CN105541278A - 一种坚果外壳轻体墙板及其制备方法 - Google Patents
一种坚果外壳轻体墙板及其制备方法 Download PDFInfo
- Publication number
- CN105541278A CN105541278A CN201511006420.1A CN201511006420A CN105541278A CN 105541278 A CN105541278 A CN 105541278A CN 201511006420 A CN201511006420 A CN 201511006420A CN 105541278 A CN105541278 A CN 105541278A
- Authority
- CN
- China
- Prior art keywords
- shell
- nut
- wall board
- nut shell
- light wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了本发明所提供的坚果外壳轻体墙板由下述重量份的原料组成:坚果外壳45-55%,氧化镁13-15%,氯化镁4-5%,粘土粉8-10%,椰壳纤维5-6%,减水剂2-3.5%,粘结剂1-6%,本发明设计的环保型植物纤维轻体墙板,原料中可再生坚果外壳、椰壳纤维的含量占总原料用量的一半多,总废物再利用达60%以上,超出同类轻体墙的水平。
Description
技术领域
本发明属于建筑材料领域,涉及一种坚果外壳轻体墙板及其制备方法。
背景技术
随着人们对节能绿色建筑的需求越来越大,国家对粘土实心砖禁止生产和使用,但目前国内墙材生产企业大部分选用粘土、碎石、砂子及轻骨料作填料,属于破坏资源生产建材。有很多企业利用农业废弃物植物秸秆作为原料生产墙板,另外添加粘合剂、阻燃剂、增强剂等,虽然在秸秆废物利用方面达到绿色环保要求,但是其添加剂有的为高能耗的水泥,没有真正意义上达到绿色环保,尤其是加工过程中,基本都要经过热压加工,需要大型设备仪器,成本高、能耗高。
核桃壳、栗子壳、花生壳、椰子壳等壳类物质作为销售废料,质地紧实,不易腐烂降解,果壳难以回收利用,造成大量的资源浪费及堆积污染,因此,避免壳类物质的浪费,生产附加值高的产品,可以有效处理固体废弃物,变废为宝。
发明内容
本发明提供了一种坚果外壳轻体墙板。
本发明所提供的坚果外壳轻体墙板由下述重量份的原料组成:坚果外壳45-55%,氧化镁13-15%,氯化镁4-5%,粘土粉8-10%,椰壳纤维5-6%,减水剂2-3.5%,粘结剂1-6%。
优选的,所述轻体墙由下述重量份的原料组成:坚果外壳58-63%,氧化镁13.5-14%,氯化镁4-5%,粘土粉8.5-9%,椰壳纤维5-6%,减水剂2.5-3%,粘结剂2.5-6%。
具体的,所述减水剂由木质素磺酸盐减水剂和萘磺酸盐减水剂以质量比8:2复配而成。
所述坚果外壳为核桃壳或栗子壳或花生壳或其两者或三者的复合物球磨混合而成。
所述坚果外壳为核桃壳、栗子壳按质量比5-8:2-5混合或核桃壳、花生壳按质量比5-8:2-5混合或核桃壳、栗子壳、花生壳按质量比5-8:1-2:1-3混合,球磨细度为300目-500目。
所述粘结剂为浓度为30-35%的PVA溶液。
上述坚果外壳轻体墙板的制备方法,包括下述步骤:
(1)将15-25%质量浓度的氯化镁溶液和70-75%质量浓度的氧化镁按比例混合得固化剂混合液;
(2)边搅拌步骤(1)中所述混合液,边在混合液中依次按比例加入将粉碎后的坚果外壳、粘土粉、椰壳纤维、粘接剂、减水剂,全部加入后,继续搅拌至物料均匀,得到混合浆料;
(3)将步骤(2)中所得混合浆料放入模具,制坯成型,室温下放置,固化后揭开模具,得到坯体;
(4)将步骤(3)中所得坯体在温度为28-35℃,湿度为30-45%下养护3-4小时即得轻体墙板。
与现有技术相比,本发明具有如下有益效果:
(1)本发明采用常见农业废弃原料核桃壳、栗子壳、花生壳、椰壳纤维作为原料,变废为宝,实现了农业资源的利用,增加了农业收入,减少了环境污染,降低了原料成本。
(2)本发明所提供的方法制得的轻体墙版其各项性能指标符合国家标准《烧结多孔砖和多孔砌块》(GB13544)的相关要求。
(3)木质素磺酸盐和萘磺酸盐为阴离子表面活性剂,能在固-液界面上产生单分子吸附,因此,当木质素磺酸盐和萘磺酸盐掺入坚果外壳、粘土粉、椰壳纤维中,可使纤维粉带负电,由于带相同电荷相互排斥而使粒子分散。同时,由于木质素磺酸盐和萘磺酸盐具有大量亲水性基团,能降低气液表面张力,从而具有引气性,可进一步改善粉体的和易性。本发明设计的环保型植物纤维轻体墙板,原料中可再生坚果外壳、椰壳纤维的含量占总原料用量的一半多,总废物再利用达60%以上,超出同类轻体墙的水平。
具体实施方式
下面结合具体实施方式,对本发明作进一步说明,但本发明的保护范围并不限于所述内容。
本发明实施例中所用化学试剂均为分析纯。
实施例1
核桃壳29%,栗子壳29%,氧化镁14%,氯化镁4%,粘土粉9%,椰壳纤维6%,减水剂木质素磺酸钠2.4%,萘磺酸钠0.6%,35%的PVA溶液6%。
(1)将15%质量浓度的氯化镁溶液和75%质量浓度的氧化镁按上述比例混合得固化剂混合液;
(2)边搅拌步骤(1)中所述混合液,边在混合液中依次按比例加入将粉碎后的坚果外壳、粘土粉、椰壳纤维、粘接剂、减水剂,全部加入后,继续搅拌至物料均匀,得到混合浆料;
(3)将步骤(2)中所得混合浆料放入模具,制坯成型,室温下放置,固化后揭开模具,得到坯体;
(4)将步骤(3)中所得坯体在温度为28-35℃,湿度为30-45%下养护3-4小时即得轻体墙板。
以下是本轻体墙的检验报告:
实施例2
核桃壳31.5%,栗子壳18.9%,花生壳12.6%,氧化镁13.5%,氯化镁4%,粘土粉8.5%,椰壳纤维6%,木质素磺酸盐2%,萘磺酸盐减水剂0.5%,35%的PVA溶液2.5%。。
(1)将15%质量浓度的氯化镁溶液和75%质量浓度的氧化镁按上述比例混合得固化剂混合液;
(2)边搅拌步骤(1)中所述混合液,边在混合液中依次按比例加入将粉碎后的坚果外壳、粘土粉、椰壳纤维、粘接剂、减水剂,全部加入后,继续搅拌至物料均匀,得到混合浆料;
(3)将步骤(2)中所得混合浆料放入模具,制坯成型,室温下放置,固化后揭开模具,得到坯体;
(4)将步骤(3)中所得坯体在温度为28℃,湿度为30%下养护4小时即得轻体墙板。
上面所述实施例对本发明的具体实施方式做了详细说明,但是本发明并不限于上述实施方式,在本领域普通技术人员所具备的知识范围内,还可以在不脱离本发明宗旨的前提下做出各种变化。
Claims (7)
1.一种坚果外壳轻体墙板,其特征在于:所述轻体墙由下述重量份的原料组成坚果外壳45-55%,氧化镁13-15%,氯化镁4-5%,粘土粉8-10%,椰壳纤维5-6%,减水剂2-3.5%,粘结剂1-6%。
2.根据权利要求1所述的坚果外壳轻体墙板,其特征在于:所述轻体墙由下述重量份的原料组成:坚果外壳58-63%,氧化镁13.5-14%,氯化镁4-5%,粘土粉8.5-9%,椰壳纤维5-6%,减水剂2.5-3%,粘结剂2.5-6%。
3.根据权利要求1所述的坚果外壳轻体墙板,其特征在于:所述减水剂由木质素磺酸盐减水剂和萘磺酸盐减水剂以质量比8:2复配而成。
4.根据权利要求1所述的坚果外壳轻体墙板,其特征在于:所述坚果外壳为核桃壳或栗子壳或花生壳或其两者或三者的复合物球磨混合而成。
5.根据权利要求4所述的坚果外壳轻体墙板,其特征在于:所述坚果外壳为核桃壳、栗子壳按质量比5-8:2-5混合或核桃壳、花生壳按质量比5-8:2-5混合或核桃壳、栗子壳、花生壳按质量比5-8:1-2:1-3混合,球磨细度为300目-500目。
6.根据权利要求1所述的坚果外壳轻体墙板,其特征在于:所述粘结剂为浓度为30-35%的PVA溶液。
7.制备权利要求1或2所述的坚果外壳轻体墙板的方法,包括下述步骤:
(1)将15-25%质量浓度的氯化镁溶液和70-75%质量浓度的氧化镁按比例混合得固化剂混合液;
(2)边搅拌步骤(1)中所述混合液,边在混合液中依次按比例加入将粉碎后的坚果外壳、粘土粉、椰壳纤维、粘接剂、减水剂,全部加入后,继续搅拌至物料均匀,得到混合浆料;
(3)将步骤(2)中所得混合浆料放入模具,制坯成型,室温下放置,固化后揭开模具,得到坯体;
(4)将步骤(3)中所得坯体在温度为28-35℃,湿度为30-45%下养护3-4小时即得轻体墙板。