CN112745526A - 一种水性皮革着色剂 - Google Patents
一种水性皮革着色剂 Download PDFInfo
- Publication number
- CN112745526A CN112745526A CN202011606762.8A CN202011606762A CN112745526A CN 112745526 A CN112745526 A CN 112745526A CN 202011606762 A CN202011606762 A CN 202011606762A CN 112745526 A CN112745526 A CN 112745526A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- leather
- raw materials
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于合成革技术领域，特别涉及一种水性皮革着色剂，其由如下重量份比的原料制备而成：颜料100份；功能助剂8‑66份；消泡剂0.4‑3.3份；一乙醇胺0.1‑1.6份和水34.8‑175.7份；所述功能助剂为江苏无锡米科思新材料科技有限公司生产的Mix sperse 855w。本发明的有益效果在于：本发明的水性皮革着色剂，不含有任何溶剂和任何载体树脂，且具有高浓度、强着色、高光泽、低粘度、优异的防盐雾性、优异的耐酒精擦拭、鲜艳度优、储存时间长的优点。可适用于全水性聚氨脂任何基料的着色，且饱和度非常稳定。以上这些优点解决了目前市场上流通的水性着色剂的缺陷，使之皮革制造企业油改水、油转水工程顺利实施。
Description
技术领域
本发明属于合成革技术领域，特别涉及一种水性皮革着色剂。
背景技术
《GB-37824-209涂料油墨及胶粘剂工业大气污染物排放标准》据最新规定相关行业如果有超标排放，相关企业和负责人将承担法律责任。随着环保政策的收紧和全国近百个城市禁油令，水性产品再一次被推上了风口浪尖。大气污染排放限制包括如下表1的污染物项目。
表1
因政策收紧，新机遇、新挑战，制革行业同样因上游材料的创新改变，产品升级换代也迫在眉睫，同时也为开发环境友好型，生态型产品创造新的机遇。油转水、油改水还是大势所趋。水性皮革着色剂是生产水性皮革必不可少、不可或缺的材料，在这种背景下就必须有新型全水性功能型着色剂满足市场需求，使制革行业油改水顺利进行。
发明内容
本发明所要解决的技术问题是：提供一种性能好且不含有任何溶剂和任何载体树脂的水性皮革着色剂。
为了解决上述技术问题，本发明采用的技术方案为：提供一种水性皮革着色剂，其特征在于，由如下重量份比的原料制备而成：颜料100份；功能助剂8-66份；消泡剂0.4-3.3份；一乙醇胺0.1-1.6份和水34.8-175.7份；所述功能助剂为江苏无锡米科思新材料科技有限公司生产的Mix sperse 855w。
优选的，上述水性皮革着色剂具体由如下重量份比的原料制备而成：二氧化钛100份；功能助剂8份；消泡剂0.4份；一乙醇胺0.1份和水34.8份。
优选的，上述水性皮革着色剂具体由如下重量份比的原料制备而成：氧化铁黄100份；功能助剂16份；消泡剂0.8份；一乙醇胺0.2份和水66.3份。
优选的，上述水性皮革着色剂具体由如下重量份比的原料制备而成：PK-122红100份；功能助剂66份；消泡剂3.3份；一乙醇胺1.6份和水175.7份。
优选的，上述水性皮革着色剂中，所述消泡剂为BYK-024。
本发明的有益效果在于：本发明的水性皮革着色剂不含任何溶剂和任何载体树脂，且具有高浓度、强着色、高光泽、低粘度、优异的防盐雾性、优异的耐酒精擦拭、鲜艳度优、储存时间长的优点，可适用于全水性聚氨脂任何基料的着色，且饱和度非常稳定。以上这些优点解决了目前市场上流通的水性着色剂的缺陷，使皮革制造企业油改水、油转水工程可顺利实施。
具体实施方式
为详细说明本发明的技术内容、所实现目的及效果，以下结合实施方式予以说明。
水性聚氨脂保留了传统的溶剂型聚脂的一些优良性能，而且还具有生产成本低、安全不燃、不污染环境、不易损伤被涂饰表面、易操作和改性等优点。因其水性聚氨脂按原材料、结构等分类很多，在开发全水性着色剂剂时不可能一一对应那么多产品，必有一种无载体树脂多功能的着色剂来满足各种需求。
现市场流通的水性着色剂的缺点：目前市场上流通的水性着色剂，其大部分产品都是打着打擦边球生产伪水性着色剂。号称结合油性的疏水性和水性的环保性，但是使用后出现褪色、掉色质量不合格现象，导致整个市场被质疑。所谓的水性产品其产品媒介肯定是水，但是水固有的物性：沸点100℃、凝固点0℃、密度为1g/cm3能溶解多种物质形成溶液，但是在没有外在的辅助作用，其溶解力在常温下还是处于惰性。这样的理论中就必然有一种加速它的溶解力的功能型材料推动完成，又加上水的密度大，在配方中如果设定的配方没有考虑到水本身在配方中最大的承载。就会导致产品的上下分离、稳定型差、储存时间短。
本发明解决原有普通型水性皮革着色剂的缺点；解决表1中的物料受限，使油转水顺利实施。
实施例1
一种水性皮革着色剂，由如下重量份比的原料制备而成：二氧化钛100份；江苏无锡米科思新材料科技有限公司生产的Mix sperse 855w功能性助剂8份；BYK-024 0.4份；一乙醇胺0.1份和水34.8份。
实施例2
一种水性皮革着色剂，由如下重量份比的原料制备而成：氧化铁黄100份；江苏无锡米科思新材料科技有限公司生产的Mix sperse 855w功能性助剂16份；BYK-024 0.8份；一乙醇胺0.2份和水66.3份。
实施例3
一种水性皮革着色剂，由如下重量份比的原料制备而成：PK-122红100份；江苏无锡米科思新材料科技有限公司生产的Mix sperse 855w功能性助剂66份；BYK-024 3.3份；一乙醇胺1.6份和水175.7份。
本发明所用原料具有以下特点：
1、本发明的使用的江苏无锡米科思新材料科技有限公司生产的Mix sperse855w功能性助剂具有以下特征：有代替树脂承载力的作用、有调理、分散、有定向和不定向，反复包裹整个体系的作用。其能够改善原配方中这些缺陷：①耐盐雾性差；②耐酒精差；③色浓度低；④色泽不艳、易分层、粘度高、不易分散。
江苏无锡米科思新材料科技有限公司生产的Mix sperse 855w是不含有VOCAPEOC(烷基酚聚氧乙稀醚)的水性润湿、分散、流平、防腐、防尘、增光，并稳定所有类型的产品的颜料(有机、无机、填料、炭黑)具有强降粘的效果，可使浓缩色浆具有非常低的粘度。良好的相溶性储存稳定性，非常好的耐水性，耐盐雾性，优秀的耐候性和低起泡性。
江苏无锡米科思新材料科技有限公司生产的Mix sperse 855w的产品信息：a、化学组成：含高颜料亲和基因的共聚物水溶性；b、典型物化数据(此物化数据非质量指标)，外观：浅黄色液体；子类型：活性物质含量：45％；PH值：6.5-8.5。
2、BYK-024消泡剂：成份-聚硅氧烷混合物；外观-液体；水中溶解度-优；主要用于水性着色剂的硅树脂消泡剂。用于基于聚氨脂、丙烯酸脂、聚氨脂，生产过程中非常有效不影响色彩接受度和光泽度。
3、PH值调节剂-一乙醇胺
一乙醇胺是一种有机物，分子式为G2H7NO，分子量为61.08，无色液体相对密度1.0180，闪点93.3℃。常温下看无色粘稠液体，主要是用于PH值调节作用，使之着色剂加入水性聚氨脂体系中有一个稳定的饱和值。
4、亲水基颜料
主要是指亲水基团又称疏油基团，具有溶于水或者容易与水亲和的原子团。可能吸收水分子或溶解于水。具有这种官能团的固体表面易被水润湿。①阴离子表面活性的亲水基因有羧酸基，磺酸基，磷酸基等；②阳离子表面活性剂的亲水基(团)氨基季氨基；③非离子表面活性剂的亲水基(团)有由合氨基团组成醚基和羟基与羧酸脂、嵌段聚醚等。
对比试验例
一、本发明配方相对现有技术改进
以下举例新旧配方对照说明。其中，表2为水性白色对比，表3为水性土黄对比，表4为水性紫红对比。
表2
表3
表4
由上述表2、表3和表4可知：
①浓度对比：本发明的水性白现配方比原配方高16％；本发明的水性土黄现配方比原配方高12.5％；本发明的水性紫红现配方比原配方高279％。
②环保性：本发明配方不含任何添加剂，不含载体材料，应用体系更广。③本发明配方比原配方更优化，更好控制生产流程。
二、本发明配方相对现有技术的使用测试
表5
| 使用对比例1配方 | 实施例1配方 | |
| 检测项 | 检测结果 | 检测结果 |
| 浓度 | 59.7％ | 69.7％ |
| 是否含有溶剂 | 有 | 无 |
| 是否载体树脂 | 有 | 无 |
| 耐酒精次数 | 10次 | 20次 |
| 耐盐雾 | 差 | 优 |
| 耐候性 | 7-8级 | 7-8级 |
| 耐热性 | 5级 | 5级 |
| 亲水性 | 一般 | 优 |
| 着色剂应用范围 | 有针对性选择 | 水性聚氨脂体系一 |
| 耐迁移性 | 4-5级 | 5 |
| 环保性 | SGS ROS | SGS ROS FDA |
表6
| 使用对比例2配方 | 实施例2配方 | |
| 检测项 | 检测结果 | 检测结果 |
| 浓度 | 48.5％ | 54.5％ |
| 是否含有溶剂 | 有 | 无 |
| 是否载体树脂 | 有 | 无 |
| 耐酒精次数 | 10次 | 20-25次 |
| 耐盐雾 | 差 | 优 |
| 耐候性 | 7-8级 | 7-8级 |
| 耐热性 | 5级 | 5级 |
| 亲水性 | 一般 | 优 |
| 着色剂应用范围 | 有针对性选择 | 水性聚氨脂体系二 |
| 耐迁移性 | 4-5级 | 5级 |
| 环保性 | SGS ROS | SGS ROS FDA |
表7
上述表5，表6和表7中：
水性聚氨脂体系一包括如下重量份比原料：水性聚酯乳液IPDI，45份；聚酯多元醇，80份；DEG，12份；DMPA，5份；丙酮100份；三乙胺，4份；水143份；合计总量389份。
水性聚氨脂体系二包括如下重量份比原料：1、水性聚醚乳液IPDI，45份；聚醚多元醇，80份；DEG，12份；DMPA，5份；丙酮，100份；TEA 4份；水，143份；配方合计总量389份。
水性聚氨脂体系三包括如下重量份比原料：水性聚碳乳液；IPDI，45份；聚碳多元醇，80份；DEG，12份；DMPA，5份；丙酮，100份；TEA，4份；水，143份；配方合计总量389份。
由上表5、表6和表7可得，本发明水性皮革着色剂，满足了水性着色剂不含有任何溶剂和任何载体树脂的需求，有很好的耐盐雾性、耐酒精次数，属于高浓度浓缩全水性着色剂。有非常好的展延性和良好的饱和度。本发明着色剂产品储存更久，应用范围更广，使皮革制造企业油改水工程可顺利实施。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等同变换，或直接或间接运用在相关的技术领域，均同理包括在本发明的专利保护范围内。
Claims (5)
1.一种水性皮革着色剂，其特征在于，由如下重量份比的原料制备而成：颜料100份；功能助剂8-66份；消泡剂0.4-3.3份；一乙醇胺0.1-1.6份和水34.8-175.7份；所述功能助剂为江苏无锡米科思新材料科技有限公司生产的Mix sperse 855w。
2.根据权利要求1所述水性皮革着色剂，其特征在于，具体由如下重量份比的原料制备而成：二氧化钛100份；功能助剂8份；消泡剂0.4份；一乙醇胺0.1份和水34.8份。
3.根据权利要求1所述水性皮革着色剂，其特征在于，具体由如下重量份比的原料制备而成：氧化铁黄100份；功能助剂16份；消泡剂0.8份；一乙醇胺0.2份和水66.3份。
4.根据权利要求1所述水性皮革着色剂，其特征在于，具体由如下重量份比的原料制备而成：PK-122红100份；功能助剂66份；消泡剂3.3份；一乙醇胺1.6份和水175.7份。
5.根据权利要求1-4任一项所述水性皮革着色剂，其特征在于，所述消泡剂为BYK-024。