CN111978778A - Coating with functions of interior wall putty and interior wall primer and preparation method thereof - Google Patents
Coating with functions of interior wall putty and interior wall primer and preparation method thereof Download PDFInfo
- Publication number
- CN111978778A CN111978778A CN202011062228.5A CN202011062228A CN111978778A CN 111978778 A CN111978778 A CN 111978778A CN 202011062228 A CN202011062228 A CN 202011062228A CN 111978778 A CN111978778 A CN 111978778A
- Authority
- CN
- China
- Prior art keywords
- putty
- interior wall
- primer
- construction
- functions
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a coating with functions of inner wall putty and inner wall primer and a preparation method thereof, which mainly comprises the following components in parts by weight: the coating comprises a bactericide, a dispersing agent, a defoaming agent, an antifreezing agent, a film-forming auxiliary agent, starch ether, bentonite, a lubricant, lignocellulose, a thickening agent, a pH regulator, acrylic emulsion, heavy calcium powder and cellulose ether. The paint disclosed by the invention not only meets the standard of the N type in the inner wall putty JG/T298-2010, but also meets the standard of the inner wall primer in GB/T9756-2018. The putty paste can be used for batch scraping construction without adding water and stirring on site like putty paste, and the putty accords with the water-resistant standard and has high strength. The putty can be also added with water for roller coating construction, the filling performance is good, the construction of primer is not needed after the putty construction is completed, a lot of manpower is saved, and the indoor decoration efficiency is accelerated.
Description
Technical Field
The invention belongs to the technical field of coatings, and particularly relates to a coating with functions of inner wall putty and inner wall primer and a preparation method thereof.
Technical Field
The existing interior wall primer does not consider the construction performance of interior wall putty, only can be used for brushing paint which can not be scraped for construction, the filling effect of a pile base layer is poor, the existing interior wall putty also does not have the construction performance of the primer, and the primer film-forming property is not achieved after the water adding construction. However, with the rising of decoration labor cost and the like in recent years, decoration companies have great demands for products combining putty and primer, so that the primer can be constructed simultaneously when the putty is constructed, and the construction efficiency is improved.
Disclosure of Invention
The paint provided by the invention has various construction performances of the inner wall putty and the inner wall primer, so that the construction is simpler and more convenient, and a large amount of manpower and material resources can be saved.
The invention is realized by the following technical scheme:
a coating with functions of interior wall putty and interior wall primer is mainly composed of the following components in parts by weight:
the antifreezing agent is propylene glycol.
The film-forming assistant is decaglycol ester.
The pH regulator is AMP-95.
A preparation method of a functional coating with interior wall putty and interior wall primer comprises the following steps:
firstly, dispersing 40-60 parts of heavy calcium powder and cellulose ether in a first container with the stirring speed of 400-500 rpm for 4-5 minutes;
then, 200 parts of water 160-;
then the rotating speed is increased to 800-;
then the rotating speed is increased to 1000-1500 rpm, and 80-120 parts of heavy calcium powder and the materials in the first container are added and stirred for 8-10 minutes;
adding the rest heavy calcium powder, stirring for 25-30 min, and adding water to adjust viscosity.
Compared with the prior art, the invention has the following beneficial effects:
the paint disclosed by the invention not only meets the standard of the N type in the inner wall putty JG/T298-2010, but also meets the standard of the inner wall primer in GB/T9756-2018. The putty paste can be used for batch scraping construction without adding water and stirring on site like putty paste, and the putty accords with the water-resistant standard and has high strength. The putty can be also added with water for roller coating construction, the filling performance is good, the construction of primer is not needed after the putty construction is completed, a lot of manpower is saved, and the indoor decoration efficiency is accelerated.
The product can be directly used for batch scraping construction, and can also be used for roller coating construction by adding 10-30% of water according to the mass ratio.
Detailed Description
The invention will be further elucidated with reference to the following specific examples:
the components of the following examples are preferably as follows:
the aqueous acrylic emulsion is produced by the Dow chemical method, and the product type is DC-430V.
The dispersant type block easy manufacturer in the invention is produced by Rohm and Haas (China) Limited company.
The antifoam model CF246 manufacturer of the invention was bleomy in uk.
The thickener of the present invention is produced by ASE60 manufacturer, Rohm and Haas (China) Co.
The starch ether type 301 manufacturer of the present invention is Ivy, Netherlands
The lubricant used in the present invention is optibert 602 manufactured by bibex chemical corporation, usa
The cellulose ether used in the invention is PMK-40Z, and the manufacturer is Shanghai Hui Guang Fine chemical Co., Ltd
The raw materials mentioned above are the preferred materials in the formula, and the rest materials can be selected to meet the requirements for production.
Example 1
The functional coating with the interior wall putty and the interior wall primer is prepared according to the mass parts of the components listed in the table 1, and the specific preparation method comprises the following steps:
firstly, dispersing 40 parts of heavy calcium powder and cellulose ether in a first container with the stirring speed of 400 rpm for 5 minutes;
then, 160 parts of water, a bactericide, a dispersing agent, a defoaming agent, an antifreezing agent, a film-forming assistant, starch ether, bentonite, a lubricant and lignocellulose are sequentially added into a second container with the stirring speed of 300 revolutions per minute, and the mixture is stirred for 15 minutes;
then increasing the rotating speed to 800 revolutions per minute, adding the thickening agent, the PH regulator and the acrylic emulsion, and continuing stirring for 10 minutes;
then the rotating speed is increased to 1000 r/min, and 80 parts of heavy calcium carbonate powder and the materials in the first container are added and stirred for 10 min;
and adding the rest heavy calcium powder, stirring for 25 minutes, and finally adding water to adjust the viscosity to obtain the calcium bicarbonate.
Example 2
The functional coating with the interior wall putty and the interior wall primer is prepared according to the mass parts of the components listed in the table 1, and the specific preparation method comprises the following steps:
firstly, 50 parts of heavy calcium powder and cellulose ether are dispersed for 4 minutes in a first container with the stirring speed of 500 revolutions per minute;
then, sequentially adding 180 parts of water, a bactericide, a dispersing agent, a defoaming agent, an antifreezing agent, a film-forming assistant, starch ether, bentonite, a lubricant and lignocellulose into a second container with the stirring speed of 600 revolutions per minute, and stirring for 10 minutes;
then increasing the rotating speed to 1000 revolutions per minute, adding the thickening agent, the PH regulator and the acrylic emulsion, and continuing stirring for 8 minutes;
then, the rotating speed is increased to 1500 rpm, and 100 parts of heavy calcium carbonate powder and the materials in the first container are added and stirred for 8 minutes;
then adding the rest heavy calcium powder, stirring for 30 minutes, and finally adding water to adjust the viscosity to obtain the calcium bicarbonate.
Example 3
The functional coating with the interior wall putty and the interior wall primer is prepared according to the mass parts of the components listed in the table 1, and the specific preparation method comprises the following steps:
firstly, 60 parts of heavy calcium powder and cellulose ether are dispersed for 5 minutes in a first container with the stirring speed of 450 revolutions per minute;
then, 200 parts of water, a bactericide, a dispersing agent, a defoaming agent, an antifreezing agent, a film-forming assistant, starch ether, bentonite, a lubricant and lignocellulose are sequentially added into a second container with the stirring speed of 500 revolutions per minute, and the mixture is stirred for 12 minutes;
then increasing the rotating speed to 900 revolutions per minute, adding the thickening agent, the PH regulator and the acrylic emulsion, and continuing stirring for 9 minutes;
then, the rotating speed is increased to 1200 r/min, and then 120 parts of heavy calcium carbonate powder and the materials in the first container are added and stirred for 9 min;
and adding the rest heavy calcium powder, stirring for 28 minutes, and finally adding water to adjust the viscosity to obtain the calcium bicarbonate.
Table 1 examples 1-3 amounts of each component used
Examples 1-3 detection methods: the performance indexes can refer to the N-type standard in JG/T298-2010 and the interior wall primer standard in GB/T9756-2018, and the limited substances refer to GB 18582-2009. Each performance index test was performed on the above examples 1 to 3, and the results are shown in tables 2 and 3 below
TABLE 2 test results of examples 1-3 according to JG/T298-
Table 3 test results for examples 1-3
What has been described above is merely a preferred embodiment of the present invention. It should be noted that a person skilled in the art could make several modifications and variations without departing from the principle of the present invention, which should also be regarded as the protection scope of the present invention.
Claims (5)
1. The coating with the functions of the interior wall putty and the interior wall primer is characterized by mainly comprising the following components in parts by weight:
2. the paint with the functions of interior wall putty and interior wall primer as claimed in claim 1, wherein: the antifreezing agent is propylene glycol.
3. The paint with the functions of interior wall putty and interior wall primer as claimed in claim 1, wherein: the film-forming assistant is decaglycol ester.
4. The paint with the functions of interior wall putty and interior wall primer as claimed in claim 1, wherein: the pH regulator is AMP-95.
5. The method for preparing the paint with the functions of the inner wall putty and the inner wall primer according to any one of the claims 1 to 4, which is characterized by comprising the following steps:
firstly, dispersing 40-60 parts of heavy calcium powder and cellulose ether in a first container with the stirring speed of 400-500 rpm for 4-5 minutes;
then, 200 parts of water 160-;
then the rotating speed is increased to 800-;
then the rotating speed is increased to 1000-1500 rpm, and 80-120 parts of heavy calcium powder and the materials in the first container are added and stirred for 8-10 minutes;
adding the rest heavy calcium powder, stirring for 25-30 min, and adding water to adjust viscosity.