CN113078054A - 一种电极层的制备方法及半导体结构 - Google Patents
一种电极层的制备方法及半导体结构 Download PDFInfo
- Publication number
- CN113078054A CN113078054A CN202110320608.2A CN202110320608A CN113078054A CN 113078054 A CN113078054 A CN 113078054A CN 202110320608 A CN202110320608 A CN 202110320608A CN 113078054 A CN113078054 A CN 113078054A
- Authority
- CN
- China
- Prior art keywords
- layer
- electrode layer
- graphene
- target substrate
- electrode
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种电极层的制备方法及半导体结构,该制备方法包括以下步骤:提供一基底,并依次形成石墨烯层、至少一电极层及支撑层;将由电极层及支撑层组成的叠层结构从石墨烯层表面机械剥离;将叠层结构转移至目标衬底,电极层与目标衬底的表面接触;去除支撑层,并使电极层留在目标衬底的表面。本发明通过在石墨烯上制作电极层,利用石墨烯与电极层间较弱的范德华接触易于剥离的特点,实现任意电极层的剥离,并转移至任意目标衬底形成范德华接触,扩展了电极层的可应用范围,减少了电极层制作过程对目标衬底材料的损伤,有助于提高器件性能,并降低电极层的制作成本。
Description
技术领域
本发明属于半导体集成电路技术领域,涉及一种电极层的制备方法及半导体结构。
背景技术
电极制作是半导体领域中不可或缺的加工工艺。然而一般通过电子束蒸发或热蒸发在衬底上形成电极的方法会在一定程度上破坏衬底材料的结构,进而影响衬底材料的性能,尤其对于原子级厚度的二维材料影响最大。
因此,如何提供一种电极层的制备方法及半导体结构,以减少对衬底的损伤,并提升器件的电学性能,成为本领域技术人员亟待解决的一个重要技术问题。
发明内容
鉴于以上所述现有技术的缺点,本发明的目的在于提供一种电极层的制备方法及半导体结构,用于解决现有技术中电极层制作过程中容易损伤衬底,导致器件的电学性能下降的问题。
为实现上述目的及其他相关目的,本发明提供一种电极层的制备方法,包括以下步骤:
提供一基底;
形成石墨烯层于所述基底的上表面;
形成至少一电极层于所述石墨烯层的上表面;
形成支撑层于所述石墨烯层的上表面,所述支撑层覆盖所述电极层;
将由所述电极层及所述支撑层组成的叠层结构从所述石墨烯层表面机械剥离;
将所述叠层结构转移至目标衬底,所述电极层与所述目标衬底的表面接触;
去除所述支撑层,并使所述电极层留在所述目标衬底的表面。
可选地,所述基底采用刚性基底。
可选地,所述基底包括锗层、碳化硅层、锗硅层、硅层、铜层、镍层、陶瓷层及玻璃层中的至少一种。
可选地,所述石墨烯层包括单层石墨烯及多层石墨烯中的一种或多种。
可选地,形成所述电极层的方法包括化学气相沉积法、物理气相沉积法、原子层沉积法中的至少一种。
可选地,所述化学气相沉积法包括等离子体增强化学气相沉积法,所述物理气相沉积法包括电子束蒸发法及热蒸发法中的至少一种,所述原子层沉积法包括等离子增强原子层沉积法。
可选地,所述电极层的材质包括金属及多晶硅中的至少一种。
可选地,形成所述支撑层包括以下步骤:
施加有机溶液于所述电极层及所述石墨烯层的上表面;
干燥所述有机溶液以得到所述支撑层。
可选地,所述有机溶液包括光刻胶溶液。
可选地,形成所述支撑层包括以下步骤:
提供一柔性膜层以覆盖所述电极层;
通过加热加压使所述柔性膜层软化并紧贴所述电极层及所述石墨烯层的上表面以构成所述支撑层。
可选地,采用胶带粘附所述支撑层背面以将所述叠层结构从所述石墨烯层表面机械剥离,或者直接掀起所述支撑层以将所述叠层结构从所述石墨烯层表面机械剥离。
可选地,通过溶解法去除所述支撑层。
可选地,通过加热所述支撑层以降低所述支撑层与所述电极层之间的粘附力,并通过机械剥离法去除所述支撑层。
可选地,所述电极层与所述目标衬底表面的接触包括范德华接触。
可选地,所述目标衬底包括二维材料层及三维材料层中的至少一种。
本发明还提供一种半导体结构,包括:
目标衬底;
至少一电极层,位于所述目标衬底上,其中,所述电极层是通过如上任意一项所述的电极层的制备方法转移于所述目标衬底上。
如上所述,本发明的电极层的制备方法及半导体结构通过在石墨烯上制作电极层,利用石墨烯与电极层间较弱的范德华接触易于剥离的特点,实现任意电极层的剥离;将剥离的电极层转移至任意目标衬底形成范德华接触,扩展了电极层的可应用范围,同时转移工艺减少了电极层制作过程对目标衬底材料的损伤,实现了更优性能的电极层接触,也降低了制作过程所需的工艺条件,因此降低了电极层的制作成本。
附图说明
图1显示为本发明的电极层的制备方法的工艺流程图。
图2显示为本发明的电极层的制备方法提供一基底的示意图。
图3显示为本发明的电极层的制备方法形成石墨烯层于所述基底的上表面的示意图。
图4显示为本发明的电极层的制备方法形成电极层于所述石墨烯层的上表面的示意图。
图5显示为所述电极层在所述石墨烯层上的一种平面布局图。
图6显示为本发明的电极层的制备方法形成支撑层于所述石墨烯层上表面的示意图。
图7显示为本发明的电极层的制备方法将由所述电极层及所述支撑层组成的叠层结构从所述石墨烯层表面机械剥离的示意图。
图8显示为本发明的电极层的制备方法将所述叠层结构转移至目标衬底的示意图。
图9显示为本发明的电极层的制备方法去除所述支撑层,并使所述电极层留在所述目标衬底的表面的示意图。
元件标号说明
S1~S7 步骤
1 基底
2 石墨烯层
3 电极层
4 支撑层
5 目标衬底
具体实施方式
以下通过特定的具体实例说明本发明的实施方式,本领域技术人员可由本说明书所揭露的内容轻易地了解本发明的其他优点与功效。本发明还可以通过另外不同的具体实施方式加以实施或应用,本说明书中的各项细节也可以基于不同观点与应用,在没有背离本发明的精神下进行各种修饰或改变。
请参阅图1至图9。需要说明的是,本实施例中所提供的图示仅以示意方式说明本发明的基本构想,遂图式中仅显示与本发明中有关的组件而非按照实际实施时的组件数目、形状及尺寸绘制,其实际实施时各组件的型态、数量及比例可为一种随意的改变,且其组件布局型态也可能更为复杂。
实施例一
本实施例中提供一种电极层的制备方法,请参阅图1,显示为该方法的工艺流程图,包括以下步骤:
S1:提供一基底;
S2:形成石墨烯层于所述基底的上表面;
S3:形成至少一电极层于所述石墨烯层的上表面;
S4:形成支撑层于所述石墨烯层的上表面,所述支撑层覆盖所述电极层;
S5:将由所述电极层及所述支撑层组成的叠层结构从所述石墨烯层表面机械剥离;
S6:将所述叠层结构转移至目标衬底,所述电极层与所述目标衬底的表面接触;
S7:去除所述支撑层,并使所述电极层层留在所述目标衬底的表面。
首先请参阅图2,执行步骤S1:提供一基底1。
作为示例,所述基底1采用刚性基底,以为后续制作的各层材料提供良好的支撑。所述基底1包括但不限于锗层、碳化硅层、锗硅层、硅层、铜层、镍层、陶瓷层及玻璃层中的至少一种,例如所述衬底1可以是单一的锗层或碳化硅层,也可以是硅层/铜层叠层、硅层/镍层叠层、陶瓷层/铜层叠层、陶瓷层/镍层叠层、玻璃层/铜层叠层、玻璃层/镍层叠层、硅层/锗硅层/锗层叠层、硅层/锗层叠层等。
然后请参阅图3,执行步骤S2:形成石墨烯层2于所述基底1的上表面。
作为示例,可采用化学气相沉积法、电弧法或其他合适的方法形成所述石墨烯层2于所述基底1的上表面,所述石墨烯层2包括但不限于单层石墨烯、多层石墨烯中的一种或多种。
本实施例中,优选采用锗基底,并采用化学气相沉积法在所述锗基底表面生长得到单层石墨烯。
需要指出的是,多层石墨烯在不同区域可能具有不同层数的石墨烯,表面较为粗糙,后续制备的电极层也具有相对粗糙的下表面,而单层石墨烯具有非常光滑的表面,使得制备于单层石墨烯表面的电极层也具有更光滑的下表面,且由于单层石墨烯的层数均一,在后续剥离过程中电极层的表面不易残留石墨烯。
在另一实施例中,也可采用碳化硅基底直接生长得到所述石墨烯层2,其中,在加热过程中,碳化硅基底表面的碳析出并重组得到所述石墨烯层2。
再请参阅图4,执行步骤S3:采用化学气相沉积法(CVD)、物理气相沉积法(PVD)、原子层沉积法(ALD)中的至少一种或其它合适的方法形成至少一电极层3于所述石墨烯层2的上表面。所述化学气相沉积法包括但不限于等离子增强化学气相沉积法(PECVD),所述物理气相沉积法包括但不限于电子束蒸发法、热蒸发法等,所述原子层沉积法包括但不限于等离子增强原子层沉积法(PEALD)。
作为示例,所述电极层3的材质包括但不限于金属及多晶硅中的至少一种,所述金属包括但不限于钨、铝、钌、钯、铂、钴、镍、氮化钛、氮化钽等材料中的一种或多种。所述电极层3可作为栅电极层或其它功能层。
作为示例,可通过在所述石墨烯层2表面沉积电极材料,并图形化所述电极材料,得到电极层阵列。
在另一实施例,也可在所述石墨烯层2表面形成光刻胶层,并图形化所述光刻胶层以得到多个暴露出所述石墨烯层2的开口,然后沉积电极材料于所述开口中及所述光刻胶层表面,并剥离所述光刻胶层以得到电极层阵列。
作为示例,请参阅图5,显示为所述电极层3在所述石墨烯层2上的一种平面布局图。
需要指出的是,电极层阵列的具体排布规则可根据需要进行调整,不以图5所呈现的示例为限。
再请参阅图6,执行步骤S4:形成支撑层4于所述石墨烯层2的上表面,所述支撑层4覆盖所述电极层3。
作为示例,可通过施加有机溶液于所述电极层3及所述石墨烯层2的上表面,并干燥所述有机溶液以得到所述支撑层5。所述有机溶液包括但不限于光刻胶溶液,例如PMMA(聚甲基丙烯酸甲酯)光刻胶溶液。施加所述有机溶液的方法包括但不限于旋涂法。
在另一实施例中,也可通过提供一成型的柔性膜层以覆盖所述电极层3,并通过加热加压使所述柔性膜层软化并紧贴所述电极层3及所述石墨烯层2的上表面以构成所述支撑层4。
再请参阅图7,执行步骤S5:将由所述电极层3及所述支撑层4组成的叠层结构从所述石墨烯层2表面机械剥离。
具体的,由于所述石墨烯层2不存在或仅存在极少量的悬挂键,因此所述电极层3与所述石墨烯层2之间主要通过较弱的范德华力接触,因此所述叠层结构易于从所述基底1表面的所述石墨烯层2表面剥离下来。
作为示例,可采用胶带粘附所述支撑层4背面以将所述叠层结构从所述石墨烯层2表面机械剥离,或者直接掀起所述支撑层4以将所述叠层结构从所述石墨烯层2表面机械剥离。
再请参阅图8,执行步骤S6:将所述叠层结构转移至目标衬底5并使所述叠层结构与所述目标衬底5贴合,其中,所述电极层3与所述目标衬底5的表面接触。
作为示例,所述目标衬底5包括二维材料层及三维材料层中的至少一种,所述二维材料层包括但不限于石墨烯、过渡金属硫族化合物、黑磷等原子级厚度的二维材料,所述三维材料层包括但不限于硅、锗、锗硅、绝缘体上硅、绝缘体上锗硅、III-V族化合物、钙钛矿材料等三维半导体衬底,所述目标衬底5中可预先制备有沟道结构或其它所需的结构。
再请参阅图9,执行步骤S7:去除所述支撑层4,并使所述电极层3留在所述目标衬底5的表面。
作为示例,当所述支撑层4较薄时,或者容易撕裂时,或者经过一定处理后所述支撑层4与所述目标衬底5的结合力仍大于所述支撑层4与所述电极层3的结合力时,可通过溶解法去除所述支撑层4。当所述支撑层4较厚,例如大于数百微米时,或者所述支撑层4不易撕裂时,或者所述支撑层4与所述目标衬底5的结合力小于所述支撑层4与所述电极层3的结合力时,可通过机械剥离法去除所述支撑层4,在机械剥离所述支撑层4前,可通过加热所述支撑层以降低所述支撑层与所述电极层之间的粘附力,使得所述支撑层4更易剥离。
至此,将制备于所述石墨烯层2上的电极层3转移至所述目标衬底5表面,所述电极层3与所述目标衬底5表面的接触为范德华接触或主要为范德华接触,避免了直接在所述目标衬底5上制备电极层3时原材料与目标衬底反应的问题,也避免了直接在所述目标衬底5上制备电极层3时所需的高温条件对所述目标衬底5的损伤,从而能够保持所述目标衬底5材料的本征性质,不仅有利于提升所制作器件的电学性能,还能够扩展电极层3的可应用范围。同时,在所述石墨烯层2上制作电极层3可以扩大制作电极层3的工艺窗口,加工周期明显低于常规工艺所需时间,从而有利于降低电极层3的制作成本。
实施例二
本实施例中提供一种半导体结构,请参阅图9,显示为该半导体结构的剖面结构示意图,包括目标衬底5及位于所述目标衬底5上的至少一电极层3,其中,所述电极层3是通过如实施例一中所述的电极层的制备方法转移于所述目标衬底5上。所述电极层3的具体形态可以根据需要进行调整。
综上所述,本发明的电极层的制备方法及半导体结构通过在石墨烯上先行沉积电极层,利用石墨烯与电极层间较弱的范德华力使得电极层易于从石墨烯上剥离下来。将剥离好的电极层通过转移工艺转移至目标衬底,再将支撑层去除,就实现了对目标衬底无损伤的电极层制作,且目标衬底与电极层的接触为范德华接触。通过该方法能够方便地在任意目标衬底上进行电极层制作,极大扩展了电极层可应用的范围,且加工周期明显低于常规工艺所需时间,工艺成本也能够大大降低。通过实现目标衬底与电极层间的范德华接触,也能够保持材料的本征性质,提升所制作器件的电学性能。所以,本发明有效克服了现有技术中的种种缺点而具高度产业利用价值。
上述实施例仅例示性说明本发明的原理及其功效,而非用于限制本发明。任何熟悉此技术的人士皆可在不违背本发明的精神及范畴下,对上述实施例进行修饰或改变。因此,举凡所属技术领域中具有通常知识者在未脱离本发明所揭示的精神与技术思想下所完成的一切等效修饰或改变,仍应由本发明的权利要求所涵盖。
Claims (16)
1.一种电极层的制备方法,其特征在于,包括以下步骤:
提供一基底;
形成石墨烯层于所述基底的上表面;
形成至少一电极层于所述石墨烯层的上表面;
形成支撑层于所述石墨烯层的上表面,所述支撑层覆盖所述电极层;
将由所述电极层及所述支撑层组成的叠层结构从所述石墨烯层表面机械剥离;
将所述叠层结构转移至目标衬底,所述电极层与所述目标衬底的表面接触;
去除所述支撑层,并使所述电极层留在所述目标衬底的表面。
2.根据权利要求1所述的电极层的制备方法,其特征在于:所述基底采用刚性基底。
3.根据权利要求1所述的电极层的制备方法,其特征在于:所述基底包括锗层、碳化硅层、锗硅层、硅层、铜层、镍层、陶瓷层及玻璃层中的至少一种。
4.根据权利要求1所述的电极层的制备方法,其特征在于:所述石墨烯层包括单层石墨烯及多层石墨烯中的一种或多种。
5.根据权利要求1所述的电极层的制备方法,其特征在于:形成所述电极层的方法包括化学气相沉积法、物理气相沉积法、原子层沉积法中的至少一种。
6.根据权利要求5所述的电极层的制备方法,其特征在于:所述化学气相沉积法包括等离子体增强化学气相沉积法,所述物理气相沉积法包括电子束蒸发法及热蒸发法中的至少一种,所述原子层沉积法包括等离子增强原子层沉积法。
7.根据权利要求1所述的电极层的制备方法,其特征在于:所述电极层的材质包括金属及多晶硅中的至少一种。
8.根据权利要求1所述的电极层的制备方法,其特征在于,形成所述支撑层包括以下步骤:
施加有机溶液于所述电极层及所述石墨烯层的上表面;
干燥所述有机溶液以得到所述支撑层。
9.根据权利要求8所述的电极层的制备方法,其特征在于:所述有机溶液包括光刻胶溶液。
10.根据权利要求1所述的电极层的制备方法,其特征在于,形成所述支撑层包括以下步骤:
提供一柔性膜层以覆盖所述电极层;
通过加热加压使所述柔性膜层软化并紧贴所述电极层及所述石墨烯层的上表面以构成所述支撑层。
11.根据权利要求1所述的电极层的制备方法,其特征在于:采用胶带粘附所述支撑层背面以将所述叠层结构从所述石墨烯层表面机械剥离,或者直接掀起所述支撑层以将所述叠层结构从所述石墨烯层表面机械剥离。
12.根据权利要求1所述的电极层的制备方法,其特征在于:通过溶解法去除所述支撑层。
13.根据权利要求1所述的电极层的制备方法,其特征在于:通过加热所述支撑层以降低所述支撑层与所述电极层之间的粘附力,并通过机械剥离法去除所述支撑层。
14.根据权利要求1所述的电极层的制备方法,其特征在于:所述电极层与所述目标衬底表面的接触包括范德华接触。
15.根据权利要求1所述的电极层的制备方法,其特征在于:所述目标衬底包括二维材料层及三维材料层中的至少一种。
16.一种半导体结构,其特征在于,包括:
目标衬底;
至少一电极层,位于所述目标衬底上,其中,所述电极层是通过如权利要求1-15任意一项所述的电极层的制备方法转移于所述目标衬底上。