CN112457759A - Clear primer with good adhesion effect - Google Patents

Clear primer with good adhesion effect Download PDF

Info

Publication number
CN112457759A
CN112457759A CN202011396806.9A CN202011396806A CN112457759A CN 112457759 A CN112457759 A CN 112457759A CN 202011396806 A CN202011396806 A CN 202011396806A CN 112457759 A CN112457759 A CN 112457759A
Authority
CN
China
Prior art keywords
parts
agent
defoamer
good adhesion
emulsion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202011396806.9A
Other languages
Chinese (zh)
Inventor
金建法
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Hasman Coatings Co ltd
Original Assignee
Zhejiang Hasman Coatings Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Hasman Coatings Co ltd filed Critical Zhejiang Hasman Coatings Co ltd
Priority to CN202011396806.9A priority Critical patent/CN112457759A/en
Publication of CN112457759A publication Critical patent/CN112457759A/en
Pending legal-status Critical Current

Abstract

The invention discloses a clear primer with good adhesion effect, which comprises, by weight, 700 parts of waterborne polyurethane emulsion 650-one, 300 parts of styrene-acrylic emulsion 250-one, 1-2 parts of multifunctional amine assistant, 5-7 parts of defoaming agent, 45-55 parts of diethylene glycol monobutyl ether, 25-35 parts of zinc stearate, 2.5-3.5 parts of thickening agent, 2.5-3.5 parts of wetting agent and 2.5-3.5 parts of flatting agent.

Description

Clear primer with good adhesion effect
Technical Field
The invention relates to the technical field of paint, in particular to clear primer with good adhesion effect.
Background
The primer is the first layer of the paint system and is used for improving the adhesive force of the finish paint, increasing the fullness of the finish paint, providing alkali resistance, providing an anti-corrosion function and the like, and simultaneously ensuring the uniform absorption of the finish paint so that the paint system can exert the best effect. The primer can be omitted when the finish paint has good quality, and the finish paint has different functions from the primer, so that the finish paint is more focused on the final decoration and appearance effects, and the primer is focused on improving the adhesive force, the anticorrosion function, the alkali resistance and the like.
Traditional clear priming paint fixed content is lower, leads to feeling relatively poor, and is not level and smooth enough, and the adhesion is poor, can not be fine adhere to on the wall, and long-time the use can lead to the finish to drop, shines into danger easily, provides a solution to below the above problem.
Disclosure of Invention
The invention aims to provide the clear primer with good adhesion effect, which has the advantages of high solid content, good hand feeling, good adhesion and difficult shedding.
The technical purpose of the invention is realized by the following technical scheme:
the clear primer with good adhesion effect comprises, by weight, 700 parts of aqueous polyurethane emulsion 650-.
Preferably, the defoamer comprises an NY-563A defoamer and a BYK-024 defoamer, wherein the ratio of the NY-563A defoamer to the BYK-024 defoamer is 1: 1.
Preferably, the multifunctional amine assistant is AMP-95, and the thickener is a polyurethane thickener.
Preferably, the lubricant is an aqueous wetting agent, and the leveling agent is an organosilicon leveling agent.
Preferably, the feed comprises the following components in parts by weight: 650 parts of aqueous polyurethane emulsion, 300 parts of phenylpropyl emulsion, 2 parts of multifunctional amine assistant, 7 parts of defoamer, 45 parts of diethylene glycol butyl ether, 25 parts of zinc stearate, 3.5 parts of thickener, 2.5 parts of wetting agent, 2.5 parts of flatting agent, wherein the ratio of NY-563A defoamer to BYK-024 defoamer is 1: 1.
Preferably, the feed comprises the following components in parts by weight: 700 parts of waterborne polyurethane emulsion, 250 parts of phenylpropyl emulsion, 1 part of multifunctional amine assistant, 5 parts of defoaming agent, 55 parts of diethylene glycol butyl ether, 30 parts of zinc stearate, 2.5 parts of thickening agent, 2.5 parts of wetting agent and 2.5 parts of flatting agent, wherein the ratio of NY-563A defoaming agent to BYK-024 defoaming agent is 1: 1.
Preferably, the feed comprises the following components in parts by weight: 680 parts of waterborne polyurethane emulsion, 290 parts of phenylpropyl emulsion, 1.5 parts of multifunctional amine assistant, 6 parts of defoaming agent, 50 parts of diethylene glycol butyl ether, 30 parts of zinc stearate, 3 parts of thickening agent, 3 parts of wetting agent and 3 parts of leveling agent, wherein the ratio of NY-563A defoaming agent to BYK-024 defoaming agent is 1: 1.
Preferably, the feed comprises the following components in parts by weight: 700 parts of waterborne polyurethane emulsion, 300 parts of phenylpropyl emulsion, 2 parts of multifunctional amine assistant, 7 parts of defoamer, 45 parts of diethylene glycol butyl ether, 25 parts of zinc stearate, 3 parts of thickener, 3 parts of wetting agent and 3 parts of leveling agent, wherein the ratio of NY-563A defoamer to BYK-024 defoamer is 1: 1.
Preferably, the plastic formulation is made by the steps of:
(1) preparing the defoaming agent according to the proportion as required;
(2) sequentially adding the waterborne polyurethane emulsion, the styrene-acrylic emulsion, the defoaming agent, the flatting agent, the wetting agent, the thickening agent and the zinc stearate according to the formula ratio, and mixing and stirring for about 30 minutes to obtain a mixture;
(3) and adding diethylene glycol monobutyl ether and the multifunctional amine assistant into the mixture in sequence, and continuing stirring for about 10 minutes.
The invention has the beneficial effects that: the styrene-acrylic emulsion has the solid content of 40-45 percent, the styrene-acrylic emulsion has good adhesion, the adhesive film is transparent, the water-resistant, oil-resistant, heat-resistant and aging-resistant performances are good, the waterborne polyurethane is pollution-free, safe and reliable, the mechanical performance is good, the compatibility is good, the modification is easy, an NY-563A defoamer aqueous system has strong defoaming capability, the foam stabilizing performance is good, a BYK-024 defoamer has good compatibility and strong defoaming capability, the two defoamers are mixed in equal proportion, the defoaming effect is improved, the organosilicon leveling agent can effectively reduce the surface tension of the coating liquid, improve the leveling property and uniformity of the coating liquid, improve the permeability of the coating liquid, reduce the possibility of generating spots and stains during brushing, increase the coverage property, enable the film to be uniform and natural, the aqueous wetting agent has good water solubility and smoothness, can effectively reduce the surface tension and high wetting permeability, prevent shrinkage cavities, the multifunctional amine auxiliary agent has the advantages that the multifunctional amine auxiliary agent has no pollution to the environment, does not have adverse effect on the environment, is a standard green environment-friendly high polymer material, increases the flatness and the glossiness by zinc stearate, takes diethylene glycol butyl ether as a solvent, has stable pH value for adjusting the emulsion adhesive, and has the functions of moistening and dispersing.
Detailed Description
The following description is only a preferred embodiment of the present invention, and the protection scope is not limited to the embodiment, and any technical solution that falls under the idea of the present invention should fall within the protection scope of the present invention. It should also be noted that modifications and embellishments within the scope of the invention may occur to those skilled in the art without departing from the principle of the invention.
Example 1
The clear primer with good adhesion effect comprises the following components in parts by weight: 650 parts of aqueous polyurethane emulsion, 300 parts of phenylpropyl emulsion, 2 parts of multifunctional amine assistant, 7 parts of defoamer, 45 parts of diethylene glycol butyl ether, 25 parts of zinc stearate, 3.5 parts of thickener, 2.5 parts of wetting agent, 2.5 parts of flatting agent, wherein the ratio of NY-563A defoamer to BYK-024 defoamer is 1: 1.
Example 2
The clear primer with good adhesion effect comprises the following components in parts by weight: 700 parts of waterborne polyurethane emulsion, 250 parts of phenylpropyl emulsion, 1 part of multifunctional amine assistant, 5 parts of defoaming agent, 55 parts of diethylene glycol butyl ether, 30 parts of zinc stearate, 2.5 parts of thickening agent, 2.5 parts of wetting agent and 2.5 parts of flatting agent, wherein the ratio of NY-563A defoaming agent to BYK-024 defoaming agent is 1: 1.
Example 3
The clear primer with good adhesion effect comprises the following components in parts by weight: 680 parts of waterborne polyurethane emulsion, 290 parts of phenylpropyl emulsion, 1.5 parts of multifunctional amine assistant, 6 parts of defoaming agent, 50 parts of diethylene glycol butyl ether, 30 parts of zinc stearate, 3 parts of thickening agent, 3 parts of wetting agent and 3 parts of leveling agent, wherein the ratio of NY-563A defoaming agent to BYK-024 defoaming agent is 1: 1.
Example 4
The clear primer with good adhesion effect is characterized by comprising the following components in parts by weight: 700 parts of waterborne polyurethane emulsion, 300 parts of phenylpropyl emulsion, 2 parts of multifunctional amine assistant, 7 parts of defoamer, 45 parts of diethylene glycol butyl ether, 25 parts of zinc stearate, 3 parts of thickener, 3 parts of wetting agent and 3 parts of leveling agent, wherein the ratio of NY-563A defoamer to BYK-024 defoamer is 1: 1.
The clear primer formulations of examples 1 to 4 above were all made by the following steps:
(1) preparing the defoaming agent according to the proportion as required;
(2) sequentially adding the aqueous polyurethane emulsion, the defoaming agent, the flatting agent, the wetting agent, the thickening agent and the zinc stearate according to the formula ratio, and mixing and stirring for about 30 minutes to obtain a mixture;
(3) and adding diethylene glycol monobutyl ether and the multifunctional amine assistant into the mixture in sequence, and continuing stirring for about 10 minutes.
And (3) performance testing:
the clear primer was prepared according to the clear primer formulations of examples 1 to 4 above, and the clear primer was tested for solid content, hand and adhesion.
The first embodiment is as follows: the solid content is high, the hand feeling is poor, and the adhesion is poor;
example two: the solid content is low, the hand feeling is good, and the adhesion is good;
example three: the solid content is high, the hand feeling is good, and the adhesion is good;
example four: high solid content, poor hand feeling and poor adhesion.

Claims (9)

1. The clear primer with good adhesion effect is characterized by comprising, by weight, 700 parts of waterborne polyurethane emulsion 650-one, 300 parts of styrene-acrylic emulsion 250-one, 1-2 parts of multifunctional amine assistant, 5-7 parts of defoaming agent, 45-55 parts of diethylene glycol monobutyl ether, 25-35 parts of zinc stearate, 2.5-3.5 parts of thickening agent, 2.5-3.5 parts of wetting agent and 2.5-3.5 parts of flatting agent.
2. The clear primer with good adhesion according to claim 1, wherein the defoamer comprises NY-563A defoamer and BYK-024 defoamer, wherein the ratio of NY-563A defoamer to BYK-024 defoamer is 1: 1.
3. The primer according to claim 1, wherein the multifunctional amine additive is AMP-95 and the thickener is a polyurethane thickener.
4. The clear primer with good adhesion effect as claimed in claim 1, wherein the lubricant is an aqueous wetting agent, and the leveling agent is an organosilicon leveling agent.
5. The clear primer with good adhesion effect according to claim 1, which is characterized by comprising the following components in parts by weight: 650 parts of aqueous polyurethane emulsion, 300 parts of phenylpropyl emulsion, 2 parts of multifunctional amine assistant, 7 parts of defoamer, 45 parts of diethylene glycol butyl ether, 25 parts of zinc stearate, 3.5 parts of thickener, 2.5 parts of wetting agent, 2.5 parts of flatting agent, wherein the ratio of NY-563A defoamer to BYK-024 defoamer is 1: 1.
6. The clear primer with good adhesion effect according to claim 1, which is characterized by comprising the following components in parts by weight: 700 parts of waterborne polyurethane emulsion, 250 parts of phenylpropyl emulsion, 1 part of multifunctional amine assistant, 5 parts of defoaming agent, 55 parts of diethylene glycol butyl ether, 30 parts of zinc stearate, 2.5 parts of thickening agent, 2.5 parts of wetting agent and 2.5 parts of flatting agent, wherein the ratio of NY-563A defoaming agent to BYK-024 defoaming agent is 1: 1.
7. The clear primer with good adhesion effect according to claim 1, which is characterized by comprising the following components in parts by weight: 680 parts of waterborne polyurethane emulsion, 290 parts of phenylpropyl emulsion, 1.5 parts of multifunctional amine assistant, 6 parts of defoaming agent, 50 parts of diethylene glycol butyl ether, 30 parts of zinc stearate, 3 parts of thickening agent, 3 parts of wetting agent and 3 parts of leveling agent, wherein the ratio of NY-563A defoaming agent to BYK-024 defoaming agent is 1: 1.
8. The clear primer with good adhesion effect according to claim 1, which is characterized by comprising the following components in parts by weight: 700 parts of waterborne polyurethane emulsion, 300 parts of phenylpropyl emulsion, 2 parts of multifunctional amine assistant, 7 parts of defoamer, 45 parts of diethylene glycol butyl ether, 25 parts of zinc stearate, 3 parts of thickener, 3 parts of wetting agent and 3 parts of leveling agent, wherein the ratio of NY-563A defoamer to BYK-024 defoamer is 1: 1.
9. The clear primer with good adhesion effect according to claim 1, wherein the plastic formula is prepared by the following steps:
(1) preparing the defoaming agent according to the proportion as required;
(2) sequentially adding the aqueous polyurethane emulsion, the defoaming agent, the flatting agent, the wetting agent, the thickening agent and the zinc stearate according to the formula ratio, and mixing and stirring for about 30 minutes to obtain a mixture;
(3) and adding diethylene glycol monobutyl ether and the multifunctional amine assistant into the mixture in sequence, and continuing stirring for about 10 minutes.
CN202011396806.9A 2020-12-04 2020-12-04 Clear primer with good adhesion effect Pending CN112457759A (en)