星马蒂克制，天然硅粉碎品)
参考例1
在乙烯-醋酸乙烯共聚物(商品名埃巴特H2020，醋酸乙烯含量15重量％，住友化学工业制)中，加入受阻胺类化合物A(商品名其努品622-LD其巴盖义制)0.3重量％，水滑石类化合物(商品名DHT4A协和化学工业制)3，0重量％，紫外线吸收剂(商品名，斯密索布130住友化学制)0.1重量％，抗氧化剂R(商品名伊尔卡克斯1010，其巴盖义制)0.1重量％，作为防浊剂的单甘油单硬脂酸酯1.4重量％，二甘油二硬脂酸酯0.6重量％，作为润滑剂的硬脂酸酰胺0.2重量％(均表示树脂组合物中的重量％)，使用密闭混合机，在130℃下混练5分钟后，用造粒机进行造粒，得到组合物颗粒。将其作为树脂组合物(a)。接着在乙烯-醋酸乙烯共聚物中(商品名埃巴特D2011，醋酸乙烯含量5重量％，住友化学工业制)加入受阻胺类化合物A0.3重量％，紫外线吸收剂(商品名斯密索布130住友化学制)0.1重量％，抗氧化剂R0.1重量％、单甘油单硬脂酸酯1.4重量％、二甘油二硬脂酸酯0.6重量％、硬脂酸酰胺0.2重量％(均表示树脂组合物中的重量％)，与树脂组合物(a)同样地得到颗粒，将其作为树脂组合物(b)。以树脂组合物(a)作为中间层，树脂组合物(b)作为两个外层，使用吹塑成形机制作膜厚100μm的薄膜(中间层60μm、两外层各20μm)，在不进行石灰硫黄剂处理下进行耐气候性试验。结果，耐气候半衰期为950小时。
参考例2
除了不使用紫外线吸收剂(商品名斯密索布130，住友化学制)以外，与参考例1同样地制作膜厚100μm的膜(中间层60μm、两外层各20μm)，在不进行石灰硫黄剂处理条件下，进行耐气候试验。结果耐气候半衰期为900小时。
从上述参考例可以看出，不用无机硫剂处理时，紫外线吸收剂的添加与否，对于耐气候性的差别影响很微小。与此相反，当用无机硫剂处理后，由实施例1和比较例1可明显地看出紫外线吸收剂的效果极大。
Claims (32)
1，聚烯烃类树脂被覆膜，其特征是由受阻胺类化合物、水滑石类化合物、紫外线吸收剂及聚烯烃类树脂组成，使用在用无机硫剂处理土壤和/或植物的园艺设施温室、地窖的栽培中。
2，权利要求1所述的聚烯烃类树脂被覆膜，其中的聚烯烃类树脂被覆膜含有受阻胺类化合物0.02-5重量％、水滑石类化合物0.1-25重量％、紫外线吸收剂0.01-3重量％。
3，权利要求2所述的聚烯烃类树脂被覆膜，其中的聚烯烃类树脂被覆膜至少是由2层以上组成的多层结构。
4，权利要求3所述的聚烯烃类树脂被覆膜，其中的聚烯烃类树脂被覆膜是由3层组成的多层结构。
5，权利要求2或3所述的聚烯烃类树脂被覆膜，其中的聚烯烃类树脂是聚乙烯、乙烯-α-烯烃共聚物及乙烯-醋酸乙烯共聚物中的至少一种。
6，权利要求5所述的聚烯烃类树脂被覆膜，其中的聚乙烯是密度0.93g/cm3以下的低密度的聚乙烯。
7，权利要求1所述的聚烯烃类树脂被覆膜，其中的无机硫剂是从石灰硫磺合剂、硫磺粉剂、水合硫黄剂，硫磺驱烟剂及石灰硫磺气溶胶中选出的至少1种。
8，在用聚烯烃类树脂被覆膜被覆的园艺设施温室、地窖内，用无机硫剂处理土壤和/或植物的方法，该膜是由受阻胺类化合物、水滑石类化合物、紫外线吸收剂及聚烯烃类树脂制成的。
9，权利要求8所述的方法，其中的聚烯烃类树脂被覆膜含有受阻胺类化合物0.02-5重量％、水滑石类化合物0.1-25重量％、紫外线吸收剂0.01-3重量％。
10，权利要求9所述的方法，其中的聚烯烃类树脂被覆膜至少是由2层以上组成的多层结构。
11，权利要求10所述的方法，其中的聚烯烃类树脂被覆膜是由3层组成的多层结构。
12，权利要求9或10所述的方法，其中的聚烯烃类树脂是从聚乙烯、乙烯-α-烯烃共聚物及乙烯-醋酸乙烯共聚物中选出的至少1种。
13，权利要求12所述的方法，其中的聚乙烯是密度0.93g/cm3以下的低密度的聚乙烯。
14，权利要求8所述的方法，其中的无机硫剂是从石灰硫磺合剂、硫磺粉剂、水合硫黄剂、硫磺驱烟剂及石灰硫磺气溶胶中选出的至少1种。
15，使用聚烯烃类树脂被覆膜的植物栽培方法，该方法是在用聚烯烃类树脂被覆膜被覆的园艺设施温室、地窖内，并至少1次用无机硫剂处理土壤和/或植物，上述膜是由受阻胺类化合物、水滑石类化合物、紫外线吸收剂及聚烯烃类树脂组制成。
16，权利要求15所述的植物栽培方法，其中的聚烯烃类树脂被覆膜含有受阻胺系化合物0.02-5重量％、水滑石类化合物0.1-25重量％、紫外线吸收剂0.01-3重量％。
17，权利要求16所述的植物栽培方法，其中的聚烯烃类树脂被覆膜至少是由2层以上组成的多层结构。
18，权利要求17所述的植物栽培方法，其中的聚烯烃类树脂被覆膜是由3层组成的。
19，权利要求16或17所述的植物栽培方法，其中的聚烯烃类树脂是从聚乙烯、乙烯-α-烯烃共聚物及乙烯-醋酸乙烯共聚物中选出的至少1种。
20，权利要求19所述的植物栽培方法，其中的聚烯烃类树脂是密度0.93g/cm3以下的低密度的聚乙烯。
21，权利要求15所述的植物栽培方法，其中的无机硫剂是从石灰硫磺合剂、硫磺粉剂、水合硫黄剂、硫磺驱烟剂及石灰硫磺气溶胶中选出的至少1种。
22，权利要求15所述的植物栽培方法，其中的植物是果树类。
23，权利要求15所述的植物栽培方法，其中的植物是草莓、甜瓜、西瓜、黄瓜、蔷薇、菊。
24，在园艺设施温室、地窖内，至少1次用无机硫剂处理土壤和/或植物的园艺设施温室、地窖栽培中，由受阻胺类化合物、水滑石类化合物、紫外线吸收剂及聚烯烃类树脂制成的聚烯烃树脂被覆膜作为设施园艺温室、地窖被覆膜的应用。
25，权利要求24所述的被覆膜的用途，其中的聚烯烃类树脂被覆膜含有受阻胺系化合物0.02-5重量％、水滑石类化合物0.1-25重量％、紫外线吸收剂0.01-3重量％。
26，权利要求25所述的被覆膜的应用，其中的聚烯烃类树脂被覆膜至少是由2层以上组成的多层结构。
27，权利要求26所述的被覆膜的应用，其中的聚烯烃类树脂被覆膜是由3层组成的。
28，权利要求27所述的被覆膜的应用，其中的聚烯烃类树脂被覆膜是从聚乙烯、乙烯-α-烯烃共聚物及乙烯-醋酸乙烯共聚物中选出的至少1种的聚烯烃类树脂被覆膜。
29，权利要求28所述的被覆膜的应用，其中聚烯烃树脂被覆膜是密度为0.93g/cm3以下的低密度聚乙烯树脂被覆膜。
30，权利要求24所述的被覆膜的应用，其中的无机硫剂是从石灰硫磺合剂、硫磺粉剂、水合硫黄剂、硫磺驱烟剂及石灰硫磺气溶胶中选出的至少1种用于处理园艺设施温室、地窖栽培中，使用由受阻胺类化合物、水滑石类化合物、紫外线吸收剂及聚烯烃系树脂制成的聚烯烃树脂被覆膜。
31，权利要求24所述的被覆膜的应用，其中园艺设施温室、地窖栽培是果树类植物园艺设施温室、地窖栽培，使用由受阻胺类化合物、水滑石类化合物、紫外线吸收剂及聚烯烃类树脂制成的聚烯烃树脂被覆膜。
32，权利要求24所述的被覆膜的应用，其中设施园艺、地窖栽培是草莓、甜瓜、西瓜、黄瓜、蔷薇、菊类植物的设施园艺、地窖栽培，使用由受阻胺类化合物、水滑石类化合物、紫外线吸收剂及聚烯烃类树脂制成的聚烯烃树脂被覆膜。