CN111410532A - 一种氧化锆陶瓷手机背板加工方法 - Google Patents

一种氧化锆陶瓷手机背板加工方法 Download PDF

Info

Publication number
CN111410532A
CN111410532A CN202010282299.XA CN202010282299A CN111410532A CN 111410532 A CN111410532 A CN 111410532A CN 202010282299 A CN202010282299 A CN 202010282299A CN 111410532 A CN111410532 A CN 111410532A
Authority
CN
China
Prior art keywords
mobile phone
pressure
cylinder body
back plate
zirconia ceramic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202010282299.XA
Other languages
English (en)
Inventor
颜井意
杜建周
高巍
艾多梅
郭心语
梁佳维
刘广巍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Dongpu Fine Ceramics Technology Co ltd
Original Assignee
Jiangsu Dongpu Fine Ceramics Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Dongpu Fine Ceramics Technology Co ltd filed Critical Jiangsu Dongpu Fine Ceramics Technology Co ltd
Priority to CN202010282299.XA priority Critical patent/CN111410532A/zh
Publication of CN111410532A publication Critical patent/CN111410532A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种氧化锆陶瓷手机背板加工方法，包括以下步骤：氧化锆粉末为90％—95％，氧化钇1％—2.6％，氧化钙0.4％—2％，氧化镁0.2％—0.9％，氧化铈1％—1.5％氧化锌1.5％—3.7％，其余为添加剂，球磨混合、真空干燥、研磨过筛，冷等静压，将装有粉末混料的密封弹性模具，置于盛有传压介质的缸体中，然后闭合上端塞，框架沿导轨底座滑行至缸体正上方，将上端塞压住。接着，加压设备通过缸体底部的高压油路，对缸体内部传压介质施加超高压力，此时模具内的物料受压成型。烧结,抛光打磨。本发明所述的氧化锆陶瓷手机背板，采用冷等静压工艺工艺，添加多种多种稳定剂、着色剂，有吸睛的金属光泽与玉石质感的同时，增强了氧化锆材料的韧性，改善了氧化锆陶瓷脆性大的缺陷。

Description

一种氧化锆陶瓷手机背板加工方法
技术领域
本发明属于手机背板加工领域，具体涉及一种氧化锆陶瓷手机背板加工方法。
背景技术
现代科技的飞速发展对物件的外观兼性能提出了新的更高的要求，材料设计的理念也从发展单一材料性能指标变为开发具备多种功能复合的材料体系。在众多材料设计的案例中，氧化锆陶瓷(Zirconia ceramics)材料就是一类典型代表。氧化锆陶瓷材料是一大类非常重要的先进功能材料，因其原料成本相对较低、无辐射、光泽独特、坚固耐磨、不屏蔽信号、散热性好、有良好的生物相容性，是与金属及玻璃相比更胜一筹的手机背板材料。但是由于氧化锆陶瓷本身脆性大，断裂韧性小的缺陷，其应用前景受到了一定的限制。氧化锆材料的增韧增强已成为国际上一个新的研究领域和研究热点。
中国发明专利CN106625034B公开的一种氧化锆陶瓷板的加工方法，为了生产适用于大尺寸手机后盖的陶瓷板，利用多线切割机将氧化锆陶瓷块切割，利用倒角砂轮将平板状氧化锆陶瓷边缘加工成2.5D形状，最后采用金刚石砂轮在自制单抛机上进行抛光。这种加工方式，需要采用线切割机、研磨机、砂轮机等设备，工作环境恶劣，易产生废粉、火光，且加工精度难以保证。
发明内容
针对现有技术所存在的上述不足，本发明的目的是提供一种氧化锆陶瓷手机背板加工方法，采用冷等静压，低温烧结工艺制备。对环境温度没有特殊的要求，提高氧化锆陶瓷手机背板的加工精度和一致性，保证了制备工艺的便捷可行性。
为了实现上述目的，本发明提供一种氧化锆陶瓷手机背板加工方法，包括以下步骤：
一种氧化锆陶瓷手机背板加工方法，包括以下步骤：
配料:
称取各组分质量百分比如下：
氧化锆粉末为90％—95％，
氧化钇1％—2.6％，
氧化钙0.4％—2％，
氧化镁0.2％—0.9％，
氧化铈1％—1.5％
氧化锌1.5％—3.7％，
其余为添加剂，
球磨混合、真空干燥、研磨过筛，
按照球料比称取适量的大小球磨球与一定量的去离子水放入球磨罐中；最后放入按配方表配比完成的待混合物，搅拌均匀，添加去离子水控制变量；放入球磨机中球磨12小时；然后取出，将装满混料的瓷盘放入真空干燥箱中，将干燥箱抽真空后加热干燥，将腔体抽至一定真空即可，干燥温度为80℃，约12小时，混料呈龟裂状即完全干燥；取出放入研钵研磨过100目筛；
冷等静压，
将混合均匀的氧化锆陶瓷粉末放入专用手机背板模具后，采用小型等静压机压制成型得到手机背板胚体；首先将装有粉末混料的密封弹性模具，置于盛有传压介质的缸体中，然后闭合上端塞，框架沿导轨底座滑行至缸体正上方，将上端塞压住。接着，加压设备通过缸体底部的高压油路，对缸体内部传压介质施加超高压力，此时模具内的物料受压成型。经一段时间保压后，减压阀开启，缸体内压力逐渐回复至常压，框架后移，上端塞开启，最后取出成型样品；
烧结,
压制完成后将成型的胚体陶瓷背板放入箱式节能烧结炉中，通过烧结得到手机陶瓷背板粗制样板；烧结程序设置十六个半小时缓慢升温至最高温1490℃，650℃排胶，保温烧结3h，6h缓慢降温至700℃，最后自然降温至室温可取出样品；
抛光打磨，
将烧制成功的手机背板放上拖拽式精密碾磨抛光机进行抛光打磨，得到质感光滑、颜色光亮的成品背板。
进一步地，所述添加剂，包括2％—5％的粘结剂、1％—2％的分散剂，粘结剂为PVA，分散剂为三乙醇胺。
进一步地，过筛时放入振动过筛机，得到混合均匀的氧化铝混合陶瓷粉末。
本发明的工作原理：
采用的特殊冷等静压工艺是本专利的创新独特之处，首先与温等静压，热等静压工艺相比，没有对环境温度的特殊要求，进一步降低了制备成本更加易为操作实现；其次与常规成型技术相比，等静压成型的制品密度高，压坯的密度均匀一致，不会出现压坯密度分布不均现象，使压制出的样品更具有一致性，有利于大规模批量化生产。
配料配方中采用多种稳定剂氧化钇、氧化钙、氧化镁，最佳混合比例提高了氧化锆粉末的稳定性，间接的改善了氧化锆陶瓷脆性大的缺陷；氧化锌作为白色的着色剂，解决了对氧化锆基陶瓷手机背板的外观美感需求与使用性能要求，在保证了手机背板拥有吸睛的金属光泽与玉石质感的同时，增强了氧化锆材料的韧性，让氧化锆基手机背板的设想更具可行性。
本发明的有益效果：
本发明所述的氧化锆陶瓷手机背板，从微观和宏观上设计氧化锆陶瓷手机背板，结合陶瓷体系“组分-工艺-性能”之间的关系，进行创新性配比设计，采用专用模具按照，可制备拥有金属光泽和亮度，玉石的质感和均匀度，颜色艳丽多变，过渡自然且同时兼备高稳定性，高断裂韧性，加工精度高等优异性能的氧化锆陶瓷基手机背板，采用的特殊工艺冷等静压压制，与常规成型技术相比等静压成型的制品密度高，压坯的密度均匀一致，不会出现压坯密度分布不均现象。
附图说明
图1为本发明所述的氧化锆陶瓷手机背板加工方法的流程示意图。
具体实施方式
下面结合附图和具体实施例详细描述一下本发明的具体内容。
如图1所示，一种氧化锆陶瓷手机背板加工方法，包括以下步骤：
A1.配料:
称取各组分质量百分比如下：
氧化锆粉末为90％—95％，
氧化钇1％—2.6％，
氧化钙0.4％—2％，
氧化镁0.2％—0.9％，
氧化铈1％—1.5％
氧化锌1.5％—3.7％，
其余为添加剂，
A2.球磨混合、真空干燥、研磨过筛，
按照球料比称取适量的大小球磨球与一定量的去离子水放入球磨罐中；最后放入按配方表配比完成的待混合物，搅拌均匀，添加去离子水控制变量；放入球磨机中球磨12小时；然后取出，将装满混料的瓷盘放入真空干燥箱中，将干燥箱抽真空后加热干燥，将腔体抽至一定真空即可，干燥温度为80℃，约12小时，混料呈龟裂状即完全干燥；取出放入研钵研磨过100目筛；
A3.冷等静压，
将混合均匀的氧化锆陶瓷粉末放入专用手机背板模具后，采用小型等静压机压制成型得到手机背板胚体；首先将装有粉末混料的密封弹性模具，置于盛有传压介质的缸体中，然后闭合上端塞，框架沿导轨底座滑行至缸体正上方，将上端塞压住。接着，加压设备通过缸体底部的高压油路，对缸体内部传压介质施加超高压力，此时模具内的物料受压成型。经一段时间保压后，减压阀开启，缸体内压力逐渐回复至常压，框架后移，上端塞开启，最后取出成型样品；
A4.烧结,
压制完成后将成型的胚体陶瓷背板放入箱式节能烧结炉中，通过烧结得到手机陶瓷背板粗制样板；烧结程序设置十六个半小时缓慢升温至最高温1490℃，650℃排胶，保温烧结3h，6h缓慢降温至700℃，最后自然降温至室温可取出样品；
A5.抛光打磨，
将烧制成功的手机背板放上拖拽式精密碾磨抛光机进行抛光打磨，得到质感光滑、颜色光亮的成品背板。
在实际应用中，所述添加剂，包括2％—5％的粘结剂、1％—2％的分散剂，粘结剂为PVA，分散剂为三乙醇胺。
在实际应用中，过筛时放入振动过筛机，得到混合均匀的氧化铝混合陶瓷粉末。
综上所述：：本发明可制备颜色多变，各种型号的3D陶瓷手机背板，加工方式便捷简易，制备成本合理适中，细节处理精细得当，产出的样品兼备外观美感与优异性能，大大提升了氧化锆陶瓷基手机背板的市场价值与应用前景。
以上叙述了本发明的基本原理、主要特征及优点。本行业的技术人员应该了解，上述实施方式只为说明本发明的技术构思及特点，其目的在于让熟悉此项技术的人士能够了解本发明的内容并加以实施，并不能以此限制本发明的保护范围，凡根据本发明精神实质所作的等效变化或修饰，都应涵盖在本发明的保护范围内。

Claims (3)

1.一种氧化锆陶瓷手机背板加工方法，其特征在于：包括以下步骤：
A1.配料:
称取各组分质量百分比如下：
氧化锆粉末为90％—95％，
氧化钇1％—2.6％，
氧化钙0.4％—2％，
氧化镁0.2％—0.9％，
氧化铈1％—1.5％
氧化锌1.5％—3.7％，
其余为添加剂，
A2.球磨混合、真空干燥、研磨过筛，
按照球料比称取适量的大小球磨球与一定量的去离子水放入球磨罐中；最后放入按配方表配比完成的待混合物，搅拌均匀，添加去离子水控制变量；放入球磨机中球磨12小时；然后取出，将装满混料的瓷盘放入真空干燥箱中，将干燥箱抽真空后加热干燥，将腔体抽至一定真空即可，干燥温度为80℃，约12小时，混料呈龟裂状即完全干燥；取出放入研钵研磨过100目筛；
A3.冷等静压，
将混合均匀的氧化锆陶瓷粉末放入专用手机背板模具后，采用小型等静压机压制成型得到手机背板胚体；首先将装有粉末混料的密封弹性模具，置于盛有传压介质的缸体中，然后闭合上端塞，框架沿导轨底座滑行至缸体正上方，将上端塞压住；接着，加压设备通过缸体底部的高压油路，对缸体内部传压介质施加超高压力，此时模具内的物料受压成型；经一段时间保压后，减压阀开启，缸体内压力逐渐回复至常压，框架后移，上端塞开启，最后取出成型样品；
A4.烧结，
压制完成后将成型的胚体陶瓷背板放入箱式节能烧结炉中，通过烧结得到手机陶瓷背板粗制样板；烧结程序设置十六个半小时缓慢升温至最高温1490℃，650℃排胶，保温烧结3h，6h缓慢降温至700℃，最后自然降温至室温可取出样品；
A5.抛光打磨，
将烧制成功的手机背板放上拖拽式精密碾磨抛光机进行抛光打磨，得到质感光滑、颜色光亮的成品背板。
2.根据权利要求1所述的一种氧化锆陶瓷手机背板加工方法，其特征在于：所述添加剂，包括2％—5％的粘结剂、1％—2％的分散剂，粘结剂为PVA，分散剂为三乙醇胺。
3.根据权利要求1或2所述的一种氧化锆陶瓷手机背板加工方法，其特征在于：过筛时放入振动过筛机，得到混合均匀的氧化铝混合陶瓷粉末。
CN202010282299.XA 2020-04-11 2020-04-11 一种氧化锆陶瓷手机背板加工方法 Pending CN111410532A (zh)