CN1122404A - Composite fireproof antitheft door plate and producing technology thereof - Google Patents
Composite fireproof antitheft door plate and producing technology thereof Download PDFInfo
- Publication number
- CN1122404A CN1122404A CN 95105496 CN95105496A CN1122404A CN 1122404 A CN1122404 A CN 1122404A CN 95105496 CN95105496 CN 95105496 CN 95105496 A CN95105496 A CN 95105496A CN 1122404 A CN1122404 A CN 1122404A
- Authority
- CN
- China
- Prior art keywords
- slurry
- door plate
- antitheft door
- frame
- antitheft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The main material of the said door sheet includes steel frame, fibre cloth, antitheft steel wire net, mineral wool and size. The prodn processes include the inner frame soldering with hollow square steel, tapping of the frame for hingle and lock, soldering steel wire net onto the frame, mineral wool filling into the frame, size painting onto the steel wire net to form smooth door sheet. The size consists of MgO-MgCl2 solution, hydrochloric acid, oxalic acid, No.191 resin, trisodium phosphate, defoaming agent, etc. The door sheet is fireproof and antitheft.
Description
The present invention relates to a kind of antitheft door plate and processing technology thereof, particularly a kind of composite fireproof antitheft door plate and processing technology thereof.
At present, the door sheet made from magnesia composite material exists three shortcomings clearly promptly: return halogen, get damp, be out of shape; And generally firm inadequately, can not be antitheft.
The objective of the invention is to avoid above-mentioned the deficiencies in the prior art part and provide a kind of fireproof performance good, the distortion of can not getting damp, and have the composite fireproof antitheft door plate and the processing technology thereof of antitheft effect.
Purpose of the present invention can reach by following measure: the present invention includes steel frame, glass fabric, antitheft gauze wire cloth, mineral wool, slurry, calculate to make 1 film gate sheet, slurry is by magnesia 45kg~55kg, magnesium chloride solution 40kg~50kg, hydrochloric acid 0.5~0.8kg, oxalic acid 0.8kg~1.2kg, 191
#Resin 2.2kg~2.5kg, tertiary sodium phosphate 1.0~1.5kg, defoamer a little, Pa a little.Calculate to make 1 film gate sheet, its processing technology is for to be welded into a sheet inner frame with hollow square steel, with steel frame in steel loose-leaf and the internal tapping of door lock place, with gauze wire cloth plane and steel frame welding, mineral wool is filled in the steel frame, slurry is applied on the gauze wire cloth, it is unilateral to form smooth bright and clean door.
Purpose of the present invention can also reach by following measure: get magnesia 50kg, magnesium chloride solution 45kg, hydrochloric acid 0.65kg, oxalic acid 1kg, 191 in the slurry
#Resin 2.35kg, tertiary sodium phosphate 1.25kg are best.Preparation places magnesium chloride solution with magnesia during slurry, adds hydrochloric acid simultaneously, mixes and stirs with mixer, progressively adds oxalic acid, tertiary sodium phosphate, defoamer, Pa again and stirs into pasty state, adds 191 again during use
#Resin stirs and got final product in 1~2 minute.
The present invention has following advantage compared to existing technology;
1, fireproof performance is good, for not firing product; And can bear 10000 newton's fracture resistence force, satisfy antitheft requirement fully.
2, can not get damp, return halogen, can not be out of shape, manufacturing process is easy, raw material state-owned resource abundance, and energy-saving safe, cost is lower, and use value is widely arranged.
The present invention is described in further detail below in conjunction with accompanying drawing (embodiment):
Embodiment one:
Calculate to make 1 film gate sheet, get hollow square steel and be welded into a sheet inner frame; With steel frame in steel loose-leaf and the internal tapping of door lock place, so that fixedly loose-leaf and door lock are used; With gauze wire cloth plane and steel frame welding; Mineral wool is filled in the steel frame; Slurry is applied on the gauze wire cloth, and it is unilateral to form smooth bright and clean door; Maintenance can be used after 29 days.And slurry adopts magnesium oxide solution 45kg, magnesium oxide solution 50kg (22~27 ° of concentration), hydrochloric acid 0.5kg, oxalic acid 1.2kg, 191
#Resin 2.2kg, tertiary sodium phosphate 1.5kg, defoamer a little, a little preparation of Pa.Process for preparation is; Magnesia is placed magnesium chloride solution, add hydrochloric acid simultaneously, mix and stir, progressively add oxalic acid, tertiary sodium phosphate, defoamer, Pa again and stir into pasty state, add 191 during use with mixer
#Resin stirs and got final product in 1~2 minute.
Embodiment two:
Slurry adopts magnesia 55kg, magnesium oxide solution 40kg (22~27 ° of concentration), hydrochloric acid 0.8kg, oxalic acid 0.8kg, 191
#Resin 2.5kg, tertiary sodium phosphate 1kg, defoamer a little, a little preparation of Pa.Process for preparation is identical with embodiment one.And adopt the antitheft door plate manufacturing process of embodiment one promptly to can be made into composite fireproof antitheft door plate of the present invention.
Embodiment three:
Slurry adopts magnesia 50kg, magnesium oxide solution 45kg (22~27 ° of concentration), hydrochloric acid 0.65kg, oxalic acid 1kg, 191
#Resin 2.35kg, tertiary sodium phosphate 1.25kg, defoamer a little, a little preparation of Pa.Process for preparation is identical with embodiment one.And adopt the antitheft door plate manufacturing process of embodiment one promptly to can be made into composite fireproof antitheft door plate of the present invention.
Claims (4)
1, a kind of composite fireproof antitheft door plate and manufacturing process thereof, it is characterized in that: comprise steel frame, glass fabric, antitheft gauze wire cloth, mineral wool, slurry, calculate to make 1 sheet, slurry is by magnesia 45kg~55kg, magnesium chloride solution 40kg~50kg, hydrochloric acid 0.5~0.8kg, oxalic acid 0.8kg~1.2kg, 191
#Resin 2.2kg~2.5kg, tertiary sodium phosphate 1.0~1.5kg, defoamer a little, Pa a little.
2, antitheft door plate according to claim 1 and manufacturing process thereof is characterized in that: get magnesia 50kg, magnesium chloride solution 45kg, hydrochloric acid 0.65kg, oxalic acid 1kg, 191 in the slurry
#Resin 2.35kg, tertiary sodium phosphate 1.25kg are best.
3, a kind of composite flame-proof antitheft door plate and manufacturing process thereof, it is characterized in that: calculate to make 1 film gate sheet, its processing technology is for to be welded into a sheet inner frame with hollow square steel, with steel frame in steel loose-leaf and the internal tapping of door lock place, with gauze wire cloth plane and steel frame welding, mineral wool is filled in the steel frame, slurry is applied on the gauze wire cloth, it is unilateral to form smooth bright and clean door.
4, according to claim 1 and 3 described antitheft door plate and processing technologys thereof, it is characterized in that: during the preparation slurry, magnesia is placed magnesium chloride solution, add hydrochloric acid simultaneously, with mixer, mix and stir, progressively add oxalic acid again, tertiary sodium phosphate, defoamer, Pa stir into pasty state, add 191 again during use
#Resin stirs and got final product in 1~2 minute.