CN112973713A - Hydrofining catalyst and preparation method thereof - Google Patents
Hydrofining catalyst and preparation method thereof Download PDFInfo
- Publication number
- CN112973713A CN112973713A CN202011490432.7A CN202011490432A CN112973713A CN 112973713 A CN112973713 A CN 112973713A CN 202011490432 A CN202011490432 A CN 202011490432A CN 112973713 A CN112973713 A CN 112973713A
- Authority
- CN
- China
- Prior art keywords
- hours
- organic solvent
- catalyst
- metal
- alumina carrier
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to the field of hydrogenation catalysts, and discloses a hydrofining catalyst and a preparation method thereof. The preparation method comprises the following steps: (1) uniformly mixing the alumina carrier, a silicon source and water, stirring for 0.5-24 hours at room temperature-90 ℃, filtering, drying, and roasting for 2-5 hours at 550-800 ℃ to obtain a modified alumina carrier; (2) dipping active metal in the modified alumina carrier in an organic solvent, and drying; (3) and (3) roasting the product obtained in the step (2) in an inert atmosphere, wherein the roasting temperature is 300-700 ℃, and the roasting time is 0.5-5 hours, so as to obtain the hydrofining catalyst. Can effectively improve the physicochemical property of the carrier, obviously improve the dispersion degree of the active metal on the surface of the catalyst, and is suitable for the preparation of hydrodemetallization, hydrodesulfurization and hydroconversion catalysts.
Description
Technical Field
The invention relates to the field of hydrogenation catalysts, in particular to a hydrofining catalyst and a preparation method thereof.
Background
With the increasing strictness of environmental regulations, new diesel oil standards put more strict requirements on the sulfur mass fraction, the aromatic hydrocarbon mass fraction and the cetane number of diesel oil products. The yield of the catalytic cracking diesel oil is about 30 percent of the total yield of the diesel oil, and the catalytic cracking diesel oil cannot be directly used as the diesel oil due to low cetane number, high mass fractions of sulfur, nitrogen and colloid, dark color of an oil product and poor stability. The hydrogenation process is one of the most effective process means for improving the quality of oil products, and the hydrogenation catalyst is the most important and key technology in the hydrogenation process.
Hydrogenation catalysts generally consist of a metal or metal oxide having a hydrogenation function and a carrier, and commonly used metal components are group VIB and group VIII metals, such as cobalt, molybdenum, nickel, tungsten, etc., and such catalysts generally have the metal active component supported on the carrier by an impregnation method. Commonly used supports are alumina or siliceous alumina. In order to further improve the activity and stability of the catalyst, the carrier is often modified to make it more suitable for deep hydrofining of poor diesel oil fractions.
CN1133723C discloses a distillate oil hydrorefining catalyst and a preparation method thereof, wherein, alumina pellets containing 5-15 wt% of silicon dioxide are used as carriers and contain MoO321-28 wt%, NiO 2-8 wt% and CoO 0.03-2.0 wt%, and two-stage spray soaking is adopted. The catalyst has higher hydrodesulfurization and hydrodenitrogenation activities at the same time, and is suitable for hydrofining of inferior distillate oil containing more sulfur and nitrogen at the same time.
WO2007084438 discloses a selective hydrodesulphurisation catalyst comprising 8-30 wt% of molybdenum selected from group VIB, 2-8 wt% of cobalt selected from group VIII, and a suitable amount of organic substance as complexing agent on a silicon carrier. When the catalyst is used for treating catalytic cracking gasoline raw materials, the olefin saturation rate is low.
CN1123765.1 discloses a diesel hydrotreating catalyst, which contains a carrier and indium and/or tungsten and nickel and/or cobalt loaded on the carrier, wherein the carrier is composed of alumina and zeolite, the weight ratio of the alumina to the zeolite is 90:10-50:50, the alumina is alumina compounded by small pore alumina and large pore alumina according to the weight ratio of 75:25-50:50, wherein, the small pore alumina is alumina with the diameter of less than 80 angstrom pores accounting for more than 95% of the total pore volume, and the large pore alumina is alumina with the diameter of 60-600 angstrom pores accounting for more than 70% of the total pore volume.
CN1049679C discloses a diesel oil hydroconversion catalyst, which takes alumina and Y-type molecular sieve as carriers and contains at least one VIB group metal and at least one VIll group metal, wherein the catalyst carrier comprises 40-90 w% of alumina, 0-20 w% of amorphous silica-alumina and 5-40 w% of molecular sieve, the pore volume of the Y-type molecular sieve is 0.40-0.52ml/g, and the specific surface is 750-900m2Unit cell constant 2.420-2.500nm, SiO2/A12O3In the ratio of 7-15, the content of VIB group metal oxide in the catalyst is 10-30 w%, and the content of VIll group metal oxide in the catalyst is 2-15 w%. It is suitable for the hydrogenation conversion of 150-400 deg.C petroleum fraction, especially for the conversion of catalytic cracking Light Cycle Oil (LCO) with high sulfur, nitrogen and aromatic hydrocarbon contents and low cetane number, and features that under the milder condition, the contents of sulfur, nitrogen and aromatic hydrocarbon are reduced and the cetane number of the product is greatly raised.
CN1289828A discloses a new compound prepared from gamma-Al2O3Or by containing SiO2gamma-Al of (2)2O3The hydrofining catalyst as carrier has W, Mo, Ni and P as active components. With SiO2Modified Al2O3The hydrogenation catalyst which is a carrier has improved performance, but the carrier has lower acid content and fewer strong acid centers, is not beneficial to ring opening and breaking of nitrogen heterocycles, and has poor denitrification activity.
Disclosure of Invention
The invention aims to overcome the defects of poor properties such as specific surface area, pore volume and the like and low catalytic hydrogenation activity of the alumina carrier of the existing hydrogenation catalyst, and provides a hydrofining catalyst and a preparation method thereof.
In order to achieve the above object, specifically, the present invention provides a method for preparing a hydrorefining catalyst, comprising:
(1) mixing alumina carrier, silicon source and deionized water, stirring at room temperature-90 deg.c for 0.5-24 hr, filtering, stoving, and roasting at 550 deg.c and 800 deg.c for 2-5 hr.
(2) Dipping the modified alumina carrier in an organic solvent to obtain active metal, and drying;
(3) and roasting the alumina carrier impregnated with the metal in an inert gas atmosphere at the roasting temperature of 300-700 ℃ for 0.5-5 hours to obtain the hydrofining catalyst.
The invention also provides a hydrofining catalyst prepared by the method.
According to the technical scheme, the alumina carrier is modified by adopting the silicon-containing solution, so that on one hand, the pore size distribution of the carrier can be effectively improved, the macropores are increased, the acidity of the catalyst is adjusted, and the addition of silicon is found to be beneficial to enhancing the interaction of the active component of the catalyst and the carrier; the organic solvent dipping method can obviously improve the dispersion degree of the active metal on the surface of the catalyst. The method is particularly suitable for preparing hydrodemetallization, hydrodesulfurization and hydroconversion catalysts.
Additional features and advantages of the invention will be set forth in the detailed description which follows.
Detailed Description
The following examples are intended to further illustrate the present invention and to assist the reader in better understanding the nature and advantages of the present invention, but are not to be construed as limiting the scope of the invention in any way.
The invention provides a preparation method of a hydrofining catalyst, which comprises the following specific steps:
(1) uniformly mixing the alumina carrier, a silicon source and water, stirring for 0.5-24 hours at room temperature-90 ℃, filtering, drying, and roasting for 2-5 hours at 550-800 ℃ to obtain a modified alumina carrier;
(2) dipping active metal in the modified alumina carrier in an organic solvent, and drying;
(3) and (3) roasting the product obtained in the step (2) in an inert atmosphere, wherein the roasting temperature is 300-700 ℃, and the roasting time is 0.5-5 hours, so as to obtain the hydrofining catalyst.
In some embodiments provided herein, step (1) is used to prepare a composite alumina support, and modification of the support may be achieved to provide a final improvement in performance of the resulting hydrogenation catalyst. Preferably, the specific surface area of the alumina carrier is 70-400m2The pore volume is 0.2-1.5 mL/g. To be able to provide better carrier performance.
In some embodiments of the present invention, step (1) is used to modify the alumina, and the silicon source is used to provide silicon modification, and the resulting modified alumina can provide better promotion of the hydrogenation reaction. Preferably, the silicon source may be a silica sol, a silica gel or a water glass, preferably a silica sol.
In some embodiments provided herein, in step (1), the alumina, the silicon source (calculated as silica) and the deionized water are mixed in a ratio of 1: (0.1-1): (1-20) mixing. The addition amount can be controlled to realize that the obtained modified alumina carrier has a proper pore structure. Preferably, the ratio of alumina: the weight ratio of the silicon source may be 1:0.1, 1:0.2, 1:0.3, 1:0.4, 1:0.5, 1:0.6, 1:07, 1:0.8, 1:0.9, 1:1, and ranges consisting of any two of the foregoing values; alumina: the weight ratio of water may preferably be 1:1 to 11, preferably 1:1, 1:2, 1:3, 1:4, 1:5, 1:6, 1:7, 1:8, 1:9, 1:10, 1:11, and ranges consisting of any two of the above values.
The drying in step (1) may be performed at 100-120 ℃ for 10-15 hours.
In some embodiments provided by the present invention, step (2) is used for supporting the active metal, and the active metal required by the hydrofining catalyst of the present invention is supported on the composite alumina carrier. Preferably, in the step (2), the active metal is a group VIII and/or a group VIB metal, the group VIII metal is at least one of Fe, Ni, and Co, and the group VIB metal is W and/or Mo. The dosage of the active metal is further preferably 0.1 wt% -30 wt% of the VIII group metal calculated by metal oxide and 0.08 wt% -20 wt% of the VIB group metal calculated by metal oxide relative to the composite alumina carrier. Preferably, the group VIII metal is used in an amount of 5 wt% to 20 wt% and the group VIB metal is used in an amount of 5 wt% to 20 wt%.
In some embodiments provided by the present invention, preferably, in step (3), the impregnating process includes: dissolving the precursor of the active metal in the organic solvent, then mixing with the composite zirconia carrier, and keeping for 0.5-12 hours under stirring or standing, wherein the composite zirconia carrier: the solid-liquid weight ratio of the organic solvent is 1: (0.5-5); preferably, the number of said impregnations is at least 1. The precursor of the active metal may be selected from compounds containing the active metal which are soluble in the organic solvent, and may be, for example, ferric chloride, ammonium molybdate, cobalt nitrate, ammonium metatungstate, nickel nitrate. Wherein, after the impregnation process is finished, drying is carried out for 10-15 hours at the temperature of 80-120 ℃, and the organic solvent is removed. The precursor of the active metal is used in an amount satisfying the addition amount of the active metal.
In some embodiments provided herein, preferably, the organic solvent has a normal boiling point of preferably 40 to 100 ℃. Preferably, the organic solvent may be one or more of alkane, aromatic hydrocarbon, alcohol, ketone, ether, ester, halogenated alkane. Preferably, the organic solvent is one or more of n-hexane, cyclohexane, heptane, benzene, toluene, methanol, ethanol, isopropanol, acetone, butanone and chloroform. The organic solvent and the amount used for impregnating the active metal in the step (3) can help to improve the dispersion degree of the active metal on the surface of the catalyst.
In some embodiments provided by the present invention, preferably, in the step (4), the calcination temperature is 450-650 ℃, and the calcination time is 1-4 hours.
The invention also provides a hydrogenation catalyst prepared by the preparation method.
In some embodiments provided herein, the catalyst obtained has a specific surface area of 250-400m2(ii)/g, preferably 310- & ltwbr/& gtm & lt 330 & gt2(ii)/g; the pore volume is 0.5-0.7mL/g, preferably 0.55-0.65 mL/g. The total amount of acid is 0.5-0.7mmol/g, preferably 0.55-0.65 mmol/g. The hydrofining catalyst comprises the following components: based on the total amount of the catalyst, the content of alumina is 30-65 wt%, the content of silica is 5-40 wt%, the content of VIII group metal (calculated by metal oxide) is 0.1-30 wt%, and the content of VIB group metal (calculated by metal oxide) is 0.08-20 wt%. The composition of the hydrofining catalyst can be measured by a fluorescence analysis method and can also be calculated by preparation feeding.
The invention also provides a method for hydrorefining catalytic cracking diesel, which comprises the following steps: the catalytic cracking diesel oil is subjected to hydrofining reaction in the presence of a hydrofining catalyst, and the hydrofining catalyst is the distillate oil hydrofining catalyst.
The catalytic cracking diesel oil may be diesel oil produced from a catalytic cracking process of petroleum refining. The conditions of the hydrofinishing reaction may be: the temperature is 300--1The volume ratio of the hydrogen to the raw material catalytic cracking diesel oil is 200-500: 1.
By using the hydrofining catalyst, the hydrodesulfurization rate of catalytic cracking diesel oil reaches 100%, and the denitrification rate is more than 94.0%.
The present invention will be described in detail below by way of examples.
In the following examples and comparative examples:
the specific surface area and the pore volume of the catalyst are measured by a BET test method;
the total acid amount of the catalyst is measured by pyridine infrared spectrometry;
the sulfur content in the raw oil and the hydrogenation product is measured by a gas chromatography method;
the hydrodesulfurization rate is 1- (the content of sulfur in the raw oil-the content of sulfur in the hydrogenated product)/the content of sulfur in the raw oil is multiplied by 100 percent;
the hydrogenation denitrification rate is 1- (the content of nitrogen in the raw oil-the content of nitrogen in the hydrogenation product)/the content of nitrogen in the raw oil is multiplied by 100%.
Example 1
650g of alumina (86% by weight in terms of solids content, Al)2O3559g), 560g of silica sol (silica content 25%, silica content 140g), 2800g of deionized water were mixed, aged at room temperature with stirring for 2 hours, filtered, dried at 120 ℃ for 12 hours, and calcined at 750 ℃ for 2 hours to obtain a modified alumina support. Alumina: silicon oxide: the weight ratio of water is 1:0.25: 5.
339g of ferric chloride and 272g of ammonium molybdate are dissolved in 800g of ethanol (with the purity of 99.9%) to prepare an impregnation solution, the obtained impregnation solution and the modified alumina carrier (relative to the modified alumina carrier, the dosage of ferric oxide is 10 wt%, and the dosage of molybdenum oxide is 20 wt%) are uniformly mixed (the solid-liquid weight ratio of the modified alumina carrier to the organic solvent is 1: 2), the mixture is kept at room temperature for 12 hours, and then the obtained product is dried for 24 hours at the temperature of 100 ℃ and is calcined for 4 hours at the temperature of 500 ℃ in a nitrogen atmosphere. Catalyst A1 was obtained. The analytical results of catalyst A1 are shown in Table 1.
Example 2
547g of alumina (86% by weight in terms of solids content, Al)2O3470.4g), 1200g of silica sol (the content of silica is 25 percent, the weight of silica is 300g) and 1400g of deionized water are mixed, stirred and aged for 1 hour at 40 ℃, dried for 12 hours at 120 ℃ after filtration, and roasted for 3 hours at 650 ℃ to obtain the modified alumina carrier. Alumina: silicon oxide: the weight ratio of water was 1:0.64: 2.98.
280g of cobalt nitrate Co (NO)3)2·6H2O and 160g of ammonium metatungstate are dissolved in 900g of ethanol (the purity is 99.9%) to prepare an impregnation solution, the obtained impregnation solution is uniformly mixed with the modified alumina carrier (relative to the modified alumina carrier, the dosage of cobalt oxide is 8 wt%, and the dosage of tungsten oxide is 15 wt%) (the solid-liquid weight ratio of the modified alumina carrier to the organic solvent is 1: 2), the mixture is kept at room temperature for 8 hours, and then the obtained product is dried at 120 ℃ for 6 hours and is calcined at 550 ℃ for 2 hours in a nitrogen atmosphere. Catalyst A2 was obtained. The analytical results of catalyst A2 are shown in Table 1.
Example 3
465g of alumina (86% by weight in terms of solids content, Al)2O3399.9g), 1400g of silica sol (the content of silica is 25 percent, and the content of silica is 350g) and 4000g of deionized water are mixed, stirred and aged for 1 hour at the temperature of 60 ℃, dried for 12 hours at the temperature of 120 ℃ after filtration, and roasted for 5 hours at the temperature of 550 ℃ to obtain the modified alumina carrier. Alumina: silicon oxide: the weight ratio of water was 1:0.88: 10.
489g of nickel nitrate and 68g of ammonium molybdate were dissolved in 600g of cyclohexane (purity: 99.9%) to prepare an impregnation solution, the obtained impregnation solution was uniformly mixed with the above-mentioned modified alumina carrier (the amount of nickel oxide was 20 wt% and the amount of molybdenum oxide was 5 wt% with respect to the modified alumina carrier) (the solid-liquid weight ratio of the modified alumina carrier to the organic solvent was 1: 2), the mixture was kept at room temperature for 12 hours, and then the obtained product was dried at 120 ℃ for 6 hours and calcined at 600 ℃ for 3 hours under a nitrogen atmosphere. Catalyst A3 was obtained. The analytical results of catalyst A3 are shown in Table 1.
Example 4
442g of alumina (86% by weight in terms of solids content, Al)2O3380.1g), 1480g of silica sol (silica content 25%, silica content 370g) and 2600g of deionized water were mixed, aged at 60 ℃ for 1.5 hours with stirring, filtered, dried at 120 ℃ for 12 hours, and calcined at 700 ℃ for 2 hours to obtain a modified alumina carrier. Alumina: silicon oxide: the weight ratio of water was 1:0.97: 6.84.
175g of cobalt nitrate Co (NO)3)2·6H2O and 272g of ammonium molybdate are dissolved in 1000g of cyclohexane (with the purity of 99.9%) to prepare an impregnation solution, the obtained impregnation solution is uniformly mixed with the modified alumina carrier (the weight ratio of cobalt oxide to organic solvent is 1:3 relative to the modified alumina carrier, the weight ratio of cobalt oxide to molybdenum oxide is 5 wt%, and the weight ratio of molybdenum oxide to organic solvent is 20 wt%), the mixture is kept at room temperature for 24 hours, and then the obtained product is dried at 120 ℃ for 6 hours and is calcined at 650 ℃ for 3 hours in a nitrogen atmosphere. Catalyst A4 was obtained. The analytical results of catalyst A4 are shown in Table 1.
Example 5
523g of alumina (86% strength by weight in terms of solids, Al)2O3449.8g), 1200g of silica sol (25% silica content, 300% silica)g) And 2700g of deionized water, stirring and aging at 90 ℃ for 1.5 hours, filtering, drying at 120 ℃ for 12 hours, and roasting at 700 ℃ for 2 hours to obtain the modified alumina carrier. Alumina: silicon oxide: the weight ratio of water is 1:0.67: 6.00.
526g of cobalt nitrate Co (NO)3)2·6H2O and 106g of ammonium metatungstate are dissolved in 1000g of butanone (the purity is 99.9%) to prepare an impregnation solution, the obtained impregnation solution is uniformly mixed with the modified alumina carrier (the solid-liquid weight ratio of the modified alumina carrier to the organic solvent is 1:2, the dosage of cobalt oxide is 15 wt% and the dosage of tungsten oxide is 10 wt% relative to the modified alumina carrier), the mixture is kept at room temperature for 24 hours, and then the obtained product is dried at 120 ℃ for 6 hours and is calcined at 550 ℃ for 3 hours in a nitrogen atmosphere. Catalyst A5 was obtained. The analytical results of catalyst A5 are shown in Table 1.
Comparative example 1
339g of ferric chloride and 272g of ammonium molybdate are dissolved in 800g of deionized water to prepare an impregnation solution, the obtained impregnation solution and an alumina carrier are uniformly mixed, the mixture is kept at room temperature for 12 hours, then the obtained product is dried for 24 hours at 100 ℃, and is roasted for 4 hours at 500 ℃ in an air atmosphere. Comparative catalyst D1 was obtained. The results of the catalyst analysis are shown in Table 1.
Comparative example 2
650g of alumina (86% by weight in terms of solids content, Al)2O3559g), 560g of silica sol (silica content 25%, silica content 140g), 2800g of deionized water were mixed, aged at room temperature with stirring for 2 hours, filtered, dried at 120 ℃ for 12 hours, and calcined at 750 ℃ for 2 hours to obtain a modified alumina support. Alumina: silicon oxide: the weight ratio of water is 1:0.25: 5.
339g of ferric chloride and 272g of ammonium molybdate are dissolved in 800g of deionized water to prepare an impregnation solution, the obtained impregnation solution is uniformly mixed with the modified alumina carrier (relative to the modified alumina carrier, the dosage of ferric oxide is 12 wt%, and the dosage of molybdenum oxide is 23 wt%) (the solid-liquid weight ratio of the modified alumina carrier to water is 1: 2), the mixture is kept at room temperature for 12 hours, and then the obtained product is dried at 100 ℃ for 24 hours and is calcined at 500 ℃ for 4 hours in an air atmosphere. Comparative catalyst D1 was obtained. The results of the catalyst analysis are shown in Table 1.
TABLE 1
The results in table 1 show that the catalyst prepared by the method of the invention has higher specific surface area and pore volume, higher acid amount, higher metal dispersion degree on the surface of the carrier and higher hydrogenation activity.
Examples 6 to 10
The catalysts A1-A5 were subjected to hydrodesulfurization and denitrification reactions in accordance with the feed oils and evaluation conditions provided in Table 2. The reaction evaluation results are shown in Table 3.
TABLE 2
Raw oil | Catalytic diesel fuel |
Density at 20 ℃ in kg/m3 | 975 |
S, ppm (by mass) | 6500 |
N, ppm (by mass) | 880 |
Partial pressure of hydrogen, MPa | 6.0 |
Temperature, C | 340 |
Volumetric space velocity h-1 | 2.0 |
Volume ratio of hydrogen to oil | 300 |
Comparative examples 3 to 4
Catalysts D1-D2 were subjected to hydrodesulfurization and denitrogenation in the same manner as in examples 6-10. The reaction evaluation results are shown in Table 3.
TABLE 3
The results in table 3 show that the catalyst provided by the invention has higher catalytic hydrogenation activity, and the catalytic diesel hydrogenation performance of the catalyst is obviously superior to that of a comparative catalyst.
The preferred embodiments of the present invention have been described above in detail, but the present invention is not limited thereto. Within the scope of the technical idea of the invention, many simple modifications can be made to the technical solution of the invention, including combinations of various technical features in any other suitable way, and these simple modifications and combinations should also be regarded as the disclosure of the invention, and all fall within the scope of the invention.
It should be noted that the technical features described in the above embodiments may be combined in any manner without contradiction. The invention is not described in detail in order to avoid unnecessary repetition.
In addition, various different embodiments of the present invention can be combined arbitrarily, and the same should be regarded as the disclosure of the present invention as long as it does not depart from the idea of the present invention.
Claims (10)
1. A preparation method of a hydrofining catalyst comprises the following steps:
(1) uniformly mixing the alumina carrier, a silicon source and water, stirring for 0.5-24 hours at room temperature-90 ℃, filtering, drying, and roasting for 2-5 hours at 550-800 ℃ to obtain a modified alumina carrier;
(2) dipping active metal in the modified alumina carrier in an organic solvent, and drying;
(3) and (3) roasting the product obtained in the step (2) in an inert atmosphere, wherein the roasting temperature is 300-700 ℃, and the roasting time is 0.5-5 hours, so as to obtain the hydrofining catalyst.
2. The method according to claim 1, wherein the silicon source is a silica sol, a silica gel or a water glass, preferably a silica sol.
3. The method of claim 1 or 2, wherein the alumina support: silicon source: the weight ratio of water is 1: (0.1-1): (1-20), wherein the silicon source is calculated by silicon oxide.
4. The process according to any one of claims 1-3, wherein the active metal is a group VIII and/or a group VIB metal, the group VIII metal being at least one of Fe, Ni, Co, the group VIB metal being W and/or Mo.
5. The process according to any one of claims 1 to 4, wherein the group VIII metal is present in an amount of from 0.1% to 30% by weight, calculated as metal oxide, and the group VIB metal is present in an amount of from 0.08% to 20% by weight, calculated as metal oxide, with respect to the modified alumina support.
6. The method according to any one of claims 1 to 5, wherein during the impregnation, one or more auxiliary agents selected from P, B, Ti and Zr are added into the organic solvent.
7. The method of any of claims 1-6, wherein the impregnating comprises: dissolving the precursor of the active metal in the organic solvent, then mixing with the modified alumina carrier, and keeping for 0.5-12 hours under stirring or standing, wherein the modified alumina carrier: the solid-liquid weight ratio of the organic solvent is 1: (0.5-5);
preferably, the number of said impregnations is at least 1.
8. The method according to any one of claims 1 to 7, wherein the organic solvent has a normal boiling point of 40 to 100 ℃;
preferably, the organic solvent is one or more of alkane, aromatic hydrocarbon, alcohol, ketone, ether, ester and halogenated alkane, and the organic solvent is one or more of n-hexane, cyclohexane, heptane, benzene, toluene, methanol, ethanol, isopropanol, acetone, butanone and chloroform.
9. The method as claimed in any one of claims 1 to 8, wherein, in the step (3), the calcination temperature is 450 ℃ and 650 ℃, and the calcination time is 1 to 4 hours.
10. A hydrorefining catalyst obtained by the production method according to any one of claims 1 to 9.