CN112045328B - 一种核级承压设备贯穿件压力边界j型焊缝返修方法 - Google Patents

一种核级承压设备贯穿件压力边界j型焊缝返修方法 Download PDF

Info

Publication number
CN112045328B
CN112045328B CN202010831302.9A CN202010831302A CN112045328B CN 112045328 B CN112045328 B CN 112045328B CN 202010831302 A CN202010831302 A CN 202010831302A CN 112045328 B CN112045328 B CN 112045328B
Authority
CN
China
Prior art keywords
pressure
welding seam
nuclear
bearing equipment
welding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202010831302.9A
Other languages
English (en)
Other versions
CN112045328A (zh
Inventor
吕俊娥
袁春田
周清利
郑东宏
于敬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Nuclear Engineering Research and Design Institute Co Ltd
Original Assignee
Shanghai Nuclear Engineering Research and Design Institute Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Nuclear Engineering Research and Design Institute Co Ltd filed Critical Shanghai Nuclear Engineering Research and Design Institute Co Ltd
Priority to CN202010831302.9A priority Critical patent/CN112045328B/zh
Publication of CN112045328A publication Critical patent/CN112045328A/zh
Application granted granted Critical
Publication of CN112045328B publication Critical patent/CN112045328B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明的目的在于公开一种核级承压设备贯穿件压力边界J型焊缝返修方法，它包括如下步骤：(1)将J型焊缝位置以下的贯穿件，通过机械加工的方式去除，加工到J型焊缝坡口的水平标高以上位置；(2)在剩余的贯穿件下端底部进行焊接坡口加工，采用耐腐蚀的焊材进行焊接，形成焊缝，在贯穿件和承压设备上形成新的核级承压设备贯穿件压力边界；与现有技术相比，核电厂在役检查时，若发现核级承压设备贯穿件压力边界J型焊缝出现泄漏后，通过上述返修方法，可以有效地进行返修，恢复承压设备贯穿件的压力边界，实现本发明的目的。

Description

一种核级承压设备贯穿件压力边界J型焊缝返修方法
技术领域
本发明涉及一种承压设备返修方法，特别涉及一种核级承压设备贯穿件压力边界J型焊缝返修方法。
背景技术
压水堆核电站核级承压设备的贯穿件，采用J型焊缝作为贯穿件的压力边界。在贯穿件J型焊缝的焊接过程中若焊材选择不合适、焊接工艺不过关、焊接操作不规范、焊接过程质量控制不当，或在核电站运行过程中运行环境的影响，有可能会导致贯穿件J型焊缝在机组运行过程中出现泄漏，导致承压设备贯穿件的压力边界发生破坏。
因此，特别需要一种核级承压设备贯穿件压力边界J型焊缝返修方法，以解决上述现有存在的问题。
发明内容
本发明的目的在于提供一种核级承压设备贯穿件压力边界J型焊缝返修方法，针对现有技术的不足，可以有效地进行返修，恢复承压设备贯穿件的压力边界。
本发明所解决的技术问题可以采用以下技术方案来实现：
一种核级承压设备贯穿件压力边界J型焊缝返修方法，其特征在于，它包括如下步骤：
(1)将J型焊缝位置以下的贯穿件，通过机械加工的方式去除，加工到J型焊缝坡口的水平标高以上位置；
(2)在剩余的贯穿件下端底部进行焊接坡口加工，采用耐腐蚀的焊材进行焊接，形成焊缝，在贯穿件和承压设备上形成新的核级承压设备贯穿件压力边界。
在本发明的一个实施例中，J型焊缝发生泄漏后，将原来的J型焊缝、预堆焊层、耐蚀层遗留在核级承压设备上，不再作为承压设备贯穿件压力边界的一部分。
在本发明的一个实施例中，将J型焊缝位置以下的贯穿件，通过机械加工的方式去除，加工到J型坡口焊缝的水平标高以上位置，且与原J型焊缝位置保持一定的距离，避免将新焊接的焊缝与J型焊缝位置存在重叠。
在本发明的一个实施例中，所述耐腐蚀的焊材包括但不限于镍基焊材ERNiCrFe-7(52)和镍基焊材ENiCrFe-7(152)。
在本发明的一个实施例中，焊接完成后在焊缝位置进行表面处理并进行液体渗透检测。
进一步，所述表面处理包括但不限于机械加工、辊压和抛光。
本发明的核级承压设备贯穿件压力边界J型焊缝返修方法，与现有技术相比，核电厂在役检查时，若发现核级承压设备贯穿件压力边界J型焊缝出现泄漏后，通过上述返修方法，可以有效地进行返修，恢复承压设备贯穿件的压力边界，实现本发明的目的。
本发明的特点可参阅本案图式及以下较好实施方式的详细说明而获得清楚地了解。
附图说明
图1为本发明的核级承压设备贯穿件压力边界J型焊缝的示意图；
图2为本发明的核级承压设备贯穿件压力边界J型焊缝返修的示意图。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体图示，进一步阐述本发明。
实施例
如图1和图2所示，本发明的核级承压设备贯穿件压力边界J型焊缝返修方法，它包括如下步骤：
(1)将J型焊缝位置以下的贯穿件1，通过机械加工(例如机械切削、镗孔机加等)的方式去除，加工到J型焊缝5坡口的水平标高以上位置，且与原J型焊缝位置保持一定的距离，至少要避免新焊接的焊缝与J型焊缝位置存在重叠；
(2)采用机械加工的方式在剩余的贯穿件1下端底部进行焊接坡口加工，采用耐腐蚀的焊材进行焊接，形成焊缝，在贯穿件和承压设备上形成新的核级承压设备贯穿件压力边界。
将原来的J型焊缝5、预堆焊层4、耐蚀层3遗留在核级承压设备2上，不再作为承压设备贯穿件1的压力边界的一部分。
在贯穿件1焊接坡口位置、附近的承压设备2孔表面进行液体渗透检测。
采用的耐腐蚀焊材，例如镍基焊材ERNiCrFe-7(UNS N06052)、ENiCrFe-7(UNSW86152)或其他耐腐蚀焊材,在贯穿件1坡口位置进行焊接，形成焊缝6，在贯穿件1和承压设备2上形成新的核级承压设备贯穿件压力边界。
焊接完成后在焊缝6位置进行表面机械加工处理、然后进行辊压、抛光等方法处理，消除焊接残余应力；对焊缝6位置进行液体渗透检测。
在核电站核级承压设备贯穿件压力边界J型焊缝返修完成后，无需进行额外的压力试验，可通过***加压过程，观察焊接返修后有无再次泄漏，并在后续的在役检查过程中进行重点检查。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内，本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (2)

1.一种核级承压设备贯穿件压力边界J型焊缝返修方法，其特征在于，它包括如下步骤：
(1)将J型焊缝位置以下的贯穿件，通过机械加工的方式去除，加工到J型焊缝坡口的水平标高以上位置；
(2)在剩余的贯穿件下端底部进行焊接坡口加工，采用耐腐蚀的焊材进行焊接，形成焊缝，在贯穿件和承压设备上形成新的核级承压设备贯穿件压力边界；
J型焊缝发生泄漏后，将原来的J型焊缝、预堆焊层、耐蚀层遗留在核级承压设备上，不再作为承压设备贯穿件压力边界的一部分；
将J型焊缝位置以下的贯穿件，通过机械加工的方式去除，加工到J型坡口焊缝的水平标高以上位置，且与原J型焊缝位置保持一定的距离，避免将新焊接的焊缝与J型焊缝位置存在重叠；
焊接完成后在焊缝位置进行表面处理并进行液体渗透检测；
所述耐腐蚀的焊材为镍基焊材ERNiCrFe-7或ENiCrFe-7。
2.如权利要求1所述的核级承压设备贯穿件压力边界J型焊缝返修方法，其特征在于，所述表面处理为机械加工、辊压和抛光。
CN202010831302.9A 2020-08-18 2020-08-18 一种核级承压设备贯穿件压力边界j型焊缝返修方法 Active CN112045328B (zh)