CN111607677A - 一种铁水鱼雷罐降铁耗的操作方法 - Google Patents
一种铁水鱼雷罐降铁耗的操作方法 Download PDFInfo
- Publication number
- CN111607677A CN111607677A CN201910134845.2A CN201910134845A CN111607677A CN 111607677 A CN111607677 A CN 111607677A CN 201910134845 A CN201910134845 A CN 201910134845A CN 111607677 A CN111607677 A CN 111607677A
- Authority
- CN
- China
- Prior art keywords
- molten iron
- steel
- scrap steel
- temperature
- iron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种铁水鱼雷罐降铁耗的操作方法,将废钢采用破碎的方式加工为破碎料,要求尺寸在100×100mm以内,同时要求破碎料堆比重>1.60t/m3,将废钢运输至铁水鱼雷罐兑铁位料仓,根据高炉铁水出铁温度计算出满足炼钢温度需求的废钢加入量,高炉铁水温度/℃1400‑1530、鱼雷罐吨位/t 420‑450、加废钢降温范围/℃5‑10、废钢加入量控制范围kg/t 7‑18,高炉兑铁前期利用旋转溜槽将废钢加入到鱼雷罐中,在鱼雷罐兑铁后期利用铁水的搅拌作用,促进鱼雷罐中废钢的熔化。本发明能够减少冶炼过程中球团、白云石等渣料的加入所产生的化学反应,降低冶炼过程中人工干预氧枪操作的频次。
Description
技术领域
本发明涉及一种铁水鱼雷罐降铁耗的操作方法。
背景技术
在现阶段钢铁企业开展降铁耗工作主要采用提高废钢料斗容积、分布加废钢等方式,一次性将废钢加入炉内进行冶炼。但是由于生产节奏等影响因素不允许二次加废钢的操作方法,废钢加入炉内的实际量成为降低铁耗的限制性环节,在铁水还存在热富裕时,基本采用渣料此类冷却剂来平衡炉内热平衡,预防炉内温度过高产生喷溅等事故。采用此类冷却剂平衡炉内热量,既造成了生产成本的增加,又会导致炉内渣量增加进而钢铁料消耗的增加。
发明内容
本发明的目的在于提供一种铁水鱼雷罐降铁耗的操作方法,能够减少冶炼过程中球团、白云石等渣料的加入所产生的化学反应,降低冶炼过程中人工干预氧枪操作的频次,更加有利于一键炼钢的可操性及稳定性。
本发明的目的是这样实现的,一种铁水鱼雷罐降铁耗的操作方法,将废钢采用破碎的方式加工为破碎料,要求尺寸在100×100mm以内,同时要求破碎料堆比重>1.60t/m3,将废钢运输至铁水鱼雷罐兑铁位料仓,根据高炉铁水出铁温度计算出满足炼钢温度需求的废钢加入量,高炉铁水温度/℃ 1400-1530、鱼雷罐吨位/t 420-450、加废钢降温范围/℃5-10、废钢加入量控制范围kg/t 7-18,高炉兑铁前期利用旋转溜槽将废钢加入到鱼雷罐中,在鱼雷罐兑铁后期利用铁水的搅拌作用,促进鱼雷罐中废钢的熔化。
每一炉高炉铁水成分及温度输入热量平衡计算模型,采用料仓加入废钢破碎料来平衡鱼雷罐内多余的热量:
Q废钢=m废钢×{C固•(t熔-t初始)+废钢的熔化潜热+C液•( t出-t熔)}
1kg废钢在达到1350℃铁水温度时的冷却效应是:Q废钢=1254.11 kJ/kg。
Q铁水=m铁水×{C固•(t熔-t初始)+铁水的熔化潜热+C液•( t出-t熔)}
1kg铁水在降低1℃时的物理热是:Q铁=447.98kJ/kg,
m铁水×Q铁水=m废钢×Q废钢
通过计算1kg铁水降低1℃所发出的热量,根据铁水鱼雷罐内热平衡确定废钢破碎料加入量,具体如表1、表2所示:
表1、鱼雷罐温度变化趋势表
项目 | 炼钢需求温度/℃ | 运输过程损失/℃ | 铁水入罐温度/℃ | 鱼雷罐配加废钢温度/℃ |
温度变化 | 1350 | 80-100 | 1430-1450 | T≥1470 |
表2、鱼雷罐加废钢平横计算表
主要改进效果:
1、采用铁水鱼雷罐降铁耗的操作方法,打破了降铁耗过程中废钢不能足量加入转炉内的限制性环节,做到了利用市场废钢资源充足的条件降低铁水消耗、提升了合格钢坯产量。
2、采用铁水鱼雷罐降铁耗的操作方法,利用鱼雷罐铁水吨位大、搅拌力充足及保温效果好等优势,确保鱼雷罐内的废钢充分熔化,通过炼钢铁水化验过程明确成分变化情况,避免了传统废钢加入模式中P、S有害元素不确定性对冶炼渣料加入量及质量控制的影响。
3、采用铁水鱼雷罐降铁耗的操作方法,减少冶炼过程中球团、白云石等渣料的加入所产生的化学反应,降低了冶炼过程中人工干预氧枪操作的频次,更加有利于一键炼钢的可操性及稳定性。
具体实施方式
一种铁水鱼雷罐降铁耗的操作方法,将废钢采用破碎的方式加工为破碎料,要求尺寸在100×100mm以内,同时要求破碎料堆比重>1.60t/m3,将废钢运输至铁水鱼雷罐兑铁位料仓,根据高炉铁水出铁温度计算出满足炼钢温度需求的废钢加入量,高炉铁水温度/℃ 1400-1530、鱼雷罐吨位/t 420-450、加废钢降温范围/℃ 5-10、废钢加入量控制范围kg/t 7-18,高炉兑铁前期利用旋转溜槽将废钢加入到鱼雷罐中,在鱼雷罐兑铁后期利用铁水的搅拌作用,促进鱼雷罐中废钢的熔化。
Claims (1)
1.一种铁水鱼雷罐降铁耗的操作方法,其特征在于:将废钢采用破碎的方式加工为破碎料,要求尺寸在100×100mm以内,同时要求破碎料堆比重>1.60t/m3,将废钢运输至铁水鱼雷罐兑铁位料仓,根据高炉铁水出铁温度计算出满足炼钢温度需求的废钢加入量,高炉铁水温度/℃ 1400-1530、鱼雷罐吨位/t 420-450、加废钢降温范围/℃ 5-10、废钢加入量控制范围kg/t 7-18,高炉兑铁前期利用旋转溜槽将废钢加入到鱼雷罐中,在鱼雷罐兑铁后期利用铁水的搅拌作用,促进鱼雷罐中废钢的熔化。