CN112430071A - 一种易清洁的日用陶瓷制品及其制备方法 - Google Patents
一种易清洁的日用陶瓷制品及其制备方法 Download PDFInfo
- Publication number
- CN112430071A CN112430071A CN202011300969.2A CN202011300969A CN112430071A CN 112430071 A CN112430071 A CN 112430071A CN 202011300969 A CN202011300969 A CN 202011300969A CN 112430071 A CN112430071 A CN 112430071A
- Authority
- CN
- China
- Prior art keywords
- parts
- easy
- weight
- water
- blank
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种易清洁的日用陶瓷制品及其制备方法，属于陶瓷制品技术领域，包括陶瓷坯体和釉面层，所述陶瓷坯体由包括以下重量份的原料制成：石英粉41‑46份、高岭土36‑45份、氧化锆5‑10份、膨润土12‑18份、贝壳粉10‑20份、电熔镁砂12‑25份、纳米海泡石5‑8份、三聚磷酸钠3‑12份和水32‑87份；所述釉面层由包括以下重量份的原料制成：钾长石21‑25份、硅灰石晶须16‑20份；本发明使得陶瓷制品具有很好的耐磨性能，提升使用质量，增加陶瓷制品的光滑度，不易粘黏污染物，便于清洁，极大提高陶瓷制品的韧性，使得陶瓷制品具有很好的防碰撞性能，不易损坏，使用寿命长。
Description
技术领域
本发明属于陶瓷制品技术领域，具体涉及一种易清洁的日用陶瓷制品及其制备方法。
背景技术
现在主要包括日用陶瓷，建筑陶瓷和卫生洁具等，日用陶瓷就是平常用的陶瓷杯子、盘子什么的建筑陶瓷就是瓷砖什么的卫生洁具包括卫生间里面经常能看到的比如浴缸，洗脸池等等。现有的陶瓷制品在韧性较弱，使得陶瓷制品容易造成划痕，卫生间的浴室柜以及马桶都是陶瓷制品，现有的卫生间的浴室柜以及马桶表面容易附着一些污渍，一些比较顽固的污渍清洁起来不便，因此，需要一种易清洁的日用陶瓷制品及其制备方法来解决以上问题。
发明内容
本发明的目的在于提供一种易清洁的日用陶瓷制品及其制备方法，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：一种易清洁的日用陶瓷制品，包括陶瓷坯体和釉面层，所述陶瓷坯体由包括以下重量份的原料制成：石英粉41-46份、高岭土36-45份、氧化锆5-10份、膨润土12-18份、贝壳粉10-20份、电熔镁砂12-25份、纳米海泡石5-8份、三聚磷酸钠3-12份和水32-87份；所述釉面层由包括以下重量份的原料制成：钾长石21-25份、硅灰石晶须16-20份、氧化钛3-14份、二氧化硅20-40份、氢氧化铝15-25 份、松节油5-15份、环氧氯丙烷6-17份、固化剂4-13份和水22-47份。
进一步，所述陶瓷坯体由包括以下重量份的原料制成：石英粉41份、高岭土36份、氧化锆5份、膨润土12份、贝壳粉10份、电熔镁砂12、纳米海泡石5份、三聚磷酸钠3和水32份。
进一步，所述陶瓷坯体由包括以下重量份的原料制成：石英粉46份、高岭土45份、氧化锆10份、膨润土18份、贝壳粉20份、电熔镁砂15、纳米海泡石8份、三聚磷酸钠12份和水87份。
进一步，所述釉面层由包括以下重量份的原料制成：钾长石21份、硅灰石晶须16份、氧化钛3份、二氧化硅20份、氢氧化铝15份、松节油5份、环氧氯丙烷6份、固化剂4份和水22份。
进一步，所述釉面层由包括以下重量份的原料制成：钾长石25份、硅灰石晶须20份、氧化钛14份、二氧化硅40份、氢氧化铝25份、松节油15份、环氧氯丙烷17份、固化剂13份和水47份。
本发明的另一方面提供了一种易清洁的日用陶瓷制品的制备方法，包括以下步骤：
S1、按上述重量份称取石英粉、高岭土、氧化锆、膨润土、贝壳粉、电熔镁砂、纳米海泡石、三聚磷酸钠和水加入球磨机研磨、过200-400目筛，然后进行除泡，得到坯浆，用液压榨泥机压滤成泥饼，泥饼含水量18-22％，备用。
S2、将S1的泥饼按造型制成毛坯，粗坯定型，自然阴干后进行修整、粘结、雕刻制成精胚；
S3、将精胚晾干后入窑于840-880℃素烧4-6h，窑温自然冷却至30-50℃后出窑，得到素胎，使用喷射材料对素胎进行塑性加工，使素胎的表面形成均匀分布的直线状位错组织。
S4、按上述重量份称取钾长石、硅灰石晶须、氧化钛、二氧化硅、氢氧化铝、松节油、环氧氯丙烷、固化剂和水混合，进行球磨，经过湿磨过的釉料浆通过300目筛，备用；
S5、将S3中得到的素胎浸入S4得到的釉浆中，晾干后，得到素坯；
S6、将素坯最后采用逐渐升温的方式，升温至1180-1240℃的条件下进行烧制2-4小时，然后降温至600-880℃，持续3-8小时，即得高硅陶瓷制品。
进一步，所述S3中，所述喷射材料为含有维氏硬度为500以上且为所述陶瓷制品的硬度为50以下、平均粒径为0.1μm－200μm、表面为凸曲面的微粒。
进一步，所述S4中，固化剂为乙烯基三胺、对羟基苯磺酸中的任一种。
与现有技术相比，本发明的有益效果是：
通过石英粉、高岭土、氧化锆、膨润土制作陶瓷坯料，使得陶瓷制品具有很好的耐磨性能，提升使用质量。
通过在釉面层内加入氢氧化铝、硫化钠、松节油、环氧氯丙烷和固化剂增加陶瓷制品的光滑度，不易粘黏污染物，便于清洁。
本发明采用使用喷射材料对陶瓷制品进行塑性加工处理，极大提高陶瓷制品的韧性，使得陶瓷制品具有很好的防碰撞性能，不易损坏，使用寿命长。
本发明使得陶瓷制品具有很好的耐磨性能，提升使用质量，增加陶瓷制品的光滑度，不易粘黏污染物，便于清洁，极大提高陶瓷制品的韧性，使得陶瓷制品具有很好的防碰撞性能，不易损坏，使用寿命长。
具体实施方式
下面结合实施例对本发明做进一步的描述。
以下实施例用于说明本发明，但不能用来限制本发明的保护范围。实施例中的条件可以根据具体条件做进一步的调整，在本发明的构思前提下对本发明的方法简单改进都属于本发明要求保护的范围。
实施例一
本发明提出的一种易清洁的日用陶瓷制品，包括陶瓷坯体和釉面层，所述陶瓷坯体由包括以下重量份的原料制成：石英粉41-46份、高岭土36-45份、氧化锆5-10份、膨润土12-18份、贝壳粉10-20份、电熔镁砂12-25份、纳米海泡石5-8份、三聚磷酸钠3-12份和水32-87份；所述釉面层由包括以下重量份的原料制成：钾长石21-25份、硅灰石晶须16-20份、氧化钛3-14份、二氧化硅20-40份、氢氧化铝15-25份、松节油5-15份、环氧氯丙烷6-17份、固化剂 4-13份和水22-47份。
本发明提出的一种易清洁的日用陶瓷制品的制备方法，包括以下步骤：
S1、按上述重量份称取石英粉、高岭土、氧化锆、膨润土、贝壳粉、电熔镁砂、纳米海泡石、三聚磷酸钠和水加入球磨机研磨、过200目筛，然后进行除泡，得到坯浆，用液压榨泥机压滤成泥饼，泥饼含水量18％，备用。
S2、将S1的泥饼按造型制成毛坯，粗坯定型，自然阴干后进行修整、粘结、雕刻制成精胚；
S3、将精胚晾干后入窑于840℃素烧4h，窑温自然冷却至30℃后出窑，得到素胎，使用喷射材料对素胎进行塑性加工，使素胎的表面形成均匀分布的直线状位错组织。
S4、按上述重量份称取钾长石、硅灰石晶须、氧化钛、二氧化硅、氢氧化铝、松节油、环氧氯丙烷、固化剂和水混合，进行球磨，经过湿磨过的釉料浆通过300目筛，备用；
S5、将S3中得到的素胎浸入S4得到的釉浆中，晾干后，得到素坯；
S6、将素坯最后采用逐渐升温的方式，升温至1180℃的条件下进行烧制 2-4小时，然后降温至600℃，持续3小时，即得高硅陶瓷制品。
实施例二
本发明提出的一种易清洁的日用陶瓷制品，包括陶瓷坯体和釉面层，所述陶瓷坯体由包括以下重量份的原料制成：石英粉46份、高岭土45份、氧化锆10份、膨润土18份、贝壳粉20份、电熔镁砂25份、纳米海泡石8份、三聚磷酸钠12份和水87份；所述釉面层由包括以下重量份的原料制成：钾长石25份、硅灰石晶须20份、氧化钛14份、二氧化硅40份、氢氧化铝25份、松节油15份、环氧氯丙烷17份、固化剂13份和水47份。
本发明提出的一种易清洁的日用陶瓷制品的制备方法，包括以下步骤：
S1、按上述重量份称取石英粉、高岭土、氧化锆、膨润土、贝壳粉、电熔镁砂、纳米海泡石、三聚磷酸钠和水加入球磨机研磨、过400目筛，然后进行除泡，得到坯浆，用液压榨泥机压滤成泥饼，泥饼含水量22％，备用。
S2、将S1的泥饼按造型制成毛坯，粗坯定型，自然阴干后进行修整、粘结、雕刻制成精胚；
S3、将精胚晾干后入窑于880℃素烧6h，窑温自然冷却至50℃后出窑，得到素胎，使用喷射材料对素胎进行塑性加工，使素胎的表面形成均匀分布的直线状位错组织。
S4、按上述重量份称取钾长石、硅灰石晶须、氧化钛、二氧化硅、氢氧化铝、松节油、环氧氯丙烷、固化剂和水混合，进行球磨，经过湿磨过的釉料浆通过300目筛，备用；
S5、将S3中得到的素胎浸入S4得到的釉浆中，晾干后，得到素坯；
S6、将素坯最后采用逐渐升温的方式，升温至1240℃的条件下进行烧制4 小时，然后降温至880℃，持续8小时，即得高硅陶瓷制品。
实施例三
本发明提出的一种易清洁的日用陶瓷制品，包括陶瓷坯体和釉面层，所述陶瓷坯体由包括以下重量份的原料制成：石英粉44份、高岭土40份、氧化锆7份、膨润土15份、贝壳粉15份、电熔镁砂18份、纳米海泡石7份、三聚磷酸钠7份和水58份；所述釉面层由包括以下重量份的原料制成：钾长石23份、硅灰石晶须18份、氧化钛8份、二氧化硅30份、氢氧化铝20份、松节油10份、环氧氯丙烷11份、固化剂8份和水32份。
本发明提出的一种易清洁的日用陶瓷制品的制备方法，包括以下步骤：
S1、按上述重量份称取石英粉、高岭土、氧化锆、膨润土、贝壳粉、电熔镁砂、纳米海泡石、三聚磷酸钠和水加入球磨机研磨、过300目筛，然后进行除泡，得到坯浆，用液压榨泥机压滤成泥饼，泥饼含水量20％，备用。
S2、将S1的泥饼按造型制成毛坯，粗坯定型，自然阴干后进行修整、粘结、雕刻制成精胚；
S3、将精胚晾干后入窑于860℃素烧5h，窑温自然冷却至40℃后出窑，得到素胎，使用喷射材料对素胎进行塑性加工，使素胎的表面形成均匀分布的直线状位错组织。
S4、按上述重量份称取钾长石、硅灰石晶须、氧化钛、二氧化硅、氢氧化铝、松节油、环氧氯丙烷、固化剂和水混合，进行球磨，经过湿磨过的釉料浆通过300目筛，备用；
S5、将S3中得到的素胎浸入S4得到的釉浆中，晾干后，得到素坯；
S6、将素坯最后采用逐渐升温的方式，升温至1220℃的条件下进行烧制3 小时，然后降温至730℃，持续5小时，即得高硅陶瓷制品。
本发明通过石英粉、高岭土、氧化锆、膨润土制作陶瓷坯料，使得陶瓷制品具有很好的耐磨性能，提升使用质量。通过在釉面层内加入氢氧化铝、硫化钠、松节油、环氧氯丙烷和固化剂增加陶瓷制品的光滑度，不易粘黏污染物，便于清洁。本发明采用使用喷射材料对陶瓷制品进行塑性加工处理，极大提高陶瓷制品的韧性，使得陶瓷制品具有很好的防碰撞性能，不易损坏，使用寿命长。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (8)
1.一种易清洁的日用陶瓷制品，其特征在于：包括陶瓷坯体和釉面层，所述陶瓷坯体由包括以下重量份的原料制成：石英粉41-46份、高岭土36-45份、氧化锆5-10份、膨润土12-18份、贝壳粉10-20份、电熔镁砂12-25份、纳米海泡石5-8份、三聚磷酸钠3-12份和水32-87份；所述釉面层由包括以下重量份的原料制成：钾长石21-25份、硅灰石晶须16-20份、氧化钛3-14份、二氧化硅20-40份、氢氧化铝15-25份、松节油5-15份、环氧氯丙烷6-17份、固化剂4-13份和水22-47份。
2.根据权利要求1所述的一种易清洁的日用陶瓷制品，其特征在于：所述陶瓷坯体由包括以下重量份的原料制成：石英粉41份、高岭土36份、氧化锆5份、膨润土12份、贝壳粉10份、电熔镁砂12、纳米海泡石5份、三聚磷酸钠3和水32份。
3.根据权利要求1所述的一种易清洁的日用陶瓷制品，其特征在于：所述陶瓷坯体由包括以下重量份的原料制成：石英粉46份、高岭土45份、氧化锆10份、膨润土18份、贝壳粉20份、电熔镁砂15、纳米海泡石8份、三聚磷酸钠12份和水87份。
4.根据权利要求1所述的一种易清洁的日用陶瓷制品，其特征在于：所述釉面层由包括以下重量份的原料制成：钾长石21份、硅灰石晶须16份、氧化钛3份、二氧化硅20份、氢氧化铝15份、松节油5份、环氧氯丙烷6份、固化剂4份和水22份。
5.根据权利要求1所述的一种易清洁的日用陶瓷制品，其特征在于：所述釉面层由包括以下重量份的原料制成：钾长石25份、硅灰石晶须20份、氧化钛14份、二氧化硅40份、氢氧化铝25份、松节油15份、环氧氯丙烷17份、固化剂13份和水47份。
6.一种权利要求1-5中任意一项所述的一种易清洁的日用陶瓷制品的制备方法，其特征在于：包括以下步骤：
S1、按上述重量份称取石英粉、高岭土、氧化锆、膨润土、贝壳粉、电熔镁砂、纳米海泡石、三聚磷酸钠和水加入球磨机研磨、过200-400目筛，然后进行除泡，得到坯浆，用液压榨泥机压滤成泥饼，泥饼含水量18-22％，备用。
S2、将S1的泥饼按造型制成毛坯，粗坯定型，自然阴干后进行修整、粘结、雕刻制成精胚；
S3、将精胚晾干后入窑于840-880℃素烧4-6h，窑温自然冷却至30-50℃后出窑，得到素胎，使用喷射材料对素胎进行塑性加工，使素胎的表面形成均匀分布的直线状位错组织。
S4、按上述重量份称取钾长石、硅灰石晶须、氧化钛、二氧化硅、氢氧化铝、松节油、环氧氯丙烷、固化剂和水混合，进行球磨，经过湿磨过的釉料浆通过300目筛，备用；
S5、将S3中得到的素胎浸入S4得到的釉浆中，晾干后，得到素坯；
S6、将素坯最后采用逐渐升温的方式，升温至1180-1240℃的条件下进行烧制2-4小时，然后降温至600-880℃，持续3-8小时，即得高硅陶瓷制品。
7.根据权利要求6所述的一种易清洁的日用陶瓷制品的制备方法，其特征在于：所述S3中，所述喷射材料为含有维氏硬度为500以上且为所述陶瓷制品的硬度为50以下、平均粒径为0.1μm－200μm、表面为凸曲面的微粒。
8.根据权利要求6所述的一种易清洁的日用陶瓷制品的制备方法，其特征在于：所述S4中，固化剂为乙烯基三胺、对羟基苯磺酸中的任一种。