CN111021069A - Preparation method of jute fiber antibacterial blended fabric - Google Patents
Preparation method of jute fiber antibacterial blended fabric Download PDFInfo
- Publication number
- CN111021069A CN111021069A CN201811175645.3A CN201811175645A CN111021069A CN 111021069 A CN111021069 A CN 111021069A CN 201811175645 A CN201811175645 A CN 201811175645A CN 111021069 A CN111021069 A CN 111021069A
- Authority
- CN
- China
- Prior art keywords
- fabric
- fibers
- layer
- jute
- cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention particularly relates to a preparation method of a jute fiber antibacterial blended fabric, which comprises the following steps: manufacturing a surface layer: the surface layer is made of jute fiber antibacterial fabric, the jute fiber antibacterial fabric is formed by interweaving warps and wefts, the warps are blended yarns of jute fibers and cotton fibers, and the wefts are blended yarns of wool fibers and cotton fibers; manufacturing the intermediate layer: the first fabric layer and the third fabric layer are formed by blending wool fibers and cotton fibers, then blending the wool fibers and the cotton fibers, and weaving the wool fibers and the jute fibers into cloth, the second fabric layer is made of cotton fiber yarns, and the first fabric layer, the second fabric layer and the third fabric layer are attached together in sequence in a dispensing or needle sewing mode; manufacturing an inner layer; and (6) attaching the components into a whole. According to the preparation method of the jute fiber antibacterial blended fabric, the prepared fabric has a good jute fiber antibacterial function, and the preparation process is simple and easy to operate.
Description
Technical Field
The invention belongs to the technical field of fabrics, and particularly relates to a preparation method of a jute fiber antibacterial blended fabric.
Background
With the increasing awareness of environmental protection and health care, more and more people are paying attention to natural fibers, and cotton fibers are widely applied to the production of various textiles as the most common natural fibers. At present, yarns on the market come out endlessly, are different in material structure, and are widely applied to the living fields of weaving, rope making, thread making and the like. Xinjiang cotton fiber is well known in the textile industry due to its softness and length, is known as a continuous medium-grade product by people, and has the advantages of less frequent combing, uniform and smooth evenness and high dyeability. However, the elasticity and the heat retention of the cotton fiber blended yarn on the market at present are not good, so that the woven fabric has the defects of poor heat retention effect and poor elasticity.
Preventing bacteria from harming human body is being paid more and more attention by consumers. Jute fiber is a protective fiber for protecting human body from bacteria.
In view of the above, it is needed to develop a method for preparing jute fiber antibacterial blended fabric.
Disclosure of Invention
The invention aims to provide a preparation method of a jute fiber antibacterial blended fabric, which comprises the following steps:
a, manufacturing a surface layer: the surface layer is made of jute fiber antibacterial fabric, the jute fiber antibacterial fabric is formed by interweaving warps and wefts, the warps are blended yarns of jute fibers and cotton fibers, and the wefts are blended yarns of wool fibers and cotton fibers;
b, manufacturing an intermediate layer: the first fabric layer and the third fabric layer are formed by blending wool fibers and cotton fibers, then blending the wool fibers and the cotton fibers, and weaving the wool fibers and the jute fibers into cloth, the second fabric layer is made of cotton fiber yarns, and the first fabric layer, the second fabric layer and the third fabric layer are attached together in sequence in a dispensing or needle sewing mode;
c, manufacturing of the inner layer: firstly, uniformly mixing jute fibers, wool fibers and cotton fibers, then carrying out cotton cleaning, cotton carding, drawing, roving, fine sand, automatic spooling, yarn steaming, high-speed doubling and double twisting treatment to obtain fine imitation yarns, and then weaving to obtain lining fabric;
d, integrating lamination: and sequentially laminating the surface layer, the middle layer and the inner layer, and then curing, shaping and calendaring to obtain the product.
Preferably, the time for the cooking and processing in the step d is 10-20h, the temperature is 20-50 ℃, and the humidity is 40-60%.
Preferably, in the step d, the calendering temperature is 60-100 ℃, and the pressure is 50-100Kg/cm2The speed is 15-30 m/min. .
Due to the adoption of the technical scheme, the invention has the following advantages and beneficial effects:
according to the preparation method of the jute fiber antibacterial blended fabric, the prepared fabric has a good jute fiber antibacterial function, and the preparation process is simple and easy to operate.
Detailed Description
In order to more clearly illustrate the invention, the invention is further described below in connection with preferred embodiments. It is to be understood by persons skilled in the art that the following detailed description is illustrative and not restrictive, and is not to be taken as limiting the scope of the invention.
Example 1
A preparation method of a jute fiber antibacterial blended fabric comprises the following steps:
a, manufacturing a surface layer: the surface layer is made of jute fiber antibacterial fabric, the jute fiber antibacterial fabric is formed by interweaving warps and wefts, the warps are blended yarns of jute fibers and cotton fibers, and the wefts are blended yarns of wool fibers and cotton fibers;
b, manufacturing an intermediate layer: the first fabric layer and the third fabric layer are formed by blending wool fibers and cotton fibers, then blending the wool fibers and the cotton fibers, and weaving the wool fibers and the jute fibers into cloth, the second fabric layer is made of cotton fiber yarns, and the first fabric layer, the second fabric layer and the third fabric layer are attached together in sequence in a dispensing or needle sewing mode;
c, manufacturing of the inner layer: firstly, uniformly mixing jute fibers, wool fibers and cotton fibers, then carrying out cotton cleaning, cotton carding, drawing, roving, fine sand, automatic spooling, yarn steaming, high-speed doubling and double twisting treatment to obtain fine imitation yarns, and then weaving to obtain lining fabric;
d, integrating lamination: and sequentially laminating the surface layer, the middle layer and the inner layer, and then curing, shaping and calendaring to obtain the product.
The curing and processing time in the step d is 10 hours, the temperature is 20 ℃, the humidity is 40 percent, the calendering and processing temperature in the step d is 60 ℃, and the pressure is 50Kg/cm2The speed was 15 m/min.
Example 2
A preparation method of a jute fiber antibacterial blended fabric comprises the following steps:
a, manufacturing a surface layer: the surface layer is made of jute fiber antibacterial fabric, the jute fiber antibacterial fabric is formed by interweaving warps and wefts, the warps are blended yarns of jute fibers and cotton fibers, and the wefts are blended yarns of wool fibers and cotton fibers;
b, manufacturing an intermediate layer: the first fabric layer and the third fabric layer are formed by blending wool fibers and cotton fibers, then blending the wool fibers and the cotton fibers, and weaving the wool fibers and the jute fibers into cloth, the second fabric layer is made of cotton fiber yarns, and the first fabric layer, the second fabric layer and the third fabric layer are attached together in sequence in a dispensing or needle sewing mode;
c, manufacturing of the inner layer: firstly, uniformly mixing jute fibers, wool fibers and cotton fibers, then carrying out cotton cleaning, cotton carding, drawing, roving, fine sand, automatic spooling, yarn steaming, high-speed doubling and double twisting treatment to obtain fine imitation yarns, and then weaving to obtain lining fabric;
d, integrating lamination: and sequentially laminating the surface layer, the middle layer and the inner layer, and then curing, shaping and calendaring to obtain the product.
The time for curing and processing in the step d is 20 hours, the temperature is 50 ℃, and the humidity is 60%. In the step d, the calendering temperature is 100 ℃ and the pressure is 100Kg/cm2The speed was 30 m/min.
After detection, the indexes of the jute fiber antibacterial spun yarns prepared in the two examples are shown in the following table
Breaking Strength N (warp direction) | Breaking Strength N (weft) | Jute (jute)Antibacterial rate of fiber/%) | |
Example 1 | 221N | 207N | 95 |
Example 2 | 219N | 208N | 94 |
The foregoing shows and describes the general principles, essential features, and advantages of the invention. It will be understood by those skilled in the art that the present invention is not limited to the embodiments described above, which are given by way of illustration of the principles of the present invention, and that various changes and modifications may be made without departing from the spirit and scope of the invention as defined by the appended claims. The scope of the invention is defined by the appended claims and equivalents thereof.
Claims (3)
1. A preparation method of a jute fiber antibacterial blended fabric is characterized by comprising the following steps:
a, manufacturing a surface layer: the surface layer is made of jute fiber antibacterial fabric, the jute fiber antibacterial fabric is formed by interweaving warps and wefts, the warps are blended yarns of jute fibers and cotton fibers, and the wefts are blended yarns of wool fibers and cotton fibers;
b, manufacturing an intermediate layer: the first fabric layer and the third fabric layer are formed by blending wool fibers and cotton fibers, then blending the wool fibers and the cotton fibers, and weaving the wool fibers and the jute fibers into cloth, the second fabric layer is made of cotton fiber yarns, and the first fabric layer, the second fabric layer and the third fabric layer are attached together in sequence in a dispensing or needle sewing mode;
c, manufacturing of the inner layer: firstly, uniformly mixing jute fibers, wool fibers and cotton fibers, then carrying out cotton cleaning, cotton carding, drawing, roving, fine sand, automatic spooling, yarn steaming, high-speed doubling and double twisting treatment to obtain fine imitation yarns, and then weaving to obtain lining fabric;
d, integrating lamination: and sequentially laminating the surface layer, the middle layer and the inner layer, and then curing, shaping and calendaring to obtain the product.
2. The method for preparing the jute fiber antibacterial blended fabric according to claim 1, wherein the jute fiber antibacterial blended fabric comprises the following steps: the curing and processing time in the step d is 10-20h, the temperature is 20-50 ℃, and the humidity is 40-60%.
3. The method for preparing the jute fiber antibacterial blended fabric according to claim 2, which is characterized by comprising the following steps: in the step d, the calendering temperature is 60-100 ℃, and the pressure is 50-100Kg/cm2The speed is 15-30 m/min.