CN1122351A - 低温常温水中速干腻子 - Google Patents
低温常温水中速干腻子 Download PDFInfo
- Publication number
- CN1122351A CN1122351A CN 95104621 CN95104621A CN1122351A CN 1122351 A CN1122351 A CN 1122351A CN 95104621 CN95104621 CN 95104621 CN 95104621 A CN95104621 A CN 95104621A CN 1122351 A CN1122351 A CN 1122351A
- Authority
- CN
- China
- Prior art keywords
- quick
- drying
- main body
- emplaster
- solidifying agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种低温常温水中速干腻子,它由主体灰膏和固化剂混合配制而成,其中主体灰膏由水、环氧树脂、不饱和树脂、甘油、二甲基苯铵、松香和填料组成,固化剂由苯甲酰、二丁脂和颜料组成。本发明成本低,使用范围广,可在低温和水中速干,不开裂、不脱落,易打磨,可用于车辆、船只、机床、家具等的修补、填平、翻新。
Description
本发明涉及一种低温常温水中速干腻子,属于涂料领域。
目前腻子种类很多,但干燥时间长,易开裂、脱落。常温快速固化腻子、聚脂腻子等虽然工艺性好,但成本较高,而且在潮湿天气和水中不易干燥。中国专利93107061.9公开了一种低温常温速干腻子,它解决了低温快干问题,但在水中不易干燥,同样存在开裂脱落及不易打磨等问题。
本发明的目的在于克服上述现有技术的不足之处,特别是解决低温和水中速干问题,而提供一种生产工艺简单、成本低、使用方便的低温常温水中速干腻。
本发明的目的是这样实现的:它由主体灰膏加配固化剂制成,主体灰膏包括环氧树脂和填料石英粉、石膏粉外,还含有水、不饱和树脂、甘油、二甲基苯铵、松香和填料钛白粉、滑石粉,固化剂包括苯甲酰、二丁脂和颜料。
本发明主体灰膏的各成份配比(重量%)是:
水10—30%;
环氧树脂3—15%;
甘油1—10%;
二甲基苯铵1—10%;
松香1—10%;
不饱和树脂5—15%;
填料20—60%。
固化剂各成份配比(重量%)是:
苯甲酰50—90%;
二丁脂5—45%;
颜料5—10%,为红、兰、黄色。
本发明主体灰膏中填料的各组份配比(重量%)是:
石英粉30—45%;
石膏粉10—20%;
滑石粉30—40%;
钛自粉10—20%。
本发明的主体灰膏和固化剂分别制取,分别包装,使用时二者的配比(重量%)是100∶1—5,搅拌均匀即可。
本发明与现有技术相比,其优点在于:
1.适应性强,干燥时间短,特别是在低温、海水、河水中仍可速干,且干后易打磨。其适应温度—25℃—100℃,干燥时间为15秒—15小时;
2、配制工艺简单易行,薄厚一次成型,不开裂、不脱落,粘接性强,不与油漆反应,喷漆后平滑光亮;
3、使用范围广泛,可用于车辆、船只、机床、家具等的外壳修补、填平、翻新。
4、由于加入了水,减少了树脂用量,成本更为低廉。
下面结合实施例对本发明作进一步详述:
取水180克,环氧树脂40克、甘油10克、二甲基苯铵10克、松香10克,不饱和树脂170克,填料580克(其中石英粉232克,石膏粉87克,滑石粉203克,钛白粉58克)混合搅拌均匀后即得主体灰膏,单一包装备用。
取苯甲酰70克,二丁脂20克,颜料10克,混合搅拌均匀后即得固化剂,单一包装备用。
使用时,将主体灰膏1000克加配固化剂50克搅拌均匀后即可使用。温度高时,可适当减少固化剂,但用量不低于1%。
Claims (5)
1、一种低温常温水中速干腻子,由主体灰膏加配固化剂制成,主体灰膏包括环氧树脂和填料石英粉、石膏粉,固化剂包括苯甲酰、二丁脂和颜料,其特征在于:
主体灰膏还含有水、不饱和树脂、甘油、二甲基苯铵、松香和填料钛自粉、滑石粉。
2、根据权利要求1所述的低温常温水中速干腻子,其特征在于主体灰膏的各成份配比(重量%)是:
水10—30%;
环氧树脂3—15%;
甘油1—10%;
二甲基苯铵1—10%;
松香1—10%;
不饱和树脂5—15%;
填料20—60%。
3、根据权利要求1所述的低温常温水中速干腻子,其特征在于固化剂各成份配比(重量%)是:
苯甲酰50—90%;
二丁脂5—45%;
颜料5—10%。
4、根据权利要求1所述的低温常温水中速干腻子,其特征在于填料的各组份配比(重量%)是:
石英粉30—45%;
石膏粉10—20%;
滑石粉30—40%;
钛白粉10—20%。
5、根据权利要求1所述的低温常温水中速干腻子,其特征在于主体灰膏和固化剂在使用时的配比(重量%)是100∶1—5,搅拌均匀即可。