CN112246083A - 一种负氧离子空气净化剂、及其制备方法和应用 - Google Patents
一种负氧离子空气净化剂、及其制备方法和应用 Download PDFInfo
- Publication number
- CN112246083A CN112246083A CN202010922081.6A CN202010922081A CN112246083A CN 112246083 A CN112246083 A CN 112246083A CN 202010922081 A CN202010922081 A CN 202010922081A CN 112246083 A CN112246083 A CN 112246083A
- Authority
- CN
- China
- Prior art keywords
- air purifying
- purifying agent
- mass
- deionized water
- negative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种负氧离子空气净化剂、及其制备方法和应用，属于空气净化剂技术领域。所述负氧离子空气净化剂由负离子混合液、触媒混合液和消毒杀菌液按质量比为1:1:1制成，其中，所述负离子混合液由煅烧后的电气石粉、纳米氧化锌、纳米氧化铈和去离子水制成；所述触媒混合液由纳米氧化锌、二氧化锰水溶液去离子水制成；所述消毒杀菌液由鼠尾草提取物、芦荟提取物和去离子水制成。本发明的负氧离子空气净化剂，可以释放大量的负氧离子，不仅可以快速去除空气中的甲醛、苯、二甲苯、氨和二氧化氮等有害气体，还能在几分钟内去除异味，从而达到灭菌杀毒、净化空气的目的。
Description
技术领域
本发明涉及一种负氧离子空气净化剂、及其制备方法和应用，属于空气净化剂技术领域。
背景技术
空气净化剂是指利用自然物质本身所具有的吸附、分解原理，经过现代科学技术处理，所形成的具有消除空气中有害气体、去除各种异味的产品。目前的空气净化剂分为如下几种：一、利用生物提取物制剂合成，缺点是含有诸多的生物菌种，分解甲醛及二甲苯的速度较慢，净化效果不理想。二、采用纯化学制品合成而得(如二氧化钛光触媒喷剂及甲醛清除剂)，缺点是存在安全隐患且易形成二次污染。三、利用一些植物(如菠萝)简单地置放在房屋中，缺点是以散发香气来掩盖异味，不能与空气中的污染物发生反应，净化效果不理想。
负氧离子是指获得多余电子而带负电荷的氧气离子，它是空气中的氧分子结合了自由电子而形成的。负氧离子是空气中的分子在高压或强射线的作用下被电离所产生的自由电子大部分被氧气所获得的。其中一类因此获得一些电子的带负电荷(电子带负电荷)的氧气离子被称为“负氧离子”，另一类是健康杀手超氧自由基。负氧离子不仅具有净化空气的作用同时还有除臭、灭菌杀毒、净化人体血液等多方面的作用与功能。
但目前，市面上的负氧离子空气净化剂的净化效果并不理想，具体分析如下：
1、由纳米二氧化钛晶体胶体复合而成的负氧离子空气净化剂，由于纳米二氧化钛具有对人体肺部有严重伤害作用，使用该类产品有损人体健康。
2、由硅藻类合成的负氧离子空气净化剂，作用时间短，效果不明显。
3、一些化学制剂合成的负氧离子空气净化剂容易产生二次污染，对人体造成伤害。
鉴于此，有必要开发一种新的负氧离子空气净化剂及其制备方法，以解决现有技术的不足。
发明内容
本发明的目的之一是提供一种负氧离子空气净化剂。本发明的负氧离子空气净化剂，由负离子混合液、触媒混合液和消毒杀菌液三种溶液制成，集合了负离子、新型触媒和消毒杀菌的三种功效，可以释放大量的负氧离子，不仅可以快速去除空气中的甲醛、苯、二甲苯、氨和二氧化氮等有害气体，还能在几分钟内去除异味，从而达到灭菌杀毒、净化空气的目的。
本发明解决上述技术问题的方案如下：一种负氧离子空气净化剂，由负离子混合液、触媒混合液和消毒杀菌液按质量比为1:1:1制成，其中，所述负离子混合液由如下质量百分数的原料制成：煅烧后的电气石粉20％-30％、纳米氧化锌2％-15％、纳米氧化铈0.01％-0.5％和去离子水55％-77％；所述触媒混合液由如下质量百分数的原料制成：纳米氧化锌18％-30％、质量百分浓度为2％的二氧化锰水溶液15％-30％和去离子水40％-67％；所述消毒杀菌液由如下质量百分数的原料制成：鼠尾草提取物0.1％-1.2％、芦荟提取物1％-12％和去离子水86％-98％。
本发明的负氧离子空气净化剂的原理介绍：
本发明的负氧离子空气净化剂由负离子混合液、触媒混合液和消毒杀菌液三种溶液制成，集合了负离子、新型触媒和消毒杀菌的三种功效，能够释放出高浓度的负氧离子，可以快速去除空气中的甲醛、苯、二甲苯、氨和二氧化氮等有害气体，还能在几分钟内去除异味，从而达到灭菌杀毒、净化空气的目的。
第一点，负离子混合液由煅烧后的电气石粉、纳米氧化锌、纳米氧化铈和去离子水制成，分别介绍如下：
1、电气石，是一种结构和成份复杂的含硼硅酸盐矿物，属三方晶系。电气石由于具有特殊晶体结构，能够自动和永久地释放负离子，进而被称之为天然的负氧离子发生器。电气石粉是把电气石原矿经过去除杂质后，经过机械粉碎得到的粉体。电气石粉经过锻烧处理，具有如下优点：(1)可使自身发出的远红外线的波长固定在8μm-12μm，符合人体适合的安全范围。(2)可消除电气石粉里的其它杂质(如铁、锂)，得到更纯净的电气石粉，从而在后续添加纳米氧化铈后，负离子释放的浓度高于添加纳米氧化铈前的6-10倍，增强去除空气中的有害气体。使空气中的负氧离子浓度更高，空气更清新。
上述电气石粉可以市售购买，如可以购自河北铭驰矿产品有限公司。
2、纳米氧化锌，是粒径为1nm-100nm的氧化锌，由于晶粒的细微化，其表面电子结构和晶体结构发生变化，产生了传统氧化锌所不具有的表面效应、体积效应、量子尺寸效应和宏观隧道效应，是一种新型的触媒材料。
上述纳米氧化锌可以市售购买，如可以购自广西柳州锌品有限责任公司。
3、纳米氧化铈，是粒径为1nm-100nm的氧化铈，具有良好的催化、耐高温、紫外吸收性等优良性能。
上述纳米氧化铈可以市售购买，如可以购自天津高科新材料科技有限公司。
煅烧后的电气石粉、纳米氧化锌和纳米氧化铈结合在一起，能够使电石气释放的负离子数量成6-10倍甚至更高倍数的增长。由于纳米氧化锌属于多价无机化合物，因此它有许多特殊性质，如压电性、荧光性、可见光催化活性、吸收和散射紫外线能力等，电气石粉在催化剂纳米氧化铈与纳米氧化锌的共同作用下，释放出更多的负离子储存混合液中，高倍率释放负氧离子，负氧离子浓度可由原来的800个/cm3-3000个/cm3增长到59000个/cm3-65000个/cm3，达到消毒杀菌，净化空气的功效。
第二点，触媒混合液由纳米氧化锌、二氧化锰混合制成，纳米氧化锌加入二氧化锰作为催化剂，能大幅提高去除甲醛的能力，十分钟内甲醛去除率达98％以上，非常地快速有效。
第三点，消毒杀菌液由鼠尾草提取物、芦荟提取物和去离子水制成。其中，鼠尾草提取物中富含二萜、三萜、黄酮和各种酚类化合物，具有抗菌消炎、解毒消肿和去除异味的功效，是去除空气中的有害气体的理想物料。芦荟提取物为百合科植物芦荟叶的粉末状提取物，具有超强吸收甲醛及二甲苯等有害气体(十分钟内甲醛、二甲苯等有害气体去除率达98％以上)，从而达到净化空气的效果。
上述鼠尾草提取物可以市售购买，如可以购自陕西昊辰生物科技有限公司。
上述芦荟提取物可以市售购买，如可以购自陕西汇能达生物科技有限公司。
本发明的负氧离子空气净化剂的有益效果是：
1、本发明的负氧离子空气净化剂，可以释放大量的负氧离子，不仅可以快速去除空气中的甲醛、苯、二甲苯、氨和二氧化氮等有害气体，还能在几分钟内去除异味，从而达到灭菌杀毒、净化空气的目的。
2、本发明的负氧离子空气净化剂，安全无毒，喷撒使用后无有害物质残留，人误食无毒性，对人体无害。
3、本发明的负氧离子空气净化剂，能自动捕捉空气中悬浮的超细颗粒物，以达到除烟降尘、快速杀菌消毒、净化空气的目的，也可提升空气中的负氧离子浓度，从而使空气具有负氧离子的还原性、抗衰老、营养化等功能，达到提高人体免疫力的效果，从而控制疾病的传播。
本发明的负氧离子空气净化剂的使用方法是：
可以涂抹、喷雾或涂擦到多种载体(如布料、木器、金属、塑料等)表面，也可以薫蒸或浸泡。
在上述技术方案的基础上，本发明还可以做如下改进。
进一步，由负离子混合液、触媒混合液和消毒杀菌液按质量比为1:1:1制成，其中，所述负离子混合液由如下质量百分数的原料制成：煅烧后的电气石粉25％、纳米氧化锌8％、纳米氧化铈0.05％和去离子水66.95％；所述触媒混合液由如下质量百分数的原料制成：纳米氧化锌24％、质量百分浓度为2％的二氧化锰水溶液22％和去离子水54％；所述消毒杀菌液由如下质量百分数的原料制成：鼠尾草提取物0.5％、芦荟提取物6％和去离子水93.5％。
采用上述进一步的有益效果是：以上是本案的最佳参数，得到的负氧离子空气净化剂的功效最佳。释放出的负氧离子浓度高达65904个/cm3，从而有效提高人体健康，具体是：(1)调整我们的神经从而改善大脑皮层功能，对改善失眠、神经衰弱、抑郁等具有显著效果。(2)净化血液，加速身体血液循环通畅。(3)活化细胞，以达到抗氧化、防衰老的目的。(4)增强免疫力，改善各种慢性病及维持人体健康。
本发明的目的之二是提供上述负氧离子空气净化剂的制备方法。本发明的制备方法简单，原料来源广泛，成本低廉，市场前景广阔，适合规模化推广应用。
本发明解决上述技术问题的方案如下：一种负氧离子空气净化剂的制备方法，包括如下步骤：
步骤1：制备负离子混合液
取电气石粉，煅烧后，得到煅烧后的电气石粉；
分别称取如下质量百分数的原料：煅烧后的电气石粉20％-30％、纳米氧化锌2％-15％、纳米氧化铈0.01％-0.5％和去离子水55％-77％，混合搅拌均匀，得到负离子混合液；
步骤2：制备触媒混合液
分别称取如下质量百分数的原料：纳米氧化锌18％-30％、质量百分浓度为2％的二氧化锰水溶液15％-30％和去离子水40％-67％，先将称取的纳米氧化锌加入到去离子水中，混合分散后，再与称取的二氧化锰水溶液混合均匀，得到触媒混合液；
步骤3：制备消毒杀菌液
分别称取如下质量百分数的原料：鼠尾草提取物0.1％-1.2％、芦荟提取物1％-12％和去离子水10％-20％，混合搅拌均匀，调节pH值为7-8，得到消毒杀菌液；
步骤4：制备负氧离子空气净化剂
取步骤1得到的负离子混合液、步骤2得到的触媒混合液和步骤3得到的消毒杀菌液，混合均匀后，再加热，除色、过滤，取滤液，即为负氧离子空气净化剂。
本发明的负氧离子空气净化剂的制备方法的有益效果是：
本发明的制备方法简单，原料来源广泛，成本低廉，市场前景广阔，适合规模化推广应用。
在上述技术方案的基础上，本发明还可以做如下改进。
进一步，步骤1中，所述电气石粉的粒径为5000目-8000目。
采用上述进一步的有益效果是：采用上述粒径的电气石粉，煅烧后，制备负离子混合液的效果更好，释放出的负离子浓度更高。经本发明人研究发现，1250目的电气石粉，经煅烧后释放的负离子量是800个/cm3；2000目的电气石粉，经煅烧后释放的负离子量是1600个/cm3；3000目的电气石粉，经煅烧后释放的负离子量是2100个/cm3；5000目的电气石粉，经煅烧后释放的负离子量是4200个/cm3。
进一步，步骤1中，所述煅烧的温度为400℃-600℃，时间为2h-5h。
采用上述进一步的有益效果是：采用上述参数，煅烧的效果更好。增加比表面积的效果更好、释放出的负离子量更多。一般而言，煅烧在马弗炉中进行。
进一步，步骤1中，所述搅拌的转速为3000转/min-6000转/min，时间为30min-45min。
采用上述进一步的有益效果是：采用上述参数，搅拌混合均匀、分散、剪切、增加比表面积的效果更好、释放高浓度负离子的量更多。
进一步，步骤3中，所述调节pH值采用碳酸氢钠。
采用上述进一步的有益效果是：采用碳酸氢钠可以调节pH值为7-8。
进一步，步骤4中，所述加热的温度为76℃-89℃，时间为30min-40min。
采用上述进一步的有益效果是：采用上述加热温度，可以对混合溶液进行活化处理，使负离子能更多更有效的释放出来。
进一步，步骤4中，所述除色采用活性炭。
采用上述进一步的有益效果是：采用活性炭进行除色处理，更加简便高效。
进一步，步骤4中，所述过滤是指采用孔径为0.425nm-0.45nm的沸石分子筛。
采用上述进一步的有益效果是：采用上述参数的沸石分子筛，过滤的效果更好，可以更深层过滤残留物。
本发明的目的之三是提供上述负氧离子空气净化剂的应用。本发明的负氧离子空气净化剂可以用于空气净化领域，用于去除空气中的甲醛、苯、二甲苯、氨和二氧化氮等有害气体，还能在几分钟内去除异味。
本发明解决上述技术问题的方案如下：上述负氧离子空气净化剂在空气净化领域中的应用。
本发明的负氧离子空气净化剂的应用的有益效果是：
本发明的负氧离子空气净化剂可以用于空气净化领域，用于去除空气中的甲醛、苯、二甲苯、氨和二氧化氮等有害气体，还能在几分钟内去除异味。
具体实施方式
以下结合具体实施例对本发明的原理和特征进行描述，所举实例只用于解释本发明，并非用于限定本发明的范围。
实施例1
本实施例的负氧离子空气净化剂，由负离子混合液、触媒混合液和消毒杀菌液按质量比为1:1:1制成，其中，所述负离子混合液由如下质量的原料制成：煅烧后的电气石粉20kg、纳米氧化锌15kg、纳米氧化铈0.01kg和去离子水64.99kg；所述触媒混合液由如下质量的原料制成：纳米氧化锌18kg、质量百分浓度为2％的二氧化锰水溶液30kg和去离子水52kg；所述消毒杀菌液由如下质量的原料制成：鼠尾草提取物0.1kg、芦荟提取物12kg和去离子水87.9kg。
上述负氧离子空气净化剂的制备方法，包括如下步骤：
步骤1：制备负离子混合液
取粒径为5000目的电气石粉，于400℃煅烧5h后，得到煅烧后的电气石粉；
分别称取如下质量的原料：煅烧后的电气石粉20kg、纳米氧化锌15kg、纳米氧化铈0.01kg和去离子水64.99kg，采用转速为3000转/min，时间为45min，混合搅拌均匀，得到负离子混合液。
步骤2：制备触媒混合液
分别称取如下质量的原料：纳米氧化锌18kg、质量百分浓度为2％的二氧化锰水溶液30kg和去离子水52kg，先将称取的纳米氧化锌加入到去离子水中，混合分散后，再与称取的二氧化锰水溶液混合均匀，得到触媒混合液。
步骤3：制备消毒杀菌液
分别称取如下质量的原料：鼠尾草提取物0.1kg、芦荟提取物12kg和去离子水87.9kg，混合搅拌均匀，用碳酸氢钠调节pH值为7，得到消毒杀菌液。
步骤4：制备负氧离子空气净化剂
取步骤1得到的负离子混合液、步骤2得到的触媒混合液和步骤3得到的消毒杀菌液，混合均匀后，再于76℃加热40min，活性炭除色，采用孔径为0.425nm的沸石分子筛过滤，取滤液，即为负氧离子空气净化剂。
实施例2
本实施例的负氧离子空气净化剂，由负离子混合液、触媒混合液和消毒杀菌液按质量比为1:1:1制成，其中，所述负离子混合液由如下质量的原料制成：煅烧后的电气石粉25kg、纳米氧化锌8kg、纳米氧化铈0.05kg和去离子水66.95kg；所述触媒混合液由如下质量百分数的原料制成：纳米氧化锌24kg、质量百分浓度为2％的二氧化锰水溶液22kg和去离子水54kg；所述消毒杀菌液由如下质量的原料制成：鼠尾草提取物0.5kg、芦荟提取物6kg和去离子水93.5kg。
上述负氧离子空气净化剂的制备方法，包括如下步骤：
步骤1：制备负离子混合液
取粒径为6000目的电气石粉，于500℃煅烧3.5h后，得到煅烧后的电气石粉；
分别称取如下质量的原料：煅烧后的电气石粉25kg、纳米氧化锌8kg、纳米氧化铈0.05kg和去离子水66.95kg，采用转速为4500转/min，时间为38min，混合搅拌均匀，得到负离子混合液。
步骤2：制备触媒混合液
分别称取如下质量百原料：纳米氧化锌24kg、质量百分浓度为2％的二氧化锰水溶液22kg和去离子水54kg，先将称取的纳米氧化锌加入到去离子水中，混合分散后，再与称取的二氧化锰水溶液混合均匀，得到触媒混合液。
步骤3：制备消毒杀菌液
分别称取如下质量的原料：鼠尾草提取物0.5kg、芦荟提取物6kg和去离子水93.5kg，混合搅拌均匀，用碳酸氢钠调节pH值为7.5，得到消毒杀菌液。
步骤4：制备负氧离子空气净化剂
取步骤1得到的负离子混合液、步骤2得到的触媒混合液和步骤3得到的消毒杀菌液，混合均匀后，再于83℃加热35min，活性炭除色，采用孔径为0.45nm的沸石分子筛过滤，取滤液，即为负氧离子空气净化剂。
实施例3
本实施例的负氧离子空气净化剂，由负离子混合液、触媒混合液和消毒杀菌液按质量比为1:1:1制成，其中，所述负离子混合液由如下质量的原料制成：煅烧后的电气石粉30kg、纳米氧化锌2kg、纳米氧化铈0.5kg和去离子水67.5kg；所述触媒混合液由如下质量百分数的原料制成：纳米氧化锌30kg、质量百分浓度为2％的二氧化锰水溶液15kg和去离子水55kg；所述消毒杀菌液由如下质量的原料制成：鼠尾草提取物1.2kg、芦荟提取物1kg和去离子水97.8kg。
上述负氧离子空气净化剂的制备方法，包括如下步骤：
步骤1：制备负离子混合液
取粒径为8000目的电气石粉，于600℃煅烧2h后，得到煅烧后的电气石粉；
分别称取如下质量的原料：煅烧后的电气石粉30kg、纳米氧化锌2kg、纳米氧化铈0.5kg和去离子水67.5kg，采用转速为6000转/min，时间为30min，混合搅拌均匀，得到负离子混合液。
步骤2：制备触媒混合液
分别称取如下质量的原料：纳米氧化锌30kg、质量百分浓度为2kg的二氧化锰水溶液15kg和去离子水55kg，先将称取的纳米氧化锌加入到去离子水中，混合分散后，再与称取的二氧化锰水溶液混合均匀，得到触媒混合液。
步骤3：制备消毒杀菌液
分别称取如下质量原料：鼠尾草提取物1.2kg、芦荟提取物1kg和去离子水97.8kg，混合搅拌均匀，用碳酸氢钠调节pH值为8，得到消毒杀菌液。
步骤4：制备负氧离子空气净化剂
取步骤1得到的负离子混合液、步骤2得到的触媒混合液和步骤3得到的消毒杀菌液，混合均匀后，再于89℃加热30min，活性炭除色，采用孔径为0.45nm的沸石分子筛过滤，取滤液，即为负氧离子空气净化剂。
实验例1
在10平方米房间(关窗)内，分别将甲醛、苯、二甲苯、氨和二氧化氮置入各带有有害气体的房间，记录使用前甲醛、苯、二甲苯、氨、二氧化氮、PM2.5、PM10的浓度以及负氧离子数。检测方法参照《室内空气质量标准》GB/T18883-2002。环境温度25℃，相对湿度为55％。甲醛、二甲苯测试用NGP40多功能气体检测仪。负氧离子释放量、PM2.5、PM10的测试用鼎盟空气负氧离子测试仪。
将实施例1-实施例3制备得到的负氧离子空气净化剂各100ml喷雾房间四周，分别记录使用0.5h后甲醛、苯、二甲苯、氨、二氧化氮和PM2.5的浓度以及负氧离子数。计算甲醛、苯、二甲苯、氨、二氧化氮和PM2.5的去除率以及负氧离子增加量。结果如表1所示。
表1测试结果
注：按照根据《GB3095-2012环境空气质量标准》中的规定，一级标准为为PM2.5≤35μg/m3，一级标准为PM10≤50μg/m3。
综上，本发明的负氧离子空气净化剂，可以释放大量的负氧离子，不仅可以快速去除空气中的甲醛、苯、二甲苯、氨和二氧化氮等有害气体，还能在几分钟内去除异味，从而达到灭菌杀毒、净化空气的目的。
对比例1
本对比例的空气净化剂，与实施例1不同的是，没有负离子混合液，具体是由触媒混合液和消毒杀菌液按质量比为1:1制成，其中，所述触媒混合液由如下质量的原料制成：纳米氧化锌18kg、质量百分浓度为2％的二氧化锰水溶液30kg和去离子水52kg；所述消毒杀菌液由如下质量的原料制成：鼠尾草提取物0.1kg、芦荟提取物12kg和去离子水87.9kg。将触媒混合液与消毒杀菌液两者混合均匀后，并在76℃加热40min，活性炭除色，采用孔径为0.425nm的沸石分子筛过滤，取滤液，即为空气净化剂。
对比例2
本对比例的空气净化剂，与实施例2不同的是，没有触媒混合液，具体是由负离子混合液和消毒杀菌液按质量比为1:1制成，其中，所述负离子混合液由如下质量的原料制成：煅烧后的电气石粉25kg、纳米氧化锌8kg、纳米氧化铈0.05kg和去离子水66.95kg；所述消毒杀菌液由如下质量的原料制成：鼠尾草提取物0.5kg、芦荟提取物6kg和去离子水93.5kg。将制得的负离子混合液与制得的消毒杀菌液两者混合均匀后，并在83℃加热35min，活性炭除色，采用孔径为0.45nm的沸石分子筛过滤，取滤液，即为空气净化剂。
对比例3
本对比例的空气净化剂，与实施例3不同的是，没有消毒杀菌液，具体是由负离子混合液和触媒混合液按质量比为1:1制成，其中，所述负离子混合液由如下质量的原料制成：煅烧后的电气石粉30kg、纳米氧化锌2kg、纳米氧化铈0.5kg和去离子水67.5kg；所述触媒混合液由如下质量百分数的原料制成：纳米氧化锌30kg、质量百分浓度为2％的二氧化锰水溶液15kg和去离子水55kg；所述消毒杀菌液由如下质量的原料制成：鼠尾草提取物1.2kg、芦荟提取物1kg和去离子水97.8kg。将制得的负离子混合液与制得的触媒混合液两者混合均匀后，并在89℃加热30min，活性炭除色，采用孔径为0.45nm的沸石分子筛过滤，取滤液，即为空气净化剂。
实验例2
在10平方米房间(关窗)内，分别将甲醛、苯、二甲苯、氨和二氧化氮置入各带有有害气体的房间，记录使用前甲醛、苯、二甲苯、氨、二氧化氮、PM2.5、PM10的浓度以及负氧离子数。检测方法参照《室内空气质量标准》GB/T18883-2002。环境温度25℃，相对湿度为55％。甲醛、二甲苯测试用NGP40多功能气体检测仪。负氧离子释放量、PM2.5、PM10的测试用鼎盟空气负氧离子测试仪。
将对比例1-对比例3制备得到的空气净化剂各100ml喷雾房间四周，分别记录使用0.5h后甲醛、苯、二甲苯、氨、二氧化氮和PM2.5的浓度以及负氧离子数。计算甲醛、苯、二甲苯、氨、二氧化氮和PM2.5的去除率以及负氧离子增加量。结果如表2所示。
表2测试结果
注：按照根据《GB3095-2012环境空气质量标准》中的规定，一级标准为为PM2.5≤35μg/m3，二级标准为PM2.5≤75μg/m3。
由表1和表2可知，实施例1的负离子空气净化剂中，由于添加负离子混合液，负氧离子数增加量为59936个/cm3。而对比例1中，由于没有添加负离子混合液，负氧离子数增加量仅为485个/cm3。
由表1和表2可知，实施例2的负离子空气净化剂中，由于添加了触媒混合液，0.5小时内甲醛去除率达98％以上。而对比例2中，由于没有添加触媒混合液，0.5小时内甲醛去除率仅为95％。
由表1和表2可知，实施例3的负离子空气净化剂中，由于添加了消毒杀菌液，0.5小时内甲醛、二甲苯等有害气体去除率达98％以上。而对比例3中，由于没有添加消毒杀菌液，0.5小时内甲醛、二甲苯等有害气体去除率仅为96％。
综上，本发明的负氧离子空气净化剂，可以释放大量的负氧离子，不仅可以快速去除空气中的甲醛、苯、二甲苯、氨和二氧化氮等有害气体，还能在几分钟内去除异味，从而达到灭菌杀毒、净化空气的目的。
以上所述仅为本发明的较佳实施例，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (10)
1.一种负氧离子空气净化剂，其特征在于，由负离子混合液、触媒混合液和消毒杀菌液按质量比为1:1:1制成，其中，
所述负离子混合液由如下质量百分数的原料制成：煅烧后的电气石粉20％-30％、纳米氧化锌2％-15％、纳米氧化铈0.01％-0.5％和去离子水55％-77％；
所述触媒混合液由如下质量百分数的原料制成：纳米氧化锌18％-30％、质量百分浓度为2％的二氧化锰水溶液15％-30％和去离子水40％-67％；
所述消毒杀菌液由如下质量百分数的原料制成：鼠尾草提取物0.1％-1.2％、芦荟提取物1％-12％和去离子水86％-98％。
2.根据权利要求1所述的负氧离子空气净化剂，其特征在于，由负离子混合液、触媒混合液和消毒杀菌液按质量比为1:1:1制成，其中，所述负离子混合液由如下质量百分数的原料制成：煅烧后的电气石粉25％、纳米氧化锌8％、纳米氧化铈0.05％和去离子水66.95％；所述触媒混合液由如下质量百分数的原料制成：纳米氧化锌24％、质量百分浓度为2％的二氧化锰水溶液22％和去离子水54％；所述消毒杀菌液由如下质量百分数的原料制成：鼠尾草提取物0.5％、芦荟提取物6％和去离子水93.5％。
3.一种负氧离子空气净化剂的制备方法，其特征在于，包括如下步骤：
步骤1：制备负离子混合液
取电气石粉，煅烧后，得到煅烧后的电气石粉；
分别称取如下质量百分数的原料：煅烧后的电气石粉20％-30％、纳米氧化锌2％-15％、纳米氧化铈0.01％-0.5％和去离子水55％-77％，混合搅拌均匀，得到负离子混合液；
步骤2：制备触媒混合液
分别称取如下质量百分数的原料：纳米氧化锌18％-30％、质量百分浓度为2％的二氧化锰水溶液15％-30％和去离子水40％-67％，先将称取的纳米氧化锌加入到去离子水中，混合分散后，再与称取的二氧化锰水溶液混合均匀，得到触媒混合液；
步骤3：制备消毒杀菌液
分别称取如下质量百分数的原料：鼠尾草提取物0.1％-1.2％、芦荟提取物1％-12％和去离子水10％-20％，混合搅拌均匀，调节pH值为7-8，得到消毒杀菌液；
步骤4：制备负氧离子空气净化剂
取步骤1得到的负离子混合液、步骤2得到的触媒混合液和步骤3得到的消毒杀菌液，质量比为1：1：1混合均匀后，再加热，除色、过滤，取滤液，即为负氧离子空气净化剂。
4.根据权利要求3所述的负氧离子空气净化剂的制备方法，其特征在于，步骤1中，所述电气石粉的粒径为5000目-8000目；所述煅烧的温度为400℃-600℃，时间为2h-5h。
5.根据权利要求3所述的负氧离子空气净化剂的制备方法，其特征在于，步骤1中，所述搅拌的转速为3000转/min-6000转/min，时间为30min-45min。
6.根据权利要求3所述的负氧离子空气净化剂的制备方法，其特征在于，步骤3中，所述调节pH值采用碳酸氢钠。
7.根据权利要求3所述的负氧离子空气净化剂的制备方法，其特征在于，步骤4中，所述加热的温度为76℃-89℃，时间为30min-40min。
8.根据权利要求3所述的负氧离子空气净化剂的制备方法，其特征在于，步骤4中，所述除色采用活性炭。
9.根据权利要求3-8任一项所述的负氧离子空气净化剂的制备方法，其特征在于，步骤4中，所述过滤是指采用孔径为0.425nm-0.45nm的沸石分子筛。
10.权利要求1或2所述的负氧离子空气净化剂在空气净化领域中的应用。