CN110938841A - 新型板状石墨阳极 - Google Patents

新型板状石墨阳极 Download PDF

Info

Publication number
CN110938841A
CN110938841A CN201911315907.6A CN201911315907A CN110938841A CN 110938841 A CN110938841 A CN 110938841A CN 201911315907 A CN201911315907 A CN 201911315907A CN 110938841 A CN110938841 A CN 110938841A
Authority
CN
China
Prior art keywords
plate
graphite
anode
novel
insulating layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201911315907.6A
Other languages
English (en)
Inventor
谢雄
陈晓春
康钦科
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xinshao State Antimony Industry Co Ltd
Original Assignee
Xinshao State Antimony Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xinshao State Antimony Industry Co Ltd filed Critical Xinshao State Antimony Industry Co Ltd
Priority to CN201911315907.6A priority Critical patent/CN110938841A/zh
Publication of CN110938841A publication Critical patent/CN110938841A/zh
Pending legal-status Critical Current

Abstract

本发明提出了一种新型板状石墨阳极，由石墨板、固定夹板和导电梁构成，所述石墨板与固定夹板之间设有绝缘层，所述石墨板中间有若干分布均匀的流动孔。本发明延长了阳极使用寿命，新型阳极8个月以上对石墨板进行一次重新更换，大大节省了员工劳动强度、延长了生产时间降低了生产成本。减小了矿浆搅动的阻力，改善了电解槽的搅拌情况。消除了电解时尖端放电的现象，大大提高了电解效率。

Description

新型板状石墨阳极
技术领域
本发明涉及电化学技术领域，具体涉及一种新型板状石墨阳极。
背景技术
高砷锑金精矿矿浆电解项目是北京科技大学与新邵辰州锑业有限责任公司共同研发的新型湿法电解生产锑的技术，电解目前采用的阳极为栅栏状石墨材质，每块阳极共有25根截面为长方形的石墨棒组成，上端采用钛固定支架。在使用过程中，经常因为电路密度分布不均匀导致部分石墨黏合剂老化造成石墨阳极发生电化学腐蚀而毁坏，使用寿命约为6-8个月，对生产的连续稳定及员工劳动强度造成了一定的影响。
发明内容
本发明的目的在于提出一种新型板状石墨阳极，延长了阳极使用寿命，新型阳极8个月以上对石墨板进行一次重新更换。
本发明的技术方案是这样实现的：
本发明提供一种新型板状石墨阳极，由石墨板、固定夹板和导电梁构成，所述石墨板与固定夹板之间设有绝缘层，所述石墨板中间有若干分布均匀的流动孔。
作为本发明的进一步改进，所述固定夹板为PP材质。
作为本发明的进一步改进，所述石墨板通过钛制螺丝在导电梁上进行固定。
作为本发明的进一步改进，所述流动孔至少有3个。
作为本发明的进一步改进，所述石墨板的尺寸为长2000mm，宽320mm，高40mm。
作为本发明的进一步改进，所述绝缘层为一层涂有聚四氟乙烯乳液的宽带。
作为本发明的进一步改进，所述绝缘层的宽度在100-120mm。
作为本发明的进一步改进，所述导电梁的材质为铜或银。
作为本发明的进一步改进，所述导电梁的材质为铜。
本发明具有如下有益效果：
1.延长了阳极使用寿命，新型阳极8个月以上对石墨板进行一次重新更换，
2.大大节省了员工劳动强度、延长了生产时间降低了生产成本。
3.减小了矿浆搅动的阻力，改善了电解槽的搅拌情况。
4.消除了电解时尖端放电的现象，大大提高了电解效率。
附图说明
为了更清楚地说明本发明实施例或现有技术中的技术方案，下面将对实施例或现有技术描述中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本发明的一些实施例，对于本领域普通技术人员来讲，在不付出创造性劳动性的前提下，还可以根据这些附图获得其他的附图。
图1为本发明新型板状石墨阳极的结构示意图；
其中，1.石墨板；2.绝缘层；3.导电梁；4.固定夹板；5.流动孔。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
一种新型板状石墨阳极，由石墨板1、固定夹板4和导电梁3构成，所述石墨板1与固定夹板4之间设有绝缘层2，所述石墨板1中间有若干分布均匀的流动孔5。板中间有若干分布均匀的流动孔5，便于矿浆流通。石墨板1之间用PP材质的固定夹板4进行固定与拉紧，防止因搅动而引起阳极晃动。石墨板1与导电梁3采用钛制螺丝在导电梁3上进行固定，并在石墨板1阳极与溶液接触面处进行绝缘处理，设有绝缘层2，从而延长阳极使用寿命。
流动孔5至少有3个。
石墨板1的尺寸为长2000mm，宽320mm，高40mm。
绝缘层2为一层涂有聚四氟乙烯乳液的宽带，绝缘层2的宽度在100mm。
导电梁3的材质为铜。
实施例2
一种新型板状石墨阳极，由石墨板1、固定夹板4和导电梁3构成，所述石墨板1与固定夹板4之间设有绝缘层2，所述石墨板1中间有若干分布均匀的流动孔5。石墨板1之间用PP材质的固定夹板4进行固定与拉紧。石墨板1与导电梁3采用钛制螺丝在导电梁3上进行固定，并在石墨板1阳极与溶液接触面处进行绝缘处理，设有绝缘层2。
流动孔5至少有3个。
石墨板1的尺寸为长2000mm，宽320mm，高40mm。
绝缘层2为一层涂有聚四氟乙烯乳液的宽带，绝缘层2的宽度在120mm。
导电梁3的材质为银。
实施例3
一种新型板状石墨阳极，由石墨板1、固定夹板4和导电梁3构成，所述石墨板1与固定夹板4之间设有绝缘层2，所述石墨板1中间有若干分布均匀的流动孔5。石墨板1之间用PP材质的固定夹板4进行固定与拉紧。石墨板1与导电梁3采用钛制螺丝在导电梁3上进行固定，并在石墨板1阳极与溶液接触面处进行绝缘处理，设有绝缘层2。
流动孔5至少有3个。
石墨板1的尺寸为长2000mm，宽320mm，高40mm。
绝缘层2为一层涂有聚四氟乙烯乳液的宽带，绝缘层2的宽度在110mm。
导电梁3的材质为铜。
与现有技术相比，本发明延长了阳极使用寿命，新型阳极8个月以上对石墨板进行一次重新更换，大大节省了员工劳动强度、延长了生产时间降低了生产成本。减小了矿浆搅动的阻力，改善了电解槽的搅拌情况。消除了电解时尖端放电的现象，大大提高了电解效率。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (9)

1.一种新型板状石墨阳极，其特征在于，由石墨板、固定夹板和导电梁构成，所述石墨板与固定夹板之间设有绝缘层，所述石墨板中间有若干分布均匀的流动孔。
2.根据权利要求1所述一种新型板状石墨阳极，其特征在于，所述固定夹板为PP材质。
3.根据权利要求1所述一种新型板状石墨阳极，其特征在于，所述石墨板通过钛制螺丝在导电梁上进行固定。
4.根据权利要求1所述一种新型板状石墨阳极，其特征在于，所述流动孔至少有3个。
5.根据权利要求1所述一种新型板状石墨阳极，其特征在于，所述石墨板的尺寸为长2000mm，宽320mm，高40mm。
6.根据权利要求1所述一种新型板状石墨阳极，其特征在于，所述绝缘层为一层涂有聚四氟乙烯乳液的宽带。
7.根据权利要求6所述一种新型板状石墨阳极，其特征在于，所述绝缘层的宽度在100-120mm。
8.根据权利要求1所述一种新型板状石墨阳极，其特征在于，所述导电梁的材质为铜或银。
9.根据权利要求8所述一种新型板状石墨阳极，其特征在于，所述导电梁的材质为铜。
CN201911315907.6A 2019-12-19 2019-12-19 新型板状石墨阳极 Pending CN110938841A (zh)