CN111941968A - 耐压、耐腐蚀橡胶气囊布复合材料及其制备方法 - Google Patents
耐压、耐腐蚀橡胶气囊布复合材料及其制备方法 Download PDFInfo
- Publication number
- CN111941968A CN111941968A CN202010798722.1A CN202010798722A CN111941968A CN 111941968 A CN111941968 A CN 111941968A CN 202010798722 A CN202010798722 A CN 202010798722A CN 111941968 A CN111941968 A CN 111941968A
- Authority
- CN
- China
- Prior art keywords
- rubber
- fiber cloth
- resistant
- cloth
- vulcanized
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种耐压、耐腐蚀橡胶气囊布复合材料及其制备方法，包括基础纤维布、涂覆于基础纤维布上的粘结橡胶层、以及贴合于涂覆粘结橡胶层后的基础纤维布上的预硫化橡胶组合物片材；所述基础纤维布包括玻璃纤维布、碳纤维布、高强尼龙纤维布、超高分子量纤维布、聚酰亚胺纤维布中的一种；所述粘结橡胶包括液体丁腈橡胶、液体聚丁二烯橡胶、端羧基液体丁腈橡胶、段羟基液体丁腈橡胶、端羧基液体聚丁二烯橡胶、端羟基液体聚丁二烯橡胶及氯化液体石蜡中的一种。本方案中的橡胶气囊布复合材料具有抗压性好、耐腐蚀性强的优点，可用于加工生产各种可充气的气囊制品，如管道封堵、船用、减震、桥梁、建筑工程、浇注用空芯构建及民用领域等。
Description
技术领域
本发明涉及橡胶技术领域，具体涉及一种耐压、耐腐蚀橡胶气囊布复合材料及其制备方法。
背景技术
橡胶布是由橡胶涂层和基材(如织物)构成的复合材料制品，广泛用于防水、密封、保温、防护等领域，如CN103507341B公开了一种用于软管的橡胶布，其基础纤维布为芳纶纤维，外层橡胶为硅橡胶；CN101210389B提供了一种低发烟耐燃橡胶布的加工方法，其外层胶料为氯磺化橡胶，基础纤维布为聚酯布、尼龙布、棉布、尼龙/聚酯混纺纱布，填充氢氧化铝、硼酸锌；CN101209607A涉及一种未加硫再生丁基橡胶布及加工方法，其操作是将丁基再生橡胶加入三元乙丙，加白烟、煅烧土、防老剂混炼压延，与基布贴合，不用硫化，用于路面、房屋等的防水层铺垫；CN104441911A公开了一种消防用耐燃耐磨橡胶布的制备方法，聚酰胺纤维布作为基布，橡胶糊，氯磺化聚乙烯混炼胶片，压延贴合基布硫化成型。橡胶气囊布是特殊的橡胶布，其构成主要有基层纤维布(帘子布)及交联的橡胶层构成，纤维层作为橡胶气囊布的骨架起到支撑作用，交联的橡胶层同样具有优异的力学强度和气密性，因而采用橡胶气囊布可以制备可充气的制品，如管道封堵气囊、船用气囊、减震气囊、浇注用空芯构件、民用领域等。由于橡胶气囊布复合材料属于特殊的橡胶布，其技术要求和使用比普通的橡胶布要严格，因而产品种类和相关开发与通用橡胶布对比相对较少，国内从事橡胶气囊布复合材料开发的企业和单位远少于通用橡胶布。
CN102086637B，提供了一种高压无缝大型橡胶气囊及其生产工艺，其特点是采用EPDM橡胶做外胶，丁基橡胶做内胶，高强帘子线做基础纤维布，氯丁胶、天然胶作为中层胶；CN201711393967.0报道了一种高强度气囊布的生产方法，用于汽车的安全气囊，其方法是将PA66及其他交联剂、助剂通过熔融流延涂覆到汽车气囊上，形成高强度安全气囊布。
然而，专利申请CN102086637B中提供的高压无缝大型橡胶气囊，外层橡胶层为通用橡胶，橡胶力学性能一般，制品不耐油、不耐化学品腐蚀，形成制品的质量较低。
发明内容
本发明所要解决的技术问题是：如何提高橡胶布的耐油、耐化学品腐蚀程度。
本发明解决其技术问题所采用的技术方案是：一种耐压、耐腐蚀橡胶气囊布复合材料，包括基础纤维布、涂覆于基础纤维布上的粘结橡胶层、以及贴合于涂覆粘结橡胶层后的基础纤维布上的预硫化橡胶组合物片材；
所述基础纤维布包括玻璃纤维布、碳纤维布、高强尼龙纤维布、超高分子量纤维布、聚酰亚胺纤维布中的一种；
所述粘结橡胶包括液体丁腈橡胶、液体聚丁二烯橡胶、端羧基液体丁腈橡胶、段羟基液体丁腈橡胶、端羧基液体聚丁二烯橡胶、端羟基液体聚丁二烯橡胶及氯化液体石蜡中的一种；
所述预硫化橡胶组合物片材包括耐腐蚀橡胶或气密性橡胶、硫化剂或交联剂、补强剂、纳米填料以及增塑剂。
一种耐压、耐腐蚀橡胶气囊布复合材料的制备方法，包括：
在基础纤维布上涂覆粘结橡胶，形成基础高强度纤维布；
制备预硫化橡胶组合物片材；
由基础高强度纤维布和预硫化橡胶组合物片材，制备预硫化的橡胶气囊布组合物片材；
硫化预硫化的橡胶气囊布组合物片材，制备耐压、耐腐蚀橡胶气囊布复合材料。
进一步的，所述在基础纤维布上涂覆粘结橡胶包括：
将50份粘结橡胶等溶于50～100份溶剂中形成粘结胶液，将基础纤维布在粘结胶液中浸渍10～30min，使粘结胶液均匀浸渍于基础纤维布内外，脱除溶剂，形成基础高强度纤维布。
进一步的，所述在基础纤维布上涂覆粘结橡胶包括：
将50份粘结橡胶等溶于50～100份溶剂中形成粘结胶液，将一定量的上述粘结胶液，用机械涂刷的方法均聚涂覆在基础纤维布表面形成基础高强度纤维布。
进一步的，所述制备预硫化橡胶组合物片材，包括：
将100份耐腐蚀橡胶或气密性橡胶、0.1～5份硫化剂或交联剂、1～5份补强剂、1～10份纳米填料以及增塑剂加入到密炼机中于80～100℃下密炼10～30min排料，形成预硫化橡胶母料；
将预硫化橡胶母料通过开炼机或多辊压延机辊压成片制备预硫化橡胶组合物片材，其中，辊压温度为40～60℃，预硫化橡胶组合物片材厚度控制在0.5～5.0mm，预硫化橡胶组合物片材宽度由辊压设备出胶调节挡板控制，预硫化橡胶组合物片材长度由滑动切刀根据需求切割。
进一步的，所述耐腐蚀橡胶包括丙烯酸酯橡胶、氯磺化橡胶、氢化丁腈橡胶、丁腈橡胶、氟橡胶中的一种；
所述气密性橡胶包括丁基橡胶、氯化丁基橡胶、溴化丁基橡胶及环氧化天然橡胶中的一种；
所述硫化剂或交联剂包括硫磺、二硫化四甲基秋兰姆、过氧化二苯甲酰、三烯丙基异三聚氰酸酯中的一种；
所述补强剂包括炭黑或白炭黑，所述炭黑型号为110、N220、N330、N339、N351、N375、N550、N660、N774中的一种，所述白炭黑为气相法白炭黑或沉淀法白炭黑；
所述纳米填料包括纳米碳酸钙、纳米滑石粉、纳米二氧化硅、纳米硫酸钙、钛酸钾晶须中的一种或多种。
进一步的，所述由基础高强度纤维布和预硫化橡胶组合物片材，制备预硫化的橡胶气囊布组合物片材，包括：
将基础高强度纤维布及预硫化橡胶组合物片材经过辊压工艺贴合加工成预硫化的橡胶气囊布组合物片材，辊压后预硫化的橡胶气囊布组合物片材的厚度为0.5～5.0mm。
进一步的，所述辊压工艺为：
一层基础纤维布辊压贴合一层预硫化橡胶组合物片材，或一层基础纤维布辊压贴合二层预硫化橡胶组合物片材，或两层基础纤维布隔层辊压三层预硫化橡胶组合物片材。
进一步的，所述硫化预硫化的橡胶气囊布组合物片材，制备耐压、耐腐蚀橡胶气囊布复合材料，包括：
设定鼓式硫化箱的硫化温度及硫化时间，硫化温度为140～200℃，硫化时间设定在20～40min；
将硫化预硫化的橡胶气囊布组合物片材放入鼓式硫化箱进行硫化，制备耐压、耐腐蚀橡胶气囊布复合材料。
本发明的有益效果是：
该橡胶气囊布复合材料具有抗压性好、耐腐蚀性强的优点，可用于加工生产各种可充气的气囊制品，如管道封堵、船用、减震、桥梁、建筑工程、浇注用空芯构建及民用领域等。
附图说明
下面结合附图和实施例对本发明作进一步说明。
图1为一布一胶的结构示意图；
图2为一布二胶的结构示意图；
图3为两布三胶的结构示意图。
图中：1、基础纤维布；2、粘结橡胶。
具体实施方式
现在结合附图对本发明作详细的说明。此图为简化的示意图，仅以示意方式说明本发明的基本结构，因此其仅显示与本发明有关的构成。
一种耐压、耐腐蚀橡胶气囊布复合材料，如图1-3所示，包括基础纤维布1、涂覆于基础纤维布1上的粘结橡胶2层、以及贴合于涂覆粘结橡胶2层后的基础纤维布1上的预硫化橡胶组合物片材。
可以理解的是，基础纤维布1作为基础载体，粘结橡胶2层涂覆在基础纤维布1上，最后再将预硫化橡胶组合物片材贴合到涂覆了粘结橡胶2层的基础纤维布1上，对其进行硫化操作，具体如下。
其中，基础纤维布1包括玻璃纤维布、碳纤维布、高强尼龙纤维布、超高分子量纤维布、聚酰亚胺纤维布中的一种。
粘结橡胶2包括液体丁腈橡胶、液体聚丁二烯橡胶、端羧基液体丁腈橡胶、段羟基液体丁腈橡胶、端羧基液体聚丁二烯橡胶、端羟基液体聚丁二烯橡胶及氯化液体石蜡中的一种。
预硫化橡胶组合物片材包括耐腐蚀橡胶或气密性橡胶、硫化剂或交联剂、补强剂、纳米填料以及增塑剂。
一种耐压、耐腐蚀橡胶气囊布复合材料的制备方法，包括步骤S101-S104，具体如下：
S101、在基础纤维布1上涂覆粘结橡胶2，形成基础高强度纤维布。
具体地，本步骤有两种实施方式来将粘结橡胶2涂覆到基础纤维布1上，然后形成基础高强度纤维布，具体如下：
第一种方式：
将50份粘结橡胶2等溶于50～100份溶剂中形成粘结胶液，将基础纤维布1在粘结胶液中浸渍10～30min，使粘结胶液均匀浸渍于基础纤维布1内外，脱除溶剂，形成基础高强度纤维布。
可以理解的是，首先利用粘结橡胶2和溶剂形成粘结胶液，然后将粘结胶液均匀浸渍于基础纤维布1内外，形成基础高强度纤维布。
第二种方式：
将50份粘结橡胶2等溶于50～100份溶剂中形成粘结胶液，将一定量的上述粘结胶液，用机械涂刷的方法均聚涂覆在基础纤维布1表面形成基础高强度纤维布。
可以理解的是，本方式是采用机械涂刷的方法均聚涂覆在基础纤维布1表面形成基础高强度纤维布。
S102、制备预硫化橡胶组合物片材。
将100份耐腐蚀橡胶或气密性橡胶、0.1～5份硫化剂或交联剂、1～5份补强剂、1～10份纳米填料以及增塑剂加入到密炼机中于80～100℃下密炼10～30min排料，形成预硫化橡胶母料；
将预硫化橡胶母料通过开炼机或多辊压延机辊压成片制备预硫化橡胶组合物片材，其中，辊压温度为40～60℃，预硫化橡胶组合物片材厚度控制在0.5～5.0mm，预硫化橡胶组合物片材宽度由辊压设备出胶调节挡板控制，预硫化橡胶组合物片材长度由滑动切刀根据需求切割。
其中，耐腐蚀橡胶包括丙烯酸酯橡胶、氯磺化橡胶、氢化丁腈橡胶、丁腈橡胶、氟橡胶中的一种。
气密性橡胶包括丁基橡胶、氯化丁基橡胶、溴化丁基橡胶及环氧化天然橡胶中的一种。
硫化剂或交联剂包括硫磺、二硫化四甲基秋兰姆、过氧化二苯甲酰、三烯丙基异三聚氰酸酯中的一种。
补强剂包括炭黑或白炭黑，所述炭黑型号为110、N220、N330、N339、N351、N375、N550、N660、N774中的一种，所述白炭黑为气相法白炭黑或沉淀法白炭黑。
纳米填料包括纳米碳酸钙、纳米滑石粉、纳米二氧化硅、纳米硫酸钙、钛酸钾晶须中的一种或多种。
S103、由基础高强度纤维布和预硫化橡胶组合物片材，制备预硫化的橡胶气囊布组合物片材。
具体地，将基础高强度纤维布及预硫化橡胶组合物片材经过辊压工艺贴合加工成预硫化的橡胶气囊布组合物片材，辊压后预硫化的橡胶气囊布组合物片材的厚度为0.5～5.0mm。
其中，辊压工艺为：
一层基础纤维布1辊压贴合一层预硫化橡胶组合物片材，或一层基础纤维布1辊压贴合二层预硫化橡胶组合物片材，或两层基础纤维布1隔层辊压三层预硫化橡胶组合物片材。
可以理解的是，本方案可以根据需要来设定橡胶布的基础纤维布1的层数以及预硫化橡胶组合物片材，以满足制品的需要。
S104、硫化预硫化的橡胶气囊布组合物片材，制备耐压、耐腐蚀橡胶气囊布复合材料。
具体地，设定鼓式硫化箱的硫化温度及硫化时间，硫化温度为140～200℃，硫化时间设定在20～40min；将硫化预硫化的橡胶气囊布组合物片材放入鼓式硫化箱进行硫化，制备耐压、耐腐蚀橡胶气囊布复合材料。
现通过以下实施例对本发明做出更详细的说明，但本发明并不限于这些实施例。
实施例1
(1)将100份耐油、耐腐的丁腈橡胶，1.5份硫磺，0.5份二硫化四甲基秋兰姆，3.5份炭黑N330，5份纳米碳酸钙及适量增塑剂，加入到密炼机中于85℃下密炼20min排料；将密炼好的耐油、耐腐蚀预硫化橡胶母料在开炼机或多辊压延机上压片，形成耐油、耐腐蚀预硫化橡胶胶片，压片温度为45℃，胶片厚度为2.6mm。
(2)将100份气密性好的氯化丁基橡胶，1.5份硫磺，0.3份二硫化四甲基秋兰姆，2.5份炭黑N330，5份纳米滑石粉及适量增塑剂，加入到密炼机中于85℃下密炼20min排料；将密炼好的耐油、耐腐蚀预硫化橡胶母料在开炼机或多辊压延机上压片，形成气密预硫化橡胶胶片，压片温度为45℃，胶片厚度为2.6mm。
(3)采用涂刷工艺，将功能化液体粘结橡胶2端羧基液体丁腈橡胶均匀的涂覆在高强尼龙纤维布的一侧，形成具有超强粘结性的预贴合基础纤维布1。
(4)将耐油、耐腐蚀预硫化丁腈橡胶胶片密实覆盖在气密预硫化橡胶胶片上，然后将气密预硫化氯化丁基橡胶一侧紧密覆盖在预贴合基础纤维布1涂覆液体粘结橡胶2一侧，通过多辊压延机将上述混合胶片压延、压实，形成预硫化橡胶气囊布复合材料胶片，胶片厚度为5.0mm。
(5)通过鼓式硫化箱硫化交联上述预硫化橡胶气囊布复合材料胶片，硫化温度为175℃，硫化时间为30min，经过硫化交联工艺后，形成一布一胶式耐压、耐腐蚀橡胶气囊布复合材料。
实施例2
(1)将100份耐油、耐腐的氯磺化橡胶，1.5份硫磺，0.3份二硫化四甲基秋兰姆，2.5份炭黑N220，3.5份纳米二氧化硅及适量增塑剂，加入到密炼机中于90℃下密炼25min排料；将密炼好的耐油、耐腐蚀预硫化橡胶母料在开炼机或多辊压延机上压片，形成耐油、耐腐蚀预硫化橡胶胶片，压片温度为45℃，胶片厚度为2.8mm。
(2)将100份气密性好的溴化丁基橡胶，1.5份硫磺，0.25份二硫化四甲基秋兰姆，2.5份炭黑N220，3.5份纳米纳米滑石粉及适量增塑剂，加入到密炼机中于90℃下密炼25min排料；将密炼好的耐油、耐腐蚀预硫化橡胶母料在开炼机或多辊压延机上压片，形成气密预硫化橡胶胶片，压片温度为45℃，胶片厚度为2.8mm。
(3)采用涂刷工艺，将功能化液体粘结橡胶2端羧基液体丁腈橡胶均匀的涂覆在高强玻璃纤维布的一侧，形成具有超强粘结性的预贴合基础纤维布1。
(4)将耐油、耐腐蚀预硫化氯磺化橡胶胶片密实覆盖在气密预硫化橡胶胶片上，然后将气密预硫化溴化丁基橡胶一侧紧密覆盖在预贴合基础纤维布1涂覆液体粘结橡胶2一侧，通过多辊压延机将上述混合胶片压延、压实，形成预硫化橡胶气囊布复合材料胶片，胶片厚度为5.0mm。
(5)通过鼓式硫化箱硫化交联上述预硫化橡胶气囊布复合材料胶片，硫化温度为170℃，硫化时间为25min，经过硫化交联工艺后，形成一布一胶式耐压、耐腐蚀橡胶气囊布复合材料。
实施例3
(1)将100份耐油、耐腐的丁腈橡胶，1.5份硫磺，0.5份二硫化四甲基秋兰姆，3.5份炭黑N330，5份纳米碳酸钙及适量增塑剂，加入到密炼机中于85℃下密炼20min排料；将密炼好的耐油、耐腐蚀预硫化橡胶母料在开炼机或多辊压延机上压片，形成耐油、耐腐蚀预硫化橡胶胶片，压片温度为50℃，胶片厚度为2.7mm。
(2)将100份气密性好的溴化丁基橡胶，1.5份硫磺，0.3份二硫化四甲基秋兰姆，2.5份炭黑N330，5份纳米碳酸钙及适量增塑剂，加入到密炼机中于85℃下密炼20min排料；将密炼好的耐油、耐腐蚀预硫化橡胶母料在开炼机或多辊压延机上压片，形成气密预硫化橡胶胶片，压片温度为50℃，胶片厚度为2.7mm。
(3)采用浸渍或涂刷工艺，将功能化液体粘结橡胶2端羧基液体丁腈橡胶均匀的涂覆在高强尼龙纤维布的二侧，形成具有超强粘结性的预贴合基础纤维布1。
(4)将耐油、耐腐蚀预硫化丁腈橡胶胶片密实覆盖在预贴合基础纤维布1涂覆液体粘结橡胶2一侧；将气密预硫化溴化丁基橡胶紧密覆盖在预贴合基础纤维布1涂覆液体粘结橡胶2的另一侧；通过多辊压延机将上述混合胶片压延、压实，形成预硫化橡胶气囊布复合材料胶片，胶片厚度为5.0mm。
(5)通过鼓式硫化箱硫化交联上述预硫化橡胶气囊布复合材料胶片，硫化温度为165℃，硫化时间为30min，经过硫化交联工艺后，形成一布二胶式耐压、耐腐蚀橡胶气囊布复合材料。
实施例4
(1)将100份耐油、耐腐的丙烯酸酯橡胶，1.5份硫磺，0.3份二硫化四甲基秋兰姆，2.5份炭黑N330，3.5份纳米二氧化硅及适量增塑剂，加入到密炼机中于85℃下密炼20min排料；将密炼好的耐油、耐腐蚀预硫化橡胶母料在开炼机或多辊压延机上压片，形成耐油、耐腐蚀预硫化橡胶胶片，压片温度为40℃，胶片厚度为2.5mm。
(2)将100份气密性好的丁基橡胶，1.5份硫磺，0.3份二硫化四甲基秋兰姆，2.5份炭黑N330，3.5份纳米二氧化硅及适量增塑剂，加入到密炼机中于85℃下密炼20min排料；将密炼好的耐油、耐腐蚀预硫化橡胶母料在开炼机或多辊压延机上压片，形成气密预硫化橡胶胶片，压片温度为40℃，胶片厚度为2.5mm。
(3)采用浸渍或涂刷工艺，将功能化液体粘结橡胶2端羟基液体丁腈橡胶均匀的涂覆在高分子量聚乙烯纤维布的二侧，形成具有超强粘结性的预贴合基础纤维布1。
(4)将耐油、耐腐蚀预硫化丙烯酸酯橡胶胶片密实覆盖在预贴合基础纤维布1涂覆液体粘结橡胶2一侧；将气密预硫丁基橡胶紧密覆盖在预贴合基础纤维布1涂覆液体粘结橡胶2的另一侧；通过多辊压延机将上述混合胶片压延、压实，形成预硫化橡胶气囊布复合材料胶片，胶片厚度为5.0mm。
(5)通过鼓式硫化箱硫化交联上述预硫化橡胶气囊布复合材料胶片，硫化温度为170℃，硫化时间为30min，经过硫化交联工艺后，形成一布二胶式耐压、耐腐蚀橡胶气囊布复合材料。
实施例5
(1)将100份耐油、耐腐的丁腈橡胶，1.5份硫磺，0.3份二硫化四甲基秋兰姆，2.5份炭黑N550，5.0份纳米碳酸钙及适量增塑剂，加入到密炼机中于85℃下密炼20min排料；将密炼好的耐油、耐腐蚀预硫化橡胶母料在开炼机或多辊压延机上压片，形成耐油、耐腐蚀预硫化丁腈橡胶胶片，压片温度为45℃，胶片厚度为2.0mm。
(2)将100份气密性好的丁基橡胶，1.5份硫磺，0.3份二硫化四甲基秋兰姆，2.5份炭黑N550，5.0份纳米碳酸钙及适量增塑剂，加入到密炼机中于85℃下密炼20min排料；将密炼好的耐油、耐腐蚀预硫化橡胶母料在开炼机或多辊压延机上压片，形成气密预硫化丁基橡胶胶片，压片温度为45℃，胶片厚度为2.0mm。
(3)采用浸渍或涂刷工艺，将功能化液体粘结橡胶2端羟基液体丁腈橡胶均匀的涂覆在高分子量聚乙烯纤维布的二侧，形成具有超强粘结性的预贴合基础纤维布1。
(4)将两层预贴合基础纤维布1中间密实放入气密预硫化丁基橡胶胶片，两层基础纤维布1的外侧分别贴合预硫化丁腈橡胶胶片；通过多辊压延机将上述混合胶片压延、压实，形成预硫化橡胶气囊布复合材料胶片，胶片厚度为5.0mm。
(5)通过鼓式硫化箱硫化交联上述预硫化橡胶气囊布复合材料胶片，硫化温度为175℃，硫化时间为25min，经过硫化交联工艺后，形成二布三胶式耐压、耐腐蚀橡胶气囊布复合材料。
实施例6
(1)将100份耐油、耐腐的丁腈橡胶，1.5份硫磺，0.3份二硫化四甲基秋兰姆，3.5份炭黑N330，2.5份纳米碳酸钙及适量增塑剂，加入到密炼机中于85℃下密炼25min排料；将密炼好的耐油、耐腐蚀预硫化橡胶母料在开炼机或多辊压延机上压片，形成耐油、耐腐蚀预硫化丁腈橡胶胶片，压片温度为45℃，胶片厚度为2.0mm。
(2)将100份耐油、耐腐的丙烯酸酯橡胶，1.5份硫磺，0.3份二硫化四甲基秋兰姆，3.5份炭黑N330，2.5份纳米碳酸钙及适量增塑剂，加入到密炼机中于85℃下密炼25min排料；将密炼好的耐油、耐腐蚀预硫化橡胶母料在开炼机或多辊压延机上压片，形成耐油、耐腐蚀预硫化丙烯酸酯橡胶胶片，压片温度为45℃，胶片厚度为2.0mm。
(3)将100份气密性好的溴化丁基橡胶，1.5份硫磺，0.3份二硫化四甲基秋兰姆，2.5份炭黑N330，5.0份纳米碳酸钙及适量增塑剂，加入到密炼机中于85℃下密炼20min排料；将密炼好的耐油、耐腐蚀预硫化橡胶母料在开炼机或多辊压延机上压片，形成气密预硫化丁基橡胶胶片，压片温度为45℃，胶片厚度为2.0mm。
(3)采用浸渍或涂刷工艺，将功能化液体粘结橡胶2端羟基液体丁腈橡胶均匀的涂覆在高分子量聚乙烯纤维布的二侧，形成具有超强粘结性的预贴合基础纤维布1。
(4)将两层预贴合基础纤维布1中间密实放入气密预硫化丁基橡胶胶片，两层基础纤维布1的外侧分别贴合预硫化丁腈橡胶胶片和预硫化丙烯酸酯橡胶胶片；通过多辊压延机将上述混合胶片压延、压实，形成预硫化橡胶气囊布复合材料胶片，胶片厚度为5.0mm。
(5)通过鼓式硫化箱硫化交联上述预硫化橡胶气囊布复合材料胶片，硫化温度为175℃，硫化时间为25min，经过硫化交联工艺后，形成二布三胶式耐压、耐腐蚀橡胶气囊布复合材料。
对比例1
(1)将100份通用乙丙橡胶，1.5份硫磺，0.5份二硫化四甲基秋兰姆，3.5份炭黑N330，5份纳米碳酸钙及适量增塑剂，加入到密炼机中于80℃下密炼25min排料；将密炼好的预硫化橡胶母料在开炼机或多辊压延机上压片，形成预硫化乙丙橡胶胶片，压片温度为45℃，胶片厚度为5.0mm。
(2)将预硫化乙丙橡胶胶片密实覆盖在通用尼龙纤维布上，通过多辊压延机将上述混合胶片压延、压实，形成预硫化乙丙橡胶气囊布复合材料胶片，胶片厚度为5.0mm。
(3)通过鼓式硫化箱硫化交联上述预硫化橡胶气囊布复合材料胶片，硫化温度为175℃，硫化时间为30min，经过硫化交联工艺后，形成一布一胶式橡胶气囊布复合材料。
对比例2
(1)将100份通用乙丙橡胶，1.5份硫磺，0.3份二硫化四甲基秋兰姆，3.5份炭黑N330，5份纳米滑石粉及适量增塑剂，加入到密炼机中于80℃下密炼20min排料；将密炼好的预硫化橡胶母料在开炼机或多辊压延机上压片，形成预硫化乙丙橡胶胶片，压片温度为45℃，胶片厚度为2.6mm。
(2)将100份通用天然橡胶，1.5份硫磺，0.3份二硫化四甲基秋兰姆，3.5份炭黑N330，5份纳米滑石粉及适量增塑剂，加入到密炼机中于80℃下密炼20min排料；将密炼好的预硫化橡胶母料在开炼机或多辊压延机上压片，形成预硫化天然橡胶胶片，压片温度为45℃，胶片厚度为2.6mm。
(3)将预硫化乙丙橡胶胶片、预硫化天然橡胶胶片分别密实覆盖在通用尼龙纤维布两侧，通过多辊压延机将上述混合胶片压延、压实，形成预硫化橡胶气囊布复合材料胶片，胶片厚度为5.0mm。
(4)通过鼓式硫化箱硫化交联上述预硫化橡胶气囊布复合材料胶片，硫化温度为170℃，硫化时间为30min，经过硫化交联工艺后，形成一布二胶式橡胶气囊布复合材料。
对比例3
(1)将100份丁苯橡胶，1.5份硫磺，0.3份二硫化四甲基秋兰姆，2.5份炭黑N330，2.5份纳米碳酸钙及适量增塑剂，加入到密炼机中于85℃下密炼25min排料；将密炼好的预硫化橡胶母料在开炼机或多辊压延机上压片，形成预硫化丁苯橡胶胶片，压片温度为45℃，胶片厚度为2.0mm。
(2)将100份乙丙橡胶，1.5份硫磺，0.3份二硫化四甲基秋兰姆，2.5份炭黑N330，2.5份纳米碳酸钙及适量增塑剂，加入到密炼机中于85℃下密炼25min排料；将密炼好的预硫化橡胶母料在开炼机或多辊压延机上压片，形成预硫化乙丙橡胶胶片，压片温度为45℃，胶片厚度为2.0mm。
(3)将100份天然橡胶，1.5份硫磺，0.3份二硫化四甲基秋兰姆，2.5份炭黑N330，5.0份纳米碳酸钙及适量增塑剂，加入到密炼机中于85℃下密炼25min排料；将密炼好的预硫化橡胶母料在开炼机或多辊压延机上压片，形成预硫化天然橡胶胶片，压片温度为45℃，胶片厚度为2.0mm。
(4)将两层预贴合基础纤维布1中间密实放入天然橡胶胶片，两层基础纤维布1的外侧分别贴合预硫化丁苯橡胶胶片和预硫化乙丙橡胶胶片；通过多辊压延机将上述混合胶片压延、压实，形成预硫化橡胶气囊布复合材料胶片，胶片厚度为5.0mm。
(5)通过鼓式硫化箱硫化交联上述预硫化橡胶气囊布复合材料胶片，硫化温度为170℃，硫化时间为30min，经过硫化交联工艺后，形成二布三胶式橡胶气囊布复合材料。
测试要求及测试结果如下：
耐压、耐腐蚀橡胶气囊布复合材料测试要求
| 测试项目 | 测试方法 | 指标要求 |
| 密度，g/cm<sup>3</sup> | GB/T533 | 1.5±0.5 |
| 硬度(Shore A) | GB/T531 | 56～64 |
| 断裂伸长率，％ | GB/T528 | ≥400 |
| 拉伸强度，MPa | GB/T528 | ≥10.0 |
| 剥离强度，N/50mm | GB/T528 | ≥120 |
实施列与对比例测试结果
以上述依据本发明的理想实施例为启示，通过上述的说明内容，相关的工作人员完全可以在不偏离本发明的范围内，进行多样的变更以及修改。本项发明的技术范围并不局限于说明书上的内容，必须要根据权利要求范围来确定其技术性范围。
Claims (9)
1.一种耐压、耐腐蚀橡胶气囊布复合材料，其特征在于，包括基础纤维布、涂覆于基础纤维布上的粘结橡胶层、以及贴合于涂覆粘结橡胶层后的基础纤维布上的预硫化橡胶组合物片材；
所述基础纤维布包括玻璃纤维布、碳纤维布、高强尼龙纤维布、超高分子量纤维布、聚酰亚胺纤维布中的一种；
所述粘结橡胶包括液体丁腈橡胶、液体聚丁二烯橡胶、端羧基液体丁腈橡胶、段羟基液体丁腈橡胶、端羧基液体聚丁二烯橡胶、端羟基液体聚丁二烯橡胶及氯化液体石蜡中的一种；
所述预硫化橡胶组合物片材包括耐腐蚀橡胶或气密性橡胶、硫化剂或交联剂、补强剂、纳米填料以及增塑剂。
2.一种耐压、耐腐蚀橡胶气囊布复合材料的制备方法，其特征在于，包括：
在基础纤维布上涂覆粘结橡胶，形成基础高强度纤维布；
制备预硫化橡胶组合物片材；
由基础高强度纤维布和预硫化橡胶组合物片材，制备预硫化的橡胶气囊布组合物片材；
硫化预硫化的橡胶气囊布组合物片材，制备耐压、耐腐蚀橡胶气囊布复合材料。
3.根据权利要求2所述的方法，其特征在于，所述在基础纤维布上涂覆粘结橡胶包括：
将50份粘结橡胶等溶于50～100份溶剂中形成粘结胶液，将基础纤维布在粘结胶液中浸渍10～30min，使粘结胶液均匀浸渍于基础纤维布内外，脱除溶剂，形成基础高强度纤维布。
4.根据权利要求2所述的方法，其特征在于，所述在基础纤维布上涂覆粘结橡胶包括：
将50份粘结橡胶等溶于50～100份溶剂中形成粘结胶液，将一定量的上述粘结胶液，用机械涂刷的方法均聚涂覆在基础纤维布表面形成基础高强度纤维布。
5.根据权利要求2所述的方法，其特征在于，所述制备预硫化橡胶组合物片材，包括：
将100份耐腐蚀橡胶或气密性橡胶、0.1～5份硫化剂或交联剂、1～5份补强剂、1～10份纳米填料以及增塑剂加入到密炼机中于80～100℃下密炼10～30min排料，形成预硫化橡胶母料；
将预硫化橡胶母料通过开炼机或多辊压延机辊压成片制备预硫化橡胶组合物片材，其中，辊压温度为40～60℃，预硫化橡胶组合物片材厚度控制在0.5～5.0mm，预硫化橡胶组合物片材宽度由辊压设备出胶调节挡板控制，预硫化橡胶组合物片材长度由滑动切刀根据需求切割。
6.根据权利要求5所述的方法，其特征在于，所述耐腐蚀橡胶包括丙烯酸酯橡胶、氯磺化橡胶、氢化丁腈橡胶、丁腈橡胶、氟橡胶中的一种；
所述气密性橡胶包括丁基橡胶、氯化丁基橡胶、溴化丁基橡胶及环氧化天然橡胶中的一种；
所述硫化剂或交联剂包括硫磺、二硫化四甲基秋兰姆、过氧化二苯甲酰、三烯丙基异三聚氰酸酯中的一种；
所述补强剂包括炭黑或白炭黑，所述炭黑型号为110、N220、N330、N339、N351、N375、N550、N660、N774中的一种，所述白炭黑为气相法白炭黑或沉淀法白炭黑；
所述纳米填料包括纳米碳酸钙、纳米滑石粉、纳米二氧化硅、纳米硫酸钙、钛酸钾晶须中的一种或多种。
7.根据权利要求2所述的方法，其特征在于，所述由基础高强度纤维布和预硫化橡胶组合物片材，制备预硫化的橡胶气囊布组合物片材，包括：
将基础高强度纤维布及预硫化橡胶组合物片材经过辊压工艺贴合加工成预硫化的橡胶气囊布组合物片材，辊压后预硫化的橡胶气囊布组合物片材的厚度为0.5～5.0mm。
8.根据权利要求7所述的方法，其特征在于，所述辊压工艺为：
一层基础纤维布辊压贴合一层预硫化橡胶组合物片材，或一层基础纤维布辊压贴合二层预硫化橡胶组合物片材，或两层基础纤维布隔层辊压三层预硫化橡胶组合物片材。
9.根据权利要求2所述的方法，其特征在于，所述硫化预硫化的橡胶气囊布组合物片材，制备耐压、耐腐蚀橡胶气囊布复合材料，包括：
设定鼓式硫化箱的硫化温度及硫化时间，硫化温度为140～200℃，硫化时间设定在20～40min；
将硫化预硫化的橡胶气囊布组合物片材放入鼓式硫化箱进行硫化，制备耐压、耐腐蚀橡胶气囊布复合材料。