CN100503194C - Method for preparing macromolecule compound die family in use for ceramics - Google Patents
Method for preparing macromolecule compound die family in use for ceramics Download PDFInfo
- Publication number
- CN100503194C CN100503194C CNB2005100321925A CN200510032192A CN100503194C CN 100503194 C CN100503194 C CN 100503194C CN B2005100321925 A CNB2005100321925 A CN B2005100321925A CN 200510032192 A CN200510032192 A CN 200510032192A CN 100503194 C CN100503194 C CN 100503194C
- Authority
- CN
- China
- Prior art keywords
- promoter
- compound die
- curing agent
- filler
- macromolecule compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A process for preparing the composite high-molecular mould used to make ceramic products includes such steps as providing unsaturated polyester resin or silicone rubber, solidifying agent, promoter and filler, copying a sample mould, coating demoulding agent, coating the mixture of gum resin, solidifying agent and promoter, solidifying until it is not adhesive, pouring the mixture of unsaturated polyester resin, solidifying agent, promoter and filler into said sample mould, solidifying and demoulding. Its advantages are high finish degree, strength, toughness and resistance to corrosion and water, and long service life.
Description
Technical field
The present invention relates to a kind of production method of macromolecule compound die family in use for ceramics kind.
Background technology
The mould kind that present porcelain industry is adopted is all turned over gypsum, sulphur or metal material and is made, production, access times increase along with these mould kinds, some pin hole shape duck eyes and hackly phenomenon will appear in working face, the life-span of using is not high yet, increase the workload and the working strength of workers of moulding process, also increased the cost of product accordingly.
Summary of the invention
The objective of the invention is to overcome above-mentioned defective and separate, a kind of production method of macromolecule compound die family in use for ceramics kind is provided.
A kind of production method of macromolecule compound die family in use for ceramics kind, macromolecule compound die family kind are to adopt the associated curing agent of unsaturated polyester resin, promoter and filler to make, and the weight proportion of macromolecule compound die family kind component is as follows:
100 parts of unsaturated polyester resins, curing agent 0.1-1 part,
Promoter 0.1-1 part, filler 20-300 part;
Curing agent is a methyl ethyl ketone peroxide, and promoter is promoter E, and filler is a dry powder;
Pottery is with the production stage of hard macromolecule compound die family kind: get one and turn over the original mold that makes, stamp releasing agent, get gel coating resin again and put into a container, add curing agent and promoter and fully stir evenly and be coated in the original mold surface on its surface, treat gel coating resin solidify do not glue after; According to above-mentioned weight proportion, again unsaturated polyester resin is put into container, add curing agent, promoter again and stir evenly the adding filler fast, after fully stirring evenly, be cast to working face and scribble in the original mold of gel coating resin, begin initial set after half an hour, depanning in one hour is the mould kind after the initial set.
Through experiment, the mould kind that adopts said method to make has following advantage:
1, present existing plaster mold kind single-piece production number of times is about 130 times, and the number of times that the macromolecule compound die family kind that adopts said method to make is produced be it more than 50 times, thereby effectively reduced production cost,
2, the gypsum mold pore of Sheng Chaning is even, thereby has improved the quality of ceramic.
3, the gypsum mold of producing is bright and clean, and regular single-piece moulding number of times is about 140 times, and present traditional the highest can only using 100 times of gypsum mold reduced a large amount of gypsum raw materials to use, and saved resource.
4, the mould of producing is just being advised, and surface effect is good, can reach not snap gauge, and product surface does not need smart base and wash water to reduce moulding process.
The specific embodiment
According to such scheme make mould kind smooth surface, the intensity height, advantages such as corrosion-resistant long service life, the pottery of making is applicable in the ceramic industry with the mould kind.
Hard macromolecule compound die family kind is to adopt unsaturated polyester resin and associated curing agent, promoter and filler to make the macromolecule compound die family kind, and the weight proportion of its component is as follows:
100 parts of unsaturated polyester resins, 1 part of methyl ethyl ketone peroxide,
1 part of promoter E, 260 parts of dry powders;
Get one and turn over the original mold that makes, stamp releasing agent, get gel coating resin again and put into a container, add methyl ethyl ketone peroxide and promoter E and fully stir evenly and be coated in the original mold surface on its surface, treat gel coating resin solidify sticking after; According to above-mentioned weight proportion, again unsaturated polyester resin is put into container, add methyl ethyl ketone peroxide, promoter E again, stir evenly the adding filler fast, after fully stirring evenly, be cast to working face and scribble in the original mold of gel coating resin, begin initial set after half an hour, depanning in one hour is the macromolecule compound die family kind after the initial set.
Claims (1)
1, a kind of production method of macromolecule compound die family in use for ceramics kind is characterized in that:
A, described macromolecule compound die family kind are to adopt unsaturated polyester resin and associated curing agent, promoter and filler to make, and the weight proportion of macromolecule compound die family kind component is as follows:
100 parts of unsaturated polyester resins, curing agent 0.1-1 part,
Promoter 0.1-1 part, filler 20-300 part;
Described curing agent is a methyl ethyl ketone peroxide, and described promoter is promoter E, and described filler is a dry powder;
B, the pottery production stage of hard macromolecule compound die family kind:
Get one and turn over the original mold that makes, stamp releasing agent, get gel coating resin again and put into a container, add curing agent and promoter and fully stir evenly and be coated in the original mold surface on its surface, treat gel coating resin solidify sticking after; According to above-mentioned weight proportion, again unsaturated polyester resin is put into container, add curing agent, promoter again and stir evenly the adding filler fast, after fully stirring evenly, be cast to working face and scribble in the original mold of gel coating resin, begin initial set after half an hour, depanning in one hour is the mould kind after the initial set.