CN113004923B - 接头焦碳化反应后续处理工艺 - Google Patents
接头焦碳化反应后续处理工艺 Download PDFInfo
- Publication number
- CN113004923B CN113004923B CN202110405617.1A CN202110405617A CN113004923B CN 113004923 B CN113004923 B CN 113004923B CN 202110405617 A CN202110405617 A CN 202110405617A CN 113004923 B CN113004923 B CN 113004923B
- Authority
- CN
- China
- Prior art keywords
- coke
- reaction
- stage
- blowing
- condition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明属于接头焦生产技术领域，具体涉及一种接头焦碳化反应后续处理工艺，焦炭塔反应后吹气条件分为三个阶段：第一阶段：先用高温高压蒸汽吹气，高温高压蒸汽为2.5‑3.5MPa，400‑500℃，维持塔内生焦反应；第二阶段：采用中低压蒸汽，蒸汽条件是1.0‑2.0MPa，260‑380℃，继续吹扫未完全反应的油气；第三阶段：低压蒸汽大量吹扫，蒸汽条件是0.2‑0.6MPa，150‑240℃。本发明处理的接头焦碳化反应程度最优，性质比较均一，最大程度减少生焦上部的性质差异；生焦冷却采用阶梯式分布冷却法，降温速度一致，生焦内部结构均一，颗粒强度系数上部、中部、下部差别不大，从而提高产品质量。
Description
技术领域
本发明属于接头焦生产技术领域，具体涉及一种接头焦碳化反应后续处理工艺。
背景技术
接头焦为超高功率石墨电极接头用针状焦，针状焦是碳素材料中大力发展的一种优质碳种，是生产高功率超高功率石墨电极的主要原料。由于针状焦具有良好的石墨化性能，用其生产的高功率和超高功率电极具有优良的导电性、抗热震性和抗氧化性能。电炉使用由针状焦制造的的超高功率电极和普通电极相比，可使冶炼时间缩短30-50％，节电10-20％以上，生产能力可增加1.3倍，经济效益十分显著。
目前，针状焦的制备过程基本包括原料预处理、延迟焦化和煅烧三个工艺工程。聚结在焦炭塔内的针状焦生焦经吹汽、给水冷焦、泡焦、排水后，用高压水泵送来的高压水进行水力除焦，生焦焦和水一同流入储焦池。切焦水经沉淀分离焦粉后，由切焦水提升泵提升至冷、切焦水罐，以备下一周期冷焦或切焦使用。
存在的缺点：不节能、成本高；无法准确判断生焦的降温程度；吹气条件较低，导致生焦质量较低。
发明内容
本发明要解决的技术问题是：克服现有技术的不足，提供一种接头焦碳化反应后续处理工艺，节能环保，成本低，同时能够保证生焦内部结构均一，颗粒强度系数上部、中部、下部差别不大，从而提高产品质量。
本发明是采用以下技术方案实现的：
所述的焦碳化反应后续处理工艺，针状焦原料经换热和焦化加热炉加热后进入焦炭塔发生裂解和缩合反应，通过放热及吸热进行裂化生成针状焦生焦，焦炭塔反应后吹气条件分为三个阶段：
第一阶段：先用高温高压蒸汽吹气，高温高压蒸汽为2.5-3.5MPa，400-500℃，维持塔内生焦反应；
第二阶段：采用中低压蒸汽，蒸汽条件是1.0-2.0MPa，260-380℃，继续吹扫未完全反应的油气；
第三阶段：低压蒸汽大量吹扫，蒸汽条件是0.2-0.6MPa，150-240℃。
其中：
第一阶段高温高压蒸汽优选为3.0MPa，480℃。
第二阶段蒸汽条件优选为1.5MPa，300℃。
第三阶段蒸汽条件优选为0.4MPa，200℃。
焦炭塔反应后吹气条件的三个阶段为一个周期。接头焦碳化反应完成后根据焦炭塔内空高、焦炭塔的壁温等参数的不同，按照一定比例优化组合，确保反应的持续进行。吹气条件完成后再用水进行冷却、降温，此时给水一定保证给水的稳定性。
与现有技术相比，本发明的有益效果如下：
本发明处理的接头焦碳化反应程度最优，性质比较均一，最大程度减少生焦上部的性质差异；生焦冷却采用阶梯式分布冷却法，降温速度一致，生焦内部结构均一，颗粒强度系数上部、中部、下部差别不大，从而提高产品质量。
附图说明
图1为本发明的工艺流程图。
具体实施方式
下面结合附图和实施例对本发明做进一步的说明。
实施例1
如图1所示，所述的接头焦碳化反应后续处理工艺，针状焦原料经换热和焦化加热炉加热后进入焦炭塔发生裂解和缩合反应，通过放热及吸热进行裂化生成针状焦生焦，焦炭塔反应后吹气条件分为三个阶段：
第一阶段：先用高温高压蒸汽吹气，高温高压蒸汽为2.5MPa，450℃，维持塔内生焦反应；
第二阶段：采用中低压蒸汽，蒸汽条件是1.3MPa，280℃，继续吹扫未完全反应的油气；
第三阶段：低压蒸汽大量吹扫，蒸汽条件是0.3MPa，180℃。
吹气条件完成后再用水进行冷却、降温。
实施例2
如图1所示，所述的接头焦碳化反应后续处理工艺，针状焦原料经换热和焦化加热炉加热后进入焦炭塔发生裂解和缩合反应，通过放热及吸热进行裂化生成针状焦生焦，焦炭塔反应后吹气条件分为三个阶段：
第一阶段：先用高温高压蒸汽吹气，高温高压蒸汽为3.0MPa，480℃，维持塔内生焦反应；
第二阶段：采用中低压蒸汽，蒸汽条件是1.5MPa，300℃，继续吹扫未完全反应的油气；
第三阶段：低压蒸汽大量吹扫，蒸汽条件是0.4MPa，200℃。
吹气条件完成后再用水进行冷却、降温。
实施例3
如图1所示，所述的接头焦碳化反应后续处理工艺，针状焦原料经换热和焦化加热炉加热后进入焦炭塔发生裂解和缩合反应，通过放热及吸热进行裂化生成针状焦生焦，焦炭塔反应后吹气条件分为三个阶段：
第一阶段：先用高温高压蒸汽吹气，高温高压蒸汽为3.5MPa，500℃，维持塔内生焦反应；
第二阶段：采用中低压蒸汽，蒸汽条件是1.8MPa，350℃，继续吹扫未完全反应的油气；
第三阶段：低压蒸汽大量吹扫，蒸汽条件是0.5MPa，230℃。
吹气条件完成后再用水进行冷却、降温。
当然，上述内容仅为本发明的较佳实施例，不能被认为用于限定对本发明的实施例范围。本发明也并不仅限于上述举例，本技术领域的普通技术人员在本发明的实质范围内所做出的均等变化与改进等，均应归属于本发明的专利涵盖范围内。
Claims (1)
1.一种接头焦碳化反应后续处理工艺，其特征在于：针状焦原料经换热和焦化加热炉加热后进入焦炭塔发生裂解和缩合反应，通过放热及吸热进行裂化生成针状焦生焦，焦炭塔反应后吹气条件分为三个阶段：
第一阶段：先用高温高压蒸汽吹气，高温高压蒸汽为2.5MPa，450℃，维持塔内生焦反应；
第二阶段：采用中低压蒸汽，蒸汽条件是1.3MPa，280℃，继续吹扫未完全反应的油气；
第三阶段：低压蒸汽大量吹扫，蒸汽条件是0.3MPa，180℃；
焦炭塔反应后吹气条件的三个阶段为一个周期；
吹气条件完成后再用水进行冷却、降温；
所述的接头焦碳化反应后续处理工艺，节能环保，成本低，同时能够保证生焦内部结构均一。