CN111890831A - Preparation method of handicraft - Google Patents
Preparation method of handicraft Download PDFInfo
- Publication number
- CN111890831A CN111890831A CN202010776967.4A CN202010776967A CN111890831A CN 111890831 A CN111890831 A CN 111890831A CN 202010776967 A CN202010776967 A CN 202010776967A CN 111890831 A CN111890831 A CN 111890831A
- Authority
- CN
- China
- Prior art keywords
- mold
- curing
- glass fiber
- fiber reinforced
- reinforced plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention relates to the field of artware preparation methods, in particular to a preparation method of artware. The method comprises the following steps: a) firstly, spraying a layer of demoulding glue in a mould; b) then mixing the glass fiber reinforced plastic particles with a resin material, pouring the mixture into a mold, filling the mold with glue, and then putting the mold into a curing room for curing; c) demolding the mold after curing; d) then, carrying out colored drawing on the surface of the product; e) and finally spraying transparent water paint on the surface of the product. The invention uses the waste glass fiber reinforced plastic to mix a small amount of resin material to process and manufacture the artware. The raw material cost that this application used is lower, and the plasticity is stronger to manufacturing cost has been practiced thrift.
Description
Technical Field
The invention relates to the field of artware preparation methods, in particular to a preparation method of artware.
Background
The handicraft can be used as household ornament and ornament in various storefronts. The existing artware is high in manufacturing raw material cost.
Disclosure of Invention
In order to solve the technical problems described in the background art, the invention provides a method for preparing artware, which is used for processing and manufacturing artware by using waste glass fiber reinforced plastics and doping a small amount of resin material. The raw material cost that this application used is lower, and the plasticity is stronger to manufacturing cost has been practiced thrift.
The technical scheme adopted by the invention for solving the technical problems is as follows:
a preparation method of artware comprises the following steps:
a) firstly, spraying a layer of demoulding glue in a mould;
b) then mixing the glass fiber reinforced plastic particles with a resin material, pouring the mixture into a mold, filling the mold with glue, and then putting the mold into a curing room for curing;
c) demolding the mold after curing;
d) then, carrying out colored drawing on the surface of the product;
e) and finally spraying transparent water paint on the surface of the product.
Specifically, in the step b), the diameter of the glass fiber reinforced plastic particles is 0.5 mm.
Specifically, in the step b), the mixing ratio of the glass fiber reinforced plastic particles to the resin material is 65% of the glass fiber reinforced plastic particles and 35% of the resin material.
Specifically, in the step b), the curing temperature is 80-100 ℃, and the curing time is 12-24 hours.
The invention has the beneficial effects that: the invention provides a preparation method of artware, which is used for processing and manufacturing artware by doping a small amount of resin material into waste glass fiber reinforced plastics. The raw material cost that this application used is lower, and the plasticity is stronger to manufacturing cost has been practiced thrift.
Detailed Description
The invention will now be described in further detail.
The first embodiment is as follows:
a) firstly, spraying a layer of demoulding glue in a mould;
b) then mixing 65% of glass fiber reinforced plastic particles and 35% of resin material, pouring the mixture into a mold, filling the mold with glue, and then putting the mold into a curing room for curing, wherein the diameter of the glass fiber reinforced plastic particles is 0.5 mm; the curing temperature is 80 ℃, and the curing time is 24 hours;
c) demolding the mold after curing;
d) then, carrying out colored drawing on the surface of the product;
e) and finally spraying transparent water paint on the surface of the product.
Example two:
a) firstly, spraying a layer of demoulding glue in a mould;
b) then mixing 65% of glass fiber reinforced plastic particles and 35% of resin material, pouring the mixture into a mold, filling the mold with glue, and then putting the mold into a curing room for curing, wherein the diameter of the glass fiber reinforced plastic particles is 0.5 mm; the curing temperature is 100 ℃, and the curing time is 12 hours;
c) demolding the mold after curing;
d) then, carrying out colored drawing on the surface of the product;
e) and finally spraying transparent water paint on the surface of the product.
In light of the foregoing description of preferred embodiments according to the invention, many modifications and variations can be made by the worker skilled in the art without departing from the scope of the invention. The technical scope of the present invention is not limited to the content of the specification, and must be determined according to the scope of the claims.
Claims (4)
1. A preparation method of artware is characterized by comprising the following steps: the method comprises the following steps:
a) firstly, spraying a layer of demoulding glue in a mould;
b) then mixing the glass fiber reinforced plastic particles with a resin material, pouring the mixture into a mold, filling the mold with glue, and then putting the mold into a curing room for curing;
c) demolding the mold after curing;
d) then, carrying out colored drawing on the surface of the product;
e) and finally spraying transparent water paint on the surface of the product.
2. The method for preparing the handicraft according to claim 1, characterized in that: in the step b), the diameter of the glass fiber reinforced plastic particles is 0.5 mm.
3. The method for preparing the handicraft according to claim 1, characterized in that: in the step b), the mixing ratio of the glass fiber reinforced plastic particles to the resin material is 65% of the glass fiber reinforced plastic particles and 35% of the resin material.
4. The method for preparing the handicraft according to claim 1, characterized in that: in the step b), the curing temperature is 80-100 ℃, and the curing time is 12-24 hours.