CN111152534A - 具有减缓氧化抗紫外线保鲜功能的泡罩包装片材、包装容器及食用油产品 - Google Patents
具有减缓氧化抗紫外线保鲜功能的泡罩包装片材、包装容器及食用油产品 Download PDFInfo
- Publication number
- CN111152534A CN111152534A CN202010043818.7A CN202010043818A CN111152534A CN 111152534 A CN111152534 A CN 111152534A CN 202010043818 A CN202010043818 A CN 202010043818A CN 111152534 A CN111152534 A CN 111152534A
- Authority
- CN
- China
- Prior art keywords
- layer
- packaging sheet
- blister packaging
- edible oil
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种具有减缓氧化抗紫外线保鲜功能的泡罩包装片材，其包括设于内层的热封层、设于外层的印刷层、以及设于热封层和印刷层之间的阻隔层和抗紫外线成型层。此外，本发明还公开了一种包装容器，其采用上述的泡罩包装片材制得。另外，本发明还公开了一种食用油产品，其被密封包装于上述的包装容器内。所述的泡罩包装片材轻巧方便、可以制得的容量灵活，且由于所述的泡罩包装片材具有高阻隔性能，因而可以使得采用所述的泡罩包装片材包装的食用油储存时不会出现过氧化值快速增高进而导致食用油品质下降的问题。
Description
技术领域
本发明涉及一种包装材料、包装容器以及产品，尤其涉及一种高阻隔性且可以阻隔紫外线的包装材料、包装容器以及产品。
背景技术
食用油在当今生活中已不可或缺，多种类型的食用油满足着人们对营养的需求，例如:橄榄油可用于拌沙拉用，其富含多种维生素，具有抗癌，抗衰老功效，而亚麻籽油可以与酸奶混合食用，亚麻籽油含丰富的α－亚麻酸，具有降低胆固醇，美容护肤的功效，以上两种食用油可以每次约10毫升用量。
但需要指出的是，目前，直接食用的食用油的包装形式以PET瓶或玻璃瓶包装为主。并且，上述包装的售卖容量通常为500毫升以上，这使得采用玻璃瓶包装的食用油极难随身携带，而PET则在瓶体容量小的情况下吹瓶工艺极其困难。
基于此，期望获得一种包装片材，其可以质量轻以便于携带使用，且容量灵活，制造工艺简单，尤其是该包装片材非常适合用于携带食用油。
发明内容
本发明的目的之一在于提供一种具有减缓氧化抗紫外线保鲜功能的泡罩包装片材，该泡罩包装片材轻巧方便、可以制得的容量灵活，且由于该泡罩包装片材具有高阻隔性能，因而可以使得采用该泡罩包装片材包装的食用油储存时不会出现过氧化值快速增高进而导致食用油品质下降的问题。
为了实现上述目的，本发明提出了一种具有减缓氧化抗紫外线保鲜功能的泡罩包装片材，其包括设于内层的热封层、设于外层的印刷层、以及设于热封层和印刷层之间的阻隔层和抗紫外线成型层。
在本发明所述的技术方案中，考虑到食用油中含有大量不饱和脂肪酸，而氧气对于食用油的品质影响巨大，因此，本案发明人设置了阻隔层，以使得本案的泡罩包装片材具有高阻隔性，可以高强度的阻氧以及阻湿，有效阻隔气体的渗透，保留食用油的香味，减缓食用油的氧化变质，从而保证食用油的品质，并且避免食用油变质。
考虑到紫外线也会加速食用油的氧化速率，因此，在本发明所述的技术方案中，设置了抗紫外线成型层，以使得本案的泡罩包装片材具有良好的韧性以及抗冲击性，以便于泡罩包装片材吹塑成型，同时抗紫外线成型层提供了优异的力学强度，可有效抵抗紫外线(UV)，减缓食用油氧化反应速率。
此外，本发明所述的泡罩包装片材所采用的印刷层可以采用光泽度以及透明度较好的材料，一方面可以直观展示食用油的色泽，另一方面也可以起到阻湿效果，且印刷层可以具有优良的耐热性以及印刷性，以使得泡罩包装片材可以在加热吹塑成型过程中印刷效果稳定。
另外，本案中的热封层起到极好密封效果，进而保证了食用油的品质。
进一步地，在本发明所述的泡罩包装片材中，其中阻隔层临近热封层设置，并且抗紫外线成型层临近印刷层设置。
进一步地，在本发明所述的泡罩包装片材中，热封层、阻隔层、抗紫外线成型层和印刷层中相邻的两层之间设有粘结层。
进一步地，在本发明所述的泡罩包装片材中，粘结层为湿法粘结层和/或干法粘结层。
上述方案中，湿法粘结层和/或干法粘结层均可以采用现有技术获得，具体来说，湿法粘结层可以将单组份或双组份无溶剂型聚氨酯胶黏剂加到基材上，然后立即与第二层材料复合在一起，从而制得层合材料。而干法粘结层则是可以将含溶剂型胶黏剂涂布于基材上，经烘干蒸发掉溶剂，再与另一基材贴合在一起，经冷却、熟化后制得层合材料。
进一步地，在本发明所述的泡罩包装片材中，热封层包括：聚乙烯薄膜和改性聚丙烯薄膜的至少其中之一。
进一步地，在本发明所述的泡罩包装片材中，热封层的厚度为10-40μm。
进一步地，在本发明所述的泡罩包装片材，印刷层包括：流延聚丙烯薄膜、聚对苯二甲酸乙二醇酯薄膜或改性聚丙烯薄膜的至少其中之一。
进一步地，在本发明所述的泡罩包装片材中，印刷层的厚度为30-80μm。
进一步地，在本发明所述的泡罩包装片材中，阻隔层被构造为：使氧气透过量小于0.8cm3/(m2·24h·0.1MPa)。
进一步地，在本发明所述的泡罩包装片材中，抗紫外线成型层被构造为：在波长为200-400nm的光照下，光透射比小于10％。
进一步地，在本发明所述的泡罩包装片材中，阻隔层为采用多层共挤工艺制得的阻隔层。
进一步地，在本发明所述的泡罩包装片材中，阻隔层为至少采用聚乙烯层与乙烯-乙烯醇共聚物层进行多层共挤工艺制得的阻隔层。
进一步地，在本发明所述的泡罩包装片材中，其中乙烯-乙烯醇共聚物层的总厚度为5-30μm；并且/或者聚乙烯层的总厚度为10-40μm。
进一步地，在本发明所述的泡罩包装片材中，其中抗紫外线成型层至少包括含有抗紫外线功能的非结晶化聚对苯二甲酸乙二醇酯母粒。
进一步地，在本发明所述的泡罩包装片材中，其中含有抗紫外线功能的非结晶化聚对苯二甲酸乙二醇酯母粒占抗紫外线成型层的质量百分含量为2％-8％。
进一步地，在本发明所述的泡罩包装片材中，抗紫外线成型层的厚度为150-300μm。
此外，本发明的另一目的在于提供一种包装容器，该容器具有较好的包装密封性，采用该包装容器储存食用油轻便易携带，且有利于延长食用油的保质期。
为了实现上述目的，本发明提出了一种包装容器，其采用上述的泡罩包装片材制得。
另外，本发明的又一目的在于提供一种食用油产品，该食用油产品品质佳，保质期久，易于携带使用。
为了实现上述目的，本发明提出了一种食用油产品，其被密封包装于上述的包装容器内。
本发明所述的具有减缓氧化抗紫外线保鲜功能的泡罩包装片材、包装容器及食用油产品相较于现有技术具有如下所述的优点以及有益效果：
本发明所述的泡罩包装片材轻巧方便、可以制得的容量灵活，且由于所述的泡罩包装片材具有高阻隔性能，因而可以使得采用所述的泡罩包装片材包装的食用油储存时不会出现过氧化值快速增高进而导致食用油品质下降的问题。
此外，本发明所述的包装容器也同样具有上述的优点以及有益效果。
另外，本发明所述的食用油产品也同样具有上述的优点以及有益效果。
附图说明
图1示意性地显示了本发明所述的具有减缓氧化抗紫外线保鲜功能的泡罩包装片材在一些实施方式中的断面结构。
图2示意性地显示了本发明所述的具有减缓氧化抗紫外线保鲜功能的泡罩包装片材在另一些实施方式中的断面结构。
图3示意性显示了采用不同的包装储存橄榄油期间过氧化值的变化。
具体实施方式
下面将结合说明书附图和具体的实施例对本发明所述的具有高阻隔紫外线功能的泡罩包装片材、包装容器及食用油产品做进一步的解释和说明，然而该解释和说明并不对本发明的技术方案构成不当限定。
图1示意性地显示了本发明所述的具有减缓氧化抗紫外线保鲜功能的泡罩包装片材在一些实施方式中的断面结构。
如图1所示，在本实施方式中的具有高阻隔抗紫外功能的泡罩包装片材包括印刷层1、抗紫外线成型层2、阻隔层3、热封层4以及干法粘结层51。其中，热封层4设于泡罩包装片材的内层，印刷层1设于泡罩包装片材的外层，而阻隔层3以及抗紫外线成型层2设于热封层4以及印刷层1之间，并且在本实施方式中，阻隔层3临近热封层4设置，而抗紫外线成型层2临近印刷层1设置。
在本实施方式中，印刷层可以采用流延聚丙烯(CPP)薄膜、聚对苯二甲酸乙二醇酯(PET)薄膜或改性聚丙烯(PP)薄膜的至少其中之一，上述材料光泽度、透明度好，可以直观展示食用油色泽，又可起到阻湿效果，并且其优良的耐热性及印刷性，使泡罩包装片材在加热吹塑成型过程中印刷效果稳定。印刷层1的厚度可以为30-80μm。
抗紫外线成型层2被构造为：在波长为200-400nm的光照下，光透射比小于10％，并且，在本实施方式中的抗紫外线成型层2至少包括含有抗紫外线功能的非结晶化聚对苯二甲酸乙二醇酯母粒(APET)，其中含有抗紫外线功能的非结晶化聚对苯二甲酸乙二醇酯母粒占抗紫外线成型层的质量百分含量为2％-8％。抗紫外成型层的厚度可以设置为150-300μm。抗紫外线成型层2可以为热塑型环保片材，上述材料具有良好的韧性及抗冲击性，以便于泡罩包装片材吹塑成型，同时上述材料提供了优异的力学强度，并且抗紫外线(UV)功能可有效抵抗紫外线，减缓食用油氧化反应速率。
阻隔层3被构造为：使氧气透过量小于0.8cm3/(m2·24h·0.1MPa)，阻隔层3可以通过采用聚乙烯(PE)层与乙烯-乙烯醇共聚物(EVOH)层进行多层共挤工艺制得，上述材料氧气透过率低，可有效阻隔气体的渗透，保留食用油香味，减缓食用油氧化变质。在本实施方式中，乙烯-乙烯醇共聚物层的总厚度可以为5-30μm；并且/或者聚乙烯层的总厚度为10-40μm。
热封层4包括聚乙烯薄膜和改性聚丙烯薄膜的至少其中之一，上述材料具有优良的热封性，可以使得泡罩包装片材具有优异的密封性能，起到保质效果。热封层4的厚度可以为10-40μm。
在本实施方式中，在热封层4、阻隔层3、抗紫外线成型层2和印刷层1中相邻的两层之间设有干法粘结层51，其采用含溶剂型胶黏剂涂布于需要粘结的层上，经烘干蒸发掉溶剂，再与另外一层的材料贴合在一起，经冷却、熟化后制得最终泡罩包装片材。
图2示意性地显示了本发明所述的具有减缓氧化抗紫外线保鲜功能的泡罩包装片材在另一些实施方式中的断面结构。
如图2所示，在本实施方式中的具有高阻隔抗紫外功能的泡罩包装片材包括印刷层1、抗紫外线成型层2、阻隔层3、热封层4以及湿法粘结层52。其中，热封层4设于泡罩包装片材的内层，印刷层1设于泡罩包装片材的外层，而阻隔层3以及抗紫外线成型层2设于热封层4以及印刷层1之间，并且在本实施方式中，阻隔层3临近热封层4设置，而抗紫外线成型层2临近印刷层1设置。
在本实施方式中，印刷层可以采用流延聚丙烯(CPP)薄膜、聚对苯二甲酸乙二醇酯(PET)薄膜或改性聚丙烯(PP)薄膜的至少其中之一，上述材料光泽度、透明度好，可以直观展示食用油色泽，又可起到阻湿效果，并且其优良的耐热性及印刷性，使泡罩包装片材在加热吹塑成型过程中印刷效果稳定。印刷层1的厚度可以为30-80μm。
抗紫外线成型层2被构造为：在波长为200-400nm的光照下，光透射比小于10％，并且，在本实施方式中的抗紫外线成型层2至少包括含有抗紫外线功能的非结晶化聚对苯二甲酸乙二醇酯母粒(APET)，其中含有抗紫外线功能的非结晶化聚对苯二甲酸乙二醇酯母粒占抗紫外线成型层的质量百分含量为2％-8％。抗紫外成型层的厚度可以设置为150-300μm。抗紫外线成型层2可以为热塑型环保片材，上述材料具有良好的韧性及抗冲击性，以便于泡罩包装片材吹塑成型，同时上述材料提供了优异的力学强度，并且抗紫外线(UV)功能可有效抵抗紫外线，减缓食用油氧化反应速率。
阻隔层3被构造为：使氧气透过量小于0.8cm3/(m2·24h·0.1MPa)，阻隔层3可以通过采用聚乙烯(PE)层与乙烯-乙烯醇共聚物(EVOH)层进行多层共挤工艺制得，上述材料氧气透过率低，可有效阻隔气体的渗透，保留食用油香味，减缓食用油氧化变质。在本实施方式中，乙烯-乙烯醇共聚物层的总厚度可以为5-30μm；并且/或者聚乙烯层的总厚度为10-40μm。
热封层4包括聚乙烯薄膜和改性聚丙烯薄膜的至少其中之一，上述材料具有优良的热封性，可以使得泡罩包装片材具有优异的密封性能，起到保质效果。热封层4的厚度可以为10-40μm。
在本实施方式中，在热封层4、阻隔层3、抗紫外线成型层2和印刷层1中相邻的两层之间设有湿法粘结层52，湿法粘结层52可将单组份或双组份无溶剂型聚氨酯胶黏剂加到需要粘结的层材料上，然后立即与另一层的材料复合在一起，从而制得最终的泡罩包装片材。
下文表1列出了实施例1-6的泡罩包装片材所采用的具体参数以及效果。
表1.
图3示意性显示了采用不同的包装材料盛装和储存橄榄油，橄榄油的过氧化值的变化。
如图3所示，曲线I表示食用油产品采用PET瓶作为包装材料进行测试的情况，曲线II表示食用油产品采用玻璃瓶作为包装材料进行测试的情况，曲线III表示食用油产品采用本案的泡罩包装片材作为包装材料进行测试的情况。测试条件为：在温度为45℃条件下储存，食用油为橄榄油。
由图3可以看出，随着储藏时间的增加，玻璃瓶装的橄榄油过氧化值无明显变化，而本案所述的泡罩包装片材作为包装材料存储的橄榄油过氧化值变化量为1.22mmol/kg，经过45℃加速储藏60天后，其过氧化值低于6mmol/kg，远低于国家标准GB23347《橄榄油、油橄榄果渣油》中特级初榨橄榄油的上限值10mmol/kg，而采用PET瓶作为包装材料的橄榄油，其过氧化值不断增大，在第14周后超过上限值10mmol/kg。
综上所述可以看出，本发明所述的泡罩包装片材轻巧方便、可以制得的容量灵活，且由于所述的泡罩包装片材具有高阻隔性能，因而可以使得采用所述的泡罩包装片材包装的食用油储存时不会出现过氧化值快速增高进而导致食用油品质下降的问题。
此外，本发明所述的包装容器也同样具有上述的优点以及有益效果。
另外，本发明所述的食用油产品也同样具有上述的优点以及有益效果。
需要说明的是，本发明的保护范围中现有技术部分并不局限于本申请文件所给出的实施例，所有不与本发明的方案相矛盾的现有技术，包括但不局限于在先专利文献、在先公开出版物，在先公开使用等等，都可纳入本发明的保护范围。
此外，本案中各技术特征的组合方式并不限本案权利要求中所记载的组合方式或是具体实施例所记载的组合方式，本案记载的所有技术特征可以以任何方式进行自由组合或结合，除非相互之间产生矛盾。
还需要注意的是，以上所列举的实施例仅为本发明的具体实施例。显然本发明不局限于以上实施例，随之做出的类似变化或变形是本领域技术人员能从本发明公开的内容直接得出或者很容易便联想到的，均应属于本发明的保护范围。
Claims (18)
1.一种具有减缓氧化抗紫外线保鲜功能的泡罩包装片材，其特征在于，其包括设于内层的热封层、设于外层的印刷层、以及设于热封层和印刷层之间的阻隔层和抗紫外线成型层。
2.如权利要求1所述的泡罩包装片材，其特征在于，其中所述阻隔层临近热封层设置，并且所述抗紫外线成型层临近印刷层设置。
3.如权利要求1所述的泡罩包装片材，其特征在于，所述热封层、阻隔层、抗紫外线成型层和印刷层中相邻的两层之间设有粘结层。
4.如权利要求3所述的泡罩包装片材，其特征在于，所述粘结层为湿法粘结层和/或干法粘结层。
5.如权利要求1所述的泡罩包装片材，其特征在于，所述热封层包括：聚乙烯薄膜和改性聚丙烯薄膜的至少其中之一。
6.如权利要求1所述的泡罩包装片材，其特征在于，所述热封层的厚度为10-40μm。
7.如权利要求1所述的泡罩包装片材，其特征在于，所述印刷层包括：流延聚丙烯薄膜、聚对苯二甲酸乙二醇酯薄膜或改性聚丙烯薄膜的至少其中之一。
8.如权利要求1所述的泡罩包装片材，其特征在于，所述印刷层的厚度为30-80μm。
9.如权利要求1所述的泡罩包装片材，其特征在于，所述阻隔层被构造为：使氧气透过量小于0.8cm3/(m2·24h·0.1MPa)。
10.如权利要求1所述的泡罩包装片材，其特征在于，所述抗紫外线成型层被构造为：在波长为200-400nm的光照下，光透射比小于10％。
11.如权利要求1-10中任意一项所述的泡罩包装片材，其特征在于，所述阻隔层为采用多层共挤工艺制得的阻隔层。
12.如权利要求11所述的泡罩包装片材，其特征在于，所述阻隔层为至少采用聚乙烯层与乙烯-乙烯醇共聚物层进行多层共挤工艺制得的阻隔层。
13.如权利要求12所述的泡罩包装片材，其特征在于，其中所述乙烯-乙烯醇共聚物层的总厚度为5-30μm；并且/或者所述聚乙烯层的总厚度为10-40μm。
14.如权利要求1-10，12-13中任意一项所述的泡罩包装片材，其特征在于，其中所述抗紫外线成型层至少包括含有抗紫外线功能的非结晶化聚对苯二甲酸乙二醇酯母粒。
15.如权利要求14所述的泡罩包装片材，其特征在于，其中含有抗紫外线功能的非结晶化聚对苯二甲酸乙二醇酯母粒占抗紫外线成型层的质量百分含量为2％-8％。
16.如权利要求14所述的泡罩包装片材，其特征在于，所述抗紫外线成型层的厚度为150-300μm。
17.一种包装容器，其采用如权利要求1-16中任意一项所述的泡罩包装片材制得。
18.一种食用油产品，其被密封包装于如权利要求17所述的包装容器内。